KR950700448A - 웨이퍼보드의 페놀 포름알데히드 증기 압착(Phenol formaldehyde steam pressing of waferboard) - Google Patents

웨이퍼보드의 페놀 포름알데히드 증기 압착(Phenol formaldehyde steam pressing of waferboard)

Info

Publication number
KR950700448A
KR950700448A KR1019940702978A KR19940702978A KR950700448A KR 950700448 A KR950700448 A KR 950700448A KR 1019940702978 A KR1019940702978 A KR 1019940702978A KR 19940702978 A KR19940702978 A KR 19940702978A KR 950700448 A KR950700448 A KR 950700448A
Authority
KR
South Korea
Prior art keywords
resin
moisture content
less based
dry weight
oven dry
Prior art date
Application number
KR1019940702978A
Other languages
English (en)
Inventor
통 크리스토퍼 림 야우
치우 수이-퉁
Original Assignee
티이 에이취레니그
투루스 조이스트 맥밀턴
원본미기재
보오덴 인코포레이팃드
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 티이 에이취레니그, 투루스 조이스트 맥밀턴, 원본미기재, 보오덴 인코포레이팃드 filed Critical 티이 에이취레니그
Publication of KR950700448A publication Critical patent/KR950700448A/ko

Abstract

본 발명은 먼저 액체 페놀 포름 알데히드 수지(12)를 웨이퍼(10) 표면에 가한 후 분말 페놀 포름 알데히드 수지(14)를 가하고 나서 레이업(16)을 형성하고 증기 압착 기술(18)을 사용하여 승온 및 승압에서 압착시켜 레이업을 보드로 압밀시키고 페놀 포름 알데히드 수지를 고화시키는 방법에 관한 것이다.

Description

웨이퍼보드의 페놀 포름알데히드 증기 압착(Phenol formaldehyde steam pressing of waferboard)
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제 1 도는 본 발명 방법의 도식적 예시이다.

Claims (29)

  1. 미립 리그노셀룰로스 물질을 건조시키고, 적어도 35중량%의 수지 고체 함량을 갖는 액체 페놀 포름 알데히드 수지를 상기 물질 표면상에 가하고, 상기 액체 수지가 그에 가해진 상기 물질로부터 레이업을 형성하고, 상기 건조와 상기 액체 수지의 적용을 병행하여 상기 레이업이 상기 물질의 오븐 건조 중량을 기준하여 7% 이하의 수분 함량을 갖도록 보증하고, 상기 수지를 고화시키거나, 경화시키고 상기 레이업을 상기 생산품으로 압밀시키기 충분한 승온 및 승압에서 증기 압착시키는 것으로 구성되는, 미립 리그노셀룰로스 물질로부터 적어도 85psi의 평균 내부 결합 강도를 갖는 압밀된 생산품을 생산하는 방법.
  2. 제 1 항에 있어서, 상기 액체 수지의 적용 후 상기 매트의 형성전에 건조 페놀 포름알데히드 수지를 또한 상기 물질에 가하는 것을 포함하는 방법.
  3. 제 2 항에 있어서, 상기 액체 수지는 적어도 45중량%의 고체 함량을 갖는 방법.
  4. 제 2 항에 있어서, 상기 액체 페놀 포름알데히드 수지의 상기 수지 고체 함량은 상기 물질에 가해진 전체 수지의 25-75중량%로 구성되는 방법.
  5. 제 3 항에 있어서, 상기 액체 페놀 포름알데히드 수지의 상기 수지 고체 함량은 상기 물질에 가해진 전체 수지의 25-75중량%로 구성되는 방법.
  6. 제 2 항에 있어서, 상기 액체 수지는 페놀 포름알데히드 레졸수지로 구성되는 방법.
  7. 제 3 항에 있어서, 상기 액체 수지는 페놀 포름알데히드 레졸수지로 구성되는 방법.
  8. 제 4 항에 있어서, 상기 액체 수지는 페놀 포름알데히드 레졸수지로 구성되는 방법.
  9. 제 5 항에 있어서, 상기 액체 수지는 페놀 포름알데히드 레졸수지로 구성되는 방법.
  10. 제 2 항에 있어서, 상기 수분 함량은 물질의 오븐 건조 중량을 기준하여 약 6% 이하인 방법.
  11. 제 3 항에 있어서, 상기 수분 함량은 물질의 오븐 건조 중량을 기준하여 약 6% 이하인 방법.
  12. 제 4 항에 있어서, 상기 오븐 수분 함량은 물질의 오븐 건조 중량을 기준하여 약 6% 이하인 방법.
  13. 제 5 항에 있어서, 상기 오븐 수분 함량은 물질의 오븐 건조 중량을 기준하여 약 6% 이하인 방법.
  14. 제 6 항에 있어서, 상기 오븐 수분 함량은 물질의 오븐 건조 중량을 기준하여 약 6% 이하인 방법.
  15. 제 7 항에 있어서, 상기 오븐 수분 함량은 물질의 오븐 건조 중량을 기준하여 약 6% 이하인 방법.
  16. 제 8 항에 있어서, 상기 오븐 수분 함량은 물질의 오븐 건조 중량을 기준하여 약 6% 이하인 방법.
  17. 제 9 항에 있어서, 상기 오븐 수분 함량은 물질의 오븐 건조 중량을 기준하여 약 6% 이하인 방법.
  18. 제 2 항에 있어서, 상기 수분 함량은 물질의 오븐 건조 중량을 기준하여 5% 이하인 방법.
  19. 제 3 항에 있어서, 상기 수분 함량은 물질의 오븐 건조 중량을 기준하여 5% 이하인 방법.
  20. 제 4 항에 있어서, 상기 수분 함량은 물질의 오븐 건조 중량을 기준하여 5% 이하인 방법.
  21. 제 5 항에 있어서, 상기 수분 함량은 물질의 오븐 건조 중량을 기준하여 5% 이하인 방법.
  22. 제 6 항에 있어서, 상기 수분 함량은 물질의 오븐 건조 중량을 기준하여 5% 이하인 방법.
  23. 제 7 항에 있어서, 상기 수분 함량은 물질의 오븐 건조 중량을 기준하여 5% 이하인 방법.
  24. 제 8 항에 있어서, 상기 수분 함량은 물질의 오븐 건조 중량을 기준하여 5% 이하인 방법.
  25. 제 9 항에 있어서, 상기 수분 함량은 물질의 오븐 건조 중량을 기준하여 5% 이하인 방법.
  26. 제 2 항에 있어서, 액체 수지를 리그노셀룰로스 물질에 가한 후 상기 물질에 건조 수지를 가하는 방법.
  27. 제 2 항에 있어서, 건조 수지가 점착되도록 할 만큼 리그노셀룰로스가 충분히 점착성이 된 다음 건조수지를 리그노셀룰로스 물질에 가한 후 상기 액체 수지를 가하는 방법.
  28. 제 2 항에 있어서, 건조 수지와 액체 수지를 동시에 리그노셀룰로스 물질에 가하는 방법.
  29. 제27항에 있어서, 리그노셀룰로스 물질에 왁스를 가하여 점착성이 되게 한 방법.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019940702978A 1992-02-25 1993-02-25 웨이퍼보드의 페놀 포름알데히드 증기 압착(Phenol formaldehyde steam pressing of waferboard) KR950700448A (ko)