OA18096A - Hybrid adsorber heat exchanging device and method of manufacture - Google Patents
Hybrid adsorber heat exchanging device and method of manufacture Download PDFInfo
- Publication number
- OA18096A OA18096A OA1201600281 OA18096A OA 18096 A OA18096 A OA 18096A OA 1201600281 OA1201600281 OA 1201600281 OA 18096 A OA18096 A OA 18096A
- Authority
- OA
- OAPI
- Prior art keywords
- adsorbent
- silica gel
- coated
- activated carbon
- bed
- Prior art date
Abstract
The present invention provides a hybrid adsorption heat exchanging device comprising:at least one tubular or micro channel structure for carrying a heat transfer fluid; the external surface of said structure being provided with extensions in at least two locations; said extensions forming a bed there between for providing one or more adsorbent materials; a coating of adsorbent material being provided on at least a part of said extensions.
Description
HYBRID ADSORBER HEAT EXCHANGING DEVICE AND METHOD OF MANUFACTURE FIELD OF THE INVENTION
The présent invention relates to hybrid adsorber heat exchanging devices, such as heat exchanger Systems. The Systems of the invention are useful in environments where adsorbate is required to be temporarily or periodically stored and released. In particuiar, the présent invention relates to adsorbent based heat exchanger Systems for adsorption cooling, heat pump and desalination applications. The présent invention also provides a method for the manufacture of such hybrid adsorber heat exchanging devices, and 10 applications of such heat exchanging device.
BACKGROUND OF THE INVENTION
The concerns of environmental pollution and primary energy consumption issues call for the rapid development of environmentally benign energy conservative technologies. Among them, thermally powered adsorption Systems are considered as one the key 15 technologies as these Systems can recover and reuse low-temperature waste heat sources which otherwise will be purged to the ambient.
There is a recognized need to replace existing mechanically or electrically driven vapour compression based Systems used for chilling or réfrigération purposes. Such Systems typically use gases such as hydrofluoro carbons. It is now recognised that there is 20 a need to replace the use of such materials in view of the deleterious effect they hâve on the environment.
One of the mechanisms used to replace conventional vapour compression based Systems is to use heat exchangers which utilise adsorbent beds in order to ensure mass transfer as well as heat transfer.
Adsorbent materials are classified according to their properties into physical adsorbents, chemical adsorbents, and composite adsorbents. Physical adsorbents are materials that hâve differing pore sizes. Typical of this category are mesoporous silicates, zeolites, metaluminophosphates, porous carbons and métal organic frameworks. Mesoporous silicates include materials such as synthetic amorphous silica gel which consists of a rigid and continuous net of colloïdal silica connected to small grains of hydrated SiO4. Porous carbons include activated carbons obtained by.gasifying char with an oxidising agent. Zeolites include crystalline microporous alumina silicate materials and include several ranges such as HZSM-5, ZSM5, zeolite HY etc. The advantages of zeolite or zeolite based materials are their diversity of uses, and their susceptibility to modification 35 dépendent on the purpose of use. Métal organic frameworks are a new génération of materials which are microporous, hâve high porosity, uniform pore size and hâve well defined adsorption sites and large surface area. These frameworks typically comprise of organic linkers which connect métal centres.
Chemical adsorbents comprise substances used in chemisorption. These include métal chlorides such as calcium chloride, barium chloride, strontium chloride etc., sait and métal hydrides such as lithium hydride, calcium hydride, high polymerised hydrides of covalent nature, and non-metal molecular hydrides, and métal oxides.
Composite adsorbents include combinations of chemical and physical adsorbents such as combinations of métal chloride and activated carbon fibres, expanded graphite, silica gel, or zeolite. Composite adsorbents provide an advantage in enhancement of performance of physical adsorbents without incurring the effect of chemical adsorbents such as swelling, poor conductivity, or agglomération.
PRIOR ART
Several different heat exchange mechanisms hâve been postulated in the art as replacement for conventional vapour compression based réfrigération Systems. Some of these are discussed below for the purpose of reference.
A two-bed adsorbent based cooling system comprises of separated heat exchangers. Essentially, this mechanism comprises of four main parts, two reactors which function as adsorber or desorber depending on the operating mode, an evaporator and a condenser. The reactors are packed with adsorbent material to adsorb or desorb the adsorbate during the adsorption or desorption processes. The flow of the medium is regulated using réfrigérant valves.
One alternative to the two bed adsorption cooling system is a system that uses an integrated adsorption mechanism. This usually comprises two units, wherein each unit is provided with an adsorbent bed, an evaporator and a condenser. The heat exchange cycle in this device comprises of two modes - évaporation triggered adsorption which is known as adsorption/evaporation mode and desorption resulted condensation which is known as desorption/condensation mode. Control valves are provided to control the flow of secondary fluid to each unit.
Another alternative mechanism involves a three bed adsorption system. This consists of three reactors in addition to the condenser and the evaporator. A three bed heat exchange system enables continuous évaporation. This mechanism has four operational modes - preheating, desorption, pre-cooling and adsorption.
Multistage Systems are also available which are used to utilise low température heat sources. These Systems operate at températures that are not suitable for a two bed adsorption cooling system.
As discussed above, an adsorption cooling system can effectively utilize low-grade waste heat or solar thermal energy of température typically below 100°C and can produce effective cooling energy. Thermally driven adsorption cooling cycle does not require any electricity to drive the cycle and it is environmentally friendly as it utilizes naturel réfrigérants or alternatives to HFC based réfrigérants. Moreover, this System requires a lesser level of maintenance and is also free from moving parts. However, the main drawbacks of the low-temperature thermally powered adsorption cooling System are its poor performance in terms of spécifie cooling capacity and coefficient of performance and relatively largerfootprint as opposed to conventional vapour compression cycle.
Adsorption heat exchangers typically comprise a heat exchanger structure which is used for supplying and discharging thermal energy and which is in a thermal contact with a sorbent material which uses a phase change of an adsorbate working medium for binding and releasing latent heat. Heat is released through the condensation of a vaporous working medium. Conversely, the thermal energy supplied via the heat exchanger structure can be used for the renewed vaporization of the adsorbate.
Solids materials are mostly used for performing the phase change of the adsorbate, which are so-called sorbent or adsorbent materials. A characteristic for such sorbent materials are their open-pore structure with a high ratio of surface to volume. The inner cavities in these materials hâve molecular magnitude dimensions. The effect of the sorbent materials is based on adsorbing foreign atoms and foreign molécules in their micro-porous structure and thus to transfer from the gas phase to a bonded state. Examples for sorbent materials used in adsorption heat exchangers are clays such as bentonite, silica gel or zeolites. Water is usually used as the working medium for these sorbent materials since it has a high heat of condensation and is also easy to use.
