KR950008178B1 - The preparation method of transferring sheet for printing - Google Patents
The preparation method of transferring sheet for printing Download PDFInfo
- Publication number
- KR950008178B1 KR950008178B1 KR1019920015975A KR920015975A KR950008178B1 KR 950008178 B1 KR950008178 B1 KR 950008178B1 KR 1019920015975 A KR1019920015975 A KR 1019920015975A KR 920015975 A KR920015975 A KR 920015975A KR 950008178 B1 KR950008178 B1 KR 950008178B1
- Authority
- KR
- South Korea
- Prior art keywords
- printing
- layer
- transfer sheet
- coating
- pattern
- Prior art date
Abstract
내용 없음.No content.
Description
제1도는 본 발명의 프린트용 전자시트의 제조방법의 블록도에 의한 플로챠트 1.1 is a flow chart 1 according to a block diagram of a manufacturing method of a printed electronic sheet of the present invention.
제2도는 본 발명의 프린트용 전자시트의 제조방법의 블록도에 의한 플로챠트 2.2 is a flowchart according to a block diagram of a method for manufacturing an electronic sheet for printing of the present invention.
제3도는 본 발명의 프린트용 전자시트의 제조방법의 블록도에 의한 플로챠트 3.3 is a flowchart according to a block diagram of a method of manufacturing a printed electronic sheet of the present invention.
본 발명은 무늬를 그리고 착색이 되는 의류의 프린트용 전사시트로서 그림무늬를 전사프린트한 후에도 의류는 통기성이 있는 의류의 프린트용 전사시트의 제조방법에 관한 것으로 그림무늬를 신속하게 전사할 수 있는 편리한 전사시트의 제조방법에 관한 것이다.The present invention relates to a method of manufacturing a transfer sheet for printing a garment having a breathable clothing even after the transfer of the print pattern as a transfer sheet for printing the garment to be patterned and colored, convenient to quickly transfer the pattern It relates to a method for producing a transfer sheet.
주된 제조방법은 100-150g의 동판지상에 융해점이 다른 3종의 투명한 콜로이드 필름 가공의 프로세스를 행하여 그 투명막의 코팅후에 전사시트에는 원하는 도안을 그리는 것으로, 이것을 전사할 경우에는 뜨거운 아일론을 눌러대면 7-15초내에 도안을 의류위에 전사된다.The main manufacturing method is to process three kinds of transparent colloid film with different melting point on 100-150g copper sheet and draw the desired pattern on the transfer sheet after coating the transparent film. Within 7-15 seconds, the pattern is transferred onto clothing.
또 전사프린트된 도안은 통기성을 지니고 있다.In addition, the transfer printed pattern is breathable.
이와같이 본 발명은 경제적이고 실용적인 프린트의 새로운 방법을 제공하는 의류의 프린트용 전사시트의 제조방법에 관한 것이다.As such, the present invention relates to a method of manufacturing a transfer sheet for printing a garment, which provides a new method of economical and practical printing.
종래에는 의류에 그림무늬를 프린트하는 방법으로는 그때그때 디자이너가 각종의 흑백도안을 작성하고 그 도안에서 골라낸 것을 스크린프린트에 의해 프린트하는 방법을 쓰고 있다.Conventionally, as a method of printing a picture pattern on clothing, a designer creates a black and white drawing at that time and uses a screen print to print out a selection of the black and white drawings.
또 이른바 사진프린트를 파는 물건으로 하고 있는 방법도 있다. 이것은 먼저 사진을 찍고 컴퓨터에 의하여 사진을 의류에다 전사프린트하는 것이다.There is also a method of selling so-called photo prints. This involves first taking a picture and then transferring the picture onto a garment by a computer.
상기한 종래의 기술에는 다음과 같은 결점이 있다.The above prior art has the following drawbacks.
스크린 프린트에 의한 프린트는 비용이 들고 사람손이 많이가며 더구나 설비에 많은 비용이 들어 경제적이 메릿트는 없었다.Printing by screen printing is costly, human handed, and more expensive to install.
