RU2019119251A - Компонент заполнителя из полимерного композита и способ его изготовления - Google Patents
Компонент заполнителя из полимерного композита и способ его изготовления Download PDFInfo
- Publication number
- RU2019119251A RU2019119251A RU2019119251A RU2019119251A RU2019119251A RU 2019119251 A RU2019119251 A RU 2019119251A RU 2019119251 A RU2019119251 A RU 2019119251A RU 2019119251 A RU2019119251 A RU 2019119251A RU 2019119251 A RU2019119251 A RU 2019119251A
- Authority
- RU
- Russia
- Prior art keywords
- component
- paragraphs
- filler
- fibers
- honeycomb
- Prior art date
Links
- 239000000945 filler Substances 0.000 title claims 14
- 238000000034 method Methods 0.000 title claims 10
- 229920000642 polymer Polymers 0.000 title claims 4
- 239000002131 composite material Substances 0.000 title claims 3
- 238000004519 manufacturing process Methods 0.000 title claims 2
- 239000000306 component Substances 0.000 claims 17
- 241000264877 Hippospongia communis Species 0.000 claims 11
- 239000000463 material Substances 0.000 claims 9
- 229920001643 poly(ether ketone) Polymers 0.000 claims 6
- 229920001601 polyetherimide Polymers 0.000 claims 6
- 239000000758 substrate Substances 0.000 claims 6
- 239000000835 fiber Substances 0.000 claims 5
- XQUPVDVFXZDTLT-UHFFFAOYSA-N 1-[4-[[4-(2,5-dioxopyrrol-1-yl)phenyl]methyl]phenyl]pyrrole-2,5-dione Chemical compound O=C1C=CC(=O)N1C(C=C1)=CC=C1CC1=CC=C(N2C(C=CC2=O)=O)C=C1 XQUPVDVFXZDTLT-UHFFFAOYSA-N 0.000 claims 4
- 239000004696 Poly ether ether ketone Substances 0.000 claims 4
- 239000004642 Polyimide Substances 0.000 claims 4
- 239000004734 Polyphenylene sulfide Substances 0.000 claims 4
- 239000003365 glass fiber Substances 0.000 claims 4
- 229920003192 poly(bis maleimide) Polymers 0.000 claims 4
- 229920001652 poly(etherketoneketone) Polymers 0.000 claims 4
- 229920006260 polyaryletherketone Polymers 0.000 claims 4
- 229920002530 polyetherether ketone Polymers 0.000 claims 4
- 229920001721 polyimide Polymers 0.000 claims 4
- 229920000069 polyphenylene sulfide Polymers 0.000 claims 4
- 229920003002 synthetic resin Polymers 0.000 claims 4
- 239000000057 synthetic resin Substances 0.000 claims 4
- 229920001169 thermoplastic Polymers 0.000 claims 4
- 229920001187 thermosetting polymer Polymers 0.000 claims 4
- 239000004416 thermosoftening plastic Substances 0.000 claims 4
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 claims 3
- 239000000853 adhesive Substances 0.000 claims 3
- 230000001070 adhesive effect Effects 0.000 claims 3
- 150000005130 benzoxazines Chemical class 0.000 claims 3
- 239000011248 coating agent Substances 0.000 claims 3
- 238000000576 coating method Methods 0.000 claims 3
- 150000002118 epoxides Chemical class 0.000 claims 3
- 239000011159 matrix material Substances 0.000 claims 3
- 230000035699 permeability Effects 0.000 claims 3
- 150000002989 phenols Chemical class 0.000 claims 3
- 229920000728 polyester Polymers 0.000 claims 3
- 229920006295 polythiol Polymers 0.000 claims 3
- 229920005989 resin Polymers 0.000 claims 3
- 239000011347 resin Substances 0.000 claims 3
- 229920002748 Basalt fiber Polymers 0.000 claims 2
- 229920000049 Carbon (fiber) Polymers 0.000 claims 2
- 229920000271 Kevlar® Polymers 0.000 claims 2
- 239000004721 Polyphenylene oxide Substances 0.000 claims 2
- 239000004917 carbon fiber Substances 0.000 claims 2
- 230000006835 compression Effects 0.000 claims 2
- 238000007906 compression Methods 0.000 claims 2
- 239000008358 core component Substances 0.000 claims 2
- XLJMAIOERFSOGZ-UHFFFAOYSA-M cyanate Chemical compound [O-]C#N XLJMAIOERFSOGZ-UHFFFAOYSA-M 0.000 claims 2
- 239000004643 cyanate ester Substances 0.000 claims 2
- 150000002148 esters Chemical class 0.000 claims 2
- 239000004761 kevlar Substances 0.000 claims 2
- 239000002759 woven fabric Substances 0.000 claims 2
- 239000004593 Epoxy Substances 0.000 claims 1
- ISWSIDIOOBJBQZ-UHFFFAOYSA-N Phenol Chemical compound OC1=CC=CC=C1 ISWSIDIOOBJBQZ-UHFFFAOYSA-N 0.000 claims 1
