KR102138702B1 - Glace Composition for Ceramic Ware Comprising Ashes from Hawthorn-like raspberry and Preparation Method thereof - Google Patents

Glace Composition for Ceramic Ware Comprising Ashes from Hawthorn-like raspberry and Preparation Method thereof Download PDF

Info

Publication number
KR102138702B1
KR102138702B1 KR1020180122879A KR20180122879A KR102138702B1 KR 102138702 B1 KR102138702 B1 KR 102138702B1 KR 1020180122879 A KR1020180122879 A KR 1020180122879A KR 20180122879 A KR20180122879 A KR 20180122879A KR 102138702 B1 KR102138702 B1 KR 102138702B1
Authority
KR
South Korea
Prior art keywords
weight
raspberry
oxide
glaze
ash
Prior art date
Application number
KR1020180122879A
Other languages
Korean (ko)
Other versions
KR20200042592A (en
Inventor
김용득
김진욱
Original Assignee
김진욱
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김진욱 filed Critical 김진욱
Priority to KR1020180122879A priority Critical patent/KR102138702B1/en
Publication of KR20200042592A publication Critical patent/KR20200042592A/en
Application granted granted Critical
Publication of KR102138702B1 publication Critical patent/KR102138702B1/en

Abstract

본 발명은, 산딸기나무를 태운 재의 분말인 산딸기나무 재; 및 장석, 흰색고령토 및 규석을 포함하는 통상의 유약원료를 포함하는 산딸기나무 재를 포함하는 도자기용 유약 조성물을 제공한다.The present invention, raspberry ash, which is a powder of ash from a raspberry tree; And it provides a glaze composition for ceramics comprising raspberry wood ash containing a conventional glaze raw materials including feldspar, white kaolin and silica.

Description

산딸기나무재를 포함하는 도자기용 유약 조성물 및 이의 제조방법{Glace Composition for Ceramic Ware Comprising Ashes from Hawthorn-like raspberry and Preparation Method thereof}Glaze Composition for Ceramic Ware Comprising Ashes from Hawthorn-like raspberry and Preparation Method thereof
본 발명은 산딸기나무재를 포함하는 도자기용 유약 조성물 및 이의 제조방법에 관한 것이다.The present invention relates to a glaze composition for porcelain containing raspberry wood and a method for producing the same.
이 부분에 기술된 내용은 단순히 본 발명에 대한 배경정보를 제공할 뿐 종래기술을 구성하는 것은 아니다.The content described in this section merely provides background information for the present invention and does not constitute a prior art.
일반적으로 유약이란, 도자기의 표면에 점착되는 얇은 유리층으로서 도자기의 흡수성을 저하시키고 심미감을 표출시키며 도자기를 튼튼하게 하는 역할을 한다. In general, glaze is a thin glass layer that adheres to the surface of ceramics, and plays a role of lowering the absorbency of ceramics, expressing aesthetics, and strengthening ceramics.
즉, 유약은 도자기나 옹기류 등의 표면에 칠해지고 열처리 융착되어 그 표면에 광택 또는 무광택의 표면층을 형성시키기 위하여 사용되는 제제로서 투수성을 없애고 미적 효과를 증가시키며 도자기의 강도를 향상시킬 수 있다.In other words, glaze is a formulation used to form a glossy or matte surface layer on the surface of porcelain or pottery by painting and heat-fusing it on the surface. It can remove water permeability, increase aesthetic effect, and improve the strength of ceramics. .
도자기에 표면에 칠해져서 소성에 의해 광택을 띄게 하는 유약은 통상 장석, 규석, 고령토, 석회석, 활석, 형석, 골분을 주성분으로 구성될 수 있다. The glaze painted on the surface of pottery to give it a gloss by firing can usually consist of feldspar, silica stone, kaolin, limestone, talc, fluorspar, and bone powder as the main components.
이와 같이 종래의 도자기용 유약은 흙이나 돌가루만을 사용하여 유약을 만들기 때문에 나무재를 사용하였던 과거 고려, 조선 시대의 청자나 백자와 같은 고급스러운 자연미를 살리지 못하는 한계가 있었다.As described above, since the conventional glaze for ceramics is made using only soil or stone powder, there is a limit in not being able to make use of the luxurious natural beauty such as celadon or white porcelain in the past Goryeo and Joseon era when wood was used.
