KR20190141562A - Method for injecting aryl based monomer in mold for manufacturing optical material - Google Patents

Method for injecting aryl based monomer in mold for manufacturing optical material Download PDF

Info

Publication number
KR20190141562A
KR20190141562A KR1020180137354A KR20180137354A KR20190141562A KR 20190141562 A KR20190141562 A KR 20190141562A KR 1020180137354 A KR1020180137354 A KR 1020180137354A KR 20180137354 A KR20180137354 A KR 20180137354A KR 20190141562 A KR20190141562 A KR 20190141562A
Authority
KR
South Korea
Prior art keywords
mold
injection
monomer
aryl
optical material
Prior art date
Application number
KR1020180137354A
Other languages
Korean (ko)
Inventor
장동규
김준섭
Original Assignee
주식회사 케이오씨솔루션
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 케이오씨솔루션 filed Critical 주식회사 케이오씨솔루션
Priority to PCT/KR2019/004847 priority Critical patent/WO2019240370A1/en
Publication of KR20190141562A publication Critical patent/KR20190141562A/en

Abstract

The present invention relates to a method of manufacturing an optical material by injecting aryl based monomer solution into a cavity formed between a pair of molds whose outside is sealed and, more specifically, to an automatic mold injection method of a monomer for an aryl based optical material, which enables a quantitative injection in a short time period by using a vision recognition system while injecting aryl based monomer solution into the cavity. The automatic mold injection method of a monomer for an aryl based optical material includes: a step (a) of preparing a monomer composition for an aryl based optical material having a solid phase refractive index of 1.537 to 1.585 and a viscosity of 20 to 800 cps (25°C); a step (b) of mostly injecting the monomer composition into a cavity formed between a pair of molds whose outside is sealed; and a step (c) of finishing an injection of the monomer composition when an oil level is detected at a set final injection point set by sensing the oil level using the vision recognition system while injecting the monomer composition into the cavity after the step (b). According to the present invention, the monomer solution for an aryl based optical material can be automatically injected into the mold in a quantitative manner so as not to lack or overflow.

Description

아릴계 광학재료용 모노머의 몰드 자동 주입방법 {Method for injecting aryl based monomer in mold for manufacturing optical material}Method for automatic injection of monomer for aryl optical material {Method for injecting aryl based monomer in mold for manufacturing optical material}

본 발명은 외곽이 실링된 1쌍의 몰드 사이에 형성된 캐비티 내에 아릴계 모노머 용액을 주입하여 광학재료를 제조하는 방법에 관한 것으로, 보다 상세하게는 아릴계 모노머 용액을 상기 캐비티 내에 주입하면서 비전인식시스템을 사용하여 단시간 내에 정량주입이 가능하도록 한 아릴계 광학재료용 모노머의 몰드 자동 주입방법에 관한 것이다.The present invention relates to a method of manufacturing an optical material by injecting an aryl monomer solution into a cavity formed between a pair of molds having an outer seal, and more particularly, a vision recognition system while injecting an aryl monomer solution into the cavity. The present invention relates to a method for automatically injecting a mold for an aryl optical material monomer to enable a quantitative injection within a short time.

광학재료에서 플라스틱 렌즈는 유리 렌즈보다 가볍고 잘 깨지지 않으며 가공성이 좋다는 장점이 있어 근래에는 유리 렌즈보다 플라스틱 렌즈를 많이 사용하는 추세이다. 이러한 플라스틱 렌즈는 모노머(monomer)라고 하는 고분자 화합물을 몰드에 주입하여 굳힌 후 적당한 후가공을 통해 제작된다. 즉, 렌즈모양의 빈 주입공간(캐비티)을 갖는 몰드에 모노머 용액을 주입하는 방식으로 제작되는 것이다.In optical materials, plastic lenses are lighter than glass lenses, do not break easily, and have good workability. Therefore, plastic lenses are used more recently than glass lenses. Such a plastic lens is manufactured by injecting a polymer compound called a monomer into a mold and hardening it, followed by appropriate post-processing. That is, the monomer solution is manufactured by injecting a monomer solution into a mold having a lens-shaped empty injection space (cavity).

이에 관련된 종래기술로서 특허문헌 1의 '안경렌즈 제조용 몰드의 이동거리 셋팅장치'가 개시되어 있다.As a related art, Patent Document 1 discloses a 'moving distance setting device of a mold for manufacturing an eyeglass lens'.

상기 특허문헌 1은 안경렌즈 제조용 유리몰드의 이격거리를 정확하게 결정하기 위하여 몰드 척을 이용해 유리몰드를 서로 이격시켜 배치한 상태로, 유리몰드의 외주면에 테이프를 접착하고 테이핑 작업이 완료된 유리몰드에 모노머 용액을 수작업으로 주입하는 방식이 소개되어 있다.Patent Document 1 is a state in which the glass molds are spaced apart from each other using a mold chuck in order to accurately determine the separation distance of the glass mold for manufacturing the spectacle lens, the adhesive is taped to the outer peripheral surface of the glass mold and the monomer on the glass mold is completed The method of injecting the solution manually is introduced.

그런데 특허문헌 1에 개시된 바와 같은 유리몰드 내에 모노머를 수작업으로 주입하는 기술은, 전적으로 주입자의 숙련된 정도에 의존하는 것이므로 숙련도에 따라 불량이 발생할 수 있고 작업효율이 떨어지는 문제가 있다. 특히, 모노머를 매번 일정량으로 정밀 주입하는 것은 많은 숙련이 요구되므로, 미숙련자의 경우 몰드 내부에 기포가 발생할 수 있는 문제가 있다.By the way, since the technique of manually injecting the monomer into the glass mold as disclosed in Patent Document 1 depends entirely on the degree of skill of the injector, defects may occur depending on the level of skill and the work efficiency is inferior. In particular, precisely injecting a monomer in a predetermined amount every time requires a lot of skill, there is a problem that bubbles may occur in the mold in the case of unskilled people.

또한, 액상의 모노머는 인체에 유해한 휘발성 기체를 발생하므로, 오랫동안 작업할 경우 작업자의 건강에 나쁜 영향을 미칠 수 있다. In addition, the liquid monomer generates a volatile gas harmful to the human body, it may adversely affect the health of the operator when working for a long time.

아릴계 광학소재는 중굴절률 범위의 안경렌즈를 저렴하게 제조할 수 있고 중합수율이 좋다는 장점이 있다. 아릴계 광학렌즈는 주로 아릴기를 주성분으로 하는 디에틸렌글리콜 비스아릴카르보네이트와 다가알코올을 부가한 디아릴에스테르 화합물에 디아릴이소프탈레이트 등을 혼합하고 열 경화시켜서 제조한다. An aryl optical material has an advantage of being able to manufacture a spectacle lens in the medium refractive index at a low cost and having a good polymerization yield. An aryl optical lens is prepared by mixing a diaryl isophthalate or the like with a diaryl ester compound containing a diethylene glycol bisaryl carbonate mainly containing an aryl group and a polyhydric alcohol, followed by heat curing.

한국 공개특허 제10-2005-0029275호에서는 벤질알코올, 프로판올 등의 알코올 화합물과 다가알코올을 부가한 디아릴에스테르 화합물, 디아릴이소프탈레이트, 디에틸렌글리콜비스아릴카르보네이트, 디벤질말리에이트 등을 혼합 사용하여 380∼400㎚까지의 장파장의 자외선을 차단하는 광학렌즈를 제조하고 있다. 이렇게 제조된 아릴계 광학렌즈는 아닐링 과정에서의 황변 현상, 비반응성 알코올로 인한 렌즈의 미경화 및 이로 인한 내 스크레칭성 저하, 저장 중의 색상변화 등의 문제가 있다. In Korean Patent Laid-Open No. 10-2005-0029275, alcohol compounds such as benzyl alcohol and propanol and diaryl ester compounds to which polyhydric alcohols are added, diaryl isophthalate, diethylene glycol bis aryl carbonate, dibenzyl maleate, etc. The optical lens which mixes and blocks the ultraviolet-ray of long wavelength from 380-400 nm is manufactured. The aryl optical lens thus prepared has problems such as yellowing in the annealing process, uncured lens due to non-reactive alcohol, deterioration of scratch resistance, and color change during storage.

이러한 문제를 해결하기 위하여 한국 등록특허 제10-0897407호에서는 알킬렌글리콜 비스아릴카르보네이트 및 말레이트 화합물 중에서 선택된 1종 또는 2종 이상의 화합물(성분A)과 디아릴에스테르 화합물(성분B), 자외선 흡수제 및 황변현상을 막기 위한 인산에스테르를 포함하는 자외선 차단 광학렌즈용 조성물을 개시하고 있다. 400㎚ 장파장까지 자외선을 차단하면서 아닐링 후의 황변을 막아 무색 투명하고, 내광성, 광투과율, 성형성, 가공성, 내열성이 좋은 렌즈를 제공하고 있다. In order to solve this problem, Korean Patent No. 10-0897407 discloses one or two or more compounds (component A) and a diaryl ester compound (component B) selected from alkylene glycol bisaryl carbonate and maleate compounds. Disclosed is a composition for UV-blocking optical lenses comprising a ultraviolet absorber and a phosphate ester for preventing yellowing. It provides a lens which is colorless and transparent and has good light resistance, light transmittance, moldability, processability and heat resistance by blocking ultraviolet rays after annealing while blocking ultraviolet rays up to 400 nm long wavelength.

모든 광학렌즈 분야에서 생산비 절감은 주요 관심사의 하나이다. 아릴계 렌즈는 생산비가 저렴한 편이나 사람의 손을 거치지 않고 자동 생산설비 내에서 자동 주입이 가능할 경우 더욱 생산비를 낮출 수 있고, 생산성 향상은 물론 생산과정에서의 인체 유해성 문제도 해소될 수 있다. 그러나 많은 시도에도 불구하고 아직까지 주입 자동화는 어려운 실정이다. 여기에는 모노머 조성물의 조성에 따른 점도 및 가사시간의 차이도 원인이 되고 있다. Reducing production costs is a major concern for all optical lens applications. The aryl-based lens is low in production cost, but if the automatic injection in the automatic production facility without going through the human hand can further reduce the production cost, and can improve the productivity as well as the problem of human hazards in the production process. However, despite many attempts, automation of injection is still difficult. This also causes a difference in viscosity and pot life in accordance with the composition of the monomer composition.