- 229920000265 Polyparaphenylene Polymers 0.000 claims 1
- 150000001913 cyanates Chemical class 0.000 claims 1
- 229920001971 elastomer Polymers 0.000 claims 1
- 239000000806 elastomer Substances 0.000 claims 1
- 238000010438 heat treatment Methods 0.000 claims 1
- -1 polyphenylene Polymers 0.000 claims 1
- 239000011148 porous material Substances 0.000 claims 1
- 239000010453 quartz Substances 0.000 claims 1
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29D—PRODUCING PARTICULAR ARTICLES FROM PLASTICS OR FROM SUBSTANCES IN A PLASTIC STATE
- B29D99/00—Subject matter not provided for in other groups of this subclass
- B29D99/0089—Producing honeycomb structures
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B31—MAKING ARTICLES OF PAPER, CARDBOARD OR MATERIAL WORKED IN A MANNER ANALOGOUS TO PAPER; WORKING PAPER, CARDBOARD OR MATERIAL WORKED IN A MANNER ANALOGOUS TO PAPER
- B31D—MAKING ARTICLES OF PAPER, CARDBOARD OR MATERIAL WORKED IN A MANNER ANALOGOUS TO PAPER, NOT PROVIDED FOR IN SUBCLASSES B31B OR B31C
- B31D3/00—Making articles of cellular structure, e.g. insulating board
- B31D3/005—Making cellular structures from corrugated webs or sheets
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B31—MAKING ARTICLES OF PAPER, CARDBOARD OR MATERIAL WORKED IN A MANNER ANALOGOUS TO PAPER; WORKING PAPER, CARDBOARD OR MATERIAL WORKED IN A MANNER ANALOGOUS TO PAPER
- B31D—MAKING ARTICLES OF PAPER, CARDBOARD OR MATERIAL WORKED IN A MANNER ANALOGOUS TO PAPER, NOT PROVIDED FOR IN SUBCLASSES B31B OR B31C
- B31D3/00—Making articles of cellular structure, e.g. insulating board
- B31D3/02—Making articles of cellular structure, e.g. insulating board honeycombed structures, i.e. the cells having an essentially hexagonal section
- B31D3/0223—Making honeycomb cores, e.g. by piling a plurality of web sections or sheets
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B31—MAKING ARTICLES OF PAPER, CARDBOARD OR MATERIAL WORKED IN A MANNER ANALOGOUS TO PAPER; WORKING PAPER, CARDBOARD OR MATERIAL WORKED IN A MANNER ANALOGOUS TO PAPER
- B31D—MAKING ARTICLES OF PAPER, CARDBOARD OR MATERIAL WORKED IN A MANNER ANALOGOUS TO PAPER, NOT PROVIDED FOR IN SUBCLASSES B31B OR B31C
- B31D3/00—Making articles of cellular structure, e.g. insulating board
- B31D3/02—Making articles of cellular structure, e.g. insulating board honeycombed structures, i.e. the cells having an essentially hexagonal section
- B31D3/0292—Making articles of cellular structure, e.g. insulating board honeycombed structures, i.e. the cells having an essentially hexagonal section involving auxiliary operations, e.g. expanding, moistening, glue-applying, joining, controlling
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B3/00—Layered products comprising a layer with external or internal discontinuities or unevennesses, or a layer of non-planar shape; Layered products comprising a layer having particular features of form
- B32B3/10—Layered products comprising a layer with external or internal discontinuities or unevennesses, or a layer of non-planar shape; Layered products comprising a layer having particular features of form characterised by a discontinuous layer, i.e. formed of separate pieces of material
- B32B3/12—Layered products comprising a layer with external or internal discontinuities or unevennesses, or a layer of non-planar shape; Layered products comprising a layer having particular features of form characterised by a discontinuous layer, i.e. formed of separate pieces of material characterised by a layer of regularly- arranged cells, e.g. a honeycomb structure
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B3/00—Layered products comprising a layer with external or internal discontinuities or unevennesses, or a layer of non-planar shape; Layered products comprising a layer having particular features of form
