KR20210061046A - Adhesive oil film removal sheet for vehicles - Google Patents

Adhesive oil film removal sheet for vehicles Download PDF

Info

Publication number
KR20210061046A
KR20210061046A KR1020190148797A KR20190148797A KR20210061046A KR 20210061046 A KR20210061046 A KR 20210061046A KR 1020190148797 A KR1020190148797 A KR 1020190148797A KR 20190148797 A KR20190148797 A KR 20190148797A KR 20210061046 A KR20210061046 A KR 20210061046A
Authority
KR
South Korea
Prior art keywords
oil film
sheet
vehicle
adhesive
film removal
Prior art date
Application number
KR1020190148797A
Other languages
Korean (ko)
Other versions
KR102343308B1 (en
Inventor
장보고
Original Assignee
장보고
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 장보고 filed Critical 장보고
Priority to KR1020190148797A priority Critical patent/KR102343308B1/en
Publication of KR20210061046A publication Critical patent/KR20210061046A/en
Application granted granted Critical
Publication of KR102343308B1 publication Critical patent/KR102343308B1/en

Abstract

The present invention relates to an adhesive oil film removal sheet for a vehicle. More specifically, the present invention relates to the adhesive oil film removal sheet for the vehicle wherein a basic solution is impregnated, is made of a shape corresponding to a vehicle glass window, and includes an adhesive sheet made of a fiber material that adheres to the glass window and removes the oil film through surface etching according to a chemical reaction between the basic solution and the glass window, thereby having an effect of saving additional energy consumption and waste of effort when removing the oil film formed on the vehicle glass window by attaching a vehicle adhesive oil film removal sheet to a target glass window and removing it instead of a polishing method using a conventional polishing material and by being capable of being easily and conveniently constructed.

Description

차량용 점착식 유막제거 시트{Adhesive oil film removal sheet for vehicles}Adhesive oil film removal sheet for vehicles

본 발명은 차량용 점착식 유막제거 시트에 관한 것으로서, 더욱 상세하게는 차량 유리표면에 유막제거 시트를 점착하는 방식으로 손쉽게 유막을 제거할 수 있는 차량용 점착식 유막제거 시트에 관한 것이다. The present invention relates to an adhesive oil film removal sheet for a vehicle, and more particularly, to an adhesive oil film removal sheet for a vehicle capable of easily removing the oil film by attaching the oil film removal sheet to the vehicle glass surface.

유리는 통기성이나 흡수성을 전혀 갖지 않고 빛의 투과성만을 갖는 치밀한 구조의 비결정성 고체로서, 그 표면은 내부와 달리 성형 도중 휘발성 물질의 휘산과 보관중의 풍화 및 침식에 의해 나트륨과 붕소 등의 농도가 떨어지고 이산화규산층이 생겨 알칼리에 의해 이산화규소가 파괴되고 유리표면의 일부가 떨어져나감으로써 침식이 반복되거나, 물을 함유한 규산층에서 물이 건조되면 미세한 균열이 발생하기도 하여 미세한 다공질 구조로 변하게 된다.Glass is a densely structured amorphous solid that has no breathability or absorption and only transmits light. Unlike the inside, the surface of which is formed by volatilization of volatile substances during molding and weathering and erosion during storage causes concentrations of sodium and boron. As the silicon dioxide is destroyed by alkali and a part of the glass surface falls off, erosion is repeated, or when water is dried in the silicic acid layer containing water, fine cracks may occur, resulting in a fine porous structure. .

이로 인해 유리의 표면층에는 대기 중의 먼지입자, 매연, 유지류 등이 손쉽게 흡착, 확산 및 침투되어 형성된 오염막을 흔히 유막이라 부른다. 시간이 지남에 따라 유리표면의 치밀함이 상실되어 물이나 천을 이용하여 닦아도 쉽게 제거되지 않는 두터운 유막을 이루게 된다.For this reason, a polluted film formed by easily adsorbing, diffusing, and penetrating airborne dust particles, soot, oils, etc. on the surface layer of the glass is commonly called an oil film. Over time, the density of the glass surface is lost, forming a thick oil film that is not easily removed even if it is wiped with water or cloth.

특히 자동차 창유리의 경우는 대기 중의 오염 외에 자동차용 왁스 등의 원료로 사용되는 유지, 실리콘오일, 수지류 등이 흡착되어 강우시나 야간 주행 시에 구름막을 형성하거나 빛을 굴절시켜 시야를 차단함으로써 사고를 유발할 수 있다.In particular, in the case of automobile window glass, oil, silicone oil, resins, etc., which are used as raw materials for automobile wax, etc., are adsorbed in addition to pollution in the air, forming a cloud film during rainfall or driving at night, or refracting light to block the view to prevent accidents It can be triggered.

