KR970001584A - Spray solution for manufacturing mini-spangle hot dip galvanized steel with excellent corrosion resistance and paintability - Google Patents
Spray solution for manufacturing mini-spangle hot dip galvanized steel with excellent corrosion resistance and paintability Download PDFInfo
- Publication number
- KR970001584A KR970001584A KR1019950016051A KR19950016051A KR970001584A KR 970001584 A KR970001584 A KR 970001584A KR 1019950016051 A KR1019950016051 A KR 1019950016051A KR 19950016051 A KR19950016051 A KR 19950016051A KR 970001584 A KR970001584 A KR 970001584A
- Authority
- KR
- South Korea
- Prior art keywords
- galvanized steel
- dip galvanized
- mini
- corrosion resistance
- spangle
- Prior art date
Abstract
본 발명은 자동차 또는 가전제품 등에 사용되는 미니스팡글 용융아연 도금강판 제조용 분사용액에 관한 것이며, 그 목적은 내식성 및 도장성이 우수한 미니스팡글 용융아연 도금강판 제조용 분사용액을 제공함에 있다.The present invention relates to a spray solution for producing a mini-spangle hot-dip galvanized steel sheet used in automobiles or home appliances, and its object is to provide a spray solution for producing a mini-spangle hot-dip galvanized steel sheet excellent in corrosion resistance and paintability.
상기 목적달성을 위한 본 발명은 미니스팡글 용융아연 도금강판을 제조하기 위한 분사용액에 있어서, 인산나트륨 : 1∼5wt%와 수용성 콜로이달 실리카 : 0.1∼1wt%로 조성되는 내식성이 우수한 미니스팡글 용융아연 도금강판 제조용 분사용액에 관한 것을 그 요지로 한다.The present invention for achieving the above object is a mini-spangle with excellent corrosion resistance in the injection solution for producing a mini-spangle hot-dip galvanized steel sheet, sodium phosphate: 1 to 5wt% and water-soluble colloidal silica: 0.1 to 1wt% The gist of the spraying solution for the production of hot-dip galvanized steel sheet is the main point.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음Since this is an open matter, no full text was included.
Claims (1)