특허문헌 2(한국등록특허 제10-1383132호)에는 '안경 렌즈용 모노머 자동 주입장비 및 이를 이용한 안경렌즈 생산방법'이 개시되어 있다. 특허문헌 2에서는 1쌍의 몰드가 형성하는 캐비티 내부에 모노머 용액을 주입하는 단계에서 렌즈몰드의 위치를 감지하는 변위센서(레이저 센서)를 사용하는 것에 의해 렌즈몰드의 위치를 파악하고, 제2이동부에 의해 렌즈몰드에 채워지는 원료의 수위를 감지하도록 되어 있으며, 주입노즐의 모노머 주입량은 주입량조절부에 의해 조절되도록 하되, 모노머가 일정 수위에 도달하면 모노머가 주입되는 양을 1단계인 5mm와 2단계인 10mm로 조절하도록 되어 있다. Patent Document 2 (Korean Patent No. 10-1383132) discloses a monomer auto-injection equipment for eyeglass lenses and a method for producing eyeglass lenses using the same. In patent document 2, the position of a lens mold is grasped | ascertained by using the displacement sensor (laser sensor) which detects the position of a lens mold in the step of injecting a monomer solution into the cavity formed by a pair of mold, and the 2nd movement It is to detect the water level of the raw material to be filled in the lens mold by the unit, and the injection amount of the monomer of the injection nozzle is to be controlled by the injection amount adjusting unit, but when the monomer reaches a certain level, the amount of monomer injected is 5mm and 1 step It is adjusted to 10mm which is 2 steps.

그러나 특허문헌 2에서와 같이 변위센서를 사용하여 원료(모노머 조성물)의 수위를 감지하는 경우, 모노머 조성물은 물보다 점성이 높아 수위의 변화가 수평적인 변화가 아닌 2차원적인 좌우 대칭형의 포물선형을 이루게 되므로 실시간으로 수위를 정확하게 감지하기가 곤란하게 되는 문제점이 있었으며, 이로 인해 주입량의 단계적 조절에도 불구하고 정확한 양으로 주입하는 것이 어려워 주입량이 부족하거나 주입량이 과도하게 되어 제품 불량으로 이어지거나 넘쳐흐른 모노머 조성물로 인해 주입장비가 오염될 수 있었다.However, when detecting the water level of the raw material (monomer composition) using a displacement sensor as in Patent Document 2, the monomer composition is more viscous than water, so that the change in the water level is not a horizontal change but a two-dimensional symmetrical parabola. As a result, it was difficult to accurately detect the water level in real time, which made it difficult to inject the correct amount despite the stepwise adjustment of the injection amount, resulting in insufficient injection amount or excessive injection amount, leading to product defects or overflowing monomers. The composition could contaminate the injection equipment.

또, 특허문헌 3(일본등록특허 제3707189호)의 '플라스틱 제품 제조 방법 및 제조장치'에서는 플라스틱 렌즈 제조과정에서 성형용 몰드에 플라스틱 원액을 주입하는 공정을 자동화하기 위한 방법으로, 캐비티 내측의 제1,2벽부 사이의 폭을 계측하여 제1유량 및 제1시간을 설정하고, 캐비티에 제1유량으로 제1시간동안 플라스틱 원액을 주입하는 제1공정과, 제1공정에 이어 캐비티에 제1유량보다 적은 제2유량으로 플라스틱 원액을 주입하는 제2공정을 가지도록 하여 소정의 시간만 대유량으로 원액을 주입하고 그 후, 주입 종료를 향하여는 소유량으로 원액을 주입함으로써 주입 시간을 단축함과 동시에 누출량을 줄일 수 있도록 하고 있다. In addition, `` Plastic product manufacturing method and manufacturing apparatus '' of Patent Document 3 (Japanese Patent No. 3707189) is a method for automating the process of injecting a plastic stock solution into a molding mold during a plastic lens manufacturing process. The first flow rate and the first time are set by measuring the width between the first and second wall portions, and the first step of injecting the plastic stock solution for the first time at the first flow rate into the cavity; and the first step following the first step. It has a second process of injecting the plastic stock solution at a second flow rate less than the flow rate so as to inject the stock solution at a large flow rate only for a predetermined time, and then, after the injection of the stock solution at a small flow rate toward the end of the injection, At the same time, the amount of leakage can be reduced.

그러나 특허문헌 3에 의한 주입방법에서는 캐비티 내부의 공간적인 특성을 감안하여 플라스틱 원료의 주입량과 주입시간을 단계적으로 감소시키는 것에 의해 주입시간의 단축과 누출량을 줄일 수 있도록 하고 있으나, 모노머를 몰드에 주입 시 점성이 높은 모노머 용액의 유면 변화 특성을 감안하지 않음으로써 여전히 누출 불량이 발생하고 정량 주입이 어려운 단점이 있다.However, in the injection method according to Patent Document 3, it is possible to shorten the injection time and reduce the leakage amount by gradually reducing the injection amount and injection time of the plastic raw material in consideration of the spatial characteristics inside the cavity, but the monomer is injected into the mold By not considering the oil level change characteristics of the highly viscous monomer solution, there are still disadvantages in that the leakage is poor and the metering is difficult.

특허문헌 4(일본공개특허 제2007-80766호)의 '플라스틱 렌즈의 성형방법'에서는 마치 술잔을 기울여서 술을 따르는 것과 같은 방식으로 액상 성형 재료를 몰드 내부에 주입할 때 내부에 최대한 거품을 남겨두지 않고 충전시킬 수 있도록 초기에는 주입구가 상방 정중앙에서 약간 일측으로 벗어난 상태가 되도록 하여 주입을 시작하고, 어느 정도 주입이 진행되면 몰드를 회전시켜(기울여) 주입구가 상방 정중앙에 위치하도록 하여 원료 모노머를 충전하도록 한 플라스틱 렌즈의 성형방법이 개시되어 있다.In `` Plastic Lens Molding Method '' of Patent Document 4 (Japanese Patent Laid-Open No. 2007-80766), bubbles are not left as much as possible when injecting the liquid molding material into the mold in the same manner as pouring a glass by tilting a glass. Initially, the inlet is deviated to one side from the upper center in the middle so that it can be filled without filling, and when the injection is proceeded to some extent, the mold is rotated (tilt) so that the inlet is located in the upper center of gravity to fill the raw monomer. A molding method of a plastic lens is disclosed.

그러나 특허문헌 4는 거품이 잔류하지 않도록 원료를 주입하기에는 적합한 방법이나, 원료를 정확한 양만큼 주입하는 데는 여전히 어려움이 있었다.However, Patent Document 4 is a suitable method for injecting the raw material so that bubbles do not remain, but it was still difficult to inject the raw material in the correct amount.

1. 대한민국 등록실용신안 제20-0236704호1. Republic of Korea Utility Model Registration No. 20-0236704 2. 대한민국 등록특허 제10-1383132호2. Republic of Korea Patent No. 10-1383132 3. 일본 등록특허 제3707189호3. Japanese Patent No. 3707189 4. 일본공개특허 제2007-80766호4. Japanese Patent Application Publication No. 2007-80766 5. 대한민국 공개특허 제10-2005-0029275호5. Republic of Korea Patent Publication No. 10-2005-0029275 6. 대한민국 등록특허 제10-0897407호6. Republic of Korea Patent No. 10-0897407

상기와 같이 많은 선행기술에서 광학재료용 모노머를 몰드에 자동 주입하기 위한 방법을 제시하고 있으나, 모두 모노머를 넘치거나 부족하지 않게 정확한 양으로 주입하는데 어려움이 있다. 또, 각각의 모노머마다 경화속도 및 경화시간의 차이, 점성의 차이, 유면의 차이, 같은 계열의 모노머에서도 조성에 따른 차이가 있어, 단순히 주입량이나 속도를 단계적으로 조절하는 기계적인 방법으로는 모노머에 따른 차이에 대응할 수 없어 정확한 주입이 어려운 문제가 있다. As described above, many prior arts propose a method for automatically injecting a monomer for an optical material into a mold, but all have difficulty in injecting the monomer in an accurate amount without overflowing or shortening the monomer. In addition, each monomer has a difference in curing rate, curing time, difference in viscosity, difference in oil level, and composition in the same series of monomers. There is a problem that can not cope with the difference according to the exact injection.

본 발명은 상기한 문제를 해결하기 위하여 안출된 것으로, 본 발명의 목적은 주입량 부족이나 주입량 과다 없이 아릴계 광학재료용 모노머 조성물을 몰드에 정확하게 주입할 수 있는 아릴계 광학재료용 모노머의 몰드 자동 주입방법을 제공하는 것이다.The present invention has been made to solve the above problems, an object of the present invention is to automatically inject the mold of the monomer for aryl optical material that can accurately inject the monomer composition for the aryl optical material into the mold without insufficient injection amount or excessive injection amount To provide a way.

특히, 본 발명은 아릴계 광학재료용 모노머 조성물을 몰드의 캐비티에 2단계로 나누어 주입하면서, 1번째 단계에서 대부분을 주입하고 이어서 2번째 단계에서는 비전인식시스템을 사용하여 아릴계 모노머 용액의 유면을 감지하여 최종 주입지점에 유면이 감지되면 주입을 중지함으로써 주입하는 시간을 단축할 수 있으면서도 모노머 용액이 넘치거나 부족하지 않도록 정량 주입할 수 있는 아릴계 광학재료용 모노머의 몰드 자동 주입방법을 제공하는데 그 목적이 있다. In particular, the present invention injects the monomer composition for the aryl optical material divided into the cavity of the mold in two stages, the majority of the first stage is injected, and then in the second stage, the oil level of the aryl monomer solution using a vision recognition system It provides an automatic mold injection method of monomer for aryl optical materials that can detect the oil level at the final injection point and stop the injection to shorten the injection time and quantify the monomer solution so that it does not overflow or run short. There is a purpose.

상기의 목적을 달성하기 위하여 본 발명은,In order to achieve the above object, the present invention,

외곽이 실링된 1쌍의 몰드 사이에 형성된 캐비티 내에 아릴계 광학재료용 모노머 조성물을 주입하는 방법으로서,A method of injecting a monomer composition for an aryl optical material into a cavity formed between a pair of molds having an outer seal,

(a) 고상 굴절률 1.537-1.585, 점도 20~800cps(25℃)의 아릴계 광학재료용 모노머 조성물을 준비하는 단계;(a) preparing a monomer composition for an aryl optical material having a solid refractive index of 1.537 to 1.585 and a viscosity of 20 to 800 cps (25 ° C);

(b) 상기 모노머 조성물을 상기 캐비티 내에 대부분 주입하는 단계;(b) injecting most of said monomer composition into said cavity;

(c) 상기 (b)단계에 이어서 모노머 조성물을 캐비티 내로 주입하면서 비전인식시스템을 사용하여 유면을 감지하여 설정된 최종 주입지점에 유면이 감지되면 모노머 조성물의 주입을 종료하는 단계;를 포함하는, 아릴계 광학재료용 모노머의 몰드 자동 주입방법을 제공한다.(c) following the step (b) following the step of injecting the monomer composition into the cavity by using a vision recognition system to detect the oil level and the end of the injection of the monomer composition when the oil surface is detected at the final injection point; aryl comprising; Provided is a method for automatically injecting a mold for a system optical material.

상기 단계 (b)는 미리 설정된 중량 또는 부피만큼 상기 모노머 조성물을 상기 캐비티 내에 주입하거나, 또는 비전인식시스템을 사용하여 몰드 내에 미리 설정된 영역까지 주입할 수 있다. In step (b), the monomer composition may be injected into the cavity by a predetermined weight or volume, or may be injected to a predetermined area in the mold using a vision recognition system.