Adsorption based heat exchange Systems are driven by the adsorption and desorption of an adsorbate vapour by a porous solid adsorbent. In contrast to conventional vapour-compression cooling Systems which are driven by a mechanical compressor, no electrical energy is needed to drive the adsorption cycle. The basic cycle involves an adsorption phase and a desorption phase. In the adsorption phase, the réfrigérant vapour is adsorbed by the adsorbent substance resulting in the release of heat. In the desorption phase, heat is applied to the adsorbent causing desorption of the réfrigérant. The heat transferred during these processes is conveyed by a heat exchanger between the adsorbent and a heat transfer fluid (e.g. water or methanol or a water-glycol mixture) or an external environment. The adsorption and desorption processes occur in conjunction with évaporation and condensation of réfrigérant in an evaporator/condenser. The adsorption of the gaseous réfrigérant lowers the vapour pressure, promoting évaporation of the liquid réfrigérant in the evaporator. During this évaporation, heat is extracted from an environment to be cooled, resulting in réfrigération. By supplying heat to the adsorbent via the heat exchanger, the adsorbed réfrigérant is released into the vapour phase, thus regenerating the adsorbent material for the next adsorption cycle. The resulting gaseous adsorbate passes to a condenser where heat rejection to the environment takes place. As in conventional vapour-compression cooling, the liquid réfrigérant is passed through a control device (e.g. an expansion valve) back into the evaporator, and the cycle can then be repeated.
When an adsorption heat exchanger is supplied with thermal energy from the outside, e.g. by having a heat carrier liquid flow through the same, the heat flowing in from the outside needs to be transferred effectively to the porous sorbent material in orderto release the adsorbed working medium situated in the same. In the opposite case, the release of thermal energy, which means an energy flow direction out of the adsorption heat exchanger, the thermal energy released as a resuit of the condensation of the working medium on the porous sorbent material needs to be transported from the adsorption heat exchanger to the outside. Since known porous sorbent materials show adverse thermal conductivity, adsorption heat exchangers are usually produced as a combination of a heat exchanger structure with high thermal conductivity and the porous sorbent material that is used for binding and releasing the working medium. The heat exchanger structures mostly consist of metallic materials such as copper, aluminum or stainless steel, as well as other materials with a high thermal conductivity such as ceramic materials, carbon materials, carbon fiber reinforced plastic (CFRP) materials and certain plastic materials.
Heat exchangers comprise cavities for allowing direct flow with a heat carrier medium which usually does not corne into direct contact with the sorbent material. The heat exchanger structure cornes into thermal contact with the sorbent material. In the simplest of cases this occurs in the form of bulk material, with the sorbent material being mostly présent in the form of powder or by mixture with a binder in the form of pellets.
Thermally powered adsorption chillers hâve been proposed for space cooling applications. These chillers are virtually free of moving parts, except for the On/Off operation of the réfrigérant valves that separately connect the adsorbent beds to the evaporator and condenser. Therefore these Systems are highly reliable and require almost no maintenance. Adsorption chillers are also capable of being miniaturized, since adsorption of réfrigérant into and desorption of réfrigérant from the solid porous adsorbent are primarily surface, rather than bulk processes.
As seen above several methods are postulated in the art for heat exchange mechanisms. Some of the référencés are briefly discussed below.
US Patent 8,053,032 explains a method for production of a heat exchanger substrate wherein a zeolite layer is deposited/produced on the substrate surface by direct crystallization. However, there is no référencé or teaching in this patent towards any hybridization techniques.
US Patent 8,590,153 discloses an adsorption heat exchanger where an adhesive layer/coating is formed on the heat exchanger structure and the exchanger is then dipped into sorbent material to ensure adhesion thereof. The method of coating essentially comprises use of a finished manufactured heat exchanger which is thereafter coated with the sorbent material, by a process of dipping. As will be appreciated, this method may hâve the limitations of unevenness of coating thickness, agglomération of porous solid material in certain portions leading to uneven coating and thereby in itself adversely impacting performance.
US Patent Publication 2010/0136326 discloses a method by which a layer composite comprising of a métal support substrate and a silicate layer is obtained by coating the substrate surface with the silicate layer obtained through solvothermal synthesis. There is no disclosure in this publication of any attempts to hybridise heat exchange mechanisms, or attempt to improve kinetic performance of the heat exchanger without compromising on adsorbent volume or heat exchanger footprint.
US Patent Publication 2011/0183836 unveils an aluminium containing substrate for a heat exchanger. A microporous layer of aluminium phosphate zeolite is applied to the substrate, inter alia other layers. The publication again focuses on increasing the number of layers forming the coating on the substrate, wherein at least one layer is ALPO4, and does not provide any information or guidance towards attempts to increase kinetic performance of heat exchangers through hybridization techniques.
US Patent Publication 2012/0216563 discloses a heat exchanger wherein a porous material is provided in contact with the tubular portion of the exchanger in order to allow vapour to pass through. The material is a fibrous material. However, there is again no disclosure or guidance on whether this is useful for improving performance kinetics or whether additional hybridization techniques can be used.
US Patent Publication 2013/0014538 discloses a sub-assembly for an adsorption chilien The sub-assembly is provided with an adsorption component including a multiplicity of plates which are arranged in a stack. The réfrigérant sides of adjacent pairs of the plates in the stack define réfrigérant passages and an adsorbent material is provided within these passages. However, there is no disclosure or guidance therein on whether this arrangement contributes-xir provides any improvement in performance kinetics.
JP Patent Publication'Nô. 2011-240256 discloses an adsorbent block which is provided with a plurality of activated carbon fibers. These fibers are ail directed in the same direction. A cylindrical métal sheet is provided covering the outer circumference of the activated fibers, in a manner such that the axial direction. This is obtained by covering the fibers with the cylindrical métal sheet and then unidirectionally rolling out and cutting the sheet. However, there is no disclosure or guidance therein on whether this arrangement contributes or provides any improvement in performance kinetics.
JP Patent Publication No. 2005-291528 discloses a heat exchanger with enhanced adsorber capacity. The heat exchanger comprises a plate fin tube type heat exchanger with a spécifie fin pitch, fin length and fin height. Activated charcoal is used as a filler adsorbent wherein the charcoal has spécifie steam adsorbing capacity. the bed so formed is covered by a net like material to prevent leakage of the adsorbent material. However, there is no disclosure or guidance therein on whether this arrangement contributes or provides any improvement in performance kinetics. Again, the focus in this disclosure is on modifying the fin dimensions and adjusting the adsorbent material characteristics to ehhance adsorbent power.
SUMMARY OF THE INVENTION
The présent invention provides a hybrid adsorption heat exchanging device comprising at least one tubular or micro-channel structure for carrying a heat transfer fluid, the external surface of said structure being provided with extensions in at least two locations, said extensions forming a bed there between for providing one or more adsorbent materials, a coating of adsorbent material being provided on at least a part of said extensions.
In one embodiment, the extensions run longitudinally along the full length of the tubular structure or can run circumferentially around the tubular structure, with the height of each extension remaining substantially uniform along the entire length thereof.
If another embodiment, the tubular structure and the extensions are intégral, or can be connected to each otherthrough separate connecting means.
If desired, the tubular structure and the extensions are made of the same material and can be made from a heat conductive material which is metallic, ceramic based, polymeric or carbon based materials.
In another embodiment of the invention, each extension is coated with an adsorbent being the same or different from the adsorbent filling in the bed.
In yet another embodiment, the adsorbent material provided in said bed is selected from the group consisting of zeolites, mesoporous silicates, insoluble métal silicates, siiica gel type A, siiica gel type RD, siiica gel type S2, activated carbon fiber, granular activated carbon, activated alumina, highly porous activated carbon, Zr6O4(OH)4 bonded with linkers, MlL-101Cr, MOFs (metal-organic frameworks), COFs (covalent organic frameworks), FAMs (functional adsorbent materials), and the like, singularly or in any combination thereof.
