KR920004827B1 - Antimicrobial insole - Google Patents
Antimicrobial insole Download PDFInfo
- Publication number
- KR920004827B1 KR920004827B1 KR1019900007976A KR900007976A KR920004827B1 KR 920004827 B1 KR920004827 B1 KR 920004827B1 KR 1019900007976 A KR1019900007976 A KR 1019900007976A KR 900007976 A KR900007976 A KR 900007976A KR 920004827 B1 KR920004827 B1 KR 920004827B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- antibacterial
- quaternary ammonium
- insole
- ammonium salt
- Prior art date
Abstract
Description
본 발명은 항균방취 신발안창에 관한 것으로서, 더욱 상세하게는 신발안창을 구성하는 천, 접착제, 스폰지 각각에 항균제 및 방취제를 참가하여 제조함으로써 우수한 항균방취 효과를 나타내도록 하는 개선된 신발안창에 관한 것이다.The present invention relates to an antibacterial deodorizing shoe insole, and more particularly, to an improved shoe insole that exhibits an excellent antibacterial deodorizing effect by manufacturing an antibacterial agent and a deodorant in each of the cloth, the adhesive, and the sponge constituting the shoe insole. .
종래 항균방취 기능을 지닌 신발안창을 제조하는 방법에서는 안창을 구성하는 천에만 비스(트리-부틸틴)옥사이드, 알킬메틸벤질암모늄염 등을 처리하고 스폰지에는 활성탄을 사용하여 방취효과를 나타내고 있으며 국내 실용신안공개(제84-3630호), 또한 국내 특허공개 제88-2477호에 의하면 살리실산(SA), 폴리비닐알코올(PVA), 카프복시메틸셀룰로오즈(CMC)등의 수용액에 항균제 및 살균제로 황산동, 황산제 1철-L이즈코르빅산 및 살리실산 등을 신발안창용 천의 이면에 도포하고 건조하여 신발악취 방지효과를 얻고자 하였다.In the conventional method of manufacturing shoe insoles with antibacterial and deodorizing function, only bis (tri-butyltin) oxide, alkylmethylbenzyl ammonium salt, etc. are treated only on the fabric constituting the insole and activated carbon is used for the sponge to show deodorizing effect. According to Korean Patent Publication No. 84-3630, and Korean Patent Publication No. 88-2477, copper sulfate and sulfuric acid are used as an antibacterial and bactericidal agent in aqueous solutions such as salicylic acid (SA), polyvinyl alcohol (PVA), and capoxymethyl cellulose (CMC). Ferrous-L-Iscorbic acid and salicylic acid were applied to the back surface of the shoe insole and dried to obtain a shoe malodor prevention effect.
그러나, 이와 같이 천에만 항균제를 처리하였거나 항균제를 처리한 천과 흡취제를 충전시킨 스폰지를 동시에 사용하여 제조한 항균방취 신발안창의 경우, 그 사용 초기에는 항균방취 효과를 나타내나 장시간 사용하거나 몇 번 수세한 경우에는 항균방취 효과가 급격히 감소하여 악취가 발생한다.However, antibacterial deodorant insoles manufactured by using only antibacterial agent or fabric treated with antimicrobial agent and sponge filled with odorant have the antibacterial deodorization effect at the beginning of its use, but use it for a long time or several times. In the case of washing with water, the antibacterial deodorization effect is drastically reduced and odor is generated.
이러한 이유는 종래의 항균방취 신발안창은 천에는 항균처리가 되어 있으나 스폰지에는 항균처리가 되어 있지 않기 때문에 스폰지에서 악취가 발생하였다. 특히, 천과 스폰지를 접착시키는 접착제가 천과 스폰지를 차단하는 차단벽과 같은 역할을 하기 때문에 천에 처리된 항균제가 스폰지에 항균효과를 나타내기는 불가능하였다.The reason for this is that the conventional antibacterial deodorant shoe insole is treated with an antibacterial treatment on the fabric, but the sponge does not have an antibacterial treatment. In particular, since the adhesive that bonds the cloth and the sponge acts as a barrier for blocking the cloth and the sponge, the antimicrobial agent treated on the cloth cannot exhibit the antimicrobial effect on the sponge.
