RU2033290C1

RU2033290C1 - Line for descalling and drawing wire

Info

Publication number: RU2033290C1
Authority: RU
Inventors: Л.Г. Делюсто
Original assignee: Акционерное общество - Малое предприятие "Дуга"
Priority date: 1991-09-10
Filing date: 1991-09-10
Publication date: 1995-04-20

Abstract

FIELD: drawing production. SUBSTANCE: line, having unwinding apparatus, unit for, mechanically removing scale and a drawing tool, also has an apparatus for magnetizing and cooling wire, mounted before the drawing tool with possibility of longitudinal motion and being in the form of a cylindrical body, filled by liquid nitrogen, and a permanent magnet, whose poles embrace the body. EFFECT: enhanced efficiency. 1 cl, 2 dwg

Description

Изобретение относится к области волочильного производства, а именно к оборудованию для совмещения двух процессов: очистки и волочения проволоки. Известен ряд линий, основанных на совмещении процессов очистки от окалины и волочения [1]
Наиболее близким по технической сущности к предложенному является техническое решение, в котором раскрыта линия очистки и волочения проволоки [2] содержащая размоточное устройство, узел для механического удаления окалины и волочильный инструмент.The invention relates to the field of drawing production, and in particular to equipment for combining two processes: cleaning and wire drawing. A number of lines are known based on the combination of descaling and drawing processes [1]
The closest in technical essence to the proposed one is a technical solution in which a wire cleaning and drawing line [2] is disclosed, comprising an unwinding device, a unit for mechanical descaling, and a drawing tool.

Линия имеет ряд недостатков: на поверхности очищенной проволоки остаются продольные глубокие риски, которые затрудняют захват смазки, что приводит к частым обрывам проволоки и снижает производительность стана, проволока получает дополнительный наклеп в результате пропуска через роликовый окалиноломатель. В случае многократного волочения без смягчающего обжига проволока рвется в результате деформационного нагрева. The line has several drawbacks: deep deep-seated risks remain on the surface of the cleaned wire, which make it difficult to lubricate, which leads to frequent wire breaks and reduces the productivity of the mill, the wire gets additional hardening as a result of passing through a roller descaler. In the case of repeated drawing without softening firing, the wire breaks as a result of deformation heating.

Технической задачей изобретения является создание возможности в совмещенной линии вести волочение на высоких скоростях без обрывов и упрочнения на многократных станах без снижения качества проволоки. An object of the invention is to create the possibility in a combined line to draw at high speeds without breaks and hardening on multiple mills without reducing the quality of the wire.

Техническая задача решается установкой перед волочильным инструментом устройства для намагничивания и охлаждения проволоки, выполненного в виде цилиндрического корпуса, заполненного жидким азотом, и постоянного электромагнита, полюсами охватывающего корпус и установленного перед волочильным инструментом с возможностью продольного переме- щения. The technical problem is solved by installing in front of the drawing tool a device for magnetizing and cooling the wire, made in the form of a cylindrical body filled with liquid nitrogen, and a permanent electromagnet with poles covering the body and installed in front of the drawing tool with the possibility of longitudinal movement.

Деформационный нагрев зависит от начальной температуры, предела прочности проволоки, диаметра, скорости и степени обжатия проволоки, поэтому, если уменьшить деформационный нагрев за счет охлаждения проволоки, можно осуществлять волочение проволоки с большими обжатиями при меньшей кратности стана (при всех других прочих равных условиях). Охлаждая проволоку жидким азотом, можно получить отрицательную температуру на поверхности и по сечению проволоки и значительно (на 70-80%) уменьшить деформационный нагрев, в частности температуру на поверхности проволоки в конце очага деформации, при увеличении скорости волочения это позволяет сохранить высокое качество проволоки после волочения. Уменьшение средней температуры проволоки приводит к увеличению скорости движения электронов и повышению их энергии, передаваемой дислокациям во время столкновений, подвижность которых возрастает, а это приводит к повышению пластичности металла в очаге деформации. The deformation heating depends on the initial temperature, the tensile strength of the wire, the diameter, speed and degree of compression of the wire, therefore, if the deformation heating is reduced by cooling the wire, it is possible to draw the wire with large reductions at a lower multiplicity of the mill (all other things being equal). Cooling the wire with liquid nitrogen, you can get a negative temperature on the surface and the cross section of the wire and significantly (70-80%) reduce the deformation heating, in particular the temperature on the surface of the wire at the end of the deformation zone, with an increase in the drawing speed this allows you to maintain high quality wire after drawing. A decrease in the average temperature of the wire leads to an increase in the velocity of electrons and an increase in their energy transferred to dislocations during collisions, the mobility of which increases, and this leads to an increase in the ductility of the metal in the deformation zone.

