KR0184251B1 - The moulding composition of rubber gloves or boots - Google Patents
The moulding composition of rubber gloves or boots Download PDFInfo
- Publication number
- KR0184251B1 KR0184251B1 KR1019960022210A KR19960022210A KR0184251B1 KR 0184251 B1 KR0184251 B1 KR 0184251B1 KR 1019960022210 A KR1019960022210 A KR 1019960022210A KR 19960022210 A KR19960022210 A KR 19960022210A KR 0184251 B1 KR0184251 B1 KR 0184251B1
- Authority
- KR
- South Korea
- Prior art keywords
- rubber
- boots
- composition
- gloves
- rubber gloves
- Prior art date
Abstract
본 발명은 고무장갑 또는 고무장화의 성형용 조성물에 관한 것이다.The present invention relates to a composition for molding rubber gloves or rubber boots.
산업사회의 발달과 생활수준이 향상됨에 따라 고무장갑과 고무장화는 필수품화 되고 있으나, 종래의 고무장갑이나 고무장화는 이의 조성물이 생고무 또는 합성고무에 가류제 또는 충전제를 혼합하고 있는 관계로 이를 장갑 또는 장화로 사용하게 되면 혈액순환을 저해하는 요인이 되어 쉬히 피로감을 느끼게 되며, 또한 장기 착용하면 습기가 차고 세균이 번식함에 따라 무좀 등의 피부질환은 물론 심한 악취가 발생하는 폐단이 있었던 것이다.Rubber gloves and rubber boots are becoming a necessity as the development of industrial society and the standard of living improve. However, conventional rubber gloves or rubber boots are made of glove or filler due to the composition of raw rubber or synthetic rubber mixed with vulcanizing agent or filler. Or if it is used as rain boots, it becomes a factor that inhibits blood circulation, and it is easy to feel fatigue. Also, when long-term wear, moisture and bacteria grows, as well as skin diseases such as athlete's foot, as well as severe odors.
본 발명은 이상의 문제점을 해결하고자 발명한 것으로, 이의 발명 요지는 액상 생고무 또는 합성고무에 원적외선 방사가 탁월한 분말 세라믹과 무기 항균제 및 소취제를 적량 투입 혼련하여 성형용 조성물을 얻은 후 이를 침지 금형으로 침지 성형하여 장갑 또는 장화를 얻을 수 있게 한 것이며, 이와 같이 하여 얻어진 고무장갑이나 고무장화를 착용하게 되면 혈액순환이 촉진되고, 피로감이 감퇴되며, 내부에 땀이 많이 생겨도 습기가 차지 않을 뿐만 아니라 악취나 세균 번식이 억제 되어지게 한 것이다.The present invention has been invented to solve the above problems, the present invention is a powder ceramic, inorganic antimicrobial agent and deodorant excellent in far-infrared radiation to liquid raw rubber or synthetic rubber in a proper amount of kneading to obtain a molding composition and then immersing it in an immersion mold By using the rubber gloves or rubber boots obtained in this way, blood circulation is accelerated, fatigue is reduced, and even if a lot of sweat is formed, moisture is not taken up and odor or bacteria Reproduction is suppressed.
Description
제1도는 본 발명의 조성물을 고무장갑으로 성형한 실시예의 사시도1 is a perspective view of an embodiment in which the composition of the present invention is molded with rubber gloves
제2도는 본 발명의 조성물을 고무장화로 성형한 실시예의 사시도2 is a perspective view of an embodiment in which the composition of the present invention is molded with rubber boots
* 도면의 주요부분에 대한 부호의 설명* Explanation of symbols for main parts of the drawings
1 : 장갑 몸체 1' : 장화 몸체1: Glove Body 1 ': Boots Body
2 : 생고무 3 : 세라믹 분말2: raw rubber 3: ceramic powder
4 : 항균제 5 : 소취제4: antibacterial agent 5: deodorant agent
본 발명은 생고무(또는 합성고무)에 적량의 세라믹 분말과 항균제 및 소취제를 첨가하여서 된 고무장갑 또는 고무장화등의 성형용 조성물에 관한 것이다.The present invention relates to a composition for molding such as rubber gloves or rubber boots by adding an appropriate amount of ceramic powder, antibacterial agent and deodorant to raw rubber (or synthetic rubber).