따라서, 이러한 접착제의 차단막 형성으로 인해 스폰지는 항균처리가 전혀 되어 있지 않은 상태이기 때문에 안창 전체의 항균방취 효과 감소에 지배적인 원인이 되고 있으며, 이로 말미암아 여전히 착화시 악취가 발생하는 등의 불쾌감이 해소되지 못하였다.Therefore, due to the formation of the barrier film of the adhesive, since the sponge is not treated with antibacterial treatment at all, it is a dominant cause for reducing the antibacterial deodorization effect of the entire insole, thereby eliminating unpleasant odors such as odors generated during ignition. It didn't work.
일반적으로 착화시 신발 및 발에서의 악취발생의 원인은 신발내에 서식하는 각종 세균이 착화시 착화자의 발에서 분비되는 땀성분중 요소, 지방류, 유산등을 분해시킬때 암모니아등의 유독가스가 발생하기 때문이다.In general, the cause of bad smell in shoes and feet during ignition is that toxic gases such as ammonia are generated when various bacteria in the shoes decompose urea, fatty acids, and lactic acid among the sweat components secreted from the wearer's foot during ignition. Because.
착화시 초기에 분비되는 땀은 착화자의 양말을 통하여 신발안창의 천에 흡수되는데, 이때에는 안창의 천에 항균처리가 되어 있기 때문에 각종 세균이 서식하기 어렵고 따라서 악취가 발생하지 않는다.Sweat is secreted at the initial stage of ignition and absorbed into the fabric of the shoe insole through the wearer's socks. At this time, because the fabric of the insole is antibacterial, it is difficult to inhabit various bacteria and thus no odor occurs.
그러나, 장시간 착화시 혹은 활동량이 많은 경우 분비되는 남의 양이 증가하게 되어 다량의 땀이 안창의 스폰지에까지 흡수되며, 안창용 스폰지의 경우 발포에 의해 스폰지 자체가 미세한 공극으로 구성되어 있기 때문에 착화시 분비된 땀이 공극의 모세관 작용으로 인하여 스폰지의 내부까지 깊숙히 흡수된다.However, during long-time ignition or when there is a large amount of activity, the amount of secreted male increases, and a lot of sweat is absorbed by the sponge of the insole, and in the case of the insole sponge, the foam itself is secreted during ignition because the sponge itself is composed of fine pores. Sweat is absorbed deep into the sponge due to the capillary action of the pores.
이때 스폰지에 흡수된 땀은 각종 세균이나 곰팡이 등과 같은 미생물의 배치역할을 하기 때문에 미생물이 서식하기 쉽게 되고, 이 미생물이 땀의 일부 성분을 분해시키기 때문에 스폰지에 항균방취 처리가 되지 않은 종래의 항균방취 안창을 사용한 신발을 신게 되면 신발 및 발에서 심한 악취가 발생하는 것이다.At this time, the sweat absorbed by the sponge acts as a batch of microorganisms such as various bacteria and molds, and thus the microorganisms are easy to inhabit. Wearing shoes with insoles can cause bad odors in your shoes and feet.
따라서, 본 발명은 이러한 제반 문제점들을 해결하고자 종래의 방법을 개선한 것으로서 신발안창을 구성하는 천, 접착제, 스폰지의 구성체에 각각 항균방취가공을 행한 후 신발안창을 제조함으로서 신발안창내에서의 각종 미생물의 서식이 완전 차단되도록 하여 착화시 악취발생을 방지할 수 있도록 개선시킨 항균방취 신발안창을 제공하는데 그 목적이 있다.Accordingly, the present invention is an improvement of the conventional method to solve these problems, and the microorganisms in the shoe insole by manufacturing the insole after each antimicrobial deodorizing process to the fabric, adhesive, sponge constituents constituting the shoe insole The purpose of the present invention is to provide an antibacterial deodorant insole that can be completely blocked so that the odor can be prevented during ignition.
이하, 본 발명을 상세히 설명하면 다음과 같다.Hereinafter, the present invention will be described in detail.
