MA49449A - Tôle d'acier revêtue de zinc présentant une soudabilité par points de haute résistance - Google Patents
Tôle d'acier revêtue de zinc présentant une soudabilité par points de haute résistanceInfo
- Publication number
- MA49449A MA49449A MA049449A MA49449A MA49449A MA 49449 A MA49449 A MA 49449A MA 049449 A MA049449 A MA 049449A MA 49449 A MA49449 A MA 49449A MA 49449 A MA49449 A MA 49449A
- Authority
- MA
- Morocco
- Prior art keywords
- steel sheet
- high strength
- coated steel
- spot weldability
- zinc coated
- Prior art date
Links
- HCHKCACWOHOZIP-UHFFFAOYSA-N Zinc Chemical compound [Zn] HCHKCACWOHOZIP-UHFFFAOYSA-N 0.000 title 1
- 239000011701 zinc Substances 0.000 title 1
- 229910052725 zinc Inorganic materials 0.000 title 1
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K11/00—Resistance welding; Severing by resistance heating
- B23K11/10—Spot welding; Stitch welding
- B23K11/11—Spot welding
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
- C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/50—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for welded joints
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K11/00—Resistance welding; Severing by resistance heating
- B23K11/10—Spot welding; Stitch welding
- B23K11/11—Spot welding
- B23K11/115—Spot welding by means of two electrodes placed opposite one another on both sides of the welded parts
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K11/00—Resistance welding; Severing by resistance heating
- B23K11/16—Resistance welding; Severing by resistance heating taking account of the properties of the material to be welded
- B23K11/163—Welding of coated materials
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K31/00—Processes relevant to this subclass, specially adapted for particular articles or purposes, but not covered by only one of the preceding main groups
- B23K31/12—Processes relevant to this subclass, specially adapted for particular articles or purposes, but not covered by only one of the preceding main groups relating to investigating the properties, e.g. the weldability, of materials
- B23K31/125—Weld quality monitoring
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K37/00—Auxiliary devices or processes, not specially adapted to a procedure covered by only one of the preceding main groups
- B23K37/04—Auxiliary devices or processes, not specially adapted to a procedure covered by only one of the preceding main groups for holding or positioning work
- B23K37/0408—Auxiliary devices or processes, not specially adapted to a procedure covered by only one of the preceding main groups for holding or positioning work for planar work
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/18—Hardening; Quenching with or without subsequent tempering
- C21D1/19—Hardening; Quenching with or without subsequent tempering by interrupted quenching
- C21D1/20—Isothermal quenching, e.g. bainitic hardening
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/18—Hardening; Quenching with or without subsequent tempering
- C21D1/19—Hardening; Quenching with or without subsequent tempering by interrupted quenching
- C21D1/22—Martempering
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/74—Methods of treatment in inert gas, controlled atmosphere, vacuum or pulverulent material
- C21D1/76—Adjusting the composition of the atmosphere
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/002—Heat treatment of ferrous alloys containing Cr
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/005—Heat treatment of ferrous alloys containing Mn