종래기술인 등록특허 제 10-1079706호의 솔잎, 콩깍지재, 장석, 대합조개 껍질 등을 사용한 유약 조성물, 등록특허 제 10-0387920호의 산화철, 코발트 등을 사용한 유약 조성물 등은 발색력이 좋지 못해 역시 고급스러운 자연미를 살리지 못하는 단점이 있었다.The glaze composition using pine needles, bean pods, feldspar, clam shells, etc. of the prior art Patent No. 10-1079706, and the glaze composition using iron oxide, cobalt, etc. of Patent No. 10-0387920 are also luxurious natural beauty due to poor color development. There was a drawback of not being able to save.
이에 본 발명자는 따뜻하고 부드러운 느낌을 주는 고급스러운 자연미를 살릴 수 있는 도자기용 유약을 개발하고자 예의 연구를 거듭하였고, 그 결과 산딸기나무의 재가 첨가된 유약을 도자기에 적용하는 경우, 부드럽고 따뜻한 느낌을 발현할 수 있다는 것을 알게 되어 본 발명을 완성하기에 이르렀다.Accordingly, the present inventors have repeatedly studied to develop a glaze for porcelain that can make use of the luxurious natural beauty that gives a warm and soft feeling, and as a result, when applying the glaze to which the ash of raspberry is added to the porcelain, a soft and warm feeling can be expressed. It was found that it was possible to complete the present invention.
본 발명의 일 목적은 따뜻하고 부드러운 느낌을 발현시켜 고급스러운 자연미를 살릴 수 있는 환경 친화적인 도자기용 유약 및 이의 제조방법을 제공하는 것이다.An object of the present invention is to provide an environmentally friendly glaze for ceramics and a method for manufacturing the same, which can make use of a luxurious natural beauty by expressing a warm and soft feeling.
본 발명의 일 목적을 달성하기 위해, 본 발명은 산딸기나무를 태운 재의 분말인 산딸기나무 재 및 통상의 유약 원료를 포함하는 유약 조성물을 제공한다.In order to achieve one object of the present invention, the present invention provides a glaze composition comprising raspberry wood ash, which is a powder of ash burned raspberry wood, and a conventional glaze raw material.
본 발명에서 산딸기나무의 재는 산딸기나무의 가지, 뿌리 등을 한 데 모아 태우고 남은 재의 분말을 사용할 수 있다. 이러한 산딸기나무 재를 도자기용 유약의 원료로 사용하는 경우, 환경 친화적이고 고급스러운 자연미를 나타내는 도자기를 제공할 수 있다.In the present invention, the ash of the raspberry tree may be used as a powder of ash remaining after the branches and roots of the raspberry tree are collected and burned. When such raspberry wood is used as a raw material for porcelain glaze, it is possible to provide porcelain exhibiting environmentally friendly and luxurious natural beauty.
산딸기나무 재는 산화칼슘(CaO)을 함유할 수 있다. 산화칼슘(CaO)은 유약 혼합물의 용융온도를 낮출 수 있고 이에 의해 유약 조성물의 용융도가 높아질 수 있다. 즉, 산화칼슘(CaO)이 많이 함유되면 유약 조성물이 비교적 낮은 온도에서 용융되기 시작하므로 잘 녹는 도자기용 유약을 제조할 수 있는 것이다. 도자기용 유약의 용융온도가 높아 잘 녹지 않으면, 더 높은 온도와 더 긴 소성시간이 요구되므로, 산화칼슘(CaO)의 역할이 중요할 수 있다. 또한, 산화칼슘(CaO)은 유약 조성물에 포함된 원료들을 서로 잘 섞이도록 하는 매용제의 역할을 할 수 있다. Raspberry ash may contain calcium oxide (CaO). Calcium oxide (CaO) may lower the melting temperature of the glaze mixture, thereby increasing the melting degree of the glaze composition. That is, when a large amount of calcium oxide (CaO) is contained, the glaze composition begins to melt at a relatively low temperature, so that a glaze for ceramics that melts well can be manufactured. If the melting temperature of the ceramic glaze is high and it does not melt well, a higher temperature and a longer firing time are required, so the role of calcium oxide (CaO) may be important. In addition, calcium oxide (CaO) may serve as a solvent for mixing the raw materials included in the glaze composition well with each other.
또한, 산화칼슘(CaO)은 유약의 색을 부드럽게 하는 역할을 할 수 있다. 또한, 산화칼슘(CaO)은 유약의 표면 광택도를 높일 수 있다. 즉, 도자기의 외면에 적용되어 도자기의 표면의 광택도를 높일 수 있는 것이다. 다만, 과량 함유되면, 그 유약의 표면은, 갈라진 틈, 내부에서 터져 형성되는 분화구와 같은 형상의 홈 등을 포함하도록 형성될 수 있고, 매끄럽지 않고 울퉁불퉁한 표면으로 형성될 수 있다. In addition, calcium oxide (CaO) may serve to soften the color of the glaze. In addition, calcium oxide (CaO) can increase the glossiness of the glaze. In other words, it is applied to the outer surface of ceramics to increase the glossiness of the surface of ceramics. However, if it is contained in excess, the surface of the glaze may be formed to include cracks, crater-like grooves formed by bursting from the inside, and the like, and may be formed as a non-smooth and uneven surface.
