KR20200073589A - The curing process method of a translucent colorant self-leveling mortar and translucent colorant composition - Google Patents
The curing process method of a translucent colorant self-leveling mortar and translucent colorant composition Download PDFInfo
- Publication number
- KR20200073589A KR20200073589A KR1020180161917A KR20180161917A KR20200073589A KR 20200073589 A KR20200073589 A KR 20200073589A KR 1020180161917 A KR1020180161917 A KR 1020180161917A KR 20180161917 A KR20180161917 A KR 20180161917A KR 20200073589 A KR20200073589 A KR 20200073589A
- Authority
- KR
- South Korea
- Prior art keywords
- horizontal mortar
- weight
- parts
- translucent
- colorant
- Prior art date
Abstract
Description
본 발명은 수평몰탈 표면을 반투명 착색함으로써 수평몰탈 표면의 자연스러운 결과 무늬를 살리면서 다양한 색상을 표현할 수 있을 뿐만 아니라, 다양한 로고, 무늬 등의 디자인을 표현할 수 있는 수평몰탈 표면의 반투명 착색 방법 및 그 시공방법에 관한 것이다.According to the present invention, the translucent coloring method of the horizontal mortar surface and its construction can not only express various colors while utilizing the natural result pattern of the horizontal mortar surface by translucent coloring the horizontal mortar surface, but also can express various logos, patterns, and the like. It's about how.
수평몰탈은 수평몰탈 소재의 유동적인 특성을 이용하여 바닥의 수평이 잘 맞지 않는 곳을 셀프 레벨링하고, 빈티지한 노출 콘크리트 느낌을 내는 곳에 활용되는 소재이다.Horizontal mortar is a material used for self-leveling where the floor does not fit well and creating a vintage exposed concrete feeling by using the fluid properties of the horizontal mortar material.
근래에 들어 바닥에 보일러 난방을 하지 않는 미용실, 카페, 식당, 미술관 등의 상업적인 시설 공간에 널리 사용되고 있는 추세이다.Recently, it has been widely used in commercial facility spaces such as beauty salons, cafes, restaurants, and art galleries that do not heat the boiler on the floor.
종래의 수평몰탈 시공방법은 도 1에 도시한 바와 같이 바닥 정리, 하도 시공, 수평몰탈 시공, 양생, 하도 시공, 상도 시공 순서대로 이루어진다.The conventional horizontal mortar construction method is as shown in FIG. 1, in the order of floor tiling, primer construction, horizontal mortar construction, curing, primer construction, and top construction.
수평몰탈을 시공하기 위해서는 먼저, 수평몰탈을 시공할 바닥의 먼지 등 이물질을 깨끗하게 제거하는 바닥정리를 하고, 정리된 바닥에 프라이머를 도포하는 하도 시공을 실시한다.To install the horizontal mortar, first, clean up the floor to remove foreign substances such as dust on the floor where the horizontal mortar is to be installed, and then apply the primer to the cleaned floor.
그리고 수평몰탈을 바닥에 도포하면 수평몰탈이 유동하며 바닥 면을 평평하게 셀프 레벨링되고 이 상태로 양생이 된다.And when the horizontal mortar is applied to the floor, the horizontal mortar flows, and the floor surface is self-leveled flat and cured in this state.
수평몰탈이 양생되면 양생된 수평몰탈을 보호하고, 표면 광택을 내기 위해 하도 시공과 상도 시공을 차례로 실시한다.When the horizontal mortar is cured, to protect the cured horizontal mortar, and to apply a surface luster, the base construction and the top construction are sequentially performed.
이러한 수평몰탈은 수평몰탈 자체의 색상만을 내므로 사용자가 원하는 색상을 내기 위해서는 수평몰탈에 염료를 혼합하여 시공한다.Since this horizontal mortar produces only the color of the horizontal mortar itself, it is constructed by mixing dye in the horizontal mortar in order to produce the color desired by the user.
그런데, 수평몰탈은 자체 색상이 너무 어둡기때문에 밝은 색상의 염료를 혼합하더라도 색상이 탁하고 어둡게 표현되는 문제점이 있다.However, the horizontal mortar has a problem in that the color is cloudy and dark even if a dye of a light color is mixed because its color is too dark.
이러한 문제점 때문에 백색 수평몰탈을 사용하여 사용자가 원하는 색상을 표현하기도 하는데, 백색몰탈은 가격이 비싸서 경제성이 떨어지는 문제점이 있다.Due to this problem, a white horizontal mortar is used to express a color desired by a user, but the white mortar has a problem of low economical cost.
