MX2019004273A - Uso de agentes para reducir la cristalinidad en polipropileno para aplicaciones de bopp. - Google Patents
Uso de agentes para reducir la cristalinidad en polipropileno para aplicaciones de bopp.Info
- Publication number
- MX2019004273A MX2019004273A MX2019004273A MX2019004273A MX2019004273A MX 2019004273 A MX2019004273 A MX 2019004273A MX 2019004273 A MX2019004273 A MX 2019004273A MX 2019004273 A MX2019004273 A MX 2019004273A MX 2019004273 A MX2019004273 A MX 2019004273A
- Authority
- MX
- Mexico
- Prior art keywords
- polypropylene
- agents
- reduce crystallinity
- bopp
- applications
- Prior art date
Abstract
La película de BOPP incluye un polipropileno, una ausencia de un agente de nucleación, y un aditivo mezclado con el polipropileno que forma la mezcla de polipropileno/aditivo, en donde el aditivo es estearato de potasio.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US201662414111P | 2016-10-28 | 2016-10-28 | |
PCT/US2017/058861 WO2018081630A1 (en) | 2016-10-28 | 2017-10-27 | Use of agents to reduce crystallinity in polypropylene for bopp applications |
Publications (1)
Publication Number | Publication Date |
---|---|
MX2019004273A true MX2019004273A (es) | 2019-08-05 |
Family
ID=62021056
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MX2019004273A MX2019004273A (es) | 2016-10-28 | 2017-10-27 | Uso de agentes para reducir la cristalinidad en polipropileno para aplicaciones de bopp. |
Country Status (8)
Country | Link |
---|---|
US (2) | US10683408B2 (es) |
EP (1) | EP3532291A4 (es) |
JP (1) | JP6967073B2 (es) |
KR (1) | KR102411877B1 (es) |
CN (1) | CN109890615B (es) |
BR (1) | BR112019006896B1 (es) |
MX (1) | MX2019004273A (es) |
WO (1) | WO2018081630A1 (es) |
Family Cites Families (58)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
YU35844B (en) | 1968-11-25 | 1981-08-31 | Montedison Spa | Process for obtaining catalysts for the polymerization of olefines |
NL162664B (nl) | 1969-06-20 | 1980-01-15 | Montedison Spa | Werkwijze om een katalysator te bereiden voor de poly- merisatie van alkenen-1. |
US4543399A (en) | 1982-03-24 | 1985-09-24 | Union Carbide Corporation | Fluidized bed reaction systems |
US4588790A (en) | 1982-03-24 | 1986-05-13 | Union Carbide Corporation | Method for fluidized bed polymerization |
US4767735A (en) | 1987-02-02 | 1988-08-30 | Cosden Technology, Inc. | Catalyst pretreatment process |
US4794096A (en) | 1987-04-03 | 1988-12-27 | Fina Technology, Inc. | Hafnium metallocene catalyst for the polymerization of olefins |
US4975403A (en) | 1987-09-11 | 1990-12-04 | Fina Technology, Inc. | Catalyst systems for producing polyolefins having a broad molecular weight distribution |
US5158920A (en) | 1988-07-15 | 1992-10-27 | Fina Technology, Inc. | Process for producing stereospecific polymers |
FR2634212B1 (fr) | 1988-07-15 | 1991-04-19 | Bp Chimie Sa | Appareillage et procede de polymerisation d'olefines en phase gazeuse dans un reacteur a lit fluidise |
US5416228A (en) | 1991-10-07 | 1995-05-16 | Fina Technology, Inc. | Process and catalyst for producing isotactic polyolefins |
US5436304A (en) | 1992-03-19 | 1995-07-25 | Exxon Chemical Patents Inc. | Process for polymerizing monomers in fluidized beds |
