KR20190043951A - Mother of pearl plate manufactured by mother of pearl mold and manufacturing method thereof - Google Patents

Mother of pearl plate manufactured by mother of pearl mold and manufacturing method thereof Download PDF

Info

Publication number
KR20190043951A
KR20190043951A KR1020170136105A KR20170136105A KR20190043951A KR 20190043951 A KR20190043951 A KR 20190043951A KR 1020170136105 A KR1020170136105 A KR 1020170136105A KR 20170136105 A KR20170136105 A KR 20170136105A KR 20190043951 A KR20190043951 A KR 20190043951A
Authority
KR
South Korea
Prior art keywords
mother
pearl
base plate
liquid
metal deposition
Prior art date
Application number
KR1020170136105A
Other languages
Korean (ko)
Inventor
김상훈
김정철
Original Assignee
김상훈
김정철
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김상훈, 김정철 filed Critical 김상훈
Priority to KR1020170136105A priority Critical patent/KR20190043951A/en
Publication of KR20190043951A publication Critical patent/KR20190043951A/en

Abstract

The present invention relates to a mother-of-pearl decorated plate manufactured by a mother-of-pearl mold and a manufacturing method thereof, and more specifically, to a decorated plate which is to be attached to the outer surface of a product, wherein UV liquid is applied to a surface of a base plate of the decorated plate, the base plate applied with the UV liquid is pressed with a mother-of-pearl mold having mother-of-pearl attached thereto to form a mother-of-pearl pattern on the surface of the base plate, and the base plate is processed by metal deposition, and thus, the decorated plate may look similar to an actual mother-of-pearl pattern. Accordingly, it is possible to massively produce the decorated plate with a predetermined mother-of-pearl pattern without using expensive mother-of-pearl. In addition, a manufacturing process of the decorated plate with a predetermined mother-of-pearl pattern can be sequentially and quickly conducted, thereby enhancing productivity. In the present invention, the mother-of-pearl decorated plate comprises: a base plate (10); a mother-of-pearl pattern forming layer (20) formed by applying UV liquid (U) to the surface of the base plate (10) to form a mother-of-pearl pattern; and a metal deposition layer (30) formed on the mother-of-pearl pattern forming layer (20) by metal deposition, wherein the mother-of-pearl pattern forming layer (20) is formed by applying the UV liquid (U) to the upper surface of the base plate (10), pressing the UV liquid (U) with the mother-of-pearl mold (50), and curing the liquid. In addition, a manufacturing method of the mother-of-pearl decorated plate comprises: a preparation step (S100); an UV liquid applying step (S200); a mother-of-pearl pattern forming step (S300); a metal deposition step (S400); and a cutting step (S500).

Description

자개 금형에 의해 제조된 자개 장식판 및 이의 제조방법{Mother of pearl plate manufactured by mother of pearl mold and manufacturing method thereof}BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a mother-of-pearl plate manufactured by mother-of-pearl mold,

본 발명은 자개 금형에 의해 제조된 자개 장식판 및 이의 제조방법에 관한 것으로, 더욱 상세하게는 제품의 외관에 부착되는 장식판에 있어서, 상기 장식판의 베이스판 표면에 UV액을 도포하고, 상기 UV액이 도포된 베이스판을 자개가 부착된 자개 금형으로 가압하여 상기 베이스판의 표면에 자개 무늬를 형성한 후, 금속 증착 등을 하여 실제 자개 무늬와 같은 효과를 내도록 함으로써, 고가의 자개가 소모되지 않으면서 일정한 자개 무늬로 대량 생산이 가능하고, 또한 자개 무늬를 갖는 장식판의 제조 공정이 연속적이며, 신속하게 진행되어 생산성이 개선된 자개 금형에 의해 제조된 자개 장식판 및 이의 제조방법에 관한 것이다.The present invention relates to a mother-and-daughter decorative plate produced by a mother-of-pearl die and a method of manufacturing the same, and more particularly to a decorative plate attached to the outer surface of a product, The applied base plate is pressed by a mother die attached with a mother-of-pearl to form a mother-of-fee pattern on the surface of the base plate, and then metal deposition or the like is performed to achieve the same effect as the actual mother- The present invention relates to a mother-of-lucky decorative plate manufactured by a mother-of-pearl die, which can be mass-produced with a uniform mother-of-pearl pattern, and which has a continuous and rapid production process of a decorative plate having a mother-of-pearl pattern.

최근 들어, 노트북, 에어컨, 냉장고 등의 전자제품 또는 가전제품의 외장제 뿐만 아니라 휴대폰, 화장품 케이스, 액세서리 등과 같은 휴대 제품에 대한 이미지와 디자인이 중시되면서 기존의 단순한 디자인에서 탈피하여 입체적이며, 고급스러운 느낌의 디자인이 각광 받고 있다.Recently, image and design for portable products such as mobile phones, cosmetic cases, and accessories have been emphasized not only in electronic products such as notebook computers, air conditioners and refrigerators, but also in exterior products of home appliances, The design of the feeling is getting popular.

이에, 상기와 같은 제품의 표면에 다양한 무늬를 직접 인쇄하거나, 제품의 표면에 별도로 제작된 장식물을 부착하여 무늬를 형성함으로써, 제품의 품질 및 품격을 높여 상품가치를 증대시키고, 높은 부가가치를 창출하고 있다.Accordingly, various patterns are directly printed on the surface of the product, or the decorative material separately formed on the surface of the product is formed to form the pattern, thereby increasing the quality and the quality of the product to increase the value of the product, have.

특히, 상기 화장품 케이스의 경우, 디자인에 민감한 여성들이 주로 사용하기 때문에 내용물을 담아 보관하는 기능 이외에, 사용자의 시각적 심미감을 충족시키는 기능 또한 중요한 부분을 차지하게 된다.Particularly, in the case of the above-mentioned cosmetic case, since it is mainly used by design-sensitive women, the function of satisfying the visual aesthetics of the user is also an important part in addition to the function of storing contents.

이에 따라, 상기 화장품 케이스가 고급스러운 이미지를 갖도록 하는 방법이 다양하게 개발되고 있으며, 그 중 하나로 자개(조개껍데기를 공예품 제작용이나 장신구용 재료로 활용하기 위해 가공한 것)를 이용하여 제품의 표면에 무늬를 형성하는 방법이 개발되었다.Accordingly, various methods have been developed to make the cosmetic case have a luxurious image. One of the methods is to use a mother-of-pearl (a shell-shaped shell made of a material for use as a craft material or an ornamental material) A method has been developed to form a pattern on a substrate.

상기와 같은 종래 기술로 도 1에서 보는 바와 같이 대한민국 등록실용신안 제20-0334500호(자개칠 명판을 접목한 콤팩트 용기)가 개시되었다.As shown in Fig. 1, the Korean Registered Utility Model No. 20-0334500 (a compact container with a nameplate of a mother-of-pearl) is disclosed.