근래에는 유리세정제를 사용하여 유리면에 접착된 먼지, 얼룩 등의 오염을 제거하였으나, 오랜 시간 방치된 형태로 유리표면에 형성된 대기 중의 먼지입자, 매연, 유지류 등이 흡착, 확산 및 침투된 유막은 유리세정제로는 쉽게 제거하지 못하고, 또한 물이나 천을 이용하여 닦아도 쉽게 제거되지 않는 두터운 유막을 이루게 되어 운전 중 시야확보에 어려움을 안고 있었다.In recent years, a glass cleaner has been used to remove contaminants such as dust and stains adhered to the glass surface, but the oil film in which dust particles, soot, oils, etc. in the atmosphere formed on the glass surface in a form that has been left for a long time is adsorbed, diffused, and penetrated into glass. It was not easy to remove with a detergent, and it formed a thick oil film that was not easily removed even if it was wiped with water or a cloth, making it difficult to secure visibility during driving.

이러한 사고의 유발을 방지하고 확실한 시야를 확보하기 위하여, 자동차의 창유리에 형성된 이물질이나 유막을 제거할 수 있는 연마제 성분의 유막제거제가 국내시장에 유통되고 있다.In order to prevent the occurrence of such an accident and secure a clear view, an oil film remover made of an abrasive component capable of removing foreign matter or oil film formed on a window glass of an automobile is being distributed in the domestic market.

그러나 종래와 같이 유막제거제를 이용한 세정 방법은 연마제 타입의 유막제거제를 스펀지나 천에 힘주어 문질러 주는 방식으로 초보자나 관련지식 없이는 시공방법이 어렵고, 부가적으로 드는 많은 에너지 및 시간을 소모함으로써 사용이 불편하다는 문제점이 있었다.However, as in the prior art, the cleaning method using an oil film remover is a method of rubbing an abrasive-type oil film remover with force on a sponge or cloth, and the construction method is difficult without a beginner or related knowledge, and it is difficult to use because it consumes a lot of additional energy and time. There was a problem that it was uncomfortable.

대한민국 등록특허 제10-0527924-0000호 (2005.11.03.)Korean Patent Registration No. 10-0527924-0000 (2005.11.03.) 대한민국 공개특허 제10-2017-0068919호 (2017.06.20.)Republic of Korea Patent Publication No. 10-2017-0068919 (2017.06.20.) 대한민국 등록특허 제10-1861246-0000호 (2018.05.18.)Korean Patent Registration No. 10-1861246-0000 (2018.05.18.)

본 발명의 목적은 상기와 같은 문제점을 해결하기 위한 것으로, 연마제를 사용하여 힘이 많이 소모되는 연마방식으로 유막을 제거하지 않고, 사람의 마스크팩 형식처럼 자동차의 유리표면에 유막제거 시트를 점착함으로써 운전자나 시공자가 손쉽게 유막을 제거 할 수 있도록 시공의 편리함을 목적으로 하는 차량용 점착식 유막제거 시트를 제공하는 데 있다.An object of the present invention is to solve the above problems, by using an abrasive to adhere the oil film removal sheet to the glass surface of a vehicle like a human mask pack, without removing the oil film by a polishing method that consumes a lot of power. It is to provide an adhesive-type oil film removal sheet for vehicles for the purpose of convenience in construction so that the driver or installer can easily remove the oil film.

본 발명의 목적들은 이상에서 언급한 목적으로 제한되지 않으며, 언급되지 않은 또 다른 목적들은 아래의 기재로부터 본 발명의 기술분야에서 통상의 지식을 지닌 자에게 명확하게 이해될 수 있을 것이다.The objects of the present invention are not limited to the above-mentioned objects, and other objects not mentioned will be clearly understood by those of ordinary skill in the art from the following description.

염기성용액이 함침되고, 차량 유리창과 대응되는 형상으로 이루어져 상기 유리창에 점착되어 상기 염기성용액과 유리창의 화학 반응에 따른 표면식각을 통하여 유막이 제거되는 섬유재질의 부착시트를 포함하여 이루어지는 것을 특징으로 한다. It is characterized in that it comprises a fibrous adhesive sheet that is impregnated with a basic solution and has a shape corresponding to the vehicle window, and is adhered to the window and the oil film is removed through surface etching according to a chemical reaction between the basic solution and the window. .

바람직한 실시예에 따르면, 상기 염기성용액은 수산화칼륨 2~20 중량부, 이소프로필알코올 80~98 중량부를 포함할 수 있다.According to a preferred embodiment, the basic solution may contain 2 to 20 parts by weight of potassium hydroxide and 80 to 98 parts by weight of isopropyl alcohol.

