KR960004255A - 열선반사 유리 및 그 제조방법 - Google Patents

열선반사 유리 및 그 제조방법 Download PDF

Info

Publication number
KR960004255A
KR960004255A KR1019940017364A KR19940017364A KR960004255A KR 960004255 A KR960004255 A KR 960004255A KR 1019940017364 A KR1019940017364 A KR 1019940017364A KR 19940017364 A KR19940017364 A KR 19940017364A KR 960004255 A KR960004255 A KR 960004255A
Authority
KR
South Korea
Prior art keywords
metal
layer
forming
heat
metal layer
Prior art date
Application number
KR1019940017364A
Other languages
English (en)
Other versions
KR970000383B1 (ko
Inventor
이정훈
유병석
김의수
Original Assignee
최영중
한국유리공업 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 최영중, 한국유리공업 주식회사 filed Critical 최영중
Priority to KR1019940017364A priority Critical patent/KR970000383B1/ko
Publication of KR960004255A publication Critical patent/KR960004255A/ko
Application granted granted Critical
Publication of KR970000383B1 publication Critical patent/KR970000383B1/ko

Abstract

내열성 및 내구성이 향상된 열선반사 유리 및 그 제조방법이 개시된다.
본 발명의 열선반사 유리는, 유리기판(20)상에 제1질화 금속층(22), 제1확산방지용 금속층(230, 열선반사 금속층(24), 제2질화 금속층(26)이 차례로 형성되어 이루어진다. 또한 상기 열선반사 금속층(24)과 제2질화 금속층(26) 사이에 제2확산방지용 금속층(25)이 형성될 수도 있다.
본 발명의 다른 실시예로서 유리기판(30)상에 제1산화 금속층(32), 제1질화 금속층(33), 열선반사 금속층(34), 제2질화 금속층(35), 제2산화 금속층(36)이 차례로 형성되어 이루어질 수도 있다.

Description

열선반사 유리 및 그 제조방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 종래의 3층 구조의 연질 코팅유리를 나타내는 단면도이고,
제2도는 열선반사 금속층의 보호층으로서 금속층을 사용한 종래의 열처리 가능한 열선반사 유리의 단면도이고,
제3도는 본 발명의 제1실시예에 따른 열선반사 유리의 단면도이다.

Claims (31)