본 발명은 스폰지체의 기재에 천이 접착되어 있는 구조의 항균방취 신발안창에 있어서, 제4급암모늄염과 디페닐에테르 계성분중에서 선택된 어느 하나 또는 2이상의 성분으로 구성된 항균제가 천의 중량에 대해 0.01~5중량%만큼 고착된 천과 접착제 성분에 대해 제4급암모늄염과 티페닐에테르 계성분 및 비스(트리부틸틴) 옥사이드 중에서 선택된 어느 하나 이상의 성분으로 구성된 항균제 0.01~5중량%와 원적외선을 발산하는 세라믹 1~20중량%가 혼합된 접착제층, 그리고 에틸렌비닐아세테이트(EVA), 폴리우레탄(PU), 폴리비닐클로라이드(PVC), 폴리에틸렌(PE) 및 폴리프로필렌(PP)수지 중에서 선택된 어느 하나의 수지과 상기 수지성분의 중량에 대해 고상의 공지 항균제 0.01~5중량% 및 원적외선 세라믹성분 1~20중량%로 구성된 신발안창을 그 특징으로 한다.The present invention provides an antimicrobial deodorant shoe insole in which a fabric is adhered to a substrate of a sponge, wherein the antimicrobial agent composed of any one or two or more components selected from quaternary ammonium salts and diphenyl ether-based components is 0.01 to 0.01 by weight of the cloth. Ceramic that emits far infrared rays and 0.01-5% by weight of antimicrobial agent composed of at least one component selected from quaternary ammonium salts, thiphenyl ether-based components and bis (tributyltin) oxide with respect to the cloth and adhesive components fixed by 5% by weight 1 to 20% by weight of the adhesive layer and any one selected from ethylene vinyl acetate (EVA), polyurethane (PU), polyvinyl chloride (PVC), polyethylene (PE) and polypropylene (PP) resin and It is characterized by a shoe insole composed of 0.01 to 5% by weight of the solid-state known antibacterial agent and 1 to 20% by weight of the far infrared ceramic component with respect to the weight of the resin component.
이와 같은 본 발명에 따른 신발안창을 제조함에 있어서는 우선, 신발안창용 천을 상기 항균가공제를 0.01~5% 희석한 용액에 침지시키거나 상기 용액을 분사시켜 항균처리한다. 그 다음에는 접착층을 처리하는데, 이는 접착성분에 대해 0.01~5중량%만큼의 4급암모늄염, 디페닐에테르계용액 및 기타 항균제를 균질 용해시킴과 동시에 1~10중량% 만큼의 4~12㎛의 원적외선을 방출하는 원적외선 세라믹을 혼합시켜서 접착제를 제조하며, 이어서, 스폰지체 상기 고분자수지성분에 EVA와 공지의 고상분발로 이루어진 항균제, 스테아린산, 가교제, 발포제, 발포안정에 및 원적외선 세라믹을 각각 혼합하고 발포시켜서 안창용 스폰지체를 제조한 후, 상기 접착제를 이용하여 스폰지체에 상기 처리된 천을 접착, 성형시키게 되면 신발안창을 제조할 수가 있게 된다.In manufacturing the shoe insole according to the present invention, first, the cloth for shoe insole is immersed in a solution diluted 0.01 to 5% of the antimicrobial processing agent or sprayed the solution to the antibacterial treatment. The adhesive layer is then treated, which homogeneously dissolves 0.01-5% by weight of the quaternary ammonium salt, diphenyl ether solution and other antimicrobial agents, and 4-12 μm of 1-10% by weight. An adhesive is prepared by mixing far-infrared ceramics emitting far-infrared rays, followed by mixing and foaming the sponge-like polymer resin with an antimicrobial agent, stearic acid, a crosslinking agent, a foaming agent, foaming stability, and far-infrared ceramic, respectively, consisting of EVA and a known solid phase powder. After manufacturing the insole sponge body, and then using the adhesive to adhere the molded cloth to the sponge body, it is possible to manufacture a shoe insole.
