MX2010013617A - Cristal con resistencia mejorada a balas. - Google Patents

Cristal con resistencia mejorada a balas.

Info

Publication number
MX2010013617A
MX2010013617A MX2010013617A MX2010013617A MX2010013617A MX 2010013617 A MX2010013617 A MX 2010013617A MX 2010013617 A MX2010013617 A MX 2010013617A MX 2010013617 A MX2010013617 A MX 2010013617A MX 2010013617 A MX2010013617 A MX 2010013617A
Authority
MX
Mexico
Prior art keywords
laminate
transparent
mosaic
bullet
thickness
Prior art date
Application number
MX2010013617A
Other languages
English (en)
Inventor
Francoise Mennechez
Stephane Leray
Vincent Pluen
Original Assignee
Saint Gobain
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Saint Gobain filed Critical Saint Gobain
Publication of MX2010013617A publication Critical patent/MX2010013617A/es

Abstract

La invención tiene por objetivo el uso de un laminado anti-balas y/o anti-esquirlas transparente, del cual al menos una parte del espesor se constituye de un mosaico comprendiendo al menos dos elementos constitutivos transparentes, para limitar el deterioro del laminado fuera de uno de dichos al menos dos elementos constitutivos que recibe un impacto; tal laminado de dimensiones superiores a aquellas máximas posibles de una placa de zafiro monocristalino, del cual al menos una parte del espesor se constituye de un mosaico al menos en parte transparente, y del cual al menos una de sus caras exteriores se constituye de una hoja transparente continua; un cristal de un edificio o de un vehículo de transporte comprendiendo esta laminado.

Description

CRISTAL CON RESISTENCIA MEJORADA A BALA La presente invención se trata stales resistentes a balas y/o esquirlas os proyectiles del mismo tipo.
Tales cristales consisten amblajes de hojas de vidrio y mate stico transparente, unidas unas a otras as intercaladas adhesivas del ivinilbutiral (PVB), poliuretano (PU ina epoxi .
Los niveles extremadamente elevado istencia a balas pueden alcanzarse entar el espesor de los laminados, rimento de la transmisión luminosa a tr cristal .
Ciertos materiales, en particular resistencia balística muy elevados, ibién de aumentar, limitan la propagación erioro (fisuras... ) del laminado en erior de su constituyente que recibe acto. En otros términos, el deterior iende más sobre una hoja monolítica de i erf ície y material que aquellas del mosa re el mosaico, el deterioro tiene tenden numerosos casos, a delimitarse stituyente («cristal») recibiendo ac t o .
Además, se ha constatado con sorp los espacios finos entre los cristales aico, generalmente ocupados por uni ablemente orgánicas, no constit amenté una debilidad desde el punto de v la resistencia balística. impacto. El laminado es aquí transpa el sentido que una parte al menos d erficie principal lo es.
Por otra parte, los inventores obs el empleo de una cerámica transpa mite alcanzar excelentes niveles istencia a balas y/o esquirlas para f cicas mínimas del compuesto, en ge inado, y las transmisiones lumi ibles máximas a través de él. Los tér nirnos» y «máximos» se refieren a eriales transparentes utilizados en icación, en particular el vidrio.
Por consecuencia, en una realiza ticular del uso de la invención, inado comprende una cerámica transpare a disminuir la masa surfácica del lamí eto un laminado transparente anti-balas i-esquirlas de dimensiones superiore ellas máximas posibles de una placa iro monocri s tal ino , caracterizado en qu os una parte de su espesor se constituy mosaico comprendiendo al menos dos elem stitutivos transparentes, y en que un os de sus caras exteriores se constituy hoja transparente continua.
Así se evita que dicho mosaico no f si mismo una cara exterior de laminado. cto, las irregularidades de superficie aico pueden ser una fuente de engrasami ás o menos largo plazo, o de colocació herramienta de limpieza tal piaparabrisas . En particular se evit rasamiento de las uniones orgánicas de t icularmente apropiada del lado dond era el impacto; - una dicha hoja transparente con de policarbonato o equivalente, ferencia del lado opuesto a aquel dest ecibir el impacto.
Dichos al menos dos elem stitutivos transparentes pueden olíticos, laminados, de materiales idént diferentes elegidos entre una cerámica rio, una vitrocerámica y/o un mate st i co .
La cerámica empleada puede ser, era preferida, monocris talina tal com iro (A1203) monocristalino , o policrista como alúmina policristalina , cerá ta, o de oxinitruro de Al (alón) , o icarbonato (PC), acrílico tal i (metacrilato de metilo) (PMMA) o una r ionómero .
El laminado de la invención tien esor comprendido entre 30 y 120 mm , ferencia entre 40 y 100 mm.
Se constituye de hojas/mos idas (os) y al menos en parte transpare cerámica, vidrio, vit rocerámica y/o mate stico, pegadas (os) unas (os) a otras (os) as adhesivas intercaladas tal como de P El espesor de estas (os) últimas (os ejemplo un múltiplo de 0.38 ablemente 0.76 mm .
El espesor de las hojas/mosaicos árnica se comprende entre 2 y 18 mm, es i El espesor de las hojas/mosaicos rocerámica puede comprenderse entre 5 El espesor de las hojas/mosa erial plástico se comprende entre 2 y 10 Los elementos constitutivos de aico, transparentes o no, se unen un os de preferencia por una unión orgán ejemplo por un cordón de PVB de 0.38 o Sus bordes presentan chafl ucidos lo más posible, u otras forma das o biseles permitiendo el ajuste brimiento de los bordes de dos eleme stitutivos cercanos. Sin embargo, fiere la forma derecha sin chaflán o flán reducido lo más posible desde un p uirlas, por ejemplo metálico; en el laminado se incorpora sentación penetrante de material anti- ant i - esquirlas recubriendo la periferi estructura antibalas y/o ant i - esqui ría inado, y destinada a recubrir también ición de montaje de este, el hueco e l se instala; para este aspecto se erencia a la patente EP 918 629 Bl .
La invención tiene igualmente etivo un cristal de un edificio o d ículo de transporte (terrestre, acuát eo, espacial) comprendiendo un lami crito arriba .
La invención se comprenderá mejor ta del siguiente ejemplo. m lo en la cual las cifras indican esores de los constituyentes, cristal b el vidrio blanco, el zafiro ocristalino , PVB designado pol ivini lbut poliuretano y PC pol i carbonato .
Cada uno de los espesores de zafir stituye de un mosaico de cuatro cristale mm x 100 mm , pegados unos a los otros dones de 0.76 mm de PVB.
Los bordes de estos cristales prese flañes inferiores a 0.5 mm .
Este laminado tiene un espesor d una masa surfácica de 210 kg/m2, y smisión luminosa visible superior a 70%.
Satisface la norma NATO - STANAG rth Atlantic Treaty Organization - Stan eement) de nivel 4, Las hojas de vidrio y sin cerámic o zafiro, tienen la misma resiste í st ica un espesor superior a 130 mm, a surfácica superior a 320 kg/m2 y nsmisión luminosa visible inferior a 50 caso a) de arriba, y un espesor superior a 100 mm , a surfácica superior a 250 kg/m2 y nsmisión luminosa visible inferior a 58 caso b) arriba.
Las uniones entre los cristales no debilidad de laminado, que resiste a paros sobre estas uniones como, si el mos ra reemplazado por una hoja monolític i ro .

