KR20230018471A - 연속 섬유 강화 요소들을 포함하는 강화 구조물 및 그 제조 방법 - Google Patents

연속 섬유 강화 요소들을 포함하는 강화 구조물 및 그 제조 방법 Download PDF

Info

Publication number
KR20230018471A
KR20230018471A KR1020227046168A KR20227046168A KR20230018471A KR 20230018471 A KR20230018471 A KR 20230018471A KR 1020227046168 A KR1020227046168 A KR 1020227046168A KR 20227046168 A KR20227046168 A KR 20227046168A KR 20230018471 A KR20230018471 A KR 20230018471A
Authority
KR
South Korea
Prior art keywords
reinforced
fiber
cross
matrix material
elements
Prior art date
Application number
KR1020227046168A
Other languages
English (en)
Inventor
랄프 펑크
젠스 정
마틴 웰시
Original Assignee
알바니 엔지니어드 콤포짓스, 인크.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 알바니 엔지니어드 콤포짓스, 인크. filed Critical 알바니 엔지니어드 콤포짓스, 인크.
Publication of KR20230018471A publication Critical patent/KR20230018471A/ko

Abstract

강화 구조물들이 개시된다. 구조물들은 매트릭스 재료에 매립된(embedded) 연속 섬유들을 갖는 강화 요소들로 구성된다. 강화 요소들은 원하는 형상의 강화 구조물을 형성하기 위해 매트릭스 재료에 결합된다(combined).

Description

연속 섬유 강화 요소들을 포함하는 강화 구조물 및 그 제조 방법
본 발명은 연속 섬유 강화 필라멘트들(continuous fiber reinforcing filaments)로 강화된 프로파일을 포함하는 열가소성 구조물(thermoplastic structure)에 관한 것이다.
열경화성 또는 열가소성, 엘라스토머(elastomer), 탄소, 그라파이트 또는 세라믹으로 만들어진 매트릭스 뿐만 아니라, 예를 들어, 탄소(carbon), 유리, 아라미드(aramid), 세라믹 또는 현무암(basalt) 섬유들과 함께 고탄력(highly resilient) 섬유 복합 재료들(composite materials) 및 관련된 재료들을 사용하려면, 재료에 적합한 동력 전달(transmission of power)을 위해 적절한 구조들(constructions)을 사용해야 한다. 재료-관련(Material-related)은 섬유 방향(direction) 및 그것의 교차한 곳에(across) 서로 다른 기계적 특성들(properties)과 관련된 재료의 이방성(anisotropy)이 목표 방식(targeted manner)으로 사용된다는 것을 의미한다.
동력 전달(power transmission)을 위한 섬유 복합 재료로 만들어진 커넥팅 로드들(Connecting rods)은 특히 안내(guidance) 및 기계적 보관을 위해, 지지(support)를 위해, 브레이싱(bracing)을 위해, 또는 연결(connection)을 위해 사용된다. 섬유 복합 재료로 만들어진 커넥팅 로드들은 수년 동안 알려져 왔다. 이러한 커넥팅 로드들은 배타적이지는 않지만, 바람직하게는 항공기(aircraft) 또는 우주선(spacecraft)에 사용된다. 예를 들어 비행기들, 회전익 항공기(rotary-wing aircraft), 비행선들(airships), 무인 항공 시스템들(unmanned aviation systems), 로켓들 또는 인공위성들(satellites)과 같은 항공기 및 우주선의 커넥팅 로드들은 주로 압축력과 인장력들(compressive and tensile forces) 모두에 의해 축 방향(axially)으로 하중을 받는다.
무게(weight) 및 비용 절감들에 대한 요구들이 증가함에 따라 열경화성 섬유 복합 재료들로 만들어진 관형 본체들(tubular bodies)이 있는 스트럿들(struts)에 대한 알려진 디자인들의 잠재력에 한계가 있다.
열가소성 구조물(thermoplastic structure)은 커넥팅 로드들 또는 인장 및 압축 스트럿들(tension and compression struts)에 사용될 수 있으며, 외부 치수들(external dimensions)이 큰 스트럿은 미리 정해진(predetermined) 설치 공간(installation space) 내에서 달성될 수 있다.
열경화성 매트릭스(thermosetting matrix) 기반으로 섬유-강화 파이프들 및 프로파일들(profiles)을 사용할 때, 충격으로 인한 라미네이트(laminate) 손상을 가능한 한 낮게 유지하는 근본적인 문제점이 종종 있다. 고가의 강인한(tough) 변형 수지(modified resin) 시스템들은 종종 문제가 있는 충격 손상에 사용된다. 반대로, 열가소성 매트릭스 재료를 사용하는 것은 충격 거동(impact behavior)에 긍정적인 영향을 미친다.
