KR910016640A - 이온교환을 이용한 무색의 은 함유 유리와 이의 제조방법 및 광섬유 소자 - Google Patents
이온교환을 이용한 무색의 은 함유 유리와 이의 제조방법 및 광섬유 소자 Download PDFInfo
- Publication number
- KR910016640A KR910016640A KR1019910004338A KR910004338A KR910016640A KR 910016640 A KR910016640 A KR 910016640A KR 1019910004338 A KR1019910004338 A KR 1019910004338A KR 910004338 A KR910004338 A KR 910004338A KR 910016640 A KR910016640 A KR 910016640A
- Authority
- KR
- South Korea
- Prior art keywords
- alkali metal
- glass
- metal oxide
- ions
- fraction
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (8)
- 적어도 한부분은 이온교환 반응을 통해 생산되며 유리내에서 알카리금속 이온과 교환되는 은이온을 함유하고, 비가교성 산소원자의 분율이 0.03 이하인 원자구조를 갖는 유리가 되는 농도로 알카리금속 산화물과 Al2O3및/또는 B2O3를 기본조성으로 갖되 0.03보다 작은 비가교성 산소원자의 분율를 유지하면서 7.5양이온%까지의 Al2O3및/또는 B2O3가BeO, CaO, Ga2O3, La2O3, MgO, Nb2O5, Ta2O5, Yb2O3, ZnO 및 ZrO2로 구성되는 군에서 선택된 최소한 한개의 금속 산화물로 교환될 수 있는 무색인 알카리금속 산화물 -Al2O3및/또는 B2O3-SiO2유리.
- 제1항에 있어서, 은이온의 농도는 굴절을 구배를 생산하도록 유리의 부분을 따라 변화됨을 특징으로 하는 유리
- (a) 알카리금속 산화물과 Al2O3및/또는 B2O3농도는 비가교성 산소원자의 분율이 0.03보다 작은 원자구조를 갖는 유리가 되는 정도로 존재하는 알카리금속 산화물 -Al2O3및/또는 B2O3-SiO2시스템의 기본 조성을 갖되 비가교성 산소원자의 분율이 0.03보다 작게에 유지되면서 BeO, CaO, Ga2O3, La2O3, MgO, Nb2O5, Ta2O5, Yb2O3, ZnO 및 ZrO2로 구성되는 군으로 부터 선택된 최소한 한개의 금속 산화물로 7.5양이온%까지의 Al2O3및/또는 B2O와 교환될 수 있는 유리제품의 형성단계, (b) 350°∼750℃의 온도에서 적어도 한부분의 알카리금속 이온과 Ag+이온이 1:1의 비율로 교환되기에 충분한 시간동안 외부원의 은이온과 상기 제품을 접촉시키는 단계로 구성됨을 특징으로 하는 무색인 은함유 알칼리금속 산화물 -Al2O3및/또는 B2O3-SiO2유리제품의 제조방법.
- 제3항에 있어서, 접촉단계는 약 400°∼600℃의 온도에서 2∼24시간동안 행함을 특징으로 하는 방법.
- (a) 알카리금속 산화물과 Al2O3및/또는 B2O3농도는 비가교성 산소원자의 분율이 0.03보다 작은 원자구조를 갖는 유리가 되는 정도로 존재하는, 알카리금속 산화물 -Al2O3및/또는 B2O3-SiO2시스템의 기본 조성을 갖되 비가교성 산소원자의 분율이 0.03보다 작게 유지되면서 BeO, CaO, Ga2O3, La2O3, MgO, Nb2O5, Ta2O5, Yb2O3, ZnO 및 ZrO2로 구성되는 군으로 부터 선택된 최소한 한개의 금속 산화물로 7.5양이온%까지의 Al2O3및/또는 B2O와 교환될 수 있는 유리제품의 형성단계, (b) 350°∼750℃의 온도에서 적어도 일부의 알카리금속 이온과 Ag+이온이 1:1의 비율로 교환되도록 부분에 따라 변화될 수 있는 시간동안 외부원의 Ag+이온과 상기 제품을 접축시키는 단계로 구성됨을 특징으로 하는 비가교성 산소원자 분율이 0.03보다 작은 원자구조를 가지는 유리가 되는 농도로 존재하는 알카리금속 산화물 Al2O3및/또는 B2O3를 기본 조성으로 가지는 무색인 알카리 금속 산화물 -Al2O3및/또는 B2O3-SiO2유리에서 굴절율 구배를 형성시키는 방법.
- 제5항에 있어서, 외부원으로 부터의 Ag+이온은 용융 은염 배스 혹은 이온 주입을 통해서 제공됨을 특징으로 하는 방법.
- 적어도 한부분은 이온교혼 반응을 통해 생산되며 유리내에서 알카리금속 이온과 교환되는 은이온을 함유하고, 비가교성 산소원자의 분율이 0.03 이하인 원자구조를 갖는 유리가 되는 농도로 알카리금속 산화물과 Al2O3및/또는 B2O3를 기본조성으로 갖되 0.03보다 작은 비가교성 산소원자의 분율을 유지하면서 7.5양이온%까지의 Al2O3및/또는 B2O3가BeO,CaO, Ga2O3, La2O3, MgO, Nb2O5, Ta2O5, Yb2O3, ZnO 및 ZrO2로 구성되는 군에서 선택된 최소한 한개의 금속 산화물로 교환될 수 있는 무색인 알카리금속 산화물 -Al2O3및/또는 B2O3-SiO2유리로 구성되는 기질을 이용함을 특징으로 하는 광섬유 장치용 소자.
- 제7항에 있어서, Ag+이온의 농도는 굴절율 구배를 생성하도록 일부분을 통해 변화됨을 특징으로 하는 소자.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.