상기 비전인식시스템은 몰드의 윤곽과 상기 몰드에 주입되는 모노머 용액의 유면을 촬영하되, 몰드가 주입위치에 세팅된 상태를 감지하기 위하여 상기 몰드 윤곽 일부에 위치하는 제1영역과, 상기 몰드 외측에 위치한 제2영역을 설정할 수 있다. The vision recognition system photographs the contour of the mold and the oil level of the monomer solution injected into the mold, wherein the first region is located at a part of the mold contour to detect a state in which the mold is set at the injection position, and outside the mold. The second area located may be set.

상기와 같이 제1,2영역이 설정된 비전인식시스템은, 바람직하게는 콘트롤러가 상기 제1영역에서 몰드의 윤곽이 감지되면 설정된 제1주입압력으로 모노머 용액의 대부분을 몰드 내부에 주입한 후, 이어서 상기 제1주입압력보다 낮은 압력으로 잔량의 모노머 용액을 주입하면서 제2영역에서 유면이 감지되면 모노머 용액의 주입을 종료한다.In the vision recognition system in which the first and second regions are set as described above, the controller injects most of the monomer solution into the mold at the first injection pressure, when the controller detects the contour of the mold in the first region. If the oil level is detected in the second region while injecting the residual amount of the monomer solution at a pressure lower than the first injection pressure, the injection of the monomer solution is terminated.

상기 제1,2영역에서는 몰드의 윤곽 및 모노머 용액의 유면을 바람직하게는 화소수의 변화에 의해 감지한다. In the first and second regions, the contour of the mold and the oil level of the monomer solution are detected by the change in the number of pixels.

본 발명의 바람직한 실시예에서, 상기 제1영역에는 원호 형태로 가상 윤곽이 표시되고, 상기 제1영역에서 몰드 윤곽의 감지시 촬영된 몰드의 윤곽이 상기 가상 윤곽에 일치되도록 촬영위치 조정이 이루어지며, 상기 제1영역의 위치변화에 따라 제2영역의 위치가 함께 이동되어 유면 변화를 감지한다.In a preferred embodiment of the present invention, the virtual contour is displayed in the form of an arc in the first region, the photographing position is adjusted so that the contour of the mold photographed when the mold contour in the first region is matched with the virtual contour. As the position of the first region changes, the position of the second region is moved together to detect a change in oil level.

바람직한 실시예에서, 상기 제1영역은 몰드의 외곽 중 대각선 방향 즉, 몰드의 X방향 정보와 Y방향 정보를 모두 갖는 위치를 의미하는 것으로, 몰드를 주입위치로 안치시 몰드의 위치변화를 파악하기 위한 부분이고, 상기 제1영역은 제2영역의 위치 이동의 기준이 되며, 제1영역에서는 몰드가 주입위치에 안착되면 몰드의 윤곽을 곧바로 감지하게 된다.In a preferred embodiment, the first region means a position having both diagonal direction information, that is, the X direction information and the Y direction information of the mold, and the position change of the mold when the mold is placed as an injection position. The first region serves as a reference for the positional movement of the second region. In the first region, the contour of the mold is immediately detected when the mold is seated at the injection position.

바람직한 실시예에서, 상기 제2영역은 몰드 내부의 캐비티에 기포없이 모노머 용액을 가득 채우기 위해 몰드의 모노머 주입구에서 가까운 위치의 외부에 설정되어 있으며, 대체로 몰드 윤곽으로부터 1~2mm 이내의 위치에 설치된다.In a preferred embodiment, the second region is set outside of a position close to the monomer inlet of the mold to fill the monomer solution without bubbles in the cavity inside the mold, and is generally installed at a position within 1 to 2 mm from the mold contour. .

바람직한 실시예에서, 상기 콘트롤러는 시린지에 1차 주입된 모노머 용액을 몰드 내부에 주입할 때 모노머 용액의 70~99%를 높은 압력 즉, 빠른 속도로 주입하고, 나머지 잔량을 낮은 압력으로 서서히 주입하도록 시린지 구동부를 제어한다.In a preferred embodiment, the controller is to inject 70 ~ 99% of the monomer solution at a high pressure, that is, at a high speed when the first injection of the monomer solution injected into the syringe into the mold, and to slowly inject the remaining amount at a low pressure Control the syringe drive.

바람직하게는, 상기 아릴계 광학재료용 모노머 조성물은 알킬렌글리콜 비스아릴카르보네이트 및 말레이트 화합물 중에서 선택된 1종 이상의 화합물인 성분A와 아래 화학식 1로 표시되는 디아릴에스테르 화합물인 성분B를 포함한다.Preferably, the monomer composition for an aryl optical material includes component A which is at least one compound selected from alkylene glycol bisaryl carbonate and maleate compound and component B which is a diaryl ester compound represented by Formula 1 below. do.

[화학식 1][Formula 1]

Figure pat00001
Figure pat00001

(여기에서 R1은 수소원자 또는 메틸기를 나타내고, OR2 은 탄소수가 1∼5인 2가 알코올 잔기를 나타내며, m=0∼20의 정수를 나타낸다)(Wherein R 1 represents a hydrogen atom or a methyl group, OR 2 represents a divalent alcohol residue having 1 to 5 carbon atoms and an integer of m = 0 to 20)

상기 모노머 조성물은, 바람직하게는 인산에스테르 화합물을 조성물 중 0.001∼3중량%로 더 포함할 수 있다. 또한, 바람직하게는 자외선 흡수제를 조성물 중 0.01∼4중량%로 더 포함할 수 있다. 또한, 바람직하게는 벤질알코올, 부탄올, 펜탄올 중에서 선택된 1종 이상의 알코올을 더 포함할 수 있다. Preferably, the monomer composition may further comprise 0.001 to 3% by weight of a phosphate ester compound in the composition. In addition, preferably, the ultraviolet absorbent may further comprise 0.01 to 4% by weight of the composition. In addition, it may preferably further comprise at least one alcohol selected from benzyl alcohol, butanol, pentanol.

바람직하게는, 상기 모노머 조성물의 주입은 -10~50℃의 온도범위에서 이루어진다.Preferably, the injection of the monomer composition is made in the temperature range of -10 ~ 50 ℃.

본 발명에 의하면 아릴계 광학재료용 모노머의 몰드 내 주입시 비전인식시스템을 사용하여 유면을 확인하면서 최종 주입지점에 도달하면 자동으로 주입을 중지하게 되므로, 모노머 용액이 모자라지도 않고 넘치지도 않게 정량 주입이 가능하다. According to the present invention, when the aryl optical material monomer is injected into the mold, the injection is automatically stopped when the final injection point is reached while checking the oil level using a vision recognition system, so that the injection of the monomer solution is not short and does not overflow. It is possible.

또, 단순히 기계적으로 주입량이나 속도를 조절하는 것이 아니라 잔량 주입시 비전인식시스템을 사용하여 유면을 확인하면서 주입하므로, 모노머에 따른 점성의 차이, 유면 형상의 차이에 관계없이 정량 주입이 가능하다. In addition, it is possible to quantitatively irrespective of the difference in viscosity and the shape of the oil surface, because the oil is injected while checking the oil level by using a vision recognition system instead of simply adjusting the amount or speed of mechanical injection.

또, 몰드 내부의 캐비티에 1차로 빠르게 대부분의 모노머를 주입하는 단계를 둠으로써 모노머의 주입시간을 단축시킬 수 있으므로, 미리 파악한 가사 시간 내에 주입이 완료되도록 설정하는 것이 용이하고, 따라서 모노머에 따른 경화속도 및 경화시간의 차이에 관계없이 경화 전 최적의 상태에서 정량 주입이 가능하다. In addition, since the injection time of the monomers can be shortened by providing a step of injecting most of the monomers into the cavity inside the mold firstly quickly, it is easy to set the injection to be completed within a predetermined pot life, and thus curing according to the monomers. Irrespective of the difference in speed and curing time, dosing can be carried out at optimum conditions before curing.

본 발명에 따르면 주입량의 부족이나 과다에 따른 불량 없이 고품질의 아릴계 렌즈를 자동 주입에 의해 생산할 수 있으므로, 생산성을 크게 향상시킬 수 있고 인건비의 절감으로 생산비를 절감할 수 있으며, 아울러 작업자가 모노머에 직접 노출되는 문제 및 모노머 조성물의 과도한 주입으로 인한 장비의 이상 동작이나 고장 또한 방지할 수 있다.According to the present invention, it is possible to produce a high quality aryl lens by automatic injection without defects due to lack of injection amount or excessive amount, which can greatly improve productivity and reduce production cost by reducing labor costs, and also allow the operator to The problem of direct exposure and abnormal operation or failure of equipment due to excessive injection of monomer composition can also be prevented.

도 1은 본 발명의 일 실시예에 의한 렌즈 제조과정을 개략적으로 도시한 플로우차트,
도 2는 본 발명의 일 실시예에 의한 모노머 자동주입방법의 구성도,
도 3은 도 2에서 모노머 용액이 시린지 내부로 1차 흡입된 상태,
도 4는 도 3에서 모노머 용액이 몰드 내부로 주입되고 있는 상태,
도 5는 도 4에서 모노머 용액이 몰드 내부에 충만된 상태를 도시한 것이다.
1 is a flowchart schematically illustrating a lens manufacturing process according to an embodiment of the present invention;
2 is a block diagram of a monomer automatic injection method according to an embodiment of the present invention,
3 is a state in which the monomer solution is first suctioned into the syringe in FIG. 2,
4 is a state in which the monomer solution is injected into the mold in FIG.
FIG. 5 illustrates a state in which the monomer solution is filled in the mold in FIG. 4.

이하, 본 발명의 아릴계 광학재료용 모노머의 몰드 자동 주입방법을 바람직한 실시예에 의해 단계별로 설명한다. Hereinafter, a method for automatically injecting a mold of the monomer for aryl optical materials of the present invention will be described step by step by preferred embodiment.

본 발명의 아릴계 광학재료용 모노머의 몰드 자동 주입방법은, The automatic mold injection method of the monomer for the aryl optical material of the present invention,

(a) 고상 굴절률 1.537-1.585, 점도 20~800cps(25℃)의 아릴계 광학재료용 모노머 조성물을 준비하는 단계;(a) preparing a monomer composition for an aryl optical material having a solid refractive index of 1.537 to 1.585 and a viscosity of 20 to 800 cps (25 ° C);

(b) 상기 모노머 조성물을 외곽이 실링된 1쌍의 몰드 사이에 형성된 캐비티 내에 대부분 주입하는 단계;(b) injecting most of said monomer composition into a cavity formed between a pair of molds with outer seals;

(c) 상기 (b)단계에 이어서 모노머 조성물을 캐비티 내로 주입하면서 비전인식시스템을 사용하여 유면을 감지하여 설정된 최종 주입지점에 유면이 감지되면 모노머 조성물의 주입을 종료하는 단계;를 포함한다. and (c) following step (b), injecting the monomer composition into the cavity and detecting the oil level using a vision recognition system to terminate the injection of the monomer composition when oil is detected at the final injection point.