US5352749A (en) | 1992-03-19 | 1994-10-04 | Exxon Chemical Patents, Inc. | Process for polymerizing monomers in fluidized beds |
US5456471A (en) | 1992-08-18 | 1995-10-10 | Macdonald; Donald K. | Golf practice apparatus and fabricating process |
US5317036A (en) | 1992-10-16 | 1994-05-31 | Union Carbide Chemicals & Plastics Technology Corporation | Gas phase polymerization reactions utilizing soluble unsupported catalysts |
RU2120947C1 (ru) | 1993-04-26 | 1998-10-27 | Эксон Кемикэл Пейтентс Инк. | Способ газофазной полимеризации в псевдоожиженном слое |
US5462999A (en) | 1993-04-26 | 1995-10-31 | Exxon Chemical Patents Inc. | Process for polymerizing monomers in fluidized beds |
US6468936B1 (en) | 1993-04-28 | 2002-10-22 | Fina Technology, Inc. | Solid MAO/metallocene catalyst complex for propylene polymerization |
ZA943399B (en) | 1993-05-20 | 1995-11-17 | Bp Chem Int Ltd | Polymerisation process |
US6245705B1 (en) | 1993-11-18 | 2001-06-12 | Univation Technologies | Cocatalysts for metallocene-based olefin polymerization catalyst systems |
US5525678A (en) | 1994-09-22 | 1996-06-11 | Mobil Oil Corporation | Process for controlling the MWD of a broad/bimodal resin produced in a single reactor |
US5616661A (en) | 1995-03-31 | 1997-04-01 | Union Carbide Chemicals & Plastics Technology Corporation | Process for controlling particle growth during production of sticky polymers |
US5677375A (en) | 1995-07-21 | 1997-10-14 | Union Carbide Chemicals & Plastics Technology Corporation | Process for producing an in situ polyethylene blend |
ATE215571T1 (de) * | 1995-11-24 | 2002-04-15 | Chisso Corp | Propylenzusammensetzung, verfahren zu deren herstellung, polypropylenzusammensetzung und geformte gegenstände |
US5665818A (en) | 1996-03-05 | 1997-09-09 | Union Carbide Chemicals & Plastics Technology Corporation | High activity staged reactor process |
US5627242A (en) | 1996-03-28 | 1997-05-06 | Union Carbide Chemicals & Plastics Technology Corporation | Process for controlling gas phase fluidized bed polymerization reactor |
US5968864A (en) | 1996-12-20 | 1999-10-19 | Fina Technology, Inc. | Catalyst efficiency for supported metallocene catalyst |
US5807800A (en) | 1997-02-11 | 1998-09-15 | Fina Technology, Inc. | Process for producing stereospecific polymers |
US5789502A (en) | 1997-04-22 | 1998-08-04 | Fina Technology, Inc. | Process for co-polymerization of propylene and ethylene |
US6090325A (en) | 1997-09-24 | 2000-07-18 | Fina Technology, Inc. | Biaxially-oriented metallocene-based polypropylene films |
US6242545B1 (en) | 1997-12-08 | 2001-06-05 | Univation Technologies | Polymerization catalyst systems comprising substituted hafinocenes |
US6207606B1 (en) | 1998-05-15 | 2001-03-27 | Univation Technologies, Llc | Mixed catalysts and their use in a polymerization process |
US6245868B1 (en) | 1998-05-29 | 2001-06-12 | Univation Technologies | Catalyst delivery method, a catalyst feeder and their use in a polymerization process |
US7354880B2 (en) | 1998-07-10 | 2008-04-08 | Univation Technologies, Llc | Catalyst composition and methods for its preparation and use in a polymerization process |
US6147173A (en) | 1998-11-13 | 2000-11-14 | Univation Technologies, Llc | Nitrogen-containing group 13 anionic complexes for olefin polymerization |