이른바 「사진프린트」에 의한 프린트는 이 사진프린트를 경험한 사람이면 알 수 있는 바와 같이 전사프린트후의 도안색채는 때때로 선명한 색채가 못되고 보통 단조로운 청, 옥, 갈색뿐이므로 소비자가 구하는 레벨에 응할 수 없었다. 즉, 색채에 변화가 없는 도안, 비용도 싸지 않고 더구나 전사프린트에 시간이 걸려 소비자의 기대에 따르지 못하였다.So-called "photo print" prints, as can be seen by those who have experienced this photo print, sometimes the color after transfer printing cannot be vivid colors and usually only monotonous blue, jade, and brown, so they could not meet the level of the consumer. . In other words, the design does not change the color, the cost is not cheap, and also it takes time to transfer printing did not meet the expectations of consumers.
본 발명은 이와같은 결점을 해결하기 위하여 발명된 것이다.The present invention has been invented to solve such drawbacks.
이와같은 결점을 해결하여 전사프린트의 과정을 아주 간단히 하여 각종의 색채도 선명한 도안으로 할 수 있고 코스트도 낮게한 프린트용 전사시트로서, 전사프린트후의 의류가 통기성을 지니고 있는 프린트용 전사시트를 제공하기 위하여 본 발명에 있어서는 100-150g의 동판지상에 3종의 용해점이 다른 투명한 콜로이드 필름을 가공하는 프로세스를 실시하여, 그 투명막의 코팅후에 전사시트에 원하는 도안을 그린다. 이것을 전사할 때에는 뜨거운 아릴론을 눌러대면 7-15초 내에 도안이 의류위에 전사된다. 또 전사프린트된 도안은 통기성을 지니고 있다. 이와같은 경제적이고 실용적인 프린트의 새로운 방법을 제공하는 의류의 프린트용 전사시트의 제조방법을 제공할 수 있다.To solve these drawbacks, the process of transfer printing is made very simple, and various colors can be made clear, and the cost is also low. As a printing sheet for printing, the transfer sheet for printing in which clothing after transfer printing is breathable is provided. To this end, in the present invention, a process of processing three types of transparent colloidal films having different melting points on 100-150 g of copper sheet is carried out, and a desired pattern is drawn on the transfer sheet after coating of the transparent film. When transferring this, press the hot arlon and the pattern will be transferred onto the garment within 7-15 seconds. In addition, the transfer printed pattern is breathable. It is possible to provide a method for manufacturing a transfer sheet for printing a garment that provides a new method of printing such economical and practical.
위에서 설명한 프린트용 전사시트(-)위에 먼저 도안이 좌우가 반전한 무늬를 프린트한다(의류에 전사프린트후 기본 무늬와 일치한다). 또는 개인이 마음에 드는 무늬를 프린트용 전사시트위에 그릴수도 있다. 그러나 이때 주의할것은 반드시 유성 또는 방수성펜을 사용해야만 전사프린트한 가장 좋은 효과를 얻을 수 있으며 빨았을때에도 물이 빠지고 색이 바래지는 것을 방지할 수 있다.On the transfer sheet (-) for printing described above, the pattern is first printed on the left and right reversed (it matches the basic pattern after the transfer print on clothing). Or you can draw a pattern you like on the transfer sheet for printing. However, be careful to use oil-based or water-proof pens to get the best effect of transfer printing and to prevent the water from falling out and fading when washed.
전사프린트를 할때에는 T샤츠 같은 의류위에 본 발명의 프린트용 전사시트를 붙이고 아일론을 약 130-150℃의 온도로 20kg/cm-50kg/cm의 압력으로 7-15초동안 눌러댄다. 그후 기초제를 떼어낸다. 이와같이 극히 용이하게 도안을 의류위에 전사프린트를 할 수 있다.When printing a transfer, attach the transfer sheet for printing of the present invention on a garment such as a T-shirt and press the alon for 7-15 seconds at a pressure of 20kg / cm-50kg / cm at a temperature of about 130-150 ° C. Then remove the base. In this way, the print can be printed on the garment very easily.
실시예에 관하여는 도면을 참조하여 설명한다.Embodiments will be described with reference to the drawings.
본 발명의 코팅기초재로서는 100-150g의 동판지 또는 60U 또는 75U 두께의 마일라 필름이 적당하다.As the coating base material of the present invention, 100-150 g of copper paper or mylar film having a thickness of 60 U or 75 U is suitable.
