KR940005071B1 - Composition using toxicity eliminate of cement - Google Patents

Abstract

The poison-removing composition is produced by (a) mixing 30 % granite phophyry, 30 % allophane and 40 % zeolite, and crushing the mixt. to be 20-30 mesh, (b) calcining it at 1000 deg.C in the Z furnace, (c) finely crushing it to make a calcined powder and (d) mixing 30 % calcined powder with 60 % vermiculite powder, 5 % talc powder, 1 % A.E. agent, 1 % animal fats and oils, 1 % surface activating agent and 3-5 % selenium. The composition is used in the mfr. of lightweight concrete to be harmless to the animals, plants and human.

Description

Composition for removing toxicity of cement and its manufacturing method

The present invention relates to a composition for removing the toxicity of cement and a method for producing the same, which is capable of removing the toxicity of cement by heat-treating a mineral that is harmless to shrinkage and mixing it with cement, and which can produce lightweight concrete that is harmless to copper, plants and the human body. .

Conventionally, there are radioactive substances such as radon in the cement, which can cause damage.If cement powder gets into the eyes, it becomes tingling, congestion, tears, and itchy, blistering, and peeling off. If the plant such as garlic is hanged on the concrete wall, the surface of the garlic becomes crumpled, which causes direct damage to the plant such as rotting. There were many problems such as having to replenish insufficient moisture by installing.

The present invention is to remove the toxicity of cement affecting copper, plants and human body from minerals, and to produce a composition that can reinforce vitality to produce a concrete product that is light and harmless to copper, plants and human body while maintaining the toxicity of concrete. It is an object of the present invention to provide a composition for detoxification of Shimenk.

Another object of the present invention is to provide a composition for removing toxicity of cement, which can reduce the amount of industrial waste by producing concrete products having high practicality using industrial waste such as briquettes and waste minerals.

Minerals used as a main material in the preparation of the composition having such a purpose, that is, ganbanite, Uiwang, Zeolite (Zeolite), vermiculite contained in the following Tables 1 to 4.

TABLE 1

Among the minerals contained in elvan, beneficial components to the human body are carium (K), manganese (Mn), silicon (Si), calcium, magnesium (Mg), iron (Fe), titanium (Ti), phosphorus (P), aluminum (Al), sodium (Na), and the like.

TABLE 2

Uiwang is porous and has a high amount of free space between crystals, so it can absorb and remove toxins and pollutants, improve disease resistance, and elute a large amount of oxygen to solve biological oxygen demand (BOD) and chemical oxygen demand (COD). It is abundant in water to purify water quality, harmless to copper, plant and human body, and contains isotope in addition to ingredient list, so it has the property of base substitution function (CEC) which promotes the activation of molecules.

TABLE 3

Zeolite contains natural active minerals, so it has base substitution function (C.E.C: oily, moisture storage and elution ability), adsorption function and molecular sieve function.

TABLE 4

Referring to the present invention using the main material having the above components according to the embodiment as follows.

EXAMPLE

First step: 30% of elvan rock, Uranite, 30%, and 40% of zeolite are mixed and ground to 20-30 mesh.

Second Step: The composition of the first step is calcined at about 1,000 ° C. in a Z (jet) furnace.

Third step: The composition of the second step is finely ground to obtain a powder state.

4th process:

Vermiculite powder: 60%

Mixed small powder (3rd process powder): 30%

Talc powder: 5%

a. Yi (made of A.E): 1%

Surfactant: 1%

Selenium: 3-5%

Mixing is to prepare a composition for removing cement toxicity.

The composition thus prepared may be used by mixing with cement (a cement ratio of about 20%), by mixing with water or other solvents, and also suspending the solvent.

The tap water was poured into concrete blocks and general cement blocks to which the present invention was added.

[Test Example 1]

As in Test Example 1, it can be seen that the fish in the general cement block cannot live due to the chlorocalciotoxicity of tap water, and it can be seen that the block of the present invention has an excellent effect of activating life, and in particular, has excellent water purification function. Physically adsorption of harmful components in water, it was found that they are made pollution-free by oxidizing, decomposing chemical harmful substances and fixing and adsorption effects of harmful heavy metals.

As described above, the present invention can produce multifunctional concrete products that are harmless to copper, plants, and human bodies by eliminating the toxicity of cement because they are fired at a high temperature in order to make use of the characteristics of each ore and to activate the insufficient parts.

Claims (1)

30% of elvanite, 30% of Uranite, and 40% of zeolite are mixed, calcined and pulverized to powder, followed by 60% vermiculite powder, 30% mixed powder, 5% of talc powder, 1% of aging agent, 1% of surface active agent, 1% animal fat, 3% selenium, the composition for removing the toxicity of cement.