KR20220091123A - A pot made from soil and its manufacturing method - Google Patents
A pot made from soil and its manufacturing method Download PDFInfo
- Publication number
- KR20220091123A KR20220091123A KR1020200182334A KR20200182334A KR20220091123A KR 20220091123 A KR20220091123 A KR 20220091123A KR 1020200182334 A KR1020200182334 A KR 1020200182334A KR 20200182334 A KR20200182334 A KR 20200182334A KR 20220091123 A KR20220091123 A KR 20220091123A
- Authority
- KR
- South Korea
- Prior art keywords
- composition
- pot
- powder
- binder
- manufacturing
- Prior art date
Abstract
본 발명은 상토 포트 및 그 제조 방법에 관한 것으로, 특히 본 발명에 따른 상토 포트의 제조 방법은 바인더, 분말 및 상토를 혼합하여 포트 조성물을 생성하는 조성물 생성단계; 상기 조성물을 가압하여 성형하는 성형 단계; 및 성형물을 건조하는 건조 단계;를 포함하는 것을 특징으로 한다.The present invention relates to a top soil pot and a method for manufacturing the same, and in particular, the method for manufacturing a top soil pot according to the present invention includes a composition generating step of mixing a binder, powder, and top soil to produce a pot composition; A molding step of molding by pressing the composition; and a drying step of drying the molding.
Description
본 발명은 상토 포트 및 그 제조 방법에 관한 것으로, 보다 구체적으로는 환경을 오염시키는 합성 수지를 사용하지 않고 상토를 이용하여 포트를 제조함으로써, 포트에서 발아 성장된 육묘를 포트와 함께 식재할 수 있어 분갈이의 번거로움 및 이식 재배에 따른 뿌리의 손상을 방지할 수 있도록 하여 식물의 성장 속도가 증가하고 건강한 식물로 성장할 수 있도록 하는 상토 포트 및 그 제조 방법에 관한 것이다.The present invention relates to a potting soil and a method for manufacturing the same, and more specifically, by manufacturing a pot using topsoil without using a synthetic resin that pollutes the environment, the seedlings germinated in the pot can be planted together with the pot. The present invention relates to a potting soil pot and a method for manufacturing the same, which increase the growth rate of plants and enable them to grow into healthy plants by preventing the hassle of repotting and damage to roots due to transplantation.
모종(苗種, Nursery plant)이라 함은, 인류가 이용할 목적으로 재배하는 작물(作物, Crops)을 옮겨 심기 위하여 가꾼 씨앗의 싹을 말하며, 이러한 모종 심기는 작물마다 다르지만 대개 떡잎(Cotyledon)이 나오고 다음으로 새순(Bud)이 나와 잎사귀가 네댓 개 정도 되었을 때가 가장 적당하다고 보면 된다.Nursery plant refers to the buds of seeds cultivated for transplanting crops cultivated for human use. Next, it is most appropriate when new shoots appear and there are about four or five leaves.
이러한 모종을 키우는 목적은, 고추처럼 이른 2월이나 3월 초부터 파종(播種)을 해야 하는 작물의 경우 서리 피해를 방지하기 위한 것도 있고, 또 씨앗이 작아 빗물 피해를 막기 위한 것도 있지만, 가장 큰 목적으로는 모종을 내어서 옮겨심으면 소출(所出)도 많고 더 튼튼히 성장하게 하기 위해서다.The purpose of growing these seedlings is to prevent frost damage in the case of crops that need to be sown from early February or early March, such as red pepper, and also to prevent damage from rainwater because the seeds are small. The purpose is to make the seedlings grow stronger and produce more fruit when transplanted.
한편, 모종을 가꾸는데에는, 작물의 씨앗과 함께 일정분의 상토(床土, Media, bed soil)를 채워넣을 수 있는 모종포트(Seedling pot / 또는 모종트레이)가 필요하게 되는 바, 지금까지의 모종포트는 대부분 폴리에틸렌수지로 된 것이어서, 모종이 어느 정도 자라났을 때 경작지(耕作地, Cultivated land, land of cultivation)에 내어다 제대로 옮겨심는 정식(定植) 이후 그대로 버려지게 된다.On the other hand, in cultivating seedlings, a seedling pot (or seedling tray) capable of filling a certain amount of top soil (床土, media, bed soil) together with the seeds of crops is required. Most of the pots are made of polyethylene resin, and when the seedlings have grown to a certain extent, they are brought out to the cultivated land (Cultivated land, land of cultivation) and discarded after planting.
