MX2020004596A - Acero templado en prensa con propiedades personalizadas despues de un tratamiento termico novedoso. - Google Patents

Acero templado en prensa con propiedades personalizadas despues de un tratamiento termico novedoso.

Info

Publication number
MX2020004596A
MX2020004596A MX2020004596A MX2020004596A MX2020004596A MX 2020004596 A MX2020004596 A MX 2020004596A MX 2020004596 A MX2020004596 A MX 2020004596A MX 2020004596 A MX2020004596 A MX 2020004596A MX 2020004596 A MX2020004596 A MX 2020004596A
Authority
MX
Mexico
Prior art keywords
weight
preform
temperature
steel
composition
Prior art date
Application number
MX2020004596A
Other languages
English (en)
Inventor
Erik James Pavlina
Stephen Bryant Tate
Grant Aaron Thomas
Original Assignee
Ak Steel Properties Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ak Steel Properties Inc filed Critical Ak Steel Properties Inc
Publication of MX2020004596A publication Critical patent/MX2020004596A/es

Abstract

Una preforma soldada a la medida es creada al formar una preforma a partir de un acero de la composición A y un acero de la composición B y soldar juntos dichos dos aceros, calentar dicha preforma soldada a una temperatura por arriba de la temperatura Ac1 relacionada con el acero de la composición A, transferir dicha preforma a un troquel de formación, y después enfriar dicha preforma a una temperatura entre la temperatura inicial de la martensita y la temperatura final de la martensita del acero de la composición B, y mantener dicha preforma a tal temperatura o a una temperatura mayor, enfriar dicha preforma a una temperatura ambiente; la preforma soldada a la medida comprende la Aleación A y la Aleación B; en donde la Aleación comprende de 0.10 - 0.50% en peso de C, de 0.1 - 0.5% en peso de Si, de 2.0 - 8.0% en peso de Mn, de 0- 6.0% en peso de Cr, de 0.0 - 2% en peso de Mo, y de 0.0 - 0.005% en peso de B y en donde la Aleación B comprende de 0.06 - 0.12% en peso de C, de 0.1 - 0.25% en peso de Si, de 1.65 - 2.42% en peso de Mn, de 0.0 - 0.70% en peso de Cr, de 0.08 - 0.40% en peso de Mo, de 0.0 - 0.05% en peso de V, de 0.01 - 0.05% en peso de Ti, y 2% en peso de Al o menos, y en donde dicha preforma soldada a la medida es sometida a un ciclo de enfriamiento y térmico de partición en un troquel de formación.
MX2020004596A 2017-11-02 2018-11-02 Acero templado en prensa con propiedades personalizadas despues de un tratamiento termico novedoso. MX2020004596A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201762580662P 2017-11-02 2017-11-02
PCT/US2018/059006 WO2019090113A1 (en) 2017-11-02 2018-11-02 Press hardened steel with tailored properties after novel thermal treatment

Publications (1)

Publication Number Publication Date
MX2020004596A true MX2020004596A (es) 2020-08-06

Family

ID=64402282

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2020004596A MX2020004596A (es) 2017-11-02 2018-11-02 Acero templado en prensa con propiedades personalizadas despues de un tratamiento termico novedoso.

Country Status (7)

Country Link
US (1) US20190126401A1 (es)
EP (1) EP3704276B1 (es)
CA (1) CA3076934C (es)
ES (1) ES2932501T3 (es)
MX (1) MX2020004596A (es)
TW (1) TW201930611A (es)
WO (1) WO2019090113A1 (es)

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3704281A1 (en) * 2017-11-02 2020-09-09 AK Steel Properties, Inc. Press hardened steel with tailored properties
CA3149331A1 (en) * 2019-08-07 2021-02-11 United States Steel Corporation High ductility zinc-coated steel sheet products
DE102019215053A1 (de) * 2019-09-30 2021-04-01 Thyssenkrupp Steel Europe Ag Verfahren zur Herstellung eines zumindest teilweise vergüteten Stahlblechbauteils und zumindest teilweise vergütetes Stahlblechbauteil
CN112779465A (zh) * 2020-11-30 2021-05-11 江苏联峰能源装备有限公司 一种微合金车轴钢的制备方法
CN113789432B (zh) * 2021-09-16 2023-01-24 昆明理工大学 一种改善sa508-4钢焊接组织局部硬化的方法
CN117210646A (zh) * 2023-08-29 2023-12-12 武汉理工大学 一种一体式复杂构件伺服热成形分区淬火方法及一种构件