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/008—Heat treatment of ferrous alloys containing Si
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0236—Cold rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/20—Ferrous alloys, e.g. steel alloys containing chromium with copper
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/24—Ferrous alloys, e.g. steel alloys containing chromium with vanadium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/34—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/42—Ferrous alloys, e.g. steel alloys containing chromium with nickel with copper
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/44—Ferrous alloys, e.g. steel alloys containing chromium with nickel with molybdenum or tungsten
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/46—Ferrous alloys, e.g. steel alloys containing chromium with nickel with vanadium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/48—Ferrous alloys, e.g. steel alloys containing chromium with nickel with niobium or tantalum
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/50—Ferrous alloys, e.g. steel alloys containing chromium with nickel with titanium or zirconium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/54—Ferrous alloys, e.g. steel alloys containing chromium with nickel with boron
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/56—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.7% by weight of carbon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
- C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
- C23C2/0222—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating in a reactive atmosphere, e.g. oxidising or reducing atmosphere
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
- C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
- C23C2/0224—Two or more thermal pretreatments
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
- C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
- C23C2/06—Zinc or cadmium or alloys based thereon
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/26—After-treatment
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
- C23C2/36—Elongated material
- C23C2/40—Plates; Strips
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23F—NON-MECHANICAL REMOVAL OF METALLIC MATERIAL FROM SURFACE; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL; MULTI-STEP PROCESSES FOR SURFACE TREATMENT OF METALLIC MATERIAL INVOLVING AT LEAST ONE PROCESS PROVIDED FOR IN CLASS C23 AND AT LEAST ONE PROCESS COVERED BY SUBCLASS C21D OR C22F OR CLASS C25
- C23F17/00—Multi-step processes for surface treatment of metallic material involving at least one process provided for in class C23 and at least one process covered by subclass C21D or C22F or class C25
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of workpieces
- C25D5/34—Pretreatment of metallic surfaces to be electroplated
- C25D5/36—Pretreatment of metallic surfaces to be electroplated of iron or steel
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K2101/00—Articles made by soldering, welding or cutting
- B23K2101/006—Vehicles
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K2103/00—Materials to be soldered, welded or cut
- B23K2103/02—Iron or ferrous alloys
- B23K2103/04—Steel or steel alloys
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/001—Austenite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/002—Bainite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/008—Martensite