섬유-강화 프로파일들의 생산(Production) 비용들은 매우 높지만 그럼에도 불구하고 프로파일 형상(geometry)은 매우 제한적이다. 열경화성 매트릭스로 만들어진 프로파일들은 완성된 후에는 재구성(reshaped)될 수 없으며, 열가소성 폴리머(thermoplastics)와 비교하여 열경화성 폴리머(thermosets)의 충격 거동이 더 나쁘다. 게다가, FST (화재 연기 및 독성(fire smoke and toxicity)) 승인을 받았으며 항공 부문(aviation sector)을 포함한 특정 환경들에서 사용될 수 있는, 제한된 수의 열경화성 폴리머만 있다.
본 기술은 연속 섬유 강화 필라멘트들로 강화된 프로파일을 포함하는 열가소성 구조물을 제공할 수 있다. 이 프로파일은 인장 및 압축 스트럿들 및 기타 지지(supporting) 구조물들의 기반(basis)을 형성할 수 있다.
본 발명의 실시예는 연속 섬유-강화 필라멘트들 및 제1 매트릭스 재료를 포함하는 횡단면의 프로파일(cross-sectional profile)을 포함하는 강화 구조물(reinforced structure)을 포함한다. 연속 섬유-강화 필라멘트들은 연속 섬유-강화 요소들을 형성하기 위해 제1 매트릭스 재료에서 섬유-강화 요소의 길이방향 축(longitudinal axis)을 따라 매립된다(embedded).
일부 실시예들에서, 강화 구조물은 제2 매트릭스 재료를 더 포함한다. 연속 섬유-강화 요소들은 횡단면의 프로파일을 형성하기 위해 제2 매트릭스 재료에 매립된다(embedded).
한 변형에서, 제1 매트릭스 재료 및 제2 매트릭스 재료는 상이한 재료들이다. 다른 변형에서, 제1 매트릭스 재료 및 제2 매트릭스 재료는 같은 재료이다.
일 측면에서, 강화 구조물의 횡단면의 프로파일은 삼각형, 원형, 직사각형, 및 T-자형(T-shaped)으로 구성된 그룹으로부터 선택된 형상(shape)을 포함할 수 있다. 구현에서, 횡단면의 프로파일은 삼각형, 원형, 및 직사각형으로 구성된 그룹으로부터 선택된 형상의 중공 영역(hollow area)을 둘러싸는(surrounding) 외부 윤곽(outer contour)을 포함한다.
다른 측면에서, 연속 섬유-강화 요소들의 횡단면의 프로파일은 삼각형, 원형, 직사각형, 사다리꼴, 및 육각형으로 구성된 그룹으로부터 선택된 형상일 수 있다. 특정 측면에서, 연속 섬유-강화 요소들은 0.4 mm 이상의 직경(diameter)을 갖는 원형 횡단면의 형상(circular cross-sectional shape)을 포함한다.
또 다른 측면에서, 강화 구조물은 다른 연속 섬유-강화 요소들과 연결(interlocking)되거나 또는 상호교합(intermeshing)하기 위한 외부 윤곽을 포함하는 연속 섬유-강화 요소들을 포함한다.
강화 구조물은 연속 섬유-강화 요소의 섬유 부피 분율(volume fraction)이 적어도 35%일 수 있다.
특정 실시예에서, 강화 구조물은 관형 횡단면의 프로파일을 포함한다. 연속 섬유-강화 요소들은 삼각형, 원형, 직사각형, 사다리꼴, 및 육각형으로 구성되는 그룹으로부터 선택된 횡단면의 형상을 포함할 수 있다. 하나의 구현에서, 연속 섬유-강화 요소들은 0.4 mm 이상의 직경을 갖는 원형 횡단면의 형상을 포함한다. 임의의 관형 강화 구조물들에서, 연속 섬유-강화 요소의 섬유 부피 분율은 적어도 35%일 수 있다.
관형 횡단면의 프로파일을 포함하는 강화 구조물의 일 측면에서, 섬유-강화 요소들은 관형 횡단면의 직경 (D)의 원호 세그먼트(arc segment)인 횡단면의 형상을 포함할 수 있다. 섬유 강화 요소들은 강화 구조물의 관형 배열(tubular arrangement)을 형성한다. 단방향(unidirectional) 강화 테이프의 와인딩 층(winding layer)은 원호 세그먼트들의 관형 배열의 외부 표면 주위 및 외부 표면 상에(around and on an outer surface) 감길(wound) 수 있다.