또한, 산딸기나무 재는 산화마그네슘(MgO)을 함유할 수 있다. 산화마그네슘(MgO)은 위에서 언급한 산화칼슘(CaO)과 유사한 역할을 할 수 있다.In addition, the raspberry ash may contain magnesium oxide (MgO). Magnesium oxide (MgO) can play a similar role to the calcium oxide (CaO) mentioned above.
또한, 산딸기나무 재는 실리카(SiO2) 성분을 함유할 수 있다. 실리카(SiO2) 성분에 의하면 유약의 점성을 높일 수 있고, 따라서 산딸기나무 재를 이용하여 유약을 제조하는 경우 별도로 규석(점성을 높일 수 있는 성분)을 첨가하지 않을 수 있다In addition, the raspberry ash may contain a silica (SiO2) component. According to the silica (SiO2) component, the viscosity of the glaze can be increased. Therefore, when the glaze is manufactured using raspberry ash, silica (a component that can increase the viscosity) may not be added separately.
또한, 산딸기나무 재는 산화인(P2O5)을 함유할 수 있다. 이를 이용하여 도자기용 유약을 제조하는 경우 부드러운 유백색이 발현되므로, 맑고 따뜻한 느낌을 발현할 수 있다. 산딸기나무 재를 도자기용 유약에 첨가하는 경우 유백 유약, 투명 유약에 적용할 수 있으며, 특히 유백 유약에 적용하는 것이 바람직하다. 다만, 반드시 이에 한정되는 것은 아니고 공지의 어떠한 유약에도 적용될 수 있다.In addition, raspberry ash may contain phosphorus oxide (P 2 O 5 ). When the glaze for porcelain is manufactured using this, a soft milky color is expressed, and thus a clear and warm feeling can be expressed. When raspberry ash is added to porcelain glaze, it can be applied to milky glaze and transparent glaze, particularly preferably to milky glaze. However, it is not necessarily limited thereto and may be applied to any known glaze.
통상의 도자기용 유약 원료에는 이 기술분야에서 널리 사용되는 도자기 유약 원료 성분이 모두 포함될 수 있으며, 구체적으로 장석과 도석, 백운석, 석회석, 규석, 고령토 및 이들의 혼합물로 이루어진 군으로부터 선택된 것을 포함할 수 있으나, 반드시 이에 제한되는 것은 아니다.Typical ceramic glaze raw materials may include all of the ceramic glaze raw materials widely used in this technical field, and specifically, may include those selected from the group consisting of feldspar and pottery, dolomite, limestone, silica, kaolin, and mixtures thereof. However, it is not necessarily limited thereto.
통상의 유약 원료의 성분 중 장석이나 도석의 알카리 성분은 유약 원료 중 규석 성분과 반응하며 유리질을 만드는 융제 역할을 하며, 석회석과 석회석의 일종인 백운석은 유약을 더 잘 녹게 하며 경도를 높게 하는 역할을 한다. 이들의 혼합 비율은 본 발명의 속하는 기술분야의 통상의 지식을 가진 자에게 자명한 것이다.Among the ingredients of ordinary glaze raw materials, feldspar or pottery's alkali component reacts with the silica stone component of the glaze raw material and acts as a flux to make glass, and limestone and dolomite, a kind of limestone, play a role in melting the glaze better and increasing the hardness. do. These mixing ratios are apparent to those of ordinary skill in the art to which the present invention belongs.
본 발명의 일 실시예에 따른 도자기용 유약 조성물은 산딸기나무 재 40∼70 중량% 및 통상의 유약 원료 30∼60중량%를 포함할 수 있다.The glaze composition for ceramics according to an embodiment of the present invention may include 40 to 70% by weight of raspberry wood and 30 to 60% by weight of conventional glaze raw materials.
