Fixed Capacitors And Capacitor Manufacturing Machines
(AREA)
Abstract
내용 없음No content
Description
권취형 메탈라이즈드 필름 콘덴서용 메탈라이즈드 플라스틱 필름 제조방법Manufacturing method of metalized plastic film for wound metallized film capacitor
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음As this is a public information case, the full text was not included.
제1도는 권취형 멜라이즈드 필름 콘덴서의 구조도,1 is a structural diagram of a wound melized film capacitor,
제2도는 각종 권취형 메탈라이즈드 필름 콘덴서의 시간경과에 따른 커패시턴스 변화도.2 is a capacitance change diagram of the various winding-type metalized film capacitors over time.
Claims (1)
진공도가 2X10-4Torr미만인 진공조안에서 두께가 2-10㎛인 폴리프로필렌이나 폴리에틸렌테라프타레이트 필름상에 알루미늄 면저항 값으로 4-1000Ω/□이 되도록 진공증착시킨다음 연속적으로 아연을 진공증착시켜 전체 면저항이 2-8Ω/□이 되도록 한 내전압성 및 내산화성이 우수한 권취형 메탈라이드즈 필름 콘덴서용 메탈라이즈드 플라스틱 필름 제조방법.In a vacuum bath with a vacuum degree of less than 2X10 -4 Torr, vacuum deposition is carried out on a polypropylene or polyethylene terarate film having a thickness of 2-10 µm to a value of 4-1000 Ω / □ of aluminum with a sheet resistance of aluminum, followed by vacuum deposition of zinc in total. A method for producing a metallized plastic film for winding type metallized film capacitors having excellent voltage resistance and oxidation resistance with a sheet resistance of 2-8 kV / □.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.※ Note: The disclosure is based on the initial application.
KR1019900009964A1990-07-021990-07-02
Manufacturing method of metalized plastic film for wound metallized film capacitor
KR920003346A
(en)
Application of multiple coatings to a film by coating with polymeric solution, removal of solvent and application of polymeric barrier layer followed by a further coating with polymeric solution and removal of solvent