그리고 수평몰탈에 염료를 혼합하여 시공하면 바닥이 한 가지 색상만으로 표현되므로 단조롭고, 바닥에 로고, 문구, 캐릭터 등의 다양한 디자인을 표현할 수 있지만 두께 차이에 의한 수평몰탈 표면의 고유한 무늬가 본 바닥 위에 로고(디자인)와 같은 다른 색상으로 경계가 표현될 경우 연결되어야하는 수평몰탈 표면 고유의 자연스러운 무늬가 단절된다는 문제점이 있다.In addition, when the dye is mixed with horizontal mortar, the floor is expressed in only one color, so it is monotonous, and various designs such as logos, stationery, and characters can be expressed on the floor, but the unique pattern on the surface of the horizontal mortar due to thickness difference is seen on the floor. When a border is expressed in a different color such as a logo (design), there is a problem that a natural pattern unique to the horizontal mortar surface to be connected is cut off.
종래의 수평몰탈을 이용하여 바닥을 여러 색상으로 표현할 때는 수평몰탈을 시공하기 전에 바닥에 금속재질의 분리대를 설치하여 수평몰탈의 유동 경계를 형성하고, 수평몰탈을 분리대 일측에 시공한 후 다른 색상의 염료가 혼합된 수평몰탈을 분리대 타측에 시공 양생함으로써, 각각 다른 염료가 혼합된 수평몰탈이 섞이지 않도록 양생하여 바닥에 다른 색상을 표현하고 있다.When the floor is expressed in multiple colors using a conventional horizontal mortar, a metal separator is installed on the floor before construction of the horizontal mortar to form a flow boundary of the horizontal mortar, and the horizontal mortar is constructed on one side of the separator and then of different colors. By constructing and curing the horizontal mortar mixed with the dye on the other side of the separator, the horizontal mortar mixed with different dyes is cured so as not to be mixed to express different colors on the floor.
그런데, 상기와 같이 분리대를 설치하여 수평몰탈을 분리함으로써 다른 색상을 표현하는 방법은 수평몰탈 특유의 표면무늬가 단절되어 공간이 협소하게 느껴지고, 통일성과 자연미가 사라지는 문제점이 있다.However, the method of expressing different colors by separating the horizontal mortar by installing a separator as described above has a problem in that the surface pattern peculiar to the horizontal mortar is cut off, so that the space is felt narrowly, and uniformity and natural beauty disappear.
본 발명은 상기와 같은 문제점을 해결하기 위하여 안출한 것으로서 수평몰탈을 다양한 색상으로 표현하면서도 수평몰탈 표면의 고유한 무늬를 살릴 수 있고, 분리대를 설치하지 않아도 여러 색상의 수평몰탈을 표현할 수 있으며 로고, 문구, 캐릭터, 상호 등 다양한 디자인을 표현할 수 있는 수평몰탈 표면의 반투명 착색 방법을 제공하는 것이 본 발명의 목적이다.The present invention has been devised to solve the above problems, while expressing the horizontal mortar in various colors, while utilizing the unique pattern on the surface of the horizontal mortar, and without installing a separator, it is possible to express multiple colors of horizontal mortar and logo, It is an object of the present invention to provide a translucent coloring method of a horizontal mortar surface capable of expressing various designs such as stationery, characters, and trade names.
상기의 목적을 달성하기 위하여 본 발명에 의한 수평몰탈 표면의 반투명 착색방법은 시공할 바닥을 정리하는 바닥정리 단계(S100); 정리된 바닥에 프라이머를 도포하는 하도 시공단계(S200); 하도 시공단계(S200)를 통해 형성된 도막에 수평몰탈을 부어 레벨링하는 수평몰탈 시공 단계(S300); 수평몰탈을 양생하는 양생단계(S400); 스틸렌모노머(Styrene Monomer, C6H5CH=CH2) 20~24 중량부에 대해, 2-에틸헥실아크릴레이트모노머(2-ethylhexyl acrylate monomer) 15~20 중량부와, 부틸아크릴레이트(Butyl acrylate monomer) 3~4 중량부와, 유화제(계면활성제) 0.3~0.8 중량부와, 물 50~60중량부 및 염료가 혼합된 반투명 착색제를 도포하는 반투명 착색제 도포단계(S500); 및 반투명 착색제가 도포되어 형성된 도막에 상도에 수용성 코팅제 또는 에폭시 소재 도막을 형성하는 상도 시공단계(S600);를 포함하여 구성된다.In order to achieve the above object, the translucent coloring method of the horizontal mortar surface according to the present invention includes a floor rearranging step (S100) of arranging a floor to be constructed; Primer construction step of applying a primer to the cleaned floor (S200); A horizontal mortar construction step (S300) in which a horizontal mortar is poured into the coating film formed through the primer construction step (S200) to level it; Curing step for curing the horizontal mortar (S400); Styrene Monomer (C 6 H 5 CH=CH 2 ) 15-20 parts by weight of 2-ethylhexyl acrylate monomer and 20% by weight of 20-24 parts by weight of 2-ethylhexyl acrylate monomer, and Butyl acrylate monomer) 3-4 parts by weight, an emulsifier (surfactant) 0.3-0.8 parts by weight, 50-60 parts by weight of water and a semi-transparent colorant coating step of applying a translucent colorant mixed with a dye (S500); And a top coat construction step (S600) of forming a water-soluble coating agent or an epoxy material coating film on the top coat on the coating film formed by applying the translucent colorant.
