KR20200042593A - Glace Composition for Ceramic Ware Comprising Ashes from Baby Brier and Preparation Method thereof - Google Patents
Glace Composition for Ceramic Ware Comprising Ashes from Baby Brier and Preparation Method thereof Download PDFInfo
- Publication number
- KR20200042593A KR20200042593A KR1020180122880A KR20180122880A KR20200042593A KR 20200042593 A KR20200042593 A KR 20200042593A KR 1020180122880 A KR1020180122880 A KR 1020180122880A KR 20180122880 A KR20180122880 A KR 20180122880A KR 20200042593 A KR20200042593 A KR 20200042593A
- Authority
- KR
- South Korea
- Prior art keywords
- ash
- glaze
- brier
- weight
- composition
- Prior art date
Abstract
Description
본 발명은 찔레꽃나무재를 포함하는 도자기용 유약 조성물 및 이의 제조방법에 관한 것이다.The present invention relates to a glaze composition for porcelain containing brierwood and a method for manufacturing the same.
이 부분에 기술된 내용은 단순히 본 발명에 대한 배경정보를 제공할 뿐 종래기술을 구성하는 것은 아니다.The content described in this section merely provides background information for the present invention and does not constitute a prior art.
일반적으로 유약이란, 도자기의 표면에 점착되는 얇은 유리층으로서 도자기의 흡수성을 저하시키고 심미감을 표출시키며 도자기를 튼튼하게 하는 역할을 한다. In general, a glaze is a thin glass layer adhered to the surface of ceramics, which reduces the absorbency of ceramics, expresses an aesthetic sense, and serves to strengthen ceramics.
즉, 유약은 도자기나 옹기류 등의 표면에 칠해지고 열처리 융착되어 그 표면에 광택 또는 무광택의 표면층을 형성시키기 위하여 사용되는 제제로서 투수성을 없애고 미적 효과를 증가시키며 도자기의 강도를 향상시킬 수 있다.That is, the glaze is a preparation used to form a glossy or matte surface layer on the surface of a ceramic or pottery, etc. by being heat-treated and fused, thereby eliminating water permeability, increasing the aesthetic effect, and improving the strength of the ceramic. .
도자기에 표면에 칠해져서 소성에 의해 광택을 띄게 하는 유약은 통상 장석, 규석, 고령토, 석회석, 활석, 형석, 골분을 주성분으로 구성될 수 있다. Glazes that are painted on the surface of ceramics to make them shine by firing can usually consist of feldspar, silica, kaolin, limestone, talc, fluorspar, and bone powder as the main components.
이와 같이 종래의 도자기용 유약은 흙이나 돌가루만을 사용하여 유약을 만들기 때문에 나무재를 사용하였던 과거 고려, 조선 시대의 청자나 백자와 같은 고급스러운 자연미를 살리지 못하는 한계가 있었다.As described above, since the traditional glaze for ceramics makes glaze using only soil or stone powder, there was a limitation that it could not take advantage of the luxurious natural beauty such as celadon or white porcelain from the past Goryeo and Joseon Dynasty, where wood was used.
종래기술인 등록특허 제 10-1079706호의 솔잎, 콩깍지재, 장석, 대합조개 껍질 등을 사용한 유약 조성물, 등록특허 제 10-0387920호의 산화철, 코발트 등을 사용한 유약 조성물 등은 발색력이 좋지 못해 역시 고급스러운 자연미를 살리지 못하는 단점이 있었다.The glaze composition using pine needle, soybean pod, feldspar, clamshell, etc. of the registered patent No. 10-1079706, the glaze composition using iron oxide, cobalt, etc. of the registered patent No. 10-0387920 have poor color development, and are also luxurious natural beauty There was a disadvantage that could not save.