바람직한 실시예에 따르면, 상기 부착시트의 양측으로 고리형태로 연장 형성되는 탄성재질의 고리부를 더 포함할 수 있다.According to a preferred embodiment, it may further include a ring portion of an elastic material extending in a ring shape to both sides of the attachment sheet.

바람직한 실시예에 따르면, 상기 부착시트의 하부 점착면에 부착 형성되되, 상기 부착시트가 이물질로부터 오염되거나 손상되는 것을 방지하며, 시트를 차량 유리창에 부착시 제거되는 보호필름을 더 포함할 수 있다.According to a preferred embodiment, a protective film is formed attached to the lower adhesive surface of the attachment sheet, prevents the attachment sheet from being contaminated or damaged by foreign substances, and is removed when the sheet is attached to a vehicle window.

바람직한 실시예에 따르면, 상기 보호필름은 박리지 또는 필름지로 이루어 질 수 있다.According to a preferred embodiment, the protective film may be made of release paper or film paper.

바람직한 실시예에 따르면, 상기 부착시트 상부에 부착 형성되되, 외부로부터의 오염물질이 상기 부착시트에 부착되는 것을 방지하는 덮개를 더 포함할 수 있다.According to a preferred embodiment, doedoe attached to the upper portion of the attachment sheet, it may further include a cover for preventing contaminants from the outside from adhering to the attachment sheet.

바람직한 실시예에 따르면, 상기 덮개의 양측으로 연장 형성되는 탄성재질의 날개부를 더 포함할 수 있다.According to a preferred embodiment, it may further include wing portions of an elastic material extending to both sides of the cover.

바람직한 실시예에 따르면, 상기 날개부는 세로 방향으로 복수 개의 절개홈을 더 포함할 수 있다.According to a preferred embodiment, the wing portion may further include a plurality of cut grooves in the vertical direction.

바람직한 실시예에 따르면, 상기 부착시트와 상기 덮개 사이에 형성되고, 상기 부착시트에 함침 되어 있는 염기성용액을 균일하게 분산하기 위한 메쉬망을 더 포함할 수 있다.According to a preferred embodiment, it is formed between the attachment sheet and the cover, it may further include a mesh net for uniformly dispersing the basic solution impregnated in the attachment sheet.

본 발명에 따른, 차량용 점착식 유막제거 시트는 기존의 연마제를 사용한 연마방식이 아닌 차량용 점착식 유막제거 시트를 대상 유리창에 부착 후 제거하도록 하여, 쉽고 편리하게 시공할 수 있도록 하여, 차량 유리창에 형성된 유막을 제거할 때의 부가적인 에너지소비와 노력의 낭비를 절약 할 수 있는 효과가 있다.The adhesive oil film removal sheet for vehicles according to the present invention allows the vehicle adhesive oil film removal sheet to be removed after attaching to the target window, rather than the conventional polishing method using an abrasive, so that it can be easily and conveniently installed, and is formed on the vehicle window. There is an effect of saving additional energy consumption and waste of effort when removing the oil film.

또한, 염기성용액을 이용하여 유리표면을 1~2 나노미터(nm)로 깎아서 유막을 제거하여 강우시나 야간 주행 시 운전자의 시야를 확보하여 유막 현상으로 인해 일어나는 교통사고를 방지하는 효과가 있다.In addition, there is an effect of preventing traffic accidents caused by the oil film phenomenon by securing the driver's visibility during rainfall or night driving by removing the oil film by cutting the glass surface to 1 to 2 nanometers (nm) using a basic solution.

도 1은 본 발명의 일실시예에 따른 차량용 점착식 유막제거 시트의 사시도이다.
도 2는 본 발명에 따른 차량용 점착식 유막제거 시트의 다른 실시예에 따라 구조를 도시한 분해 사시도이다.
도 3은 도2의 다른 실시예에 따라 자동차 전면 유리에 점착된 상태도이다.
도 4는 본 발명에 따른 차량용 점착식 유막제거 시트의 시공방법을 도시한 순서도이다.
1 is a perspective view of an adhesive oil film removal sheet for a vehicle according to an embodiment of the present invention.
Figure 2 is an exploded perspective view showing a structure according to another embodiment of the adhesive oil film removal sheet for a vehicle according to the present invention.
3 is a diagram illustrating a state of being adhered to a windshield of a vehicle according to another exemplary embodiment of FIG. 2.
Figure 4 is a flow chart showing the construction method of the adhesive oil film removal sheet for a vehicle according to the present invention.

