KR20200097835A - Cut off mat and method for reclaiming livestock using cufoff - Google Patents

Cut off mat and method for reclaiming livestock using cufoff Download PDF

Info

Publication number
KR20200097835A
KR20200097835A KR1020190014781A KR20190014781A KR20200097835A KR 20200097835 A KR20200097835 A KR 20200097835A KR 1020190014781 A KR1020190014781 A KR 1020190014781A KR 20190014781 A KR20190014781 A KR 20190014781A KR 20200097835 A KR20200097835 A KR 20200097835A
Authority
KR
South Korea
Prior art keywords
weight
parts
mat
resin
livestock
Prior art date
Application number
KR1020190014781A
Other languages
Korean (ko)
Inventor
박인배
Original Assignee
유한회사 대산환경
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 유한회사 대산환경 filed Critical 유한회사 대산환경
Priority to KR1020190014781A priority Critical patent/KR20200097835A/en
Publication of KR20200097835A publication Critical patent/KR20200097835A/en
Priority to KR1020210121524A priority patent/KR102392486B1/en

Abstract

The present invention relates to a water-proof mat positioned in a buried hole and the livestock landfill method using the same. The livestock landfill method includes the steps of: forming a buried hole from the ground; installing a water-proof mat covering the entire area of a wall of the buried hole in the buried hole; installing a plurality of box-type kits made of a biodegradable material and filled with an eco-friendly adsorbent inside the water-proof mat; forming a first covering layer by applying soil or limestone to an upper portion of the box-type kits; burying destroyed livestocks over the first covering layer; and forming a second covering layer (140) by applying soil or limestone over the buried livestocks and installing a perforated pipe (150).

Description

차수매트를 이용한 가축 매립방법{CUT OFF MAT AND METHOD FOR RECLAIMING LIVESTOCK USING CUFOFF}Livestock reclamation method using shading mat {CUT OFF MAT AND METHOD FOR RECLAIMING LIVESTOCK USING CUFOFF}

본 발명은 가축의 살처분을 매립방식으로 하는 경우, 매립홀에 위치하는 차수매트와 그 차수매트를 이용한 가축 매립 방법에 관한 것이다.The present invention relates to a burial mat located in a burial hole and a livestock burial method using the burial mat when the killing of livestock is used as a burial method.

축산 농가 및 양식장에서는 각종 동물의 전염병을 막기 위하여 예방접종이나, 축사 및 양식장의 환경 개선등의 노력에도 불구하고 해마다 가축과 어패류 등의 동물에서 전염병이 계속 발생하고 있는 실정이며, 전염성 병균에 노출된 동물, 또는 전염병에 전염된 동물 및 질병이나 전염병으로 폐사된 동물을 처분하고 있는 실정이다.In livestock farms and farms, infectious diseases continue to occur in animals such as livestock and fish and shellfish every year despite efforts such as vaccination to prevent infectious diseases of various animals, and improvement of the environment of livestock and farms, and are exposed to infectious germs. Animals or animals transmitted by infectious diseases and animals killed by diseases or infectious diseases are being disposed of.

따라서, 최근 가축의 처분방법에 대한 관심이 높아지고 있으며, 이러한 가축의 처분방법은 매립, 소각, 퇴비화등의 방법이 있다. 매립은 전통적으로 사용되어 온 방법이며, 경제적이며 잠재적인 감염성 물질을 이송할 필요없어 안전하고, 질병에 감염된 가축을 신속하게 처리할 수 있다는 장점이 있으나, 가축 부패에 의한 오염된 물질이 누수되어 환경과 위생적 측면에서 우려의 소지가 있는 단점이 있다.Accordingly, there is a growing interest in the disposal method of livestock in recent years, and such methods of disposing of livestock include landfill, incineration, and composting. Landfill is a method that has been used traditionally. It is economical and has the advantage of being safe because it does not need to transport potentially infectious substances, and has the advantage of being able to quickly dispose of infected livestock. There are drawbacks that may be of concern in terms of hygiene and hygiene.

또한, 소각은 화재위험성 내재, 다량의 재(ash) 처리 문제 광물류 연소에 의한 지하수, 토양 오염 가능성이 높은 단점이 있다.In addition, incineration has disadvantages of high possibility of groundwater and soil contamination due to fire hazard inherent, large amount of ash treatment problem, and mineral combustion.

도 1은 종래의 가축 살처분 매립방법의 실시예를 나타낸 개략도이다.1 is a schematic diagram showing an embodiment of a conventional livestock killing method.

일반적인 가축 살처분 매립방법은 매립홀 형성단계, 방수부재 설치단계, 살균부재 설치단계,회수관 설치단계, 매립단계, 발효단계 및 회수단계를 포함한다.The general livestock disposal method includes a burial hole formation step, a waterproof member installation step, a sterilization member installation step, a collection pipe installation step, a landfill step, a fermentation step, and a recovery step.

상기 매립홀 형성단계는 지중(1)에 지면에 대하여 약 5도의 경사각을 가지도록 매립홀(10)을 형성한다. 이 때, 상기 경사각은 지면에 대하여 이상으로 형성된다.In the step of forming the buried hole, the buried hole 10 is formed in the underground 1 to have an inclination angle of about 5 degrees with respect to the ground. At this time, the inclination angle is formed more than that with respect to the ground.

또한, 상기 방수부재 설치단계는 상기 매립홀(10)의 바닥면에 방수부재(20)를 설치하여 집수정(30)을 형성한다. 따라서, 가축(2)이 발효된 침출물이 토양으로 흡수되지 않고 상기 매립홀(10)의 하측에 형성된 집수정(30)에 고이게 된다.In addition, in the step of installing the waterproof member, the water collecting well 30 is formed by installing the waterproof member 20 on the bottom surface of the buried hole 10. Accordingly, the fermented leachate of the livestock 2 is not absorbed into the soil and is collected in the water collecting well 30 formed under the buried hole 10.

이 때, 상기 매립홀(10)이 지면에 대하여 5도 이상의 경사각을 가짐으로써, 상기 침출물이 신속하게 집수정(30)으로 이송된다. 또한, 상기 경사각이 5도~8도 의 완만한 경사각으로 형성될 경우, 상기 가축(2)의 매립 과정에서의 토사붕괴를 방지하는 효과가 있었다.At this time, since the buried hole 10 has an inclination angle of 5 degrees or more with respect to the ground, the leachate is quickly transferred to the water collection well 30. In addition, when the inclination angle is formed with a gentle inclination angle of 5 degrees to 8 degrees, there is an effect of preventing soil collapse in the burial process of the livestock 2.

또한, 상기 방수부재 설치단계는 상기 매립홀(10)의 내면 전체에 상기 방수부재(20)를 설치하되 이중으로 설치하여, 매몰되는 상기 가축(2)의 뿔이나 발굽에 의해 상기 방수부재(20)가 손상되어 토양으로 침출물이 흡수되는 것을 방지한다.In addition, in the step of installing the waterproof member, the waterproof member 20 is installed on the entire inner surface of the buried hole 10, but is double-installed, so that the waterproof member 20 by the horns or hoofs of the livestock 2 to be buried. ) Is damaged and prevents the absorption of leachate into the soil.

