MX2011012289A - Articulo revestido con recubrimiento de baja-e que tiene una capa basada en estanato de zinc entre capas reflejantes de ir para moteado reducido y metodo correspondiente. - Google Patents

Articulo revestido con recubrimiento de baja-e que tiene una capa basada en estanato de zinc entre capas reflejantes de ir para moteado reducido y metodo correspondiente.

Info

Publication number
MX2011012289A
MX2011012289A MX2011012289A MX2011012289A MX2011012289A MX 2011012289 A MX2011012289 A MX 2011012289A MX 2011012289 A MX2011012289 A MX 2011012289A MX 2011012289 A MX2011012289 A MX 2011012289A MX 2011012289 A MX2011012289 A MX 2011012289A
Authority
MX
Mexico
Prior art keywords
based layer
coated article
zinc stannate
coating
low
Prior art date
Application number
MX2011012289A
Other languages
English (en)
Inventor
Richard Blacker
Jose Ferreira
Pierrot Pallotta
Muhammad Imran
Original Assignee
Ct Luxembourgeois Rech Verre
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ct Luxembourgeois Rech Verre filed Critical Ct Luxembourgeois Rech Verre
Publication of MX2011012289A publication Critical patent/MX2011012289A/es

Abstract

Se proporciona un artículo revestido el cual puede ser tratado con calor (por ejemplo, templado térmicamente) y/o curvado con calor en ciertos casos ejemplares. En ciertas modalidades ejemplares, un capa basada en estanato de zinc se proporciona entre una capa basada en óxido de estaño y una capa basada en nitruro de silicio, y se ha descubierto que esto reduce significativamente el daño de moteado indeseable con el tratamiento/curvatura con calor. Esto da por resultado una capacidad de curvatura significativamente mejorada del artículo revestido en aplicaciones tales como parabrisas de vehículos y similares.
MX2011012289A 2009-05-22 2010-05-10 Articulo revestido con recubrimiento de baja-e que tiene una capa basada en estanato de zinc entre capas reflejantes de ir para moteado reducido y metodo correspondiente. MX2011012289A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US12/453,836 US8281617B2 (en) 2009-05-22 2009-05-22 Coated article with low-E coating having zinc stannate based layer between IR reflecting layers for reduced mottling and corresponding method
PCT/US2010/001378 WO2010134957A2 (en) 2009-05-22 2010-05-10 Coated article with low-e coating having zinc stannate based layer between ir reflecting layers for reduced mottling and corresponding method

Publications (1)

Publication Number Publication Date
MX2011012289A true MX2011012289A (es) 2011-12-16

Family

ID=42542868

Family Applications (2)

Application Number Title Priority Date Filing Date
MX2011012289A MX2011012289A (es) 2009-05-22 2010-05-10 Articulo revestido con recubrimiento de baja-e que tiene una capa basada en estanato de zinc entre capas reflejantes de ir para moteado reducido y metodo correspondiente.
MX2014013483A MX351188B (es) 2009-05-22 2010-05-10 Articulo revestido con recubrimiento de baja-e que tiene una capa basada en estanato de zinc entre capas reflejantes de ir para moteado reducido y metodo correspondiente.

Family Applications After (1)

Application Number Title Priority Date Filing Date
MX2014013483A MX351188B (es) 2009-05-22 2010-05-10 Articulo revestido con recubrimiento de baja-e que tiene una capa basada en estanato de zinc entre capas reflejantes de ir para moteado reducido y metodo correspondiente.

Country Status (9)

Country Link
US (3) US8281617B2 (es)
EP (1) EP2432745B1 (es)
BR (1) BRPI1013000A2 (es)
ES (1) ES2744976T3 (es)
MX (2) MX2011012289A (es)
PL (1) PL2432745T3 (es)
RU (1) RU2523277C2 (es)
SA (1) SA110310427B1 (es)
WO (1) WO2010134957A2 (es)