본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 첨부되는 도면과함께 상세하게 후술되어 있는 실시예들을 참조하면 명확해질 것이다. 그러나 본 발명은 이하에서 개시되는 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 본 실시예들은 본 발명의 개시가 완전하도록 하며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 발명은 청구항의 범주에 의해 정의될 뿐이다. Advantages and features of the present invention, and a method of achieving them will become apparent with reference to the embodiments described below in detail together with the accompanying drawings. However, the present invention is not limited to the embodiments disclosed below, but will be implemented in various forms different from each other, and only these embodiments make the disclosure of the present invention complete, and common knowledge in the technical field to which the present invention pertains. It is provided to completely inform the scope of the invention to the possessor, and the invention is only defined by the scope of the claims.

아래 첨부된 도면을 참조하여 본 발명의 실시를 위한 구체적인 내용을 상세히 설명한다. 도면에 관계없이 동일한 부재번호는 동일한 구성요소를 지칭하며, "및/또는"은 언급된 아이템들의 각각 및 하나 이상의 모든 조합을 포함한다.With reference to the accompanying drawings below will be described in detail for the implementation of the present invention. Regardless of the drawings, the same reference numerals refer to the same elements, and "and/or" includes each and all combinations of one or more of the recited items.

본 명세서에서 사용된 용어는 실시예들을 설명하기 위한 것이며, 본 발명을 제한하고자 하는 것은 아니다. 본 명세서에서, 단수형은 문구에서 특별히 언급하지 않는 한 복수형도 포함한다. 명세서에서 사용되는 "포함한다(comprises)" 및/또는 "포함하는(comprising)"은 언급된 구성요소 외에 하나 이상의 다른 구성요소의 존재 또는 추가를 배제하지 않는다.The terms used in the present specification are for describing exemplary embodiments, and are not intended to limit the present invention. In this specification, the singular form also includes the plural form unless specifically stated in the phrase. As used herein, “comprises” and/or “comprising” do not exclude the presence or addition of one or more other elements other than the mentioned elements.

다른 정의가 없다면, 본 명세서에서 사용되는 모든 용어(기술 및 과학적 용어를 포함)는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 공통적으로 이해될 수 있는 의미로 사용될 수 있을 것이다. 또 일반적으로 사용되는 사전에 정의되어 있는 용어들은 명백하게 특별히 정의되어 있지 않는 한 이상적으로 또는 과도하게 해석되지 않는다.Unless otherwise defined, all terms (including technical and scientific terms) used in the present specification may be used with meanings that can be commonly understood by those of ordinary skill in the art to which the present invention belongs. In addition, terms defined in a commonly used dictionary are not interpreted ideally or excessively unless explicitly defined specifically.

도 1은 본 발명의 일실시예에 따른 차량용 점착식 유막제거 시트의 사시도이고, 도 2는 본 발명에 따른 차량용 점착식 유막제거 시트의 다른 실시예에 따라 구조를 도시한 분해 사시도이고, 도 3은 도2의 다른 실시예에 따라 자동차 전면 유리에 점착된 상태도이고, 도 4는 본 발명에 따른 차량용 점착식 유막제거 시트의 시공방법을 도시한 순서도이다.1 is a perspective view of an adhesive oil film removal sheet for a vehicle according to an embodiment of the present invention, and FIG. 2 is an exploded perspective view showing a structure according to another embodiment of an adhesive oil film removal sheet for a vehicle according to the present invention, and FIG. Is a state diagram adhered to the windshield of a vehicle according to another embodiment of FIG. 2, and FIG. 4 is a flowchart illustrating a method of constructing an adhesive oil film removal sheet for a vehicle according to the present invention.

이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예를 상세히 설명하기로 한다. Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

먼저, 부착시트(110)는 염기성용액이 함침 되고, 차량 유리창과 대응되는 형상으로 이루어져 상기 유리창에 점착이 가능하도록 한다.First, the attachment sheet 110 is impregnated with a basic solution and has a shape corresponding to the vehicle window so that it can be adhered to the window.

또한, 상기 부착시트(110)는 염기에 강한 PTFE(폴리테트라플루오로에틸렌) 용기에 염기성용액을 충분히 담고, 상기 부착시트(110)를 상기 용기에 담근 뒤 적절한 시간이 지난 후 들어 올림으로써 상기 부착시트(110)에 상기 염기성용액이 함침 된다.In addition, the attachment sheet 110 sufficiently contains a basic solution in a base-resistant PTFE (polytetrafluoroethylene) container, and the attachment sheet 110 is immersed in the container and lifted up after an appropriate time has passed. The basic solution is impregnated into the sheet 110.

좀 더 구체적으로 설명하자면, 상기 PTFE(폴리테트라플루오로에틸렌)는 지구상에 알려진 모든 재료 중에서 응집력이 가장 높고, 상기 PTFE(폴리테트라플루오로에틸렌)를 녹이는 용매는 없는 특성을 가져 매우 안정하여 염기와 산에서도 안전하게 사용되고 있다. To be more specific, the PTFE (polytetrafluoroethylene) has the highest cohesive strength among all materials known on the planet, and has no solvent dissolving the PTFE (polytetrafluoroethylene), so it is very stable. It is also used safely in the mountains.