상기 종래 기술은 금속성 재질 또는 합성수지 재질의 명판에 원하는 색으로 도색한 다음, 열처리로 건조시킨 후, 오려진 자개에 아교풀 칠을 하고 도색된 명판위에 올려 놓고 뜨겁게 데운 인두로 자개를 눌러 지지면서 붙이고 난 후, 상기 자개가 붙여진 명판 표면을 전체적으로 UV 코팅이나 우레탄 코팅으로 칠을 하여 명판에 형성된 자개 고유의 아름다운 색채나 빛깔을 오래 유지할 수 있도록 한 것이다.In the above prior art, a desired color is painted on a nameplate made of a metallic material or a synthetic resin, followed by drying by heat treatment, glueing the cut-out mother-of-pearl, placing it on a painted name plate, pressing the mother- After that, the surface of the nameplate with the mother-of-pearl is painted with UV coating or urethane coating as a whole, so that the beautiful color and color of the mother-of-pearl formed on the nameplate can be maintained for a long time.

하지만, 상기 종래 기술은 자개를 콤팩트 용기의 명판의 크기에 맞추어 자른 후, 상기 자개를 아교풀과 인두를 이용하여 명판에 부착해야 하므로 제조 공정이 까다롭고, 이로 인해 제조 시간이 오래 소요되어 생산성이 떨어지는 문제점이 있었으며, 제조 공정 중 상기 자개가 훼손되는 문제점이 있었다.However, the above-mentioned prior art requires that the mother-of-pearl is cut to fit the size of the nameplate of the compact container and then the mother-of-pearl is attached to the nameplate by using glue paste and the phosphorus so that the manufacturing process is complicated, There is a problem that the mother tongue is damaged during the manufacturing process.

또한, 상기 종래 기술은 상대적으로 고가인 자개를 지속적으로 구입하여 사용, 소모해야 하기 때문에 생산 원가가 상승 되고, 매번 생산되는 제품마다 자개 무늬가 달라져 일정한 자개 무늬로 대량생산을 할 수 없는 문제점이 있었다. In addition, the above-mentioned prior art has a problem in that the production cost is increased because the relatively expensive mother-of-pearl is constantly purchased, consumed and consumed, and the mother-of-pearl pattern is changed for every product produced every time, .

본 발명은 상기와 같은 문제점을 해결하기 위해 안출된 것으로, 제품의 외관에 부착되는 장식판에 있어서, 상기 장식판의 베이스판 표면에 UV액을 도포하고, 상기 UV액이 도포된 베이스판을 자개가 부착된 자개 금형으로 가압하여 상기 베이스판의 표면에 자개 무늬를 형성한 후, 금속 증착 등을 하여 실제 자개 무늬와 같은 효과를 내도록 함으로써, 고가의 자개가 소모되지 않으면서 일정한 자개 무늬로 대량 생산이 가능하도록 한 자개 금형에 의해 제조된 자개 장식판을 제공하는 데 목적이 있다.SUMMARY OF THE INVENTION The present invention has been conceived in order to solve the above-mentioned problems, and it is an object of the present invention to provide a decorative plate to be attached to the exterior of a product by applying a UV liquid on the surface of the base plate of the decorative plate, The base plate is pressed with a mother die mold to form a mother lacquer pattern on the surface of the base plate and then metal deposition or the like is performed to achieve the same effect as the actual mother lacquer pattern so that the mother lacquer can be mass- The present invention has been made in view of the above problems, and it is an object of the present invention to provide a mother-

또한, 본 발명은 베이스판 및 자개 금형을 준비하는 준비단계와, 상기 베이스판의 표면에 UV액을 도포하는 UV액 도포단계와, 상기 UV액이 도포된 베이스판을 자개가 부착된 자개 금형으로 가압하여 베이스판의 표면에 자개 무늬를 형성하는 자개 무늬 형성단계와, 상기 자개 무늬가 형성된 베이스판의 표면을 금속 증착하는 금속 증착단계 및 상기 베이스판을 일정한 크기로 절단하는 절단단계로 이루어지도록 함으로써, 자개 무늬를 갖는 장식판의 제조 공정이 연속적이며, 신속하게 진행되어 생산성이 개선된 자개 장식판의 제조방법을 제공하는 데 목적이 있다.The present invention also relates to a method of manufacturing a base plate and a mother die, comprising the steps of: preparing a base plate and a mother die; applying a UV solution onto the surface of the base plate; applying a base plate coated with the UV solution to a mother die Forming a mother-of-pearl pattern on the surface of the base plate by pressurization, a metal deposition step of metallizing the surface of the base plate on which the mother-of-pearl pattern is formed, and a cutting step of cutting the base plate to a predetermined size It is an object of the present invention to provide a method for manufacturing a mother-of-pearl plate in which a manufacturing process of a decorative plate having a mother-of-pearl pattern is continuous and rapidly performed to improve productivity.

본 발명은 제품의 표면에 부착되는 장식판에 있어서,The present invention relates to a decorative plate attached to a surface of an article,

상기 장식판은 베이스판과, 상기 베이스판의 표면에 UV액을 도포하여 자개 무늬를 형성한 자개 무늬 형성층 및 상기 자개 무늬 형성층의 표면에 금속 증착하여 형성된 금속 증착층으로 구성되되,Wherein the decorative plate comprises a base plate, a mother-of-pearl pattern layer formed by applying a UV liquid on the surface of the base plate, and a metal deposition layer formed by metal deposition on the surface of the mother-

상기 자개 무늬 형성층은 베이스판의 상부 표면에 UV액을 도포하고, 상기 UV액을 자개 금형으로 가압한 후, 경화시켜 형성되는 것을 특징으로 하는 자개 금형에 의해 제조된 자개 장식판을 제공한다.Wherein the mother-of-pearl patterning layer is formed by applying a UV liquid onto an upper surface of a base plate, pressing the UV liquid with a mother-of-pearl mold, and then curing the mother liquid.

또한, 상기 베이스판의 상부 표면 또는 베이스판의 하부 표면 또는 금속 증착층의 상부 표면 중 어느 한 곳 이상에는 인쇄층이 더 형성되는 것을 특징으로 한다.A printed layer is further formed on at least one of the upper surface of the base plate, the lower surface of the base plate, and the upper surface of the metal deposition layer.

또한, 상기 베이스판은 투명한 재질로 형성되는 것을 특징으로 한다.Further, the base plate is formed of a transparent material.

또한, 상기 금속 증착층은 알루미늄(Al), 금(Au), 니켈(Ni), 크롬(Cr), 구리(Cu), 티타늄(Ti), 주석(Tin)으로 이루어진 금속군 중에서 어느 하나 이상으로 증착되는 것이 바람직하다.The metal deposition layer may be formed of any one or more selected from the group consisting of Al, Au, Ni, Cr, Cu, Ti, and Tin It is preferable to be deposited.

또한, 상기 자개 금형은 금형의 일측면에 자개를 부착하여 형성되는 것을 특징으로 한다.In addition, the self-contained metal mold is formed by attaching a mother-of-pearl to one side of the metal mold.