Families Citing this family (33)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8281617B2 (en) 2009-05-22 2012-10-09 Centre Luxembourgeois De Recherches Pour Le Verre Et La Ceramique S.A. (C.R.V.C.) Coated article with low-E coating having zinc stannate based layer between IR reflecting layers for reduced mottling and corresponding method
US8834976B2 (en) 2010-02-26 2014-09-16 Guardian Industries Corp. Articles including anticondensation and/or low-E coatings and/or methods of making the same
US8939606B2 (en) 2010-02-26 2015-01-27 Guardian Industries Corp. Heatable lens for luminaires, and/or methods of making the same
US8559100B2 (en) * 2011-10-12 2013-10-15 Guardian Industries Corp. Coated article with low-E coating having absorbing layer over functional layer designed to increase outside reflectance
US9556066B2 (en) 2011-12-13 2017-01-31 Guardian Industries Corp. Insulating glass units with low-E and antireflective coatings, and/or methods of making the same
US9221713B2 (en) 2011-12-21 2015-12-29 Centre Luxembourgeois De Recherches Pour Le Verre Et La Ceramique S.A. (C.R.V.C.) Coated article with low-E coating having barrier layer system(s) including multiple dielectric layers, and/or methods of making the same
US9919959B2 (en) * 2012-05-31 2018-03-20 Guardian Glass, LLC Window with UV-treated low-E coating and method of making same
US9038419B2 (en) * 2012-06-08 2015-05-26 Centre Luxembourgeois De Recherches Pour Le Verre Et La Ceramique S.A. (C.R.V.C.) Method of making heat treated coated article using carbon based coating and protective film
CN102815873A (zh) * 2012-08-31 2012-12-12 东莞南玻工程玻璃有限公司 一种可夹层的、镀低辐射双银镀膜的玻璃制品
US9499438B2 (en) 2013-02-28 2016-11-22 Guardian Industries Corp. Window for attenuating RF and IR electromagnetic signals
US9206078B2 (en) * 2013-03-13 2015-12-08 Intermolecular, Inc. Barrier layers for silver reflective coatings and HPC workflows for rapid screening of materials for such barrier layers
US9309149B2 (en) * 2013-03-13 2016-04-12 Intermolecular, Inc. Systems, methods, and apparatus for production coatings of low-emissivity glass
US8940400B1 (en) * 2013-09-03 2015-01-27 Guardian Industries Corp. IG window unit including double silver coating having increased SHGC to U-value ratio, and corresponding coated article for use in IG window unit or other window
US9873633B2 (en) * 2013-11-20 2018-01-23 Guardian Europe S.A.R.L. Heat treatable coated article with low-E coating having zinc stannate based layer between IR reflecting layers and corresponding method
US20160266288A1 (en) * 2014-11-24 2016-09-15 Ut-Battelle, Llc Infrared-Blocking Nanocellulose Aerogel Windows
CN106186723B (zh) * 2016-08-31 2019-03-19 咸宁南玻节能玻璃有限公司 一种中透浅蓝色可弯钢三银低辐射镀膜玻璃及制备工艺
CN106186724B (zh) * 2016-08-31 2019-03-19 咸宁南玻节能玻璃有限公司 一种高透浅绿色可弯钢三银低辐射镀膜玻璃及制备方法
US10100202B2 (en) 2016-09-06 2018-10-16 Guardian Europe S.A.R.L. Coated article with IR reflecting layer and method of making same
RU2636995C1 (ru) * 2016-10-27 2017-11-29 Общество с ограниченной ответственностью "Пилкингтон Гласс" Изделие с гибридным энергосберегающим покрытием на стеклянной подложке
FR3059318B1 (fr) * 2016-11-30 2021-04-02 Saint Gobain Bombage de verre mince
TR201618236A2 (tr) * 2016-12-09 2017-02-21 Tuerkiye Sise Ve Cam Fabrikalari Anonim Sirketi Isil i̇şlenebi̇li̇r low-e katman i̇le kaplanmiş altlik
RU2648769C1 (ru) * 2017-02-16 2018-03-28 Общество с ограниченной ответственностью "Пилкингтон Гласс" Изделие бронзового цвета с гибридным энергосберегающим покрытием на стеклянной подложке
RU2642753C1 (ru) * 2017-02-16 2018-01-25 Общество с ограниченной ответственностью "Пилкингтон Гласс" Изделие синего цвета с гибридным энергосберегающим покрытием на стеклянной подложке
DE202018006739U1 (de) * 2017-02-20 2022-07-20 Corning Incorporated Geformte Glaslaminate
US11236003B2 (en) 2017-10-18 2022-02-01 Corning Incorporated Methods for controlling separation between glasses during co-sagging to reduce final shape mismatch therebetween
TR201718310A2 (tr) * 2017-11-20 2017-12-21 Tuerkiye Sise Ve Cam Fabrikalari Anonim Sirketi Isil i̇şlenebi̇li̇r bi̇r low-e kaplama ve üreti̇m yöntemi̇
CN109986934A (zh) * 2017-12-29 2019-07-09 法国圣戈班玻璃公司 带有二维码的车辆挡风玻璃及其制备工艺
CN108788634A (zh) * 2018-05-30 2018-11-13 四川丰科汽车部件有限公司 一种汽车护风罩生产工艺
US10301215B1 (en) * 2018-07-16 2019-05-28 Guardian Glass, LLC Low-E matchable coated articles having doped seed layer under silver, and corresponding methods
US10759693B2 (en) 2018-07-16 2020-09-01 Guardian Glass, LLC Low-E matchable coated articles having absorber film and corresponding methods
US10336651B1 (en) * 2018-07-16 2019-07-02 Guardian Glass, LLC Coated article with IR reflecting layer(s) and silicon zirconium oxynitride layer(s) and method of making same
US10822270B2 (en) 2018-08-01 2020-11-03 Guardian Glass, LLC Coated article including ultra-fast laser treated silver-inclusive layer in low-emissivity thin film coating, and/or method of making the same
RU2696748C1 (ru) * 2018-10-18 2019-08-05 Общество с ограниченной ответственностью "Пилкингтон Гласс" Изделие с гибридным сильнопоглощающим энергосберегающим покрытием на стеклянной подложке