US6180735B1 (en) | 1998-12-17 | 2001-01-30 | Univation Technologies | Catalyst composition and methods for its preparation and use in a polymerization process |
US6653254B1 (en) | 1999-02-22 | 2003-11-25 | Fina Technology, Inc | Ziegler-Natta catalyst with metallocene for olefin polymerization |
US6432860B1 (en) | 1999-03-22 | 2002-08-13 | Fina Technology, Inc. | Supported metallocene catalysts |
US6339134B1 (en) | 1999-05-06 | 2002-01-15 | Univation Technologies, Llc | Polymerization process for producing easier processing polymers |
US6489426B1 (en) * | 1999-09-10 | 2002-12-03 | Chisso Corporation | Propylene base polymer and a polypropylene film using the same |
US6271323B1 (en) | 1999-10-28 | 2001-08-07 | Univation Technologies, Llc | Mixed catalyst compounds, catalyst systems and their use in a polymerization process |
US6346586B1 (en) | 1999-10-22 | 2002-02-12 | Univation Technologies, Llc | Method for preparing a supported catalyst system and its use in a polymerization process |
US6274684B1 (en) | 1999-10-22 | 2001-08-14 | Univation Technologies, Llc | Catalyst composition, method of polymerization, and polymer therefrom |
US6380328B1 (en) | 1999-12-10 | 2002-04-30 | Univation Technologies, Llc | Catalyst systems and their use in a polymerization process |
US6420580B1 (en) | 1999-11-05 | 2002-07-16 | Univation Technologies, Llc | Catalyst compositions and method of polymerization therewith |
US6340730B1 (en) | 1999-12-06 | 2002-01-22 | Univation Technologies, Llc | Multiple catalyst system |
JP2001302723A (ja) * | 2000-02-14 | 2001-10-31 | Idemitsu Petrochem Co Ltd | プロピレン系重合体及びフィルム成形体 |
US6359072B1 (en) | 2000-02-16 | 2002-03-19 | Univation Technologies, Llc | Polyethylene films having improved optical properties |
US6777366B2 (en) | 2001-02-13 | 2004-08-17 | Fina Technology, Inc. | Method for the preparation of metallocene catalysts |
US6777367B2 (en) | 2001-02-13 | 2004-08-17 | Fina Technology, Inc. | Method for the preparation of metallocene catalysts |
JP2002294012A (ja) * | 2001-03-28 | 2002-10-09 | Sumitomo Chem Co Ltd | プロピレン−エチレン−α−オレフィンランダム共重合体を用いたシュリンクフィルム |
US6916892B2 (en) | 2001-12-03 | 2005-07-12 | Fina Technology, Inc. | Method for transitioning between Ziegler-Natta and metallocene catalysts in a bulk loop reactor for the production of polypropylene |
ES2305371T3 (es) * | 2002-06-26 | 2008-11-01 | Avery Dennison Corporation | Peliculas polimericas orientadas en la direccion de mecanizado. |
CN101163738B (zh) * | 2005-04-21 | 2011-07-13 | 巴塞尔聚烯烃意大利有限责任公司 | 双轴取向丙烯聚合物膜 |
CN101215394B (zh) * | 2008-01-15 | 2011-01-12 | 福建正亿实业有限公司 | 可降解环保型聚丙烯泡沫塑料及其制备方法 |
JP5577137B2 (ja) * | 2010-04-05 | 2014-08-20 | 日本ポリプロ株式会社 | プロピレン系樹脂フィルムの製造方法 |
US10022941B2 (en) * | 2013-09-12 | 2018-07-17 | Inteplast Group Corporation | Multilayer matte biaxially oriented polypropylene film with ultra low seal initiation temperature |
WO2016064373A1 (en) * | 2014-10-20 | 2016-04-28 | Fina Technology, Inc. | Opaque pp/pla bopp films with broad processing window |
US9994692B2 (en) * | 2014-11-25 | 2018-06-12 | Milliken & Company | Process for extruding polypropylene |
-
2017
- 2017-10-27 EP EP17863914.2A patent/EP3532291A4/en active Pending
