PL3899066T3 - Hartowana w prasie część o wysokiej odporności na opóźnione pękanie oraz sposób jej wytwarzania - Google Patents

Hartowana w prasie część o wysokiej odporności na opóźnione pękanie oraz sposób jej wytwarzania

Info

Publication number
PL3899066T3
PL3899066T3 PL18842729.8T PL18842729T PL3899066T3 PL 3899066 T3 PL3899066 T3 PL 3899066T3 PL 18842729 T PL18842729 T PL 18842729T PL 3899066 T3 PL3899066 T3 PL 3899066T3
Authority
PL
Poland
Prior art keywords
manufacturing process
high resistance
delayed fracture
hardened part
press hardened
Prior art date
Application number
PL18842729.8T
Other languages
English (en)
Inventor
Blandine REMY
Thierry STUREL
Emmanuel Lucas
Gianni BOI
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of PL3899066T3 publication Critical patent/PL3899066T3/pl

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/62—Quenching devices
    • C21D1/673—Quenching devices for die quenching
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D—WORKING OR PROCESSING OF SHEET METAL OR METAL TUBES, RODS OR PROFILES WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D22/00—Shaping without cutting, by stamping, spinning, or deep-drawing
    • B21D22/02—Stamping using rigid devices or tools
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/012—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of aluminium or an aluminium alloy
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/004—Heat treatment of ferrous alloys containing Cr and Ni
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/008—Heat treatment of ferrous alloys containing Si
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/004—Very low carbon steels, i.e. having a carbon content of less than 0,01%
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/50—Ferrous alloys, e.g. steel alloys containing chromium with nickel with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/54—Ferrous alloys, e.g. steel alloys containing chromium with nickel with boron
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/12—Aluminium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/50—Controlling or regulating the coating processes
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/004—Dispersions; Precipitations
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0278—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Heat Treatment Of Articles (AREA)
  • Heat Treatment Of Steel (AREA)
  • Other Surface Treatments For Metallic Materials (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Mounting, Exchange, And Manufacturing Of Dies (AREA)
  • Laminated Bodies (AREA)
  • Body Structure For Vehicles (AREA)
  • Pens And Brushes (AREA)
  • Materials For Medical Uses (AREA)
  • Application Of Or Painting With Fluid Materials (AREA)
  • Physical Vapour Deposition (AREA)
  • Treatment Of Steel In Its Molten State (AREA)
  • Solid-Phase Diffusion Into Metallic Material Surfaces (AREA)
PL18842729.8T 2018-12-18 2018-12-18 Hartowana w prasie część o wysokiej odporności na opóźnione pękanie oraz sposób jej wytwarzania PL3899066T3 (pl)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/IB2018/060219 WO2020128571A1 (en) 2018-12-18 2018-12-18 A press hardened part with high resistance to delayed fracture and a manufacturing process thereof

Publications (1)

Publication Number Publication Date
PL3899066T3 true PL3899066T3 (pl) 2024-02-12

Family

ID=65276223

Family Applications (1)

Application Number Title Priority Date Filing Date
PL18842729.8T PL3899066T3 (pl) 2018-12-18 2018-12-18 Hartowana w prasie część o wysokiej odporności na opóźnione pękanie oraz sposób jej wytwarzania

Country Status (16)

Country Link
US (1) US11725255B2 (pl)
EP (1) EP3899066B1 (pl)
JP (1) JP7137015B2 (pl)
KR (1) KR102538733B1 (pl)
CN (1) CN112955572B (pl)
BR (1) BR112021006244B1 (pl)
CA (1) CA3114861C (pl)
ES (1) ES2967098T3 (pl)
FI (1) FI3899066T3 (pl)
HU (1) HUE063767T2 (pl)
MA (1) MA54486B1 (pl)
MX (1) MX2021007216A (pl)
PL (1) PL3899066T3 (pl)
UA (1) UA127773C2 (pl)
WO (1) WO2020128571A1 (pl)
ZA (1) ZA202102204B (pl)

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN112981260B (zh) * 2021-02-08 2021-11-30 上海振华港机重工有限公司 一种集装箱起重机车轮钢、车轮及其制备方法
CN115305412B (zh) * 2021-05-05 2024-02-06 通用汽车环球科技运作有限责任公司 具有优异耐腐蚀性和超高强度的组合的压制硬化钢
WO2023176100A1 (ja) * 2022-03-14 2023-09-21 Ｊｆｅスチール株式会社 熱間プレス部材および熱間プレス用鋼板、ならびにそれらの製造方法