이에 본 발명자는 따뜻하고 부드러운 느낌을 주는 고급스러운 자연미를 살릴 수 있는 도자기용 유약을 개발하고자 예의 연구를 거듭하였고, 그 결과 찔레꽃나무의 재가 첨가된 유약을 도자기에 적용하는 경우, 부드럽고 따뜻한 느낌을 발현할 수 있다는 것을 알게 되어 본 발명을 완성하기에 이르렀다.Accordingly, the present inventor has conducted extensive research to develop a glaze for ceramics that can make use of a luxurious natural beauty that gives a warm and soft feeling, and as a result, when applying a glaze with a ash of a brier to ceramics, it produces a soft and warm feeling. It has been realized that the present invention can be reached to complete the present invention.
본 발명의 일 목적은 따뜻하고 부드러운 느낌을 발현시켜 고급스러운 자연미를 살릴 수 있는 환경 친화적인 도자기용 유약 및 이의 제조방법을 제공하는 것이다.One object of the present invention is to provide an environmentally friendly glaze for ceramics and a method for manufacturing the same, which can express a warm and soft feeling and utilize a luxurious natural beauty.
본 발명의 일 목적을 달성하기 위해, 본 발명은 찔레꽃나무를 태운 재의 분말인 찔레꽃나무 재 및 통상의 유약 원료를 포함하는 유약 조성물을 제공한다.In order to achieve one object of the present invention, the present invention provides a glaze composition comprising a brierwood ash which is a powder of a brierwood ash and common glaze raw materials.
찔레꽃나무는 전국의 산과 들의 기슭과 계곡에서 흔히 볼 수 있는 낙엽활엽관목이다. 찔레꽃나무는 찔레나무, 찔레꽃 가시나무 라고도 불린다. 찔레꽃나무 재는 이 찔레꽃나무를 한 데 모아 태우고 남은 재의 분말을 사용할 수 있다. 이러한 찔레꽃나무 재를 도자기용 유약의 원료로 사용하는 경우, 환경 친화적이고 고급스러운 자연미를 나타내는 도자기를 제공할 수 있다.Brier is a deciduous broad-leaved tree commonly found in the foothills and valleys of mountains and mountains nationwide. The brier tree is also called the brier tree. Brierwood ashes can be used to collect and burn the brierwood powder. When these brierwood ashes are used as a raw material for glazes for ceramics, it is possible to provide ceramics that are environmentally friendly and exhibit high-quality natural beauty.
찔레꽃나무 재는 산화칼슘(CaO)을 함유할 수 있다. 산화칼슘(CaO)은 유약 혼합물의 용융온도를 낮출 수 있고 이에 의해 유약 조성물의 용융도가 높아질 수 있다. 즉, 산화칼슘(CaO)이 많이 함유되면 유약 조성물이 비교적 낮은 온도에서 용융되기 시작하므로 잘 녹는 도자기용 유약을 제조할 수 있는 것이다. 도자기용 유약의 용융온도가 높아 잘 녹지 않으면, 더 높은 온도와 더 긴 소성시간이 요구되므로, 산화칼슘(CaO)의 역할이 중요할 수 있다. 또한, 산화칼슘(CaO)은 유약 조성물에 포함된 원료들을 서로 잘 섞이도록 하는 매용제의 역할을 할 수 있다. Brierwood ash may contain calcium oxide (CaO). Calcium oxide (CaO) can lower the melting temperature of the glaze mixture, thereby increasing the meltability of the glaze composition. That is, if a large amount of calcium oxide (CaO) is contained, the glaze composition begins to melt at a relatively low temperature, so that it is possible to manufacture a glaze for porcelain that melts well. If the melting temperature of the ceramic glaze is high and does not melt well, a higher temperature and longer firing time are required, so the role of calcium oxide (CaO) may be important. In addition, calcium oxide (CaO) may serve as a solvent for mixing the ingredients contained in the glaze composition well with each other.