Family Cites Families (40)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4806220A (en) 1986-12-29 1989-02-21 Ppg Industries, Inc. Method of making low emissivity film for high temperature processing
US5270517A (en) 1986-12-29 1993-12-14 Ppg Industries, Inc. Method for fabricating an electrically heatable coated transparency
US4898789A (en) 1988-04-04 1990-02-06 Ppg Industries, Inc. Low emissivity film for automotive heat load reduction
GB8900166D0 (en) 1989-01-05 1989-03-01 Glaverbel Glass coating
US5178980A (en) 1991-09-03 1993-01-12 Xerox Corporation Photoconductive imaging members with a fullerene compound
US5302449A (en) 1992-03-27 1994-04-12 Cardinal Ig Company High transmittance, low emissivity coatings for substrates
FR2701475B1 (fr) 1993-02-11 1995-03-31 Saint Gobain Vitrage Int Substrats en verre revêtus d'un empilement de couches minces, application à des vitrages à propriétés de réflexion dans l'infra-rouge et/ou à propriétés dans le domaine du rayonnement solaire.
US5688585A (en) 1993-08-05 1997-11-18 Guardian Industries Corp. Matchable, heat treatable, durable, IR-reflecting sputter-coated glasses and method of making same
CA2129488C (fr) 1993-08-12 2004-11-23 Olivier Guiselin Substrats transparents munis d'un empilement de couches minces, application aux vitrages d'isolation thermique et/ou de protection solaire
US5557462A (en) 1995-01-17 1996-09-17 Guardian Industries Corp. Dual silver layer Low-E glass coating system and insulating glass units made therefrom
GB9606281D0 (en) 1996-03-26 1996-05-29 Glaverbel Coated substrate for a transparent assembly with high selectivity
US5821001A (en) 1996-04-25 1998-10-13 Ppg Industries, Inc. Coated articles
FR2757151B1 (fr) 1996-12-12 1999-01-08 Saint Gobain Vitrage Vitrage comprenant un substrat muni d'un empilement de couches minces pour la protection solaire et/ou l'isolation thermique
US6495251B1 (en) * 1997-06-20 2002-12-17 Ppg Industries Ohio, Inc. Silicon oxynitride protective coatings
DE19726966C1 (de) 1997-06-25 1999-01-28 Flachglas Ag Verfahren zur Herstellung einer transparenten Silberschicht mit hoher spezifischer elektrischer Leitfähigkeit , Glasscheibe mit einem Dünnschichtsystem mit einer solchen Silberschicht und deren Verwendung
US6132881A (en) * 1997-09-16 2000-10-17 Guardian Industries Corp. High light transmission, low-E sputter coated layer systems and insulated glass units made therefrom
US6287685B1 (en) 1997-12-09 2001-09-11 3M Innovative Properties Company Rubber article capable of bonding to a pressure-sensitive adhesive and method of making
US6833194B1 (en) * 1998-05-12 2004-12-21 Ppg Industries Ohio, Inc. Protective layers for sputter coated article
JP3477148B2 (ja) * 1999-12-02 2003-12-10 カーディナル・シージー・カンパニー 耐曇り性透明フィルム積層体
US6576349B2 (en) 2000-07-10 2003-06-10 Guardian Industries Corp. Heat treatable low-E coated articles and methods of making same