또한, 상기 방수부재(20)는 비닐로 형성될 수 있으며, 목적에 벗어남 없이 다양한 재질로 변형실시가능하다.In addition, the waterproof member 20 may be formed of vinyl, and may be transformed into various materials without departing from the purpose.

상기 살균부재 설치단계는 상기 방수부재(20)의 상면에 살균부재(40)를 설치한다. 상기 살균부재(40)는 소독약품, 생석회, 사체발효제 및 볏짚거적을 포함하여 형성된다. 따라서, 상기 가축(2)의 발효가 신속하게 이루어질 수 있는 효과가 있으며, 동시에 악취가 제거되는 효과가 있었다.In the step of installing the sterilizing member, a sterilizing member 40 is installed on the upper surface of the waterproof member 20. The sterilizing member 40 is formed to include a disinfectant, quicklime, a carcass fermentation agent, and a straw bale. Therefore, there is an effect that fermentation of the livestock 2 can be made quickly, and at the same time, there is an effect of removing odor.

또한, 상기 살균부재(40)는 볏짚거적 이외에도 쌀겨, 등 목적에 벗어남 없이 다양하게 변형실시 가능하다.In addition, the sterilization member 40 can be variously modified without departing from the purpose of rice bran, etc. in addition to rice straw.

상기 회수관 설치단계는 상기 매립홀(10)의 일측에 침출물 회수관(50)을 설치한다. 상기 침출물 회수관(50)은 상기 매립홀(10)의 하측에 형성된 집수정(30)에 고인 침출물에 상기 침출물 회수관(50)의 일단부가 닿도록 상기 집수정(30)의 바닥면에 인접하도록 설치된다.In the step of installing the collection pipe, a leachate collection pipe 50 is installed at one side of the buried hole 10. The leachate collection pipe 50 is the bottom of the water collection well 30 so that one end of the leachate collection pipe 50 contacts the leachate accumulated in the water collection well 30 formed at the lower side of the buried hole 10. It is installed adjacent to the surface.

상기 매립단계는 상기 매립홀(10)에 상기 가축(2)을 넣은 후, 상기 가축(2)이 움직이지 않도록 상기 가축(2)의 상부를 면사(61)로 고정하고, 상기 면사(61) 상측으로 복토층(60)을 형성하며, 복토층의상부 및 둘레부에 나무 또는 식물(62)을 식재한다.In the reclaiming step, after placing the livestock 2 in the burying hole 10, the upper part of the livestock 2 is fixed with cotton yarn 61 so that the livestock 2 does not move, and the cotton yarn 61 The covering layer 60 is formed on the upper side, and trees or plants 62 are planted in the upper and circumferential portions of the covering layer.

상기 복토층(60)은 50cm 이상으로 형성된다. 따라서, 대기공간으로 상기 가축(2)의 발효 과정에서 발생하는 악취 및 유해가스가 방출되는 것을 방지하는 효과가 있었다.The covering layer 60 is formed to be 50 cm or more. Accordingly, there is an effect of preventing the discharge of odors and harmful gases generated during the fermentation process of the livestock 2 into the atmosphere space.

또한, 상기 매립단계는 상기 가축(2)을 상기 면사(61)로 고정함으로써, 상기 가축(2) 발효 과정에서 발생하는 가스로 인하여 상기 가축(2)이 복토층 상부로 분출되는 것을 방지하며, 발효 과정에서 발생하는 악취 또한 제거할 수 있는 효과가 있었다.In addition, in the landfilling step, by fixing the livestock 2 with the cotton yarn 61, the livestock 2 is prevented from being ejected to the upper part of the covered soil due to gas generated during the fermentation process of the livestock 2, and fermentation There was an effect of removing odors generated during the process.

또한, 상기 매립단계는 상기 나무 또는 식물(62)을 상기 복토층(60)의 상부 및 둘레부에 식재함으로써, 토양을 정화하고 토사가 붕괴되는 것을 방지함으로써, 친환경적인 효과가 있었다.In addition, the reclaiming step has an eco-friendly effect by planting the trees or plants 62 on the upper and circumferential portions of the cover layer 60 to purify the soil and prevent the soil from collapsing.

그러나 상기와 같은 종래의 방수부재(20)는 비닐로 형성되기에 침출물(수)가 발생할 수 있고, 깨질수도 있어 문제가 되었다.However, since the conventional waterproof member 20 as described above is formed of vinyl, the leachate (water) is It could happen, it could break, and it became a problem.

실시 예는 침출물(침출수)을 방지하고, 단단하고 깨지지 않고 불에 타지 않은 차수매트를 제공하는 것을 목적으로 한다.The embodiment aims to prevent leachate (leachate), and to provide a hard, unbreakable, non-burnable shading mat.

본 발명은 상기 차수매트를 이용한 가축 매립방법을 제공한다.The present invention provides a livestock landfill method using the barrier mat.

실시 예에 따른 차수매트 및 그 차수매트를 이용한 가축 매립방법은,The order mat and the livestock landfill method using the order mat according to the embodiment,

지면으로부터 일정 깊이와 너비를 갖는 매립홀(100)을 형성하는 단계;Forming a buried hole 100 having a predetermined depth and width from the ground;

상기 매립홀(100)의 내부에 매립홀 벽면 전체 면적을 커버하는 차수매트An order mat that covers the entire area of the wall of the buried hole inside the buried hole 100

(110)를 설치하는 단계;Installing 110;

상기 차수매트(110)의 내부에 생분해성 소재로 이루어지고 내부에는 친환경 흡착제가 채워져 있는 다수의 박스형 키트(120)를 설치하는 단계;Installing a plurality of box-type kits 120 made of a biodegradable material inside the water shielding mat 110 and filled with an eco-friendly adsorbent therein;

상기 차수매트(110)의 내부 바닥에 설치되어 있는 박스형 키트(120)의 상부에 흙 또는 석회석을 도포하여 제1복 토층(130)을 형성하는 단계;Forming a first cover layer 130 by applying soil or limestone to an upper portion of the box-type kit 120 installed on the inner floor of the water-shielding mat 110;

상기 제1복토층(130)의 상부에 살처분 가축을 매립하는 단계; 및Burying livestock for killing on the top of the first cover layer 130; And

상기 매립되어 있는 살처분 가축의 상부에 흙 또는 석회석을 도포하여 제2복토층(140)을 형성함과 더불어 유공 관(150)을 설치하는 단계; 를 포함하고,Applying soil or limestone to the top of the buried livestock to form a second covering layer 140 and installing a perforated pipe 150; Including,

상기 차수매트는, 부직포를 기재로한 매트에,The water-resistant mat is a non-woven fabric-based mat,

차수를 위한 폴리에칠렌(PE), 폴리프로필렌(PP) 및 폴리에스터(PET)중에서 어느 하나를 사용하며 그 중량은 100 중량부;Polyethylene (PE), polypropylene (PP), and polyester (PET) for the order are used, and the weight thereof is 100 parts by weight;