산업사회의 발달과 문화수준의 향상에 따라 고무장갑이나 고무장화 등은 필수적인 생활수단이 되어지고 있는 바, 종래 사용되고 있는 각종 고무장갑(주방용, 산업용, 의료용)은 천연 생고무(또는 합성고무)에 약간의 가류제(또는 충전제)를 첨가한 조성물로 구성되어 있기 때문에 이를 착용하게 되면 손가락이 압박을 받아 혈액순환을 저해할 뿐만 아니라 장갑 내부에서 생기는 땀 등의 습기에 의해 심한 악취와 발생하게 되고, 이로 인하여 피부에는 습진 발생과 피부각질이 벗겨지는 등의 피부 노화현상을 초래하였던 것이다.Rubber gloves and rubber boots have become an essential means of living in accordance with the development of the industrial society and the improvement of the culture level. Various types of rubber gloves (kitchen, industrial, medical) used in the past are slightly different from natural raw rubber (or synthetic rubber). Since it is composed of a composition containing a vulcanizing agent (or filler), when worn, the finger is compressed and not only inhibits blood circulation, but also causes severe odor due to moisture such as sweat generated inside the gloves. As a result, the skin caused aging symptoms such as eczema and exfoliation.
그리고 모내기와 같은 수중 작업이나 어판장과 같은 습기가 심한 곳에서 착용하고 있는 고무장화의 경우에도 상기와 같은 현상이 생기고 있는 것이다.In the case of the rubber boots worn in the water or the wet place such as fishing grounds, such as planting, the same phenomenon is occurring.
본 발명은 이상의 문제점을 해결하고자 발명한 것으로, 이의 발명 요지는 통상의 생고무(또는 합성고무)에 상온(15∼20℃)에서도 원적외선을 다량으로 방출하는 발산 효율이 월등한 세레샤이드(또는 일라이드) 계열의 세라믹 분말과 무기 항균제 및 소취제를 일정비로 혼합기에 투입하여 상온에서 충분히 혼합된 교질상의 조성물을 얻음을 특징으로 하고, 이와 같이 하여 얻어진 조성물에 통상의 고무장갑 금형(또는 고무장화)을 침지시켜 침지형식으로 고무장갑(또는 고무장화) 몸체를 얻을 수 있게 한 것이다.The present invention has been invented to solve the above problems, and the gist of the present invention is a cereside (or work) having a superior divergence efficiency of releasing a large amount of far-infrared rays at room temperature (15-20 ° C.) to ordinary raw rubber (or synthetic rubber). Ride) ceramic powder, inorganic antimicrobial agent and deodorant were introduced into the mixer at a constant ratio to obtain a gelatinous composition sufficiently mixed at room temperature. The obtained rubber gloves mold (or rubber boots) was added to the composition thus obtained. It is immersed to obtain rubber gloves (or rubber boots) body in immersion type.
이하 본 발명의 구성 및 실시예와 이에 따른 효과를 설명하면 다음과 같다.Hereinafter, the configuration and examples of the present invention and the effects thereof will be described.
(1) 먼저 조성물의 구성 성분에 있어 설명하면 다음과 같다.(1) First, the constituent components of the composition will be described as follows.
(가) 생고무(1)(또는 합성고무) - 가류 처리되지 않은 천연고무를 용제로서 용해시켜 교질상의 액체로 된 것.(A) Raw rubber (1) (or synthetic rubber)-It is made of colloidal liquid by dissolving unvulcanized natural rubber as a solvent.