US7344782B2 (en) 2000-07-10 2008-03-18 Guardian Industries Corp. Coated article with low-E coating including IR reflecting layer(s) and corresponding method
US6887575B2 (en) 2001-10-17 2005-05-03 Guardian Industries Corp. Heat treatable coated article with zinc oxide inclusive contact layer(s)
US6445503B1 (en) 2000-07-10 2002-09-03 Guardian Industries Corp. High durable, low-E, heat treatable layer coating system
US7462397B2 (en) 2000-07-10 2008-12-09 Guardian Industries Corp. Coated article with silicon nitride inclusive layer adjacent glass
US6625875B2 (en) 2001-03-26 2003-09-30 Centre Luxembourgeois De Recherches Pour Le Verre Et La Ceramique S.A. (C.R.V.C.) Method of attaching bus bars to a conductive coating for a heatable vehicle window
US6936347B2 (en) 2001-10-17 2005-08-30 Guardian Industries Corp. Coated article with high visible transmission and low emissivity
RU2342335C2 (ru) * 2002-05-03 2008-12-27 Ппг Индастриз Огайо, Инк. Подложка с теплорегулирующим покрытием для изоляционного стеклянного блока
US6632491B1 (en) 2002-05-21 2003-10-14 Guardian Industries Corp. IG window unit and method of making the same
US7140204B2 (en) 2002-06-28 2006-11-28 Guardian Industries Corp. Apparatus and method for bending glass using microwaves
US7217460B2 (en) 2004-03-11 2007-05-15 Guardian Industries Corp. Coated article with low-E coating including tin oxide interlayer
US7150916B2 (en) 2004-03-11 2006-12-19 Centre Luxembourg De Recherches Pour Le Verre Et La Ceramique S.A. (C.R.V.C.) Coated article with low-E coating including tin oxide interlayer for high bend applications
US20060029754A1 (en) * 2004-08-05 2006-02-09 Medwick Paul A Coated substrate with improved solar control properties
US20090258222A1 (en) * 2004-11-08 2009-10-15 Agc Flat Glass Europe S.A. Glazing panel
EP1828074B1 (fr) * 2004-11-08 2020-06-17 AGC Glass Europe Vitrage
US7473471B2 (en) * 2005-03-21 2009-01-06 Ppg Industries Ohio, Inc. Coating composition with solar properties
FR2898122B1 (fr) 2006-03-06 2008-12-05 Saint Gobain Substrat muni d'un empilement a proprietes thermiques
DE102006014796B4 (de) 2006-03-29 2009-04-09 Saint-Gobain Glass Deutschland Gmbh Thermisch hoch belastbares Low-E-Schichtsystem für transparente Substrate
ITRM20060181A1 (it) * 2006-03-31 2007-10-01 Pilkington Italia Spa Lastra di vetro rivestita
US8281617B2 (en) 2009-05-22 2012-10-09 Centre Luxembourgeois De Recherches Pour Le Verre Et La Ceramique S.A. (C.R.V.C.) Coated article with low-E coating having zinc stannate based layer between IR reflecting layers for reduced mottling and corresponding method
US8557391B2 (en) * 2011-02-24 2013-10-15 Guardian Industries Corp. Coated article including low-emissivity coating, insulating glass unit including coated article, and/or methods of making the same