이때, 상기 반투명 착색제는 염료 혼합 전 80~90℃의 온도 환경에서 반응하도록 구성된 것을 특징으로 한다.At this time, the translucent colorant is characterized in that it is configured to react in a temperature environment of 80 ~ 90 ℃ before mixing the dye.
또한, 상기 수평몰탈 양생단계(S400)를 실시한 후에 테이프로 수평몰탈을 구획하고, 테이프를 경계로 양측에 서로 다른 색상의 염료가 혼합된 반투명 착색제가 도포하도록 구성된 것을 특징으로 한다.In addition, after performing the horizontal mortar curing step (S400), the horizontal mortar is divided into tapes, and a translucent colorant in which dyes of different colors are mixed is applied to both sides of the tape.
그리고 본 발명에 의한 수평몰탈 표면의 반투명 착색제는 스틸렌모노머(Styrene Monomer, C6H5CH=CH2) 20~24 중량부에 대해, 2-에틸헥실아크릴레이트모노머(2-ethylhexyl acrylate monomer) 15~20 중량부와, 부틸아크릴레이트(Butyl acrylate monomer) 3~4 중량부와, 유화제(계면활성제) 0.3~0.8 중량부와, 물 50~60중량부 및 소정 양의 염료가 혼합되어 수평몰탈에 도포되도록 구성한다.And the translucent colorant on the surface of the horizontal mortar according to the present invention is 20-24 parts by weight of Styrene Monomer (C 6 H 5 CH=CH 2 ), 2-ethylhexyl acrylate monomer 15 ~20 parts by weight, 3 to 4 parts by weight of butyl acrylate (Butyl acrylate monomer), 0.3 to 0.8 parts by weight of emulsifier (surfactant), 50 to 60 parts by weight of water and a predetermined amount of dye are mixed to form a horizontal mortar. It is configured to be applied.
상기와 같이 구성된 본 발명의 수평몰탈 표면의 반투명 착색방법은 수평몰탈 본연의 무늬를 살리면서 다양한 색상을 표현할 수 있고, 분리대를 설치하지 않고서도 여러 색상을 한꺼번에 표현할 수 있다.The translucent coloring method of the horizontal mortar surface of the present invention configured as described above can express various colors while making use of the natural pattern of the horizontal mortar, and can express multiple colors at once without installing a separator.
또한, 상호, 로고, 문구, 캐릭터 등 다양한 디자인을 표현할 수 있다.Also, various designs such as trade names, logos, stationery, and characters can be expressed.
도 1은 종래의 수평몰탈 시공방법을 공정별로 도시한 순서도.
도 2는 본 발명의 일 실시예에 의한 수평몰탈 표면의 반투명 착색 방법을 공정별로 도시한 순서도.
도 3은 본 발명의 다른 실시예에 의한 수평몰탈 표면의 반투명 착색 방법을 공정별로 도시한 순서도.1 is a flow chart showing a conventional horizontal mortar construction method for each process.
Figure 2 is a flow chart showing the translucent coloring method of the horizontal mortar surface according to an embodiment of the present invention by process.
Figure 3 is a flow chart showing the translucent coloring method of the horizontal mortar surface according to another embodiment of the present invention by process.
이하에서는 본 발명의 바람직한 실시예 및 첨부하는 도면을 참조하여 본 발명을 상세하게 설명하되, 도면의 동일한 참조부호는 동일한 구성요소를 지칭함을 전제하여 설명하기로 한다.Hereinafter, the present invention will be described in detail with reference to preferred embodiments of the present invention and the accompanying drawings, and the same reference numerals in the drawings will be described on the assumption that they refer to the same components.