상기 아릴계 광학재료용 모노머 조성물은 아릴계 모노머를 주성분으로 하는 광학재료용 조성물을 모두 포함하는 의미이다. 본 발명에서 '모노머 용액'은 상기 모노머 조성물이 유동성이 있는 액상 상태일 때를 칭한다.The monomer composition for aryl optical materials is meant to include all compositions for optical materials containing aryl monomers as a main component. In the present invention, the 'monomer solution' refers to when the monomer composition is in a liquid state with fluidity.

상기 아릴계 광학재료용 모노머 조성물은 고상 굴절률 1.537-1.585, 25℃에서 점도가 20~800cps이다. 보다 바람직하게는 25℃에서 점도가 30~500cps이다.The monomer composition for an aryl optical material has a viscosity of 20 to 800 cps at a solid state refractive index of 1.537 to 1.585 and 25 ° C. More preferably, the viscosity is 30-500 cps at 25 degreeC.

바람직하게는 상기 아릴계 광학재료용 모노머 조성물은 알킬렌글리콜 비스아릴카르보네이트 및 말레이트 화합물 중에서 선택된 1종 이상의 화합물인 ‘성분A’와 아래 화학식 1로 표시되는 디아릴에스테르 화합물인 ‘성분B’를 포함한다. Preferably, the monomer composition for an aryl optical material is 'component A' which is at least one compound selected from alkylene glycol bisaryl carbonate and maleate compound and 'component B' which is a diaryl ester compound represented by Formula 1 below. Contains'

[화학식 1][Formula 1]

Figure pat00002
Figure pat00002

(여기에서 R1은 수소원자 또는 메틸기를 나타내고, OR2 은 탄소수가 1∼5인 2가 알코올 잔기를 나타내며, m=0∼20의 정수를 나타낸다)(Wherein R 1 represents a hydrogen atom or a methyl group, OR 2 represents a divalent alcohol residue having 1 to 5 carbon atoms and an integer of m = 0 to 20)

상기 성분A와 성분B는 바람직하게는 5∼70중량% 및 30∼95중량%의 비율로 혼합될 수 있다. 디아릴에스테르 화합물(성분B)의 함유량이 30% 미만이고 성분A 화합물이 70%를 초과할 경우에는 제조된 광학렌즈의 충격 강도가 낮거나 굴절율이 낮은 문제점이 있을 수 있고, 디아릴에스테르 화합물의 함유량이 95%를 초과할 때는 단량체 조성물의 점도가 높아져 유리 금형에 주입이 어려워지고 생산성이 떨어지는 문제점이 있다. 상기 성분A와 성분B는, 더욱 바람직하게는 10∼60중량% 및 40∼90중량%의 비율로 혼합될 수 있다. Component A and component B may preferably be mixed in a proportion of 5 to 70% by weight and 30 to 95% by weight. When the content of the diaryl ester compound (component B) is less than 30% and the compound A compound is more than 70%, there may be a problem that the impact strength of the manufactured optical lens is low or the refractive index is low, When the content is more than 95%, the viscosity of the monomer composition is increased, making it difficult to inject into the glass mold, and there is a problem that the productivity is lowered. Component A and component B may be more preferably mixed at a ratio of 10 to 60% by weight and 40 to 90% by weight.

상기 알킬렌글리콜 비스아릴카르보네이트는 바람직하게는 아래 화학식 2로 표시될 수 있다. 상기 알킬렌글리콜 비스아릴카르보네이트는 특히 바람직하게는 디에틸렌글리콜 비스아릴카르보네이트이다.The alkylene glycol bisaryl carbonate may be preferably represented by the following formula (2). The alkylene glycol bisaryl carbonate is particularly preferably diethylene glycol bisaryl carbonate.

[화학식 2][Formula 2]

Figure pat00003
Figure pat00003

(여기서 R4 는 수소 또는 메틸기를 나타내 고, -OR3는 탄소수가 1∼10인 2가 알코올 잔기를 나타 내고, n는 1∼10의 정수를 나타낸다.)(Wherein R 4 represents hydrogen or a methyl group, -OR 3 represents a divalent alcohol residue having 1 to 10 carbon atoms, and n represents an integer of 1 to 10).

상기 말레이트 화합물은, 바람직하게는 디벤질말레이트; 모노벤질말레이트; 디벤질푸말레이트; 메틸벤질말레이트; 메틸벤질푸말레이트; 디메틸말레이트; 디에틸말레이트; 디부틸말레이트; 디부틸푸말레이트; 모노부틸말레이트; 디펜틸말레이트 및 디펜틸푸말레이트로 구성된 군으로부터 선택될 수 있다. The maleate compound is preferably dibenzyl maleate; Monobenzylmaleate; Dibenzyl fumalate; Methylbenzylmaleate; Methylbenzyl fumalate; Dimethylmaleate; Diethylmaleate; Dibutyl maleate; Dibutyl fumarate; Monobutyl maleate; It can be selected from the group consisting of dipentyl maleate and dipentyl fumalate.

상기 화학식 1로 표시되는 디아릴에스테르 화합물은 디아릴프탈레이트, 디아릴이소프탈레이트, 디아릴테레프탈레이트 등에 2가 알코올 즉, 에틸렌글리콜, 프로필렌글리콜, 1,3-프로판디올, 1,4-부탄디올, 1,3-부탄디올, 네오펜틸글리콜 등을 일부 부가하는 에스테르교환 반응에 의하여 제조할 수 있다. The diaryl ester compound represented by the formula (1) is a dihydric phthalate, a diaryl isophthalate, a diaryl terephthalate, and the like. A dihydric alcohol, that is, ethylene glycol, propylene glycol, 1,3-propanediol, 1,4-butanediol, 1 It can manufacture by the transesterification reaction which adds a part of, 3-butanediol, neopentylglycol, etc.

상기 아릴계 광학재료용 모노머 조성물은, 인산에스테르 화합물을 더 포함할 수 있다. 본 조성물에서 인산에스테르는 아닐링 과정에서 열에 의하여 발생하는 광학렌즈의 황변 현상을 막아주는 역할을 한다. 본 조성물 중 인산에스테르는 바람직하게는 0.001∼3중량%(10∼30000ppm)로 포함되며, 더욱 바람직하게는 0.02∼2중량%(200∼20000 ppm)로 포함될 수 있다. 인산에스테르의 함유량이 0.001중량% 미만일 경우에는 열에 의한 황변을 막아 주기 어렵고, 3중량%를 초과할 경우에는 경화과정에서 고상수지로부터 유리 금형이 떨어져 있게 되어 렌즈 표면에 줄무늬가 생기는 불량이 발생할 수 있다.The monomer composition for aryl optical materials may further include a phosphate ester compound. Phosphate ester in the present composition serves to prevent the yellowing phenomenon of the optical lens generated by heat in the annealing process. The phosphate ester in the present composition is preferably contained in 0.001 to 3% by weight (10 to 30000 ppm), more preferably 0.02 to 2% by weight (200 to 20000 ppm). If the content of phosphate ester is less than 0.001% by weight, it is difficult to prevent yellowing due to heat. If the content of the phosphate ester exceeds 3% by weight, the glass mold may be separated from the solid resin during the curing process, resulting in a problem of streaking on the lens surface. .

본 조성물에 포함되는 인산에스테르는 바람직하게는 아래 화학식 3으로 표시될 수 있다. Phosphoric acid ester included in the composition may be preferably represented by the following formula (3).

[화학식 3][Formula 3]

Figure pat00004
Figure pat00004

(X, Y, Z는 수소, 할로 겐, 알킬, 알릴, 페닐, 에틸렌옥사이드 또는 프로필렌옥사이드가 부 가된 알코올 잔기 및 할로 알킬의 탄화수소로 구성된 군으로부터 선 택된 어느 하나로, 서로 같거나 다르다.)(X, Y, Z is the same or different from each other selected from the group consisting of hydrogen, halogen, alkyl, allyl, phenyl, ethylene oxide or propylene oxide added alcohol residues and hydrocarbons of halo alkyl.)

상기 화학식 3으로 표시되는 인산에스테르 화합물은, 예를 들어, 이소프로필산 포스페이 트; 디이소프로필산 포스페이트; 트리이소프로필산 포스페이트; 부틸산 포스페이트; 디부틸산포스페이트;트리부틸산포스페이트; 옥틸산 포스페이트; 디옥 틸산포스페이트; 트리옥틸산포스페이트; 이소데실산 포스페이트; 디이소데실산 포 스페이트; 트리이소데실산 포스페이트; 트리데칸올산 포스페이트; 비스(트리데칸올 산)포스페이트; 디메틸산 포스페이트; 트리메틸산 포스페이트; 디에틸산포스페이 트; 트리에틸산포스페이트; 디프로필산 에스테르; 트리프로필산 에스테르; 메틸산 포스페이트; 에틸산포스페이트; 프로필산 포스페이트; 벤질산포스페이트; 디벤질산 포스페이트; 트리벤질산포스페이트; 폴리옥시에틸렌 노닐 페놀에테르 포스페이트; 트리 폴리옥시에틸렌 노닐 페놀에테르 포스페이트 포스페이트, 비스(트리데칸올산) 포스페이트, 에틸렌글리콜 모노에틸 포스페이트, 디에틸렌글리콜 모노에틸 포스페 이트, 트리에틸렌글리콜 모노에틸 포스페이트, 디에틸렌글리콜 모노부틸 디포스페 이트, 디에틸렌글리콜 모노부틸 포스페이트, 이소프로필렌글리콜 모노에틸포스페이 트, 디이소프로필렌글리콜 모노에틸 포스페이트, 트리이소프로필렌글리콜 모노에틸 포스페이트 등이 사용될 수 있다. Phosphoric acid ester compound represented by the formula (3) is, for example, isopropyl acid phosphate; Diisopropyl acid phosphate; Triisopropyl acid phosphate; Butyric acid phosphate; Dibutyl phosphate; tributyl phosphate; Octylic acid phosphate; Dioctylate phosphate; Trioctylate phosphate; Isodecyl phosphate; Diisodecyl acid phosphate; Triisodecyl phosphate; Tridecanoic acid phosphate; Bis (tridecanol acid) phosphate; Dimethyl acid phosphate; Trimethyl acid phosphate; Diethyl phosphate; Triethyl phosphate; Dipropyl acid esters; Tripropyl acid esters; Methyl acid phosphate; Ethyl acid phosphate; Propyl acid phosphate; Benzyl phosphate; Dibenzyl acid phosphate; Tribenzyl phosphate; Polyoxyethylene nonyl phenolether phosphate; Tri polyoxyethylene nonyl phenolether phosphate phosphate, bis (tridecanoic acid) phosphate, ethylene glycol monoethyl phosphate, diethylene glycol monoethyl phosphate, triethylene glycol monoethyl phosphate, diethylene glycol monobutyl diphosphate, di Ethylene glycol monobutyl phosphate, isopropylene glycol monoethyl phosphate, diisopropylene glycol monoethyl phosphate, triisopropylene glycol monoethyl phosphate and the like can be used.