상기 차수매트의 강화재로 사용되는 섬유 100 중량부;100 parts by weight of fibers used as reinforcing materials of the water-resistant mat;

상기 섬유 100 중량부에 대하여,Based on 100 parts by weight of the fiber,

수지 30~50 중량부,30-50 parts by weight of resin,

탄화제 3~10중량부,3 to 10 parts by weight of carbonizing agent,

발포제 5~10 중량부,5 to 10 parts by weight of a foaming agent,

산촉매제 10~20 중량부,10 to 20 parts by weight of an acid catalyst,

난연제 10~20 중량부,10 to 20 parts by weight of flame retardant,

난연성 충진제 20~30 중량부,20 to 30 parts by weight of flame retardant filler,

소포제 1~3 중량부 및1 to 3 parts by weight of antifoam and

분산제 1~3 중량부가 포함되며,1 to 3 parts by weight of a dispersant are included,

상기 수지는 난연수지로써 불포화폴리에스테르수지 및 에폭시수지 중에서 어느 하나가 사용되는 것을 특징으로 하는 차수매트를 이용한 가축 매립이다.The resin is a livestock landfill using a water-resistant mat, characterized in that any one of an unsaturated polyester resin and an epoxy resin is used as a flame retardant resin.

본 발명에 따르면 침출물(침출수)을 방지하고, 단단하고 깨지지 않고 불에 타지 않은 차수매트를 제공할 수 있다.According to the present invention, it is possible to prevent leachate (leachate), and to provide a hard, non-breakable, non-burnable water-resistant mat.

도 1은 종래의 실시 예에 따른 가축 살처분 매립방법의 실시예를 나타낸 개략도
도 2는 본 발명의 일 실시예에 따른 차수매트를 이용한 가축 매립용 설치상태를 나타내는 사시도
도 3 - 도 10은 본 발명의 일 실시예에 따른 가축 매립용 매립방법을 나타내는 개략도1 is a schematic diagram showing an embodiment of a method for landfilling livestock killing according to a conventional embodiment
Figure 2 is a perspective view showing an installation state for landfilling livestock using a shading mat according to an embodiment of the present invention
Figure 3-Figure 10 is a schematic view showing a method for landfilling livestock according to an embodiment of the present invention

이하, 본 발명의 일부 실시 예들을 예시적인 도면을 통해 상세하게 설명한다. 각 도면의 구성요소들에 참조부호를 부가함에 있어서, 동일한 구성요소들에 대해서는 비록 다른 도면상에 표시되더라도 가능한 한 동일한 부호를 가지도록 하고 있음에 유의해야 한다. 또한, 본 발명의 실시 예를 설명함에 있어, 관련된 공지 구성 또는 기능에 대한 구체적인 설명이 본 발명의 실시 예에 대한 이해를 방해한다고 판단되는 경우에는 그 상세한 설명은 생략한다. Hereinafter, some embodiments of the present invention will be described in detail through exemplary drawings. In adding reference numerals to elements of each drawing, it should be noted that the same elements are assigned the same numerals as possible even if they are indicated on different drawings. In addition, in describing an embodiment of the present invention, when it is determined that a detailed description of a related known configuration or function interferes with an understanding of the embodiment of the present invention, the detailed description thereof will be omitted.

또한, 본 발명의 실시예의 구성 요소를 설명하는 데 있어서, 제 1, 제 2, A, B, (a), (b) 등의 용어를 사용할 수 있다. 이러한 용어는 그 구성 요소를 다른 구성 요소와 구별하기 위한 것일 뿐, 그 용어에 의해 해당 구성 요소의 본질이나 차례 또는 순서 등이 한정되지 않는다. In addition, in describing the constituent elements of the embodiment of the present invention, terms such as first, second, A, B, (a), (b), etc. may be used. These terms are only used to distinguish the component from other components, and the nature, order, or order of the component is not limited by the term.

또한 어떤 구성 요소가 다른 구성요소에 "연결", "결합" 또는 "접속"된다고 기재된 경우, 그 구성 요소는 그 다른 구성요소에 직접적으로 연결되거나 접속될 수 있지만, 각 구성 요소 사이에 또 다른 구성 요소가 "연결", "결합" 또는 "접속"될 수도 있다고 이해되어야 할 것이다. In addition, if a component is described as being "connected", "coupled" or "connected" to another component, the component may be directly connected or connected to the other component, but another component between each component It should be understood that elements may be “connected”, “coupled” or “connected”.

이하, 본 발명의 기술적 사상을 설명한다.Hereinafter, the technical idea of the present invention will be described.

본 발명은 가축의 살처분을 매립방식으로 하는 경우, 매립홀에 위치하는 차수매트와 그 차수매트를 이용한 가축 매립 방법에 관한 것이다.The present invention relates to a burial mat located in a burial hole and a livestock burial method using the burial mat when the killing of livestock is used as a burial method.

도 2는 본 발명의 일 실시예에 따른 차수매트를 이용한 가축 매립용 설치상태를 나타내는 사시도이고,Figure 2 is a perspective view showing an installation state for landfilling livestock using a shading mat according to an embodiment of the present invention,

도 3 - 도 10은 본 발명의 일 실시예에 따른 가축 매립용 매립방법을 나타내는 개략도이다.3 to 10 are schematic diagrams showing a method for landfilling livestock according to an embodiment of the present invention.

먼저, 본 발명에서 사용될 차수매트에 대해 설명한다.First, the order mat to be used in the present invention will be described.

본 발명의 차수매트는, The order mat of the present invention,

일반적으로 사용되는 부직포를 기재로한 매트에,On a mat based on a generally used non-woven fabric,

차수(방수포함)를 위한 폴리에칠렌(PE), 폴리프로필렌(PP) 및 폴리에스터(PET)중에서 어느 하나를 사용하며 그 중량은 100 중량부;Any one of polyethylene (PE), polypropylene (PP) and polyester (PET) for water (including waterproof) is used, and the weight thereof is 100 parts by weight;

상기 폴리에칠렌(PE), 폴리프로필렌(PP) 및 폴리에스터(PET)중에서 어느 하나를 사용하며 그 중량은 100 중량부에 대해, 탄탄하고 강화를 위해, 상기 차수매트의 강화재로 사용되는 섬유 100 중량부가 사용되며, 상기 섬유는 보강용으로 사용되며, 평직 또는 능직의 글래스 패브릭(Glass Fabric), 캐블라패브릭(Kevlar Fabric), 로빙 클로스 화이바(Roving Cloth FIber), 글래스 화이바(Glass Fiber), 케블라 화이바(Kevlar Fiber) 및 카본 화이바(Carbon Fiber) 중에서 어느 하나이다.Any one of the polyethylene (PE), polypropylene (PP) and polyester (PET) is used, and the weight is 100 parts by weight of the fiber used as a reinforcing material of the water-repellent mat for reinforcement and solidity based on 100 parts by weight. The fibers are used for reinforcement, and are plain or twilled glass fabrics, Kevlar Fabrics, Roving Cloth Fibers, Glass Fibers, and Kevlar Fibers ( Kevlar Fiber) and carbon fiber (Carbon Fiber).