(나) 세라믹 분말(2) - 상온(15∼20℃)에서도 원적외선 발산 효율이 월등한 세레샤이드계 또는 일라이드 계열의 광석 미세분발.(B) Ceramic powder (2)-Cereide- or ylide-based ore fine powder having excellent far-infrared radiation efficiency even at room temperature (15 to 20 ° C).
(다) 무기 항균제(3) - 무기 이온 교환제와 항균성 금속인 은(Ag)이온 으로서 이루어진 상품명 ALFA-103(일본국 동화 AFLHEM사 제품)(C) Inorganic antimicrobial agents (3)-Trade name ALFA-103 consisting of an inorganic ion exchanger and silver (Ag) ion, which is an antimicrobial metal.
(라) 소취제(4) - 규소(Si) 나트륨(Na) 칼슘(Ca) 철(Fe) 알미늄(Al) 아연(Zn) 마그네슘(Mg) 망간(Mn)으로된 그리콜 긴자슬 화합물로서 상품명 취균 아리아(일본 케미칼 공업(주) 제품)(D) Deodorant (4)-Silicon (Si) Sodium (Na) Calcium (Ca) Iron (Fe) Aluminum (Al) Zinc (Zn) Magnesium (Mg) Glycol Gin chain compound as a manganese (Mn) Aria (product of Nippon Chemical Industries, Ltd.)
(2) 다음으로 배합예를 설명하면 다음과 같다.(2) Next, a combination example is demonstrated.
배합 제1예Formulation Example 1
(가) 생고무(또는 합성고무) 82.5중량%(A) 82.5% by weight of raw rubber (or synthetic rubber)
(나) 세라믹 분말 7.0중량%(B) 7.0% by weight of ceramic powder
(다) 무기 항균제 0.5중량%(C) 0.5% by weight of inorganic antibacterial agent
(라) 소취제 5.0중량%(D) 5.0% by weight of deodorant
(마) 물 5.0중량%(E) 5.0% by weight of water
배합 제2예Formulation Example 2
(가) 생고무(또는 합성고무) 72.5중량%(A) 72.5% by weight of raw rubber (or synthetic rubber)
(나) 세라믹 분말 7.0중량%(B) 7.0% by weight of ceramic powder
(다) 무기 항균제 0.5중량%(C) 0.5% by weight of inorganic antibacterial agent
(라) 소취제 10.0중량%(D) Deodorant 10.0% by weight
(마) 물 10.0중량%(E) 10.0% by weight of water
배합 제3예Combination third example
(가) 생고무(또는 합성고무) 62.5중량%(A) Raw rubber (or synthetic rubber) 62.5 wt%
(나) 세라믹 분말 7.0중량%(B) 7.0% by weight of ceramic powder
(다) 무기 항균제 0.5중량%(C) 0.5% by weight of inorganic antibacterial agent
(라) 소취제 15.0중량%(D) Deodorant 15.0 wt%
(마) 물 15.0중량%(E) 15.0% by weight of water
배합 제4예Combination example 4
(가) 생고무(또는 합성고무) 52.5중량%(A) 52.5% by weight of raw rubber (or synthetic rubber)
(나) 세라믹 분말 7.0중량%(B) 7.0% by weight of ceramic powder
(다) 무기 항균제 0.5중량%(C) 0.5% by weight of inorganic antibacterial agent
(라) 소취제 20.0중량%(D) Deodorant 20.0 wt%
(마) 물 20.0중량%(E) 20.0% by weight of water
(3) 실시예를 설명하면 다음과 같다.(3) An example is described as follows.