또한, 종래의 원예용 포트는 비닐 포트로만 이루어져 있어, 식물을 정식 또는 조경공사 식재시 비닐 포트와 분을 분리할 때 분이 깨지는 경우가 많아 식물 뿌리 활착률이 떨어져 제대로 성장하지 못하는 확률이 높은 문제점이 있었다.In addition, the conventional horticultural pot consists only of a plastic pot, so when planting a plant or landscaping, when separating the plastic pot and the manure, the manure is often broken. .
이 경우, 상술한 정식 도중의 모종 훼손은 차치하더라도 수백 년 이상 자연분해가 되지 않는 합성수지소재의 그 특성상 후처리(폐기처분)에 대한 대비책을 강구해야만 했다.In this case, it was necessary to devise countermeasures for post-treatment (disposal) due to the nature of the synthetic resin material, which did not decompose naturally for more than several hundred years, apart from the damage to the seedlings during planting mentioned above.
또한, 육묘를 포트상에서 일일이 분리해야 함에 따라 작업이 번거로우면서 많은 일손이 소요되고, 또 육묘를 포트 상에서 분리시 대부분의 흙이 용탈되어 뿌리 손상 및 건조로 인해 식재 후 육묘가 고사하거나 생육발달이 멈춰 농작물의 경우 수확량이 크게 감소되는 실정이다.In addition, as the seedlings have to be separated one by one on the pot, the work is cumbersome and requires a lot of work, and when the seedlings are separated on the pot, most of the soil is leached out, and the seedlings die after planting or the growth and development stops due to root damage and drying. In the case of crops, the yield is greatly reduced.
따라서, 종래에 사용되었던 폴리에틸렌수지 즉, 비닐 또는 플라스틱을 사용하지 않고 슬러지, 이불솜, 계란껍질 및 커피가루등과 같이 사용후 버려지는 물질들을 재활용하여 제작됨으로써 친환경적이며, 정식 시 육묘를 포트상에서 일일이 분리하는 작업을 수행하지 않고 육묘를 포트와 함께 식재할 수 있어 인건비를 절감할 수 있으면서도 육묘의 흙이 용탈되어 뿌리 손상 및 건조로 인해 식재 후 육묘가 고사하거나 생육발달이 저하되는 문제점을 방지할 수 있도록 하는 포트의 개발이 요구되고 있다.Therefore, it is eco-friendly as it is produced by recycling materials discarded after use such as sludge, duvet cotton, egg shells, and coffee powder without using conventionally used polyethylene resin, that is, vinyl or plastic. Since seedlings can be planted together with a pot without separation, labor costs can be reduced, and problems such as erosion of seedling soil and root damage and drying after planting can be prevented. The development of a port that allows it is required.
상기와 같은 문제점을 해결하기 위하여 본 발명은, 밀가루, 옥수수전분 및 물을 혼합한 바인더와 계란껍질분말, 커피가루 및 숯가루를 혼합한 분말을 상토에 혼합하여 생성된 조성물을 압착 성형기에 가압하여 성형한 후 건조시켜 포트를 제조함으로써, 육묘를 포트와 함께 식재할 수 있어 인건비를 절감할 수 있으면서도 육묘의 흙이 용탈되어 뿌리 손상 및 건조로 인해 식재 후 육묘가 고사하거나 생육발달이 저하되는 문제점을 방지할 수 있을 뿐 아니라 폴리에틸렌수지를 사용하지 않고 슬러지, 이불솜, 계란껍질 및 커피가루등과 같이 사용 후 버려지는 물질들을 재활용함으로써 친환경적인 상토 포트 및 그 제조 방법을 제공하는데 목적이 있다.In order to solve the above problems, the present invention pressurizes a composition produced by mixing a binder mixed with wheat flour, corn starch and water with a powder mixed with eggshell powder, coffee powder, and charcoal powder in a medium to a press molding machine. By forming and drying the pot to manufacture the pot, the seedlings can be planted together with the pot, thereby reducing labor costs, while the soil of the seedlings is leached out and the seedlings die off or the growth and development is reduced after planting due to root damage and drying. It aims to provide an eco-friendly soil pot and its manufacturing method by recycling materials that are discarded after use, such as sludge, quilt cotton, egg shells and coffee powder, without using polyethylene resin as well as preventing it from being used.
상기한 목적을 달성하기 위한 본 발명의 실시예에 따른 상토 포트 및 그 제조 방법은 바인더, 분말 및 상토를 혼합하여 포트 조성물을 생성하는 조성물 생성단계; 상기 조성물을 가압하여 성형하는 성형 단계; 및 성형물을 건조하는 건조 단계;를 포함하는 것을 특징으로 한다.A potting pot and a method for manufacturing the same according to an embodiment of the present invention for achieving the above object is a composition generating step of mixing a binder, a powder, and a potting soil to produce a pot composition; A molding step of molding by pressing the composition; and a drying step of drying the molding.