또한 상기 섬유 100 중량부에 대하여,In addition, based on 100 parts by weight of the fiber,

수지 30~50 중량부를 사용하며, 상기 수지는 난연수지를 포함하며, 상온에서의 점도가 50~1500cp로 조절한 첨가형 난연용 불포화폴리에스테르수지, 브롬화된 에폭시수지 말단에 불포화폴리에스테르기를 갖는 비스 페놀형 비닐에스테르수지 및 에폭시수지 중에서 선택된 어느 하나를 사용한다.30 to 50 parts by weight of the resin is used, and the resin includes a flame retardant resin, an additive-type flame retardant unsaturated polyester resin having a viscosity of 50 to 1500 cp at room temperature, a bisphenol having an unsaturated polyester group at the end of the brominated epoxy resin Type any one selected from vinyl ester resin and epoxy resin is used.

탄화제 3~10중량부를 사용하며, 10~30㎛ 크기의 펜타에리스리톨(Pentaerythritol)이다.It uses 3 to 10 parts by weight of a carbonizing agent, and is pentaerythritol having a size of 10 to 30 μm.

발포제 5~10 중량부를 사용하며, 100~ 250 메시(mesh) 크기의 아조다이카본아마이드(Azodicarbonamide) 및 디니트로소펜타메틸렌 테드라민 (DinitrosoPentamethylenetetramine)중에서 선택된 어느 하나를 사용한다.5 to 10 parts by weight of a blowing agent are used, and any one selected from 100 to 250 mesh size of azodicarbonamide and dinitrosopentamethylenetetramine is used.

산촉매제 10~20 중량부를 사용하며, 폴리인산암모니아(Ammonium Polyphosphate, APP)를 포함한다.10 to 20 parts by weight of an acid catalyst is used, and ammonium polyphosphate (APP) is included.

난연제 10~20 중량부를 사용하며, 삼산화안티몬(Antimony Trioxide) 100 중량부에 대하여 염화파라핀(Chlorinated Paraffin) 100~200 중량부를 사용한다.10 to 20 parts by weight of a flame retardant is used, and 100 to 200 parts by weight of Chlorinated Paraffin are used based on 100 parts by weight of Antimony Trioxide.

난연성 충진제 20~30 중량부를 사용하며, 150~ 200 메시 크기의 수산화알루미늄(Aluminium Hydroxide)을 사용한다.20 to 30 parts by weight of a flame-retardant filler is used, and aluminum hydroxide with a size of 150 to 200 mesh is used.

소포제 1~3 중량부가 사용되며, 소포제는 혼합된 각 조성물로 부터 생성되는 기포의 발생을 제거하는 역할을 하는 것이다. 1 중량부 미만일 경우 생성되는 기포를 제거하는데 어려움이 있고, 3중량부 초과할 경우에는 혼합된 조성물로부터 발생되는 기포는 완전히 제거할 수 있으나 사용량에 비해 그 효과는 미약하다.1 to 3 parts by weight of the antifoaming agent is used, and the antifoaming agent serves to remove the generation of air bubbles generated from each of the mixed compositions. If it is less than 1 part by weight, it is difficult to remove the generated air bubbles, and when it exceeds 3 parts by weight, the air bubbles generated from the mixed composition can be completely removed, but the effect is weak compared to the amount used.

분산제 1~3 중량부가 사용되며, 불포화 폴리카르복실산계열의 것을 사용한다.1 to 3 parts by weight of a dispersant is used, and an unsaturated polycarboxylic acid series is used.

상기 수지는 난연수지로써 불포화폴리에스테르수지 및 에폭시수지 중에서 어느 하나가 사용되는 것을 특징으로 하는 차수매트를 이용한 가축 매립방법이다.The resin is a livestock landfill method using a water-repellent mat, characterized in that any one of an unsaturated polyester resin and an epoxy resin is used as a flame retardant resin.

상기의 각 조성물의 함량, 수치에 따른 임계적 의미는 다음과 같으며, 한국건설생활환경시험연구원 또는 한국건설자재 시험연구원의 시험 결과를 참고하였다.The critical meanings according to the contents and values of each of the above compositions are as follows, and the test results of the Korea Construction Living Environment Testing Institute or the Korea Construction Materials Testing Institute were referenced.

일반적으로 상온에서의 점도가 50~ 1500cp로 조절한 난연수지 30~50 중량부에 있어서, 난연수지의 점도가 50cp미만이면 첨가되는 희석제의 양이 증가하여 준불연성 패널의 물성에 나쁜 영향을 주게되고, 1500cp 초과일 경우 작업성이 나빠져 강화재와 함침이 원하는 시간에 이루어지지 않게 된다.In general, in 30 to 50 parts by weight of a flame retardant resin whose viscosity is adjusted to 50 to 1500 cp at room temperature, if the viscosity of the flame retardant resin is less than 50 cp, the amount of added diluent increases, which adversely affects the properties of the semi-non-combustible panel. If it exceeds 1500cp, workability deteriorates and impregnation with reinforcement is not performed at the desired time.

난연수지가 30 중량부 미만이면 강화재에 함침되는 수지의 절대적인 양이 부족하여 완전한 함침이 어렵고, 50 중량부를 초과하면 수지의 양이 증가함에 따라 준불연성능이 저하되는 단점이 있다.If the flame-retardant resin is less than 30 parts by weight, the absolute amount of the resin impregnated into the reinforcing material is insufficient, so that complete impregnation is difficult, and if it exceeds 50 parts by weight, the quasi-non-combustible performance decreases as the amount of resin increases.

상기의 탄화제 3~10중량부에 있어서, 탄화제는 열원과 접촉하면 산촉매제와 반응하여 탄화물을 형성하고, 그 탄화물을 통해 열 차단막을 형성하는 역할을 한다. In 3 to 10 parts by weight of the carbonizing agent, the carbonizing agent reacts with the acid catalyst to form a carbide when in contact with the heat source, and serves to form a heat barrier film through the carbide.

상기 탄화제의 사용량이 3 중량부 미만이면 산촉매제와의 반응이 떨어져 탄화층의 형성이 어렵고, 10중량부를 초과하면 산촉매제와의 반응 당량비가 적정범위를 벗어나 내화성능 확보에 어려움이 초래된다.If the amount of the carbonizing agent is less than 3 parts by weight, the reaction with the acid catalyst decreases, making it difficult to form a carbonized layer, and if it exceeds 10 parts by weight, the reaction equivalent ratio with the acid catalyst is out of the appropriate range, and it is difficult to secure fire resistance.