이때 본 발명에서 사용되는 항균제중에서 상기 4급암모늄염으로서는 유기실리콘 4급암모늄염이나 탄소수가 6~18개인 알킬기를 갖고 있는 알킬 4급암모늄염을 사용할 수가 있다.At this time, as the quaternary ammonium salt used in the present invention, an organosilicon quaternary ammonium salt or an alkyl quaternary ammonium salt having an alkyl group having 6 to 18 carbon atoms can be used.
또한, 본 발명은 상기 접착제층에 항균처리를 하지 않은 경우도 포함하는 바, 상기 항균가공처리시 접착제층에는 별도의 처리가 없더라도 어느 정도의 효과는 기대할 수 있으며, 바람직하기로는 상기와 같이 접착제층에도 처리를 하는 것이 더욱 좋은 효과를 나타낸다.In addition, the present invention also includes a case where the antimicrobial treatment is not applied to the adhesive layer, even if there is no separate treatment in the adhesive layer during the antimicrobial processing, a certain effect can be expected, preferably the adhesive layer as described above Edo treatment has a better effect.
이와 같은 본 발명을 더욱 상세히 설명하면 다음과 같다.Referring to the present invention in more detail as follows.
본 발명은 상기와 같이 신발안창을 구성하는 천과 접착제 및 스폰지체 모두에다 항균처리를 한 것으로서, 이러한 신발안창의 제조공정을 살펴보면 아래와 같다.The present invention is the antimicrobial treatment to both the cloth and the adhesive and sponge body constituting the shoe insole as described above, looking at the manufacturing process of such a shoe insole as follows.
[제1공정][Step 1]
[신발안창용 천의 항균처리][Antibacterial treatment of shoe insoles]
3-(트리메톡시실릴)프로필 옥타데실 디메틸 염화암모늄, 2,4,4'-트리클로로-2'-히츠록시디페닐에테르, 3,4,4'-트리클로로아닐리드 등의 항균제 0.01~5중량%를 희석한 용액에 천을 침지, 디핑 혹은 천에 분사하여 항균 가공된 신발안창용 천을 제조한다.Antibacterial agents such as 3- (trimethoxysilyl) propyl octadecyl dimethyl ammonium chloride, 2,4,4'-trichloro-2'-hydroxydiphenyl ether, 3,4,4'-trichloroanilide 0.01 to 5 Dipping, dipping or spraying the cloth in a diluted solution by weight by weight to prepare an antibacterial shoe sole cloth.
이때 사용 천을 면, 마, 모, 견 등의 천연섬유와 나일론, 폴리에스테르 둥의 합성섬유, 천연 및 인조가죽에도 처리가능하다.At this time, the fabric can be treated to natural fibers such as cotton, hemp, wool, silk, synthetic fibers of nylon, polyester, and natural and artificial leather.
[제2공정][Step 2]
[접착제의 항균처리][Antibacterial Treatment of Adhesives]
신발안창용 천과 각종 안창용 스폰지를 접착시 사용되는 아크릴계 접착제, 우레탄계 접착제, 클로로프렌계 접착제에 접착제의 0.01~5중량%의 알킬메틸벤질, 염화암모늄, 2,4,4'-트리클로로-2'-히드록시디페닐에테르, 3,4,4'-트리클로로 아닐리드를 첨가하여 용해 혹은 균일하게 분산시킨다.0.01-5% by weight of alkylmethylbenzyl, ammonium chloride, 2,4,4'-trichloro-2'- to acrylic adhesives, urethane adhesives and chloroprene adhesives used to bond shoe insoles and sponges for various insoles. Hydroxydiphenylether and 3,4,4'-trichloroanilide are added to dissolve or disperse uniformly.