Family Cites Families (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5114691B1 (pl) * 1969-08-14 1976-05-11
JPS59166653A (ja) 1983-03-08 1984-09-20 Hitachi Metals Ltd 圧力リング材
JPH08120339A (ja) 1994-10-25 1996-05-14 Nippon Steel Corp 急速焼戻しによる高張力鋼板の製造方法
FR2780984B1 (fr) 1998-07-09 2001-06-22 Lorraine Laminage Tole d'acier laminee a chaud et a froid revetue et comportant une tres haute resistance apres traitement thermique
JP3845271B2 (ja) 2001-06-15 2006-11-15 新日本製鐵株式会社 高温成形に適し高温成形後に高強度となるアルミもしくはアルミ−亜鉛めっき鋼板およびその製造方法
JP4725415B2 (ja) 2006-05-23 2011-07-13 住友金属工業株式会社 熱間プレス用鋼板および熱間プレス鋼板部材ならびにそれらの製造方法
CN101583486B (zh) 2006-10-30 2014-08-27 安赛乐米塔尔法国公司 涂覆的钢带材、其制备方法、其使用方法、由其制备的冲压坯料、由其制备的冲压产品和含有这样的冲压产品的制品
CA2729942C (en) 2008-07-11 2013-08-06 Nippon Steel Corporation Aluminum plated steel sheet for rapid heating hot-stamping, production method of the same and rapid heating hot-stamping method by using this steel sheet
WO2011142356A1 (ja) * 2010-05-10 2011-11-17 新日本製鐵株式会社 高強度鋼板及びその製造方法
US20130095347A1 (en) 2010-06-14 2013-04-18 Kaoru Kawasaki Hot-stamped steel, method of producing of steel sheet for hot stamping, and method of producing hot-stamped steel
JP5652321B2 (ja) 2011-05-13 2015-01-14 新日鐵住金株式会社 熱間複合成形性及び打抜き部の耐遅れ破壊特性に優れたホットスタンプ用鋼板とその製造方法
JP6001883B2 (ja) 2012-03-09 2016-10-05 株式会社神戸製鋼所 プレス成形品の製造方法およびプレス成形品
JP6001884B2 (ja) 2012-03-09 2016-10-05 株式会社神戸製鋼所 プレス成形品の製造方法およびプレス成形品
WO2014037627A1 (fr) 2012-09-06 2014-03-13 Arcelormittal Investigación Y Desarrollo Sl Procede de fabrication de pieces d'acier revêtues et durcies a la presse, et tôles prerevêtues permettant la fabrication de ces pieces
FI124825B (fi) * 2013-02-22 2015-02-13 Rautaruukki Oyj Menetelmä metallipinnoitetun ja kuumamuokatun teräskomponentin valmistamiseksi ja metallipinnoitettu teräsnauhatuote
US20160289809A1 (en) * 2013-09-19 2016-10-06 Tata Steel Ijmuiden B.V. Steel for hot forming
WO2015088523A1 (en) 2013-12-11 2015-06-18 ArcelorMittal Investigación y Desarrollo, S.L. Cold rolled and annealed steel sheet
KR101568549B1 (ko) 2013-12-25 2015-11-11 주식회사 포스코 우수한 굽힘성 및 초고강도를 갖는 열간 프레스 성형품용 강판, 이를 이용한 열간 프레스 성형품 및 이들의 제조방법
WO2016016676A1 (fr) * 2014-07-30 2016-02-04 ArcelorMittal Investigación y Desarrollo, S.L. Procédé de fabrication de tôles d'acier, pour durcissement sous presse, et pièces obtenues par ce procédé
CN105441823B (zh) 2014-09-26 2017-12-05 鞍钢股份有限公司 一种超高强度热浸镀铝钢板及其制造方法
WO2017006144A1 (en) 2015-07-09 2017-01-12 Arcelormittal Steel for press hardening and press hardened part manufactured from such steel
CN106702286A (zh) 2015-08-23 2017-05-24 孙仁 一种中碳低合金马氏体钢及其冶炼方法
KR101696121B1 (ko) 2015-12-23 2017-01-13 주식회사 포스코 내수소지연파괴특성, 내박리성 및 용접성이 우수한 열간성형용 알루미늄-철 합금 도금강판 및 이를 이용한 열간성형 부재
MX2019001828A (es) * 2016-08-30 2019-06-06 Jfe Steel Corp Lamina de acero y metodo para la fabricacion de la misma.
WO2018220412A1 (fr) 2017-06-01 2018-12-06 Arcelormittal Procede de fabrication de pieces d'acier a haute resistance mecanique et ductilite amelioree, et pieces obtenues par ce procede