또한, 본 발명에 따른 상기 조성물 생성단계는 밀가루, 옥수수전분 및 철분과 미네랄이 용해된 물을 혼합하여 바인더를 생성하는 바인더생성공정; 계란껍질분말, 커피가루 및 숯가루를 혼합하여 분말을 생성하는 분말생성공정; 및 상기 바인더 및 상기 분말을 상토에 혼합한 후 반죽하여 조성물을 생성하는 조성물 생성 공정;을 포함하는 것을 특징으로 한다.In addition, the composition generating step according to the present invention comprises: a binder production step of mixing wheat flour, corn starch, iron and water in which minerals are dissolved to produce a binder; a powder production process of mixing eggshell powder, coffee powder, and charcoal powder to produce a powder; and a composition generating process of mixing the binder and the powder with top soil and kneading the mixture to produce a composition.
또한, 본 발명에 따른 상기 성형 단계는 기 조성물을 소분하는 소분 공정;In addition, the forming step according to the present invention includes a subdivision process of subdividing the base composition;
금형이 설치된 압착 성형기에 면솜 충전재로 직조된 제1시트를 배치하는 제1시트배치공정; 기 제1시트 상단에 소분된 상기 조성물을 배치하는 조성물 배치공정; 기 조성물 상단에 면솜 충전재로 직조된 제2시트를 덮는 제2시트 배치공정; 및 상기 조성물을 가압 성형하는 가압 공정;을 포함하는 것을 특징으로 한다.A first sheet arrangement step of disposing a first sheet woven with cotton filling in a compression molding machine with a mold installed; a composition arrangement step of disposing the subdivided composition on top of the first sheet; a second sheet arrangement step of covering a second sheet woven with a cotton filling material on top of the base composition; and a pressing process of press-molding the composition.
또한, 본 발명에 따른 상기 조성물은 밀가루 5%, 옥수수전분 5%, 커피가루 3%, 계란껍질분말 3%, 숯가루 2%, 상토 50% 및 면솜 충전재 30%로 구성되고, 유기바인더 2%를 더 포함하는 것을 특징으로 한다.In addition, the composition according to the present invention is composed of flour 5%, corn starch 5%, coffee powder 3%, eggshell powder 3%, charcoal powder 2%, top soil 50% and cotton filling material 30%, organic binder 2% It is characterized in that it further comprises.
아울러, 상토 포트의 제조 방법에 의해 제조된 상토 포트인 것을 특징으로 한다.In addition, it is characterized in that the soil pot manufactured by the manufacturing method of the soil pot.
상기와 같은 본 발명에 따른 상토 포트 및 그 제조 방법에 의하면, 정식 시 육묘를 포트상에서 일일이 분리하는 작업을 수행하지 않고 육묘를 포트와 함께 식재할 수 있도록 구성됨으로써 인건비를 절감하여 경제적인 효과가 있다.According to the potting soil pot and the method for manufacturing the same according to the present invention as described above, it is configured to plant the seedlings together with the pot without separately separating the seedlings on the pot at the time of planting, thereby reducing labor costs and having an economical effect. .
또한, 육묘를 포트와 함께 식재할 수 있도록 구성되어, 육묘의 흙이 용탈되어 뿌리 손상 및 건조로 인해 식재 후 육묘가 고사하거나 생육발달이 저하되는 문제점을 방지할 수 있는 효과가 있다.In addition, it is configured so that the seedlings can be planted together with the pot, so that the soil of the seedlings is leached, and there is an effect of preventing the problems that the seedlings die or the growth and development is reduced after planting due to root damage and drying.
아울러, 포트를 폴리에틸렌수지를 사용하지 않고 슬러지, 이불솜, 계란껍질 및 커피가루등의 재활용품을 이용하여 제조함으로써, 사용 후 버려지는 물질들을 재활용하여 친환경적인 효과가 있다. In addition, by manufacturing the pot using recycled products such as sludge, quilt cotton, eggshell and coffee powder without using polyethylene resin, there is an eco-friendly effect by recycling materials discarded after use.
도 1은 본 발명에 따른 상토 포트의 제조 방법의 블록도이다.
도 2는 본 발명에 따른 상토 포트의 조성물 생성단계의 블록도이다.
도 3은 본 발명에 따른 상토 포트의 성형 단계의 블록도이다.