상기 아릴계 광학재료용 모노머 조성물은 자외선 흡수제를 더 포함할 수 있다. 바람직하게는 400㎚ 까지의 장파장 자외선을 차단할 수 있는 자외선 흡수제를 포함하며, 자외선 흡수제는 본 발명의 광학렌즈용 조성물 중 0.01∼4중량%(100∼40000ppm)로 포함되는 것이 바람직하고, 0.02∼2중량%(200∼20000ppm)로 포함되는 것이 더욱 바람직하다. 자외선 흡수제의 첨가량이 0.01중량% 미만일 때는 유효한 자외선 흡수능을 얻기 어렵고, 4중량%가 넘으면 광학렌즈의 투명도가 떨어지는 문제점이 있다.The monomer composition for an aryl optical material may further include an ultraviolet absorber. Preferably, a UV absorber capable of blocking long wavelength ultraviolet rays up to 400 nm is included, and the UV absorber is preferably contained in an amount of 0.01 to 4 wt% (100 to 40000 ppm) in the composition for an optical lens of the present invention, and 0.02 to 2 More preferably, it is contained in the weight% (200-20000 ppm). When the amount of the ultraviolet absorber added is less than 0.01% by weight, it is difficult to obtain an effective ultraviolet absorbing capacity. When the amount of the ultraviolet absorber is more than 4% by weight, the transparency of the optical lens is inferior.

상기 자외선 흡수제로는 광학렌즈에의 사용과 효과가 알려져 있는 공지의 자외선 흡수제면 제한 없이 사용될 수 있다. 예를 들어, 에틸-2-시아노-3,3-디페닐아크릴레이트, 2-(2'-히드록시-5-메틸페닐)-2H-벤조트리아졸; 2-(2'-히드록시-3',5'-디-t-부틸페닐)-5-클로로-2H-벤조트리아졸; 2-(2'-히드록시-3'-t-부틸-5'-메틸페닐)-5-클로로-2H-벤조트리아졸; 2-(2'-히드록시-3',5'-디-t-아밀페닐)-2H-벤조트리아졸; 2-(2'-히드록시-3',5'-디-t-부틸페닐)-2H-벤조트리아졸; 2-(2'-히드록시-5'-t-부틸페닐)-2H-벤조트리아졸; 2-(2'-히드록시-5'-t-옥틸페닐)-2H-벤조트리아졸; 2,4-디히드록시벤조페논; 2-히드록시-4-메톡시벤조페논; 2-히드록시-4-옥틸옥시벤조페논; 4-도데실옥시-2-히드록시벤조페논; 4-벤조록시-2-히드록시벤조페논; 2,2',4,4'-테트라히드록시벤조페논; 2,2'-디히드록시-4,4'-디메톡시벤조페논 등이 단독으로 또는 2종 이상 혼합 사용될 수 있다. 바람직하게는, 400㎚ 이하의 파장역에서 양호한 자외선 흡수능을 가지고, 본 발명의 조성물에 양호한 용해성을 갖는 2-(2'-히드록시-5-메틸페닐)-2H-벤조트리아졸, 2-히드록시-4-메톡시벤조페논, 에틸-2-시아노-3,3-디페닐아크릴레이트, 2-(2'-히드록시-5'-t-옥틸페닐)-2H-벤조트리아졸, 2,2'-디히드록시-4,4'-디메톡시벤조페논, 2-(2'-히드록시-3',5'-디-t-아밀페닐)-2H-벤조트리아졸, 2-(2'-히드록시-3,5'-디- t-부틸페닐)-5-클로로-2H-벤조트리아졸, 2-(2'-히드록시-3'-t-부틸-5'-메틸페닐)-5-클로로-2H-벤조트리아졸, 2,2-디히드록시-4,4'-디메톡시벤조페논 등을 단독으로 또는 2종 이상을 혼합 사용한다.The ultraviolet absorbent may be used without any known ultraviolet absorbent surface limitation, which is known and used in optical lenses. For example, ethyl-2-cyano-3,3-diphenylacrylate, 2- (2'-hydroxy-5-methylphenyl) -2H-benzotriazole; 2- (2'-hydroxy-3 ', 5'-di-t-butylphenyl) -5-chloro-2H-benzotriazole; 2- (2'-hydroxy-3'-t-butyl-5'-methylphenyl) -5-chloro-2H-benzotriazole; 2- (2'-hydroxy-3 ', 5'-di-t-amylphenyl) -2H-benzotriazole; 2- (2'-hydroxy-3 ', 5'-di-t-butylphenyl) -2H-benzotriazole; 2- (2'-hydroxy-5'-t-butylphenyl) -2H-benzotriazole; 2- (2'-hydroxy-5'-t-octylphenyl) -2H-benzotriazole; 2,4-dihydroxybenzophenone; 2-hydroxy-4-methoxybenzophenone; 2-hydroxy-4-octyloxybenzophenone; 4-dodecyloxy-2-hydroxybenzophenone; 4-benzooxy-2-hydroxybenzophenone; 2,2 ', 4,4'-tetrahydroxybenzophenone; 2,2'- dihydroxy-4,4'- dimethoxy benzophenone etc. can be used individually or in mixture of 2 or more types. Preferably, 2- (2'-hydroxy-5-methylphenyl) -2H-benzotriazole, 2-hydroxy having good ultraviolet absorption in the wavelength range of 400 nm or less and having good solubility in the composition of the present invention. -4-methoxybenzophenone, ethyl-2-cyano-3,3-diphenylacrylate, 2- (2'-hydroxy-5'-t-octylphenyl) -2H-benzotriazole, 2, 2'-dihydroxy-4,4'-dimethoxybenzophenone, 2- (2'-hydroxy-3 ', 5'-di-t-amylphenyl) -2H-benzotriazole, 2- (2 '-Hydroxy-3,5'-di-t-butylphenyl) -5-chloro-2H-benzotriazole, 2- (2'-hydroxy-3'-t-butyl-5'-methylphenyl)- 5-chloro-2H-benzotriazole, 2,2-dihydroxy-4,4'-dimethoxybenzophenone, or the like is used alone or in combination of two or more thereof.

상기 아릴계 광학재료용 모노머 조성물은 중합개시제(촉매)를 조성물 전체 중량에 대하여 0.01∼10중량% 포함할 수 있다. 중합 개시제로는 비닐기를 함유한 단량체를 경화시킬 수 있는 공지의 중합개시제면 제한 없이 사용될 수 있다. 예를 들어, 퍼옥시디카르보네이트화합물, 즉 디이소프로필퍼옥시디카르보네이트, 디-n-프로필퍼옥시디카르보네이트, 디-2-에틸헥실퍼옥시디카르보네이트, 디-3-메틸-3-메톡시부틸퍼옥시디카보네이트, 디-s-부틸퍼옥시디카르보네이트, 디메톡시이소프로필퍼옥시디카르보네이트, 디-에톡시에틸퍼옥시디카르보네이트, 디-4-t-부틸시클로헥실퍼옥시디카르보네이트 등이 사용될 수 있으며, 바람직하게는 디이소프로필퍼옥시디카르보네이트가 사용될 수 있다. The monomer composition for an aryl optical material may include 0.01 to 10% by weight of a polymerization initiator (catalyst) based on the total weight of the composition. The polymerization initiator may be used without limitation as long as it is a known polymerization initiator capable of curing the monomer containing a vinyl group. For example, peroxydicarbonate compounds, ie diisopropylperoxydicarbonate, di-n-propylperoxydicarbonate, di-2-ethylhexylperoxydicarbonate, di-3-methyl- 3-methoxybutylperoxydicarbonate, di-s-butylperoxydicarbonate, dimethoxyisopropylperoxydicarbonate, di-ethoxyethylperoxydicarbonate, di-4-t-butylcyclohex Silperoxydicarbonate and the like can be used, preferably diisopropylperoxydicarbonate can be used.

또, 제조되는 렌즈의 색상을 보증하기 위하여 벤질알코올, 부탄올, 펜탄올 등의 알코올 및/또는 안료를 부가할 수 있다. 안료로는, 통상 푸른 색 및 붉은색 안료가 첨가될 수 있는데, 예를 들어, 울트라마린불블루, 몰리브덴레드, 소듐아루미노술포실리케이트, 퀴나크리돈, 페로시안화 제2철을 주성분으로 하는 감청색, 함 황 나트륨알미노실리케이트의 군청색, 산화코발트와 알루미나로 만들어진 코발트 블루, 구리프탈로시아닌으로 된 프탈로시아닌 블루 등의 안료가 사용될 수 있다. 바람직한 안료의 첨가량은 단량체 조성물 대비 300ppm 이하이며, 더욱 바람직하게는 2∼200ppm 이다. 안료의 첨가량이 300ppm 이상이면 렌즈의 투명성이 떨어지는 문제점이 발생될 수 있다.In addition, alcohols and / or pigments such as benzyl alcohol, butanol and pentanol may be added to ensure the color of the lens to be manufactured. As the pigment, blue and red pigments may be added, typically, for example, ultramarine bull blue, molybdenum red, sodium aluminosulfosilicate, quinacridone, royal blue ferric cyanide, Pigments such as ultramarine blue of sodium aluminosilicate, cobalt blue made of cobalt oxide and alumina, phthalocyanine blue of copper phthalocyanine and the like can be used. The addition amount of a preferable pigment is 300 ppm or less with respect to a monomer composition, More preferably, it is 2-200 ppm. If the addition amount of the pigment is more than 300ppm may cause a problem of poor transparency of the lens.

상기 모노머 조성물은, 플라스틱 광학렌즈 분야의 통상의 기술에 따라, 이밖에도 유기염료, 착색방지제, 산화방지제, 광안정제 등을 필요에 따라 통상적인 방법으로 더 포함할 수 있다. The monomer composition may further include organic dyes, colorants, antioxidants, light stabilizers, etc. in a conventional manner as needed, in accordance with conventional techniques in the field of plastic optical lenses.

상기 모노머 조성물의 주입은, 50℃ 이하의 온도범위에서 이루어지는 것이 바람직하며, 보다 바람직하게는 -10~50℃, 더욱 바람직하게는 5~40℃ 온도범위에서 이루어지는 것이 좋다. 적절한 온도 내에서 주입이 이루어짐으로써 가사시간을 적절하게 유지할 수 있으며, 또한 최종적으로 수득되는 광학재료에서 맥리, 링, 가변미경화의 발생률을 낮춰 광학재료의 품질을 높일 수 있다. It is preferable that the injection of the monomer composition is made in a temperature range of 50 ° C or less, more preferably -10 to 50 ° C, still more preferably 5 to 40 ° C. It is possible to maintain the pot life properly by injecting at an appropriate temperature, and to improve the quality of the optical material by lowering the incidence of striae, rings, and variable uncured resins in the finally obtained optical material.

