PL441554A1 - Aluminum-glass laminate and method of its production - Google Patents

Aluminum-glass laminate and method of its production

Info

Publication number
PL441554A1
PL441554A1 PL441554A PL44155422A PL441554A1 PL 441554 A1 PL441554 A1 PL 441554A1 PL 441554 A PL441554 A PL 441554A PL 44155422 A PL44155422 A PL 44155422A PL 441554 A1 PL441554 A1 PL 441554A1
Authority
PL
Poland
Prior art keywords
thickness
aluminum
layer
glass laminate
polymer resin
Prior art date
Application number
PL441554A
Other languages
Polish (pl)
Other versions
PL243792B1 (en
Inventor
Monika Ostapiuk
Jarosław Bieniaś
Patryk Jakubczak
Original Assignee
Politechnika Lubelska
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Politechnika Lubelska filed Critical Politechnika Lubelska
Priority to PL441554A priority Critical patent/PL243792B1/en
Publication of PL441554A1 publication Critical patent/PL441554A1/en
Publication of PL243792B1 publication Critical patent/PL243792B1/en

Abstract

Przedmiotem zgłoszenia jest laminat aluminium-szkło, który charakteryzuje się tym, że w części środkowej laminatu znajdują się dwie jednakowe warstwy samonaprawiające się (4a) o grubości od 1,5 mm do 2,3 mm każda, składające się z włókien szklanych wypełnionych diizocyjanianem izoforonu i połączonych żywicą epoksydową, które ułożone są naprzemiennie z dwiema jednakowymi warstwami samonaprawiającymi się (4b) o grubości od 1,5 mm do 2,3 mm każda, składającymi się z włókien szklanych wypełnionych roztworem dietylenotriaminy składającym się z wody w ilości 10% wagowo i dietylenotriaminy w ilości 90% wagowo i połączonych żywicą epoksydową. Do zewnętrznych powierzchni skrajnych warstw samonaprawiających się (4a) i (4b) przylega adhezyjnie warstwa żywicy polimerowej (3) o grubości od 10 µm do 30 µm, która nałożona jest na warstwę ceramiczną (2) o grubości od 8 µm do 15 µm znajdującą się na arkuszu blachy (1) ze stopu aluminium o grubości od 0,3 mm do 0,5 mm, który na zewnętrznej powierzchni posiada warstwę ceramiczną (2) o grubości od 8 µm do 15 µm z nałożoną warstwą żywicy polimerowej (3) o grubości od 10 µm do 30 µm. Zgłoszenie obejmuje też sposób wytwarzania laminatu aluminium-szkło, który polega na tym, że na dwa arkusze blachy (1) ze stopu aluminium o grubości od 0,3 mm do 0,5 mm posiadające na obu powierzchniach warstwę ceramiczną (2) o grubości od 8 µm do 15 µm nakłada się obustronnie warstwę żywicy polimerowej (3) o grubości od 10 µm do 30 µm, po czym pozostawia się na czas 3 h w temperaturze 23°C.The subject of the application is an aluminum-glass laminate, characterized in that in the central part of the laminate there are two identical self-healing layers (4a) with a thickness of 1.5 mm to 2.3 mm each, consisting of glass fibers filled with isophorone diisocyanate and bonded with epoxy resin, which are laid alternately with two identical self-healing layers (4b) each 1.5 mm to 2.3 mm thick, consisting of glass fibers filled with a diethylenetriamine solution consisting of water in an amount of 10% by weight and diethylenetriamine in an amount of 90% by weight and bonded with an epoxy resin. A layer of polymer resin (3) with a thickness of 10 µm to 30 µm adheres adhesively to the outer surfaces of the extreme self-healing layers (4a) and (4b), which is applied to a ceramic layer (2) with a thickness of 8 µm to 15 µm located on on a sheet of aluminum alloy (1) with a thickness of 0.3 mm to 0.5 mm, which on the outer surface has a ceramic layer (2) with a thickness of 8 µm to 15 µm with a layer of polymer resin (3) with a thickness of from 10 µm to 30 µm. The application also covers a method of producing an aluminum-glass laminate, which consists in the fact that two metal sheets (1) made of aluminum alloy with a thickness of 0.3 mm to 0.5 mm, having a ceramic layer (2) on both surfaces with a thickness of 8 μm to 15 μm, a layer of polymer resin (3) with a thickness of 10 μm to 30 μm is applied on both sides, and then left for 3 h at 23°C.

PL441554A 2022-06-27 2022-06-27 Aluminum-glass laminate and method of its production PL243792B1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PL441554A PL243792B1 (en) 2022-06-27 2022-06-27 Aluminum-glass laminate and method of its production

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PL441554A PL243792B1 (en) 2022-06-27 2022-06-27 Aluminum-glass laminate and method of its production

Publications (2)

Publication Number Publication Date
PL441554A1 true PL441554A1 (en) 2022-11-21
PL243792B1 PL243792B1 (en) 2023-10-09

Family

ID=84191835

Family Applications (1)

Application Number Title Priority Date Filing Date
PL441554A PL243792B1 (en) 2022-06-27 2022-06-27 Aluminum-glass laminate and method of its production

Country Status (1)

Country Link
PL (1) PL243792B1 (en)

Also Published As

Publication number Publication date
PL243792B1 (en) 2023-10-09

Similar Documents

Publication Publication Date Title
PL441557A1 (en) Magnesium-glass laminate and method of its production
KR101445213B1 (en) Magnesium alloy honeycomb board and preparation method thereof
TWI433779B (en) Flexible substrate for display panel and manufacturing method of the same
PL437402A1 (en) Titanium-glass-carbon laminate and its producing method
PL437396A1 (en) Magnesium-glass laminate and its producing method
CN101224651A (en) Sheet metal and non-metal fiber film compound material
PL441554A1 (en) Aluminum-glass laminate and method of its production
PL441553A1 (en) Aluminum-glass laminate and method of its production
PL441561A1 (en) Titanium-glass laminate and method of its production
PL441558A1 (en) Magnesium-glass laminate and method of its production
CN109605859A (en) A kind of honeycomb core, cellular board and honeycomb core production method
PL441552A1 (en) Aluminum-glass laminate and method of its production
PL441559A1 (en) Titanium-glass laminate and method of its production
PL441560A1 (en) Titanium-glass laminate and method of its production
PL441555A1 (en) Magnesium-glass laminate and method of its production
DE102004031930B4 (en) Heat exchanger material, method of manufacturing a heat exchanger and heat exchanger
PL437394A1 (en) Titanium-glass laminate and its producing method
PL432777A1 (en) Method of producing magnesium-carbon laminate
PL432773A1 (en) Method of producing magnesium-carbon laminate
PL432772A1 (en) Method of producing magnesium-carbon laminate
CN219338870U (en) High-strength composite aluminum foil structure
TW202128426A (en) Multi-layer structure body
PL437392A1 (en) Magnesium-carbon laminate and its producing method
PL437399A1 (en) Aluminum-glass-carbon laminate and its producing method
PL437398A1 (en) Aluminum-carbon laminate and its producing method