KR840007525A - Flame retardant - Google Patents

Flame retardant Download PDF

Info

Publication number
KR840007525A
KR840007525A KR1019830006069A KR830006069A KR840007525A KR 840007525 A KR840007525 A KR 840007525A KR 1019830006069 A KR1019830006069 A KR 1019830006069A KR 830006069 A KR830006069 A KR 830006069A KR 840007525 A KR840007525 A KR 840007525A
Authority
KR
South Korea
Prior art keywords
weight
parts
ethylene
flame retardant
flame
Prior art date
Application number
KR1019830006069A
Other languages
Korean (ko)
Other versions
KR900003433B1 (en
Inventor
호르드빅 잔
Original Assignee
엔. 스카르 페더슨
에이/에스 노르스크 카벨파브리크
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US06/550,029 external-priority patent/US4543281A/en
Application filed by 엔. 스카르 페더슨, 에이/에스 노르스크 카벨파브리크 filed Critical 엔. 스카르 페더슨
Publication of KR840007525A publication Critical patent/KR840007525A/en
Application granted granted Critical
Publication of KR900003433B1 publication Critical patent/KR900003433B1/en

Abstract

내용 없음.No content.

Description

화염차단물질Flame retardant

본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음As this is a public information case, the full text was not included.

제1도는 생성물 A, C 및 P의 열 안정도를 조절하는 장치.1 is a device for adjusting the thermal stability of products A, C and P.

제2도는 질소대기하에 있는 샘플들의 TG곡선.2 is the TG curve of samples under nitrogen atmosphere.

Claims (21)