여기서, 상기 부착시트(110)는 부직포 또는 면과 같은 재질의 섬유로 형성된다.Here, the attachment sheet 110 is formed of a nonwoven fabric or fiber made of a material such as cotton.

또한, 상기 부착시트(110)의 하부 양측으로 고리형태로 연장 형성되는 탄성재질의 고리부(111)를 더 포함하여 형성되고, 상기 부착시트(110)를 작업 대상 유리창에 점착 후 상기 고리부(111)를 차량 사이드미러에 고정하여 사용이 가능하다. In addition, it is formed by further comprising a ring portion 111 of an elastic material extending in a ring shape to both sides of the lower side of the attachment sheet 110, and after the attachment sheet 110 is adhered to the work target glass window, the ring portion ( 111) can be used by fixing it to the vehicle side mirror.

따라서, 상기 부착시트(110)는 부직포 또는 면과 같은 재질의 섬유에 의해 염기성용액이 함침 되고 축축하게 젖은 형태로 유지가 가능하다. Therefore, the attachment sheet 110 is impregnated with a basic solution by fibers made of a material such as nonwoven fabric or cotton, and can be maintained in a moist and wet form.

또한, 상기 부착시트(110)에 함침 되어 있는 염기성 용액에 의해 화학적 반응에 따른 표면식각을 통하여 유리표면이 1~2 나노미터(nm)로 깎이게 되어 유막 제거가 가능하다.In addition, the surface of the glass is cut to 1 to 2 nanometers (nm) through surface etching according to a chemical reaction by the basic solution impregnated in the attachment sheet 110, so that the oil film can be removed.

또한, 상기 부착시트(110)에 함침되어 있는 염기성용액은 수산화칼륨 2~20 중량부, 이소프로필알코올 80~98 중량부를 포함하여 구성되어 있으며, 더욱 바람직하게는 수산화칼륨 5 중량부, 이소프로필알코올 95 중량부를 포함하여 구성될 수 있다.In addition, the basic solution impregnated in the attachment sheet 110 is composed of 2 to 20 parts by weight of potassium hydroxide, 80 to 98 parts by weight of isopropyl alcohol, more preferably 5 parts by weight of potassium hydroxide, isopropyl alcohol It may be configured to include 95 parts by weight.

상기 염기성용액은 다음과 같이 제조가 가능하다.The basic solution can be prepared as follows.

먼저, 상기 수산화칼륨을 상기 이소프로필알코올에 호모게나이저를 이용하여 분산시킨다.First, the potassium hydroxide is dispersed in the isopropyl alcohol using a homogenizer.

다음, 분산된 상기 수산화칼륨이 상기 이소프로필알코올에 완전히 용해될 수 있도록 300rpm의 속도로 교반을 실시한다.Next, stirring is performed at a speed of 300 rpm so that the dispersed potassium hydroxide can be completely dissolved in the isopropyl alcohol.

다음, 소포제, 점증제 등의 첨가제를 넣어 상기 염기성용액을 제조할 수 있다.Next, the basic solution may be prepared by adding an additive such as an antifoaming agent or a thickener.

여기서, 상기 소포제는 생산과정에서 재료에 의해 형성된 거품을 제거하는 기능을 하는 보조제 역할을 한다.Here, the antifoaming agent serves as an auxiliary agent that functions to remove bubbles formed by the material during the production process.

또한, 상기 점증제는 제품의 점착성 및 점도를 증가시키고, 유화안정성을 증진하며 물성 및 촉감을 향상시키기 위한 첨가물로 각 성분들이 서로 뭉치게 해주면서 안정화작용과 점성을 높일 수 있다.In addition, the thickener is an additive to increase the adhesiveness and viscosity of the product, improve emulsion stability, and improve physical properties and touch, and can increase the stabilization and viscosity while allowing each component to clump together.

전술된 일실시예에 추가하여 다른 실시예로, 도 2를 참고하면, 상기 부착시트(110)를 기준으로 하부 점착면에 보호필름(120), 상부에는 덮개(140)를 더 포함하여 이루어질 수 있다.In addition to the above-described embodiment, as another embodiment, referring to FIG. 2, a protective film 120 on the lower adhesive surface and a cover 140 on the upper portion may be further included based on the attachment sheet 110. have.

더불어, 상기 부착시트(110)와 상기 덮개(140)사이에 메쉬망(130)을 더 포함할 수 있다.In addition, a mesh network 130 may be further included between the attachment sheet 110 and the cover 140.