In yet another embodiment of the invention, the adsorbent material comprises adsorbent granules having a pore diameter in the range of 3 to 100 angstromto or plain or corrugated sheets with adsorbent coated or deposited thereon or a combination thereof disposed in any predetermined pattern.
In yet another embodiment of the invention, the plain or corrugated sheets are made of a thermally conductive material selected from the group consisting of aluminium, copper, graphite/expanded graphite, inorganic or organic fiber substrates or combinations thereof, and can optionally be perforated sheets.
In another embodiment of the invention extensions are corrugated on the extemal surface thereof priorto coating with adsorbent material, and wherein the coating is selected from the group consisting of zeolites, mesoporous silicates, insoluble métal silicates, silica gel type A, silica gel type RD, silica gel type S2, activated carbon fiber, granular activated carbon, activated alumina, highly porous activated carbon, Zr6O4(OH)4 bonded with linkers, MIL-101Cr, MOFs (metal-organic frameworks), COFs (covalent organic frameworks), FAMs (functional adsorbent materials), and the like, singularly or in any combination thereof.
In yet another embodiment of the invention, the heat transfer fluid is selected from the group consisting of water, lower alcohols, oils, and the like.
In another embodiment of the invention, the adsorbent material is provided with one or more dopants selected from the group consisting of inorganic metals salts such as calcium chloride, lithium bromide, magnésium chloride, magnésium sulphate, calcium nitrate, manganèse chloride, and the like
In another embodiment of the invention, one or more additives selected from the group consisting of carbon fibers, graphite fibers, and the like are also added to enhance thermal conductivity.
If desired, a polymeric mesh is provided over the adsorbent bed, wherein the polymer is aniline.
The invention also provides a method for the manufacture of a hybrid adsorption heat exchanging device, said method comprising:
- coating at least a part of a thermally conductive material with an adsorbent material;
- converting the at least partially coated thermally conductive material into a tubular structure for carrying a heat transfer fluid, and providing two or more extensions thereon, said extensions being either intégral with said coated tubular structure, or comprising at least partly adsorbent coated thermally conductive material, said extensions forming an adsorbent bed therebetween;
- providing one or more adsorbent material in said adsorbent bed.
BRIEF DESCRIPTION OF THE ACCOMPANYING DRAWINGS
The invention will be described in greater detail below inter alia, with reference to the accompanying drawings wherein:
Figure 1 is a représentation of a typical finned type block adsorber that is used in the adsorber and desorber heat exchangers.
Figure 1(a) is an exploded view of the section marked ‘A’ in Figure 1, and figure 1(b) is an isométrie view of the same.
Figure 2 is a représentation of a typical spiral-finned type tube adsorber that is used in heat exchangers.
Figure 2(a) is an exploded view of the section marked A’ in Figure 2, and figure 2(b) is an isométrie view of the same.
Figure 3(a) is a représentation of prior art finned block adsorbers wherein the adsorber bed is filled/packed with granular adsorbents.
Figure 3(b) is a représentation of prior art coated finned block adsorbers.
Figure 4(a) is a représentation of an adsorbent bed wherein the fins of the adsorber heat exchange tube are coated with a first adsorbent material and the interstitial spaces between the fins are filled with a second adsorbent material comprising granules, and covered with a suitable mesh.
Figure 4(b) is a représentation of an adsorbent bed wherein the fins of the adsorber heat exchange tube are coated with a first adsorbent material and the interstitial spaces between the fins are filled with a second adsorbent material comprising desiccant coated substrate.
Figure 4(c) is a représentation of an adsorbent bed wherein the fins of the adsorber heat exchange tube are coated with a first adsorbent material and the interstitial spaces between the fins are filled with a second adsorbent material comprising corrugated desiccant coated substrate block.
Figure 4(d) and Figure 4(e) are représentations of an adsorbent bed wherein the fins of the adsorber heat exchange tube are coated with a first adsorbent material and the interstitial spaces between the fins are filled with a second adsorbent material comprising either a corrugated or a plain desiccant coated substrate block and adsorbent granules interspersed in between the desiccant coated substrate block.
Figure 4(f) is a représentation of an adsorbent bed wherein the fins of the adsorber heat exchange tube are shaped to enhance their surface area and are coated with a first adsorbent material and the interstitial spaces between the fins are filled with a second adsorbent material comprising adsorbent granules, and covered with a suitable mesh.
Figure 5 is a représentation of the four heat transfer résistances developing the température gradient, during the heat transfer from/to the secondary fluid.
Figure 6 is a représentation of a substrate material that is coated with adsorbent, and perforations are provided thereon in predetermined or desired patterns.
Figure 7 shows the adsorption isotherm of silica gel S2 proprietary to applicants herein on water and a coated silica gel S2/water adsorbent/refrigerant pairs.
Figure 8 shows the adsorption uptake data for silica gel S2/water pair at températures in the range of 30-70°C.
Figure 9 shows the adsorption uptake data for siica gel S2/water pair at pressures in the range of 5kPa and 15kPa.
Figure 10 is a comparative représentation of adsorption isotherms of water on silica gel S2 type proprietary to applicants and commercially available Fuji RD type silica gel.
Figure 11 (a), (b) and (c) are temporal profiles of adsorption uptake and pressure of silica gel S2/water pair at adsorption températures of 30°, 50° and 70°C respectively.
Figure 12 is a comparative représentation of the spécifie capacity, in terms of cooling Watts per liter of adsorbent heat exchanger, both for prior art adsorbers and the potential spécifie capacity with different hybrid adsorption heat exchangers of the présent invention.
Figure 13 shows the cooling capacity and the COP of the adsorption chiller using conventional packing method, the advanced adsorbent-coated method and the adsorbentcoated hybrid heat exchangers.
Figure 14 shows the température profiles of the major components of the adsorption chiller for the overall heat transfer coefficient of 350 W/m2K.
Figure 15 shows the performance comparisons of adsorption chiller for pellet, adsorbent-coated and hybrid heat exchangers.
DETAILED DESCRIPTION OF THE INVENTION
A recognised need in the art has been the requirement to enhance the performance of the adsorbent bed that is used in heat exchangers in order to improve the cycle overall performance. Amongst other factors the key parameters that détermine the efficiency of the performance of an adsorbent bed are heat and mass transfer aspects. Mass transfer influences both adsorption capacity and adsorption uptake rate. Heat transfer is critical for delivery and extraction of both desorption and adsorption heat, respectively. Other parameters that also affect adsorbent bed performance include adsorbent porosity and pore size, granular size and adsorbent to métal mass ratio.
Heat transfer is subject to multiple levels of résistance within the adsorbent bed. These include the'résistance induced by métal to secondary fluid convective heat transfer, conductive heat transfer résistance through the wall of the exchanger, métal to adsorbent contact heat transfer, and conductive heat transfer résistance through adsorbent material. Of these, the heat transfer résistance engendered by métal to adsorbent contact interface plays a prédominant rôle in affecting the efficiency of a heat exchanger, and is dépendent on the nature and level of physical contact between the adsorbent and the heat exchanger métal. For example, in simple granular packed adsorbent bed Systems, even though the mass transfer performance is very high, the level of heat transfer performance is generally low due to high contact thermal résistance between the adsorbent granules and the heat exchanger métal surface.