또한, 산화칼슘(CaO)은 유약의 색을 부드럽게 하는 역할을 할 수 있다. 또한, 산화칼슘(CaO)은 유약의 표면 광택도를 높일 수 있다. 즉, 도자기의 외면에 적용되어 도자기의 표면의 광택도를 높일 수 있는 것이다. 다만, 과량 함유되면, 그 유약의 표면은, 갈라진 틈, 내부에서 터져 형성되는 분화구와 같은 형상의 홈 등을 포함하도록 형성될 수 있고, 매끄럽지 않고 울퉁불퉁한 표면으로 형성될 수 있다. In addition, calcium oxide (CaO) may serve to soften the color of the glaze. In addition, calcium oxide (CaO) can increase the surface glossiness of the glaze. That is, it can be applied to the outer surface of the ceramic to increase the glossiness of the surface of the ceramic. However, when contained in excess, the surface of the glaze may be formed to include grooves of a shape such as a crack, a crater formed by bursting from the inside, and may be formed as a smooth and uneven surface.
또한, 찔레꽃나무 재는 산화인(P2O5)을 함유할 수 있다. 이를 이용하여 도자기용 유약을 제조하는 경우 부드러운 유백색이 발현되므로, 맑고 따뜻한 느낌을 발현할 수 있다. 찔레꽃나무 재를 도자기용 유약에 첨가하는 경우 유백 유약, 투명 유약에 적용할 수 있으며, 특히 유백 유약에 적용하는 것이 바람직하다. 다만, 반드시 이에 한정되는 것은 아니고 공지의 어떠한 유약에도 적용될 수 있다.In addition, the brier ash may contain phosphorus oxide (P 2 O 5 ). When manufacturing a glaze for ceramics using this, a soft milky white color is expressed, so that a clear and warm feeling can be expressed. When the brier ash is added to the glaze for ceramics, it can be applied to a glaze and a transparent glaze, and is particularly preferably applied to a glaze. However, it is not necessarily limited to this and can be applied to any known glaze.
또한, 찔레꽃나무 재는 실리카(SiO2) 성분을 함유할 수 있다. 실리카(SiO2) 성분에 의하면 유약의 점성을 높일 수 있고, 따라서 찔레꽃나무 재를 이용하여 유약을 제조하는 경우 별도로 규석(점성을 높일 수 있는 성분)을 첨가하지 않을 수 있다In addition, the brier ash may contain a silica (SiO2) component. According to the silica (SiO2) component, the viscosity of the glaze can be increased, and thus, when preparing a glaze using an ash wood, silica (a component capable of increasing viscosity) may not be added separately.
또한, 찔레꽃나무 재는 산화마그네슘(MgO)을 함유할 수 있다. 산화마그네슘(MgO)은 위에서 언급한 산화칼슘(CaO)과 유사한 역할을 할 수 있다.In addition, the brier ash may contain magnesium oxide (MgO). Magnesium oxide (MgO) may play a role similar to the calcium oxide (CaO) mentioned above.
또한, 찔레꽃나무 재는 산화알루미늄(Al2O3)을 함유할 수 있다. 산화알루미늄(Al2O3)은 유약의 물성을 높일 수 있고, 유약의 점성을 높여 물처럼 흐르는 것을 방지할 수 있으며 광이 덜 나는 매트(matt)한 느낌을 낼 수 있게 한다.In addition, the brier ash may contain aluminum oxide (Al 2 O 3 ). Aluminum oxide (Al 2 O 3 ) can increase the physical properties of the glaze, increase the viscosity of the glaze to prevent it from flowing like water, and make the matte feel of less light.
통상의 도자기용 유약 원료에는 이 기술분야에서 널리 사용되는 도자기 유약 원료 성분이 모두 포함될 수 있으며, 구체적으로 장석과 도석, 백운석, 석회석, 규석, 고령토, 산청토 및 이들의 혼합물로 이루어진 군으로부터 선택된 것을 포함할 수 있으나, 반드시 이에 제한되는 것은 아니다.Common glaze raw materials for porcelain may include all of the ingredients of porcelain glaze widely used in this technical field, and specifically selected from the group consisting of feldspar, pottery, dolomite, limestone, silica, kaolin, sancheong earth, and mixtures thereof. May include, but is not necessarily limited to.