좀 더 구체적으로 설명하자면, 상기 보호필름(120)은, 상기 부착시트(110) 하부 점착면에 부착되고, 상기 염기성용액이 함침 되어 있는 상기 부착시트(110)가 이물질로부터 오염되거나 손상되는 것을 방지 할 수 있게 한다.In more detail, the protective film 120 is attached to the lower adhesive surface of the attachment sheet 110 and prevents the attachment sheet 110 impregnated with the basic solution from being contaminated or damaged by foreign substances. To be able to do it.

여기서, 상기 보호필름(120)은 박리지 또는 필름지가 사용된다. Here, as the protective film 120, release paper or film paper is used.

다음, 상기 메쉬망(130)은, 상기 부착시트(110)와 상기 덮개(140) 사이에 형성되어 상기 부착시트(110)에 함침 되어 있는 염기성용액의 균일하게 분산 할 수 있게 한다.Next, the mesh net 130 is formed between the attachment sheet 110 and the cover 140 so that the basic solution impregnated in the attachment sheet 110 can be uniformly dispersed.

즉, 상기 메쉬망(130)에 형성되어 있는 그물눈(131)에 일정한 염기성용액이 머금게 하여 상기 염기성용액의 균일한 분산이 가능하다.That is, a certain basic solution is contained in the mesh 131 formed in the mesh network 130, so that the basic solution can be uniformly dispersed.

다음, 상기 덮개(140)는, 상기 메쉬망(130) 상부에 적층된다.Next, the cover 140 is stacked on the mesh network 130.

이에, 상기 덮개(140)는 외부로부터는 오염물질의 유입을 막을 수 있고, 상기 부착시트(110)에 함침 되어 있는 염기성 용액이 외부로 새어나가는 것을 방지할 수 있도록 한다. Accordingly, the cover 140 may prevent the inflow of contaminants from the outside, and prevent the basic solution impregnated in the attachment sheet 110 from leaking to the outside.

또한, 상기 덮개(140)는, 외부로부터 보호가 되는 제 1면은 방수가 가능한 재질이고, 상기 메쉬망(130)과 마주하는 제 2면은 부드럽고 유연한 재질로 이루어진다.In addition, in the cover 140, a first surface protected from the outside is made of a waterproof material, and a second surface facing the mesh net 130 is made of a soft and flexible material.

또한, 상기 덮개(140)는, 양측으로 탄성재질의 날개가 연장 형성되는 날개부(141)가 형성된다.In addition, the cover 140 is formed with wing portions 141 in which wings of an elastic material are extended to both sides.

이때, 상기 날개부(141)는 작업 대상 자동차 내부 프레임에 삽입되어 상기 부착시트(110)가 점착된 상태를 고정할 수 있게 한다.At this time, the wing portion 141 is inserted into the inner frame of the vehicle to be worked so that the attachment sheet 110 can be fixed to the adhered state.

여기서, 상기 날개부(141) 탄력을 이용하여 양측으로 당겨 자동차 내부 프레임에 삽입하여 고정할 시, 상기 부착시트(110)가 작업 대상의 유리표면에 더욱 밀착되는 역할도 한다.Here, when the wing portion 141 is pulled to both sides using the elasticity and inserted into the vehicle inner frame to be fixed, the attachment sheet 110 also serves to more closely adhere to the glass surface of the work object.

또한, 상기 날개부(141)는 복수개의 절개홈(142)이 더 형성된다.In addition, the wing portion 141 is further formed with a plurality of cut grooves 142.

따라서, 상기 날개부(141)에 형성된 양측 복수개의 상기 절개홈(142)이 벌어지게 되면서 더 길게 늘어날 수 있게 한다.Accordingly, as the plurality of cutout grooves 142 formed on both sides of the wing portion 141 are opened, it can be extended longer.

한편, 상기 날개부(141)의 다른 실시예로, 양측 끝단에 고리를 형성하여 타이어 휠에 결속되도록 하여 상기 차량용 점착식 유막제거 시트팩(10)을 고정시키는 것도 가능하다.On the other hand, as another embodiment of the wing portion 141, it is possible to fix the adhesive-type oil film removal sheet pack 10 for a vehicle by forming rings at both ends to be bound to the tire wheel.

한편, 도 4를 참조하여 차량용 점착식 유막제거 시트의 시공방법에 대해서 설명하기로 한다.Meanwhile, a method of constructing an adhesive oil film removal sheet for a vehicle will be described with reference to FIG. 4.

본 발명의 차량용 점착식 유막제거 시트의 시공방법은 팩 부착 단계(S10), 방치 단계(S20), 팩 제거 단계(S30) 및 세척 단계(S40) 단계로 나뉘어 수행된다.The construction method of the adhesive oil film removal sheet for a vehicle of the present invention is performed by being divided into a pack attaching step (S10), a leaving step (S20), a pack removing step (S30), and a washing step (S40).