[실시예 1]Example 1
의료용 고무장갑을 얻기 위하여 전기한 배합예 1의 조성물에 의료용 장갑 성형의 침지 금형을 1차 침지시킨 다음 약간 건조된 상태에서 2차 침지시켜 건조시켰던 바, 0.2mm 두께 범위의 의료용 고무장갑을 얻게 되었고, 이를 종래의 의료용 고무장갑과 대비한 바, 인장 강도에 있어 별 차이가 없었으나, 이를 착용하였을 때 압박감을 느끼지 않았으며 되려 따뜻하고 안전감이 있었고 혈액 순환이 잘됨을 알수 있었으며, 종래에 비하여 땀이 많이 나는 현상이 있었으나 장갑 내부에 땀이 고인다던가 악취가 생기는 현상이 전혀 없었다.In order to obtain medical rubber gloves, the immersion mold of the medical glove molding was first immersed in the composition of Formulation Example 1 described above, and then dried by secondary immersion in a slightly dried state to obtain medical rubber gloves having a thickness range of 0.2 mm. Compared with the conventional medical rubber gloves, there was no difference in tensile strength, but it did not feel the pressure when wearing it, and it was warm and safe, and blood circulation was good. I had a phenomena, but there was no sweat or odor inside the glove.
[실시예 2]Example 2
주방용 고무장갑을 얻기 위하여 전기한 배합예 2의 조성물에 주방용 장갑 성형의 침지 금형을 1차 침지시킨 다음 침지물이 약간 건조된 상태에서 2차 침지하고, 2차 침지물이 약간 건조된 상태에서 3차 침지시킨 후 건조시켰던 바, 0.5mm 두께 범위의 주방용 고무장갑을 얻게 되었고, 이를 종래의 주방용 고무장갑과 대비한 바, 인장 강도에 있어 종래의 것보다 우수하여 수명이 현저히 연장되었고 착용감 또한 양호하였을 뿐만 아니라 혈액 순환이 잘되어지기 때문에 피로감을 감퇴시켰고 땀이 비교적 많이 나는 편이었으나 장갑 내부에 습기나 나쁜 냄새가 나는 현상은 발견할 수 없었다.In order to obtain the kitchen rubber gloves, the immersion mold of the kitchen glove molding was firstly immersed in the composition of Formulation Example 2 described above, and the second immersion was carried out with the immersion slightly dried, and the second immersion was slightly dried. After being immersed in tea and dried, it was obtained kitchen rubber gloves with a thickness range of 0.5mm, and compared with conventional kitchen rubber gloves, the tensile strength was superior to the conventional ones, which significantly extended the lifespan and was also comfortable. In addition, blood circulation was reduced, and fatigue was reduced and sweating was relatively high. However, moisture or bad smell was not found inside the gloves.
[실시예 3]Example 3
작업용 고무장갑을 얻기 위하여 전기한 배합예 3의 조성물에 작업용 장갑 성형물의 침지 금형을 전기한 바와 같이 1차, 2차, 3차에 걸쳐 침지 성형한 후 이를 착용한 바, 종래의 작업용 고무장갑에 비하여 착용감이 좋아서 작업성을 높일 수 있었고, 착용 과정 손에서 땀이 많이나는 현상이었음에도 불구하고 습기가 차거나 나쁜 냄새가 나는 현상이 전혀 없었다. 그리고 종래의 작업용 고무장갑은 장시간 착용하면 습진 현상과 피부 노화현상이 있었으나, 본 발명의 제품은 이와 같은 현상이 없고 되려 피부가 깨끗해지는 피부 미용효과가 있었다.In order to obtain working rubber gloves, the immersion mold of the work glove molding was immersed in the composition of Formulation Example 3, described above, and then worn over a first, second, and third step, and then worn. Compared to the wearing process, it was able to improve workability, and even though it was a phenomenon of sweating on the hands, there was no phenomenon of getting wet or bad smell. And the conventional rubber gloves for work for a long time when the eczema phenomenon and the skin aging phenomenon, the product of the present invention was not such a phenomenon has a skin beauty effect that the skin becomes clean.