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D3/00—Electroplating: Baths therefor
- C25D3/02—Electroplating: Baths therefor from solutions
- C25D3/22—Electroplating: Baths therefor from solutions of zinc
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Materials Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Crystallography & Structural Chemistry (AREA)
- Quality & Reliability (AREA)
- Optics & Photonics (AREA)
- Electrochemistry (AREA)
- Heat Treatment Of Sheet Steel (AREA)
- Coating With Molten Metal (AREA)
- Heat Treatment Of Steel (AREA)
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/IB2017/000753 WO2018234839A1 (fr) | 2017-06-20 | 2017-06-20 | Tôle d'acier revêtue de zinc présentant une soudabilité par points de haute résistance |
PCT/IB2018/054306 WO2018234938A1 (fr) | 2017-06-20 | 2018-06-13 | Tôle d'acier revêtue de zinc présentant une soudabilité par points de haute résistance |
Publications (2)
Publication Number | Publication Date |
---|---|
MA49449A true MA49449A (fr) | 2020-04-29 |
MA49449B1 MA49449B1 (fr) | 2021-10-29 |
Family
ID=59366454
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MA054413A MA54413A (fr) | 2017-06-20 | 2018-06-13 | Procede de fabrication d'une soudure par points par resistance |
MA49449A MA49449B1 (fr) | 2017-06-20 | 2018-06-13 | Tôle d'acier revêtue de zinc présentant une soudabilité par points de haute résistance |
Family Applications Before (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MA054413A MA54413A (fr) | 2017-06-20 | 2018-06-13 | Procede de fabrication d'une soudure par points par resistance |
Country Status (16)
Country | Link |
---|---|
US (2) | US11649522B2 (fr) |
EP (2) | EP3642379B1 (fr) |
JP (1) | JP7142037B2 (fr) |
KR (1) | KR102306471B1 (fr) |
CN (1) | CN110892087B (fr) |
BR (2) | BR122023007818B8 (fr) |
CA (1) | CA3063835C (fr) |
ES (1) | ES2886223T3 (fr) |
HU (1) | HUE056466T2 (fr) |
MA (2) | MA54413A (fr) |
MX (1) | MX2019015511A (fr) |
PL (1) | PL3642379T3 (fr) |
RU (1) | RU2732714C1 (fr) |
UA (1) | UA125620C2 (fr) |
WO (2) | WO2018234839A1 (fr) |
ZA (1) | ZA201907399B (fr) |
Families Citing this family (21)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
MX2021009065A (es) | 2019-01-29 | 2021-08-18 | Jfe Steel Corp | Lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo de fabricacion para la misma. |
JP7059979B2 (ja) * | 2019-04-25 | 2022-04-26 | Jfeスチール株式会社 | スポット溶接部材 |
MX2022010400A (es) * | 2020-02-25 | 2022-09-07 | Kobe Steel Ltd | Metodo de soldadura a resistencia por puntos. |
JP7424932B2 (ja) * | 2020-07-22 | 2024-01-30 | 株式会社神戸製鋼所 | 抵抗スポット溶接方法 |
WO2021224662A1 (fr) * | 2020-05-07 | 2021-11-11 | Arcelormittal | Procédé de recuit d'acier |
EP4163404A1 (fr) * | 2020-06-08 | 2023-04-12 | Nippon Steel Corporation | Tôle d'acier, et procédé de fabrication de celle-ci |
EP4223901A4 (fr) * | 2020-09-30 | 2024-03-13 | Nippon Steel Corp | Tôle d'acier |
WO2022102218A1 (fr) | 2020-11-11 | 2022-05-19 | 日本製鉄株式会社 | Tôle d'acier et procédé pour sa production |
US20240060163A1 (en) * | 2020-12-23 | 2024-02-22 | Voestalpine Stahl Gmbh | A zinc or zinc-alloy coated strip or steel with improved zinc adhesion |
CN114686651A (zh) * | 2020-12-31 | 2022-07-01 | 通用汽车环球科技运作有限责任公司 | 具有降低的液态金属致脆(lme)敏感性的锌涂覆的钢 |
DE102021107330A1 (de) | 2021-03-24 | 2022-09-29 | Thyssenkrupp Steel Europe Ag | Beschichtetes Stahlflachprodukt und Verfahren zu seiner Herstellung |
CN113333986A (zh) * | 2021-05-31 | 2021-09-03 | 帝国理工创新有限公司 | 一种快速成形异种合金拼焊板部件的方法 |
WO2022264585A1 (fr) * | 2021-06-15 | 2022-12-22 | Jfeスチール株式会社 | Tôle d'acier galvanisé à et élément et procédé de fabrication associé |