상기 단계 (b)는 미리 설정된 중량 또는 부피만큼 상기 모노머 조성물을 상기 캐비티 내에 주입하거나, 또는 비전인식시스템을 사용하여 몰드 내에 미리 설정된 영역까지 주입할 수 있다. 상기 단계 (c)는 비전인식시스템을 사용하여 유면을 감지하여 설정된 최종 주입지점에 유면이 감지되면 모노머 조성물의 주입을 종료한다. In step (b), the monomer composition may be injected into the cavity by a predetermined weight or volume, or may be injected to a predetermined area in the mold using a vision recognition system. The step (c) is to detect the oil surface using a vision recognition system to terminate the injection of the monomer composition when the oil surface is detected at the final injection point set.

이하, 상기 단계 (b) 및 (c)의 바람직한 실시예를 첨부된 도면에 의하여 설명한다.Hereinafter, preferred embodiments of the steps (b) and (c) will be described with reference to the accompanying drawings.

먼저, 도 1에 도시된 바와 같이 렌즈 등 광학재료를 제조하기 위하여 모노머 용액을 몰드 내부에 자동으로 주입하는 방법은 몰드의 로딩(S10), 테이핑(S20), 테이프 개방(S30), 모노머 주입(S40), 테이프 폐쇄(S50) 및 몰드 언로딩(S60) 단계를 거치게 되고, 후속 공정으로는 모노머의 경화 후 몰드로부터 분리하는 공정을 거치면 렌즈를 완성하게 되는데 이러한 공정은 기존의 방법과 기본적으로 동일하다.First, as shown in FIG. 1, a method of automatically injecting a monomer solution into a mold to manufacture an optical material such as a lens includes loading a mold (S10), taping (S20), opening a tape (S30), and injecting a monomer ( S40), the tape closing (S50) and the mold unloading (S60) step, and the subsequent process of curing the monomer after the separation from the mold to complete the lens, these processes are basically the same as the existing method Do.

본 실시예에서는 원료탱크의 모노머를 몰드의 캐비티에 주입하면서 비전인식시스템을 사용하여 유면을 감지하여 설정된 최종 주입지점에 유면이 감지되면 모노머 용액의 주입을 중지하는 구체적인 방법을 제시하고 있는바, 도 2 내지 도 5에 도시된 바와 같이 모노머 용액 탱크(10)의 모노머 용액(S)을 몰드(M)의 캐비티에 맞게 용량 조절이 가능한 시린지(20) 내부에 1차로 흡입한 후, 상기 시린지(20) 내부에 주입된 모노머 용액(S)을 몰드(M) 내부에 2차로 대부분의 양을 고속으로 주입하고, 주입압력을 낮추어 잔량을 주입하면서 최종적으로 비전인식시스템을 이용하여 모노머 용액(S)이 몰드(M) 내부에 충만되었는지를 확인한 후 주입을 종료하도록 되어 있다.In the present embodiment, the monomer of the raw material tank is injected into the cavity of the mold, and a specific method of stopping the injection of the monomer solution is provided by detecting the oil level using a vision recognition system and detecting the oil level at the final injection point. As shown in 2 to 5, the monomer solution (S) of the monomer solution tank (10) is first suctioned into the syringe (20) capable of volume control according to the cavity of the mold (M), and then the syringe (20) Inject the monomer solution (S) injected into the mold (M) in the second most of the amount at a high speed, and lower the injection pressure to inject the remaining amount, finally using the non-recognition system to the monomer solution (S) The injection is finished after confirming that the mold M is filled inside.

본 실시예에서 상기 비전인식시스템은 도 2 내지 도 5에서 알 수 있는 바와 같이 몰드(M)의 윤곽과 상기 몰드(M)의 캐비티 내에 주입되는 모노머 용액(S)의 유면(L1)을 촬영하되, 몰드(M)가 주입위치에 세팅된 상태를 감지하기 위한 상기 몰드(M) 윤곽 일부의 제1영역(A1)과, 상기 몰드(M)의 주입구 외측에 위치한 제2영역(A2)이 설정되어 있다.In the present exemplary embodiment, the vision recognition system photographs the contour of the mold M and the oil level L1 of the monomer solution S injected into the cavity of the mold M, as shown in FIGS. 2 to 5. The first region A1 of a part of the contour of the mold M and the second region A2 located outside the injection hole of the mold M are set to detect a state in which the mold M is set at the injection position. It is.

한편, 콘트롤러(C)는 상기 비전인식시스템에서 촬영된 이미지 신호 즉, 도 2에 도시된 바와 같이 상기 제1영역(A1)에서 몰드(M)의 윤곽이 감지되면 몰드(M)가 주입위치에 안착된 것으로 인식하게 되는데, 이때 촬영된 몰드(M)의 윤곽과 제1영역(A1)에 원호 형태로 표시된 가상 윤곽(L)이 일치되는지의 여부를 판단하여 일치하지 않을 경우에는 비전인식시스템을 미세조정 즉, 비전카메라의 위치를 조정하여 몰드(M)의 윤곽에 상기 가상 윤곽(L)을 일치시키는 촬영위치 조정단계를 거치게 된다.On the other hand, the controller (C) is the image signal photographed by the vision recognition system, that is, as shown in Figure 2 when the contour of the mold (M) is detected in the first area (A1), the mold (M) in the injection position In this case, the contour of the mold M and the virtual contour L displayed in the arc shape in the first area A1 are determined to match. Fine adjustment, that is, by adjusting the position of the vision camera is subjected to a photographing position adjusting step of matching the virtual contour (L) with the contour of the mold (M).

상기한 촬영위치 조정단계에서는 제1영역(A1)의 위치가 조정되는 것과 동시에 제2영역의 위치가 제1영역(A1)과 함께 동시에 등거리 이동되게 되므로 주입장치 내에서 몰드(M)의 안착위치가 약간씩 변화함에도 불구하고 비전인식시스템에서 촬영되는 제2영역(A2)은 동일한 위치를 촬영하여 모노머 용액의 유면변화를 감지하게 된다.In the photographing position adjusting step, the position of the first region A1 is adjusted and at the same time the position of the second region is equidistantly moved together with the first region A1, so that the position of the mold M is placed in the injection apparatus. Although slightly changed by the second area (A2) to be photographed in the vision recognition system to capture the same position to detect the change in the surface of the monomer solution.

또, 콘트롤러(C)는 비전인식시스템에서 촬영된 이미지를 분석하여 몰드(M)의 종류에 따라 캐비티의 용량 파악 및 주입위치 세팅여부를 감지하고, 시린지(20)의 구동부(22)와 밸브(V)의 개폐 동작을 제어하게 됨으로써 도 3에 도시된 바와 같이 모노머 용액(S)을 시린지(20) 내부로 1차 흡입하는 양과 2차로 몰드(M)에 주입하는 시점과 주입압력 및 종료시점을 제어하게 되며, 비전인식시스템의 미세위치도 조정하게 된다.In addition, the controller (C) analyzes the image taken by the vision recognition system to detect the capacity of the cavity and whether the injection position is set according to the type of the mold (M), and the drive unit 22 and the valve of the syringe 20 ( By controlling the opening and closing operation of V), as shown in FIG. 3, the amount of first suction of the monomer solution S into the syringe 20 and the time of injection of the monomer solution M into the mold M, the injection pressure, and the end point of injection are shown. Control and fine adjustment of the vision recognition system.

또, 상기 콘트롤러(C)는 터치패드나 키보드와 같은 외부입력수단에 의해 몰드(M)와 모노머 용액(S)의 종류에 따라 주입압력을 각기 다르게 세팅하게 되며, 새로운 종류의 몰드나 모노머 용액의 사용시에는 반복적인 테스트를 거쳐 입수된 데이터를 저장하여 최적의 주입압력을 찾아서 세팅할 수 있도록 되어 있다. In addition, the controller (C) sets the injection pressure differently according to the type of the mold (M) and the monomer solution (S) by an external input means such as a touch pad or a keyboard, and a new type of mold or monomer solution. In use, it is possible to find and set the optimum injection pressure by storing the data obtained through repeated tests.

본 실시예에서, 상기 구동부(22)는 도시안된 모터의 동력에 의해 플런저(23)가 진퇴작동을 하여 시린지(20)의 내부로 모노머 용액을 흡입하거나, 흡입된 모노머 용액을 몰드(M)로 주입하도록 구성되어 있으나, 본 발명은 이에 한정되지 않고 구동부(22)의 구동방식은 공지된 다양한 방식을 사용할 수 있다.In the present embodiment, the driving unit 22 inhales the monomer solution into the interior of the syringe 20 by the plunger 23 is moved forward and backward by the power of a motor (not shown), or the sucked monomer solution into the mold (M). Although configured to inject, the present invention is not limited thereto, and the driving method of the driving unit 22 may use various known methods.

위와 같은 구성으로 모노머 용액을 몰드 내부에 주입하는 바람직한 실시예를 설명하면 다음과 같다.Referring to the preferred embodiment of injecting the monomer solution into the mold in the above configuration as follows.

먼저, 1차로 도 3에 도시된 바와 같이 공급되는 몰드(M)의 종류에 따라 몰드(M)의 캐비티 용량에 일치되도록 시린지(20)에 모노머 용액(S)을 흡입하게 되는데, 이때 원료 탱크(10)와 시린지(20) 사이에 설치된 밸브(V)는 개방상태를 유지하게 되고, 노즐(21) 부분은 도시 생략된 내장형 체크밸브에 의해 외부로부터의 공기 등이 유입되는 것이 차단된 상태에서 시린지(20) 상부의 구동부(22)가 동작되어 시린지(20) 내부로 모노머 용액(S)을 정량만큼 채우게 된다.First, as shown in FIG. 3, the monomer solution S is sucked into the syringe 20 so as to match the cavity capacity of the mold M according to the type of the mold M supplied, wherein the raw material tank ( The valve (V) installed between the 10) and the syringe 20 maintains an open state, and the nozzle 21 portion of the nozzle 21 has a syringe in a state in which air from the outside is blocked by a built-in check valve (not shown). (20) The upper driving unit 22 is operated to fill the monomer 20 with the quantitative amount of the monomer solution S.

한편, 상기 밸브(V)는 콘트롤러(C)에 의해 개폐동작이 제어되도록 할 수도 있고, 체크 밸브를 사용하여 시린지(20)의 구동부(22)가 흡입 동작을 할 경우에는 개방되고, 배출동작 즉, 몰드 쪽으로의 주입시에는 자동으로 폐쇄되도록 할 수도 있음은 물론이다.On the other hand, the valve (V) may be controlled to open and close operation by the controller (C), is opened when the drive unit 22 of the syringe 20 to perform the suction operation using a check valve, that is, discharge operation Of course, the injection into the mold can also be automatically closed.