It is possible to enhance heat transfer performance of adsorbent material that is used in an adsorbent bed, by mixing adsorbent granules with métal additives to increase thermal conductivity, coating of bed heat exchanger métal with the adsorbent and avoiding the use of granules totally in order to eliminate ail contact thermal résistance, covering the adsorbent granules with a polyaniline net, adsorbent déposition over metallic foam, and use of consolidated bed methods.
One of the techniques to enhance heat transfer performance by increasing overall thermal conductivity is by adding métal particles such as aluminium, copper, or graphite/expanded graphite to adsorbent granules of zeolitic materials. While it is reported that the thermal conductivity increases significantly, and the method is also easy to follow, the limitations appear to be a réduction in mass transfer performance and also material limitations. The latter is a serious limitation since it limits the scope of applications where such adsorbent beds are used.
Another technique that is discussed in the art as a replacement to the granular bed approach is to avoid their use altogether and instead coat the métal of the heat exchanger with the adsorbent. This generally involves use of an organic agent to clean the métal surface, formation of a slurry of the adsorbent with an organic binder, and then application on the cleaned métal surface, followed by heating to remove the residual binder. Several different coating techniques are discussed and disclosed in the art. One advantage of this method is that it avoids the heat contact résistance of adsorbent and métal significantly. This method has been considered an alternative to the granular bed approach.
Another method that is discussed in the art is the formation of a polymeric net such as a polyaniline net over the granular bed. This can be done in situ using oxidative in situ polymérisation of aniline on the surface of the adsorbent granules. The disadvantage noted with this method is that while heat transfer résistance is reduced, the mass transfer performance is affected adversely.
Other attempts include déposition of adsorbent over a metallic foam. One example of this method includes 'déposition of zeolite and copper-metaiToam. The method essentially comprises coating of the metallic part of the heat exchanger with an epoxy resin, a foaming agent and a métal powder. The adsorbent material is deposited using a colloïdal seed solution. For example, in the case of zeolite, this involves seeding, followed by hydrothermal synthesis, washing and drying. It is reported that this method improves the heat transfer characteristics significantly, but results in an increase in metallic mass.
The consolidated bed approach relies on several different steps. For example, compressed adsorbent granules and clay, expandable graphite, moulding granules and addition of binder and metallic foam impregnated with adsorbent granules. It is reported that this method results in a significant increase in heat transfer performance. However, the method may not be efficient in the case of ail adsorbent materials, and also has the limitation of bed permeability and cracking.
As can be seen, the approaches that hâve been proposed in the art look at various solutions as alternatives to the granular bed approach. Conventional wisdom in the art is that granular bed approach adversely affects heat transfer performance, and the only solution is to seek a replacement for this method.
The applicants herein hâve determined that a hybrid approach provides not only the mass transfer performance which is a significant advantage of the granular bed approach, but also enhanced heat transfer performance. The method of the invention involves an integrated approach to heat exchanger performance enhancement which involves not only adopting a coating for the métal portions of a heat exchanger (or parts thereof), but also ensuring the presence of additional adsorbent material provided between such metallic parts. It has been observed in test studies that such a hybrid adsorbent based heat exchanger provides significant performance enhancement both in terms of heat and mass transfer characteristics.
The object of this invention is to provide a hybrid adsorption heat exchanger that is compact, efficient in converting input cooling power and affordable.
The essence of the invention involves heat transfer enhancement by a hybridisation technique which includes both coating of the heat exchanger fins as well as use of loose porous adsorbent materials between the fins. A réfrigérant such as water/ammonia/ethanol/methanol/other assorted réfrigérants are exothermically adsorbed and endothermically desorbed, from the porous adsorbent, which is usually packed in an adsorbent bed having good heat transfer characteristics of a single adsorbent. In an adsorbent bed, the major thermal résistances corne from the fin of the adsorber and adsorbent material which can be fully eliminated through coating of the adsorbent material. The spécifie power is intensified through packing of loose adsorbent grains between the coated fins. The invention combines the coated adsorbent as well as packing of the loose adsorbent grains or alternate means such as glass fibres wherein desiccant is either generated in situ or are pre-impregnated, or a combination of different means such as granules and glass fibres.
Figure 1 is a représentation of a typical finned type block adsorber that is used in the adsorber and desorber heat exchangers.
Figure 2 is a représentation of a typical finned type tube adsorberthat is used in heat exchangers.
Figure 3(a) is a représentation of prior art finned block adsorbers wherein the adsorber bed is filled/packed with granular adsorbents. As is évident from Fig. 3(a), the secondary fluid flows through the adsorber heat exchange tube, and the fins are provided on the external surface of the heat exchange tube. The interstitial spaces between the fins are packed with adsorber granules. The tube itself may be made of a métal such as copper which promotes heat transfer. The granular packing is finally covered with a metallic mesh. The fins are typically made of aluminium.
Figure 3(b) is a représentation of prior art finned block adsorbers. The secondary fluid flows through the adsorber heat exchange tube, and the fins are provided on the external surface of the heat exchange tube. The interstitial spaces between the fins are vacant. The tube itself may be made of a métal such as copper which promotes heat transfer. The granular packing is finally covered with a metallic mesh. The fins are typically made of aluminium and are coated with the adsorbent material using techniques disclosed in the art. The coating procedures are discussed in some detail in this document, and involve the use of resins and binders to ensure uniform déposition of adsorbent on the fins.
Figure 4(a) is a représentation of an adsorbent bed wherein the fins of the adsorber heat exchange tube are coated with a first adsorbent material and the interstitial spaces between the fins filled with a second adsorbent material comprising granules. The first and second adsorbents may be same or different. The granular bed is then covered with a metallic mesh. The coating can be uniform across the external surface of the heat exchange tube. In the alternative, only the fins are coated, and the surface of the heat exchanger tube between two fins remains uncoated.
Figure 4(b) is a représentation of an adsorbent bed wherein the fins of the adsorber heat exchange tube are coated with a first adsorbent material and the interstitial spaces between the fins filled with a second adsorbent material comprising desiccant coated paper. The desiccant coated substrate may be one wherein the desiccant is coated or impregnated into the glass fiber or may be one wherein the desiccant is generated in situ. The first and second adsorbents may be same or different. The coating can be uniform across the external surface of the heat exchange tube. In the alternative, only the fins are coated, and the surface of the heat exchanger tube between two fins remains uncoated.
Figure 4(c) is a représentation of an adsorbent bed wherein the fins of the adsorber heat exchange tube are coated with a first adsorbent material and the interstitial spaces between the fins filled with a second adsorbent material comprising corrugated desiccant coated substrate block. The desiccant coated substrate may be one wherein the desiccant is coated or impregnated into the glass fiber or may be one wherein the desiccant is generated in situ. The first and second adsorbents may be same or different. The coating can be uniform across the external surface of the heat exchange tube. In the alternative, only the fins are coated, and the surface of the heat exchanger tube between two fins remains uncoated.
Figure 4(d) and Figure 4(e) are représentations of an adsorbent bed wherein the fins of the adsorber heat exchange tube are coated with a first adsorbent material and the interstitial spaces between the fins filled with a second adsorbent material comprising either a corrugated or a plain desiccant coated substrate block and adsorbent granules interspersed in between the desiccant coated substrate block. In Figure 4(d) the substrate blocks are provided perpendicular to the axis of the tube, whereas in Figure 4(e) the substrate blocks are provided parallel to the tube axis. The desiccant coated substrate may be one wherein the desiccant is pre-coated/ impregnated into the glass fiber or may be one wherein the desiccant is generated in situ. The first and second adsorbents may be same or different. The coating can be uniform across the external surface of the heat exchange tube. In the alternative, only the fins are coated, and the surface of the heat exchanger tube between two fins remains uncoated. The substrate blocks in cases of Figures 4(b) to Figure 4(e) may also be perforated to enhance both mass and heat transfer.