Claims (1)

  1. REIVINDICACIONES 1. Uso de un laminado anti-balas i-esquirlas transparente, del cual al parte del espesor se constituye d aico comprendiendo al menos dos elem stitutivos transparentes, para limita erioro del laminado fuera de uno de d menos dos elementos constitutivos que r impacto, caracterizado en que al menos as exteriores del laminado se constituye hoja transparente continua, a maner tar que dicho mosaico no forme por si cara exterior de laminado. 2. Uso según la reivindicación acterizado en que dicho laminado comp cerámica transparente, para disminui a surfácica del laminado con resistenc mosaico comprendiendo al menos dos elem stitutivos transparentes, y en que un os de sus caras exteriores se constituy hoja transparente continua, a maner tar que dicho mosaico no forme por sí cara exterior de laminado. 4. Laminado según la reivindicació acterizado en que una dicha sparente continua es de vidrio con esor comprendido entre 2 y 6 ablemente de vidrio templado químicamente 5. Laminado según una de vindicaciones 3 o 4, caracterizado en dicha hoja transparente continua es icarbonato o equivalente. 6. Laminado según una de vindicaciones 3 a 5, caracterizado en stitutivo no transparen e, notablement erial anti-balas y/o ant i - e squi rlas . 8. Laminado según una de vindicaciones 3 a 7, caracterizado en qu orpora una presentación penetrante erial anti-balas y/o anti-esqu ubriendo la periferia de la estructura as y/o ant i - e squi rías de laminado, tinada a recubrir también, en posició taje de ese, el hueco en el cual se inst 9. Cristal de un edificio o d ículo de transporte comprendiendo inado según una de las reivindicaciones
MX2010013617A 2008-06-12 2009-06-11 Cristal con resistencia mejorada a balas. MX2010013617A (es)