  1. 유리기판(20)상에 제1질화 금속층(22), 제1확산방지용 금속층(23), 열선반사 금속층(24), 제2질화 금속층(26)이 차례로 형성되어 이루어진 열선반사 유리.
  2. 제1항에 있어서, 상기 열선반사 금속층(24)과 제2질화 금속층(26) 사이에 제2확산방지용 금속층(25)이 더욱 형성되어 이루어진 것을 특징으로 하는 열선반사 유리.
  3. 제1항 또는 제2항중 어느 한 항에 있어서, 상기 유리기판(20)은 투명한 무기질 유리 또는 유기질 유리인 것을 특징으로 하는 열선반사 유리.
  4. 제1항 또는 제2항중 어느 한 항에 있어서, 상기 제1, 제2질화 금속층(22), (26)은 가시광선 영역에서 투명한 것임을 특징으로 하는 열선반사 유리.
  5. 제4항에 있어서, 상기 제1질화 금속층(22)은 질화알루미늄(AIN) 또는 질화규소(SixNy: x는 1~3 사이의 값, y는 1~4 사이의 값)로 형성되어 있으며; 상기 제2질화 금속층(26)은 질화알루미늄(AIN) 또는 질화규소(SixNy: x는 1~3 사이의 값, y는 1~4 사이의 값)로 형성되어 이루어진 것을 특징으로 하는 열선반사 유리.
  6. 제1항에 있어서, 상기 제1확산방지용 금속층(23)은 알루미늄(Al), 크롬(Cr), 주석(Sn), 중석(W), 규소(Si), 티타늄(Ti), 니켈(Ni), 아연(Zn), 아연-알루미늄(ZnAl), 아연-주석(ZnSn)으로 이루어진 군으로부터 선택된 어느 하나의 금속으로 형성되어 있는 것을 특징으로 하는 열선반사 유리.
  7. 제2항에 있어서, 상기 제2확산방지용 금속층(25)은 알루미늄(Al), 크롬(Cr), 주석(Sn), 중석(W), 규소(Si), 티타늄(Ti), 니켈(Ni), 아연(Zn), 아연-알루미늄(ZnAl), 아연-주석(ZnSn)으로 이루어진 군으로부터 선택된 어느 하나의 금속으로 형성되어 있는 것을 특징으로 하는 열선반사 유리.
  8. 제1항 또는 제2항중의 어느 한 항에 있어서, 상기 열선반사 금속층은 은(Ag), 금(Au), 구리(Cu)로 이루어진 군으로부터 선택된 어느 하나로 형성되어 있는 것을 특징으로 하는 열선반사 유리.
  9. 유리기판(20)상에 제1질화 금속층(22), 열선반사 금속층(24), 제2확산방지용 금속층(25), 제2질화 금속층(26)이 차례로 형성되어 이루어진 열선반사 유리.
  10. 제9항에 있어서, 상기 제1, 제2질화 금속층(22), (26)은 가시광선 영역에서 투명한 것임을 특징으로 하는 열선반사 유리.
  11. 제10항에 있어서, 상기 제1질화 금속층(22)은 질화알루미늄(AIN) 또는 질화규소(SixNy: x는 1~3 사이의 값, y는 1~4 사이의 값)로 형성되어 있으며; 상기 제2질화 금속층(26)은 질화알루미늄(AIN) 또는 질화규소(SixNy: x는 1~3 사이의 값, y는 1~4 사이의 값)로 형성되어 이루어진 것을 특징으로 하는 열선반사 유리.
  12. 제9항에 있어서, 상기 제2확산방지용 금속층(25)은 알루미늄(Al), 크롬(Cr), 주석(Sn), 중석(W), 규소(Si), 티타늄(Ti), 니켈(Ni), 아연(Zn), 아연-알루미늄(ZnAl), 아연-주석(ZnSn)으로 이루어진 군으로부터 선택된 어느 하나의 금속으로 형성되어 있는 것을 특징으로 하는 열선반사 유리.
  13. 제9항에 있어서, 상기 열선반사 금속층(24)은 은(Ag), 금(Au), 구리(Cu)로 이루어진 군으로부터 선택된 어느 하나로 형성되어 있는 것을 특징으로 하는 열선반사 유리.
  14. 유리기판(30)상에 제1산화 금속층(32), 제1질화 금속층(33), 열선반사 금속층(34), 제2질화 금속층(35), 제2산화 금속층(36)이 차례로 형성되어 이루어진 열선반사 유리.