- B32B3/26—Layered products comprising a layer with external or internal discontinuities or unevennesses, or a layer of non-planar shape; Layered products comprising a layer having particular features of form characterised by a particular shape of the outline of the cross-section of a continuous layer; characterised by a layer with cavities or internal voids ; characterised by an apertured layer
- B32B3/28—Layered products comprising a layer with external or internal discontinuities or unevennesses, or a layer of non-planar shape; Layered products comprising a layer having particular features of form characterised by a particular shape of the outline of the cross-section of a continuous layer; characterised by a layer with cavities or internal voids ; characterised by an apertured layer characterised by a layer comprising a deformed thin sheet, i.e. the layer having its entire thickness deformed out of the plane, e.g. corrugated, crumpled
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
- B32B5/02—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by structural features of a fibrous or filamentary layer
- B32B5/024—Woven fabric
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J201/00—Adhesives based on unspecified macromolecular compounds
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2067/00—Use of polyesters or derivatives thereof, as moulding material
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2079/00—Use of polymers having nitrogen, with or without oxygen or carbon only, in the main chain, not provided for in groups B29K2061/00 - B29K2077/00, as moulding material
- B29K2079/08—PI, i.e. polyimides or derivatives thereof
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
- B29K2105/06—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts
- B29K2105/08—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts of continuous length, e.g. cords, rovings, mats, fabrics, strands or yarns
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
- B29K2105/06—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts
- B29K2105/08—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts of continuous length, e.g. cords, rovings, mats, fabrics, strands or yarns
- B29K2105/0809—Fabrics
- B29K2105/0845—Woven fabrics
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
- B29K2105/06—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts
- B29K2105/08—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts of continuous length, e.g. cords, rovings, mats, fabrics, strands or yarns
- B29K2105/0872—Prepregs
- B29K2105/089—Prepregs fabric
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
- B29K2105/25—Solid
- B29K2105/253—Preform
- B29K2105/256—Sheets, plates, blanks or films
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2309/00—Use of inorganic materials not provided for in groups B29K2303/00 - B29K2307/00, as reinforcement
- B29K2309/08—Glass
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2995/00—Properties of moulding materials, reinforcements, fillers, preformed parts or moulds
- B29K2995/0037—Other properties
- B29K2995/0063—Density
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
- Y10T428/24149—Honeycomb-like
Landscapes
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Textile Engineering (AREA)
- Laminated Bodies (AREA)
- Reinforced Plastic Materials (AREA)
- Compositions Of Macromolecular Compounds (AREA)
Claims (37)
1. Компонент заполнителя, в котором соблюдается следующее условие а):
а) его объёмная плотность составляет ≤ около 48, в частности, ≤ около 40, предпочтительно ≤ около 32 кг/м3, особо предпочтительно ≤ 26 кг/м3,
а также соблюдается по меньшей мере одно из двух условий b1) и b2):
b1) его отношение между модулем сжатия и объёмной плотностью составляет ≥ около 4,5 МПа/кг/м3, предпочтительно ≥ 5,5 МПа/кг/м3, особо предпочтительно ≥ 5,8 МПа/кг/м3,
b2) размер его ячеек составляет ≤ около 9,6 мм, в частности, ≤ 6,4 мм, предпочтительно ≤ 4,8 мм, особо предпочтительно ≤ 3,2 мм, совершенно особо предпочтительно ≤ 1,6 мм.