Also Published As

Publication number Publication date
US9789750B2 (en) 2017-10-17
EP2432745B1 (en) 2019-06-26
WO2010134957A3 (en) 2011-04-07
US20130230698A1 (en) 2013-09-05
BRPI1013000A2 (pt) 2018-01-16
MX351188B (es) 2017-10-05
SA110310427B1 (ar) 2014-05-25
EP2432745A2 (en) 2012-03-28
WO2010134957A2 (en) 2010-11-25
ES2744976T3 (es) 2020-02-27
US8281617B2 (en) 2012-10-09
US8440310B2 (en) 2013-05-14
RU2523277C2 (ru) 2014-07-20
US20100295330A1 (en) 2010-11-25
RU2011152392A (ru) 2013-06-27
US20130020827A1 (en) 2013-01-24
PL2432745T3 (pl) 2019-12-31

Similar Documents

Publication Publication Date Title
MX351188B (es) Articulo revestido con recubrimiento de baja-e que tiene una capa basada en estanato de zinc entre capas reflejantes de ir para moteado reducido y metodo correspondiente.
WO2006020641A3 (en) Coated article with low-e coating including tin oxide interlayer for high bend applications
MX340550B (es) Articulo revestido con recubrimiento de baja-e que tiene una capa absorbente encima de una capa funcional diseñada para incrementar la reflectancia exterior.
MX2015002863A (es) Articulo revestido con recubrimiento de baja-e que tiene capas absorbentes para reflectancia baja del lado de la pelicula y transmision visible baja.
WO2015077064A3 (en) Heat treatable coated article with low-e coating having zinc stannate based layer between ir reflecting layers and corresponding method
MX2016002011A (es) Articulo revestido con recubrimiento de baja-e que tiene transmision visible baja el cual se puede utilizar en una unidad de ventana de ig para una apariencia gris.
MX2015002862A (es) Articulo revestido con recubrimiento de baja-e que tiene capas absorbentes para reflectancia baja del lado de la pelicula y transmision visible baja.
WO2006020753A3 (en) Coated article with low-e coating including tin oxide interlayer
IN2015DN04158A (es)
MX2015003868A (es) Articulo revestido con recubrimiento de baja-e que tiene transmision visible baja.
IN2015DN04159A (es)
PL1732858T3 (pl) Powlekany wyrób z tlenkiem cyny, azotkiem krzemu i/lub tlenkiem cynku pod warstwą odbijającą IR i odpowiedni sposób
MX2010002568A (es) Articulo recubierto con un recubrimiento low-e que tiene una capa absorbente dise?ada para un color azulado deseable en angulos de observacion fuera del eje.
PL2041040T3 (pl) Sposób wytwarzania wyrobu powlekanego do zastosowania w szybkim ogrzewaniu w celu zmniejszenia emisyjności i/lub rezystancji powierzchniowej i wytworzony produkt
WO2007127060A3 (en) Photocatalytic window and method of making same
MX2012012166A (es) Articulo revestido que tiene recubrimiento de baja-e con capa(s) absorbedora(s).
MX359621B (es) Artículo revestido que tiene recubrimiento de baja-e con capa(s) absorbedora(s).
WO2006020136A3 (en) Coated article having low-e coating with ion beam treated ir reflecting layer and corresponding method
TN2011000458A1 (en) Thin film coating and method of making of making the same
WO2014191485A3 (en) Solar control glazing
MX2015012033A (es) Revestimientos de vidrio templado y no templado que tienen caracteristicas opticas similares.
WO2008107113A9 (de) Beschichtungszusammensetzung
MY171957A (en) Low-emissivity and anti-solar glazing
MX2018015579A (es) Hoja de vidrio con esmalte que refleja radiacion infrarroja.
WO2018156837A3 (en) Coated article with low-e coating having doped silver ir reflecting layer(s)

Legal Events

Date Code Title Description
FG Grant or registration