통상의 유약 원료의 성분 중 장석이나 도석의 알카리 성분은 유약 원료 중 규석 성분과 반응하며 유리질을 만드는 융제 역할을 하며, 석회석과 석회석의 일종인 백운석은 유약을 더 잘 녹게 하며 경도를 높게 하는 역할을 한다. 이들의 혼합 비율은 본 발명의 속하는 기술분야의 통상의 지식을 가진 자에게 자명한 것이다.Among the ingredients of ordinary glaze raw materials, the alkali component of feldspar or porcelain reacts with the siliceous components of the glaze raw materials and acts as a flux to make the glass. Limestone and dolomite, a type of limestone, play a role in melting glaze better and increasing hardness. do. These mixing ratios are apparent to those skilled in the art to which the present invention pertains.
본 발명의 일 실시예에 따른 도자기용 유약 조성물은 찔레꽃나무 재 50∼80 중량% 및 통상의 유약 원료 20∼50중량%를 포함할 수 있다.The glaze composition for porcelain according to an embodiment of the present invention may include 50 to 80% by weight of brierwood ash and 20 to 50% by weight of a conventional glaze raw material.
또한, 본 발명의 일 실시예에 따른 도자기용 유약 조성물은 고령토, 점토, 탄산바륨, 도석, 활석, 백운석, 골회, 황토, 벤토 나이트, 산화동, 산화코발트, 산화망간, 산화니켈, 산화티타늄, 산화주석, 산화아연 등을 제조하고자 하는 유약의 종류에 따라 더 포함할 수 있다. 본 발명의 일 실시예에 따른 도자기용 유약 조성물은 도자기에 적용되는 경우 산화동, 산화코발트, 산화망간, 산화니켈, 산화티타늄, 산화주석 등의 발색 원료를 첨가하여 비취색, 올리브 그린색, 브라운 색 등을 나타낼 수 있다. In addition, the glaze composition for ceramics according to an embodiment of the present invention is kaolin, clay, barium carbonate, pottery, talc, dolomite, bone ash, ocher, bentonite, copper oxide, cobalt oxide, manganese oxide, nickel oxide, titanium oxide, oxidation Tin, zinc oxide, etc. may be further included according to the type of glaze to be produced. The glaze composition for porcelain according to an embodiment of the present invention, when applied to porcelain, adds color-producing materials such as copper oxide, cobalt oxide, manganese oxide, nickel oxide, titanium oxide, tin oxide, etc., jade, olive green, brown, etc. Can represent
또한, 본 발명은 찔레꽃나무 재를 포함하는 도자기용 유약 조성물의 제조방법을 제공할 수 있다. 도자기용 유약 조성물의 제조방법은 찔레꽃나무 재를 준비하는 단계 및 찔레꽃나무 재와 통상의 유약 원료를 혼합하는 단계를 포함할 수 있다.In addition, the present invention can provide a method of manufacturing a glaze composition for porcelain comprising a brier ash. The method of manufacturing a glaze composition for ceramics may include preparing a brier ash and mixing the brier ash with common glaze raw materials.
찔레꽃나무 재를 준비하는 단계는, 이 기술분야에서 이용되는 일반적인 방법으로 얻어질 수 있다. 예를 들면, 찔레꽃나무가 타고 남은 재를 물과 섞고 분쇄 과정을 거친 다음 체를 이용하여 재 이외의 이물질을 걸러 준다. 체로 걸러 낸 찔레꽃나무의 재가 침전되어 가라앉으면 침전된 재로부터 잿물을 분리해 내고(여러번 반복), 남아 있는 재를 건조시켜 분말 상태로 만들어 사용할 수 있다.The step of preparing the brier ash can be obtained by a general method used in the art. For example, the ash tree burns, mixes the remaining ash with water, goes through a crushing process, and sifts out foreign matter other than ash. When the ash of the brier filtered through a sieve settles and sinks, the lye is separated from the precipitated ash (repeated several times), and the remaining ash can be dried to form a powder.
이와 같이 제조된 찔레꽃나무 재를 통상의 유약 원료와 혼합하여 본 발명의 일 실시예에 따른 도자기용 유약 조성물을 제조할 수 있다.The brier ash produced as described above may be mixed with ordinary glaze raw materials to prepare a glaze composition for ceramics according to an embodiment of the present invention.
