KR100960818B1 - Manufacturing method of window iml sheet using electro forming mold and uv pattern transfer and iml sheet manufactured by this - Google Patents

Manufacturing method of window iml sheet using electro forming mold and uv pattern transfer and iml sheet manufactured by this Download PDF

Info

Publication number
KR100960818B1
KR100960818B1 KR1020100020701A KR20100020701A KR100960818B1 KR 100960818 B1 KR100960818 B1 KR 100960818B1 KR 1020100020701 A KR1020100020701 A KR 1020100020701A KR 20100020701 A KR20100020701 A KR 20100020701A KR 100960818 B1 KR100960818 B1 KR 100960818B1
Authority
KR
South Korea
Prior art keywords
image
film
pattern
mold
sheet
Prior art date
Application number
KR1020100020701A
Other languages
Korean (ko)
Inventor
박세진
Original Assignee
주식회사 아이엠글로벌
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 아이엠글로벌 filed Critical 주식회사 아이엠글로벌
Priority to KR1020100020701A priority Critical patent/KR100960818B1/en
Application granted granted Critical
Publication of KR100960818B1 publication Critical patent/KR100960818B1/en

Abstract

PURPOSE: A manufacturing method of an IML sheet using an electroformed mold and an ultra violet pattern increase, and the IML sheet manufactured therefrom are provided to variously express images using a transfer system with a UV paint for increasing patterns. CONSTITUTION: A manufacturing method of an IML sheet using an electroformed mold and an ultra violet pattern increase comprises the following steps: preparing an electroformed mold formed with an image processing unit or a hologram processing unit(S1); spraying an UV paint(S2); settling a mother material film(S3); pressing the upper total surface of the mother material film with a compressing roller(S4); curing the UV paint using ultraviolet rays(S5); obtaining an image formation film including images or holograms by a UV imprint, including a UV coating layer by separating the mother material film from the electroformed mold(S6); and forming a printing layer on the rear side of the image formation film(S8).