본 발명은 베이스판 및 자개 금형을 준비하는 준비단계;The present invention provides a method of manufacturing a base plate and a mother die;

상기 베이스판의 표면에 UV액을 도포하는 UV액 도포단계;Applying a UV liquid onto the surface of the base plate;

상기 UV액이 도포된 베이스판을 자개가 부착된 자개 금형으로 가압하여 베이스판의 표면에 자개 무늬를 형성하는 자개 무늬 형성단계;A mother-of-pearl pattern forming step of forming a mother-of-pearl pattern on the surface of the base plate by pressing the base plate coated with the UV liquid with a mother-of-pearl-

상기 자개 무늬가 형성된 베이스판의 표면을 금속 증착하는 금속 증착단계를 포함하는 자개 장식판의 제조방법을 제공한다.And a metal deposition step of metal-depositing the surface of the base plate on which the mother-of-pearl pattern is formed.

또한, 상기 금속 증착단계에서 금속 증착된 베이스판을 일정한 형태로 절단하는 절단단계를 더 포함하는 것을 특징으로 한다.The method may further include a cutting step of cutting the metal-deposited base plate into a predetermined shape in the metal deposition step.

또한, 상기 준비단계와 UV액 도포단계 사이 또는 UV액 도포단계와 자개 무늬 형성단계 사이에는 초발수 증착 및 코팅단계를 더 포함하는 것을 특징으로 한다.In addition, the method further includes an ultra water-repellent deposition and coating step between the preparation step and the UV solution application step or between the UV solution application step and the mother skin pattern formation step.

또한, 상기 자개 무늬 형성단계는 UV액이 도포된 베이스판을 자개 금형으로 가압하는 가압단계와, 상기 베이스판과 자개 금형 사이에서 UV액을 확산시키는 UV액 확산단계와, 상기 베이스판으로부터 자개 금형을 분리하는 분리단계 및 상기 UV액을 일정 시간동안 경화시키는 UV액 경화단계로 이루어지는 것을 특징으로 한다.The mother-of-pearl forming step includes a pressing step of pressing the base plate coated with the UV liquid with a mother-of-pearl die, a UV liquid diffusion step of diffusing the UV liquid between the base plate and the mother- And a UV curing step of curing the UV liquid for a predetermined time.

또한, 상기 준비단계와 UV액 도포단계 사이에 또는 금속 증착단계 이후에 인쇄단계를 더 포함하는 것을 특징으로 한다.Further, the method further comprises a printing step between the preparation step and the UV solution application step or after the metal deposition step.

본 발명에 따른 자개 금형에 의해 제조된 자개 장식판은 베이스판 표면에 UV액을 도포하고, 상기 UV액이 도포된 베이스판을 자개가 부착된 자개 금형으로 가압하여 상기 베이스판의 표면에 자개 무늬를 형성한 후, 금속 증착 등을 하여 실제 자개 무늬와 같은 모습이 나타나도록 함으로써, 고가의 자개가 소모되지 않으면서 일정한 자개 무늬로 대량 생산이 가능한 효과가 있다.The mother-of-lacquer plate produced by the mother-of-pearl mold according to the present invention is obtained by applying a UV liquid onto the surface of a base plate, pressing the base plate coated with the UV liquid with a mother- After forming, it is possible to mass-produce a uniform mother-of-pearl pattern without consuming the expensive mother-of-pearl by making the same appearance as the actual mother-of-pearl pattern by metal deposition or the like.

또한, 본 발명에 따른 자개 장식판의 제조방법은 베이스판 및 자개 금형을 준비하는 준비단계와, 상기 베이스판의 표면에 UV액을 도포하는 UV액 도포단계와, 상기 UV액이 도포된 베이스판을 자개가 부착된 자개 금형으로 가압하여 베이스판의 표면에 자개 무늬를 형성하는 자개 무늬 형성단계와, 상기 자개 무늬가 형성된 베이스판의 표면을 금속 증착하는 금속 증착단계 및 상기 베이스판을 일정한 크기로 절단하는 절단단계로 이루어지도록 함으로써, 자개 무늬를 갖는 장식판의 제조 공정이 연속적이며, 신속하게 진행되어 생산성이 개선되는 효과가 있다.A method of manufacturing a mother-of-pearl panel according to the present invention includes the steps of preparing a base plate and a mother-of-pearl mold; applying a UV solution onto the surface of the base plate; A mother-metal pattern forming step of forming a mother-of-pearl pattern on the surface of the base plate by pressing with a mother-piece mold having mother-of-pearl, a metal deposition step of metallizing the surface of the base plate on which the mother- So that the manufacturing process of the decorative plate having the mother-of-pearl pattern can be continuously performed, and the productivity can be improved.

도 1은 자개칠 명판을 접목한 콤팩트 용기.
도 2는 본 발명의 일 실시예에 따른 자개 장식판의 사시도.
도 3은 본 발명의 일 실시예에 따른 자개 장식판의 단면도.
도 4는 본 발명의 일 실시예에 따른 자개 장식판의 금속 증착층 상부 표면에 인쇄층이 형성된 모습을 나타내는 단면도.
도 5는 본 발명의 일 실시예에 따른 자개 장식판의 베이스판 하부 표면에 인쇄층이 형성된 모습을 나타내는 단면도.
도 6은 본 발명의 일 실시예에 따른 자개 장식판의 베이스판 상부 표면에 인쇄층이 형성된 모습을 나타내는 단면도.
도 7은 본 발명의 일 실시예에 따른 자개 장식판 제조방법의 플로우차트
도 8은 본 발명의 일 실시예에 따른 자개 장식판 제조방법 중 자개 무늬 형성단계의 플로우차트.
도 9는 본 발명의 일 실시예에 따른 자개 장식판 제조방법 중 자개 무늬 형성단계에서 UV액이 도포된 베이스판을 자개 금형으로 가압하는 모습을 나타내는 사시도.
도 10은 본 발명의 일 실시예에 따른 자개 장식판 제조방법 중 자개 무늬 형성단계에서 롤러에 의해 베이스판과 자개 금형 사이에 도포된 UV액이 확산되는 모습을 나타내는 사시도.
도 11은 본 발명의 일 실시예에 따른 자개 장식판 제조방법 중 자개 무늬 형성단계에서 베이스판으로부터 자개 금형이 분리되는 모습을 나타내는 사시도.
도 12와 도 13은 본 발명의 일 실시예에 따른 자개 장식판 제조방법에 초발수 증착 및 코팅단계가 더 포함된 플로우차트.
도 14와 도 15는 본 발명의 일 실시예에 따른 자개 장식판 제조방법에 인쇄단계가 더 포함된 플로우차트.Fig. 1 is a compact container obtained by grafting a nameplate of a mother-of-pearl.
2 is a perspective view of a motherboard according to an embodiment of the present invention;
3 is a cross-sectional view of a motherboard according to an embodiment of the present invention.
4 is a cross-sectional view illustrating a printed layer formed on the upper surface of a metal deposition layer of a mother-of-pearl panel according to an embodiment of the present invention.
5 is a cross-sectional view showing a printed layer formed on a lower surface of a base plate of a mother-of-pearl panel according to an embodiment of the present invention.
6 is a cross-sectional view showing a printed layer formed on a surface of a base plate of a mother-of-pearl panel according to an embodiment of the present invention.
7 is a flowchart of a method for manufacturing a mother and son's placket according to an embodiment of the present invention
8 is a flowchart of a mother-of-pearl pattern forming process of a method for manufacturing a mother-of-pearl panel according to an embodiment of the present invention.
9 is a perspective view showing a state in which a base plate coated with a UV liquid is pressed by a mother-of-pearl mold in the mother-of-pearl patterning process of the method of manufacturing the mother-of-pearl plate according to an embodiment of the present invention.
10 is a perspective view showing a state in which a UV liquid applied between a base plate and a mother-of-pearl mold is spread by a roller in a mother-of-pearl patterning process among the method of manufacturing a mother-of-pearl plate according to an embodiment of the present invention.
11 is a perspective view showing a state in which a mother-of-pearl die is separated from a base plate in a mother-of-baby pattern formation process of the method of manufacturing a mother-of-pearl plate according to an embodiment of the present invention.
12 and 13 are flow charts that further include an ultra water-repellent deposition and coating step in a method of manufacturing a mother-of-pearl plate according to an embodiment of the present invention.
14 and 15 are flow charts further including a printing step in a method of manufacturing a mother and son's placket according to an embodiment of the present invention.