또한, 본 발명의 일 실시예에 따른 도자기용 유약 조성물은 고령토, 점토, 탄산바륨, 도석, 활석, 백운석, 골회, 황토, 벤토 나이트, 산화동, 산화코발트, 산화망간, 산화니켈, 산화티타늄, 산화주석, 산화아연 등을 제조하고자 하는 유약의 종류에 따라 더 포함할 수 있다. 본 발명의 일 실시예에 따른 도자기용 유약 조성물은 도자기에 적용되는 경우 산화동, 산화코발트, 산화망간, 산화니켈, 산화티타늄, 산화주석 등의 발색 원료를 첨가하여 비취색, 올리브 그린색, 브라운 색 등을 나타낼 수 있다. In addition, the glaze composition for ceramics according to an embodiment of the present invention is kaolin, clay, barium carbonate, pottery stone, talc, dolomite, bone ash, loess, bentonite, copper oxide, cobalt oxide, manganese oxide, nickel oxide, titanium oxide, oxidation Tin, zinc oxide, etc. may be further included depending on the type of glaze to be manufactured. When the glaze composition for ceramics according to an embodiment of the present invention is applied to ceramics, a jade color, olive green color, brown color, etc. by adding color materials such as copper oxide, cobalt oxide, manganese oxide, nickel oxide, titanium oxide, tin oxide, etc. Can represent.
또한, 본 발명은 산딸기나무 재를 포함하는 도자기용 유약 조성물의 제조방법을 제공할 수 있다. 도자기용 유약 조성물의 제조방법은 산딸기나무 재를 준비하는 단계 및 산딸기나무 재와 통상의 유약 원료를 혼합하는 단계를 포함할 수 있다.In addition, the present invention can provide a method for producing a glaze composition for ceramics containing raspberry wood. The manufacturing method of the glaze composition for ceramics may include preparing raspberry ash and mixing raspberry ash and conventional glaze raw materials.
산딸기나무 재를 준비하는 단계는, 이 기술분야에서 이용되는 일반적인 방법으로 얻어질 수 있다. 예를 들면, 산딸기나무가 타고 남은 재를 물과 섞고 분쇄 과정을 거친 다음 체를 이용하여 재 이외의 이물질을 걸러 준다. 체로 걸러 낸 산딸기나무의 재가 침전되어 가라앉으면 침전된 재로부터 잿물을 분리해 내고(여러번 반복), 남아 있는 재를 건조시켜 분말 상태로 만들어 사용할 수 있다.The step of preparing raspberry ash can be obtained by a general method used in the art. For example, the ash remaining from the raspberry tree is mixed with water and pulverized, and then foreign substances other than the ash are filtered through a sieve. When the ashes of the raspberry tree filtered through a sieve settle and settle, the lye can be separated from the precipitated ash (repeated several times), and the remaining ash can be dried to form a powder.
이와 같이 제조된 산딸기나무 재를 통상의 유약 원료와 혼합하여 본 발명의 일 실시예에 따른 도자기용 유약 조성물을 제조할 수 있다.It is possible to prepare a glaze composition for ceramics according to an embodiment of the present invention by mixing the thus prepared raspberry ash with a conventional glaze raw material.
본 발명의 추가적인 해결수단은 아래에서 이어지는 설명에서 일부 설명될 것이고, 그 설명으로부터 부분적으로 용이하게 확인할 수 있게 되거나, 또는 본 발명의 실시에 의해 지득될 수 있다.Additional solutions of the present invention will be described in part in the description that follows below, and can be partially easily identified from the description, or can be learned by the practice of the present invention.
전술한 일반적인 설명 및 다음의 상세한 설명 모두는 단지 예시적이고 설명을 위한 것이며 청구범위에 기재된 본 발명을 제한하지 않는다.Both the foregoing general description and the following detailed description are illustrative and illustrative only and do not limit the invention described in the claims.
본 발명에 따른 산딸기나무 재를 포함하는 도자기용 유약 조성물은 고급스러운 자연미를 살릴 수 있으며, 청자 유약, 분청 투명 유약, 매트 유약, 이라보 유약, 천목 유약 등 각종 색 유약의 제조에 사용될 수 있다.The glaze composition for porcelain comprising raspberry wood according to the present invention can make use of luxurious natural beauty, and can be used in the manufacture of various color glazes such as celadon glaze, buncheong transparent glaze, matt glaze, irabo glaze, and cheonmok glaze.
도 1은 본 발명의 실시예1에 따라 환원분위기로 제조된 도자기 시험편이다.
도 2는 본 발명의 실시예2에 따라 환원분위기로 제조된 도자기 시험편이다.
1 is a ceramic test piece manufactured in a reducing atmosphere according to Example 1 of the present invention.
2 is a ceramic test piece manufactured in a reducing atmosphere according to Example 2 of the present invention.
이하, 첨부된 도면을 참조하여 본 발명의 구체적인 실시형태에 대하여 상세하게 서술하도록 한다. Hereinafter, specific embodiments of the present invention will be described in detail with reference to the accompanying drawings.
다만, 본 발명의 구체적 일 실시 형태를 설명함에 있어, 관련된 공지 기능 또는 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략한다.However, in describing a specific embodiment of the present invention, if it is determined that a detailed description of a related known function or configuration may unnecessarily obscure the subject matter of the present invention, the detailed description thereof will be omitted.