도 4는 본 발명에 따른 상토 포트의 사용 상태를 나타내는 상태도이다.1 is a block diagram of a method for manufacturing a top soil pot according to the present invention.
Figure 2 is a block diagram of the composition generating step of the potting pot according to the present invention.
Figure 3 is a block diagram of the forming step of the top soil pot according to the present invention.
Figure 4 is a state diagram showing the use state of the top pot according to the present invention.
이하, 첨부한 도면을 참조하여 본 발명의 실시 예를 설명한다. 우선, 도면들 중 동일한 구성요소 또는 부품들은 가능한 한 동일한 참조부호를 나타내고 있음에 유의해야 한다. 본 발명을 설명함에 있어서 관련된 공지기능 혹은 구성에 대한 구체적인 설명은 본 발명의 요지를 모호하게 하지 않기 위해 생략한다.Hereinafter, embodiments of the present invention will be described with reference to the accompanying drawings. First, it should be noted that the same components or parts in the drawings are denoted by the same reference numerals as much as possible. In describing the present invention, detailed descriptions of related known functions or configurations are omitted so as not to obscure the gist of the present invention.
도 1은 본 발명에 따른 상토 포트의 제조 방법의 블록도이다.1 is a block diagram of a method for manufacturing a top soil pot according to the present invention.
본 발명에 따른 상토 포트의 제조 방법은 도 1에 도시된 바와 같이 조성물 생성단계(S100), 성형 단계(S200) 및 건조 단계(S300)를 포함할 수 있다.The method for manufacturing a top pot according to the present invention may include a composition generating step (S100), a molding step (S200) and a drying step (S300) as shown in FIG. 1 .
도 2는 본 발명에 따른 상토 포트의 조성물 생성단계의 블록도이다.Figure 2 is a block diagram of the composition generating step of the potting pot according to the present invention.
본 발명에 따른 상기 조성물 생성단계(S100)는 도 2에 도시된 바와 같이 바인더, 분말 및 상토를 혼합하여 포트 조성물을 생성하는 단계일 수 있다.The composition generating step (S100) according to the present invention may be a step of producing a pot composition by mixing a binder, powder, and top soil as shown in FIG.
따라서, 상기 조성물 생성단계(S100)는 바인더 생성 공정(S110), 분말 생성 공정(S120) 및 조성물 생성 공정(S130)을 포함할 수 있다.Accordingly, the composition generating step (S100) may include a binder generating process (S110), a powder generating process (S120), and a composition generating process (S130).
상기 바인더 생성 공정(S110)은 밀가루, 옥수수전분 및 철분과 미네랄이 용해된 물을 혼합하여 바인더를 생성하는 공정일 수 있다.The binder generating process ( S110 ) may be a process of generating a binder by mixing wheat flour, corn starch, and water in which iron and minerals are dissolved.
구체적으로, 상기 바인더 생성 공정(S110)은 밀가루, 옥수수전분 및 철분과 미네랄이 섞인 물을 혼합하여 바인더를 생성하는 공정으로, 밀가루 5% 및 옥수수전분 5%로 함유된 바인더를 생성하도록 구비된다.Specifically, the binder generating process (S110) is a process of generating a binder by mixing wheat flour, corn starch, and water mixed with iron and minerals, and is provided to produce a binder containing 5% wheat flour and 5% corn starch.
상기 분말 생성 공정(S120)은 계란껍질분말, 커피가루 및 숯가루를 혼합한 분말을 생성하는 공정일 수 있다.The powder generating process (S120) may be a process of generating a powder in which eggshell powder, coffee powder, and charcoal powder are mixed.
구체적으로, 상기 분말 생성 공정(S120)은 상기 바인더와 혼합되는 분말을 생성하는 공정으로, 계란껍질분말 3%, 숯가루 2% 및 커피가루 3%의 비율로 구성된 분말을 생성할 수 있다.Specifically, the powder generating process (S120) is a process of generating a powder mixed with the binder, and may produce a powder composed of 3% eggshell powder, 2% charcoal powder, and 3% coffee powder.
상기 조성물 생성 공정(S130)은 상기 바인더 및 상기 분말을 상토에 혼합한 후 반죽하여 조성물을 생성하는 공정일 수 있다.The composition generating process ( S130 ) may be a process of mixing the binder and the powder with top soil and kneading the mixture to produce a composition.