발명의 상세한 설명 또는 특허청구범위에서 어느 하나의 구성요소가 다른 구성요소를 "포함"한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 당해 구성요소만으로 이루어지는 것으로 한정되어 해석되지 아니하며, 다른 구성요소들을 더 포함할 수 있는 것으로 이해되어야 한다.When one component in the detailed description of the invention or claims "includes" another component, it is not interpreted as being limited to only the component, unless specifically stated otherwise. It should be understood that it may further include.
본 발명에 의한 수평몰탈 시공방법은 도 2에 도시한 바와 같이 바닥정리(S100), 하도 시공(S200), 수평몰탈 시공(S300), 양생(S400), 반투명 착색제 도포(S500) 및 상도 시공(S600)으로 구성된다.The horizontal mortar construction method according to the present invention, as shown in FIG. 2, floor cleaning (S100), primer construction (S200), horizontal mortar construction (S300), curing (S400), translucent colorant coating (S500) and top coat construction ( S600).
먼저 수평몰탈을 시공할 콘크리트 하지의 구배를 조정하고, 바닥에 크랙이 있는 경우에는 시간이 지나 크랙이 점점 벌어지며 수평몰탈이 손상이 가므로 이를 방지하기 위해 크랙을 메꿈 작업하며, 바닥과 접착성을 향상시키기 위해 바닥의 이물질과 먼지등을 깨끗이 제거하는 바닥정리(S100) 단계를 실시한다.First, adjust the gradient of the concrete base to be installed on the horizontal mortar, and if there is a crack on the floor, the crack gradually spreads over time and the horizontal mortar is damaged, so the crack is filled to prevent this, and the adhesiveness with the floor In order to improve the floor cleaning (S100) step to cleanly remove foreign substances and dust on the floor.
바닥정리(S100) 단계를 실시한 후에는 바닥에 프라이머를 1~2회 도포하고 충분히 건조시키는 하도 시공(S200) 단계를 실시한다.After performing the floor cleaning (S100) step, a primer application (S200) step of applying the primer 1 to 2 times on the floor and drying it sufficiently is performed.
상기 하도 시공(S200) 단계에서 바닥에 프라이머를 도포함으로써, 이후에 도포되는 수평몰탈이 바닥면에 견고하게 부착되도록 하고, 수평몰탈의 기포가 발생하는 것을 방지하는 역할을 한다.By applying a primer on the floor in the step of applying the primer (S200), the horizontal mortar applied thereafter is firmly attached to the floor surface, and serves to prevent air bubbles from being generated.
하도가 시공된 후에는 수평몰탈을 시공하는 수평몰탈 시공(S300) 단계를 실시한다.After the primer is constructed, a horizontal mortar construction (S300) step of constructing a horizontal mortar is performed.
수평몰탈은 물과 종래의 수평몰탈 제품을 규정된 혼합비율로 믹서기에 투입하여 균일하게 혼합한다. 일반적으로 수평몰탈 제품의 중량대비 20~25% 중량의 물을 혼합하여 혼합한다.The horizontal mortar is mixed uniformly by adding water and a conventional horizontal mortar product to a blender at a prescribed mixing ratio. In general, water is mixed by mixing 20 to 25% by weight of the weight of the horizontal mortar product.
균일하게 혼합된 수평몰탈을 하도 시공된 바닥에 골고루 타설한다. Evenly mixed horizontal mortar is placed evenly on the floor under construction.
수평몰탈을 타설한 후에는 양고대로 손질하여 수평몰탈이 빠르게 퍼지도록 작업하는 것이 바람직하다. 수평몰탈은 점성이 낮아서 스스로 흘러 퍼지면서 바닥면이 평탄하게 도포된다.After pouring the horizontal mortar, it is desirable to clean the horizontal mortar quickly by trimming it with a stand. The horizontal mortar is low in viscosity and spreads on its own, so the bottom surface is applied flatly.
수평몰탈 시공(S300) 단계 후에는 수평몰탈을 양생시키는 양생단계(S400)를 실시한다. 수평몰탈 타설 후 양생을 하는 도중 직사광선, 강풍 등의 기후 변화에 영향이 없도록 환경을 유지하고, 저온시에는 보온 조치로 동결을 방지하며, 직사광선이 있는 현장은 타설 후 초결상태에서 양생포를 덮어 직사광선을 피해주고 양생포 위에 물을 뿌려준다.After the horizontal mortar construction (S300), a curing step (S400) for curing the horizontal mortar is performed. Keep the environment free from direct sunlight, strong wind and other climate changes during curing after pouring the horizontal mortar, and prevent freezing by keeping warm at low temperatures, and in the case of direct sunlight, cover the curing cloth in the initial state after pouring and cover the direct sunlight And sprinkle water over the curing cloth.