시험예: 산딸기나무 재 성분 분석Test Example: Analysis of raspberry ash components
아래의 표 1은 XRF로 분석한 산딸기나무 재의 성분분석표이다. 표 1을 참조하면, 산딸기나무 재를 XRF를 사용하여 성분 분석한 결과를 파악할 수 있다. Table 1 below is a component analysis table of raspberry ash analyzed by XRF. Referring to Table 1, the results of component analysis of raspberry ash using XRF can be identified.
산딸기나무 재는 산화칼슘(CaO) 및 산화마그네슘(MgO)을 포함할 수 있다. 산딸기나무재는 산화칼슘(CaO)을 56.98중량%, 산화마그네슘(MgO)을 22.37중량 % 포함할 수 있다. 산화칼슘(CaO)및 산화마그네슘(MgO)은 앞서 언급했듯이 유약의 조성물의 용융온도를 낮출 수 있고, 유약 조성물에 혼합된 여러 성분을 잘 혼합되게 하는 매용제의 역할을 할 수 있다.The raspberry ash may contain calcium oxide (CaO) and magnesium oxide (MgO). The raspberry wood may contain 56.98% by weight of calcium oxide (CaO) and 22.37% by weight of magnesium oxide (MgO). Calcium oxide (CaO) and magnesium oxide (MgO), as mentioned above, can lower the melting temperature of the composition of the glaze, and can act as a solvent to make the various components mixed in the glaze composition well mixed.
또한, 산딸기나무 재는 산화인(P2O5)을 포함할 수 있다. 산딸기나무재는 산화인(P2O5)을 약 8.89중량% 함유할 수 있다. 산화인(P2O5)은 앞서 언급했듯이, 유약을 맑고 따뜻한 느낌이 발현되도록 할 수 있고, 유약의 느낌을 부드럽게 할 수 있다. In addition, raspberry ash may contain phosphorus oxide (P 2 O 5 ). The raspberry wood may contain about 8.89% by weight of phosphorus oxide (P 2 O 5 ). Phosphorus oxide (P 2 O 5 ), as mentioned above, can make the glaze clear and warm and soften the glaze.
또한, 산딸기나무 재는 산화규소(SiO2)를 포함할 수 있다. 산딸기나무재는 산화규소(SiO2)를 5.17중량% 함유할 수 있다.In addition, the raspberry wood ash may contain silicon oxide (SiO 2 ). The raspberry wood may contain 5.17% by weight of silicon oxide (SiO 2 ).
또한, 산딸기나무 재는 기타 성분을 1.5중량% 함유할 수 있다. 기타 성분은 그 성분 함량이 작아 유약의 특징에 큰 영향을 미치지 않는 요소를 '기타'라는 하나의 카테고리로 묶은 것으로, MnO, BaO, TiO2, ZnO, SO3, Na2O, CuO, Pm2O3 를 포함할 수 있다.In addition, the raspberry ash may contain 1.5% by weight of other components. Other ingredients are elements that do not significantly affect the characteristics of the glaze due to their small content and are grouped into one category called'Others'. MnO , BaO, TiO 2 , ZnO, SO 3 , Na 2 O, CuO, Pm 2 It may contain O 3 .
성분ingredient CaO CaO MgO MgO P2O5 P 2 O 5 SiO2 SiO 2 K2OK 2 O Al2O3 Al 2 O 3 SrOSrO Fe2O3 Fe 2 O 3 기타Etc
단위(w t%)Unit (w t%) 56.9856.98 22.3722.37 8.898.89 5.175.17 2.32.3 1.421.42 0.760.76 0.610.61 1.51.5
실시예 1Example 1
산딸기나무 재를 장석, 흰색고령토 및 규석과 혼합하되, 아래 표 2에 나타난 성분들의 조성비(유약 조성물 전체중량을 기준으로 한 중량비율)에 따라 혼합하여 10가지 종류의 유약을 제조하였다. 도 1에 첨부된 시험편은 실시예 1에 따라 제조된 10가지의 유약을 10개의 초벌구이한 시험편들에 시유한 후 가마에 넣어 환원분위기로 1230℃ 내지 1250℃에서 8 시간 내지 10시간 동안 소성하는 과정을 거쳐 제조된다. The raspberry ash was mixed with feldspar, white kaolin, and silica stone, and 10 kinds of glaze were prepared by mixing according to the composition ratio of the ingredients shown in Table 2 below (weight ratio based on the total weight of the glaze composition). The test piece attached to FIG. 1 is a process in which 10 kinds of glazes prepared according to Example 1 are applied to 10 unglazed test pieces, and then put in a kiln and fired at 1230°C to 1250°C for 8 to 10 hours in a reducing atmosphere. It is manufactured through.