Figure 4(f) is a représentation of an adsorbent bed wherein the fins of the adsorber heat exchange.tube are coated with a first adsorbent material and the interstitial spaces between the fins filled with a second adsorbent material comprising adsorbent granules. The fins are corrugated in this embodiment and may also if desired, be perforated in any desired pattern in order to enhance heat and mass transfer. The first and second adsorbents may be same or different. The coating can be uniform across the external surface of the heat exchange tube. In the alternative, only the fins are coated, and the surface of the heat exchanger tube between two fins remains uncoated.
Figure 5 is a représentation of heat transfer régions in a coated fin, and is described in detail below.
Figure 6 is a représentation of a substrate material that is coated with adsorbent, and perforations are provided thereon in predetermined or desired patterns. This substrate material can be converted into the external extensions (fins), for the heat exchanger, and adsorbent materia!>fi!led in thé beds formed thereby.
The invention essentially résides in hybridising the adsorbent bed such that not only is the fin coated with an adsorbent material, the interstitial spaces between the fins are provided with an additional adsorbent material. The second filler adsorbent material may be the same as the adsorbent material provided in the coating or may be different. For example, the filler adsorbent material may be in the form of granules that are available such as zeolite material, activated carbon, activated alumina, or silica gel. Alternatively, the filler material can comprise fibers or sheets of glass, ceramic, activated carbon, graphite, organic or inorganic substances having adsorbent material provided thereon either by coating, dipping, imprégnation or by formation in situ or any other method.
The hybrid heat exchanger of the invention provides flexibility in combining different adsorbent forms. Tests establish that this hybrid heat exchanger provides significant enhancement both in terms of mass transfer and heat transfer performance.
The approach to the invention comprised assessing current state of the art in respect of granular adsorbent provided within an uncoated finned space. It is known in the art that the efficiency (spécifie capacity) of such Systems is around 100 watts per liter of adsorbent heat exchanger. In view of this, the approach was to:
a. increase the watts output per liter of adsorbent heat exchanger volume, thus decreasing the overall volume , footprint and cost.
b. to improve the adsorption and desorption kinetics in order to additionally enhance the watts per absorber heat exchanger output thus further reducing the footprint, volume and cost of the adsorption chilien The présent invention achieves both simultaneously.
In order to increase and optimize the performance of adsorbent heat exchanging devices, multiple variables were utilized. These comprise:
1. Substrate: the hybrid absorber heat exchanger of the invention relies on one part of the heat exchanger having an adsorbent adhered thereto. The invention provides flexibility in terms of substrate choice depending on the method of adhesion that is employed to ensure adhering of the adsorbent to the substrate. The substrates can be aluminum foil, copper foil, organic métal fiber sheet, inorganic fiber sheet carbon reinforced plastic, etc. The fin types include flat/plain, corrugated, louvered, sine wave, rippled, pyramid, or pin type.
2. Substrate thickness: The substrate thickness, depending on the type of support the substrate provides to the adsorbent, and thermal conductivity as part of the overall heat exchanger design, will typically range from 0.5 mm - 2.0 mm, more typically from 0.1 mm to 1.0 mm.
3. Substrate shape: Depending on the choice of the substrate, the substrate may be fiat, corrugated, square sign wave, or differently shaped e.g. triangular etc.
4. Adsorbent: The adsorbent material to be adhered to the substrate will typically be silica gel, molecular sieve, composites, or activated carbon, and can also comprise under development adsorbents which hâve a high surface area and are heat transfer fluid tolérant. For example, if water is used as the réfrigérant, then the adsorbent should be water tolérant. If other réfrigérants are used in the adsorption chillers such as éthanol, methanol and ammonia and HFC based réfrigérants, the adsorbents should be chemically inert to such réfrigérants. Some of these adsorbents already exist while others are under development. Typically these would be from the family of MOFs, aluminum phosphate, COFs, FAMs and FMMs, composites, etc. As the enhanced surface area and bulk density are complementary factors, the adsorbents of choice can dépend on both the useful capacity under operating capacity of boundaries of the adsorbent but will be of higher bulk density so that the overall adsorption, and hence the spécifie performance in kW per adsorbent heat exchanger, is maximized. Further the kinetics of the adsorbent, in terms of adsorption and desorption, and the means to enhance the ‘kinetics’ of a given adsorbent, will also play a significant rôle to maximize the overall capacity in terms of Watt per liter of adsorbent heat exchanger.
These adsorbents, to enhance the useful capacity, can further be doped with doping agents such as inorganic métal salts such as sodium chloride, calcium chloride, lithium bromide, magnésium chloride, magnésium sulphate, calcium nitrate, manganèse chloride etc., To improve the thermal conductivity of the heat flow from within the adsorbent to the substrate, as well as overall kinetics, use can be made of adding highly conductive materials like graphite, expanded graphite, copper powder etc. in small quantities.
In some cases, there can be a combination of both doping and addition of thermally conductive materials.
5. General methods of adhering the adsorbent to the substrate: There are several known methods, as enumerated below, of adhering the adsorbent to the substrate but this invention is not limited to the existing art or methods:
a. One method of adhering the desiccant to the substrate, particularly impervious substrates, is to use non-masking binders or glues. The binder of glues can be inorganic, organic and also the combination of both.
b. Substrates, particularly porous substrates, the adsorbent can be impregnated again with the help of suitable non masking binders/loops. The binder of glues can be inorganic, organic and also the combination of both. The imprégnation may also include a dip coating method.
c. In yet another method, the substrate, particularly porous substrate, the adsorbent can be synthesized in situ without the use of binders of glues.
d. In yet another method, starting with the substrate, typically an aluminum foil, the adsorbent can be synthesized in situ on the surface of the substrate, utilizing the substrate material as one of the éléments to grow the adsorbent crystals.
Heat transfer in the adsorbent bed is managed by régénération and adsorption using a secondary fluid such as water. For the heat transfer to and from the secondary fluid there are four heat transfer résistances as is shown in Figure 5. The résistances are:
R.1 The convective heat transfer résistance between the secondary fluid and the métal wall.
R.2 The heat transfer résistance through the wall of the heat exchanger.
R.3 The contact heat transfer résistance between the métal and adsorbent.
R.4 The conductive heat transfer résistance through the desiccant mass
As can be seen the heat exchanging device design can affect the heat transfer résistances.
In the above, R3 is prédominant and most significant. Thus far, the effort and attempt has been to coat adsorbents on the heat exchanger métal surface, typically the extended fin, typically aluminium. In doing so the conductive heat transfer résistance through the desiccant mass (R4) has been ignored and eliminated as no further adsorbent is placed between the extended heat exchanger surfaces. While the benefit is gained through réduction of R3, there is a significant trade off and loss of adsorption capacity and therefore mass transfer as the amount/mass of desiccant gets limited in the applied coating, thus reducing the adsorbent to métal mass ratio.