- 2017-10-27 MX MX2019004273A patent/MX2019004273A/es unknown
- 2017-10-27 WO PCT/US2017/058861 patent/WO2018081630A1/en unknown
- 2017-10-27 US US15/796,547 patent/US10683408B2/en active Active
- 2017-10-27 CN CN201780066189.6A patent/CN109890615B/zh active Active
- 2017-10-27 BR BR112019006896-1A patent/BR112019006896B1/pt active IP Right Grant
- 2017-10-27 KR KR1020197009950A patent/KR102411877B1/ko active IP Right Grant
- 2017-10-27 JP JP2019523081A patent/JP6967073B2/ja active Active
-
2020
- 2020-05-07 US US16/868,916 patent/US11359070B2/en active Active
Also Published As
Publication number | Publication date |
---|---|
WO2018081630A1 (en) | 2018-05-03 |
US10683408B2 (en) | 2020-06-16 |
CN109890615B (zh) | 2023-04-21 |
EP3532291A1 (en) | 2019-09-04 |
US11359070B2 (en) | 2022-06-14 |
JP2020500242A (ja) | 2020-01-09 |
KR102411877B1 (ko) | 2022-06-22 |
BR112019006896B1 (pt) | 2022-12-06 |
EP3532291A4 (en) | 2020-06-03 |
US20180118919A1 (en) | 2018-05-03 |
KR20190073364A (ko) | 2019-06-26 |
BR112019006896A2 (pt) | 2019-07-02 |
JP6967073B2 (ja) | 2021-11-17 |
US20200277468A1 (en) | 2020-09-03 |
CN109890615A (zh) | 2019-06-14 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
TWD163722S (zh) | 可攜式電子裝置之部分 | |
MX2019002558A (es) | Mezclas de polietileno nucleadas y su uso en articulos moldeados. | |
TWD179356S (zh) | 自動注射裝置之部分 | |
TWD172231S (zh) | 可攜式電子裝置之部分 | |
MX2016008317A (es) | Accesorio de herramienta con porcion de fijacion removible. | |
MX2017006124A (es) | Accesorios para el cabello y método para sujetar los mismos. | |
PH12016500002A1 (en) | Improved clamp for use with a cutting device | |
MX2019005081A (es) | Composicion de polipropileno espumado. | |
MX2019005477A (es) | Composicion de polipropileno para aplicaciones de formacion de espuma. | |
MX2018008411A (es) | Composicion de poliolefina con resistencia mejorada. | |
MX2017007675A (es) | Composiciones de polietileno con propiedades opticas mejoradas. | |
HUE051595T2 (hu) | Geopolimer adalékanyag alkalmazása nem brómozott égésgátlóval kombinációban polimer habokban | |
EA201700279A1 (ru) | Полипропилен с улучшенным внешним видом | |
TWD181123S (zh) | 可攜式電子裝置之部分 | |
MX2017005866A (es) | Material poroso de poliolefina. | |
MX2018012082A (es) | Compuestos tricarboxilicos como agentes coalescentes bajos en compuestos organicos volatiles (voc) y agentes plastificantes. | |
MX2018005150A (es) | Uso de nucleacion para mejorar la eflorescencia de resbalamiento en resinas de polipropileno con metaloceno. | |
MX2017007632A (es) | Composiciones de polietileno que tienen propiedades de bisagra viva. | |
MX2019004273A (es) | Uso de agentes para reducir la cristalinidad en polipropileno para aplicaciones de bopp. | |
GB2539615A (en) | Article moveable between two positions and a method of combining two or more of the same | |
MX2016011631A (es) | Composicion captadora de oxigeno para material plastico. | |
MY183648A (en) | Polypropylene compound with improved optical property and gel level | |
SA519402031B1 (ar) | تركيبة بولي أوليفين لرقاقة غير موجهة بخاصية حجز أكسجين محسنة | |
UA82656U (ru) | Порошковая смесь для диффузионного хромирования | |
MX368697B (es) | Pinza mejorada para utilizar con un dispositivo de corte. |