2. Компонент заполнителя по п. 1, отличающийся тем, что он представляет собой сотовый компонент, при этом сотовый компонент имеет многоугольную, предпочтительно шестиугольную, прямоугольную или кругообразную геометрическую форму ячейки.
3. Компонент заполнителя по любому из пп. 1 или 2, отличающийся тем, что он получен из стеклянных волокон (Е-, S2-), углеродных волокон, волокон кевлара, волокон базальта, предпочтительно из волокон кварцевого стекла, или из гибридных конструкций из указанных волокон.
4. Компонент заполнителя по любому из пп. 1-3, отличающийся тем, что он является полимерным композитом из волокон кварцевого стекла.
5. Компонент заполнителя по любому из пп. 1-4, отличающийся тем, что он получен из полимера, содержащего термореактивную или термопластичную матрицу, предпочтительно из группы, состоящей из сложных эфиров цианата или полиимидов, при необходимости, также фенолов, эпоксидов, бензоксазинов, бисмалеимида (ВМI), полиэфиримидов (PEI), полиэфиркетонов (полиэфиркатон (PEK), полиэфирэфиркетон (PEEK), полиарилэфиркетон (PAEK), полиэфиркетонкетон (PEKK)), политиоэфиров (полифениленсульфид (PPS)), полиэфиров (полифенилен (PP), полифенилепоксид (PPO)).
6. Компонент заполнителя по любому из пп. 1-5, отличающийся тем, что он является композитом, состоящим из волокон и/или другого материала подложки или наполнителя и полимера, содержащего термореактивную или термопластичную матрицу, предпочтительно из группы, стоящей из сложных эфиров цианата или полиимидов, при необходимости, также фенолов, эпоксидов, бензоксазинов, ВМI, полиэфиримидов (PEI), полиэфиркетонов (PEK, PEEK, PAEK, PEKK), политиоэфиров (PPS), полиэфиров (PP, PPO).
7. Компонент заполнителя по любому из пп. 1-6, отличающийся тем, что он получен из тканого материала и/или материала, подобного нетканому материалу.
8. Компонент заполнителя по п. 7, отличающийся тем, что тканый материал не полностью пропитан и/или не полностью покрыт и обеспечивает воздухопроницаемость через имеющие открытые поры стенки между ячейками.
9. Компонент заполнителя по любому из пп. 1-8, отличающийся тем, что он обладает высокой термостойкостью, превышающей 350°С.
10. Компонент заполнителя по любому из пп. 1-9, отличающийся тем, что он имеет превосходные диэлектрические свойства, при этом диэлектрическая постоянная составляет ≤ 1,1, в частности, ≤ 1,0, коэффициент потерь < 0,003, в частности, < 0,002.
11. Компонент заполнителя по любому из пп. 1-10, отличающийся тем, что он имеет отношение между прочностью при сжатии и объёмной плотностью ≥ около 0,04 МПа/кг/м3, предпочтительно ≥ 0,06 МПа/кг/м3.