관형 횡단면의 프로파일을 포함하는 강화 구조물의 다른 측면에서, 섬유-강화 요소들은 관형 횡단면의 직경 (D)의 원호 세그먼트인 횡단면의 형상을 포함할 수 있다. 원호 세그먼트들은 섬유-강화 요소들의 모서리들(edges) 사이에 갭들(gaps)을 포함하는 강화 구조물의 관형 배열을 형성한다. 매트릭스 재료는 관형 배열의 외부 표면을 둘러싸고 갭들을 채울 수 있다. 단방향 강화 열가소성 테이프의 와인딩 층은 매트릭스 재료의 외부 표면 주위 및 외부 표면 상에 감길(wound) 수 있다.
본 발명의 실시예는 관형 횡단면의 직경 (D)의 원호 세그먼트들 중 적어도 2개를 형성하는 단계 및 적어도 2개의 원호 세그먼트들을 갖는 강화 구조물의 관형 배열을 형성하는 단계를 포함하는 관형 횡단면의 프로파일을 갖는 강화 구조물을 형성하는 방법이다. 이는 상기 형성된 관형 배열의 외부 표면 주위 및 외부 표면 상에 층(layer)을 감는(winding) 단계를 포함할 수 있다.
강화 구조물을 형성하는 방법의 일 측면에서, 인접한(adjacent) 원호 세그먼트들의 모서리들은 접촉 위치들(contact locations)에서 서로 접촉하고(contact) 접착된다(adhered). 특정 구현에서, 원호 세그먼트들은 서로 접착하기 위한 연결되는(interlocking) 요소들이다.
강화 구조물을 형성하는 방법의 다른 측면에서, 관형 배열을 형성하고 그리고 원호 세그먼트들의 외부(outside) 표면에 매트릭스 재료를 적용하는, 인접한 원호 세그먼트들의 모서리들 사이에 갭이 있고, 매트릭스 재료는 갭들을 채운다.
관형 배열을 포함하는 강화 구조물을 형성하는 방법의 임의의 측면에서, 외부 표면에 감긴(wound) 층은 단방향 강화 열가소성 테이프일 수 있다. 또는, 상기 층은 단방향 강화 열경화성 테이프이다. 이러한 측면들 중 하나에서, 상기 방법은 정의된(defined) 와인딩 피드 폭 및 회전(winding feed width and rotation)을 갖고 프리텐션(pretension) 하에 층을 감는 단계 및 결합(bonding)을 돕기 위한 관형 배열 및 테이프의 매트릭스를 용융시키기(melt) 위해 층을 가열하는 단계를 포함한다.
도 1은 원형 횡단면(cross-section)을 포함하는 섬유-강화 요소의 횡단면의 프로파일을 도시한다.
도 2는 직사각형 횡단면을 포함하는 섬유-강화 요소의 횡단면의 프로파일을 도시한다.
도 3은 직조된(woven) 섬유-강화 요소의 횡단면을 도시한다.
도 4A-4D는 섬유-강화 요소들로 구성된 구조적(structural) 요소들의 횡단면의 형상들의 예들을 도시한다.
도 5는 연속 섬유-강화 연결된(interlocking) 요소의 횡단면의 프로파일을 도시한다.
도 6은 도 5의 적어도 2개의 연결된(interlocking) 섬유-강화 요소들을 포함하는 구조적 관형 요소의 횡단면의 형상의 상세도를 도시한다.
도 7은 원호 세그먼트 프로파일을 포함하는 섬유-강화 요소의 횡단면을 도시한다.
도 8은 강화 층(layer of reinforcement)과 함께 도 7의 요소들을 사용하는 제1 강화 관형 구조물(first reinforced tubular structure)의 횡단면의 프로파일을 도시한다.
도 9는 강화 층과 함께 도 7의 요소들을 사용하는 제2 강화 관형 구조물의 횡단면의 프로파일을 도시한다.
도 10A-10B는 강화된 관형 구조물을 달성하기 위해 원호 세그먼트 프로파일을 포함하는 여러 섬유-강화 요소들을 고정하기 위해 후프 층(hoop layer)을 적용하기 위한 메커니즘을 도시한다.