EP4339308A1 (fr) * | 2021-06-15 | 2024-03-20 | JFE Steel Corporation | Tôle d'acier galvanisé à et élément et procédé de fabrication associé |
KR20220169497A (ko) * | 2021-06-18 | 2022-12-28 | 주식회사 포스코 | 굽힘 특성이 우수한 고항복비 초고강도 강판 및 그 제조방법 |
CN113414516B (zh) * | 2021-07-07 | 2022-09-09 | 北京科技大学 | 一种先进高强钢点焊焊接性的预判评价方法 |
JPWO2023054705A1 (fr) * | 2021-10-01 | 2023-04-06 | ||
CN117836457A (zh) * | 2021-10-01 | 2024-04-05 | 日本制铁株式会社 | 钢焊接构件 |
CN115156845A (zh) * | 2022-06-16 | 2022-10-11 | 唐山钢铁集团高强汽车板有限公司 | 一种防止镀层粘辊的镀锌热成形钢生产方法 |
CN116463547B (zh) * | 2022-06-30 | 2024-01-09 | 宝山钢铁股份有限公司 | 一种120公斤级超高强度镀锌钢板及其制造方法 |
CN116463546B (zh) * | 2022-06-30 | 2024-01-09 | 宝山钢铁股份有限公司 | 一种100公斤级超高强度镀锌钢板及其制造方法 |
Family Cites Families (25)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5857141A (en) | 1996-06-11 | 1999-01-05 | Illinois Tool Works Inc. | Metal-core weld wire for welding galvanized steels |
TW504519B (en) * | 1999-11-08 | 2002-10-01 | Kawasaki Steel Co | Hot dip galvanized steel plate excellent in balance of strength and ductility and in adhesiveness between steel and plating layer, and method for producing the same |
JP4173990B2 (ja) | 2002-12-27 | 2008-10-29 | 新日本製鐵株式会社 | 溶接用亜鉛系合金めっき鋼材およびその電縫鋼管 |
JP2005002415A (ja) | 2003-06-12 | 2005-01-06 | Nippon Steel Corp | 溶接性に優れた溶融Zn系めっき鋼材 |
JP4303655B2 (ja) | 2004-07-29 | 2009-07-29 | 新日本製鐵株式会社 | 溶接部の耐食性および耐亜鉛脆化割れ性に優れた亜鉛めっき鋼板の溶接方法 |
JP4741376B2 (ja) | 2005-01-31 | 2011-08-03 | 新日本製鐵株式会社 | 外観が良好な高強度合金化溶融亜鉛めっき鋼板及びその製造方法と製造設備 |
JP2006265671A (ja) | 2005-03-25 | 2006-10-05 | Nisshin Steel Co Ltd | 加工性及び耐溶融金属脆化割れ性に優れた合金化溶融亜鉛めっき高張力鋼板 |
WO2007086158A1 (fr) | 2006-01-30 | 2007-08-02 | Nippon Steel Corporation | Feuille d’acier zinguee au feu de grande resistance presentant une excellente aptitude au moulage et convenant particulierement au placage, feuille d’acier zinguee au feu de grande resistance alliee et procedes et appareils pour les fabriquer |
EP1832667A1 (fr) | 2006-03-07 | 2007-09-12 | ARCELOR France | Procédé de fabrication de tôles d'acier à très hautes caractéristiques de résistance, de ductilité et de tenacité, et tôles ainsi produites |
JP5223366B2 (ja) | 2007-02-08 | 2013-06-26 | Jfeスチール株式会社 | 成形性および溶接性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
EP1990431A1 (fr) | 2007-05-11 | 2008-11-12 | ArcelorMittal France | Procédé de fabrication de tôles d'acier laminées à froid et recuites à très haute résistance, et tôles ainsi produites |
EP2009128A1 (fr) | 2007-06-29 | 2008-12-31 | ArcelorMittal France | Acier au silicium galvanisé ou recuit après galvanisation |
EP2009129A1 (fr) | 2007-06-29 | 2008-12-31 | ArcelorMittal France | Processus de fabrication d'une plaque d'acier galvanisée par régulation DFF |
KR20140128458A (ko) * | 2009-03-31 | 2014-11-05 | 제이에프이 스틸 가부시키가이샤 | 고강도 용융 아연 도금 강판 및 그 제조 방법 |
CA2781815C (fr) | 2009-11-30 | 2015-04-14 | Nippon Steel Corporation | Tole d'acier a haute resistance presentant une excellente resistance a la fragilisation par l'hydrogene et une resistance a la traction maximum de 900 mpa ou plus, et procede de production de celle-ci |
JP5499664B2 (ja) | 2009-11-30 | 2014-05-21 | 新日鐵住金株式会社 | 疲労耐久性に優れた引張最大強度900MPa以上の高強度冷延鋼板及びその製造方法、並びに、高強度亜鉛めっき鋼板及びその製造方法 |
RU2470097C2 (ru) | 2010-09-07 | 2012-12-20 | Государственное образовательное учреждение высшего профессионального образования "Казанский государственный энергетический университет" (КГЭУ) | Способ изготовления фольги из чистого ферромагнитного металла и устройство для его осуществления (варианты) |