[제3공정][Step 3]
[스폰지의 항균처리][Antibacterial treatment of sponge]
신발안창용 스폰지로 사용할 수 있는 엘틸렌비닐아세테이트(EVA), 폴리우레탄(PU), 폴리비닐클로라이드(PVC), 폴리에틸렌(PE) 또는 폴리프로필렌(pp) 등의 수지에 항균제로써 메틸벤질암모늄, 2,4,4'-트리클로로-2'-히드록시티페닐에테프, 3,4,4'-트리클로로카바닐리드, 5-클로로-2-(2,4-디클로로페녹시) 페놀 및 α-브로모-시안알데하드로 구성된 항균제 및 각종 첨가제를 예컨대 하기의 조성으로 혼련한다.Methylbenzyl ammonium, 2, as an antibacterial agent to resins such as elethylene vinyl acetate (EVA), polyurethane (PU), polyvinyl chloride (PVC), polyethylene (PE) or polypropylene (pp), which can be used as a sponge for insoles 4,4'-trichloro-2'-hydroxythiphenylether, 3,4,4'-trichlorocarbinide, 5-chloro-2- (2,4-dichlorophenoxy) phenol and α- Antibacterial agents and various additives composed of bromo-cyanaldehyde are kneaded, for example, in the following composition.
EVA 120~ 170중량부 EVA 120 ~ 170 parts by weight
항균제 1~3중량부 1 to 3 parts by weight of antibacterial agent
스테아린산 1~3중량부 Stearic acid 1-3 parts by weight
가교제 1~3중량부 1-3 parts by weight of crosslinking agent
발포제 5~10중량부 5 to 10 parts by weight of blowing agent
발포안정제 1~5중량부 1 to 5 parts by weight of foam stabilizer
세라믹 1~3중량부 1-3 parts by weight of ceramic
상기 혼련물을 100~180℃에서 가교 발포하여 신발안창용 스폰지를 제작한다.The kneaded material is crosslinked and foamed at 100 to 180 ° C. to prepare a shoe sole sponge.
특히, 이때 제2공정에서와 같이 원적외선을 방사하는 세라믹의 충전에 의해 항균방취 효과를 상승시킨다.In particular, the antimicrobial deodorizing effect is increased by filling the ceramic emitting far-infrared rays as in the second step.
[제4공정][Step 4]
[신발안창의 제조][Manufacture of shoe insoles]
제1공정에서 제작된 항균방취 가공된 신발안창용 천을 제2공정에서 제작된 접착제로서 제3공정에서 제작된 스폰지에 접착시킨 후 100~180℃에서 건조시키고 성형시켜서 항균방취 기능을 지닌 신발용 안창을 제조한다.The antibacterial deodorized shoe insole fabricated in the first process was bonded to the sponge produced in the third process as the adhesive produced in the second process, dried and molded at 100-180 ° C. Manufacture.
상술한 바와 같이 본 발명에 따라 제조된 신발안창은 종래의 것보다 항균, 방취 기능에서 오랜 사용에도 월등히 우수한 효과를 나타낼 뿐 아니라 보온효과도 향상시킨 효과가 있는 것이다.As described above, the shoe insole manufactured according to the present invention exhibits an excellent effect even on long-term use in antibacterial and deodorizing functions as compared to the conventional one, and also has an effect of improving the warming effect.
이하, 본 발명을 실시예에 의거 상세히 설명한다.Hereinafter, the present invention will be described in detail based on examples.
[실시예1]Example 1
[제1공정][Step 1]
면으로 된 신발안창용 천을 하기와 같은 조성으로 된 50℃용액에 10분간 침지한 후 110℃에서 완전 건조하였다.A cotton insole cloth was immersed in a 50 ° C. solution having the following composition for 10 minutes and then completely dried at 110 ° C.
5-클로로-2-(2,4-디클로로페녹시)페놀 0.1중량부 0.1 parts by weight of 5-chloro-2- (2,4-dichlorophenoxy) phenol
3-(프리메톡시실릴)프로필 옥타데실 디메틸염화암모늄 0.1중량부 0.1 part by weight of 3- (premethoxysilyl) propyl octadecyl dimethyl ammonium chloride
에폭시 수지 10중량부 10 parts by weight of epoxy resin
물 89.8중량부 89.8 parts by weight of water
[제2공정][Step 2]
클로로프렌 접착제와 항균제를 하기의 조성으로 균일하게 분산되도록 교반하였다.The chloroprene adhesive and the antimicrobial agent were stirred to uniformly disperse the following composition.