다음, 2차로 도 4에 도시된 바와 같이 비인전식시스템에 의해 촬영된 이미지에서 제1영역(A1)에 몰드(M)의 윤곽이 감지되면 이를 가상 윤곽(L)과 일치되도록 카메라의 위치를 미세조정하게 되며, 이에 의해 몰드(M)가 주입위치에 안착된 것으로 파악하게 되고, 구동부(22)가 상기 1차와는 반대방향으로 구동되어 시린지(20) 내부의 모노머 용액(S)이 노즐(21)을 통해 몰드(M) 내부로 주입되게 되는데, 이때 상기 밸브(V)는 폐쇄된 상태를 유지하게 되며, 노즐(21)에 구비된 체크밸브는 개방된 상태에서, 상기 구동부(22)의 구동은 미리 설정된 양만큼의 모노머 용액(S)만을 주입하게 되는바, 미리 설정된 양은 시린지(20)에 1차 주입된 양의 70~99%가 되도록, 보다 바람직하게는 90~98%가 되도록 설정되어 있다.Next, when the contour of the mold M is detected in the first area A1 in the image captured by the non-electrical system, as shown in FIG. 4, the position of the camera is finely adjusted to match the virtual contour L. It is understood that the mold M is seated at the injection position, and the driving unit 22 is driven in the opposite direction to the primary, so that the monomer solution S inside the syringe 20 is nozzled. It is injected into the mold (M) through the 21, wherein the valve (V) is maintained in a closed state, the check valve provided in the nozzle 21 in the open state of the drive unit 22 The driving is to inject only a predetermined amount of the monomer solution (S), the predetermined amount is set to be 70 to 99% of the amount first injected into the syringe 20, more preferably 90 to 98% It is.

상기 단계에서 모노머 용액(S)의 주입압력은 모노머 용액의 점도나 몰드 내부의 캐비티 두께 등에 따라서 모노머 용액에 기포가 발생하지 않는 범위 내에서는 최고의 압력으로 주입하도록 함으로써 주입시간의 단축을 도모할 수 있도록 한다.In this step, the injection pressure of the monomer solution S may be injected at the highest pressure within the range where bubbles are not generated in the monomer solution according to the viscosity of the monomer solution or the cavity thickness inside the mold, so that the injection time can be shortened. do.

마지막으로, 상기와 같이 구동부(22)의 구동에 의해 시린지(20) 내부의 모노머 용액(S) 대부분이 몰드(M) 내부에 주입된 후에는 구동부(22)의 구동속도를 상대적으로 느리게 하여 조심스럽게 잔량의 주입이 이루어지도록 하게 되는바, 이때에는 도 5에 도시된 바와 같이 비전인식시스템에 의해 주입구(I)의 외측에 위치한 제2영역(A2)에서 모노머 용액(S)의 유면이 감지되는지를 확인하게 될 때까지 주입하게 되며, 표면장력에 의해 몰드(M)의 주입구(I) 외측 약 1~2mm외측에 위치한 제2영역(A2)에서 모노머 용액(S)유면이 감지되면 시린지 구동부(22)의 동작을 중지시킴으로써 모노머 용액(S)의 주입을 완료하게 되며, 후속공정으로 개방했던 실링 테이프(T)를 다시 감아 주입구(I)를 폐쇄한 후, 몰드의 언로딩 과정을 거치게 되면 몰드(M)에 모노머 용액(S)의 주입이 완료된다.Finally, after the majority of the monomer solution S in the syringe 20 is injected into the mold M by the driving of the driving unit 22 as described above, the driving speed of the driving unit 22 is relatively slowed to be careful. In this case, as shown in FIG. 5, whether the oil level of the monomer solution S is detected in the second area A2 located outside the injection hole I by the vision recognition system as shown in FIG. 5. Until it is confirmed, and when the surface of the monomer solution (S) is detected in the second area (A2) located about 1 to 2 mm outside of the injection hole (I) of the mold (M) by the surface tension, the syringe driver ( The injection of the monomer solution S is completed by stopping the operation of 22). The sealing tape T, which was opened in the subsequent process, is wound again to close the injection port I, and then the mold is unloaded. Injection of monomer solution (S) to (M) is completed The.

상기와 같은 과정을 거쳐 제1영역(A1)에서의 몰드(M)의 윤곽이 가상 윤곽(L)에 일치되게 되면 공급된 몰드의 종류에 따라 미리 설정된 제1주입압력으로 모노머 용액(S)을 몰드(M) 내부에 대부분 주입하게 되고, 이후 상기 제1주입압력보다 상대적으로 낮은 압력으로 잔량의 주입을 진행하여 몰드(M)의 외측에 위치한 제2영역(A2)에서 유면(L1)이 나타나는지의 여부를 확인하여 유면(L1)이 나타나게 되면 모노머 용액의 주입을 종료하고, 유면이 나타나지 않을 경우에는 모노머 용액을 제2영역(A2)에 유면이 나타날때까지 미세한 압력으로 주입하게 된다.When the contour of the mold M in the first region A1 is matched to the virtual contour L through the above process, the monomer solution S is applied at a first injection pressure set in advance according to the type of the supplied mold. Most of the injection into the mold (M), and then the remaining amount is injected at a pressure relatively lower than the first injection pressure and whether the oil surface (L1) appears in the second area (A2) located outside the mold (M) When the oil surface (L1) appears to confirm whether the injection of the monomer solution is terminated, if the oil surface does not appear, the monomer solution is injected at a minute pressure until the oil surface appears in the second region (A2).

한편, 상기 제1영역 및 제2영역에서는 몰드의 윤곽 또는 모노머 용액의 유면을 화소수의 변화에 의해 감지하게 되는바, 몰드의 윤곽과 모노머 용액의 유면은 공기와 몰드 및 모노머 용액간의 밀도 차이에 의해 그 경계부분이 선형의 음영으로 보여지게 되며, 이에 의해 각 영역에서 촬영되는 선형의 음영이 형성하는 화소수에 의하여 몰드의 윤곽 및 모노머 용액의 유면이 형성되는 것을 알 수 있다.Meanwhile, in the first region and the second region, the contour of the mold or the oil level of the monomer solution is detected by the change in the number of pixels. The contour of the mold and the oil level of the monomer solution are determined by the difference in density between air, the mold, and the monomer solution. As a result, the boundary portion is shown as a linear shade, whereby the outline of the mold and the oil surface of the monomer solution are formed by the number of pixels formed by the linear shade photographed in each region.

본 실시예에서, 상기 영역(A1,A2)에서 감지되는 몰드(M)의 윤곽 및 모노머 용액의 유면 두께는 대체로 일정하므로 검출되는 화소수도 거의 일정하지만 주변장치부가 모두 빠르게 동작중이며, 설비 주변에 사람 및 기타 장치의 이동이 있고, 이것에 의해 몰드나 모노머 용액에 기이한 현상으로 반사되어 오검출되는 경우가 있으므로 검출되는 화소수의 변화량과 음영의 진행방향에 대하여도 감지하여 각종 노이즈에 의한 오검출을 방지할 수 있도록 한다.In this embodiment, the contour of the mold M detected in the areas A1 and A2 and the surface thickness of the monomer solution are generally constant, so that the number of pixels detected is almost constant, but the peripheral parts are all operating rapidly, And other movements of the device, which may be reflected by a strange phenomenon in the mold or the monomer solution, and thus may be misdetected. To prevent this.

본 실시예에서 상기 제1주입압력으로 주입되는 모노머 용액의 양은 전체 주입량의 70~99%가 적정하지만 본 발명은 이에 한정되지 않으며, 몰드의 종류와 모노머 용액의 점도에 따라서 1차 주입량은 다소 다르게 설정할 수도 있음은 물론이다. 상기 제1주입압력으로 주입되는 모노머 용액의 양은, 보다 바람직하게는 전체 주입량의 90~98%이다. In the present embodiment, the amount of the monomer solution injected at the first injection pressure is appropriately 70 to 99% of the total injection amount, but the present invention is not limited thereto, and the primary injection amount is somewhat different depending on the type of mold and the viscosity of the monomer solution. Of course, it can be set. The amount of the monomer solution injected at the first injection pressure is more preferably 90 to 98% of the total injection amount.

상술한 본 발명의 실시예에 의한 모노머 용액 자동 주입방법에 따르면 초기에는 몰드 내부에 빠른 속도 즉, 높은 압력으로 최단시간 내에 모노머 용액을 대부분 주입하고, 그 이후 제2영역에서 모노머 용액의 유면이 감지죌 때까지 상대적으로 느린 속도로 몰드 내부의 캐비티가 충만될때까지 잔량을 주입함으로써 모노머 용액의 주입에 소요되는 시간을 단축시키면서도 넘치지 않게 정확한 양을 주입할 수 있으므로 공정시간 단축에 따른 생산성 향상과 더불어 균일한 품질의 렌즈를 제조할 수 있게 되는 이점이 있으며, 모노머 주입량의 부족이나 과도에 따른 불량발생 및 제조장치의 오동작 또한 유발하지 않게 되는 등의 이점도 있다.According to the method of automatically injecting the monomer solution according to the embodiment of the present invention described above, most of the monomer solution is initially injected into the mold at a high speed, that is, at a high pressure, within the shortest time, and then the oil level of the monomer solution is detected in the second region. By injecting the remaining amount until the cavity inside the mold is filled at a relatively slow speed until shortening, it is possible to shorten the time required for the injection of the monomer solution while injecting the correct amount without overflow. There is an advantage in that it is possible to manufacture a lens of a quality, there is also an advantage such that the failure caused by the lack or excessive amount of monomer injection, and also does not cause malfunction of the manufacturing apparatus.

위와 같은 본 발명의 바람직한 실시예에 의하면 점성을 갖는 모노머 용액을 몰드 내부의 캐비티에 1차로 높은 압력으로 빠르게 대부분 주입한 후, 최종 단계에서 비전인식시스템을 사용하면서 주입압력를 낮추어 잔량을 서서히 주입하여 충만되도록 하게 되므로 주입 용량이 초과될 우려가 없다. 또, 몰드 내부에 모노머 용액을 단시간 내에 대부분을 주입한 후 비전인식시스템으로 제2영역에서의 모노머 용액이 감지되면 주입을 종료하게 되므로 기포의 잔류도 없고 모노머 용액의 주입량이 넘치지도 모자라지도 않게 정확하게 정량이 주입되므로 균일한 품질의 렌즈를 생산할 수 있고, 모노머의 주입시간을 단축시킬 수 있어 모노머 주입작업의 효율성을 극대화할 수 있다. 이에 따라 모노머 용액의 주입량 부족으로 인한 불량의 방지와 더불어 모노머 용액의 과도한 주입으로 인하여 발생하는 장비의 이상동작이나 고장을 예방할 수 있다.According to a preferred embodiment of the present invention as described above, the most viscous monomer solution is rapidly injected into the cavity inside the mold at a high pressure first, and then the remaining pressure is gradually filled to reduce the injection pressure while using the vision recognition system in the final step to fill it. As such, there is no risk of exceeding the injection capacity. In addition, most of the monomer solution is injected into the mold within a short time, and when the monomer solution in the second area is detected by the vision recognition system, the injection is terminated, so that there is no bubble remaining and the injection amount of the monomer solution is precisely determined. Since the injection can produce a lens of uniform quality, and can shorten the injection time of the monomer can maximize the efficiency of the monomer injection operation. Accordingly, it is possible to prevent failure due to insufficient injection amount of the monomer solution and to prevent abnormal operation or failure of equipment caused by excessive injection of the monomer solution.