RU2544977C2 (ru) | 2010-11-26 | 2015-03-20 | ДжФЕ СТИЛ КОРПОРЕЙШН | СТАЛЬНОЙ ЛИСТ С Al-Zn ПОКРЫТИЕМ, НАНЕСЕННЫМ СПОСОБОМ ГОРЯЧЕГО ОКУНАНИЯ |
JP5936390B2 (ja) | 2011-02-28 | 2016-06-22 | 日新製鋼株式会社 | 溶融Zn−Al−Mg系めっき鋼板および製造方法 |
WO2012168564A1 (fr) | 2011-06-07 | 2012-12-13 | Arcelormittal Investigación Y Desarrollo Sl | Tôle d'acier laminée à froid et revêtue de zinc ou d'alliage de zinc, procédé de fabrication et utilisation d'une telle tôle |
KR101606658B1 (ko) | 2011-09-30 | 2016-03-25 | 신닛테츠스미킨 카부시키카이샤 | 아연 도금 강판 및 그 제조 방법 |
WO2014037627A1 (fr) * | 2012-09-06 | 2014-03-13 | Arcelormittal Investigación Y Desarrollo Sl | Procede de fabrication de pieces d'acier revêtues et durcies a la presse, et tôles prerevêtues permettant la fabrication de ces pieces |
JP5852690B2 (ja) * | 2013-04-26 | 2016-02-03 | 株式会社神戸製鋼所 | ホットスタンプ用合金化溶融亜鉛めっき鋼板 |
KR20150073005A (ko) | 2013-12-20 | 2015-06-30 | 주식회사 포스코 | 용접부 균열 저항성이 우수한 오스테나이트계 아연도금강판 및 이의 제조방법 |
MX2017000188A (es) | 2014-07-03 | 2017-05-01 | Arcelormittal | Metodo para producir una hoja de acero revestida o no revestida de resistencia ultra alta y hoja obtenida por dicho metodo. |
-
2017
- 2017-06-20 WO PCT/IB2017/000753 patent/WO2018234839A1/fr active Application Filing
-
2018
- 2018-06-13 MA MA054413A patent/MA54413A/fr unknown
- 2018-06-13 EP EP18735715.7A patent/EP3642379B1/fr active Active
- 2018-06-13 HU HUE18735715A patent/HUE056466T2/hu unknown
- 2018-06-13 RU RU2020101918A patent/RU2732714C1/ru active
- 2018-06-13 CA CA3063835A patent/CA3063835C/fr active Active
- 2018-06-13 CN CN201880037315.XA patent/CN110892087B/zh active Active
- 2018-06-13 EP EP21177833.7A patent/EP3892748A1/fr active Pending
- 2018-06-13 JP JP2019570524A patent/JP7142037B2/ja active Active
- 2018-06-13 UA UAA202000315A patent/UA125620C2/uk unknown
- 2018-06-13 KR KR1020197036977A patent/KR102306471B1/ko active IP Right Grant
- 2018-06-13 BR BR122023007818A patent/BR122023007818B8/pt active IP Right Grant
- 2018-06-13 ES ES18735715T patent/ES2886223T3/es active Active
- 2018-06-13 WO PCT/IB2018/054306 patent/WO2018234938A1/fr active Application Filing
- 2018-06-13 MA MA49449A patent/MA49449B1/fr unknown
- 2018-06-13 BR BR112019025057A patent/BR112019025057B8/pt active IP Right Grant
- 2018-06-13 PL PL18735715T patent/PL3642379T3/pl unknown
- 2018-06-13 MX MX2019015511A patent/MX2019015511A/es unknown
- 2018-06-13 US US16/614,734 patent/US11649522B2/en active Active
-
2019
- 2019-11-07 ZA ZA2019/07399A patent/ZA201907399B/en unknown
-
2023
- 2023-05-10 US US18/195,578 patent/US20230272502A1/en active Pending
Also Published As
Publication number | Publication date |
---|---|
JP7142037B2 (ja) | 2022-09-26 |
US20200181729A1 (en) | 2020-06-11 |
MA49449B1 (fr) | 2021-10-29 |
BR112019025057A2 (pt) | 2020-06-16 |
BR122023007818B8 (pt) | 2023-11-07 |
KR102306471B1 (ko) | 2021-09-30 |
EP3642379A1 (fr) | 2020-04-29 |
EP3642379B1 (fr) | 2021-08-04 |
MX2019015511A (es) | 2020-02-24 |
BR122023007818B1 (pt) | 2023-09-19 |
CA3063835C (fr) | 2022-03-01 |
MA54413A (fr) | 2021-10-13 |
US11649522B2 (en) | 2023-05-16 |
CA3063835A1 (fr) | 2018-12-27 |
EP3892748A1 (fr) | 2021-10-13 |
ES2886223T3 (es) | 2021-12-16 |
BR112019025057B8 (pt) | 2023-11-07 |
ZA201907399B (en) | 2021-09-29 |
WO2018234938A1 (fr) | 2018-12-27 |
UA125620C2 (uk) | 2022-05-04 |
CN110892087B (zh) | 2022-03-25 |
BR112019025057B1 (pt) | 2023-09-12 |
CN110892087A (zh) | 2020-03-17 |
HUE056466T2 (hu) | 2022-02-28 |
RU2732714C1 (ru) | 2020-09-22 |
JP2020524743A (ja) | 2020-08-20 |
WO2018234839A1 (fr) | 2018-12-27 |
PL3642379T3 (pl) | 2022-01-03 |
US20230272502A1 (en) | 2023-08-31 |