The présent invention aims to maintain a near optimal adsorbent to métal mass ratio by combining the desiccant coated extended surface of metal/fin by not only reducing R3 but also considerably improve the kinetics, along with the use of granular material within the coated fins spaces even though limited R4 will be encountered, thus providing an overall performance enhancement of >35/40% in terms of Watts per liter of adsorbent heat exchanger using the traditional adsorbent heat exchanger with adsorbent granular material packed within the heat exchanger fin surface. There are also other methods of filling the voids as described hereinafter.
The adsorbent is adhered to the substrate by applying silica gel granular/powder to aluminum foil using a non-masking binder from a class of organic and as well as separately inorganic binders, and also using pore cleaning agentfs] for the adsorbent. Zeolites can also be used instead of silica gel.
The coating on the extensions can be achieved by any method that is already known, such as that disclosed in US Patent 8,053,032 (direct crystallization of a zeolite layer on a substrate), US Patent Publication 2010/0136326 (coating the substrate surface with a silicate layer obtained through solvothermal synthesis),
US Patent Publication 2011/0183836 (coating an aluminium containing substrate with a microporous layer ofrafciminium phosphate zeolite), or any other method known in the art for coating the substratë and fins.
Irrespective of the method of adhering the adsorbent to the substrate or the substrate type, the amount of adsorbent has to be optimal so that too much adsorbent does not inhibit heat transfer from the outside layer to the heat exchanger. Typically the adsorbent quantity can vary from 10 GSM to 500 GSM but will more specifically lie within 150 to 300
GSM depending upon the adsorbent, the method of adhering the absorbent to the substrate, the bulk density of adsorbent and the use, if any, of the binder/glue.
In the hybrid adsorbent heat exchanger, while the heat exchanger surface has adsorbent adhered to by means and methods explained above but not limited thereto, in the présent invention, the adsorbent is filled within the voids of the extended fin heat exchanger surface. The choice of the type and methods of placement of such adsorbents can be as follows:
1. Plane naturally granular adsorbent, of suitable mesh size e.g. silica gel
2. Adsorbent in powder form but made into granules of suitable mesh.
3. Adsorbent adhéré to a substrate, as a sheet, or as sheet glass or in any other shape
e.g. corrugated, square/rectangular, triangular etc. with or without doping, with or without thermally conductive additives like expanded graphite, graphene etc.
In the présent invention of the hybrid heat exchanger, extensive testing has been done using granular silica gel. In the application of adsorption chillers, while there is a choice of many working pairs of adsorbent and réfrigérants, the most typically and commonly used or employed is the silica gel-water pair. In most adsorption chillers under manufacturer and also the research being done in this field around the world, the outstanding silica gel of choice is and has been the high density granular or beaded silica gel as available .from Fuji Sylsia Co. Ltd., Japan. This material typically has a surface area in the range of 600-800 m2/g and bulk density of 700-900 g/liter, depending upon the whether the material is beaded or granular, and if granular on the mesh side.
The présent invention also benchmarks a new hybrid adsorbent heat exchanger with the traditional adsorbent heat exchanger using Fuji RD type silica gel. Fuji RD type silica gel, because of its characteristics and kinetics, has become the adsorbent of choice for silica gel-water pair based adsorption chillers, globally, both in commercial production and research. Applicants herein hâve also developed a proprietary silica gel labeled S2, which through extensive testing, has shown outstanding performance potential as an adsorbent for silica gel-water based adsorption chillers. Examples of its performance and kinetics are shown in Figs. 7-11.
Adsorption capacity of adsorbent/refrigerant pair dépends on the porous properties (pore size, pore vôlumeond pore diameter) of adsorbent and ‘isothermal characteristics of the pair. The porous properties of various zeolites, silica gels, activated carbons, activated alumina, MOFs (metal-organic frameworks), COFs (covalent organic frameworks), and FAMs (functional adsorbent materials) are presented which are determined from the nitrogen adsorption isotherms. The standard nitrogen gas adsorption/desorption measurements on various adsorbents at liquid nitrogen of température 77.4 K are performed. Surface area of each adsorbent is determined by the Brunauer, Emmett and
Teller (BET) plot of nitrogen adsorption data. Table 1 shows the surface area, pore volume and apparent density of silica gels (A and RD type), activated carbon fibers of type FX-400 and A 20, granular activated carbon, activated carbon powder of type Maxsorb III and two different MOFs. As can be seen from Table 1, the BET surface area of Maxsorb III and 5 MIL-101Cr are as high as 3140 and 4100 m2/g, respectively. However, utilization of
Maxsorb III and MIL-101Cr as adsorbents in commercial adsorption chillers has been hindered due mainly to its cost, which is above USD 300 per kg. On the other hand silica gels hâve been used in commercial adsorption chillers and the cost of silica gel samples is around 10-15 USD per kg.
Table 1. Porous properties of various potential adsorbent materials.
Adsorbent | Surface area (mV) | Pore volume (cm3-g-1) | Apparent density (g-cm’3) |
Silica gel (type A) | 650 | 0.28 | 0.73 |
Silica gel (type RD) | 720 | 0.37 | 0.7 |
Silica gel (type S2) | 700 | 0.34- | 0.73 |
Activated carbon fiber (FX 400) | 700-2500 | 0.5-1.4 | 0.3 |
Activated carbon Fiber (A- 20) | 1900 | 1.028 | 0.25 |
Granular activated carbon | 700-1500 | 0.5-1.0 | 0.4 |
Highly porous activated carbon (Maxsorb III) | 3140 | 1.7 | 0.31 |
ZreO4(OH)4(Linker)6 | 2064 | 0.97 | - |
MIL-101Cr | 4100 | 2.0 |
Turning now to figures 7 onwards, the graphical représentations display the enhanced adsorbent capacity of the invention.
Figure 7 shows the adsorption isotherms of parent silica gel S2/water and coated
S2/water adsorbent/refrigerant pairs for adsorption température of 30°C and pressure 15 ranges from 0.7 to 3.8 kPa. .•For-ithe...said adsorption isotherm, the adsorbent sample température is kept constant w'nîlst the evaporator température increases stepwise until the relative pressure reaches above 0.9. It can be seen from Fig. 7 that, the adsorption capacity of silica gel S2/water pair is as high as 0.34 kg kg’1at adsorption température of 30°C and pressure at around 3.6 kPa. The adsorption capacity of coated silica gel S2/water 20 pair is similar to that of the parent S2/water pair. It can be observed that, for both parent
S2/water pair and coated S2/water pairs, the adsorption capacity increases linearly with the increase of pressure in the whole studied range.
Figures 8 and 9 show the adsorption uptake data of silica gel S2/water pair for températures 30 - 70°C and pressure up to 5 kPa and 15 kPa, respectively. The former pressure rage is suitable for adsorption cooling applications and the relatively higher pressures are required for adsorption desalination applications. As can be observed from Figs. 8 and 9, the adsorption uptake values increase linearly with the increase in pressure for ail measured adsorption températures, which implies that the parent silica gel S2/water paper is suitable for both adsorption cooling and desalination applications.
Figure 10 shows the adsorption isotherms of silica gel S2/water pair and silica gel RD/water pair for températures between 30 and 70°C and pressure up to 5 kPa, which is the operation range of silica gel/water based adsorption chillers. It is évident from Fig. 10 that the adsorption isotherms data of silica gel S2/water and silica gel RD/water pairs are comparable and one can choose either adsorbent depending on the cost and availability of the adsorbent.