구분division 산딸기나무재Raspberry wood 장석feldspar 흰색고령토White kaolin 규석burr
1One 7070 1010 1010 1010
22 6060 1010 2020 1010
33 6060 2020 1010 1010
44 5050 1010 3030 1010
55 5050 2020 2020 1010
66 5050 3030 1010 1010
77 4040 1010 4040 1010
88 4040 2020 3030 1010
99 4040 3030 2020 1010
1010 4040 4040 1010 1010
도 1은 본 발명의 실시예1에 따라 환원분위기로 제조된 도자기 시험편이다. 1번에서 10번으로 갈수록 산딸기나무재의 함량은 점점 감소될 수 있다. 도 1의 1번 내지 10번의 도자기 시험편을 참조하여 산딸기나무 재의 함량비율 감소됨에 따른 유약의 색상 및 표면의 변화를 관찰해보면, 산딸기나무 재의 함량비율이 감소될수록 유약의 색상은 광택이 있는 밝은 녹색에서 광택이 점점 약해지고 녹색 또한 점점 옅어지는 것을 파악할 수 있다. 1 is a ceramic test piece manufactured in a reducing atmosphere according to Example 1 of the present invention. As you go from No. 1 to No. 10, the content of raspberry ash may gradually decrease. Referring to the porcelain specimens 1 to 10 of FIG. 1, the color of the glaze and the surface change according to the decrease in the content ratio of raspberry ash were observed. As the content ratio of raspberry ash decreases, the color of the glaze is bright green with gloss. You can see that the gloss is getting weaker and the green is also getting lighter.
또한, 시험편 7번을 참조하면, 다른 시험편과는 다른 황색 빛깔이 섞인 녹색인 것을 파악할 수 있다. 이는 후술하는 실시예2와 같이, 천목유와 혼합되어 진하고 어두운 가지색의 광택을 내는 유약이 될 수 있다.In addition, referring to test piece No. 7, it can be seen that the green color is mixed with a different yellow color from other test pieces. As in Example 2 to be described later, this may be a glaze that is mixed with natural wood oil to give a dark and dark eggplant color gloss.
실시예 2Example 2
실시예2는 실시예1의 7번 조성물과 종래의 천목유약을 절반씩 혼합한 유약을 10개의 초벌구이한 시험편들에 시유한 후 가마에 넣어 환원분위기로 1230℃ 내지 1250℃에서 8 시간 내지 10시간 동안 소성하는 과정을 거쳐 제조된다. 여기서, 실시예1과 다른 점은, 실시예1은 10개의 시험편이 모두 조성이 조금씩 다른 유약이 적용된 것이고, 실시예2는 10개의 시험편이 모두 같은 조성이다. In Example 2, the glaze obtained by mixing the composition 7 of Example 1 and the conventional cheonmok glaze in half was applied to 10 unglazed specimens and put in a kiln at 1230°C to 1250°C for 8 hours to 10 hours. It is manufactured through the process of firing during the process. Here, the difference from Example 1 is that in Example 1, all 10 test pieces were applied with a glaze slightly different in composition, and in Example 2, all 10 test pieces had the same composition.
도 2를 참조하면, 10개의 시험편이 서로 다른 색깔을 내는 것을 알 수 있다. 실시예2의 10개의 시험편은 각 시험편에 적용되는 온도의 차이에 의해 색깔 및 빛깔의 차이가 발생할 수 있다. 4번, 5번, 7번 및 8번은 가해지는 온도가 다른 것에 비해 높기 때문에, 진하고 어두운 푸른 빛깔의 가지색이 발현될 수 있다. 이 외 1번 내지 3번, 6번, 9번 및 10번은 가해지는 온도가 다른 것에 비해 낮기 때문에, 비교적 상기 푸른 빛깔의 가지색이 덜 발현될 수 있다.Referring to FIG. 2, it can be seen that 10 test pieces exhibit different colors. In the 10 test pieces of Example 2, differences in color and color may occur due to the difference in temperature applied to each test piece. 4, 5, 7 and 8 have a higher temperature than the others, so a dark and dark blue eggplant color can be expressed. In addition, since the temperature applied to Nos. 1 to 3, No. 6, No. 9, and No. 10 is lower than that of the others, the bluish eggplant color may be relatively less expressed.