본 명세서에서 용어들 "포함하는(comprising)" 및 "포함한다(comprises)"는 "포함하는(including)", "포함한다(includes)" 또는 "갖는(having)"을 의미할 수 있거나, 또는 미국 특허법에서 "포함하는(comprising)" 또는 "구성한다(comprises)" 용어에 일반적으로 부여되는 의미를 가질 수 있다. 용어들 "본질적으로 구성된(consisting)" 또는 "본질적으로 구성되다(consists)"는 청구범위에 사용된 경우 미국 특허법에서 부여된 의미를 갖는다. 본 발명의 다른 측면들은 다음 개시에서 기술되거나 (및 본 발명의 범위 내에서)그로부터 자명하다.
용어들 "실들(threads)", "섬유들(fibers)", "필라멘트들(filaments)", 및 "얀들(yarns)"은 다음 설명에서 상호교환적으로 사용된다. 본 발명에서 사용된 "실들", "섬유들", "필라멘트들" 및 "얀들(yarns)"은 모노필라멘트들(monofilaments), 멀티필라멘트 얀들, 꼬인(twisted) 얀들, 멀티필라멘트 토우들(multifilament tows), 직조된(textured) 얀들, 꼰(braided) 얀들, 코팅된(coated) 얀들, 이성분(bicomponent) 얀들 뿐만 아니라 당업자에게 공지된 임의의 재료로 만들어진 얀들을 지칭할 수 있다. 얀들(Yarns)은 탄소, 유리섬유, 면, 아라미드, 폴리아미드, 폴리에스테르(polyester), 금속, 폴리에틸렌, 및/또는 원하는 물리적, 열적, 화학적 또는 다른 특성들을 나타내는 다른 재료들로 만들어질 수 있다.
용어들 "매립된(embedded)" 및 "캡슐화된(encapsulated)"은 상호교환적으로 사용된다.
본 발명에 따른 섬유-강화 구조물들은 강도 및 강성(strength and rigidity)과 같은 기계적 특성들을 향상시키기 위해 프로파일 횡단면이 연속 섬유-강화 요소들로 채워지는 것을 특징으로 할 수 있다. 특정 적용(application)에서, 이러한 섬유-강화 구조물들은 커넥팅 로드들 또는 인장 및 압축 스트럿들과 같은 지지 부재들(support members)을 위한 횡단면의 프로파일을 제공할 수 있으며, 여기서 가능한 가장 큰 외부 치수들(external dimensions)을 갖는 스트럿은 미리 정해진(predetermined) 설치 공간 내에서 달성될 수 있다.
도 1은 섬유-강화 요소 100의 횡단면의 프로파일을 도시한다. 원형 횡단면의 형상은 도시되지만, 직사각형, 삼각형, 사다리꼴, 육각형 등을 포함하지만, 이에 제한되지 않는 다른 횡단면의 형상들이 고려된다. 연속 섬유-강화 요소들은 적어도 35%의 섬유 부피 함량(volume content)을 가질 수 있다. 섬유-강화 요소는 매트릭스 104에 매립된(embedded) 연속 섬유-강화 필라멘트들 105을 포함하고, 섬유-강화 요소 100의 길이에 걸쳐 연속적이며, 횡단면의 프로파일에 걸쳐 분포된다(distributed). 연속 섬유-강화 요소들 100은 적어도 0.40 mm의 직경을 가질 수 있다.
섬유-강화 필라멘트들은 직물들(textiles), 탄소, 유리, 현무암, 플라스틱, 세라믹, 아라미드, 폴리에스테르, 나일론, 및 레이온(rayon)을 포함하지만, 이에 제한되지 않는 재료들로 구성된다. 매트릭스 재료는 폴리프로필렌 (PP), 폴리아마이드(Polyamide) (PA), 아크릴로니트릴 부타디엔 스티렌(Acrylonitrile butadiene styrene) (ABS), 폴리에틸렌 이민(Polyethylene Imine) (PEI), 폴리프탈아마이드(Polyphthalamide) (PPA), 폴리페닐렌 설파이드(Polyphenylene sulfide) (PPS), 폴리아릴에테르케톤(Polyaryletherketone) (PAEK), 폴리에테르케톤케톤(Polyetherketoneketone) PEKK), 또는 폴리에테르에테르케톤(Polyetheretherketone) (PEEK)을 포함하지만, 이에 제한되는 것은 아니다. 직물들(Textiles)은 직조된 직물들(woven fabrics), 꼰(braids), 니트된 직물들(knitted fabrics), 및 레이드 직물들(laid fabrics)을 형성하기 위해 유리, 탄소, 현무암, 세라믹 및/또는 플라스틱으로 만들어진 단일(single) 섬유 필라멘트들 또는 로빙들(rovings)을 포함한다.