또한 상기 탄화제의 크기가 3㎛ 미만일 경우에는 탄화제의 표면적 증가로 산촉매제와의 반응이 용이하나 그 효과에 비해 비경제적이고 10㎛를 초과할 경우에는 탄화제의 표면적 저하로 산촉매제와 반응이 원활하게 진행되지 않는다.In addition, when the size of the carbonization agent is less than 3㎛, the reaction with the acid catalyst is easy due to the increase in the surface area of the carbonization agent, but it is uneconomical compared to the effect, and when it exceeds 10㎛, the reaction with the acid catalyst due to the decrease in the surface area of the carbonization agent. It doesn't go smoothly.

또한 발포제 5~10 중량부에 있어서, 발포제는 정해진 분해온도에서 열 분해되어 불활성가스를 방출하여 패널(매트)의 탄화층을 발포시켜 단열성능을 지속적으로 유지하는 역할을 한다. 상기 발포제의 사용량이 5 중량부 미만이면 생성되는 가스량이 적어 발포 탄화층이 요구되는 정도로 이루어지지 않을 수 있고, 10 중량부를 초과하면 가스의 발생량 과다로 오히려 탄화층 형성이 어려워 요구하는 내화성능 유지에 어려움이 있다.In addition, in 5 to 10 parts by weight of the foaming agent, the foaming agent is thermally decomposed at a predetermined decomposition temperature to release an inert gas, thereby foaming the carbonized layer of the panel (mat) to continuously maintain the thermal insulation performance. If the amount of the foaming agent is less than 5 parts by weight, the amount of gas generated may not be achieved as required, and if it exceeds 10 parts by weight, the amount of gas generated is excessive, making it difficult to form a carbonized layer to maintain the required fire resistance. There are difficulties.

또한 산촉매제 10~20중량부에 있어서, 산촉매제인 폴리인산암모니아(Ammonium Polyphosphate, APP)를 가열하면 인산(phosphoric acid)이 형성되고 이는 물리적 차단막으로 사용되는 탄소화합물의 탈수소반응에 참여한다. In addition, in 10 to 20 parts by weight of the acid catalyst, when the acid catalyst, ammonium polyphosphate (APP) is heated, phosphoric acid is formed, which participates in the dehydrogenation reaction of the carbon compound used as a physical barrier.

산촉매제의 사용량이 10 중량부 미만일경우에는 탄화제, 발포제 등과의 반응이 미약하여 적정한 양의 탄화층이 생성되지 않을 우려가 있고 20 중량부를 초과할 경우에는 요구되는 탄화층보다 더 많이 발포됨으로 인해 발포층의 탈리현상으로 내화성능이 저하된다.If the amount of acid catalyst used is less than 10 parts by weight, the reaction with the carbonizing agent and the blowing agent is weak, so that an appropriate amount of carbonized layer may not be formed. If it exceeds 20 parts by weight, more than the required carbonized layer is foamed. The fire resistance performance decreases due to the detachment of the foam layer.

또한 난연제 10~20 중량부에 있어서, 난연제의 사용량이 10 중량부 미만일 경우 삼산화안티몬의 함량이 5중량부 미만으로 염화파라핀과 난연성의 상승작용을 발생시키기엔 삼산화안티몬이 부족한 함량이고, 20중량부 초과할 경우 염소가스가 다량 발생하여 난연성 향상의 효과보다 환경적인 유해성이 부각될 수 있다.In addition, in 10 to 20 parts by weight of the flame retardant, when the amount of the flame retardant is less than 10 parts by weight, the content of antimony trioxide is less than 5 parts by weight, and antimony trioxide is insufficient to generate a synergistic effect of flame retardancy with paraffin chloride, and 20 parts by weight. If it is exceeded, a large amount of chlorine gas may be generated, and environmental hazards may be emphasized rather than the effect of improving flame retardancy.

또한 난연성 충진제 20~30 중량부에 있어서, 수산화알루미늄은 매트에서 연소시 발연량이 매우 적기 때문에 환경 측면에서 양호한 난연제의 역할 뿐만 아니라 매트의 경도(hardness)와 압축강도 등의 물리적 특성을 향상시키는 충진제로서의 역할을 한다. 난연성 충진제의 함량이 20 중량부 미만일 경우 난연효과가 현저히 떨어지고, 30 중량부 초과할 경우 충진제의 증가로 인한 점도도 증가하여 작업성 떨어진다.In addition, in 20 to 30 parts by weight of the flame-retardant filler, aluminum hydroxide has a very small amount of smoke when burning in the mat, so it is not only a good flame retardant in terms of environment, but also as a filler that improves physical properties such as hardness and compressive strength of the mat. Plays a role. When the content of the flame-retardant filler is less than 20 parts by weight, the flame retardant effect decreases significantly, and when the content of the flame-retardant filler is more than 30 parts by weight, the viscosity increases due to the increase of the filler, resulting in poor workability.

또한 소포제 1~3 중량부에 있어서, 소포제는 혼합된 각 조성물로 부터 생성되는 기포의 발생을 제거하는 역할을 하는 것이다. 1 중량부 미만일 경우 생성되는 기포를 제거하는데 어려움이 있고, 3중량부 초과할 경우에는 혼합된 조성물로부터 발생되는 기포는 완전히 제거할 수 있으나 사용량에 비해 그 효과는 미약하다.In addition, in 1 to 3 parts by weight of the antifoaming agent, the antifoaming agent serves to remove the generation of air bubbles generated from each of the mixed compositions. If it is less than 1 part by weight, it is difficult to remove the generated air bubbles, and when it exceeds 3 parts by weight, the air bubbles generated from the mixed composition can be completely removed, but the effect is weak compared to the amount used.

또한 분산제 1~3 중량부가 포함되어 매트에 있어서, 분산제는 혼합되는 조성물의 습윤성을 향상시켜 각 조성물의 점성폭을 조절함으로써 각 조성물의 투입량을 증가시켜 매트성능을 향상시키는 역할을 한다.In addition, 1 to 3 parts by weight of a dispersant is included in the mat, and the dispersant improves the wettability of the composition to be mixed to adjust the viscosity width of each composition, thereby increasing the amount of each composition added to improve mat performance.

상기 분산제의 사용량이 1 중량부 미만일 경우 혼합되는 각 조성물이 완전히 분산되지 않을 우려가 있고, 3중량부 초과할 경우 혼합되는 각 조성물은 고르게 분산시킬 수 있으나 사용량에 비해 그 효과는 미미하다.If the amount of the dispersant is less than 1 part by weight, there is a concern that each composition to be mixed may not be completely dispersed, and if it exceeds 3 parts by weight, each composition to be mixed can be evenly dispersed, but its effect is insignificant compared to the amount used.

본 발명에서 사용되는 각 성분과 함량의 예는 다음과 같다.Examples of each component and content used in the present invention are as follows.