먼저, 팩 부착 단계(S10)는 유막을 제거하기 위한 작업 대상 차량 유리창에 상기 차량용 점착식 유막제거 시트팩(10)을 부착하는 시공 작업 단계로서, 상기 부착시트(110) 하부 점착면에 상기 부착시트(110) 점착면을 보호하기 위한 상기 보호 필름(120)을 제거한다. First, the pack attaching step (S10) is a construction work step of attaching the vehicle adhesive oil film removal sheet pack 10 to a target vehicle window for removing the oil film, and the attachment to the adhesive surface under the attachment sheet 110 The protective film 120 for protecting the adhesive surface of the sheet 110 is removed.

다음, 상기 부착시트(110)의 점착면과 작업 대상 차량 유리창을 모두 덮게 부착시킨다.Next, attach to cover both the adhesive surface of the attachment sheet 110 and the window of the vehicle to be operated.

다음, 상기 덮개(140)에 연장 형성되어 있는 상기 날개부(141)를 차량 내부 프레임에 삽입하여 상기 차량용 점착식 유막제거 시트팩(10)을 고정시킨다. Next, the wing portion 141 extending from the cover 140 is inserted into the vehicle inner frame to fix the adhesive-type oil film removal sheet pack 10 for the vehicle.

다음, 방치 단계(S20)는 상기 부착시트(110)에 함침 되어 있는 염기성용액에 의해 화학적 반응에 따른 표면식각을 통하여 유리표면이 1~2 나노미터(nm)로 깎이게 되어 유막을 제거하게 된다.Next, in the leaving step (S20), the surface of the glass is cut to 1 to 2 nanometers (nm) through surface etching according to a chemical reaction by the basic solution impregnated in the attachment sheet 110 to remove the oil film. .

다음, 팩 제거 단계(S30)에서는 상기 염기성용액에 의해 유막이 제거되는 상기 방치 단계(S30)를 거친 후, 차량 내부 프레임에 삽입되어 있는 상기 날개부(141)를 제거하고, 작업 대상 차량 유리표면으로부터 부착되어 있는 상기 차량용 점착식 유막제거 시트팩(10)을 제거한다.Next, in the pack removal step (S30), after the leaving step (S30) in which the oil film is removed by the basic solution, the wing part 141 inserted into the vehicle interior frame is removed, and the glass surface of the vehicle to be operated The adhesive-type oil film removal sheet pack 10 for a vehicle attached from is removed.

다음, 세척 단계(S40)에서는 작업 대상 유리 표면에 남아 있는 오염물질 또는 상기 염기성용액을 제거 하기위하여 물 또는 수증기로 세척을 진행하는 작업 단계로써 세척 후, 남은 물기를 수건 또는 천으로 제거하면 시공 작업이 완료된다.Next, in the washing step (S40), the cleaning is performed with water or steam to remove the contaminants or the basic solution remaining on the surface of the target glass.After washing, the remaining water is removed with a towel or cloth. This is done.

따라서, 전술한 바와 같은 차량용 점착식 유막제거 시트의 구성에 의해서, 작업 대상의 자동차 유리 표면에 부착하여 상기 부착시트(110)에 함침 되어 있는 염기성용액에 의한 화학적 반응에 따른 표면식각을 통하여 유리 표면이 1~2 나노미터(nm)로 깎여서 유막을 제거 후 차량용 점착식 유막제거 시트를 제거 할 수 있도록 하여, 차량 유리창에 형성된 유막을 제거할 때의 시공의 편리함과 부가적인 에너지와 시간 등의 낭비를 절약 할 수 있다.Therefore, by the configuration of the vehicular adhesive oil film removal sheet as described above, the glass surface is adhered to the surface of the vehicle glass to be worked and the surface of the glass is etched according to a chemical reaction by the basic solution impregnated in the attachment sheet 110. After removing the oil film by cutting it into 1~2 nanometers (nm), it is possible to remove the adhesive-type oil film removal sheet for vehicles, so that the convenience of construction and additional energy and time when removing the oil film formed on the window of a vehicle You can save waste.

이상과 첨부된 도면을 참조하여 본 발명의 실시예를 설명하였지만, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자는 본 발명이 그 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해되어야 한다. Although the embodiments of the present invention have been described with reference to the above and the accompanying drawings, those of ordinary skill in the art to which the present invention pertains can be implemented in other specific forms without changing the technical spirit or essential features of the present invention. You can understand that there is. Therefore, it is to be understood that the embodiments described above are illustrative and non-limiting in all respects.