본 발명의 추가적인 해결수단은 아래에서 이어지는 설명에서 일부 설명될 것이고, 그 설명으로부터 부분적으로 용이하게 확인할 수 있거나, 또는 본 발명의 실시에 의해 지득될 수 있다.Additional solutions of the present invention will be described in part in the description that follows, and may be readily identified in part from the description, or may be learned by practice of the present invention.
전술한 일반적인 설명 및 다음의 상세한 설명 모두는 단지 예시적이고 설명을 위한 것이며 청구범위에 기재된 본 발명을 제한하지 않는다.Both the foregoing general description and the following detailed description are illustrative and illustrative only and do not limit the invention described in the claims.
본 발명에 따른 찔레꽃나무 재를 포함하는 도자기용 유약 조성물은 고급스러운 자연미를 살릴 수 있으며, 청자 유약, 분청 투명 유약, 매트 유약, 이라보 유약, 천목 유약 등 각종 색 유약의 제조에 사용될 수 있다.The glaze composition for ceramics comprising the brier ash according to the present invention can utilize a luxurious natural beauty, and can be used in the manufacture of various color glazes such as celadon glaze, transparent clear glaze, matt glaze, irabo glaze, celestial glaze.
도 1은 본 발명의 실시예에 따라 환원분위기로 제조된 도자기 시험편이다.1 is a porcelain test piece manufactured in a reducing atmosphere according to an embodiment of the present invention.
이하, 첨부된 도면을 참조하여 본 발명의 구체적인 실시형태에 대하여 상세하게 서술하도록 한다. Hereinafter, specific embodiments of the present invention will be described in detail with reference to the accompanying drawings.
다만, 본 발명의 구체적 일 실시 형태를 설명함에 있어, 관련된 공지 기능 또는 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략한다.However, in describing a specific embodiment of the present invention, when it is determined that a detailed description of a related known function or configuration may unnecessarily obscure the subject matter of the present invention, the detailed description will be omitted.
시험예: 찔레꽃나무 재 성분 분석Test Example: Brier ash component analysis
아래의 표 1은 XRF로 분석한 찔레꽃나무 재의 성분분석표이다. 표 1을 참조하면, 찔레꽃나무 재를 XRF를 사용하여 성분 분석한 결과를 파악할 수 있다. Table 1 below is a component analysis table of the brier ash analyzed by XRF. Referring to Table 1, it is possible to grasp the results of the component analysis of the brier ash using XRF.
찔레꽃나무 재는 산화칼슘(CaO) 및 산화마그네슘(MgO)을 포함할 수 있다. 찔레꽃나무 재는 찔레꽃나무 재 전체 중량을 기준으로 산화칼슘(CaO)을 63.57중량%, 산화마그네슘(MgO)을 6.92중량% 포함할 수 있다. 산화칼슘(CaO)및 산화마그네슘(MgO)은 앞서 언급했듯이 유약의 조성물의 용융온도를 낮출 수 있고, 유약 조성물에 혼합된 여러 성분을 잘 혼합되게 하는 매용제의 역할을 할 수 있다.Brierwood ash may include calcium oxide (CaO) and magnesium oxide (MgO). The brier ash may include 63.57% by weight calcium oxide (CaO) and 6.92% by weight magnesium oxide (MgO) based on the total weight of the brier ash. Calcium oxide (CaO) and magnesium oxide (MgO), as mentioned above, can lower the melting temperature of the composition of the glaze, and can serve as a solvent for mixing various components well mixed in the glaze composition.
또한, 찔레꽃나무 재는 산화규소(SiO2)를 포함할 수 있다. 찔레꽃나무 재는 찔레꽃나무 재 전체 중량을 기준으로 산화규소(SiO2)를 12.16중량% 함유할 수 있다.In addition, the brier ash may include silicon oxide (SiO 2 ). The brier ash may contain 12.16% by weight of silicon oxide (SiO 2 ) based on the total weight of the brier ash.