본 발명과 본 발명의 실시에 의해 달성되는 기술적 과제는 다음에서 설명하는 바람직한 실시예들에 의해 명확해 질 것이다. 이하, 첨부된 도면을 참조하여 본 발명의 일 실시예에 따른 자개 금형에 의해 제조된 자개 장식판을 상세히 살펴보면 다음과 같다.BRIEF DESCRIPTION OF THE DRAWINGS The above and other objects, features and advantages of the present invention will be more apparent from the following detailed description taken in conjunction with the accompanying drawings, in which: FIG. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will now be described in detail with reference to the annexed drawings.

도 2는 본 발명의 일 실시예에 따른 자개 장식판의 사시도이고, 도 3은 본 발명의 일 실시예에 따른 자개 장식판의 단면도이다.FIG. 2 is a perspective view of a mother-of-pearl panel according to an embodiment of the present invention, and FIG. 3 is a sectional view of a mother-house panel according to an embodiment of the present invention.

본 발명의 일 실시예에 따른 자개 금형에 의해 제조된 자개 장식판은 베이스판(10)과, 상기 베이스판(10)의 표면에 UV액(U)을 도포하여 자개 무늬를 형성한 자개 무늬 형성층(20) 및 상기 자개 무늬 형성층(20)의 표면에 금속 증착하여 형성된 금속 증착층(30)으로 구성되되, 상기 자개 무늬 형성층(20)은 베이스판(10)의 상부 표면에 UV액(U)을 도포하고, 상기 UV액(U)을 자개 금형(50)으로 가압한 후, 경화시켜 형성되는 것을 특징으로 한다.A mother-of-pearl decoration plate manufactured by a mother-of-pearl mold according to an embodiment of the present invention comprises a base plate 10 and a mother-of-pearl pattern layer (U) on the upper surface of the base plate (10), and a metal deposition layer (30) formed by depositing metal on the surface of the mother glass pattern formation layer (20) Applying the UV liquid (U) to the mother die (50), and curing the UV liquid (U).

상기 장식판(1)은 제품의 외관에 부착되어 제품의 심미성을 향상시키는 동시에, 소비자에게 상기 제품의 정보를 제공하는 역할을 하게 된다.The decorative plate 1 is attached to the outer surface of the product to improve the aesthetics of the product and to provide the information of the product to the consumer.

상기 장식판(1)은 도 3에서 보는 바와 같이 베이스판(10)과 자개 무늬 형성층(20) 및 금속 증착층(30)을 포함하는 층상 구조를 갖는다.The decorative plate 1 has a layered structure including a base plate 10, a mother-of-pearl patterning layer 20 and a metal deposition layer 30, as shown in FIG.

상기 베이스판(10)은 얇은 두께를 갖는 평평한 형태의 판으로 형성되거나, 중앙 부분이 상부로 볼록한 또는 오목한 곡면 형태의 판으로 형성될 수 있다.The base plate 10 may be formed of a flat plate having a thin thickness, or may be formed of a plate having a convex or concave curved surface shape having a central portion upward.

상기 베이스판(10)은 투명한 재질로 형성되되, 합성수지 재질 또는 유리 재질로 형성되는 것이 바람직하며, 특히 PC(Polycarbonate), PET(Polyethylene terephthalate) 재질로 형성되는 것이 바람직하다.The base plate 10 is formed of a transparent material, and is preferably formed of a synthetic resin material or a glass material. The base plate 10 is preferably made of PC (Polycarbonate) or PET (polyethylene terephthalate).

상기 자개 무늬 형성층(20)은 도 2에서 보는 바와 같이 베이스판(10)의 상부 표면에 형성되어 실제 자개와 같이 입체적인 형태의 자개 무늬를 띄게 된다.The mother-of-pearl pattern layer 20 is formed on the upper surface of the base plate 10 as shown in FIG. 2, and has a three-dimensional pattern like a mother-of-pearl.

상기 자개 무늬 형성층(20)은 베이스판(10)에 UV(ultraviolet rays)액을 도포하고, 일측에 자개(52)가 부착된 자개 금형(50)으로 상기 UV액(U)이 도포된 부분을 가압하여 형성된다.The mother-of-pearl embossing layer 20 is formed by applying ultraviolet rays to a base plate 10 and forming a mother die 50 having a mother shell 52 attached on one side thereof with a portion coated with the UV liquid U And is pressurized.

즉, 베이스판(10)의 일측면에 UV액(U)을 도포하고, 상기 UV액(U)이 도포된 부분을 자개 금형(50)으로 가압하게 되면, 상기 자개 금형(50)에 부착된 자개(52)가 UV액(U)이 도포된 부분에 찍히면서 상기 베이스판(10)에 입체적인 자개 무늬가 나타나게 되고, 이후 상기 UV액(U)을 자외선 건조를 통해 일정 시간 경화시킴으로써, 상기 베이스판(10)의 일측면에 자개 무늬 형성층(20)을 만드는 것이다.That is, when the UV liquid U is applied to one side of the base plate 10 and the portion coated with the UV liquid U is pressed by the mother die 50, The mother liquor 52 is stuck on the portion to which the UV liquid U is applied so that a three-dimensional mother liquor pattern appears on the base plate 10 and then the UV liquid U is cured for a certain time by ultraviolet drying, Thereby forming the mother-of-pearl embossing layer 20 on one side of the plate 10.

이에 따라, 본 발명의 일 실시예에 따른 자개 장식판은 자개(52)가 부착된 자개 금형(50)으로 동일한 자개 무늬를 갖는 장식판(1)을 지속적으로 생산할 수 있어, 고가의 자개가 소모되지 않으면서 일정한 자개 무늬를 갖는 장식판(1)을 대량 생산할수 있게 된다.Accordingly, the mother-of-pearl panel according to the embodiment of the present invention can continuously produce the decorative plate 1 having the same mother-of-fringe pattern with the mother-of-pearl die 50 having the mother-daughter pair 52 attached thereto, It is possible to mass-produce the decorative plate (1) having a regular mother-of-pearl pattern.

상기 자개 금형(50)은 실제 자개(52)를 얇게 잘라 금형판의 일측면에 부착한 다음, 깨끗하게 세척하여 형성된다.The mother die 50 is formed by thinly cutting the mother mother die 52 and attaching the mother die 52 to one side of the die plate, and then cleaning the mother die 52 cleanly.