Also Published As

Publication number Publication date
WO2020128571A1 (en) 2020-06-25
ES2967098T3 (es) 2024-04-26
EP3899066B1 (en) 2023-10-04
BR112021006244B1 (pt) 2023-04-04
EP3899066A1 (en) 2021-10-27
KR102538733B1 (ko) 2023-05-31
CA3114861C (en) 2023-06-27
JP7137015B2 (ja) 2022-09-13
US11725255B2 (en) 2023-08-15
MA54486A (fr) 2022-03-30
HUE063767T2 (hu) 2024-01-28
ZA202102204B (en) 2022-02-23
US20220025480A1 (en) 2022-01-27
MA54486B1 (fr) 2023-11-30
BR112021006244A2 (pt) 2021-07-06
FI3899066T3 (fi) 2023-12-04
CN112955572A (zh) 2021-06-11
UA127773C2 (uk) 2023-12-27
CA3114861A1 (en) 2020-06-25
CN112955572B (zh) 2023-02-17
MX2021007216A (es) 2021-07-15
JP2022513667A (ja) 2022-02-09
KR20210072069A (ko) 2021-06-16

Similar Documents

Publication Publication Date Title
ZA202102204B (en) A press hardened part with high resistance to delayed fracture and a manufacturing process thereof
PL3396533T3 (pl) Programowalny sprzęt do obliczeń gruboziarnistych i na macierzach rzadkich z zaawansowanym szeregowaniem
GB202005188D0 (en) A press hardening method
EP3278897A4 (en) Press molding method, method for manufacturing component in which said press molding method is used, and component manufactured using said press molding method
ZA201906130B (en) Pyrrolidinones and a process to prepare them
EP3718669A4 (en) DESIGN PROCESS OF A MOLDED LAMINATE ARTICLE, PRODUCTION PROCESS, PRODUCTION DEVICE AND PROGRAM
EP3412640A4 (en) HIGH STRENGTH AND LARGE CERAMIC PLATE WITH LOW SCRINCTION AND METHOD OF MANUFACTURING THEREOF
EP3080322A4 (en) Martensitic steel with delayed fracture resistance and manufacturing method
SG10202102922UA (en) Manufacturing line, process, and sintered article
PL3283551T3 (pl) Kompozycja aktywowanej ligniny, sposób jej wytwarzania oraz jej zastosowanie
SG11202004253QA (en) Oil-and-fat composition and manufacturing method thereof
EP3100797A4 (en) Press molding method, manufacturing method for press-molded component, and method for determining preform shape for use in said methods
ZA202004149B (en) A manufacturing process of press hardened parts with high productivity
PL3156506T3 (pl) Sposób częściowego ogrzewania promieniowaniem do wytwarzania części hartowanych w procesie tłoczenia i układ do takiego wytwarzania
EP3260215A4 (en) Press forming method and press forming mold
EP3636362A4 (en) METHOD OF MANUFACTURING A COMPRESSED BODY AND PRESS LINE
GB201712006D0 (en) An agriculture composition, a method manufacturing thereof, and a method using thereof
SG11202106988YA (en) Pseudo-boehmite, manufacturing process and application thereof
ZA201905675B (en) Organic slow-acting fertilizer using plantaginis semen husk and manufacturing method therefor
EP3284610A4 (en) Gravure cylinder and manufacturing method thereof
EP3296266A4 (en) Fibrous basic magnesium sulfate, manufacturing method therefor and resin composition thereof
EP3378958A4 (en) PLATED STEEL SHEET AND METHOD OF MANUFACTURING THE SAME
EP3085678A4 (en) Piezoelectric ceramic, manufacturing method therefor, and electronic component
IL256215B (en) Composite ceramic material and method of making it
EP2985091A4 (en) Press molding apparatus and method of production therefor