강화재로 사용되는 섬유 100 중량부에 대하여, 수지 30~50 중량부,Based on 100 parts by weight of fiber used as a reinforcing material, 30 to 50 parts by weight of resin,

펜타에리스리톨(Pentaerythritol)를 포함하는 탄화제 3~10중량부,3 to 10 parts by weight of a carbonizing agent containing pentaerythritol,

아조다이카본아마이드(Azodicarbonamide) 및 디니트로소펜타메틸렌테드라민Azodicarbonamide and dinitrosopentamethylenetedramine

(DinitrosoPentamethylenetetramine)중에서 선택된 어느 하나의 발포제 5~10 중량부,5-10 parts by weight of any one blowing agent selected from (DinitrosoPentamethylenetetramine),

폴리인산암모니아(Ammonium Polyphosphate, APP)를 포함하는 산촉매제 10~20 중량부,10 to 20 parts by weight of an acid catalyst containing ammonium polyphosphate (APP),

삼산화안티몬(Antimony Trioxide) 및 염화파라핀(Chlorinated Paraffin)를 포함하는 난연제 10~20 중량부,10 to 20 parts by weight of a flame retardant including Antimony Trioxide and Chlorinated Paraffin,

수산화알루미늄(Aluminium Hydroxide)을 포함하는 난연성 충진제 20~30 중량부,20-30 parts by weight of a flame-retardant filler containing aluminum hydroxide,

소포제 1~3 중량부 및1 to 3 parts by weight of antifoam and

불포화 폴리카르복실산계열을 포함하는 분산제 1~3 중량부가 포함되고,1 to 3 parts by weight of a dispersant containing an unsaturated polycarboxylic acid series is included,

상기 수지는 난연수지로써 불포화폴리에스테르수지 및 에폭시수지 중에서 어느 하나가 사용된다.The resin is a flame retardant resin, and any one of an unsaturated polyester resin and an epoxy resin is used.

상기와 성분들과 그 함량에 의거 서로 믹싱하여, 성형틀에 의거 차수매트가제조하며, 성형방법은 기존의 방식을 이용한다.By mixing with each other based on the above ingredients and their content, the order mat is manufactured based on a molding mold, and the molding method uses an existing method.

이하 상기 본 발명의 차수매트를 이용한 가축 매립방법에 대해 설명한다.Hereinafter, a method for landfilling livestock using the shading mat of the present invention will be described.

도 2는 본 발명의 일 실시예에 따른 가축 매립용 생분해성 키트(120)의 설치상태를 나타내는 사시도이다.Figure 2 is a perspective view showing the installation state of the biodegradable kit 120 for landfill livestock according to an embodiment of the present invention.

도 2에 도시한 바와 같이, 여기서는 가축 매립시 키트 본체의 실제 사용상태를 보여준다. 사각의 박스형 본 발명의 차수매트(110)가 마련되고, 상기 차수매트(110)의 바닥에는 함께 조립되어 있는 다수의 키트 본체가 설치된다.As shown in Figure 2, here shows the actual state of use of the kit body during livestock landfill. A rectangular box-type water shielding mat 110 of the present invention is provided, and a plurality of kit bodies assembled together are installed on the bottom of the water shielding mat 110.

그리고, 이렇게 설치되는 키트 본체의 상부에 흙 등이 복토된 후, 그 위에 가축 사체가 놓여질 수 있게 된다.Then, after soil or the like is covered on the upper part of the kit body installed in this way, the carcasses of livestock can be placed thereon.

따라서, 가축 사체로부터 발생하는 침출물(수)는 박스형 차수매트(110)의 바닥에 설치되어 있는 키트 본체(13)내에 그대로 유입될 수 있게 된다.Accordingly, the leachate (water) generated from the carcasses of livestock can be directly introduced into the kit body 13 installed on the bottom of the box-type water mat 110.

여기서, 상기 박스형 차수매트(110)는 그 내부에 매립되는 가축 사체로부터의 침출수가 주변 토양 속으로 그대로 스며들지 못하도록 완벽하게 차수시켜주는 역할을 하게 된다.In this case, the box-type shading mat 110 plays a role of completely submerging the leachate from livestock carcasses buried therein so as not to penetrate into the surrounding soil.

특히, 상기 박스형 차수매트(110)와 후술하는 덮개(160)의 경우에도 PBS(Polybutylene Succinate), PBSA(Polybutylene Succinate-co-butylene Adipate), PLA(Poly lactic Acid) 등과 같은 생분해성 소재로 이루어질 수 있게 된다.In particular, in the case of the box-type water barrier mat 110 and the cover 160 to be described later, it may be made of biodegradable materials such as PBS (Polybutylene Succinate), PBSA (Polybutylene Succinate-co-butylene Adipate), PLA (Poly lactic acid), etc. There will be.

따라서, 이와 같이 구성되는 가축 매립용 생분해성 키트 및 차수매트를 이용하여 가축을 매립하는 방법에 대해 살펴보면 다음과 같다.Accordingly, a method of landfilling livestock using the biodegradable kit for landfilling of livestock and the shading mat configured as described above will be described as follows.

도 3 내지 9는 본 발명의 일 실시예에 따른 가축 매립용 생분해성 키트를 이용한 가축 매립방법을 나타내는 개략도이다.3 to 9 are schematic diagrams showing a livestock landfill method using a biodegradable kit for landfilling livestock according to an embodiment of the present invention.

각 도면에 도시한 바와 같이, 먼저 살처분 가축의 매립을 위한 매립홀(100)을 형성하는 단계를 수행한다.As shown in each figure, first, a step of forming a buried hole 100 for burial of livestock for killing is performed.

즉, 굴삭기 등을 사용하여 지면으로부터 일정한 깊이와 가로 및 세로의 너비를 갖는 대략 사각형, 마름모형등을 포함한 다영한 형태의 매립 구덩이를 만든다.In other words, using an excavator, etc., various types of buried pit, including approximately square and rhombus, having a certain depth and horizontal and vertical width from the ground are made.

다음, 이렇게 형성한 매립홀(100)의 내부에 차수 등을 위해 매립홀에 대응되는 사각의 통 모양으로 되어 있는 박스형 차수매트(110)를 설치한다.Next, a box-shaped order mat 110 having a rectangular cylindrical shape corresponding to the buried hole is installed in the interior of the buried hole 100 formed in this way.

이때의 박스형 차수매트(110)는 매립홀(100)의 규격에 맞게 미리 제작한 것을 사용할 수 있으며, 이렇게 설치되는 박스형 차수매트(110)는 매립홀(100)의 벽면 전체 면적 및 바닥을 커버하는 형태로 설치될 수 있게 된다.At this time, the box-type ordering mat 110 may be used that is manufactured in advance according to the standard of the buried hole 100, and the box-type ordering mat 110 installed in this way covers the entire area of the wall and the floor of the buried hole 100. It can be installed in a form.

다음, 박스형 차수매트(110)의 설치가 완료되면, 박스형 차수매트(110)의 내부 바닥쪽에 생분해성 소재로 이루어진 다수의 박스형 키트(120)를 설치하는 단계를 수행한다.Next, when the installation of the box-type watering mat 110 is completed, a step of installing a plurality of box-type kits 120 made of a biodegradable material is performed on the inner bottom of the box-type watering mat 110.