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2008110670A1 (fr) * 2007-03-14 2008-09-18 Arcelormittal France Acier pour formage a chaud ou trempe sous outil a ductilite amelioree
WO2012120020A1 (en) * 2011-03-07 2012-09-13 Tata Steel Nederland Technology Bv Process for producing high strength formable steel and high strength formable steel produced therewith
FI20115702L (fi) * 2011-07-01 2013-01-02 Rautaruukki Oyj Menetelmä suurlujuuksisen rakenneteräksen valmistamiseksi ja suurlujuuksinen rakenneteräs

Also Published As

Publication number Publication date
CA3076934C (en) 2023-03-21
WO2019090113A1 (en) 2019-05-09
ES2932501T3 (es) 2023-01-20
CA3076934A1 (en) 2019-05-09
EP3704276B1 (en) 2022-09-21
EP3704276A1 (en) 2020-09-09
US20190126401A1 (en) 2019-05-02
TW201930611A (zh) 2019-08-01

Similar Documents

Publication Publication Date Title
MX2020004596A (es) Acero templado en prensa con propiedades personalizadas despues de un tratamiento termico novedoso.
AR067594A1 (es) Lamina de acero laminada en caliente y procedimiento para la fabricacion de la lamina de acero.
MX2012007359A (es) Acero, producto plano de acero, pieza de acero y procedimiento para producir una pieza de acero.
EA201290835A1 (ru) Термообработанный стальной материал, способ его получения и базовый стальной материал для него
BR112017010093A2 (pt) ?método para fabricar um produto de aço e produto de aço?
MX2020004769A (es) Hoja de acero laminada en frio y un metodo para la fabricacion de la misma.
AR066508A1 (es) Un proceso para fabricar una chapa de acero recocido y laminada en frio, con una muy alta resistencia , y una chapa producida de esta manera
RU2014130096A (ru) Высокопрочная бесшовная стальная труба для применения в нефтяной скважине, обладающая высокой стойкостью к растрескиванию под действием напряжений в сульфидсодержащей среде
MX2020004787A (es) Hoja de acero tratada termicamente laminada en frio y un metodo de fabricacion de la misma.
MX2020004784A (es) Hoja de acero laminada en frio y tratada termicamente y un metodo de fabricacion de la misma.
ECSP17024484A (es) Método de producción de hojalata conteniendo una lámina de acero de silicio de grano no orientado, lámina de acero obtenida y uso de ésta
AR104260A1 (es) Una varilla de bombeo de acero, método para fabricarla y acero utilizado para la varilla
RU2015155181A (ru) Способ изготовления детали путем горячей деформации стальной заготовки
AR065764A1 (es) Pieza de acero, articulo soldado y procedimiento para fabricar dicha pieza
AR075976A1 (es) Metodo para la manufactura de tuberias sin costura
SG11201907930QA (en) HIGH-Mn STEEL AND PRODUCTION METHOD THEREFOR
PE20141418A1 (es) Metodo de fabricacion de tubos de acero para varillas de perforacion con propiedades mecanicas mejoradas, y varillas obtenidas a traves de los mismos
RU2015101733A (ru) Бесшовная труба из высокопрочной нержавеющей стали с высокой коррозионной стойкостью для нефтяной скважины и способ её изготовления
IN2014CN02685A (es)
MX2017010558A (es) Aleacion a base de niquel con alta amplitud de fusion adecuada para soldadura fuerte de acero super austenitico.
RU2015143271A (ru) Воздушно-закаливаемая бейнитная сталь
MX2017000201A (es) Metodo para producir una hoja de acero de alta resistencia que tiene resistencia y capacidad de formacion mejoradas y hoja obtenida.
UA118699C2 (uk) Спосіб отримання високоміцного сталевого листа з покриттям, що має покращену міцність і пластичність, та отриманий лист
AR105167A1 (es) Acero resistente a la corrosión, método para producir dicho acero y uso del mismo
MX356324B (es) Método para la fabricación de acero martensítico con límite de elasticidad muy alto y placa o pieza obtenida por tal método.