Abstract
Description
Изобретение относится к производству сплавов на основе свинца, используемых преимущественно в аккумуляторах. The invention relates to the production of lead-based alloys used primarily in batteries.
Известен сплав на основе свинца, содержащий серебро, таллий, стронций, сурьму /1/. Known lead-based alloy containing silver, thallium, strontium, antimony / 1 /.
Известен сплав на основе свинца следующего состава, мас. % : кобальт 0,001-0,5; алюминий 0,005-0,05; кальций 0,05-0,1; олово 0,05-0,1; свинец остальное /2/. Known alloy based on lead of the following composition, wt. %: cobalt 0.001-0.5; aluminum 0.005-0.05; calcium 0.05-0.1; tin 0.05-0.1; lead the rest / 2 /.
Целью изобретения является повышение коррозионной стойкости сплава. The aim of the invention is to increase the corrosion resistance of the alloy.
Цель достигается тем, что в состав сплава дополнительно вводят цирконий, при следующем соотношении компонентов, мас. % : кобальт 0,01-0,05; алюминий 0,1-0,2; кальций 0,05-0,1; олово 0,05-0,15; цирконий 0,5-1,0; свинец остальное. The goal is achieved by the fact that the composition of the alloy is additionally introduced zirconium, in the following ratio of components, wt. %: cobalt 0.01-0.05; aluminum 0.1-0.2; calcium 0.05-0.1; tin 0.05-0.15; zirconium 0.5-1.0; lead the rest.
В таблице приведены составы сплава. The table shows the alloy compositions.
Коррозионная стойкость /потери в весе в сульфатных растворах/ сплава составит 0,001-0,0015 г/м2 ч для всех составов.Corrosion resistance / weight loss in sulfate solutions / alloy will be 0.001-0.0015 g / m 2 h for all compositions.
Claims (1)
Кобальт 0,01 - 0,05,
Алюминий 0,1 - 0,2
Кальций 0,05 - 0,1
Олово 0,05 - 0,15
Цирконий 0,5 - 1,0
Свинец ОстальноеLEAD BASED ALLOY, containing cobalt, aluminum, calcium and tin, characterized in that, in order to increase corrosion resistance, it additionally contains zirconium in the following ratio of components, wt. %:
Cobalt 0.01 - 0.05,
Aluminum 0.1 - 0.2
Calcium 0.05 - 0.1
Tin 0.05 - 0.15
Zirconium 0.5 - 1.0
Lead Else
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SU5039759 RU2012624C1 (en) | 1992-04-23 | 1992-04-23 | Lead-base alloy |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SU5039759 RU2012624C1 (en) | 1992-04-23 | 1992-04-23 | Lead-base alloy |
Publications (1)
Publication Number | Publication Date |
---|---|
RU2012624C1 true RU2012624C1 (en) | 1994-05-15 |
Family
ID=21603004
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
SU5039759 RU2012624C1 (en) | 1992-04-23 | 1992-04-23 | Lead-base alloy |
Country Status (1)
Country | Link |
---|---|
RU (1) | RU2012624C1 (en) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP2024133A2 (en) * | 2006-02-23 | 2009-02-18 | RSR Technologies, Inc. | Improved alloy and anode for use in the electrowinning of metals |
-
1992
- 1992-04-23 RU SU5039759 patent/RU2012624C1/en active
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP2024133A2 (en) * | 2006-02-23 | 2009-02-18 | RSR Technologies, Inc. | Improved alloy and anode for use in the electrowinning of metals |
JP2009527652A (en) * | 2006-02-23 | 2009-07-30 | アールエスアール テクノロジーズ, インコーポレイテッド | Improved alloys and anodes for use in electrowinning metals |
EP2024133A4 (en) * | 2006-02-23 | 2010-10-06 | Rsr Technologies Inc | Improved alloy and anode for use in the electrowinning of metals |
JP4864101B2 (en) * | 2006-02-23 | 2012-02-01 | アールエスアール テクノロジーズ, インコーポレイテッド | Improved alloys and anodes for use in electrowinning metals |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CA2124722A1 (en) | Battery grids and plates and lead-acid batteries made using such grids and plates | |
ATE207975T1 (en) | LEAD-CALCIUM ALLOYS, ESPECIALLY BATTERY GRIDS | |
CA2061023A1 (en) | Zinc alloy powder for alkaline cell and method to produce the same | |
IE36739L (en) | Antimony lead alloys | |
RU2012624C1 (en) | Lead-base alloy | |
PL357637A1 (en) | Alloy for thin positive grid for lead acid batteries and method for manufacture of grid | |
HUP9701466A2 (en) | Well chippable alloys of aluminium | |
RU2012623C1 (en) | Lead-base alloy | |
US4137378A (en) | Calcium-strontium-lead grid alloy for use in lead-acid batteries | |
US4343872A (en) | Calcium-strontium-lead grid alloy for use in lead-acid batteries | |
JPS5721793A (en) | Brazed aluminum heat exchanger | |
JPS57158347A (en) | Shape storage alloy | |
JPS57121896A (en) | Solder alloy | |
JPS56166353A (en) | Functional copper alloy | |
GB1304095A (en) | ||
JPS57110646A (en) | High-purity aluminum alloy foil for anode of electrolytic capacitor | |
SU801598A1 (en) | Aluminium-base alloy | |
RU2012634C1 (en) | Aluminium-base alloy | |
RU2012617C1 (en) | Copper-base alloy | |
JPS5794537A (en) | Cu alloy having high heat resistance and high conductivity | |
RU2012616C1 (en) | Stannous bronze | |
RU92006750A (en) | ALUMINUM ALLOY FOR ANODES OF CHEMICAL SOURCES OF CURRENT | |
JPH0620689A (en) | Manganese dry battery | |
RU1785539C (en) | Aluminum based alloy | |
RU2012637C1 (en) | Aluminium-base alloy |