이때, 상기 박스형 키트(120)는 내부에 왕겨, 활성탄, 황토, 목분, 소석회 등과 같은 친환경 흡착제(14)가 채워져 있고, 상부는 타공망 형태의 상판(10)으로 마감되어 있는 형태로서, 여러 개가 조립되어 박스형 차수매트(110)의 전체 바닥면적에 걸쳐 꼭 맞게 설치될 수 있게 된다.At this time, the box-type kit 120 is filled with an eco-friendly adsorbent 14 such as rice husk, activated carbon, loess, wood flour, slaked lime, etc., and the upper part is a form in which the top plate 10 in the form of a perforated net is closed, and several are assembled. As a result, it can be installed snugly over the entire floor area of the box-type water-order mat 110.

물론, 이때의 박스형 키트(120)의 바닥판(미도시)에는 다수의 배출구(미도시)가 형성될 수 있다.Of course, a plurality of outlets (not shown) may be formed on the bottom plate (not shown) of the box-type kit 120 at this time.

다음, 상기 박스형 차수매트(110)의 내부 바닥에 설치되어 있는 박스형 키트(120)의 상부에 흙 또는 석회석을 도포하여 제1복토층(130)을 형성하는 단계를 수행한다.Next, a step of forming the first cover layer 130 is performed by applying soil or limestone to the upper part of the box-type kit 120 installed on the inner floor of the box-type water-blocking mat 110.

여기서, 상기 제1복토층(130)은 흙만으로 일정 두께로 쌓거나, 또는 석회석만으로 일정 두께로 쌓을 수 있으며, 흙 위에 석회석 또는 석회석 위에 흙 등 흙과 석회석을 2개의 층으로 쌓을 수도 있다.Here, the first cover layer 130 may be stacked with only soil to a certain thickness, or may be stacked with only limestone to a certain thickness, and soil and limestone such as soil or limestone may be stacked in two layers on the soil.

물론, 이때의 제1복토층(130)을 형성하는 단계없이 곧바로 박스형 키트(120)의 상부에 가축 사체를 매립할 수도 있다.Of course, it is also possible to embed livestock carcasses on top of the box-type kit 120 immediately without the step of forming the first cover layer 130 at this time.

다음, 상기 제1복토층(130)을 쌓은 후 그 상부에 살처분 가축을 매립하는 단계를 수행한다.Next, after the first cover layer 130 is stacked, the step of burying livestock for killing is performed.

다음, 가축 사체 매립 후 그 위에 흙 또는 석회석을 도포하여 제2복토층(140)을 형성하고, 이와 더불어 유공관(150)을 설치하는 단계를 수행한다.Next, after the livestock carcasses are buried, the second cover layer 140 is formed by applying soil or limestone thereon, and the step of installing the perforated pipe 150 is performed.

여기서, 상기 제2복토층(140)은 지면으로부터 봉분(封墳)의 형태로 쌓을 수 있으며, 상기 유공관(150)의 경우 가축 사체가 매립되어 있는 박스형 차수매트(110)의 내부와 통하면서 외부로 노출되는 일반적인 형태로 설치할 수 있다.Here, the second cover layer 140 may be stacked from the ground in the form of a bongbun, and in the case of the merit pipe 150, while communicating with the inside of the box-type water mat 110 in which the carcasses are buried, It can be installed in an exposed general form.

그리고, 살처분한 가축을 매립한 후에 제2복토층(140)을 형성하게 되는데, 바람직하기로는 제2복토층(140)을 형성하기 전에 박스형 차수매트(110)의 상부를 생분해성 소재로 이루어진 덮개(160)로 마감할 수도 있으며, 이 경우에는 박스형 차수매트(110)에 씌워진 덮개(160)의 상부로 흙 또는 석회석을 도포하여 봉분(封墳) 형태의 제2복토층(140)을 형성할 수 있다.And, after burying the discarded livestock, the second cover layer 140 is formed, preferably, before forming the second cover layer 140, the upper portion of the box-shaped subsurface mat 110 is covered with a biodegradable material ( 160), and in this case, soil or limestone may be applied to the upper portion of the cover 160 covered on the box-type shading mat 110 to form a second covering layer 140 in the form of a bonbun (封墳). .

따라서, 바닥에는 생분해성 소재의 박스형 키트가 깔려 있고, 또 둘레 및 그 바닥에는 박스형 차수매트로 차단되어 있는 형태의 매립영역에 살처분 가축을 매립함으로써, 가축 사체에서 발생되는 침출수는 복토층을 거쳐 박스형 키트의 내부로 유입되고, 이렇게 유입된 침출수는 내부의 친환경 흡착제에 의해 흡착되어 키트 내에서 일정기간 체류하게 된다.Therefore, a box-type kit made of biodegradable material is laid on the floor, and by burying livestock for disposal in a landfill area blocked by a box-type water mat on the circumference and on the floor, the leachate generated from the animal carcasses passes through the cover layer and is box-shaped. The leachate that is introduced into the interior of the kit and thus introduced is adsorbed by the environmentally friendly adsorbent inside and stays in the kit for a certain period of time.

이와 같이, 본 발명은 도 10과 같이 살처분 가축의 매립 방법으로써, 본 발명에 의한차수매트를 사용하여 침출방지와 함께 탄탄하고 깨지지 않은 매립형태를 유지할 수 있다.As described above, the present invention is a method of burying livestock for disposal as shown in FIG. 10, and a solid and unbroken buried form can be maintained while preventing leaching by using the repellent mat according to the present invention.

상기한 바와 같이 본 발명은 가축의 살처분을 매립방식으로 하는 경우, 매립홀에 위치하는 차수매트와 그 차수매트를 이용한 가축 매립 방법에 관한 것이다.As described above, the present invention relates to an ordering mat located in a burial hole and a livestock landfill method using the ordering mat when the killing of livestock is used as a burial method.

이상의 설명은 본 발명의 기술 사상을 예시적으로 설명한 것에 불과한 것으로서, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 수정 및 변형이 가능할 것이다. 따라서, 본 발명에 개시된 실시 예들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시예에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다. The above description is merely illustrative of the technical idea of the present invention, and those of ordinary skill in the art to which the present invention pertains will be able to make various modifications and variations without departing from the essential characteristics of the present invention. Accordingly, the embodiments disclosed in the present invention are not intended to limit the technical idea of the present invention, but to explain the technical idea, and the scope of the technical idea of the present invention is not limited by these embodiments. The scope of protection of the present invention should be interpreted by the following claims, and all technical ideas within the scope equivalent thereto should be interpreted as being included in the scope of the present invention.