열가소성, 연속 섬유-강화 요소는 예를 들어, 연속 섬유-강화 필라멘트들이 공급(fed)되는 인발(pultrusion) 공정에 의해 생산될 수 있다.
도 2는 직사각형 횡단면(cross-section) 갖고, 매트릭스 재료 204에 매립된(embedded) 섬유-강화 필라멘트들 205을 포함하는, 섬유-강화 요소 200의 연속적인 섬유-강화 전체(full) 프로파일을 도시한다. 섬유-강화 요소의 치수들은 너비(wide) 0.5 인치(12.7 mm) × 두께 0.008 인치 (0.2 mm) 이상일 수 있다.
도 3은 섬유들 310과 섞여 짜여진(interwoven) 직물 강화(textile reinforcing) 필라멘트들 307 및 매트릭스 재료 304를 포함하는, 직조된(woven) 섬유-강화 요소 300의 횡단면을 도시한다. 반-제품된 직물(semi-finished textile) 생산품들(products)을 사용함으로써, 섬유들 310을 갖는 요소 300의 길이방향 축(longitudinal axis)에 대해 가로축으로(transversely) 추가적인 강화들(reinforcements)이 달성될 수 있다. 요소 300은 임의의 형상이 고려되는 바와 같이 편의상 직사각형 횡단면의 형상을 갖는 것으로 도시되어 있다. 타원형(oval-shaped) 횡단면을 갖는 직물 강화 필라멘트들(Textile reinforcing filaments) 307이 도시되었지만 다른 형상들이 고려된다. 또한, 직물 강화 필라멘트들 307의 형상은 압축력들(compressive forces)을 받을 때 변경될(altered) 수 있다.
직조된 섬유-강화 요소들 300은 본 발명에서 설명된 바와 같이 임의의 원하는 횡단면의 프로파일을 갖는 강화 구조물들을 형성하기 위해 결합될(combined) 수 있다.
도 4A-4D는 전술한 섬유-강화 요소들로 구성될 수 있는 구조적 요소들의 횡단면의 형상들의 비-제한적인 예들을 도시한다. 다른 형상들이 고려되지만, 원형 섬유-강화 요소들이 편의상 표시된다. 도 4A-4C의 횡단면의 형상들은 형상들의 둘레들(perimeters)인 외부 윤곽들(outer contours)이다. 즉, 구조적 요소들의 둘레들은 중공 영역 H를 둘러싸고 있다.
도 4A는 매트릭스 재료 430에 매립된(embedded) 섬유-강화 요소들 410로 구성된 원형 구조적 요소 400을 도시한다. 위에서 논의된, 매트릭스 재료 430는, 섬유-강화 요소 410의 매트릭스 재료와 동일하거나 다를 수 있다. 도 4B는 매트릭스 재료 430에 매립된(embedded) 섬유-강화 요소들 410로 구성된 직사각형 구조적 요소 404를 도시한다. 도 4C는 매트릭스 재료 430에 매립된(embedded) 섬유-강화 요소들 410로 구성된 삼각형 구조적 요소 406를 도시한다. 도 4D는 매트릭스 재료 430에 매립된 섬유-강화 요소들 410로 구성된 T-자형 구조적 요소 408를 도시한다. 도 4A-D는 섬유-강화 요소들로부터 형성될 수 있는 구조적 요소 형상들의 예들을 도시한다. 다른 구조적(structural) 요소 형상들(element shapes)이 고려된다.
도 5는 연속 섬유-강화 필라멘트들 510과 관련된 연속 섬유-강화 연결된(interlocking) 요소 500의 단면(section)을 도시한다. 섬유-강화 필라멘트들은 도 1관련하여 전술한 것들과 유사할 수 있다. 섬유-강화 필라멘트들은 요소 500의 길이를 따라 단방향으로 놓일(lie) 수 있고 매트릭스 재료 540에 매립될 수 있다.
연속 섬유-강화 요소들 500은 기능적 외부 윤곽 502의 결과로 연결되(interlock)거나 상호교합(intermesh)될 수 있다. 연결된(interlocking) 요소 500는 머리 부분(head portion) 504 및 꼬리 부분(tail portion) 506을 갖는 하나의 가능한 연결된(interlocking) 기능적 외부 윤곽 502을 도시한다. 머리 부분 504은 도 6에 도시된 바와 같이, 꼬리 부분 506에 연결되(interlock)거나 중첩되(nest)도록 형상화된다. 당업자에게 공지된 연결되는(interlock) 다른 기능적 외부 윤곽들은 현재 개시된 기술의 발명적 개념을 벗어나지 않고 고려된다.