Description

전주금형 및 유브이 패턴증식을 이용한 아이엠엘 시트 제조방법과 이에 의해 제조된 아이엠엘 시트{MANUFACTURING METHOD OF WINDOW IML SHEET USING ELECTRO FORMING MOLD AND UV PATTERN TRANSFER AND IML SHEET MANUFACTURED BY THIS}Method for manufacturing IML sheet using Jeonju mold and UV pattern growth and manufactured EL sheet manufactured by it
본 발명은 각종 케이스류나 커버류로 사용되는 인몰드(IML; In Mold Labeling) 사출제품을 만드는데 활용하기 위한 아이엠엘(IML; In Mold Laminate)용 시트 제조기술에 관한 것으로서, 더욱 상세하게는 전주금형을 마스터금형으로 사용함과 아울러 UV도료를 이용한 전사방식을 활용함으로써 균일한 제품의 생산을 가능하게 할 뿐만 아니라 홀로그램이나 스핀 또는 헤어라인 등의 정교하면서도 미세한 패턴 형성을 가능하게 하여 심미감 및 입체감을 부여할 수 있도록 한 전주금형 및 유브이 패턴증식을 이용한 아이엠엘(IML) 시트 제조방법과 이에 의해 제조된 아이엠엘 시트에 관한 것이다.
The present invention relates to a sheet manufacturing technology for IML (In Mold Laminate) for use in making In Mold Labeling (IML) injection products used as various cases or covers. In addition to the use of a master mold and the transfer method using UV paint, not only the production of uniform products is possible, but also the delicate and fine pattern formation such as hologram, spin or hairline, etc., gives aesthetic and three-dimensional impression. The present invention relates to an IML sheet manufacturing method using an electroformed mold and UV pattern growth, and to an IML sheet manufactured thereby.
일반적으로 인몰드 사출제품은 투명한 필름 원단에 실크 인쇄로 칼라를 구현한 후 포밍(forming) 및 커팅(cutting)된 필름을 금형에 삽입하여 사출 성형하는 방식으로 만들어지는 제품을 의미한다.In general, an in-mold injection product refers to a product that is formed by inserting a formed and cut film into a mold by forming a color by silk printing on a transparent film fabric and then injection molding.
이러한 인몰드 사출제품은 휴대폰이나 화장품의 케이스류 또는 커버류, 휴대폰의 윈도우 및 각종 전자제품의 윈도우, 전자제품의 키패드류, 자동차 내부패널 등 산업자재로 많이 활용되고 있다.Such in-mold injection products are widely used as industrial materials such as cases or covers of mobile phones or cosmetics, windows of mobile phones and windows of various electronic products, keypads of electronic products, and internal panels of automobiles.
그런데, 종래 상술한 바와 같은 용도로 많이 활용되는 인몰드 사출제품은 인쇄 및 사출을 행하는 공정 중에 불량이 많이 발생하는 등 불량률이 높은 문제점이 있었고, 필름 박리는 물론 제품의 휨 발생 등 후변형의 우려가 큰 문제점이 있었으며, 균일한 제품을 생산하는데 따른 어려움이 있었다.By the way, the in-mold injection molded products that are widely used for the above-mentioned uses have a high defect rate such as a large number of defects during printing and injection process, and there is a concern of post deformation such as film peeling and product warping. There was a big problem, and there was a difficulty in producing a uniform product.
또한, 종래 인몰드 사출제품은 그 표면에 홀로그램이나 스핀 또는 헤어라인 등의 정교하면서도 미세한 패턴을 형성시킬 수 없는 문제점이 있었으며, 이로 인해 시각적 미려함을 위한 심미감 및 입체감 표현의 어려움 등 다양성을 추구하는데 따른 한계가 있었다.
In addition, the conventional in-mold injection products have a problem in that they cannot form elaborate and fine patterns such as holograms, spins, or hairlines on the surface thereof, thereby pursuing diversity such as difficulty in expressing aesthetics and three-dimensional feelings for visual beauty. There was a limit.
본 발명은 상술한 문제점 등을 감안하여 안출된 것으로서, 전주금형을 마스터금형으로 사용함과 아울러 UV도료를 이용한 전사방식을 활용함으로써 균일한 제품의 생산을 가능하게 할 뿐만 아니라 홀로그램이나 스핀 또는 헤어라인 등의 정교하면서도 미세한 패턴 형성을 가능하게 하여 심미감 및 입체감을 부여하는 등 다양성을 추구할 수 있도록 한 전주금형 및 유브이 패턴증식을 이용한 아이엠엘(IML) 시트 제조방법과 이에 의해 제조된 아이엠엘 시트를 제공하는데 그 목적이 있다.The present invention has been made in view of the above-mentioned problems, such as not only enables the production of uniform products by using the electroforming mold as a master mold, but also by using a transfer method using UV coating, as well as holograms, spins, hairlines, etc. Method of manufacturing IML sheet using Jeonju mold and UV pattern growth to enable diversity such as giving aesthetic and three-dimensional impression by enabling fine and fine pattern formation The purpose is to provide.
또한, 본 발명은 기존 인몰드 사출제품에서 지적되고 있는 높은 불량률과 필름 박리의 문제점은 물론 제품의 휨 발생 등 후변형의 우려를 개선할 수 있도록 하는 전주금형 및 유브이 패턴증식을 이용한 아이엠엘(IML) 시트 제조방법과 이에 의해 제조된 아이엠엘 시트를 제공하는데 있다.
In addition, the present invention is IML (IML) using the Jeonju mold and UV pattern growth to improve the problems of high defect rate and film peeling point that is pointed out in the existing in-mold injection products, as well as post-deformation, such as warpage of the product ) Sheet manufacturing method and ILM sheet produced thereby.