100 : 매립홀 ,110 : 박스형 차수시트
120 : 박스형 키트 ,130 : 제1복토층
140 : 제2복토층 ,150 : 유공관, 160 : 덮개100: buried hole, 110: box type order sheet
120: box-type kit, 130: first cover layer
140: second cover layer, 150: merit pipe, 160: cover

Claims (3)

지면으로부터 일정 깊이와 너비를 갖는 매립홀(100)을 형성하는 단계;
상기 매립홀(100)의 내부에 매립홀 벽면 전체 면적을 커버하는 차수매트
(110)를 설치하는 단계;
상기 차수매트(110)의 내부에 생분해성 소재로 이루어지고 내부에는 친환경 흡착제가 채워져 있는 다수의 박스형 키트(120)를 설치하는 단계;
상기 차수매트(110)의 내부 바닥에 설치되어 있는 박스형 키트(120)의 상부에 흙 또는 석회석을 도포하여 제1복 토층(130)을 형성하는 단계;
상기 제1복토층(130)의 상부에 살처분 가축을 매립하는 단계; 및
상기 매립되어 있는 살처분 가축의 상부에 흙 또는 석회석을 도포하여 제2복토층(140)을 형성함과 더불어 유공 관(150)을 설치하는 단계; 를 포함하고,
상기 차수매트는,
부직포를 기재로한 매트에,
차수를 위한 폴리에칠렌(PE), 폴리프로필렌(PP) 및 폴리에스터(PET)중에서 어느 하나를 사용하며 그 중량은 100 중량부;
상기 차수매트의 강화재로 사용되는 섬유 100 중량부;
상기 섬유 100 중량부에 대하여,
수지 30~50 중량부,
탄화제 3~10중량부,
발포제 5~10 중량부,
산촉매제 10~20 중량부,
난연제 10~20 중량부,
난연성 충진제 20~30 중량부,
소포제 1~3 중량부 및
분산제 1~3 중량부가 포함되며,
상기 수지는 난연수지로써 불포화폴리에스테르수지 및 에폭시수지 중에서 어느 하나가 사용되는 것을 특징으로 하는 차수매트를 이용한 가축 매립방법.Forming a buried hole 100 having a predetermined depth and width from the ground;
An order mat that covers the entire area of the wall of the buried hole inside the buried hole 100
Installing 110;
Installing a plurality of box-type kits 120 made of a biodegradable material inside the water shielding mat 110 and filled with an eco-friendly adsorbent therein;
Forming a first cover layer 130 by applying soil or limestone to an upper portion of the box-type kit 120 installed on the inner floor of the water-shielding mat 110;
Burying livestock for killing on the top of the first cover layer 130; And
Applying soil or limestone to the top of the buried livestock to form a second covering layer 140 and installing a perforated pipe 150; Including,
The order mat,
On a non-woven mat based,
Polyethylene (PE), polypropylene (PP), and polyester (PET) for the order are used, and the weight thereof is 100 parts by weight;
100 parts by weight of fibers used as reinforcing materials of the water-resistant mat;
Based on 100 parts by weight of the fiber,
30-50 parts by weight of resin,
3 to 10 parts by weight of carbonizing agent,
5 to 10 parts by weight of a foaming agent,
10 to 20 parts by weight of an acid catalyst,
10 to 20 parts by weight of flame retardant,
20 to 30 parts by weight of flame retardant filler,
1 to 3 parts by weight of antifoam and
1 to 3 parts by weight of a dispersant are included,
The resin is a livestock landfill method using a water-resistant mat, characterized in that any one of an unsaturated polyester resin and an epoxy resin is used as a flame retardant resin. 부직포를 기재로한 매트에,
차수를 위한 폴리에칠렌(PE), 폴리프로필렌(PP) 및 폴리에스터(PET)중에서 어느 하나를 사용하며 그 중량은 100 중량부;
상기 차수매트의 강화재로 사용되는 섬유 100 중량부;
상기 섬유 100 중량부에 대하여,
수지 30~50 중량부,
탄화제 3~10중량부,
발포제 5~10 중량부,
산촉매제 10~20 중량부,
난연제 10~20 중량부,
난연성 충진제 20~30 중량부,
소포제 1~3 중량부 및
분산제 1~3 중량부가 포함되며,
상기 수지는 난연수지로써 불포화폴리에스테르수지 및 에폭시수지 중에서 어느 하나가 사용되는 것을 특징으로 하는 차수매트.On a non-woven mat based,
Polyethylene (PE), polypropylene (PP), and polyester (PET) for the order are used, and the weight thereof is 100 parts by weight;
100 parts by weight of fibers used as reinforcing materials of the water-resistant mat;
Based on 100 parts by weight of the fiber,
30-50 parts by weight of resin,
3 to 10 parts by weight of carbonizing agent,
5 to 10 parts by weight of a foaming agent,
10 to 20 parts by weight of an acid catalyst,
10 to 20 parts by weight of flame retardant,
20 to 30 parts by weight of flame retardant filler,
1 to 3 parts by weight of antifoam and
1 to 3 parts by weight of a dispersant are included,
The resin is a water-resistant mat, characterized in that any one of an unsaturated polyester resin and an epoxy resin is used as a flame retardant resin. 제 2항에 있어서,
강화재로 사용되는 섬유 100 중량부에 대하여,
수지 30~50 중량부,
펜타에리스리톨(Pentaerythritol)를 포함하는 탄화제 3~10중량부,
아조다이카본아마이드(Azodicarbonamide) 및 디니트로소펜타메틸렌테드라민
(DinitrosoPentamethylenetetramine)중에서 선택된 어느 하나의 발포제 5~10 중량부,
폴리인산암모니아(Ammonium Polyphosphate, APP)를 포함하는 산촉매제 10~20 중량부,
삼산화안티몬(Antimony Trioxide) 및 염화파라핀(Chlorinated Paraffin)를 포함하는 난연제 10~20 중량부,
수산화알루미늄(Aluminium Hydroxide)을 포함하는 난연성 충진제 20~30 중량부,
소포제 1~3 중량부 및
불포화 폴리카르복실산계열을 포함하는 분산제 1~3 중량부가 포함되고,
상기 수지는 난연수지로써 불포화폴리에스테르수지 및 에폭시수지 중에서 어느 하나가 사용되는 것을 특징으로 하는 차수매트.The method of claim 2,
Based on 100 parts by weight of fiber used as a reinforcing material,
30-50 parts by weight of resin,
3 to 10 parts by weight of a carbonizing agent containing pentaerythritol,
Azodicarbonamide and dinitrosopentamethylenetedramine
5-10 parts by weight of any one blowing agent selected from (DinitrosoPentamethylenetetramine),
10 to 20 parts by weight of an acid catalyst containing ammonium polyphosphate (APP),
10 to 20 parts by weight of a flame retardant including Antimony Trioxide and Chlorinated Paraffin,
20-30 parts by weight of a flame-retardant filler containing aluminum hydroxide,
1 to 3 parts by weight of antifoam and
1 to 3 parts by weight of a dispersant containing an unsaturated polycarboxylic acid series is included,
The resin is a water-resistant mat, characterized in that any one of an unsaturated polyester resin and an epoxy resin is used as a flame retardant resin.
KR1020190014781A 2019-02-08 2019-02-08 Cut off mat and method for reclaiming livestock using cufoff KR20200097835A (en)