도 6은 적어도 2개 연결된(interlocking) 섬유-강화 요소들 500을 포함하는 강화 구조물 600의 하나의 구현을 도시한다. 섬유-강화 구조물 600은 원하는 외부 형상 602을 형성하기 위해, 섬유-강화 연결된(interlocking) 요소들의 매트릭스 재료 540와 동일하거나 상이할 수 있는, 매트릭스 재료 640 내의 적어도 2개 섬유-강화 요소들 500의 연결되는(interlocking) 것에 의해 형성될 수 있는, 임의의 원하는 외부 형상을 가질 수 있다.
도 7은 매트릭스 재료 706에 매립된 섬유-강화 필라멘트들 705로 구성된 섬유-강화 요소 702의 다른 구현의 횡단면을 도시한다. 섬유-강화 요소들 702은 원(circle)의 원호 세그먼트일 수 있다. 요소 702의 두께(thickness) W는 1 mm일 수 있지만 임의의 원하는 두께가 형성될 수 있다.
도 8은 섬유-강화 요소들 802, 804, 806, 808로부터 형성된 강화된 관형 구조물 801의 횡단면을 도시한다. 각각의 섬유-강화 요소들 802, 804, 806, 808은 도 7과 관련하여 위에서 논의된 바와 같이 형성된 원의 원호 세그먼트일 수 있다. 요소들 802, 804, 806, 808은 와인딩(winding) 층 803에 의해 요소들 802, 804, 806, 808의 외부에서 둘러싸이고 접촉될 수 있는, 직경 D를 갖는 원을 형성한다. 도시된 바와 같이, 각각의 섬유-강화 요소 802, 804, 806, 808는 1/4(quarter) (90°) 원호 세그먼트이다. 섬유-강화 요소들이 2개 이상 있을 수 있으므로, 설명의 편의를 위해 도 8을 도시한다. 더욱이, 그들 요소들은 임의의 수의 원호(arc) 각도들(degrees)일 수 있으며 반드시 동일한 수의 원호 각도들일 필요는 없다.
요소들 802, 804, 806, 808은 관형 구조물을 형성하기 위해 접촉 위치들 810에서 조립될(assembled) 수 있다. 요소들 802, 804, 806, 808은 당업자에게 공지된 임의의 알려진 메커니즘에 의해 접촉 위치들 810에서 서로 접착될(adhered) 수 있다. 대안적으로, 원호 세그먼트들은 원호 세그먼트들의 내부 표면 상의, 접착제 등을 위한 접착 지점들(adherence points)을 갖는 맨드릴(mandrel) 상에 미리 고정될 수 있다. 더욱이, 요소들 802, 804, 806, 808은 도 5와 관련하여 위에서 논의된 바와 같이 연결된(interlocking) 요소들이 됨으로써 서로 접착될 수 있다 . 와인딩 층 803은 후술하는 바와 같이 형성된 관형 구조물 주위에 감긴(wound) 단방향 강화 열가소성 테이프를 사용하여 형성될 수 있다.
도 9는 섬유-강화 요소들 902, 904, 906, 908로부터 형성된, 강화된 관형 구조물 901의 횡단면을 도시한다. 각각의 섬유-강화 요소들 902, 904, 906, 908은 도 7과 관련하여 위에서 논의된 바와 같이 형성된 원의 원호 세그먼트일 수 있다. 요소들 902, 904, 906, 908은 원호 세그먼트들 사이에 갭들 910을 갖는 원을 형성한다. 매트릭스 재료 914는 갭들 910을 채울 수 있고, 또한 공-압출(co-extrusion) 공정 또는 다른 알려진 수단들(means)에 의해 달성될 수 있는, 그들의 외부에서 요소들을 둘러싸고 접촉할 수 있다. 와인딩 층 903은 매트릭스 재료 914의 외부를 둘러싸고 접촉할 수 있다. 와인딩 층 903은 후술하는 바와 같이, 형성된 관형 구조물 주위에 감긴(wound) 단방향 강화 열가소성 또는 열경화성 테이프를 사용하여 형성될 수 있다. 도 9의 도시는 섬유-강화 요소들이 2개 이상일 수 있으므로 설명의 편의를 위한 것이다. 더욱이, 이들 요소들은 임의의 수의 원호 각도들일 수 있으며 반드시 동일한 수의 원호 각도일 필요는 없다.
도 10A는 원호 세그먼트 요소들 802, 804, 806, 808일 수 있는, 원호 세그먼트 요소들 1002이 맨드릴 1007 상에 배치되는(positioned) 제1 공정 단계를 도시한다.