  15. 제14항에 있어서, 상기 제1, 제2산화 금속층(32), (36)은 굴절률이 1.45~2.5범위내이고, 가시광선 영역에서 투명한 것임을 특징으로 하는 열선반사 유리.
  16. 제15항에 있어서, 상기 제1, 제2산화 금속층(32), (36)은 산화주석(SnOx:x는 1~2 사이의 값), 이산화 규소(SiO2), 산화알루미늄(Al2O3), 산화아연(ZnO), 이산화티타늄(TiO2), 아연주석산화물(ZnSnOx), 아연알루미늄산화물(ZnAlOx), 인듐주석산화물(InSnOx)로 이루어진 군으로부터 선택된 어느 하나로 형성되는 것을 특징으로 하는 열선반사 유리.
  17. 제14항 내지 제16항중의 어느 한 항에 있어서, 상기 제1, 제2질화 금속층(33), (35)은 가시광선 영역에서 투명한 것임을 특징으로 하는 열선반사 유리.
  18. 제17항에 있어서, 상기 제1질화 금속층(33)은 질화알루미늄(AIN) 또는 질화규소(SixNy: x는 1~3 사이의 값, y는 1~4 사이의 값)로 형성되어 있으며; 상기 제2질화 금속층(35)은 질화알루미늄(AIN) 또는 질화규소(SixNy: x는 1~3 사이의 값, y는 1~4 사이의 값)로 형성되어 이루어진 것을 특징으로 하는 열선반사 유리.
  19. 제14항에 있어서, 상기 열선반사 금속층(34)은 은(Ag), 금(Au), 구리(Cu)로 이루어진 군으로부터 선택된 어느 하나로 형성되어 있는 것을 특징으로 하는 열선반사 유리.
  20. 유리기판(30)상에 제1산화 금속층(32), 제1질화 금속층(33), 열선반사 금속층(34), 상기 열선반사 금속층 보호층 금속층(37), 제2산화 금속층(36)이 차례로 형성되어 이루어진 열선반사 유리.
  21. 제20항에 있어서, 상기 제1, 제2산화 금속층(32), (36)은 산화주석(SnOx:x는 1~2 사이의 값), 이산화 규소(SiO2), 산화알루미늄(Al2O3), 산화아연(ZnO), 이산화티타늄(TiO2), 아연주석산화물(ZnSnOx), 아연알루미늄산화물(ZnAlOx), 인듐주석산화물(InSnOx)로 이루어진 군으로부터 선택된 어느 하나로 형성되는 것을 특징으로 하는 열선반사 유리.
  22. 제20항 또는 제21항중의 어느 한 항에 있어서, 상기 제1질화 금속층(33)은 지로하알루미늄(AIN) 또는 질화규소(SixNy: x는 1~3 사이의 값, y는 1~4 사이의 값)로 형성되어 이루어진 것을 특징으로 하는 열선반사 유리.
  23. 제20항에 있어서, 상기 열선반사 금속층(34)은 보호용 금속층(37)은 Al, Ta, W, Ni, Fe, Cr, Sn, Ti, Si로 이루어진 군으로부터 선택된 어느 하나의 금속으로 형성되는 것을 특징으로 하는 열선반사 유리.
  24. 유리기판(30)상에 제1산화 금속층(32), 열선반사 금속층 보호용 금속층(38), 열선반사 금속층(34), 제2질화 금속층(35), 제2산화 금속층(36)이 차례로 형성되어 이루어진 것을 특징으로 하는 열선반사 유리.
  25. 제24항에 있어서, 상기 제1, 2산화 금속층(32), (36)은 산화주석(SnOx:x는 1~2 사이의 값), 이산화 규소(SiO2), 산화알루미늄(Al2O3), 산화아연(ZnO), 이산화티타늄(TiO2), 아연주석산화물(ZnSnOx), 아연알루미늄산화물(ZnAlOx), 인듐주석산화물(InSnOx)로 이루어고; 상기 제2질화 금속층(35)은 질화알루미늄(AIN), 또는 질화규소(SixNy: x는 1~3 사이의 값, y는 1~4 사이의 값)로 형성되어 이루어진 것을 특징으로 하는 열선반사 유리.