구체적으로, 상기 조성물 생성 공정(S130)은 상토에 상기 바인더 및 상기 분말을 혼합한 후 반죽하여 상기 상토 포트(1)를 구성하는 조성물을 생성하는 공정으로, 밀가루 5%, 옥수수전분 5%, 계란껍질분말 3%, 숯가루 2%, 커피가루 3% 및 상토 50%의 비율을 갖는 조성물을 철분과 미네랄이 용해된 물과 혼합한 후 일정한 텐션을 갖을 수 있도록 반죽하여 조성물을 생성하도록 한다.Specifically, the composition generating process (S130) is a process of mixing the binder and the powder with top soil and kneading it to produce a composition constituting the top soil pot 1, 5% wheat flour, 5% corn starch, eggs After mixing a composition having a ratio of 3% shell powder, 2% charcoal powder, 3% coffee powder, and 50% top soil with water in which iron and minerals are dissolved, knead it to have a certain tension to produce a composition.
이 때, 상기 조성물은 상기한 성분에 유기바인더를 2%를 더 포함하여 구성될 수 있다.At this time, the composition may be configured to further include 2% of the organic binder in the above-mentioned component.
도 3은 본 발명에 따른 상토 포트의 성형 단계의 블록도이다.Figure 3 is a block diagram of the forming step of the top soil pot according to the present invention.
본 발명에 따른 상기 성형 단계(S200)는 도 3에 도시된 바와 같이 상기 조성물을 가압하여 성형하는 단계일 수 있다.The molding step (S200) according to the present invention may be a step of molding by pressing the composition as shown in FIG.
구체적으로, 상기 성형 단계(S200)는 상기 조성물 생성 단계(S100)에서 생성된 조성물을 일정량 소분한 후 열압착기에 넣고 가압하여 포트의 형상을 형성하도록 구비되는 단계일 수 있다.Specifically, the forming step (S200) may be a step in which a predetermined amount of the composition generated in the composition generating step (S100) is subdivided and then put into a thermocompressor and pressurized to form the shape of the pot.
따라서, 상기 성형 단계(S200)는 소분 공정, 제1시트배치공정, 조성물 배치 공정, 제2시트 배치 공정 및 가압 공정을 포함할 수 있다.Accordingly, the forming step (S200) may include a subdivision process, a first sheet arrangement process, a composition arrangement process, a second sheet arrangement process, and a pressing process.
상기 소분 공정(S210)은 조성물 생성 공정(S100)에서 반죽이 완료된 조성물을 포트 제작에 필요한 양만큼을 소분하는 공정일 수 있다.The subdivision process ( S210 ) may be a process of subdividing the composition for which the kneading is completed in the composition creation process ( S100 ) by an amount required for pot production.
상기 제1시트 배치 공정(S220)은 금형이 설치된 압착 성형기에 면솜 충전재로 직조된 제1시트를 배치하는 공정일 수 있다.The first sheet arrangement process ( S220 ) may be a process of disposing the first sheet woven with cotton filler in a compression molding machine in which a mold is installed.
구체적으로, 상기 제1시트 배치 공정(S220)은 상기 소분 공정에 의해 소분된 조성물을 압착기에 배치시키기 전에 이루어지는 공정으로, 상기 조성물을 가압하는 압착 성형기에 제1시트를 배치시키는 공정일 수 있다.Specifically, the first sheet arrangement process ( S220 ) is a process performed before the composition subdivided by the subdivision process is placed in a press, and may be a process of placing the first sheet in a press molding machine for pressing the composition.
또한, 상기 제1시트는 얇게 직조된 면솜 충전재로 직조된 것으로 면솜 패딩일 수 있다.In addition, the first sheet may be a cotton padding that is woven with a thinly woven cotton filling material.
따라서, 상기 제1시트 배치 공정(S220)은 상기 성형기 저면에 얇게 편 면솜 패딩을 깔도록 하는 공정으로 상기 제1시트 상단에 상기 조성물이 배치될 수 있다.Therefore, the first sheet arrangement process (S220) is a process of thinly layering one-sided cotton padding on the bottom surface of the molding machine, and the composition may be disposed on the upper end of the first sheet.
상기 조성물 배치 공정(S230)은 상기 제1시트 상단에 소분된 상기 조성물을 배치하는 공정일 수 있다.The composition arrangement process ( S230 ) may be a process of disposing the subdivided composition on the top of the first sheet.
상기 제2시트 배치 공정(S240)은 상기 조성물 상단에 면솜 충전재로 직조된 제2시트를 덮는 공정일 수 있다.The second sheet arrangement process ( S240 ) may be a process of covering the second sheet woven with a cotton filling material on the top of the composition.