도 10B는 맨드릴 1007 상에 배치된 원호 세그먼트 요소들 1002이 단방향 강화 열가소성 테이프 1012로 제조된 와인딩 층 1003에 의해 강화되는 제2 공정 단계를 도시한다. 와인딩 층 1003은 예를 들어 열가소성 와인딩(winding)에 의해 생성된 후프(와인딩 층 1003) 와인딩으로서 도시되며, 열원(heat source) 1008은 테이프 1012의 매트릭스를 녹이고(melts) 프리텐션(pretension) 1010 하에 정의된 와인딩 피드 폭(feed width) 1011 및 회전(rotation) 1009으로 감긴다(wound). 후프 와인딩에 의해, 원호 세그먼트 요소들이 튜브 본체에 고정되고 통합된다(consolidated). 와인딩 층은 교차(cross)-감긴(wound) 층일 수도 있다. 교차-감긴(wound) 층들의 경우, 와인딩 층들은 원호 세그먼트들의 길이방향 축에 대해 약 90°의 후프 와인딩 각도(angle)에서 벗어난다. 예를 들어, 테이프의 교차-감긴(wound) 층은 원호 세그먼트들의 길이방향 축에 대해 ±45°로 감길 수 있다. 다른 와인딩 각도들도 고려된다. 와인딩 층은 하나 또는 하나 이상의 층일 수 있다.
와인딩 공정은 불연속적이거나 연속적일 수 있다. 연속적인 와인딩의 경우, 원호 세그먼트 요소들은 공-압출에 의해 미리-고정될 수 있다. 대안적으로, 관형 구조물의 원호 세그먼트는 섬유-강화 요소들을 제조하는(fabricating) 중간 단계 없이 직접 인발될(pultruded) 수 있다. 또한, 불연속적인 와인딩과 달리, 구성요소(component)가 아닌 와인더(winder)가 회전한다. 연속적인 와인딩의 경우, 맨드릴을 제거하기 위해 미리-고정하는 것이 충분할 수 있다.
다른 구현들은 다음 청구범위 내에 있다.

Claims (25)

  1. 횡단면의 프로파일 (400, 404, 406, 408, 600, 801, 901)을 포함하는 강화 구조물에 있어서,
    연속 섬유-강화 필라멘트들 (105, 205, 307, 510, 705); 및
    제1 매트릭스 재료 (104, 204, 304, 540, 706)를 포함하고,
    연속 섬유-강화 필라멘트들은 연속 섬유-강화 요소들 (100, 200, 300, 500, 702)을 형성하기 위해 제1 매트릭스 재료에서 섬유-강화 요소의 길이방향 축을 따라 매립되는 것을 특징으로 하는 강화 구조물.
  2. 제1항에 있어서,
    제2 매트릭스 재료 (430, 640)를 포함하며,
    상기 연속 섬유-강화 요소들은 횡단면의 프로파일을 형성하기 위해 제2 매트릭스 재료에 매립되는 강화 구조물.
  3. 제2항에 있어서,
    상기 제1 매트릭스 재료 및 제2 매트릭스 재료는 상이한 재료들인 강화 구조물.
  4. 제2항에 있어서,
    상기 제1 매트릭스 재료 및 제2 매트릭스 재료는 동일한 재료인 강화 구조물.
  5. 제1항 내지 제4항 중 어느 한 항에 있어서,
    상기 횡단면의 프로파일은 삼각형, 원형, 직사각형, 및 T-자형으로 구성되는 그룹으로부터 선택된 형상을 포함하는 강화 구조물.
  6. 제5항에 있어서,
    상기 횡단면의 프로파일은 삼각형, 원형, 및 직사각형으로 구성되는 그룹으로부터 선택된 형상의 중공 영역을 둘러싸는 외부 윤곽을 포함하는 강화 구조물.
  7. 제1항 내지 제6항 중 어느 한 항에 있어서,
    상기 연속 섬유-강화 요소들은 삼각형, 원형, 직사각형, 사다리꼴, 및 육각형으로 구성되는 그룹으로부터 선택된 횡단면의 형상을 포함하는 강화 구조물.
  8. 제1항 내지 제7항 중 어느 한 항에 있어서,
    상기 연속 섬유-강화 요소들은 다른 연속 섬유-강화 요소들과 연결되거나 또는 상호교합하기 위한 외부 윤곽을 포함하는 강화 구조물.
  9. 제1항 내지 제8항 중 어느 한 항에 있어서,
    상기 섬유 강화 요소들은 서로 연결되고 제2 매트릭스 재료에 매립되는 강화 구조물.