  26. 유리기판(20)을 스퍼터링장치의 코팅실에 넣은 후 진공을 형성하는 단계; 질소분위기 하에서 금속타켓을 스퍼터링하여 상기 유리기판(20)상에 제1질화 금속층(22)을 형성하는 단계; 아르곤분위기 하에서 상기 제1질화 금속층(22)상에 제1확산방지용 금속층(23)을 형성하는 단계;; 아르곤 분위기 하에서 상기 제1확산방지용 금속층(23)상에 열선반사 금속층(24)을 형성하는 단계; 및 질소분위기 하에서 상기 열선반사 금속층(24)상에 제2질화 금속층(26)을 형성하는 단계를 구비하여 이루어진 것을 특징으로 하는 열선반사 유리의 제조방법.
  27. 제26항에 있어서, 상기 열선반사 금속층(24) 형성단계와 제2질화 금속층(26) 형성단계 사이에, 이르곤분위기 하에서 상기 열선반사 금속층(24)상에 제2확산방지용 금속층(25)을 형성하는 단계를 더욱 포함하는 것을 특징으로 하는 열선반사 유리의 제조방법.
  28. 유리기판(20)을 스퍼터링장치의 코팅실에 넣은 후 진공을 형성하는 단계; 질소분위기 하에서 금속타켓을 스퍼터링하여 상기 유리기판(20)상에 제1질화 금속층(22)을 형성하는 단계; 아르곤분위기 하에서 상기 제1질화 금속층(22)상에 열선반사 금속층(24)을 형성하는 단계; 아르곤분위기 하에서 상기 열선반사 금속층(24)상에 제2확산방지용 금속층(25)을 형성하는 단계; 및 질소분위기 하에서 상기 제2확산방지용 금속층(25)상에 제2질화 금속층(26)을 형성하는 단계를 구비하여 이루어진 열선반사 유리의 제조방법.
  29. 유리기판(30)을 스퍼터링장치의 코팅실에 넣은 후 진공을 형성하는 단계; 산소분위기 하에서 상기 유리기판(30)상에 제1산화 금속층(32)을 형성하는 단계; 질소분위기 하에서 상기 제1산화 금속층(32)상에 제1질화 금속층(33)을 형성하는 단계; 아르곤분위기 하에서 상기 제1질화 금속층(33)상에 열선반사 금속층(34)을 형성하는 단계; 질소분위기 하에서 상기 열선반사 금속층(34)상에 제2질화 금속층(35)을 형성하는 단계; 및 산소분위기 하에서 상기 제2질화 금속층(35)상에 제2산화 금속층(36)을 형성하는 단계를 구비하여 이루어진 열선반사 유리의 제조방법.
  30. 유리기판(30)을 스퍼터링장치의 코팅실에 넣은 후 진공을 형성하는 단계; 산소분위기 하에서 상기 유리기판(30)상에 제1산화 금속층(32)을 형성하는 단계; 질소분위기 하에서 상기 제1산화 금속층(32)상에 제1질화 금속층(33)을 형성하는 단계; 아르곤분위기 하에서 상기 제1질화 금속층(33)상에 열선방사 금속층(34)을 형성하는 단계; 아르곤 분위기 하에서 상기 열선반사 금속층(34)상에 상기 열선반사 금속층(34) 보호용 금속층(37)을 형성하는 단계; 및 산소분위기 하에서 상기 보호층 금속층(37)상에 제2산화 금속층(36)을 형성하는 단계를 구비하여 이루어진 것을 특징으로 하는 열선반사 유리의 제조방법.
  31. 유리기판(30)을 스퍼터링장치의 코팅실에 넣은 후 진공을 형성하는 단계; 산소분위기 하에서 상기 유리기판(30)상에 제1산화 금속층(32)을 형성하는 단계; 아르곤분위기 하에서 상기 제1지로하 금속층(32)상에 열선반사 금속층(34) 보호용 금속층(38)을 형성하는 단계; 아르곤분위기 하에서 상기 보호용 금속층(38)상에 열선반사 금속층(34)을 형성하는 단계; 질소분위기 하에서 상기 열선반사 금속층(34)상에 제2질화 금속층(35)을 형성하는 단계; 및 산소분위기 하에서 상기 제2질화 금속층(35)상에 제2산화 금속층(36)을 형성하는 단계를 구비하여 이루어진 것을 특징으로 하는 열선반사 유리의 제조방법.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019940017364A 1994-07-19 1994-07-19 열선반사 유리 및 그 제조방법 KR970000383B1 (ko)