가해지는 온도가 다른 이유는, 가마에 시편을 투입하여 소성할 때, 열원과의 거리 차이 때문일 수 있다. 4번, 5번, 7번 및 8번 시험편은 열원과의 거리가 가까워 1250℃ 내지 1300℃의 온도가 가해질 수 있고, 특히 7번 시험편의 경우 1300℃ 내지 1350℃의 온도가 가해질 수 있다. 도 2를 참조하면 높은 온도에서 소성될수록 진하고 어두운 푸른 빛깔의 가지색이 발현됨을 파악할 수 있다.The reason why the applied temperature is different may be due to the difference in distance from the heat source when the specimen is put into a kiln and fired. Specimens 4, 5, 7 and 8 may be subjected to a temperature of 1250°C to 1300°C because the distance to the heat source is close, and in particular, in the case of the 7th test piece, a temperature of 1300°C to 1350°C may be applied. Referring to FIG. 2, it can be seen that as the sintering at a higher temperature is performed, a dark and dark blue multicolored color is expressed.
여기서, 종래의 천목유약은 천목유약 전체 중량을 기준으로 장석 50중량%, 카오린 10 내지 15중량%, 규석 10중량%, 활석 5중량%, 참나무재 10중량% 및 철(Fe) 10 내지 15중량%를 함유할 수 있다. Here, the conventional cheonmok glaze is 50% by weight of feldspar, 10 to 15% by weight of kaolin, 10% by weight of silica, 5% by weight of talc, 10% by weight of oak wood and 10 to 15% by weight of iron (Fe) based on the total weight of the cheonmok glaze %.
즉, 실시예2 조성물은 실시예2조성물 전체 중량을 기준으로 실시예1 7번 조성물 50중량% 및 천목유약 50중량%를 포함할 수 있다. 결과적으로, 산딸기나무재 20중량%, 장석 5중량%, 흰색고령토 20중량%, 규석 5중량% 및 장석 25중량%, 카오린 5내지 7.5중량%, 규석 5중량%, 활석 2.5중량%, 참나무재 5중량%, 철 5내지 7.5중량%를 함유할 수 있다. That is, the Example 2 composition may include 50% by weight of the composition No. 7 of Example 1 and 50% by weight of Cheonmok glaze based on the total weight of the Example 2 composition. As a result, 20% by weight of raspberry wood, 5% by weight of feldspar, 20% by weight of white kaolin, 5% by weight of silica and 25% by weight of feldspar, 5 to 7.5% by weight of kaolin, 5% by weight of silica, 2.5% by weight of talc, oak ash It may contain 5% by weight and 5 to 7.5% by weight of iron.
정리하면, 산딸기나무재 20중량%, 장석 5중량%, 흰색고령토 20중량%, 규석 10중량% 및 장석 25중량%, 카오린 5내지 7.5중량%, 활석 2.5중량%, 참나무재 5중량%, 철 5내지 7.5중량%를 함유할 수 있다.In summary, 20 wt% raspberry wood, 5 wt% feldspar, 20 wt% white kaolin, 10 wt% silica and 25 wt% feldspar, 5 to 7.5 wt% kaolin, 2.5 wt% talc, 5 wt% oak wood, iron It may contain 5 to 7.5% by weight.
이와 같이, 진하고 어두운 푸른 빛깔의 가지색을 띠는 고급스러운 느낌을 발현하고자 할 때 본 발명의 실시예2에 따른 유약 조성물을 사용할 수 있고, 목표하는 느낌에 따라 열원과의 거리를 적절히 조절하여 소성할 수 있다.In this way, when trying to express a luxurious feeling of a dark blue hue, the glaze composition according to Example 2 of the present invention can be used, and the distance to the heat source can be appropriately adjusted according to the desired feeling to be fired. I can.
본 실시예는 본 발명의 기술적 사상을 예시적으로 설명한 것에 불과하고, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 본 실시예의 다양한 수정 및 변형이 가능할 것이다. 본 실시예는 본 발명의 기술적 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 따라서 본 실시예에 의하여 본 발명의 권리범위가 한정되는 것은 아니다. 본 발명의 보호범위는 청구범위에 의하여 해석되어야 하며, 그와 동등하거나 균등하다고 인정되는 모든 기술적 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 한다.This embodiment is merely illustrative of the technical idea of the present invention, and those skilled in the art to which the present invention pertains may have various modifications and variations of this embodiment without departing from the essential characteristics of the present invention. It will be possible. This embodiment is not intended to limit the technical spirit of the present invention but to explain it, and accordingly, the scope of the present invention is not limited by the present embodiment. The scope of protection of the present invention should be interpreted by the claims, and all technical ideas recognized as equivalent or equivalent should be interpreted as being included in the scope of the present invention.