또한, 찔레꽃나무 재는 산화인(P2O5)을 포함할 수 있다. 찔레꽃나무 재는 찔레꽃나무 재 전체 중량을 기준으로 산화인(P2O5)을 8.35중량% 함유할 수 있다. 산화인(P2O5)은 앞서 언급했듯이, 유약을 맑고 따뜻한 느낌이 발현되도록 할 수 있고, 유약의 느낌을 부드럽게 할 수 있다. In addition, the brier ash may include phosphorus oxide (P 2 O 5 ). Brierwood ash may contain 8.35% by weight of phosphorus oxide (P 2 O 5 ) based on the total weight of brierwood ash. As mentioned above, phosphorus oxide (P 2 O 5 ) can make the glaze develop a clear and warm feeling, and soften the feel of the glaze.
또한, 찔레꽃나무 재는 산화알루미늄(Al2O3)을 함유할 수 있다. 찔레꽃나무 재는 찔레꽃나무 재 전체 중량을 기준으로 산화알루미늄(Al2O3)을 3.43중량% 함유할 수 있다. 이에 의하면 유약의 점성을 높여 물처럼 흐르는 것을 방지할 수 있으며 광이 덜 나는 매트(matt)한 느낌을 낼 수 있다.In addition, the brier ash may contain aluminum oxide (Al 2 O 3 ). The brier ash may contain 3.43% by weight of aluminum oxide (Al 2 O 3 ) based on the total weight of the brier ash. According to this, the viscosity of the glaze can be increased to prevent it from flowing like water, and a matte feeling with less light can be produced.
또한, 찔레꽃나무 재는 찔레꽃나무 재 전체 중량을 기준으로 기타 성분을 1.84중량% 함유할 수 있다. 기타 성분은 그 성분 함량이 작아 유약의 특징에 큰 영향을 미치지 않는 요소를 '기타'라는 하나의 카테고리로 묶은 것으로, TiO2, ZnO, MnO, Na2O, BaO, SO3, CuO, Cl, Pm2O3를 포함할 수 있다.In addition, the brier ash may contain 1.84% by weight of other components based on the total weight of the brier ash. Other ingredients are those that have a small content and do not significantly affect the characteristics of the glaze, and are grouped into one category called 'other'. TiO 2 , ZnO, MnO, Na 2 O, BaO, SO 3 , CuO, Cl, Pm 2 O 3 .
실시예Example
찔레꽃나무 재를 장석, 규석 및 산청토와 혼합하되, 아래 표 2에 기재한 성분들의 조성비(유약 조성물 전체중량을 기준으로 한 중량비율)에 따라 혼합하여 15가지 종류의 유약을 제조하였다. 도 1에 첨부된 시험편은 표2에 기재한 조성비에 따라 제조된 15가지의 유약을 15개의 초벌구이한 시험편들에 시유한 후 가마에 넣어 환원분위기로 1230℃ 내지 1250℃에서 8 시간 내지 10시간 동안 소성하는 과정을 거쳐 제조된다. The brierwood ash was mixed with feldspar, silica, and sancheong, but mixed in accordance with the composition ratio (weight ratio based on the total weight of the glaze composition) of the components shown in Table 2 below to prepare 15 types of glaze. The test specimen attached to FIG. 1 was fed into 15 kiln-baked test specimens after 15 glazes prepared according to the composition ratios shown in Table 2, and then put them in a kiln for 8 hours to 10 hours at 1230 ° C to 1250 ° C in a reducing atmosphere It is manufactured through the process of firing.