C : 콘트롤러
I : 주입구
L : 가상 윤곽
L1 : 유면
M : 몰드
A1,A2 : 감지 영역
S : 모노머 용액
T : 실링 테이프
V : 밸브
10 : 원료 탱크
20 : 시린지
21 : 노즐
22 : 구동부
23 : 플런저
C: Controller
I: inlet
L: virtual contour
L1: oil cotton
M: Mold
A1, A2: detection area
S: monomer solution
T: sealing tape
V: Valve
10: raw material tank
20: syringe
21: nozzle
22: drive unit
23: plunger

Claims (14)

외곽이 실링된 1쌍의 몰드 사이에 형성된 캐비티 내에 아릴계 광학재료용 모노머 조성물을 주입하는 방법으로서,
(a) 고상 굴절률 1.537-1.585, 점도 20~800cps(25℃)의 아릴계 광학재료용 모노머 조성물을 준비하는 단계;
(b) 상기 모노머 조성물을 상기 캐비티 내에 대부분 주입하는 단계;
(c) 상기 (b)단계에 이어서 모노머 조성물을 캐비티 내로 주입하면서 비전인식시스템을 사용하여 유면을 감지하여 설정된 최종 주입지점에 유면이 감지되면 모노머 조성물의 주입을 종료하는 단계;를 포함하는, 아릴계 광학재료용 모노머의 몰드 자동 주입방법.
A method of injecting a monomer composition for an aryl optical material into a cavity formed between a pair of molds having an outer seal,
(a) preparing a monomer composition for an aryl optical material having a solid refractive index of 1.537 to 1.585 and a viscosity of 20 to 800 cps (25 ° C);
(b) injecting most of said monomer composition into said cavity;
(c) following the step (b) following the step of injecting the monomer composition into the cavity by detecting the oil level using a vision recognition system to terminate the injection of the monomer composition when the oil surface is detected at the final injection point set; Mold injection method of monomer for optical system materials.
청구항 1에 있어서,
상기 비전인식시스템은 몰드의 윤곽과 상기 몰드에 주입되는 모노머 용액의 유면을 촬영하되, 몰드가 주입위치에 세팅된 상태를 감지하기 위하여 상기 몰드 윤곽 일부에 위치하는 제1영역과, 상기 몰드 외측에 위치한 제2영역을 설정하는 것을 특징으로 하는, 아릴계 광학재료용 모노머의 몰드 자동 주입방법.
The method according to claim 1,
The vision recognition system photographs the contour of the mold and the oil level of the monomer solution injected into the mold, wherein the first region is located at a part of the mold contour to detect a state in which the mold is set at the injection position, and outside the mold. A method for automatically injecting a mold for monomers for aryl optical materials, characterized in that a second region is located.
청구항 2에 있어서,
상기 비전인식시스템은 콘트롤러가 상기 제1영역에서 몰드의 윤곽이 감지되면 설정된 제1주입압력으로 모노머 용액의 대부분을 몰드 내부에 주입한 후, 이어서 상기 제1주입압력보다 낮은 압력으로 잔량의 모노머 용액을 주입하면서 제2영역에서 유면이 감지되면 모노머 용액의 주입을 종료하는 것을 특징으로 하는, 아릴계 광학재료용 모노머의 몰드 자동 주입방법.
The method according to claim 2,
The vision recognition system, when the controller detects the contour of the mold in the first region, injects most of the monomer solution into the mold at the first injection pressure. Then, the remaining amount of the monomer solution is lower than the first injection pressure. The injection of the monomer solution, characterized in that the injection of the monomer solution is terminated when the oil level is detected in the second region, injection molding method of the monomer for an aryl optical material.
청구항 2 또는 3에 있어서,
상기 제1,2영역에서는 몰드의 윤곽 및 모노머 용액의 유면을 화소수의 변화에 의해 감지하는 것을 특징으로 하는, 아릴계 광학재료용 모노머의 몰드 자동 주입방법.
The method according to claim 2 or 3,
In the first and second regions, the contour of the mold and the oil level of the monomer solution are detected by changing the number of pixels.
청구항 2 또는 3에 있어서,
상기 제1영역에는 원호 형태로 가상 윤곽이 표시되고, 상기 제1영역에서 몰드 윤곽의 감지시 촬영된 몰드의 윤곽이 상기 가상 윤곽에 일치되도록 촬영위치 조정이 이루어지며, 상기 제1영역의 위치변화에 따라 제2영역의 위치가 함께 이동되어 유면 변화를 감지하는 것을 특징으로 하는, 아릴계 광학재료용 모노머의 몰드 자동 주입방법.
The method according to claim 2 or 3,
The virtual contour is displayed on the first region in the form of an arc, and the photographing position is adjusted so that the contour of the mold photographed when the mold contour is detected in the first region matches the virtual contour, and the position change of the first region is performed. According to claim 1, wherein the position of the second region is moved together to detect the change in the surface, automatic injection of the mold for the aryl optical material monomer.
청구항 2 또는 3에 있어서,
상기 제1영역은 몰드의 외곽 중 몰드의 X방향 정보와 Y방향 정보를 모두 갖는 위치에 설정되는 것을 특징으로 하는, 아릴계 광학재료용 모노머의 몰드 자동 주입방법.
The method according to claim 2 or 3,
And the first region is set at a position having both the X direction information and the Y direction information of the mold among the outer edges of the mold.
청구항 3에 있어서,
상기 모노머 조성물을 몰드 내부에 제1주입압력으로 주입하는 단계에서는 몰드 내부 캐비티 용적의 70~99%를 주입하는 것을 특징으로 하는, 아릴계 광학재료용 모노머의 몰드 자동 주입방법.
The method according to claim 3,
In the step of injecting the monomer composition into the mold at a first injection pressure, 70 to 99% of the cavity volume inside the mold, characterized in that the injection, automatic mold injection method of the monomer for aryl optical material.
청구항 1 내지 3 중 어느 한 항에 있어서,
상기 아릴계 광학재료용 모노머 조성물은, 알킬렌글리콜 비스아릴카르보네이트 및 말레이트 화합물 중에서 선택된 1종 이상의 화합물인 성분A와 아래 화학식 1로 표시되는 디아릴에스테르 화합물인 성분B를 포함하는 것을 특징으로 하는, 아릴계 광학재료용 모노머의 몰드 자동 주입방법.
[화학식 1]
Figure pat00005

(여기에서 R1은 수소원자 또는 메틸기를 나타내고, OR2 은 탄소수가 1∼5인 2가 알코올 잔기를 나타내며, m=0∼20의 정수를 나타낸다)
The method according to any one of claims 1 to 3,
The monomer composition for an aryl optical material may include component A which is at least one compound selected from alkylene glycol bisaryl carbonate and maleate compound, and component B which is a diaryl ester compound represented by Formula 1 below. An automatic mold injection method of an aryl optical material monomer.
[Formula 1]
Figure pat00005

(Wherein R 1 represents a hydrogen atom or a methyl group, OR 2 represents a divalent alcohol residue having 1 to 5 carbon atoms and an integer of m = 0 to 20)
청구항 8에 있어서,
상기 성분A와 성분B는 5∼70중량%와 30∼95중량%의 비율로 혼합되는 것을 특징으로 하는, 아릴계 광학재료용 모노머의 몰드 자동 주입방법.
The method according to claim 8,
The component A and the component B are mixed with each other in a proportion of 5 to 70% by weight and 30 to 95% by weight.
청구항 8에 있어서,
상기 말레이트 화합물은 디벤질말레이트; 모노벤질말레이트; 디벤질푸말레이트; 메틸벤질말레이트; 메틸벤질푸말레이트; 디메틸말레이트; 디에틸말레이트; 디부틸말레이트; 디부틸푸말레이트; 모노부틸말레이트; 디펜틸말레이트 및 디펜틸푸말레이트로 구성된 군으로부터 선택되는 것을 특징으로 하는, 아릴계 광학재료용 모노머의 몰드 자동 주입방법.
The method according to claim 8,
The maleate compound is dibenzyl maleate; Monobenzylmaleate; Dibenzyl fumalate; Methylbenzylmaleate; Methylbenzyl fumalate; Dimethylmaleate; Diethylmaleate; Dibutyl maleate; Dibutyl fumarate; Monobutyl maleate; A method for automatically injecting a mold for an aryl optical material, characterized in that it is selected from the group consisting of dipentyl maleate and dipentyl fumalate.
청구항 8에 있어서,
상기 알킬렌글리콜 비스아릴카르보네이트는 아래 화학식 2로 표시되는 것을 특징으로 하는, 아릴계 광학재료용 모노머의 몰드 자동 주입방법.
[화학식 2]
Figure pat00006

(여기서 R4 는 수소 또는 메틸기를 나타내고, -OR3는 탄소수가 1∼10인 2가 알코올 잔기를 나타내고, n는 1∼10의 정수를 나타낸다.)
The method according to claim 8,
The alkylene glycol bisaryl carbonate is represented by the following formula (2), automatic injection of the mold of the monomer for an aryl optical material.
[Formula 2]
Figure pat00006

(Wherein R 4 represents hydrogen or a methyl group, -OR 3 represents a divalent alcohol residue having 1 to 10 carbon atoms, and n represents an integer of 1 to 10).
청구항 8에 있어서,
상기 아릴계 광학재료용 모노머 조성물은 인산에스테르 화합물을 조성물 중 0.001∼3중량%로 더 포함하는 것을 특징으로 하는, 아릴계 광학재료용 모노머의 몰드 자동 주입방법.
The method according to claim 8,
The monomer composition for aryl optical materials further comprises a phosphoric acid ester compound in an amount of 0.001 to 3% by weight in the composition.
청구항 8에 있어서,
상기 아릴계 광학재료용 모노머 조성물은 벤질알코올, 부탄올, 펜탄올 중에서 선택된 1종 이상의 알코올을 더 포함하는 것을 특징으로 하는, 아릴계 광학재료용 모노머의 몰드 자동 주입방법.
The method according to claim 8,
The monomer composition for an aryl optical material may further include at least one alcohol selected from benzyl alcohol, butanol, and pentanol.
청구항 8에 있어서,
상기 모노머 조성물의 주입이 -10~50℃의 온도범위에서 이루어지는 것을 특징으로 하는, 아릴계 광학재료용 모노머의 몰드 자동 주입방법.
The method according to claim 8,
Injection of the monomer composition is characterized in that made in the temperature range of -10 ~ 50 ℃, automatic mold injection method of the monomer for an aryl optical material.
KR1020180137354A 2018-06-14 2018-11-09 Method for injecting aryl based monomer in mold for manufacturing optical material KR20190141562A (en)