수평몰탈이 경화된 후에는 수평몰탈 표면에 반투명 착색제를 도포하는 반투명 착색제 도포(S500) 단계를 실시한다.After the horizontal mortar is cured, a step of applying a translucent colorant (S500) to apply a translucent colorant to the horizontal mortar surface is performed.
반투명 착색제는 스틸렌모노머(Styrene Monomer, C6H5CH=CH2) 20~24 중량부와, 2-에틸헥실아크릴레이트모노머(2-ethylhexyl acrylate monomer) 15~20 중량부와, 부틸아크릴레이트(Butyl acrylate monomer) 3~4 중량부와, 유화제(계면활성제) 0.3~0.8 중량부와, 물 50~60중량부를 혼합, 유화시켜서 80~90℃의 온도에서 반응시키고, 사용자가 원하는 색상의 염료가 혼합되어 구성된 것이다.The translucent colorant is 20 to 24 parts by weight of Styrene Monomer (C 6 H 5 CH=CH 2 ), 15 to 20 parts by weight of 2-ethylhexyl acrylate monomer, and butyl acrylate ( Butyl acrylate monomer) 3~4 parts by weight, emulsifier (surfactant) 0.3~0.8 parts by weight, and 50-60 parts by weight of water are mixed and emulsified to react at a temperature of 80~90℃, and the dye of the color desired by the user It is composed of mixed.
본 발명의 실시예에서 유화제로는 태동화학의 SLS 제품과 LG화학의 Np40 제품을 혼합하여 사용한다.In the embodiment of the present invention, as an emulsifier, SLS products of Taedong Chemical and Np40 products of LG Chemical are mixed and used.
스틸렌모노머(Styrene Monomer)는 가교제(열가소성 물질의 분자체와 화학적으로 반응하여 분자체를 상호연결하는 물질)역할을 하는 것이다.Styrene Monomer (Styrene Monomer) is a crosslinking agent (a substance that chemically reacts with a molecular sieve of a thermoplastic material to interconnect the molecular sieve).
스틸렌모노머(Styrene Monomer)는 20~24 중량부가 혼합되는데, 스틸렌모노머(Styrene Monomer)가 20 중량부 미만으로 혼합되면 겨울철 제조시 물과의 혼합이 원활하게 이루어지지 않아서 경화지연이 발생하고, 스틸렌모노머(Styrene Monomer)가 24 중량부를 초과하여 혼합되면 경화가 너무 급격하게 이루어져 시공성이 현저하게 저하되므로 스틸렌모노머(Styrene Monomer)는 20~24 중량부를 혼합하는 것이 바람직하다.Styrene Monomer (Styrene Monomer) is mixed with 20 to 24 parts by weight.If Styrene Monomer is mixed with less than 20 parts by weight, curing delay occurs due to the lack of smooth mixing with water during winter production. When (Styrene Monomer) is mixed in excess of 24 parts by weight, curing is so rapid that workability is remarkably lowered, so it is preferable to mix 20 to 24 parts by weight of Styrene Monomer.
2-에틸헥실아크릴레이트모노머(2-ethylhexyl acrylate monomer)는 코팅제, 잉크첨가 코팅도료, 투명성, UV안정성 및 접착성을 목적으로 모노머끼리 반응할 때 점도를 유지하며 표면의 매끄러움을 유지하는 목적으로 혼합된다. 2-ethylhexyl acrylate monomer is mixed for the purpose of maintaining viscosity and reacting with monomers when reacting with monomers for the purpose of coating, ink-added coating, transparency, UV stability, and adhesion. do.