S10 : 팩 부착 단계
S20 : 방치 단계
S30 : 팩 제거 단계
S40 : 세척 단계
10 : 차량용 점착식 유막제거 시트팩
110 : 부착시트 111 : 고리부
120 : 보호필름 130 : 메쉬망
131 : 그물눈 140 : 덮개
141 : 날개부 142 : 절개홈
S10: step of attaching the pack
S20: neglect stage
S30: Steps to remove the pack
S40: washing step
10: Vehicle adhesive oil film removal sheet pack
110: attachment sheet 111: hook portion
120: protective film 130: mesh net
131: mesh 140: cover
141: wing part 142: incision groove

Claims (9)

염기성용액이 함침되고, 차량 유리창과 대응되는 형상으로 이루어져 상기 유리창에 점착되어 상기 염기성용액과 유리창의 화학 반응에 따른 표면식각을 통하여 유막이 제거되는 섬유재질의 부착시트를 포함하여 이루어지는 것을 특징으로 하는 차량용 점착식 유막제거 시트. Characterized in that it comprises a fibrous attachment sheet that is impregnated with a basic solution and has a shape corresponding to the vehicle window, and is adhered to the window and the oil film is removed through surface etching according to a chemical reaction between the basic solution and the window. Adhesive oil film removal sheet for vehicles. 제1항에 있어서,
상기 염기성용액은 수산화칼륨 2~20 중량부, 이소프로필알코올 80~98 중량부를 포함하는 것을 특징으로 하는 차량용 점착식 유막제거 시트.
The method of claim 1,
The basic solution includes 2 to 20 parts by weight of potassium hydroxide and 80 to 98 parts by weight of isopropyl alcohol.
제1항에 있어서,
상기 부착시트의 하부 양측으로 고리형태로 연장 형성되는 탄성재질의 고리부가 더 형성되는 것을 특징으로 하는 차량용 점착식 유막제거 시트.
The method of claim 1,
An adhesive oil film removal sheet for a vehicle, characterized in that further annular portions of an elastic material are formed extending in a ring shape to both sides of the lower portion of the attachment sheet.
제1항에 있어서,
상기 부착시트의 하부 점착면에 부착 형성되되, 상기 부착시트가 이물질로부터 오염되거나 손상되는 것을 방지하며, 시트를 차량 유리창에 부착시 제거되는 보호필름이 더 포함되는 것을 특징으로 하는 차량용 점착식 유막제거 시트.
The method of claim 1,
It is attached to the lower adhesive surface of the attachment sheet, prevents the attachment sheet from being contaminated or damaged by foreign substances, and further includes a protective film that is removed when the sheet is attached to a vehicle window Sheet.
제4항에 있어서,
상기 보호필름은 박리지 또는 필름지인 것을 특징으로 하는 차량용 점착식 유막제거 시트.
The method of claim 4,
The protective film is a vehicular adhesive oil film removal sheet, characterized in that the release paper or film paper.
제1항에 있어서,
상기 부착시트 상부에 부착 형성되되, 외부로부터의 오염물질이 상기 부착시트에 부착되는 것을 방지하는 덮개가 더 포함되는 것을 특징으로 하는 차량용 점착식 유막제거 시트.
The method of claim 1,
Doedoe attached to the upper portion of the attachment sheet, the adhesive-type oil film removal sheet for a vehicle, characterized in that it further comprises a cover that prevents contamination from the outside from adhering to the attachment sheet.
제6항에 있어서,
상기 덮개의 양측으로 연장 형성되는 탄성재질의 날개부가 더 형성되는 것을 특징으로 하는 차량용 점착식 유막제거 시트
The method of claim 6,
An adhesive oil film removal sheet for a vehicle, characterized in that the wing portions of an elastic material extending to both sides of the cover are further formed
제7항에 있어서,
상기 날개부는 세로 방향으로 복수 개의 절개홈이 더 형성되는 것을 특징으로 하는 차량용 점착식 유막제거 시트.
The method of claim 7,
The wing portion is an adhesive type oil film removal sheet for a vehicle, characterized in that the plurality of cut grooves are further formed in the vertical direction.
제5항에 있어서,
상기 부착시트와 상기 덮개 사이에 형성되고, 상기 부착시트에 함침 되어 있는 염기성용액을 균일하게 분산하기 위한 메쉬망이 더 포함되는 것을 특징으로 하는 차량용 점착식 유막제거 시트.
The method of claim 5,
An adhesive oil film removal sheet for a vehicle, which is formed between the attachment sheet and the cover, and further comprises a mesh net for uniformly dispersing the basic solution impregnated in the attachment sheet.
KR1020190148797A 2019-11-19 2019-11-19 Adhesive oil film removal sheet for vehicles KR102343308B1 (en)