[실시예 4]Example 4
수중 작업용 고무장화를 얻기 위하여 전기한 배합예 4의 조성물에 수중작업용 고무장화 침지 금형을 1차, 2차, 3차에 걸쳐 침지 성형한 바, 0.7mm 두께 범위의 수중 작업용 고무장화를 얻게 되었다. 이를 착용한 바, 종래의 고무장화에 비해 착지감이 한결 부드러웠고 내구성도 탁월하였다. 그리고 혈액순환이 잘되어 압박감이나 피로감이 없었으며 비교적 땀이 많이나는 형편이었음에도 습기가 차거나 악취가 생기는 폐단이 없었다.In order to obtain the rubber boots for underwater work, the rubber boots immersion mold for underwater work was immersed in the composition of Formulation Example 4 described above in the first, second, and third steps to obtain the rubber boots for underwater work in the 0.7 mm thickness range. When worn, the landing was softer and more durable than conventional rubber boots. There was no pressure or fatigue due to good blood circulation, and there was no dampness or odor caused by relatively sweaty conditions.
이상과 같이 본 발명의 조성물을 이용하여 의료용 고무장갑, 주방용 고무장갑, 작업용 고무장갑, 수중 작업용 고무장화를 성형하여 사용한 바, 종래와 비교할 때 착용감이 좋고 비교적 땀이 많이 났으나 상대적으로 습기가 적고 악취도 발생되지 않았다는 점은 본원 발명이 채택하고 있는 조성 성분 가운데있어 세라믹 분말(3)은 상온(15∼20℃)에서도 원적외선 발산이 탁월한 세레샤이드 계열 또는 일라이드 계열의 광석이므로 이를 장갑이나 장화로 만들어 착용하면 인체에서 발산되는 체열(36∼37℃)에 의해 더 많는 원적외선을 발산하게 되고, 이와 같이 발산된 원적외선은 인체의 모세혈관을 자극하여 혈액 순환을 촉진시켜주기 때문에 착용감이 좋을 뿐만 아니라 피로감을 감소 시켜주며, 또한 비교적 땀이 많이 발생한데도 불구하고 습기가 차거나 악취가 생기지 않는 것은 본 발명의 조성물인 소취제가 수분제거와 악취 등을 제거한데 기인한 것이며, 또한 장기 착용하였을 때 무좀등의 세균이 생기지 않는 이유는 본원 발명의 조성물 가운데 함유된 무기 항균제가 각종 세균의 번식을 억제한데 있는 것이다.As described above, medical rubber gloves, kitchen rubber gloves, rubber gloves for work, rubber boots for underwater work are used by using the composition of the present invention. Compared with the conventional one, the wearability is good and the sweat is relatively high, but the moisture is relatively low. The fact that no odor was generated is also among the components of the present invention. Since the ceramic powder (3) is a cereside-based or ylide-based ore having excellent far-infrared radiation even at room temperature (15-20 ° C), it is used as a glove or boots. If the wear is made to wear more far-infrared rays by the body heat (36 ~ 37 ℃) emitted from the human body, the far-infrared rays emitted in this way stimulates the human capillaries to promote blood circulation, as well as good fit Reduces fatigue, and despite being sweaty, wet or bad The reason is that the deodorant which is the composition of the present invention removes moisture and odor, and the reason why bacteria such as athlete's foot does not occur when worn for a long time is because the inorganic antimicrobial agent contained in the composition of the present invention It is to suppress the reproduction.
따라서 본 발명의 조성물은 의료용 고무장갑, 주방용 고무장갑, 작업용 고무장갑 또는 수중이나 습기가 많은곳의 작업 현장에서 착용하는 고무장화의 성형 조성물로 사용하기에 최적되게 하였기 때문에 산업적으로 크게 기여할 수 있어 매우 유용한 발명이다.Therefore, the composition of the present invention can contribute greatly industrially because it is optimized for use as a molding composition for medical rubber gloves, kitchen rubber gloves, working rubber gloves or rubber boots worn in the work site of water or high humidity places. It is a useful invention.
Claims (1)