상기 2-에틸헥실아크릴레이트모노머는 20~24 중량부가 혼합되는데, 2-에틸헥실아크릴레이트모노머가 20 중량부 미만으로 혼합되면 투명성, UV안정성 및 접착성이 저하되어 코팅막이 분리되거나 자외선에 의한 부식이 발생하고, 2-에틸헥실아크릴레이트모노머가 24 중량부를 초과하여 혼합되면 반투명 착색제가 탁해지고 점도가 높아져 표면이 매끄럽지 못하게 되므로 2-에틸헥실아크릴레이트모노머는 20~24 중량부가 혼합되는 것이 바람직하다.The 2-ethylhexyl acrylate monomer is mixed in an amount of 20 to 24 parts by weight. When the 2-ethylhexyl acrylate monomer is mixed in an amount of less than 20 parts by weight, transparency, UV stability and adhesiveness are lowered, resulting in separation of the coating film or corrosion by ultraviolet rays. When this occurs and the 2-ethylhexyl acrylate monomer is mixed in excess of 24 parts by weight, the translucent colorant becomes turbid and the viscosity becomes high, so that the surface is not smooth, so the 2-ethylhexyl acrylate monomer is preferably mixed in an amount of 20 to 24 parts by weight. .
부틸아크릴레이트(Butyl acrylate monomer)는 코팅제인 반투명 착색제의 접착성을 높이고 도막에 탄력을 부여하기 위해 혼합되는 것으로서 3~4 중량부가 혼합된다.Butyl acrylate monomer (Butyl acrylate monomer) is a coating agent to increase the adhesion of the translucent colorant and to give elasticity to the coating film is mixed with 3-4 parts by weight.
유화제(계면활성제)는 상기 스틸렌모노머(Styrene Monomer), 2-에틸헥실아크릴레이트모노머(2-ethylhexyl acrylate monomer) 및 부틸아크릴레이트(Butyl acrylate monomer)가 물에 골고루 섞이도록 하는 역할을 한다.The emulsifier (surfactant) serves to mix the Styrene Monomer, 2-ethylhexyl acrylate monomer and Butyl acrylate monomer evenly in water.
그리고 물이 50~60 중량부가 혼합되는데, 물이 50 중량부 미만으로 혼합되면 점도가 높아져서 반투명 착색제의 점도가 높아져 셀프 레벨링이 제대로 이루어지지 않고, 물이 60 중량부를 초과하여 혼합되면 경화에 많은 시간이 소요되므로 물은 50~60 중량부를 혼합하는 것이 바람직하다.And 50 to 60 parts by weight of water is mixed. When water is mixed to less than 50 parts by weight, the viscosity increases, and the viscosity of the translucent colorant increases, so that self-leveling does not occur properly. Since it is required, it is preferable to mix 50-60 parts by weight of water.
그리고 상기 유화제(계면활성제)는 상기 스틸렌모노머(Styrene Monomer), 2-에틸헥실아크릴레이트모노머(2-ethylhexyl acrylate monomer) 및 부틸아크릴레이트(Butyl acrylate monomer)는 석유화학 고형분 100%의 유성이므로 물과 혼합, 희석하여 80℃ 이상의 온도에서 분자반응시켜 제조된다.And the emulsifier (surfactant) is styrene monomer, 2-ethylhexyl acrylate monomer (2-ethylhexyl acrylate monomer) and butyl acrylate (Butyl acrylate monomer) is petrochemical solid 100% oily, so water and It is prepared by molecular reaction at 80°C or higher by mixing and diluting.
이 혼합물에 사용자가 원하는 색상의 염료의 양을 조절하여 혼합함으로써 반투명의 착색제가 구성된다.A semi-transparent colorant is formed by mixing the mixture by adjusting the amount of dye of a color desired by the user.
하도시공(S200)을 통해 프라이머를 도포하여 경화시킨 후 수평몰탈을 시공하게 되면 가벼운 수지가 위로 뜨는데, 그 상태에서 반투명 착색제를 도포하면 수지가 많은 부분은 착색제가 얕게 침투하고, 수지가 적은 부분은 착색제가 깊게 침투되어 착색제 침투 깊이에 따른 음영효과가 나타나 도 4와 같이 투명몰탈 본연의 자연스러운 무늬가 형성되며, 반투명 도막에 의해 수평몰탈 본연의 자연스러운 무늬가 색상과 함께 표현되어 빈티지 효과가 돋보이게 된다.After applying the primer through the primer (S200) to harden it and then applying a horizontal mortar, the light resin floats up.If a translucent colorant is applied in this state, the part with a lot of resin penetrates shallowly and the part with less resin As the colorant penetrates deeply, a shadowing effect according to the depth of penetration of the colorant appears to form a natural natural pattern of the transparent mortar as shown in FIG. 4, and the natural pattern of the horizontal mortar natural color is expressed by the translucent coating layer, thereby enhancing the vintage effect.