На фиг. 1 изображена схема линии очистки от окалины и волочения проволоки; на фиг. 2 схема устройства для намагничивания и охлаждения проволоки. In FIG. 1 is a diagram of a descaling and wire drawing line; in FIG. 2 diagram of a device for magnetizing and cooling a wire.

Линия содержит размоточное устройство 1, петлеуловитель 2, окалиноломатель 3, установку 4 для очистки проволоки с помощью ферромагнитных абразивных порошков, устройство 5 для намагничивания и охлаждения проволоки, волочильный стан 6 (с одним или несколькими барабанами). The line contains an unwinding device 1, a loop catcher 2, a descaler 3, an installation 4 for cleaning the wire using ferromagnetic abrasive powders, a device 5 for magnetizing and cooling the wire, drawing mill 6 (with one or more drums).

Устройство для намагничивания и охлаждения проволоки перед волочением содержит расходную емкость 7 с жидким азотом при температуре 196^оС, изотермическую камеру 8, электромагнит 9 для намагничивания проволоки 10.Apparatus for magnetization and cooling the wire before drawing comprises a storage container 7 with liquid nitrogen at a temperature of 196 ^{° C,} isothermal chamber 8, 9 electromagnet for magnetization wire 10.

Работа линии происходит следующим образом. Бунт катанки подается на размоточное устройство 1 и через петлеуловитель 2 конец катанки заправляется в окалиноломатель 3, в установку 4 для очистки и далее в устройство 5 для намагничивания и охлаждения проволоки 10, после чего конец затачивается и пропускается через волоку первого блока (барабана) волочильного стана 6. Включаются последовательно в работу установка для очистки проволоки, устройство для намагничивания и охлаждения проволоки, волочильный стан. The line is as follows. The wire rod rip is fed to the unwinding device 1 and through the loop catcher 2 the end of the wire rod is fed into the descaling machine 3, into the cleaning unit 4 and then into the device 5 for magnetizing and cooling the wire 10, after which the end is sharpened and passed through the fiber of the first block (drum) of the drawing mill 6. The installation for cleaning the wire, the device for magnetizing and cooling the wire, and the drawing mill are included in series.

Устройство для намагничивания и охлаждения проволоки работает следующим образом. Из расходной емкости 7 жидкий азот подается в изотермическую камеру 8, в которой жидкий азот испаряется, превращаясь в газ. При этом происходит охлаждение проволоки 10 до отрицательной температуры. Одновременно проволока намагничивается при помощи электромагнита 9. Обработанная проволока поступает в волоку на волочильный стан. A device for magnetization and cooling of the wire works as follows. From the supply tank 7, liquid nitrogen is supplied to the isothermal chamber 8, in which liquid nitrogen evaporates, turning into gas. When this occurs, the cooling of the wire 10 to a negative temperature. At the same time, the wire is magnetized by means of an electromagnet 9. The processed wire enters the wire drawing on the drawing mill.

Предложенная линия позволяет увеличить производительность и повысить качество проволоки. The proposed line allows you to increase productivity and improve the quality of the wire.

Claims

LINE CLEANING AND DRAWING WIRE, comprising an unwinding device, a unit for mechanical descaling and drawing tools, characterized in that the line is equipped with a device for magnetizing and cooling the wire, made in the form of a cylindrical body filled with liquid nitrogen, and a permanent electromagnet, poles covering the body and installed in front of the drawing tool with the possibility of longitudinal movement.