Figures 11 (a), 11 (b) and 11 (c) show the temporal profiles of adsorption uptake and pressure of the silica gel S2/water pair at adsorption températures of 30, 50 and 70°C, respectively. It is visible from Figs. 11(a) - 11 (c) that the adsorption kinetics of the studied pair is relatively faster at the early stages of adsorption processes. Moreover, more than 80% of total uptake occurs within the first 5 minutes and thus the silica gel S2/water pair seems to suitable for adsorption cooling applications.
The starting point for the production of an adsorption heat exchanger in accordance with the invention is at first a heat exchanger structure which is produced separately. It is produced according to the known method from materials of high thermal conductivity. Suitable for this purpose hâve proven to be metallic Systems such as ones made of copper, aluminum, carbon, reinforced plastic or spécial steel. Ceramic materials or combined material Systems are also possible.
Suitable heat exchanger structures realize a circulation System for a heat carrier medium which is in connection with the outside area of the adsorption heat exchanger. In addition, heating wires or other heat sources can be embedded for heating the heat exchanger structures. In order'to'prb'duce the largest possible surface towards the sorbent material system, a lamella-like or honeycomb-like structure is preferred. It can also be in the form of a sponge or foam. Based on this heat exchanger structure which is produced separately at first, an inside coating with sorbent material is now carried out as follows.
In a first method step, an adhesive layer is applied to the wall of the heat exchanger facing towards the sorbent material, which hereinafter shall be referred to as inside wall. An adhesive is used for this purpose which forms a solid layer at first. For realizing said adhesive layers it is possible to use different methods such as immersion, flooding or spraying. The method steps of adhesive coating can further be repeated for setting an optimal layer thickness. It is especially advantageous in this respect to set the viscosity of the applied adhesive by tempering or by enriching or évaporation with solvents for example. It is alternatively also possible to apply the adhesive in a solid powdery state to the walls of the heat exchanger. Such powder coating is especially useful in planar heat exchanger structures.
The heat exchanger can further be filled at first with powdery adhesive which is then activated by heating of the heat exchanger structure in régions of the heat exchanger close to the wall, so that there is bonding in the area close to the walls and the subséquent removal of the non-adhering powdery adhesive material from the areas remote of the walls is possible by shaking, blowing or rinsing. Irrespective of the choice of adhesive or the chosen application method, the adhesive layer in the région close to the wall must adhéré at least in such a stable manner that during the subséquent method step in which the sorbent material is introduced into the heat exchanger there is no functionally impairing mixture of the adhesive of the sorbent material.
After the coating steps are completed and the coating on the metallic portions are dry, the interstitial .spaces can be filled in with conventional granular adsorbent material, or with glass fiber sheets that are impregnated with adsorbent material (or where the adsorbent is formed in situ using technology proprietary to applicants). Contrary to disclosures in the art, the heat transfer performance of this hybrid heat exchanger is significantly high over what has hitherto been known in the art.
Studies show that the heat transfer performance of the hybrid heat exchanger device of the invention are significantly higher than those of either of the two currently available prior art Systems - which use either a granular bed or a coated fin System in isolation.
The primary difficulty of adsorption heat pumps is the poor heat transfer between the adsorbent materials and the heat transferring media namely cooling medium for adsorption process and heating medium for desorption process. Conventional adsorber heat exchangers or the conventional manner of packing the adsorber materials is packing the adsorbent around'the'finned-tube of the heat exchanger. This»method is.widely used due to the simplicity in the manufacturing and the limitation ’in the attachment or coating technology of the adsorbent to the fins of the heat exchanger.
The effective coating of the adsorbent materials on the extended surfaces of the heat exchanger can greatly improve in the heat and mass transfer mechanism of the adsorber of adsorption cycles. Two significantly outstanding features or advantages of the coated adsorber heat exchangers are (1) the improvement in adsorption kinetics via effective heat transfer and (2) the réduction in thermal mass. The major contribution of the former feature is the réduction in cycle time whilst the less thermal mass directly translates to better performance or coefficient of performance (COP). These two features synergistically improve the adsorption cycle both energetically, footprint-wise and more importantly the lowering in capital cost.
Figure 13 shows the cooling capacity and the COP of the adsorption chiller using conventional packing method, the advanced adsorbent-coated method and the adsorbentcoated hybrid heat exchangers. It should be noted that the evaporator and the condenser remain the same for both cases. It is observed that the adsorbent-coated and adsorbentcoated hybrid types provide significant performance improvement.
The overall heat transfer coefficient of the advanced adsorbent-coated and adsorbent-coated hybrid heat exchanger is around 350 to 350 W/m2K depending on the adsorber/desorber configuration. Figure 14 shows the température profiles of the major components of the adsorption chiller for the overall heat transfer coefficient of 350 W/m2K. As can be seen from Figure 14, ail four heat exchangers work efficiently and the chiller produces effective cooling due to faster adsorption kinetics resulted from improved heat transfer and smaller thermal mass.
Figure 15 shows the performance comparisons of adsorption chiller for pellet, adsorbent-coated and hybrid heat exchangers. The performance comparisons hâve been made in terms of spécifie cooling power (SCP), coefficient of performance (COP) and volumétrie efficiency. As can be seen from Figure 15, the SCP and COP values for coated and hybrid type heat exchangers are comparable. However, SCP increases about 8% and COP increases more than 100% in case of coated and hybrid type heat exchangers due to faster kinetics and less thermal mass. On the other hand, the volumétrie efficiency of hybrid heat exchanger is about 35% higher than the pellet type heat exchanger and about 18% higher than that of the adsorbent-coated heat exchanger due to higher mass of adsorbent in the same volume which results in more cooling power and thus significantly contribute in the réduction of adsorption system footprint and capital cost.
Another advantage of the invention that has been observed from studies conducted is that the spécifie capacity of the hybrid heat exchanger device of the invention is significantly better-'than those ·Όί prior art adsorbers. Figure 12 is· a comparative représentation of the spécifie capacity, in terms of cooling Watts per liter of adsorbent heat exchanger, both for prior art adsorbers and the potential spécifie capacity with different hybrid heat exchangers of the présent invention.
Claims (36)
1. A hybrid adsorption heat exchanging device comprising:
at least one tubular or micro channel structure for carrying a heat transfer fluid; the external surface of said structure being provided with extensions in at least two locations;
said extensions forming a bed therebetween for providing one or more adsorbent materials;
a coating of adsorbent material being provided on at least a part of said extensions.
2. A device as claimed in claim 1 wherein the extensions run longitudinally along the full length of the tubular or micro channel structure or run circumferentially around the tubular or micro channel structure.
3. A device as claimed in claim 1 or 2 wherein the height of each extension remains uniform along its entire length.
4. A device as claimed in any of daims 1 to 3 wherein the extensions are intégral with said tubular or micro channel structure or are connected thereto by external connectors.
5. A device as claimed in claim 4 wherein the tubular or micro channel structure and the extensions are made of the same material.
6. A device as claimed in any of daims 1 to 5 wherein the tubular or micro channel structure and/or the extensions comprise a heat conductive material selected from metallic, ceramic based, polymeric or carbon based materials.