그리고 수평몰탈을 보호하기 위해 수용성 코팅제 또는 에폭시를 도포하는 상도시공(S600) 단계를 실시하여야 하는데, 상도시공(S600)을 시공하기 전에 접착력을 증가시키기 위해 하도 시공을 실시하여야 한다.In addition, in order to protect the horizontal mortar, a step of applying a water-soluble coating agent or epoxy (S600) should be carried out, and before applying the coating (S600), a primer must be applied to increase adhesion.
본 발명은 상술한 반투명 착색제를 도포하여 형성된 도막이 이 하도 역할을 하므로 별도의 상도 시공전 하도를 시공할 필요가 없으므로 경비와 시간을 절약할 수 있다.In the present invention, since the coating film formed by applying the above-mentioned translucent colorant acts as a lower coat, there is no need to construct a separate coat before applying the top coat, thereby saving cost and time.
상기와 같이 반투명 착색제 도포(S500) 단계를 실시하여 형성된 반투명 도막에 수용성 코팅제 또는 에폭시를 도포하는 상도 시공(S600) 단계를 실시하여 수평몰탈과 반투명 색상 도막을 보호하도록 한다.By applying the translucent colorant (S500) as described above, a top coat construction (S600) step of applying a water-soluble coating agent or epoxy to the translucent coating film formed is performed to protect the horizontal mortar and the translucent color coating.
그리고 본 발명은 분리대를 설치하지 않고서도 각기 다른 색상으로 바닥이 표현되도록 구성할 수 있다.And the present invention can be configured to represent the floor in different colors without installing a separator.
도 3에 도시한 바와 같이, 수평몰탈 시공(S300)과 양생(S400) 단계를 실시한 후에 다른 색상으로 표현할 경계에 테이핑 작업으로 바닥을 구획하는 테이핑 구획(S510) 단계를 실시한다.As illustrated in FIG. 3, after performing the steps of horizontal mortar construction (S300) and curing (S400), a step of taping section (S510) for dividing the floor with a taping operation at a boundary to be expressed in different colors is performed.
테이핑 구획(S510) 단계를 실시한 후에 테이핑을 경계로 양측을 각각 서로 다른 색상의 염료가 혼합된 반투명 착색제를 도포한 후, 테이프를 제거함으로써 수평몰탈 본연의 무늬가 끊기지 않으면서도 여러 색상을 표현할 수 있으므로 수평몰탈 무늬의 연결성과 통일성이 높아진다.After performing the step of taping section (S510), after applying a translucent colorant mixed with dyes of different colors on both sides with a taping as a border, by removing the tape, multiple colors can be expressed without breaking the natural pattern of horizontal mortar. The connection and unity of the horizontal mortar pattern increases.
또한, 스텐실 고법을 통해 도 5와 같이 상호, 로고, 이미지, 캐릭터 등의 다양한 형태를 표현할 수 있다.In addition, various forms such as a company name, a logo, an image, and a character can be expressed through the stencil method.
상기와 같이 구성된 본 발명의 수평몰탈 표면의 반투명 착색방법은 수평몰탈 본연의 무늬를 살리면서 다양한 색상을 표현할 수 있고, 분리대를 설치하지 않고서도 여러 색상을 한꺼번에 표현할 수 있다.The translucent coloring method of the horizontal mortar surface of the present invention configured as described above can express various colors while making use of the natural pattern of the horizontal mortar, and can express multiple colors at once without installing a separator.
이상 상술한 실시예를 통해 본 발명의 기술적 사상을 살펴보았다.The technical idea of the present invention has been described through the above-described embodiment.
본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 본 발명의 기재사항으로부터 상기 살펴본 실시예를 다양하게 변형하거나 변경할 수 있음은 자명하다.It is apparent that a person having ordinary knowledge in the technical field to which the present invention pertains can variously modify or change the embodiments described above from the description of the present invention.
또한, 비록 명시적으로 도시되거나 설명되지 아니하였다 하여도 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 본 발명의 기재사항으로부터 본 발명에 의한 기술적 사상을 포함하는 다양한 형태의 변형을 할 수 있음은 자명하며, 이는 여전히 본 발명의 권리범위에 속한다.In addition, although not explicitly shown or described, a person having ordinary skill in the art to which the present invention pertains can make various modifications including the technical spirit according to the present invention from the description of the present invention. Is self-evident, which still falls within the scope of the present invention.
첨부하는 도면을 참조하여 설명된 상기의 실시예는 본 발명을 설명하기 위한 목적으로 기술된 것이며 본 발명의 권리범위는 이러한 실시예에 국한되지 아니한다.The above-described embodiments described with reference to the accompanying drawings are described for the purpose of illustrating the present invention, and the scope of the present invention is not limited to these embodiments.