상기 금속 증착층(30)은 도 3에서 보는 바와 같이 자개 무늬 형성층(20)의 상부 표면에 금속 증착하여 형성된다.As shown in FIG. 3, the metal deposition layer 30 is formed by vapor-depositing metal on the upper surface of the mother-of-

상기 금속 증착층(30)은 다양한 금속으로 증착되는데, 특히 알루미늄(Al), 금(Au), 니켈(Ni), 크롬(Cr), 구리(Cu), 티타늄(Ti), 주석(Tin)으로 이루어진 금속군 중에서 어느 하나 이상으로 증착되는 것이 바람직하다.The metal deposition layer 30 may be formed of various metals such as aluminum, gold, nickel, chromium, copper, titanium and tin. It is preferable that the metal is deposited in at least one of the metal groups.

예를 들어, 자개 무늬 형성층(20)의 상부 표면을 알루미늄(Al)으로 증착할 경우 상기 자개 무늬가 은 색상을 띄게 되며, 구리(Cu)로 증착할 경우 상기 자개 무늬가 적색 또는 금 색상을 띄게 된다.For example, when the upper surface of the mother-of-pearl pattern layer 20 is vapor-deposited with aluminum (Al), the mother-of-pearl pattern is silver-colored. When the copper is deposited by copper (Cu) do.

또한, 상기와 같은 여러 종류의 금속을 혼합하여 증착함으로써, 상기 자개 무늬가 다양한 빛깔로 표현되도록 할 수도 있다.In addition, by mixing and depositing the above-mentioned various metals, the mother-of-pearl pattern can be expressed in various colors.

따라서, 상기 자개 무늬 형성층(20)의 자개 무늬가 사용자에게 다양한 색상으로 비춰지도록 할 수 있으며, 또한 상기 자개 무늬가 보다 부각되는 효과를 나타낼 수 있게 된다.Accordingly, the mother-of-pearl pattern of the mother-of-pearl pattern layer 20 can be displayed to the user in various colors, and the mother-of-pearl pattern can be more emphasized.

도 4는 본 발명의 일 실시예에 따른 자개 장식판의 금속 증착층 상부 표면에 인쇄층이 형성된 모습을 나타내는 단면도이고, 도 5는 본 발명의 일 실시예에 따른 자개 장식판의 베이스판 하부 표면에 인쇄층이 형성된 모습을 나타내는 단면도이며, 도 6은 본 발명의 일 실시예에 따른 자개 장식판의 베이스판 상부 표면에 인쇄층이 형성된 모습을 나타내는 단면도이다.FIG. 4 is a cross-sectional view illustrating a printed layer formed on the upper surface of a metal deposition layer of a mother-of-jewelry plate according to an embodiment of the present invention, FIG. 5 is a cross- FIG. 6 is a cross-sectional view illustrating a printed layer formed on a surface of a base plate of a mother-of-pearl panel according to an embodiment of the present invention.

상기 금속 증착층(30)의 상부 표면에는 도 4에서 보는 바와 같이 인쇄층(40)이 더 형성되어 상기 인쇄층(40)이 외부로 직접 노출되면서 보여지도록 할 수 있다.As shown in FIG. 4, a print layer 40 is further formed on the upper surface of the metal deposition layer 30 so that the print layer 40 can be directly exposed to the outside.

상기 인쇄층(40)은 다양한 컬러(color)의 로고, 문자, 이미지, 패턴 등으로 형성되어 자개 장식판(1)의 아름다움을 더욱 돋보이게 할 수 있다.The print layer 40 may be formed of a variety of colors, such as a logo, a letter, an image, a pattern, etc., to further enhance the beauty of the mother-of-

상기 인쇄층(40)은 패드인쇄, 옵셋인쇄, 스크린인쇄, 전사인쇄 및 디지털 인쇄 중 어느 하나를 선택하여 인쇄되는 것이 바람직하다.The printing layer 40 is preferably printed by selecting one of pad printing, offset printing, screen printing, transfer printing, and digital printing.

또한, 상기 베이스판(10)의 하부 표면에는 도 5에서 보는 바와 같이 인쇄층(40)이 더 형성되어 상기 인쇄층(40)이 베이스판(10)과 자개 무늬 형성층(20)을 통과하면서 비춰지도록 할 수 있다.5, a print layer 40 is further formed on the lower surface of the base plate 10 so that the print layer 40 passes through the base plate 10 and the mother-of- .

상기와 같이 인쇄층(40)이 베이스판(10)의 하부면에 형성된 경우 상기 인쇄층(40)은 다양한 컬러(color)의 로고, 문자, 이미지, 패턴 등으로 형성될 수 있는 것은 물론, 하부면 전체에 형성될 수도 있다. 이처럼, 인쇄층(40)이 베이스판(10)의 하부면 전체에 형성되면 상기 인쇄층(40)은 외부로 보여지는 자개 무늬의 배경 색상을 결정 짓게 된다.When the print layer 40 is formed on the lower surface of the base plate 10 as described above, the print layer 40 may be formed of various colors, such as logos, letters, images, patterns, Or may be formed over the entire surface. As such, when the print layer 40 is formed on the entire lower surface of the base plate 10, the print layer 40 determines the background color of the naked-eye pattern seen to the outside.

또한, 상기 베이스판(10)과 자개 무늬 형성층(20) 사이에는 도 6에서 보는 바와 같이 인쇄층(40)이 더 형성되어 상기 인쇄층(40)이 자개 무늬 형성층(20)을 통과하면서 비춰지도록 할 수 있다.6, a print layer 40 is further formed between the base plate 10 and the mother-of-pearl pattern layer 20 so that the print layer 40 can be seen to pass through the mother pattern 20, can do.

상기와 같이 인쇄층(40)이 장식판(1)의 내측에 형성될 경우, 상기 인쇄층(40)의 다양한 컬러(color)의 로고, 문자, 이미지, 패턴 등이 외부로 은은하면서 자연스럽게 비춰지게 된다.When the print layer 40 is formed on the inner side of the decorative plate 1 as described above, various colors of logo, characters, images, patterns, etc. of the print layer 40 are gently and smoothly projected to the outside .

물론, 상기 인쇄층(40)은 금속 증착층(30)의 상부 표면 또는 베이스판(10)의 하부 표면 또는 상부 표면 중 어느 한 곳 이상에 함께 형성될 수도 있다. 이와 같이, 인쇄층(40)이 여러 위치에 동시에 형성될 경우 각각의 인쇄층(40)에 형성된 컬러(color)의 로고, 문자, 이미지, 패턴 등은 서로 간섭받지 않도록 각각 적절한 위치에 배치될 수 있고, 심미감을 보다 향상시키기 위해 서로 다른 형태 또는 색상으로 형성될 수 있다.Of course, the print layer 40 may be formed on at least one of the upper surface of the metal deposition layer 30 or the lower surface or the upper surface of the base plate 10. In this way, when the print layer 40 is formed at a plurality of positions at the same time, a logo, a character, an image, a pattern, and the like formed in each print layer 40 can be disposed at appropriate positions And may be formed in different shapes or colors to further improve the sense of beauty.

