KR930000419A - Permeable Colored Ceramic Paving Blocks - Google Patents

Permeable Colored Ceramic Paving Blocks Download PDF

Info

Publication number
KR930000419A
KR930000419A KR1019910010158A KR910010158A KR930000419A KR 930000419 A KR930000419 A KR 930000419A KR 1019910010158 A KR1019910010158 A KR 1019910010158A KR 910010158 A KR910010158 A KR 910010158A KR 930000419 A KR930000419 A KR 930000419A
Authority
KR
South Korea
Prior art keywords
paving block
block according
cement
water
composite
Prior art date
Application number
KR1019910010158A
Other languages
Korean (ko)
Other versions
KR930011265B1 (en
Inventor
이호영
Original Assignee
이호영
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이호영 filed Critical 이호영
Priority to KR1019910010158A priority Critical patent/KR930011265B1/en
Publication of KR930000419A publication Critical patent/KR930000419A/en
Application granted granted Critical
Publication of KR930011265B1 publication Critical patent/KR930011265B1/en

Abstract

내용 없음No content

Description

투수성 유색 세라믹 포장블록Permeable Colored Ceramic Paving Blocks

본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음Since this is an open matter, no full text was included.

제1도는 본 발명의 투수성 포장용 세라믹 포장블록의 기본형이다.1 is a basic type of the water-permeable paving ceramic paving block of the present invention.

제2도는 본 발명의 인터록킹형 블록이고,2 is an interlocking block of the present invention,

제3도는 본 발명의 인터록킹형 블록의 모자익이고,3 is a middle of the interlocking block of the present invention,

제4도는 본 발명의 블록의 절단도이고,4 is a cutaway view of the block of the invention,

제5도는 본 발명의 블록 제조 공정도이다.5 is a block manufacturing process diagram of the present invention.

Claims (9)

세라믹 입자를 합성수지 접착제로 혼합 접합시킨 표층과 쇄석 골재, 시멘트 및 물의 혼합물을 경화시켜서 된 모체로 되는 2층 복합재의 투수성 유색 세라믹 포장블록.A water-permeable colored ceramic paving block of a two-layer composite, which is a matrix formed by curing a mixture of ceramic particles bonded with a synthetic resin adhesive and a mixture of crushed aggregate, cement and water. 제1항에 있어서, 세라믹 입자가 점토류를 소성하여 된 입경 0.5 내지 3㎜인 복합재 포장블록.The composite paving block according to claim 1, wherein the ceramic particles have a particle size of 0.5 to 3 mm by firing clays. 제1항에 있어서, 합성수지 접착제가 비스페놀 A의 디글리시딜에테르형의 에폭시 수지를 변성 폴리아미드수지로 경화시켜서 되는 복합재 포장블록.The composite packaging block according to claim 1, wherein the synthetic resin adhesive is obtained by curing a diglycidyl ether-type epoxy resin of bisphenol A with a modified polyamide resin. 제1항에 있어서, 표층의 두께가 5 내지 10㎜ 그리고 모체의 두께가 5㎝ 내지 10㎝인 복합재 포장블록.The composite paving block according to claim 1, wherein the surface layer has a thickness of 5 to 10 mm and a mother thickness of 5 cm to 10 cm. 시멘트, 골재 및 물을 혼합하여 모체 배합물을 만드는 배합공정, 세라믹 입자, 에폭시수지, 경화제 및 첨가제를 혼합하여 표층 배합물을 만드는 배합공정, 모체 배합물의 계량 및 공급 공정, 형틀 세척공정, 1차 진동 및 압축공정, 일차 압축 성형된 모체위에 표층 배합물을 계량 공급하는 공정, 가열된 상부 형틀로 또는 비접착성 필름을 가하는 2차 진동 및 압축공정, 및 증기양생 공정으로 이루어진 포장 블록의 제조방법.Blending process of mixing cement, aggregate and water to make the parent compound, Blending process of mixing ceramic particles, epoxy resin, hardener and additives to make the surface compound, Weighing and supplying of the parent compound, Mold washing process, Primary vibration and A method of manufacturing a paving block, comprising a compression process, a process of metering and supplying a surface layer compound on a primary compression-molded matrix, a secondary vibration and compression process by applying a non-adhesive film to a heated upper template, or a steam curing process. 제5항에 있어서, 시멘트를 골재 1부 기준 0.15부 내지 0.30중량부 혼합하고, 물을 시멘트 1부 기준 0.2 내지 0.4중량부 혼합하는 포장용 블록의 제조방법.The method for producing a paving block according to claim 5, wherein the cement is mixed with 0.15 parts by weight to 0.30 parts by weight based on 1 part of aggregate and the water is mixed with 0.2 to 0.4 parts by weight based on 1 part of cement. 제5항에 있어서, 압축공정을 100 내지 150㎏/㎠에서 하며, 상부 형틀을 60 내지 900℃로 가열하거나 비접착성 필름을 가하고 압축하는 제조방법.The production method according to claim 5, wherein the compression process is performed at 100 to 150 kg / cm 2, and the upper mold is heated to 60 to 900 ° C. or a non-adhesive film is added and compressed. 제5항에 있어서, 증기 양생을 60 내지 80℃에서 1 내지 10시간 실시하는 포장용 블록의 제조방법.The method of manufacturing a paving block according to claim 5, wherein steam curing is carried out at 60 to 80 ° C for 1 to 10 hours. 제5항에 있어서, 형틀 세척 공정이 임의 순서로 각 공정중에 수행되는 포장용 블록의 제조방법.The method of manufacturing a paving block according to claim 5, wherein the mold cleaning process is performed during each process in any order. ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.※ Note: The disclosure is based on the initial application.
KR1019910010158A 1991-06-19 1991-06-19 Ceramic packing block KR930011265B1 (en)