S100 : 바닥정리 단계
S200 : 하도시공 단계
S300 : 수평몰탈 시공 단계
S400 : 양생 단계
S500 : 반투명 착색제 도포 단계
S510 : 테이핑 구획 단계
S600 : 상도시공 단계S100: Floor cleaning step
S200: subcontracting stage
S300: horizontal mortar construction stage
S400: curing stage
S500: Translucent colorant application step
S510: Taping compartment step
S600: phase of construction
Claims (4)
정리된 바닥에 프라이머를 도포하는 하도 시공단계(S200);
하도 시공단계(S200)를 통해 형성된 도막에 수평몰탈을 부어 레벨링하는 수평몰탈 시공 단계(S300);
수평몰탈을 양생하는 양생단계(S400);
스틸렌모노머(Styrene Monomer, C6H5CH=CH2) 20~24 중량부에 대해, 2-에틸헥실아크릴레이트모노머(2-ethylhexyl acrylate monomer) 15~20 중량부와, 부틸아크릴레이트(Butyl acrylate monomer) 3~4 중량부와, 유화제(계면활성제) 0.3~0.8 중량부와, 물 50~60중량부 및 염료가 혼합된 반투명 착색제를 도포하는 반투명 착색제 도포단계(S500); 및
반투명 착색제가 도포되어 형성된 도막에 상도에 수용성 코팅제 또는 에폭시 소재 도막을 형성하는 상도 시공단계(S600);를 포함하여 구성된 것을 특징으로 하는 수평몰탈 표면의 반투명 착색방법.
Floor cleaning step of cleaning the floor to be constructed (S100);
Primer construction step of applying a primer to the cleaned floor (S200);
A horizontal mortar construction step (S300) in which a horizontal mortar is poured into the coating film formed through the primer construction step (S200) to level it;
Curing step for curing the horizontal mortar (S400);
Styrene Monomer (C 6 H 5 CH=CH 2 ) 15-20 parts by weight of 2-ethylhexyl acrylate monomer and 20% by weight of 20-24 parts by weight of 2-ethylhexyl acrylate monomer, and Butyl acrylate monomer) 3-4 parts by weight, an emulsifier (surfactant) 0.3-0.8 parts by weight, 50-60 parts by weight of water and a semi-transparent colorant coating step of applying a translucent colorant mixed with a dye (S500); And
A semi-transparent coloring method of a horizontal mortar surface, characterized in that it comprises a; top coat construction step (S600) of forming a water-soluble coating agent or an epoxy material coating film on the top coat formed by applying a translucent colorant.
상기 반투명 착색제는 염료 혼합 전 혼80~90℃의 온도 환경에서 반응하도록 구성된 것을 특징으로 하는 수평몰탈 표면의 반투명 착색방법.
According to claim 1,
The translucent colorant is a translucent coloring method of a horizontal mortar surface, characterized in that it is configured to react in a temperature environment of 80 to 90°C before mixing the dye.
상기 수평몰탈 양생단계(S400)를 실시한 후에 테이프로 수평몰탈을 구획하고, 테이프를 경계로 양측에 서로 다른 색상의 염료가 혼합된 반투명 착색제가 도포하도록 구성된 것을 특징으로 하는 수평몰탈 표면의 반투명 착색방법.
According to claim 1,
After performing the horizontal mortar curing step (S400), the horizontal mortar is partitioned, and the translucent coloring method of the horizontal mortar surface is characterized in that a translucent colorant mixed with dyes of different colors is applied to both sides of the tape as a border. .
2-에틸헥실아크릴레이트모노머(2-ethylhexyl acrylate monomer) 15~20 중량부와,
부틸아크릴레이트(Butyl acrylate monomer) 3~4 중량부와,
유화제(계면활성제) 0.3~0.8 중량부와,
물 50~60중량부 및 소정 양의 염료가 혼합되어 수평몰탈에 도포되도록 구성된 것을 특징으로 하는 수평몰탈 표면의 반투명 착색제.
Styrene Monomer (C 6 H 5 CH=CH 2 ) 20 to 24 parts by weight,
15 to 20 parts by weight of 2-ethylhexyl acrylate monomer (2-ethylhexyl acrylate monomer),
Butyl acrylate (Butyl acrylate monomer) 3-4 parts by weight,
Emulsifier (surfactant) 0.3 to 0.8 parts by weight,
A translucent colorant on the surface of a horizontal mortar, characterized in that 50-60 parts by weight of water and a predetermined amount of dye are mixed and applied to the horizontal mortar.