클로로프렌접착제 99중량부 99 parts by weight of chloroprene adhesive
3,4,4'-트리클로로아닐리드 1중량부 1 part by weight of 3,4,4'-trichloroanilide
세라믹 2중량부 2 parts by weight of ceramic
[제3공정][Step 3]
안창용 스폰지를 하기와 같은 조성으로 수지를 혼련 후 150℃에서 20분간 가교 발포시켜 제조하였다The insole sponge was prepared by kneading the resin with a composition as follows and then crosslinking foaming at 150 ° C. for 20 minutes.
EVA 150중량부 EVA 150 parts by weight
5-클로로-2-(2,4-디클로로페녹시페놀) 1.1중량부 1.1 parts by weight of 5-chloro-2- (2,4-dichlorophenoxyphenol)
스테아린산 1.5중량부 Stearic acid 1.5 parts by weight
디큐밀퍼옥사이드(DCP) 1.38중량부 Dicumyl peroxide (DCP) 1.38 parts by weight
아조디카본아마이드 11중량부 Azodicarbonamide 11 parts by weight
ZnO 2.5중량부 ZnO 2.5 parts by weight
알킬메틸벤질암모늄클로라이드(알킬기가 C6~C18인 것의 혼합물) Alkylmethylbenzyl ammonium chloride (mixture of alkyl groups having C 6 to C 18 )
1.0중량부1.0 parts by weight
원적외선 세라믹 3중량부 Far infrared ceramic 3 parts by weight
가교 발포된 에틸렌비닐 아세테이트(EVA) 스폰지에 상기 2공정에서 제조한 접착제로 상기 1공정에서 제작한 항균처리된 천을 접착하여 120℃에서 2분간 건조후 150℃에서 성형하여 신발안창으로 제조하였다. 항균효과는 다음 표 1에서 나타내었다.The antimicrobial treated fabric prepared in step 1 was bonded to the crosslinked foamed ethylene vinyl acetate (EVA) sponge using the adhesive prepared in step 2, dried at 120 ° C. for 2 minutes, and then molded at 150 ° C. to prepare a shoe insole. The antimicrobial effect is shown in Table 1 below.
[실시예2]Example 2
신발안창용 우레탄 프리마에 항균제를 하기 조성으로 혼합하여 항균제가 함유된 우레탄 프리마를 제조하였다.An antimicrobial agent was mixed with an urethane prima for shoe insoles in the following composition to prepare a urethane prima containing an antimicrobial agent.
폴리우레탄수지 150중량부 150 parts by weight of polyurethane resin
알킬메틸벤질암모늄클로라이드(알킬기가 C6~C18인 것의 혼합물) Alkylmethylbenzyl ammonium chloride (mixture of alkyl groups having C 6 to C 18 )
1중량부1 part by weight
5-클로로-2-(2,4-디클로로메톡시)페놀 1중량부 1 part by weight of 5-chloro-2- (2,4-dichloromethoxy) phenol
바이오 세라믹 8중량부 Bio ceramics 8 parts by weight
상기 조성으로 제조된 우레탄 프리마를 실시예 1의 1공정에서 제조한 안창용 천과 함께 모울드에 넣고 중합과 동시에 가교 발포시켜 항균방취 가공된 우레탄 신발안창을 제조하였다. 항균효과는 다음 표 1에 나타내었다.The urethane prima prepared in the above composition was put into a mold together with the fabric for insoles prepared in step 1 of Example 1 and crosslinked and foamed at the same time to prepare an antibacterial and deodorized urethane insole. The antimicrobial effect is shown in Table 1 below.
[비교예][Comparative Example]
실시예 1의 공정에서 제작된 항균처리된 천을 시중의 클로로프렌접착제로서 EVA 스폰지에 접착하여 150℃에서 2분간 건조한 후 150℃에서 성형하여 EVA 안창으로 제조하였다. 항균결과는 표 1에 예시하였다.The antimicrobial treated fabric prepared in Example 1 was bonded to an EVA sponge as a commercial chloroprene adhesive, dried at 150 ° C. for 2 minutes, and molded at 150 ° C. to prepare an EVA insole. Antibacterial results are shown in Table 1.
[표 1]TABLE 1
Claims (4)