그 다음에 기초재의 한쪽 표면상에 3종이 용해점이 다른 투명한 콜로이드 필름을 순차적으로 균일하게 코팅한다. 코팅의 제1층이 되는 투명한 콜로이드 필름에는 낮은 용해점의 물질, 예를들면 포리아미드, 파라핀, 스테아린산 및 로진을 석유용제 예를들면, 토루엔, 크실렌 또는 100# 용제로 희석(비율 약 1:1), 용해한 후 다시 이소보틸알콜(1,B,A)을 적당한 비율로 혼합한다. 그후 100℃-120℃로 데워서 용해시키고, 다시 냉각한 후 줄무늬판을 이용하여 기초재위에 적당한 두께로 코팅한다(제1도에 표시한 바와같다). 이와같이 하여 기초재의 표면상에 1층의 투명한 콜로이드 필름을 형성하여 제1차 코팅과정을 완성한다. 또 상기 각 재료비율과 고형분의 농도는 대기온도나 가열로 같지 않으므로 적당히 조정한다.Then, on one surface of the base material, three types of transparent colloid films having different melting points were sequentially uniformly coated. The transparent colloidal film, which serves as the first layer of the coating, may be diluted with low melting materials such as polyamide, paraffin, stearic acid and rosin with petroleum solvents such as toluene, xylene or 100 # solvents (ratio about 1: 1) After dissolving, isobotyl alcohol (1, B, A) is mixed at an appropriate ratio. It is then warmed to 100 ° C.-120 ° C. to dissolve, cooled again, and then coated with a stripe to a suitable thickness on the base material (as shown in FIG. 1). In this way, the first coating process is completed by forming a transparent colloid film of one layer on the surface of the base material. In addition, the concentration of each material and the concentration of the solid content are not the same as the air temperature or the heating furnace, so they are appropriately adjusted.
제2도에 표시한 바와같이 높은 융해점의 열가소성 고무(T.P.R) 또는 에틸렌-초산비닐(E.V.A)중의 하나와 적당량의 산화방지제(1%-3%)를 혼합한후 석유용제로 희석되고 가열용해하여 25%-35%의 고체농도를 형성한다. 이 형성에 관하여는 상온에서도 진행이 가능하지만 용해속도를 높이고자 할때에는 100℃-120℃까지 가열할 수 있다. 그리고 앞에 설명한 형성과정에 있어서 고형분이 점착상태(겔상태)일때 줄무늬판을 이용하여 제1층 코팅을 마친 기초제위에 코팅을 하여 제2층의 투명한 콜로이드 필름을 형성한다.As shown in FIG. 2, one of a high melting point thermoplastic rubber (TPR) or ethylene-vinyl acetate (EVA) is mixed with an appropriate amount of antioxidant (1% -3%), diluted with petroleum solvent, and dissolved by heating. Form a solid concentration of 25% -35%. Regarding this formation, it is possible to proceed even at room temperature, but to increase the dissolution rate, it can be heated to 100 ° C-120 ° C. In the above-described forming process, when the solid component is in an adhesive state (gel state), the first colloidal coating layer is coated on the base layer after the first layer coating using a stripe plate to form a transparent colloid film of the second layer.
제3도에 표시한 바와같이 본 발명의 제3층인 즉 최상층의 열가소성 접착제의 코팅 순서인데 제2층의 코팅과 같으며 열가소성 고무(T.P.R) 또는 에틸렌-초산 비닐(E.V.A)중의 하나와 적당량의 석유수지를 1:8비율로 혼합한 산화방지제, 파라핀, 포리비닐납을 가하고 다시 석유용제를 가하여 가열용해를 진행하여 여과한 후 냉각하여 제1층, 제2층의 코팅을 마친 기초제의 제2층 코팅위에 다시 코팅을 하여 제3층의 투명한 콜로이드 필름을 형성한다.As shown in FIG. 3, the coating layer of the third layer of the present invention, that is, the uppermost layer of the thermoplastic adhesive, is the same as the coating of the second layer, and one of thermoplastic rubber (TPR) or ethylene-vinyl acetate (EVA) and an appropriate amount of petroleum. Antioxidant, paraffin, and polyvinyl lead mixed with resin at a ratio of 1: 8 were added, and then petroleum solvent was added, followed by heat dissolution, followed by filtration and cooling, followed by coating of the first and second layers. Recoating over the layer coating forms a transparent colloidal film of the third layer.