또한, 상기 금속 증착층(30)의 상부 표면에는 투명 코팅층(미도시)이 더 형성되어 상기 금속 증착층(30)이 벗겨지지 않도록 할 수 있다. 도 4에서 보는 바와 같이, 금속 증착층(30)의 상부 표면에 인쇄층(40)이 형성된 경우에는 상기 인쇄층(40)의 상부에 투명 코팅층(미도시)이 더 형성되어 상기 인쇄층(40)이 벗겨지지 않도록 할 수 있다. 상기 투명 코팅층(미도시)는 투명한 재질의 합성수지 재질 또는 유리 재질로 형성되는 것이 바람직하다.Further, a transparent coating layer (not shown) may be formed on the upper surface of the metal deposition layer 30 to prevent the metal deposition layer 30 from being peeled off. 4, when a printing layer 40 is formed on the upper surface of the metal deposition layer 30, a transparent coating layer (not shown) is further formed on the printing layer 40 to form the printing layer 40 Can be prevented from being peeled off. The transparent coating layer (not shown) is preferably formed of a transparent synthetic resin material or a glass material.

이하, 첨부된 도면을 참조하여 본 발명의 일 실시예에 따른 자개 장식판의 제조방법을 상세히 살펴보면 다음과 같다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, a method for manufacturing a mother-of-pearl panel according to an embodiment of the present invention will be described in detail with reference to the accompanying drawings.

도 7은 본 발명의 일 실시예에 따른 자개 장식판 제조방법의 플로우차트이다.7 is a flowchart of a method of manufacturing a mother-of-mine plate according to an embodiment of the present invention.

본 발명의 일 실시예에 따른 자개 장식판의 제조방법은 도 7에서 보는 바와 같이 준비단계(S100)와, UV액 도포단계(S200)와, 자개 무늬 형성단계(S300)와, 금속 증착단계(S400) 및 절단단계(S500)을 포함한다.7, a method of manufacturing a mother-of-pearl panel according to an exemplary embodiment of the present invention includes a preparing step S100, a UV solution applying step S200, a mother-of-pearl pattern forming step S300, a metal deposition step S400 And a cutting step S500.

상기 준비단계(S100)는 자개 장식판을 제조하기 위해 베이스판(10)과 상기 베이스판(10)의 일측면에 자개 무늬를 형성하는 자개 금형(50)을 미리 준비하는 단계이다.The preparation step S100 is a step of preparing a base plate 10 and a mother-of-mind mold 50 for forming a mother-of-pearl pattern on one side of the base plate 10 in order to manufacture a mother-of-

앞서 설명한 바와 같이, 상기 베이스판(10)은 투명한 재질의 판 형태이며, 상기 자개 금형(50)의 일측에는 자개(52)가 부착되어 있다.As described above, the base plate 10 is in the form of a transparent plate, and a mother shell 52 is attached to one side of the mother die 50.

상기 UV액 도포단계(S200)는 베이스판(10)의 상부 표면에 UV액(U)을 도포하는 단계이다. 상기 UV액 도포단계(S200)에서 베이스판(10)의 상부 표면에 도포되는 UV액(U)의 두께를 다르게 함에 따라, 이후 자개 무늬 형성단계(S300)에서 형성되는 자개 무늬의 입체감이 조절될 수 있다.The UV liquid application step (S200) is a step of applying the UV liquid (U) onto the upper surface of the base plate (10). As the thickness of the UV liquid (U) applied to the upper surface of the base plate (10) is changed in the UV liquid application step (S200), the three-dimensional effect of the mother liquor pattern formed in the mother lattice pattern formation step (S300) .

도 12와 도 13은 본 발명의 일 실시예에 따른 자개 장식판 제조방법에 초발수 증착 및 코팅단계가 더 포함된 플로우차트이다.12 and 13 are flowcharts further including an ultra water-repellent deposition and coating step in the method of manufacturing a mother-of-pearl panel according to an embodiment of the present invention.

도 12와 도 13에서 보는 바와 같이, 상기 준비단계(S100)와 UV액 도포단계(S200) 사이 또는 UV액 도포단계(S200)와 자개 무늬 형성단계(S300) 사이에는 자개 금형(50)의 자개(52) 표면에 초발수(超發水) 증착 또는 코팅을 진행하는 초발수 증착 및 코팅단계(S600)를 더 포함할 수 있다.As shown in FIGS. 12 and 13, between the preparation step (S100) and the UV solution application step (S200) or between the UV solution application step (S200) and the mother skin pattern formation step (S300) (S600) for super-water-repellent deposition or coating on the surface of the substrate (52).

상기 초발수(超發水)는 물을 흡수하지 않고 바깥으로 튕겨내는 성질을 말하는 것으로, 상기 초발수 증착 및 코팅이란 어떤 물질의 표면이 상기와 같은 성질을 갖도록 증착 또는 코팅하는 것을 의미한다.The super water repellent refers to a property of repelling water without absorbing water. The super water repellent deposition and coating means that the surface of a substance has a property as described above.

상기 초발수 증착 및 코팅단계(S600)는 UV액(U)이 도포된 베이스판(10)을 자개 금형(50)으로 가압하였다가 분리할 때, 상기 자개 금형(50)과 베이스판(10)이 용이하게 떨어질 수 있도록 하기 위한 것이다.The super water-repellent deposition and coating step S600 is performed by pressing the mother die 50 and the base plate 10 when the base plate 10 coated with the UV liquid U is pressed and separated by the mother die 50, So that it can easily fall.

도 8은 본 발명의 일 실시예에 따른 자개 장식판 제조방법 중 자개 무늬 형성단계의 플로우차트이고, 도 9는 본 발명의 일 실시예에 따른 자개 장식판 제조방법 중 자개 무늬 형성단계에서 UV액이 도포된 베이스판을 자개 금형으로 가압하는 모습을 나타내는 사시도이며, 도 10은 본 발명의 일 실시예에 따른 자개 장식판 제조방법 중 자개 무늬 형성단계에서 롤러에 의해 베이스판과 자개 금형 사이에 도포된 UV액이 확산되는 모습을 나타내는 사시도이고, 도 11은 본 발명의 일 실시예에 따른 자개 장식판 제조방법 중 자개 무늬 형성단계에서 베이스판으로부터 자개 금형이 분리되는 모습을 나타내는 사시도이다.FIG. 8 is a flowchart illustrating a method of manufacturing a mother-of-pearl pattern according to an exemplary embodiment of the present invention. FIG. 9 is a flowchart illustrating a method of manufacturing a mother- FIG. 10 is a perspective view showing a state in which a base plate is pressurized with a mother-of-pearl mold according to an embodiment of the present invention. FIG. 11 is a perspective view showing a state in which a mother-of-pearl mold is separated from a base plate in a mother-house pattern formation process of the method of manufacturing a mother-of-pearl plate according to an embodiment of the present invention.

상기 자개 무늬 형성단계(S300)는 UV액(U)이 도포된 베이스판(10)을 자개(52)가 부착된 자개 금형(50)으로 가압하여 상기 베이스판(10)의 표면에 자개 무늬를 형성하는 단계이다.The mother-of-pearl pattern forming step S300 includes pressing the base plate 10 coated with the UV liquid U onto the mother plate 50 with the mother shell 52 attached thereto to form a mother-of-pearl pattern on the surface of the base plate 10 .