7. A device as claimed in claim 1 wherein each extension is coated with an adsorbent being the same or different from the adsorbent filling in the bed, and wherein the adsorbent material provided in said bed is selected from the group consisting of zeolites, mesoporous silicates, insoluble métal silicates, silica gel type A, silica gel type RD, silica gel type S2, activated carbon fiber, granular activated carbon, activated alumina, highly porous activated carbon, Zr6O4(OH)4 bonded with linkers, MIL-101Cr, metal-organic frameworks, covalent organic frameworks, functional adsorbentmaterials, and the like, singularly or in any combination thereof.
8. A device as claimed in claim 7 wherein the adsorbent material comprises adsorbent granules having a pore diameter in the range of 3 to 100 Angstrom.
9. A device as claimed in claim 7 wherein the adsorbent material comprises corrugated sheets with adsorbent coated or deposited thereon.
10. A device as claimed in claim 9 wherein the corrugated sheets are made of a thermally conductive material selected from the group consisting of aluminium, copper, graphite/expanded graphite, inorganic or organic fiber substrates or any combinations thereof
11. A device as claimed in claim 9 and 10 wherein said corrugated sheets comprise perforated sheets.
12. A device as claimed in claim 7 to 11 wherein the adsorbent material comprises of a combination of adsorbent granules and adsorbent coated or deposited sheets.
13. A device as claimed in any preceding claim wherein the extensions are corrugated on the external surface thereof priorto coating with adsorbent material.
14. A device as claimed in claim 1 wherein the extensions are coated with an adsorbent material selected from the group consisting of zeolites, mesoporous silicates, insoluble métal silicates, silica gel type A, silica gel type RD, silica gel type S2, activated carbon fiber, granular activated carbon, activated alumina, highly porous activated carbon, Zr6O4(OH)4 bonded with linkers, MIL-101Cr, metal-organic frameworks, covalent organic frameworks, functional adsorbent materials, and the like, singularly or in any combination thereof.
15. A device as claimed in any preceding claim wherein the heat transfer fluid is selected from the group consisting of water, lower alcohols, and oils, and the like.
16. A device as claimed in any preceding claim wherein the adsorbent material is provided with one or more fillers selected from the group consisting of zeolites, mesoporous silicates, insoluble métal silicates, silica gel type A, silica gel type RD, silica gel type S2, activated carbon fiber, granular activated carbon, activated alumina, highly porous activated carbon, Zr6O4(OH)4 bonded with linkers, MIL-101Cr, metalorganic frameworks, covalent organic frameworks, functional adsorbent materials, and the like, singularly or in any combination thereof.
17. A device as claimed in claim 16 wherein said filler is a doped filler, wherein the doping agent is selected from the group consisting of inorganic metals salts such as calcium chloride, lithium bromide, magnésium chloride, magnésium sulphate, calcium nitrate, manganèse chloride, and the like
18. A device as claimed in any preceding claim wherein in addition to the adsorbent material in the bed, one or more additives selected from the group consisting of copper aluminium, graphite/expanded graphite, and the like are added to enhance thermal conductivity.
19. A device as claimed in any preceding claim wherein a polymeric mesh is provided over the adsorbent bed, wherein the polymeric mesh is preferably a polyaniline mesh.
20. A method for the manufacture of a hybrid adsorption heat exchanging device, said method comprising:
coating at least part of a thermally conductive material with an adsorbent;
- converting the at least partially coated thermally conductive material into a tubular structure for carrying a heat transfer fluid, and providing two or more extensions thereon, said extensions being either intégral with said coated tubular structure, or comprising at least partly adsorbent coated thermally conductive material, said extensions forming an adsorbent bed therebetween;
providing one or more adsorbent material in said adsorbent bed.
21. A method as claimed in claim 20 wherein each extension is coated with an adsorbent being the same or different from the adsorbent filling in the bed, wherein the adsorbent material provided in said bed is selected from the group consisting of zeolites, mesoporous silicates, insoluble métal silicates, silica gel type A, silica gel type RD, silica gel type S2, activated carbon fiber, granular activated carbon, activated alumina, highly porous activated carbon, Zr6O4(OH)4 bonded with linkers, MIL-101Cr, metal-organic frameworks, covalent organic frameworks, functional adsorbent materials, and the like, singularly or in any combination thereof.
22. A method as claimed in claim 21 wherein the adsorbent material comprises adsorbent granules having a pore diameter in the range of 3 to 100 Angstrom.
23. A method as claimed in claim 21 wherein the adsorbent material comprises corrugated sheets with adsorbent coated or deposited thereon, and wherein the corrugated sheets are preferably made of a thermally conductive material selected from the group consisting of aluminium, copper, graphite/expanded graphite, inorganic or organic fiber substrates or any combinations thereof.
24. A method as claimed in claim 23 wherein said corrugated sheets comprise perforated sheets.
25. A method as claimed in claim 23 and 24 wherein the adsorbent material comprises of a combination of adsorbent granules and adsorbent coated or deposited sheets.
26. A method as claimed in any preceding claim 20 to 25 wherein the extensions are corrugated on the external surface thereof prior to coating with adsorbent.
27. A method as claimed in claim 20 wherein the extensions are coated with an adsorbent material selected from the group consisting of zeolites, mesoporous silicates, insoluble métal silicates, silica gel type A, silica gel type RD, silica gel type S2, activated carbon Tiber,· granular activated carbon, activated alumina, highly porous activated carbon, Zf6O4(O'H)4 bonded with linkers, MIL-101Cr, metal-organic frameworks, covalent organic frameworks, functional adsorbent materials, and the like, singularly or in any combination thereof.
28. A method device as claimed in any preceding claim 20 to 27 wherein the heat transfer fluid is selected from the group consisting of water, lower alcohols, and oils, and the like.
29. A method as claimed in any preceding claim 20 to 28 wherein the adsorbent material is provided with one or more fillers selected from the group consisting of zeolites, mesoporous silicates, insoluble métal silicates, silica gel type A, silica gel type RD, silica gel type S2, activated carbon fiber, granular activated carbon, activated alumina, highly porous activated carbon, Zr6O4(OH)4 bonded with linkers, MIL-101Cr, metalorganic frameworks, covalent organic frameworks, functional adsorbent materials, and the like, singularly or in any combination thereof.
30. A method as claimed in claim 29 wherein said filler is a doped filler, wherein the doping agent is selected from the group consisting of inorganic metals salts such as calcium chloride, lithium bromide, magnésium chloride, magnésium sulphate, calcium nitrate, manganèse chloride, and the like.
31. A method as claimed in any preceding claim 20 to 30 wherein in addition to the adsorbent material in the bed, one or more additives selected from the group consisting of copper aluminium, graphite/expanded graphite are also added to enhance thermal conductivity.
32. A method as claimed in any preceding claim 20 to 31 wherein a polymeric mesh is provided over the adsorbent bed, wherein the polymeric mesh is preferably a polyaniline mesh.
33. A method as claimed in claim 20 wherein the adsorbent bed is provided with a desiccant coated substrate wherein the desiccant is coated or impregnated or generated in situ onto said substrate.
34. A method as claimed in claim 20 wherein the desiccant is attached to the substrate through non-masking binder or glue or a combination thereof.
35. A device as claimed in any of preceding daims 1 to 23 for use in an environment requiring periodic ortemporary storage and subséquent release of adsorbate such as water.
36. A device as claimed in claim 35 an adsorption réfrigération machine, chilled beams, an automobile air conditioning unit, a domestic integra! air conditioning unit, a domestic split level air conditioning unit, and the like.