에틸렌 공중합체 매트릭스 60-100중량부, 수산화알루미늄 50-450중량부 및 탄산칼슘과 탄산칼슘-마그네슘의 구성기로부터 선별된 것 150-600중량부로 구성되는 화염차단물질Flame barrier material consisting of 60-100 parts by weight of an ethylene copolymer matrix, 50-450 parts by weight of aluminum hydroxide and 150-600 parts by weight selected from the constituents of calcium carbonate and calcium carbonate-magnesium 제1항에 있어서, 탄성제 11-30중량부, 중합체 연화제 0-10중량부, 활제 8-15중량부, 산화칼슘 8-15중량부 및 색제 1중량부를 포함하는 화염차단물질.The flame retardant according to claim 1, comprising 11-30 parts by weight of an elastomer, 0-10 parts by weight of a polymer softener, 8-15 parts by weight of lubricant, 8-15 parts by weight of calcium oxide, and 1 part by weight of a colorant. 제2항에 있어서, 상기 활제가 파라핀왁스로 구성되는 화염차단물질.The flame retardant of claim 2, wherein said lubricant is comprised of paraffin wax. 제2항에 있어서, 상기 탄성제가 에틸렌프로펜 고무로 구성되는 화염차단물질.The flame retardant according to claim 2, wherein the elastic agent is composed of ethylene propene rubber. 제2항에 있어서, 상기 색제가 카본블랙으로 구성되는 화염차단물질.The flame retardant of claim 2, wherein the colorant comprises carbon black. 제2항에 있어서, 상기 공중합체 100중량부당 약 1.5중량부가 존재하는 폴리트리메틸 디히드로퀴놀린으로 구성되는 산화방지제를 포함하는 화염차단물질.The flame retardant of claim 2, wherein the flame retardant comprises an antioxidant comprised of polytrimethyl dihydroquinoline present in about 1.5 parts by weight per 100 parts by weight of the copolymer. 제1항에 있어서, 코팅이나 페인팅 조성물 형태의 화염차단물질.The flame retardant of claim 1, wherein the flame retardant is in the form of a coating or painting composition. 제1항에 있어서, 상기 에메렌 공중합체가 에틸렌-비닐 아세테이트, 에틸렌-아크릴 메타크틸산, 에렌릴산, 에틸렌-에틸아크릴레이트, 에틸렌-비닐 아세테이트-메타크릴산, 에틸렌-이소부틸 아크릴레이트, 에틸렌메틸 메타크릴레이트 및 에틸렌-비닐 아세테이트-카본 모녹사이드로 구성되는 기로부터 선별된 화염차단물질.The method of claim 1, wherein the ethylene copolymer is ethylene-vinyl acetate, ethylene-acrylic methacrylic acid, eryryl acid, ethylene-ethyl acrylate, ethylene-vinyl acetate-methacrylic acid, ethylene-isobutyl acrylate, ethylene Flame barrier material selected from the group consisting of methyl methacrylate and ethylene-vinyl acetate-carbon monoxide. 제1항에 있어서, 상기 에틸렌 공중합체가 에틸렌-에틸 아크릴레이트인 화염차단물질.The flame retardant of claim 1, wherein said ethylene copolymer is ethylene-ethyl acrylate. 에틸렌-에틸 아크릴레이트 100중량부, 수산화알루미늄 220중량부, 탄산칼슘 220중량부, 활제 10중량부, 탄성제 11중량부, 산화칼슘 11중량부 및 색제 1중량부로 구성되는 강성의 화염차단물질.Rigid flame barrier material consisting of 100 parts by weight of ethylene-ethyl acrylate, 220 parts by weight of aluminum hydroxide, 220 parts by weight of calcium carbonate, 10 parts by weight of lubricant, 11 parts by weight of elastomer, 11 parts by weight of calcium oxide and 1 part by weight of colorant. 에틸렌-에틸 아크릴레이트 80중량부, 수산화알루미늄 150중량부, 탄산칼슘 150중량부, 활제 10중량부, 탄성제 30중량부, 산화칼슘 11중량부, 중합체 연화제 10중량부 및 색제 1중량부로 구성되는 가요성 화염차단물질.80 parts by weight of ethylene-ethyl acrylate, 150 parts by weight of aluminum hydroxide, 150 parts by weight of calcium carbonate, 10 parts by weight of lubricant, 30 parts by weight of elastomer, 11 parts by weight of calcium oxide, 10 parts by weight of polymer softener and 1 part by weight of colorant. Flexible flame retardant. 제1항에 있어서, 환경온도에서 건조시킨 성분을 혼합하고 이들 혼합물을 약 150℃의 용융온도에서 축출시켜 연속형태의 축출물을 형성하고 이러한 연속 축출물을 분획구분시키므로서 구성되는 화염차단물질을 제조하는 방법.The flame retardant according to claim 1, wherein the flame-blocking material constituted by mixing the components dried at an environmental temperature and extracting the mixture at a melting temperature of about 150 DEG C to form a continuous extract and fractionating the continuous extract. How to manufacture. 제12항에 있어서, 상기 방법에 의해 제조된 분획구분된 축축물.The fractionated moist product of claim 12 produced by the method. 제13항에 있어서, 분획구분된 축출물을 약 150℃에서 바람직한 형태로 축출시키므로서 구성되는 물질을 코팅시킨 화염차단물질을 제조하는 방법.15. The method of claim 13, wherein the material is coated with a material that is constructed by discharging the fractionated leachate into the desired form at about 150 < 0 > C. 에틸렌-에틸 아크릴레이트 중합체 80-100중량부, 수산화알루미늄 150-200중량부, 탄산칼슘과 탄산칼슘-마그네슘의 구성기로부터 선별된 것 150-200중량부, 탄성제 11-30중량부, 중합체 연화제 0-10중량부, 활제 10중량부, 산화칼슘 11중량부 및 색제 1중량부로 구성되는 전기케이블 보호용 도관형태의 화염차단물질..80-100 parts by weight of ethylene-ethyl acrylate polymer, 150-200 parts by weight of aluminum hydroxide, 150-200 parts by weight selected from the constituents of calcium carbonate and calcium carbonate-magnesium, 11-30 parts by weight of elastomer, softener Flame shielding material in the form of a conduit for protecting an electrical cable, comprising 0-10 parts by weight, 10 parts by weight of lubricant, 11 parts by weight of calcium oxide, and 1 part by weight of colorant. 제2항에 있어서, 성분들을 분말형태로 혼합하여 약 30℃에서 유리된 혼합물을 형성하고 상기 혼합물을 약 130℃에서 축출시켜 산출된 축출물을 냉각하고 환경온도에서 저장하기 위해 입자로 분획 구분시키므로서 구성되는 화염차단물질을 제조하는 방법.The method of claim 2, wherein the components are mixed in powder form to form a free mixture at about 30 ° C., and the mixture is fractionated into particles for cooling the resulting effluent by storage at about 130 ° C. Method for producing a flame barrier material consisting of. 제16항에 있어서, 상기 방법에 의해 제조된 입자를 120°까지의 온도에서 축출시키므로서 구성되는 관형태의 화염차단물질을 제조하는 방법.The method according to claim 16, wherein the particles produced by the method are expelled at a temperature of up to 120 ° to produce a tubular flame shield. 제17항에 있어서, 상기 방법에 의해 제조된 관형태의 축출된 화염차단물질.18. A tubular evicted flame arrestor according to claim 17, wherein said tubular form is produced by said method. 제18항에 있어서, 와부스틸 브레이딩 및 외부 보호용 코팅제에 의해 제조된 관형태의 축출된 화염차단물질.19. A tubular, evicted flame retardant according to claim 18, which is prepared by Waboosteel braiding and an external protective coating. 제19항에 있어서, 외부보호용 코팅제가 가소성 물질인 축출된 화염차단물질.20. The withdrawn flame retardant of claim 19, wherein the outer protective coating is a plastic material. ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.※ Note: The disclosure is based on the initial application.
KR1019830006069A 1982-12-21 1983-12-21 Fire resistant material KR900003433B1 (en)