KR20200008142A (ko) | 2020-01-23 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
MA49449A (fr) | Tôle d'acier revêtue de zinc présentant une soudabilité par points de haute résistance | |
EP3536435A4 (fr) | Procédé de soudage par points par résistance d'une tôle d'acier à haute résistance zinguée ayant de bonnes propriétés de jonction | |
EP3901318A4 (fr) | Tôle d'acier galvanisée à haute résistance ayant une excellente soudabilité par point de résistance électrique et son procédé de fabrication | |
MA49778A (fr) | Procédé de production d'une tôle d'acier à haute résistance présentant une résistance, une ductilité et une aptitude au formage améliorées | |
EP3378965A4 (fr) | Tôle d'acier à haute résistance, galvanisée par immersion à chaud, ayant d'excellentes résistances au décollement au choc et à la corrosion d'une section ouvrée | |
HUE062069T2 (hu) | Hidegen hengerelt és hõkezelt acéllemez, ellenállás ponthegesztett kötés és eljárások elõállításukra | |
EP3561141A4 (fr) | Matériau en acier aluminisé par immersion à chaud doté d'une excellente résistance à la corrosion et une excellente aptitude au façonnage, et son procédé de fabrication | |
MA53357A (fr) | Procédé de production d'une tôle d'acier revêtue haute résistance présentant une résistance, une ductilité et une aptitude au formage améliorées | |
EP3901319A4 (fr) | Tôle d'acier revêtuee de zinc présentant une excellente aptitude à la soudure par points et son procédé de fabrication | |
EP2823959A4 (fr) | Plaque métallique revêtue pour véhicules, présentant une excellente aptitude au soudage par résistance, une excellente résistance à la corrosion et une excellente aptitude au moulage | |
MA49159A (fr) | Procédé de production d'une tôle d'acier à haute résistance présentant une résistance et une aptitude au formage améliorées et tôle d'acier à haute résistance ainsi obtenue | |
MA51084A (fr) | Une tôle d'acier revêtue haute résistance présentant une résistance et une aptitude au formage améliorées | |
EP3561155A4 (fr) | Acier plaqué d'alliage de zinc à soudabilité et résistance à la corrosion supérieures | |
MA49777A (fr) | Procédé de production d'une tôle d'acier à haute résistance présentant une résistance et une aptitude au formage améliorées et tôle ainsi obtenue | |
EP3561147A4 (fr) | Acier plaqué d'alliage de zinc ayant une excellente soudabilité et une excellente résistance à la corrosion | |
EP3239347A4 (fr) | Acier plaqué d'alliage de zinc présentant d'excellentes propriétés d'aptitude au soudage et de résistance à la corrosion d'unité de traitement et son procédé de fabrication | |
FR3017069B1 (fr) | Element de renfort en acier revetu par une composition adhesive a base d'aldehyde aromatique et de polyphenol | |
EP2952285A4 (fr) | FIL DE SOUDURE À L'ARC SUBMERGÉ POUR ACIER HAUTE RÉSISTANCE 2,25Cr-1Mo-V ET MÉTAL DE SOUDAGE | |
ZA201904658B (en) | Resistance spot welding method for joining zinc coated steel sheets | |
ZA202001589B (en) | A method for the manufacture of a coated steel sheet, two spot welded metal sheets and use thereof | |
EP3680054A4 (fr) | Procédé de soudage par friction-malaxage par points à double action | |
EP3000916A4 (fr) | Acier plaqué d'alliage d'al doté d'excellentes propriétés anticorrosion après application | |
EP3900866A4 (fr) | Élément de soudage par points | |
MA51268A (fr) | Substrat en d'acier revêtu par immersion à chaud | |
EP3733924A4 (fr) | Matériau d'acier plaqué d'alliage de zinc multicouche présentant une soudabilité par points et une résistance à la corrosion excellentes |