Claims (6)

  1. 산딸기나무를 태운 재의 분말인 산딸기나무 재; 및
    장석, 흰색고령토 및 규석을 포함하는 유약원료를 포함하고,
    유약 조성물 전체 중량을 기준으로 상기 산딸기나무 재는 40중량%, 상기 장석은 10중량%, 상기 흰색고령토는 40중량%, 상기 규석은 10중량%이며,
    상기 산딸기나무 재는 상기 산딸기나무 재 전체 중량을 기준으로 산화칼슘(CaO) 56.98중량%, 산화마그네슘(MgO) 22.37중량%, 산화인(P2O5) 8.89중량%, 산화규소(SiO2) 5.17중량%, 산화칼륨(K2O) 2.3중량%, 산화알루미늄(Al2O3) 1.42중량%, 산화스트론튬(SrO) 0.76중량% 및 산화철(Fe2O3) 0.61중량%를 포함하고,
    도자기에 적용되었을 때 황색 빛깔이 섞인 녹색 계열의 빛깔이 발현되는 것을 특징으로 하는 산딸기나무 재를 포함하는 도자기용 유약 조성물.
    Raspberry ash, a powder of ashes from raspberry trees; And
    Contains glaze raw materials including feldspar, white kaolin, and silica,
    Based on the total weight of the glaze composition, the raspberry ash is 40% by weight, the feldspar is 10% by weight, the white kaolin is 40% by weight, and the silica stone is 10% by weight,
    The raspberry ash is calcium oxide (CaO) 56.98 wt%, magnesium oxide (MgO) 22.37 wt%, phosphorus oxide (P 2 O 5 ) 8.89 wt%, silicon oxide (SiO 2 ) 5.17 based on the total weight of the raspberry tree ash Wt%, potassium oxide (K 2 O) 2.3 wt%, aluminum oxide (Al 2 O 3 ) 1.42 wt%, strontium oxide (SrO) 0.76 wt%, and iron oxide (Fe 2 O 3 ) 0.61 wt%,
    A glaze composition for ceramics comprising raspberry wood, characterized in that a greenish hue mixed with a yellow hue is expressed when applied to ceramics.
  2. 삭제delete
  3. 삭제delete
  4. 산딸기나무 재 40중량%, 장석 10중량%, 흰색고령토 40중량% 및 규석 10중량%로 이루어진 산딸기나무 재를 포함하는 유약 50중량%; 및
    장석 50중량%, 카오린 10 내지 15중량%, 규석 10중량%, 활석 5중량%, 참나무재 10중량% 및 철(Fe) 10 내지 15중량%를 포함하는 천목유약 50중량%를 포함하고,
    상기 산딸기나무 재는 상기 산딸기나무 재 전체 중량을 기준으로 산화칼슘(CaO) 56.98중량%, 산화마그네슘(MgO) 22.37중량%, 산화인(P2O5) 8.89중량%, 산화규소(SiO2) 5.17중량%, 산화칼륨(K2O) 2.3중량%, 산화알루미늄(Al2O3) 1.42중량%, 산화스트론튬(SrO) 0.76중량% 및 산화철(Fe2O3) 0.61중량%를 포함하며,
    1350℃의 온도로 소성되는 도자기에 적용되었을 때, 진하고 어두운 푸른 빛깔이 발현되는 것을 특징으로 하는 산딸기나무 재를 포함하는 도자기용 유약 조성물.
    50% by weight of glaze containing raspberry ash consisting of 40% by weight of raspberry ash, 10% by weight of feldspar, 40% by weight of white kaolin, and 10% by weight of silicate; And
    Feldspar 50% by weight, kaolin 10 to 15% by weight, silicate 10% by weight, talc 5% by weight, oak wood 10% by weight, and iron (Fe) 10 to 15% by weight containing 50% by weight,
    The raspberry ash is calcium oxide (CaO) 56.98 wt%, magnesium oxide (MgO) 22.37 wt%, phosphorus oxide (P 2 O 5 ) 8.89 wt%, silicon oxide (SiO 2 ) 5.17 based on the total weight of the raspberry tree ash Wt%, potassium oxide (K 2 O) 2.3 wt%, aluminum oxide (Al 2 O 3 ) 1.42 wt%, strontium oxide (SrO) 0.76 wt% and iron oxide (Fe 2 O 3 ) 0.61 wt%,
    When applied to ceramics fired at a temperature of 1350° C., a dark and dark blue hue is expressed. A glaze composition for ceramics comprising raspberry wood ash.
  5. 삭제delete
  6. 삭제delete
KR1020180122879A 2018-10-16 2018-10-16 Glace Composition for Ceramic Ware Comprising Ashes from Hawthorn-like raspberry and Preparation Method thereof KR102138702B1 (en)