구체적으로, 상기 제2시트 배치 공정(S240)은 상기 성형기에 배치된 조성물의 상단을 커버하도록 제2시트를 덮는 공정으로, 상기 제2시트는 얇게 직조된 면솜 충전재로 직조된 면솜 패딩일 수 있다.Specifically, the second sheet arrangement process (S240) is a process of covering the second sheet to cover the upper end of the composition disposed in the molding machine, and the second sheet may be a cotton padding woven with a thinly woven cotton filling material. .
상기 가압 공정(S250)은 상기 조성물을 가압 성형하는 공정일 수 있다.The pressing process (S250) may be a process of press-molding the composition.
구체적으로, 상기 가압 공정(S250)은 성형기의 저면에 상기 제1시트를 깔고 상기 제1시트 상단에 소분된 조성물을 배치하며, 상기 조성물 상단에 제2시트를 배치시킨 후 성형기를 이용하여 상기 조성물을 가압하는 공정일 수 있다.Specifically, in the pressing process (S250), the first sheet is laid on the bottom surface of the molding machine, the subdivided composition is placed on the top of the first sheet, and the second sheet is placed on the top of the composition, and then the composition is used using a molding machine. It may be a process of pressurizing.
따라서, 상기 가압 공정(S250)은 반죽 상태로 된 조성물을 미세한 기공이 있는 금형을 설치한 압축 성형기에 놓고 성형시간 25 내지 125초 동안 가압 성형하여 포트를 제조하도록 한다.Therefore, in the pressing step (S250), the kneaded composition is placed in a compression molding machine equipped with a mold having fine pores and press-molded for a molding time of 25 to 125 seconds to manufacture a pot.
또한, 상기 가압 공정(S250)은 상기 조성물을 일반적으로 사용되는 포트의 형상으로 형성시킬 수 있으나, 상기 상트의 형상은 특별한 제한은 없으며, 평단면이 원형 또는 직사각형, 정사각형, 육각형, 삼각형, 오각형 등 다양한 형태가 되도록 제조할 수 있다. In addition, the pressing process (S250) may form the composition in the shape of a port generally used, but the shape of the top is not particularly limited, and the flat cross-section is circular or rectangular, square, hexagonal, triangular, pentagonal, etc. It can be manufactured to be in various forms.
또한, 상기 가압 공정(S250)은 상기 포트의 두께에 특별한 제한은 없으며, 포트 내부에 식재된 식물 뿌리가 뻗어나갈 수 있는 공간을 갖도록 구성되며 포트의 두께는 3 내지 7mm로 형성되는 것이 바람직할 수 있다.In addition, the pressing process (S250) is not particularly limited in the thickness of the pot, is configured to have a space in which the plant roots planted inside the pot can extend, and it may be preferable that the pot has a thickness of 3 to 7 mm. have.
따라서, 상기 성형 단계(S200)는 상기 반죽이 완료된 조성물을 일정한 양으로 소분한 후 성형기의 하단에 제1시트를 깔고 상기 제1시트 상단에 소분된 조성물을 배치시키며, 상기 조성물 상단에 제2시트를 배치시킨 후 성형기의 가압에 의해 상기 조성물이 포트의 형상을 갖을 수 있도록 구성된다.Therefore, in the forming step (S200), the kneaded composition is subdivided into a predetermined amount, the first sheet is laid on the lower end of the forming machine, the subdivided composition is placed on the upper end of the first sheet, and the second sheet is placed on the upper end of the composition. It is configured so that the composition can have the shape of a pot by pressing the molding machine after placing it.
상기 건조 단계(S300)는 상기 성형 단계(S200)를 마친 성형물을 건조시키는 공정일 수 있다.The drying step (S300) may be a process of drying the molding after the molding step (S200) has been completed.
따라서, 본 발명에 따른 상기 상토 포트(1)는 밀가루 5%, 옥수수전분 5%를 철분 및 미네랄이 섞인 물과 혼합하여 바인더를 만들고, 계란껍질분말 3%, 커피가루 3%, 숯가루 2%를 혼합하여 분말을 만들며, 상기 바인더와 상기 분말을 상토 50% 및 유기바인더 2%와 혼합하여 반죽한 후 일정한 텐션을 갖도록 하고, 포트 하나의 분량 만큼으로 소분하여 성형기에 넣고 압착 성형하여 제조할 수 있다.Therefore, in the top pot 1 according to the present invention, 5% of wheat flour and 5% of corn starch are mixed with iron and mineral water to make a binder, and eggshell powder 3%, coffee powder 3%, charcoal powder 2% to make a powder, mix the binder and the powder with 50% top soil and 2% organic binder and knead to have a certain tension, divide it into one pot amount, put it in a molding machine, and press molding. have.