  10. 제7항 또는 제9항에 있어서,
    상기 연속 섬유-강화 요소들은 0.4mm 이상의 직경을 갖는 원형 횡단면의 형상을 포함하는 강화 구조물.
  11. 제1항 내지 제10항 중 어느 한 항에 있어서,
    상기 연속 섬유-강화 요소의 섬유 부피 분율은 적어도 35%인 강화 구조물.
  12. 제1항에 있어서,
    상기 횡단면의 프로파일은 관형인 강화 구조물.
  13. 제12항에 있어서,
    상기 연속 섬유-강화 요소들은 삼각형, 원형, 직사각형, 사다리꼴, 및 육각형으로 구성되는 그룹으로부터 선택된 횡단면의 형상을 포함하는 강화 구조물.
  14. 제13항에 있어서,
    상기 연속 섬유-강화 요소들은 0.4mm 이상의 직경을 갖는 원형 횡단면의 형상을 포함하는 강화 구조물.
  15. 제12항 내지 제14항 중 어느 한 항에 있어서,
    상기 연속 섬유-강화 요소의 섬유 부피 분율은 적어도 35%인 강화 구조물.
  16. 제12항 내지 제15항 중 어느 한 항에 있어서,
    상기 섬유-강화 요소들 (702, 802, 804, 806, 808, 902, 904, 906, 908)은 관형 횡단면의 직경(D)의 원호 세그먼트인 횡단면의 형상을 포함하는 강화 구조물.
  17. 제16항에 있어서,
    강화 구조물의 관형 배열을 형성하는 섬유 강화 요소들 (802, 804, 806, 808); 및
    관형 배열의 외부 표면 주위 및 외부 표면 상에 감긴 단방향 강화 테이프의 와인딩 층 (803)을 포함하는 강화 구조물.
  18. 제16항에 있어서,
    섬유-강화 요소들의 모서리들 사이에 갭들 (910)을 포함하는 강화 구조물의 관형 배열을 형성하는 섬유 강화 요소들 (902, 904, 906, 908);
    관형 배열의 외부 표면을 둘러싸고 갭들을 채우는 제2 매트릭스 재료 (914); 및
    제2 매트릭스 재료의 외부 표면 주위 및 외부 표면 상에 감긴 단방향 강화 열가소성 테이프의 와인딩 층 (903)을 포함하는 강화 구조물.
  19. 제12항에 따른 관형 횡단면의 프로파일을 갖는 강화 구조물의 형성 방법에 있어서,
    상기 관형 횡단면의 직경(D)의 적어도 2개의 원호 세그먼트들을 형성하는 단계;
    상기 적어도 2개의 원호 세그먼트들을 갖는 보강 구조물의 관형 배열을 형성하는 단계; 및
    상기 형성된 관형 배열의 외부 표면 주위 및 외부 표면 상에 층을 와인딩하는 단계;를 포함하는 강화 구조물의 형성 방법.
  20. 제19항에 있어서,
    인접한 원호 세그먼트들의 모서리들은 접촉 위치들에서 서로 접촉하고 접착되는 강화 구조물의 형성 방법.
  21. 제19항에 있어서,
    상기 원호 세그먼트들은 서로 접착하기 위한 연결된 요소들인 강화 구조물의 형성 방법.
  22. 제19항에 있어서,
    상기 관형 배열을 형성하는 인접한 원호 세그먼트들의 모서리들 사이에 갭이 있고,
    상기 원호 세그먼트들의 외부 표면 상에 매트릭스 재료를 적용하고, 상기 매트릭스 재료는 갭들을 채우는 강화 구조물의 형성 방법.
  23. 제19항 내지 제22항 중 어느 한 항에 있어서,
    상기 와인딩 층이 단방향 강화 열가소성 테이프인 강화 구조물의 형성 방법.
  24. 제19항 내지 제22항 중 어느 한 항에 있어서,
    상기 와인딩 층이 단방향 강화 열경화성 테이프인 강화 구조물의 형성 방법.
  25. 제23항 또는 제24항 중 어느 한 항에 있어서,
    정의된 와인딩 피드 폭 및 회전으로 프리텐션 하에 와인딩 층을 와인딩하는 단계; 및
    상기 테이프의 매트릭스를 녹이고 상기 관형 배열을 가열하기 위해, 와인딩 층을 가열하는 단계;를 포함하는 강화 구조물의 형성 방법.
KR1020227046168A 2020-05-29 2021-05-24 연속 섬유 강화 요소들을 포함하는 강화 구조물 및 그 제조 방법 KR20230018471A (ko)