상기 자개 무늬 형성단계(S300)는 도 8에서 보는 바와 같이 UV액(U)이 도포된 베이스판(10)을 자개 금형(50)으로 가압하는 가압단계(S310)와, 상기 베이스판(10)과 자개 금형(50) 사이에서 UV액(U)을 확산시키는 UV액 확산단계(S320)와, 상기 베이스판(10)으로부터 자개 금형(50)을 분리하는 분리단계(S330) 및 상기 UV액(U)을 일정 시간동안 경화시키는 UV액 경화단계(S340)로 이루어진다.As shown in FIG. 8, the mother-of-pearl pattern forming step S300 includes a pressing step S310 of pressing the base plate 10 coated with the UV liquid U onto the mother die 50, A separating step S330 of separating the mother die 50 from the base plate 10 and a step of separating the UV liquid U from the base plate 10, U) is cured for a predetermined period of time (S340).

상기 가압단계(S310)에서는 도 9에서 보는 바와 같이, 베이스판(10)의 UV액(U)이 도포된 부분을 자개 금형(50)의 자개(52)로 눌러 상기 자개(52)의 패턴을 UV액(U)에 그대로 찍게 된다.9, the portion of the base plate 10 to which the UV liquid U is applied is pressed by the mother shell 52 of the mother die 50 to form the pattern of the mother wafer 52 It is directly photographed in the UV liquid (U).

상기 UV액 확산단계(S320)에서는 도 10에서 보는 바와 같이, 겹쳐진 베이스판(10)과 자개 금형(50)를 한 쌍의 롤러(R) 사이에 넣고 상기 베이스판(10)과 자개 금형(50)이 롤러(R)에 의해 상, 하로 눌려지면서 이동되도록 한다. 이때, 상기 베이스판(10)과 자개 금형(50) 사이에서 UV액(U)이 넓게 확산된다.10, the overlapped base plate 10 and the mother die mold 50 are put between a pair of rollers R, and the base plate 10 and the mother die 50 Are moved upwardly and downwardly by the roller (R). At this time, the UV liquid (U) diffuses widely between the base plate (10) and the mother die mold (50).

상기 분리단계(S330)에서는 이미 초발수 증착 및 코팅단계(S600)에서 자개 금형(50)의 자개(52) 표면에 초발수 증착 및 코팅을 진행하였기 때문에, 도 11에서 보는 바와 같이 베이스판(10)의 일측면으로부터 자개 금형(50)의 자개(52)가 쉽게 분리된다.In the separation step S330, super water-repellent deposition and coating are already performed on the surface of the mother shell 52 of the mother die 50 in the super water-repellent deposition and coating step S600, The mother-of-pearl 52 of the mother-of-metal mold 50 is easily separated.

상기 UV액 경화단계(S340)는 UV액(U)이 자외선 건조를 통해 경화(硬化)되는 것이 바람직하다.In the UV curing step (S340), it is preferable that the UV liquid (U) is cured by ultraviolet drying.

상기 금속 증착단계(S400)는 자개 무늬가 형성된 베이스판(10)의 상부 표면에 금속 증착하는 단계이다. 상기 금속 증착단계(S400)에서는 자개 무늬가 형성된 베이스판(10)을 진공 챔버(미도시)에 투입하고, 진공 조건에서 상기 베이스판(10)의 자개 무늬의 표면을 다양한 금속으로 진공 증착할 수 있다. 이에 따라, 상기 자개 무늬가 다양한 색상으로 비춰지는 동시에, 보다 부각되면서 사용자에게 보여지게 된다.The metal deposition step (S400) is a step of depositing a metal on the upper surface of the base plate 10 on which the mother-of-pearl pattern is formed. In the metal deposition step (S400), the base plate 10 on which the mother-of-pearl pattern is formed is put into a vacuum chamber (not shown), and the surface of the mother-of-pearl pattern of the base plate 10 is vacuum- have. As a result, the mother-of-pearl pattern is displayed in various colors, and is displayed to the user while being highlighted.

상기 절단단계(S500)는 표면에 자개 무늬가 형성되고, 금속 증착된 베이스판(10)을 부착하고자 하는 제품의 외관에 맞추어 원형 또는 다각형 등 다양한 형태로 절단하는 단계이다. 상기 절단단계(S500)에서는 표면에 자개 무늬가 형성되고, 금속 증착된 베이스판(10)이 CNC(computer numerical control) 가공 또는 레이저(laser) 가공에 의해 절단되거나, 프레스(press)를 이용하여 형태를 만드는 타발 가공에 의해 절단되는 것이 바람직하다. The cutting step S500 is a step of cutting a base plate 10, which is formed with a nettle pattern on its surface, into various shapes such as a circular shape or a polygonal shape according to the appearance of a product to which the base plate 10 is attached. In the cutting step S500, the base plate 10 on which the base metal 10 is formed is cut by CNC (computer numerical control) processing or laser processing, It is preferable to cut it by a punching process.

도 14와 도 15는 본 발명의 일 실시예에 따른 자개 장식판 제조방법에 인쇄단계가 더 포함된 플로우차트이다.FIGS. 14 and 15 are flow charts including a printing step in the method of manufacturing the mother and son's placket according to an embodiment of the present invention.

상기 준비단계(S100)와 UV액 도포단계(S200) 사이 또는 금속 증착단계(S400)와 절단단계(S500) 사이에는 인쇄단계(S700)를 더 포함할 수 있다. 상기 인쇄단계(S700)에서는 다양한 컬러(color)의 로고, 문자, 이미지, 패턴 등이 형성되기 때문에, 자개 장식판(1)의 아름다움을 더욱 돋보이게 할 수 있다.A printing step S700 may be further included between the preparation step S100 and the UV solution application step S200 or between the metal deposition step S400 and the cutting step S500. In the printing step S700, a logo, a character, an image, a pattern and the like of various colors are formed, so that the beauty of the mother-of-baby's plate 1 can be further enhanced.

도 14에서 보는 바와 같이, 준비단계(S100)와 UV액 도포단계(S200) 사이에 인쇄단계(S700)를 포함하는 경우 인쇄층(40)을 베이스판(10)의 상부 표면 또는 하부 표면에 형성할 수 있으며, 도 15에서 보는 바와 같이 금속 증착단계(S400)와 절단단계(S500) 사이에 인쇄단계(S700)를 포함하는 경우 인쇄층(40)을 베이스판(10)의 하부 표면 또는 금속 증착층(30)의 상부 표면에 형성할 수 있다.14, when the printing step S700 is included between the preparing step S100 and the UV liquid applying step S200, the printing layer 40 is formed on the upper surface or the lower surface of the base plate 10 15, when the printing step S700 is included between the metal deposition step S400 and the cutting step S500, the printing layer 40 is formed on the lower surface of the base plate 10 or on the metal deposition Layer 30 as shown in FIG.