또한, 상기 상토 포트(1)는 상기 성형기의 저면에 얇게 직조된 면솜 패딩으로 구성된 제1시트를 바닥에 깔고, 소분된 조성물을 상측에 배치하며, 상기 조성물 상단에 패딩솜으로 구성된 제2시트를 덮은 후 압착 성형하여 포트의 형상으로 성형 후 건조시켜 제조할 수 있다.In addition, the top pot (1) is a first sheet composed of a thinly woven cotton padding on the bottom of the molding machine on the bottom, a subdivided composition is placed on the upper side, and a second sheet composed of padding cotton is covered on the top of the composition It can be manufactured by compression molding after molding into the shape of a pot, and then drying.
아울러, 상기 상토 포트는 식물을 키우는 다양한 형태의 화분을 모두 포함하는 개념일 수 있으며, 따라서, 상기 상토 포트의 제조 방법은 식물을 키우는 다양한 형태의 화분의 제조 방법일 수도 있다.In addition, the potting soil pot may be a concept including all types of pots of various types for growing plants, and thus, the method of manufacturing the potting pot may be a method of manufacturing various types of pots for growing plants.
도 4는 본 발명에 따른 상토 포트의 사용 상태를 나타내는 상태도이다.Figure 4 is a state diagram showing the use state of the top pot according to the present invention.
따라서, 상기 상토 포트(1)는 작물의 씨앗과 함께 일정분의 상토를 채운 상태에서 트레이(10)에 배치되어 모종을 키우는 데 사용되며, 상기 모종이 경작지에 옮겨 정식되어야 하는 경우 상기 포트(1)에서 모종을 빼내어 정식하지 않고 포트에서 발아 성장된 육묘를 포트와 함께 식재할 수 있도록 구성됨으로써, 분갈이의 번거로움 및 이식 재배에 따른 뿌리의 손상을 방지할 수 있으며 육묘의 정식이 용이하면서도 친환경으로 이루어질 수 있도록 한다.Therefore, the pot (1) is placed on the tray (10) in a state filled with a certain amount of top soil together with the seeds of the crop and used to grow seedlings, and when the seedlings need to be transplanted to cultivated land, the pot (1) )), so that the seedlings germinated and grown in the pot can be planted together with the pot, thereby preventing the hassle of repotting and damage to the roots due to transplanted cultivation. make it happen
또한, 본 발명에 따른 상기 상토 포트는 상기한 바와 같이 모종을 키우고 정식 후 버려지는 포트일 수 있으나, 일반적인 육묘를 키우는 화분일 수도 있다.In addition, the potting soil pot according to the present invention may be a pot discarded after growing and planting seedlings as described above, but may also be a pot for growing general seedlings.
따라서, 상기 상토 포트는 식물을 키우는 다양한 형태의 화분을 모두 포함하는 개념일 수 있다.Therefore, the potting soil may be a concept including all of various types of pots for growing plants.
상기와 같은 본 발명에 따른 상토 포트 및 그 제조 방법에 의하면, 정식 시 육묘를 포트상에서 일일이 분리하는 작업을 수행하지 않고 육묘를 포트와 함께 식재할 수 있도록 구성됨으로써 인건비를 절감하여 경제적인 효과가 있다.According to the potting soil pot and the method for manufacturing the same according to the present invention as described above, it is configured to plant the seedlings together with the pot without separately separating the seedlings on the pot at the time of planting, thereby reducing labor costs and having an economical effect. .
또한, 육묘를 포트와 함께 식재할 수 있도록 구성되어, 육묘의 흙이 용탈되어 뿌리 손상 및 건조로 인해 식재 후 육묘가 고사하거나 생육발달이 저하되는 문제점을 방지할 수 있는 효과가 있다.In addition, it is configured so that the seedlings can be planted together with the pot, so that the soil of the seedlings is leached, and there is an effect of preventing the problems that the seedlings die or the growth and development is reduced after planting due to root damage and drying.
또한, 포트를 폴리에틸렌수지를 사용하지 않고 슬러지, 이불솜, 계란껍질 및 커피가루등의 재활용품을 이용하여 제조함으로써, 사용 후 버려지는 물질들을 재활용하여 친환경적인 효과가 있다. In addition, the pot is manufactured using recycled materials such as sludge, quilt cotton, eggshell and coffee powder without using polyethylene resin, thereby recycling materials discarded after use, thereby having an eco-friendly effect.