마지막으로 70℃의 저온으로 건조하여 이와같은 과정을 거쳐 본 발명의 프린트용 전사 시트를 완성한다.Finally, it is dried at a low temperature of 70 ℃ through this process to complete the transfer sheet for printing of the present invention.
앞에 설명한 코팅과정에 있어서 줄무늬판 부분만 제외하면 기계의 롤러 방식에 의한 코팅도 가능하다.In the above-described coating process, except for the stripe plate part, coating by the roller method of the machine is also possible.
또 앞에 설명한 프린트용 전사시트(-)위에 먼저 아름다운 도안을 좌우반전하여무늬를 프린트한다(의류에 전사프린트한 후, 기본무늬와 일치함). 또 개인적으로 마음에 드는 무늬를 프린트용 전사시트위에 그려넣을 수도 있다. 그러나 이때 주의할 것은 반드시 유성 또는 방수성펜을 사용할것이며, 이로인하여 전사프린트후에 가장 좋은 효과를 얻을 수 있으며, 빨래후 물이 빠지거나 빛이 바래지는 것을 방지할 수 있다.On the transfer sheet (-) for printing described above, a pattern is printed by first inverting a beautiful pattern (transfer printing onto clothing and then matching the basic pattern). You can also personally draw your favorite pattern on the transfer sheet for printing. However, be careful to use oil-based or water-resistant pen, which is the best effect after the transfer print, and can prevent water from falling out or fading after washing.
전사프린트를 할때에는 T셔츠와 같은 의류위에 본 발명의 프린트용 전사시트를 붙이고 아일론을 약 130-150℃ 온도로 20kg/cm-50kg/cm의 압력으로 7-15초간 눌러댄다. 그후 기초제를 떼어내는 아주 쉽게 도안을 의류상에 전사프린트할 수가 있다.In the case of transfer printing, attach the transfer sheet for printing of the present invention on a garment such as a T-shirt and press the iron for 7-15 seconds at a pressure of 20kg / cm-50kg / cm at a temperature of about 130-150 ° C. After that, it is very easy to transfer the pattern onto the garment.
본 발명의 프린트용 전사시트에 의한 프린트는 전사프린트후 의복의 무늬부분이 프린트 전과같이 통기성을 지니며 또 종래 프린트 방식에 의한것과 같이 의복의 섬유구멍을 만들지 않으므로 의복자체가 갖는 통기성을 잃지 않는다.In the printing by the transfer sheet for printing of the present invention, the pattern portion of the garment after the transfer printing is as breathable as before printing and does not lose the breathability of the garment itself because it does not make the fiber hole of the garment as in the conventional printing method.
위에서 설명한 투명한 콜로이드 필름을 겔상태로나 콜로이드 상태로도 만들수 있다. 또 기초제위의 부분적인 코팅이나 전체적인 코팅에도 사용할 수 있고 대량의 수요 및 넓은 면적에 전사프린트하는데 편리하다.The transparent colloidal film described above can also be made in gel or colloidal form. In addition, it can be used for partial coating or overall coating of base material, and is convenient for transfer printing in large demand and large area.
위의 설명으로 명백한 바와같이 본 발명에는 다음과 같은 효과가 있다.As apparent from the above description, the present invention has the following effects.
(가) 신속하고 대량으로 생산되는 산업상의 메릿트가 있다.(A) There is an industrial merit that is produced quickly and in large quantities.
(나) 본 발명에 의한 프린트용 전사시트를 이용하면 의류위에 전사프린트가 간단히 할수있어 편리하다.(B) The transfer sheet for printing according to the present invention is convenient because it can simplify the transfer printing on the garment.
(다) 본 발명에 의한 프린트용 전사시트에 의하여 프린트된 의류의 무늬부분은 의류가 본래 지닌 통기성을 잃지 않는다.(C) The patterned part of the garment printed by the transfer sheet for printing according to the present invention does not lose the breathability originally possessed by the garment.
(라) 종래 의류의 프린트는 출하 시점에서 모양이 한정되지만 본 발명에 의한 프린트용 전사시트에 의하면 수시로 각종 무늬를 추가 프린트할 수 있다.(D) The printing of conventional clothes is limited in shape at the time of shipment, but according to the transfer sheet for printing according to the present invention, various patterns can be additionally printed at any time.
Claims (4)