이상, 본 발명에서 설명한 것은 자개 금형에 의해 제조된 자개 장식판 및 이의 제조방법을 실시하기 위한 하나의 실시예에 불과한 것으로, 본 발명은 상기 실시예에 한정되는 것이 아니다. 첨부된 청구범위에서 청구하는 바와 같이 본 발명의 요지를 벗어남이 없이 당해 발명이 속하는 분야에서 통상의 지식을 가진 자라면 누구든지 다양한 변경 실시가 가능한 범위까지 본 발명의 범위에 속하는 것으로 간주 되어야 할 것이다.As described above, the present invention is only one embodiment for carrying out the method of manufacturing the mother-of-lacquer plate and the method for manufacturing the mother-of-pearl plate made by the mother-of-pearl, and the present invention is not limited to the above embodiments. It will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the present invention as defined by the appended claims and their equivalents. .

1: 장식판 10: 베이스판
20: 자개 무늬 형성층 30: 금속 증착층
40: 인쇄층 50: 자개 금형
52: 자개 S100: 준비단계
S200: UV액 도포단계 S300: 자개 무늬 형성단계
S310: 가압단계 S320: UV액 확산단계
S330: 분리단계 S400: 금속 증착단계
S500: 절단단계 S600: 초발수 증착 및 코팅단계
S700: 인쇄단계1: decorative plate 10: base plate
20: mother-of-pearl patterning layer 30: metal deposition layer
40: print layer 50: mother die
52: mother-of-pearl S100: preparatory step
S200: UV solution application step S300: mother liquor pattern formation step
S310: Pressurization step S320: UV solution diffusion step
S330: Separation step S400: Metal deposition step
S500: Cutting step S600: super water-repellent deposition and coating step
S700: Printing step

Claims (10)

제품의 표면에 부착되는 장식판에 있어서,
상기 장식판은 베이스판과, 상기 베이스판의 표면에 UV액을 도포하여 자개 무늬를 형성한 자개 무늬 형성층 및 상기 자개 무늬 형성층의 표면에 금속 증착하여 형성된 금속 증착층으로 구성되되,
상기 자개 무늬 형성층은 베이스판의 상부 표면에 UV액을 도포하고, 상기 UV액을 자개 금형으로 가압한 후, 경화시켜 형성되는 것을 특징으로 하는 자개 금형에 의해 제조된 자개 장식판.
A decorative plate attached to a surface of a product,
Wherein the decorative plate comprises a base plate, a mother-of-pearl pattern layer formed by applying a UV liquid on the surface of the base plate, and a metal deposition layer formed by metal deposition on the surface of the mother-
Wherein the mother-of-pearl patterning layer is formed by applying a UV liquid onto an upper surface of a base plate, pressing the UV liquid with a mother-of-pearl mold, and then curing the mother liquid.
제 1 항에 있어서,
상기 베이스판의 상부 표면 또는 베이스판의 하부 표면 또는 금속 증착층의 상부 표면 중 어느 한 곳 이상에는 인쇄층이 더 형성되는 것을 특징으로 하는 자개 금형에 의해 제조된 자개 장식판.
The method according to claim 1,
Wherein a printed layer is further formed on at least one of the upper surface of the base plate, the lower surface of the base plate, or the upper surface of the metal deposition layer.
제 1 항에 있어서,
상기 베이스판은 투명한 재질로 형성되는 것을 특징으로 하는 자개 금형에 의해 제조된 자개 장식판.
The method according to claim 1,
Wherein the base plate is made of a transparent material.
제 1 항에 있어서,
상기 금속 증착층은 알루미늄(Al), 금(Au), 니켈(Ni), 크롬(Cr), 구리(Cu), 티타늄(Ti), 주석(Tin)으로 이루어진 금속군 중에서 어느 하나 이상으로 증착되는 것을 특징으로 하는 자개 금형에 의해 제조된 자개 장식판.
The method according to claim 1,
The metal deposition layer is deposited on at least one of a metal group consisting of Al, Au, Ni, Cr, Cu, Ti, and Tin The mother-of-pearl plate being manufactured by a mother-of-pearl die.
제 1 항에 있어서,
상기 자개 금형은 금형의 일측면에 자개를 부착하여 형성되는 것을 특징으로 하는 자개 금형에 의해 제조된 자개 장식판.
The method according to claim 1,
Wherein the mother-of-cord mold is formed by attaching a mother-of-pearl to one side of the mold.
베이스판 및 자개 금형을 준비하는 준비단계;
상기 베이스판의 표면에 UV액을 도포하는 UV액 도포단계;
상기 UV액이 도포된 베이스판을 자개가 부착된 자개 금형으로 가압하여 베이스판의 표면에 자개 무늬를 형성하는 자개 무늬 형성단계;
상기 자개 무늬가 형성된 베이스판의 표면을 금속 증착하는 금속 증착단계를 포함하는 자개 장식판의 제조방법.
Preparing a base plate and a mother die;
Applying a UV liquid onto the surface of the base plate;
A mother-of-pearl pattern forming step of forming a mother-of-pearl pattern on the surface of the base plate by pressing the base plate coated with the UV liquid with a mother-of-pearl-
And a metal deposition step of metal-depositing the surface of the base plate on which the mother-of-pearl pattern is formed.
제 6 항에 있어서,
상기 금속 증착단계에서 금속 증착된 베이스판을 일정한 형태로 절단하는 절단단계를 더 포함하는 것을 특징으로 하는 자개 장식판의 제조방법.
The method according to claim 6,
Further comprising a cutting step of cutting the metal-deposited base plate into a predetermined shape in the metal deposition step.
제 6 항에 있어서,
상기 준비단계와 UV액 도포단계 사이 또는 UV액 도포단계와 자개 무늬 형성단계 사이에는 초발수 증착 및 코팅단계를 더 포함하는 것을 특징으로 하는 자개 장식판의 제조방법.
The method according to claim 6,
Further comprising a super water-repellent deposition and coating step between the preparation step and the UV solution application step or between the UV solution application step and the mother-of-pearl pattern formation step.
제 6 항에 있어서,
상기 자개 무늬 형성단계는 UV액이 도포된 베이스판을 자개 금형으로 가압하는 가압단계와, 상기 베이스판과 자개 금형 사이에서 UV액을 확산시키는 UV액 확산단계와, 상기 베이스판으로부터 자개 금형을 분리하는 분리단계 및 상기 UV액을 일정 시간동안 경화시키는 UV액 경화단계로 이루어지는 것을 특징으로 하는 자개 장식판의 제조방법.
The method according to claim 6,
The mother-of-pearl pattern forming step includes a pressing step of pressing the base plate coated with the UV liquid with a mother-of-pearl die, a UV liquid diffusion step of diffusing the UV liquid between the base plate and the mother-of-pearl die, And a UV curing step of curing the UV liquid for a predetermined period of time.
제 6 항에 있어서,
상기 준비단계와 UV액 도포단계 사이에 또는 금속 증착단계 이후에 인쇄단계를 더 포함하는 것을 특징으로 하는 자개 장식판의 제조방법.The method according to claim 6,
Further comprising a printing step between the preparation step and the UV solution application step or after the metal deposition step.
KR1020170136105A 2017-10-19 2017-10-19 Mother of pearl plate manufactured by mother of pearl mold and manufacturing method thereof KR20190043951A (en)