12. Способ изготовления компонента заполнителя из имеющего открытые поры материала подложки, при этом:
i) на полотно материала из материала подложки посредством средства для нанесения наносят полосы из клеящего вещества в виде правильных узоров,
ii) формируют стопку из отрезков полотна материала, которые накладываются друг на друга со смещением относительно узора из полос таким образом, что
iia) полосы на нижележащем отрезке в каждом случае располагаются между полосами лежащего поверх него отрезка,
или
iib) полосы на нижележащем отрезке в каждом случае располагаются со смещением, но не по центру между полосами лежащего поверх него отрезка,
iii) расположенные друг на друге отрезки соединяют между собой в местах полос,
iv) стопку расширяют, образуя при этом сотовую форму с многоугольной структурой, в частности, сотовую форму шестиугольной, прямоугольной или кругообразной геометрической формы ячеек для получения шестиугольных, перерасширенных, прямоугольных и 3D сотовых заполнителей,
v) сотовую форму пропитывают и/или покрывают синтетической смолой,
vi) сотовую форму, покрытую синтетической смолой, подвергают стадии отверждения для отверждения синтетической смолы,
vii) полученную таким образом сотовую форму разрезают с образованием сотовых компонентов.
13. Способ по п. 12, отличающийся тем, что имеющая открытые поры подложка является тканым материалом и/или материалом, подобным нетканому материалу, предпочтительно, но не исключительно, содержащим стеклянные волокна (E-, S2-, кварц), углеродные волокна, волокна кевлара, волокна базальта или гибридные тканые материалы из перечисленных волокон.
14. Способ по п. 13, отличающийся тем, что подложка частично предварительно пропитана или покрыта смолой для уменьшения пористости перед процессом расширения, причём после нанесения покрытия пористость составляет менее 40%, что покрытие характеризуется весовым отношением от 10 до 75% относительно веса подложки и что после нанесения покрытия и, при необходимости, отверждения подложка с покрытием является термостабильной при 160 – 250°С и гибкой для деформации таких полученных предварительной пропиткой слоёв при расширении с использованием низких усилий расширения.
15. Способ по п. 13, отличающийся тем, что подложку в виде сотового компонента не полностью пропитывают и/или покрывают смолой, обеспечивая воздухопроницаемость через имеющие открытые поры стенки между ячейками.
16. Способ по любому из пп. 12-14, отличающийся тем, что в качестве клеящего вещества используют термореактивный материал, термопласт или эластомер, предпочтительно, но не исключительно, клеящее вещество из фенола, эпоксида, полиимида, сложного эфира цианата.
17. Способ по любому из пп. 12-16, отличающийся тем, что после стадии iv) расширения проводят стабилизацию сотовой формы путём термообработки.
18. Способ по любому из пп. 12-17, отличающийся тем, что в качестве смолы используется термореактивная или термопластичная матричная система предпочтительно из группы, состоящей из сложных эфиров цианата или полиимидов, при необходимости, также фенолов, эпоксидов, бензоксазинов, ВМI, полиэфиримидов (PEI), полиэфиркетонов (PEK, PEEK, PAEK, PEKK), политиоэфиров (PPS), полиэфиров (PP, PPO).
19. Способ по любому из пп. 12-18, отличающийся тем, что стадии v) и vi) проводят одно- или многократно для нанесения одного или нескольких слоёв синтетической смолы.
20. Компонент заполнителя, изготовленный способом по любому из пп. 12-19.
21. Компонент заполнителя по п. 20, отличающийся тем, что имеющая открытые поры подложка не полностью пропитана и/или покрыта, обеспечивая воздухопроницаемость через имеющие открытые поры стенки между ячейками.
22. Компонент заполнителя по п. 20 или 21, отличающийся тем, что он обладает превосходными диэлектрическими свойствами, при этом диэлектрическая постоянная составляет ≤ 1,1, в частности, ≤ 1,0, коэффициент потерь < 0,003, в частности, < 0,002.
23. Компонент заполнителя по любому из пп. 20-22, отличающийся тем, что он характеризуется отношением между модулем сжатия и объёмной плотностью ≥ около 5,5 МПа/кг/м3, предпочтительно ≥ около 5,8 МПа/кг/м3.