도 1은 본 발명의 실시예에 따라 환원분위기로 제조된 도자기 시험편이다. 도 1의 1번 내지 10번의 도자기 시험편을 참조하여 각 성분의 함량비율 변화에 따른 유약의 색상 및 표면의 변화를 관찰해보면, 우측 하단으로 갈수록 찔레꽃나무 재의 함량비율이 감소되는데, 찔레꽃나무 재 함량비율이 낮을수록 유백색을 띠고, 찔레꽃나무 재 함량비율이 높을수록 옅은 녹색을 띠는 것을 파악할 수 있다. 1 is a porcelain test piece manufactured in a reducing atmosphere according to an embodiment of the present invention. Referring to the
특히, 8번 및 9번 시험편은 밝은 유백색을 띠는 것을 파악할 수 있다. 8번 조성물은 유약 조성물 전체 중량을 기준으로 찔레꽃나무 재 50중량%, 장석 20중량%, 규석 25중량% 및 산청토 5중량%을 포함할 수 있다. 또한 9번 조성물은 유약 조성물 전체 중량을 기준으로 찔레꽃나무 재 50중량%, 장석 30중량%, 규석 15중량% 및 산청토 5중량%을 포함할 수 있다.In particular, it can be seen that
정리하면, 밝은 유백색을 띠는 유약 조성물은 유약 조성물 전체 중량을 기준으로 찔레꽃나무 재 50중량%, 장석 20 내지 30중량%, 규석 15 내지 25중량% 및 산청토 5중량%을 포함할 수 있다. In summary, the bright milky white glaze composition may include 50% by weight of ash wood, 20 to 30% by weight of feldspar, 15 to 25% by weight of silica, and 5% by weight of acid chrysanthemum based on the total weight of the glaze composition.
본 실시예는 본 발명의 기술적 사상을 예시적으로 설명한 것에 불과하고, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 본 실시예의 다양한 수정 및 변형이 가능할 것이다. 본 실시예는 본 발명의 기술적 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 따라서 본 실시예에 의하여 본 발명의 권리범위가 한정되는 것은 아니다. 본 발명의 보호범위는 청구범위에 의하여 해석되어야 하며, 그와 동등하거나 균등하다고 인정되는 모든 기술적 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 한다.This embodiment is merely illustrative of the technical idea of the present invention, and those skilled in the art to which the present invention pertains may have various modifications and variations of this embodiment without departing from the essential characteristics of the present invention. It will be possible. This embodiment is not intended to limit the technical spirit of the present invention but to explain it, and accordingly, the scope of the present invention is not limited by the present embodiment. The scope of protection of the present invention should be interpreted by the claims, and all technical ideas recognized as equivalent or equivalent should be interpreted as being included in the scope of the present invention.
Claims (4)
장석, 규석 및 산청토를 포함하는 통상의 유약원료
를 포함하는 찔레꽃나무 재를 포함하는 도자기용 유약 조성물.Brierwood ash, which is a powder of brierwood ashes; And
Normal glaze raw materials including feldspar, wollastonite and acid
Glaze composition for porcelain comprising a brier ash comprising a.
유약 조성물 전체 중량을 기준으로 상기 찔레꽃나무 재는 50~80중량%, 상기 통상의 유약원료는 20~50중량%인 것
을 특징으로 하는 찔레꽃나무 재를 포함하는 도자기용 유약 조성물.According to claim 1,
The brier ash is 50 to 80% by weight based on the total weight of the glaze composition, and the conventional glaze raw material is 20 to 50% by weight
A glaze composition for porcelain comprising a brierwood ash characterized in that.
유약 조성물 전체 중량을 기준으로 상기 찔레꽃나무 재는 50중량%, 상기 장석은 20 내지 30중량%, 상기 규석은 15 내지 25중량% 및 상기 산청토는 5중량%인 것
을 특징으로 하는 찔레꽃나무 재를 포함하는 도자기용 유약 조성물.According to claim 2,
Based on the total weight of the glaze composition, the brierwood ash is 50% by weight, the feldspar is 20 to 30% by weight, the silica is 15 to 25% by weight, and the acidic soil is 5% by weight
A glaze composition for porcelain comprising a brierwood ash characterized in that.
장석, 규석 및 산청토를 포함하는 통상의 유약원료와 상기 찔레꽃나무 재를 혼합하는 단계
를 포함하는 찔레꽃나무 재를 포함하는 도자기용 유약 조성물의 제조방법.Preparing brier ashes; And
Mixing the common brimwood materials including feldspar, wollastonite, and sancheongra and the brier ash
Method of manufacturing a glaze composition for porcelain comprising a brier ash comprising a.