이상에 설명한 본 명세서 및 청구범위에 사용되는 용어 및 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니 되며, 본 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.The terms and words used in the present specification and claims described above should not be construed as being limited to conventional or dictionary meanings, and the present inventors have adequately defined the concept of terms to describe their invention in the best way. It should be interpreted as meaning and concept consistent with the technical idea of the present invention based on the principle that it can be defined as
따라서, 본 명세서에 기재된 도면 및 실시 예에 도시된 구성은 본 발명의 가장 바람직한 하나의 실시 예에 불과할 뿐이고, 본 발명의 기술적 사상을 모두 대변하는 것이 아니므로, 본 출원시점에 있어서 이들을 대체할 수 있는 다양한 균등물과 변형 예들이 있을 수 있음을 이해하여야 한다.Accordingly, the configurations shown in the drawings and embodiments described in this specification are merely one of the most preferred embodiments of the present invention, and do not represent all of the technical spirit of the present invention, so they can be substituted at the time of the present application. It should be understood that there may be various equivalents and variations that exist.
1 : 상토 포트
10 : 트레이
S100 : 조성물 생성 단계
S110 : 바인더 생성 공정
S120 : 분말 생성 공정
S130 : 조성물 생성 공정
S200 : 성형 단계
S210 : 소분 공정
S220 : 제1시트 배치 공정
S230 : 조성물 배치 공정
S240 : 제2시트 배치 공정
S250 : 가압 공정
S300 : 건조 단계1: top pot 10: tray
S100: composition generation step S110: binder generation step
S120: powder production process S130: composition production process
S200: forming step S210: subdivision process
S220: first sheet arrangement process S230: composition arrangement process
S240: second sheet arrangement process S250: pressurization process
S300 : Drying stage
Claims (5)
상기 조성물을 가압하여 성형하는 성형 단계; 및
성형물을 건조하는 건조 단계;
를 포함하는 것을 특징으로 하는 상토 포트의 제조 방법.
A composition generating step of mixing a binder, powder and top soil to produce a pot composition;
A molding step of molding by pressing the composition; and
a drying step of drying the molding;
A method of manufacturing a top pot, characterized in that it comprises a.
상기 조성물 생성단계는,
밀가루, 옥수수전분 및 철분과 미네랄이 용해된 물을 혼합하여 바인더를 생성하는 바인더생성공정;
계란껍질분말, 커피가루 및 숯가루를 혼합하여 분말을 생성하는 분말생성공정; 및
상기 바인더 및 상기 분말을 상토에 혼합한 후 반죽하여 조성물을 생성하는 조성물 생성 공정;
을 포함하는 것을 특징으로 하는 상토 포트의 제조 방법.
The method of claim 1,
The composition production step,
a binder production process for producing a binder by mixing wheat flour, corn starch, and water in which iron and minerals are dissolved;
a powder production process of mixing eggshell powder, coffee powder, and charcoal powder to produce a powder; and
a composition production step of mixing the binder and the powder with top soil and kneading the mixture to produce a composition;
A method of manufacturing a top pot, characterized in that it comprises a.
상기 성형 단계는,
상기 조성물을 소분하는 소분 공정;
금형이 설치된 압착 성형기에 면솜 충전재로 직조된 제1시트를 배치하는 제1시트배치공정;
상기 제1시트 상단에 소분된 상기 조성물을 배치하는 조성물 배치공정;
상기 조성물 상단에 면솜 충전재로 직조된 제2시트를 덮는 제2시트 배치공정; 및
상기 조성물을 가압 성형하는 가압 공정;
을 포함하는 것을 특징으로 하는 상토 포트의 제조 방법.
3. The method of claim 2,
The forming step is
a subdivision process of subdividing the composition;
A first sheet arrangement step of disposing a first sheet woven with cotton filling in a compression molding machine with a mold installed;
a composition arrangement step of disposing the subdivided composition on top of the first sheet;
a second sheet arrangement step of covering a second sheet woven with a cotton filler on the top of the composition; and
a pressing process of press-molding the composition;
A method of manufacturing a top pot, characterized in that it comprises a.
상기 조성물은,
밀가루 5%, 옥수수전분 5%, 커피가루 3%, 계란껍질분말 3%, 숯가루 2%, 상토 50% 및 면솜 충전재 30%로 구성되고,
유기바인더 2%를 더 포함하는 것을 특징으로 하는 상토 포트의 제조 방법.
4. The method of claim 3,
The composition is
It is composed of wheat flour 5%, corn starch 5%, coffee powder 3%, eggshell powder 3%, charcoal powder 2%, top soil 50% and cotton filling material 30%,
Method of producing a top pot pot, characterized in that it further comprises an organic binder 2%.