본 발명은 정교하면서도 미세한 패턴의 형성을 가능하게 하는 전주 가공을 통해 이미지가공부 및/또는 홀로그램가공부를 형성시킨 전주금형을 구비하는 제1단계; 상기 전주금형의 상면에 UV반응을 갖는 UV도료를 도포하는 제2단계; 상기 UV도료가 도포된 전주금형의 상면으로 모재필름을 안착시키는 제3단계; 상기 모재필름 상부 전체면을 압착롤러로 평탄하게 압착 처리하는 제4단계; 상기 모재필름의 상측에서 자외선을 조사하여 UV도료를 경화시키는 제5단계; 상기 전주금형으로부터 모재필름을 분리해내어 모재필름의 하부면에 위치하여 UV도료층을 갖되 UV전사에 의해 이미지 및/또는 홀로그램이 형성된 이미지형성필름을 얻어내는 제6단계; 상기 이미지형성필름의 배면에 위치하도록 인쇄되며, 빛 투과차단기능의 발휘를 위한 인쇄층을 형성시키는 제7단계를 포함하여 제조되는 전주금형 및 UV패턴증식을 이용한 아이엠엘 시트 제조방법을 특징으로 한다.The present invention comprises a first step of having a pole mold for forming an image processing portion and / or a hologram processing portion through the electroforming processing to enable the formation of a fine and fine pattern; A second step of applying a UV paint having a UV reaction on the upper surface of the electroforming mold; A third step of seating the base film on the upper surface of the electroforming mold to which the UV coating is applied; A fourth step of flat pressing the entire upper surface of the base film with a pressing roller; A fifth step of curing UV paint by irradiating ultraviolet rays from the upper side of the base film; A sixth step of separating the base film from the electroforming mold to obtain an image forming film having a UV coating layer on the lower surface of the base film, the image and / or hologram being formed by UV transfer; It is printed so as to be located on the back of the image forming film, characterized in that the EL sheet manufacturing method using the electroforming mold and UV pattern growth prepared by the seventh step of forming a printed layer for the light transmission blocking function. .
이때, 상기 제6단계와 제7단계 사이에는 이미지형성필름에 인쇄층을 형성하기 전에 건식증착방식에 의한 금속증착막을 형성시키는 단계가 개입될 수 있는 것을 특징으로 한다.At this time, between the sixth step and the seventh step, the step of forming a metal deposition film by a dry deposition method may be involved before forming the printing layer on the image forming film.
본 발명은 상기한 아이엠엘 시트 제조방법에 의해 제조된 아이엠엘 시트를 특징으로 한다.
The present invention is characterized by an IMD sheet manufactured by the IMD sheet manufacturing method described above.
본 발명은 정교하면서도 미세한 패턴 형성이 용이한 전주금형을 마스터금형으로 사용함과 아울러 UV도료를 이용한 전사방식으로 패턴을 증식하므로 각종 이미지를 다양하게 표출시킬 수 있을 뿐만 아니라 홀로그램 등의 패턴을 이중모드로 용이하게 표출시킬 수 있는 유용함을 제공하며, 심미감이나 입체감을 부여할 수 있어 시각적인 미려함을 더해줄 수 있음은 물론 균일한 품질로 아이엠엘 시트를 생산할 수 있게 된다.The present invention uses the electroforming mold, which is easy to form a fine and fine pattern, as a master mold, and also propagates the pattern by a transfer method using UV paint, so that various images can be expressed in various modes as well as patterns such as holograms in dual mode. It provides the usefulness that can be easily expressed, and can add aesthetic or three-dimensional feeling to add visual aesthetic, as well as to produce IML sheet with uniform quality.
본 발명은 기존 인몰드 사출제품에서 지적되고 있는 높은 불량률과 필름 박리의 문제점은 물론 제품의 휨 발생 등 후변형의 우려를 개선할 수 있다.
The present invention can improve the problems of post-deformation, such as the occurrence of warpage of the product as well as problems of high defect rate and film peeling pointed out in the existing in-mold injection products.
도 1은 본 발명의 실시예에 의한 아이엠엘 시트 제조방법을 나타낸 블록흐름도.
도 2는 본 발명의 실시예에 의한 아이엠엘 시트 제조방법을 나타낸 공정도.
도 3은 본 발명에 의해 제조된 아이엠엘용 시트의 적용 예시를 보인 도면.
1 is a block flow diagram showing a method for manufacturing ILM sheet according to an embodiment of the present invention.
Figure 2 is a process chart showing a method of manufacturing ILM sheet according to an embodiment of the present invention.
Figure 3 is a view showing an application example of the sheet for IM produced by the present invention.
본 발명을 첨부한 도면을 참조하여 상세히 설명하면 다음과 같다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.
도 1 및 도 2를 참조하여, 본 발명의 실시예에 의한 전주금형 및 UV 패턴증식을 이용한 아이엠엘(IML; In Mold Laminate) 시트 제조방법은 도 2(a)에서와 같이 각종 문자나 문양 또는 패턴(이하에서는 이들을 통일하는 대체용어로 "이미지"로 지칭하기로 한다.)을 형성하기 위한 이미지가공부(11)를 포함하는 전주금형(10)을 구비한다(S1).1 and 2, an IML sheet manufacturing method using the electroforming mold and UV pattern growth according to an embodiment of the present invention as shown in Figure 2 (a) The electroforming mold 10 including the image processing unit 11 for forming the pattern (hereinafter, referred to as "image" in the alternative terminology for unifying them) is provided (S1).
이때, 상기 전주금형(10)의 이미지가공부(11)는 전주(electro forming) 가공을 통해 음각이나 양각 또는 이들의 혼합형태(음각+양각)를 갖도록 형성시킨 것으로서, 전주금형(10)의 전체를 차지하거나 또는 일부분으로 형성될 수 있다 할 것이며, 이러한 전주금형(10)을 이미지 전사를 위한 마스터금형으로 사용함으로써 NC나 CNC 등의 기계적 가공이나 레이저 가공 또는 사출성형방식에 비해 이미지를 더욱 정교하게 표출시킬 수 있으면서도 미세한 부분까지 용이하게 형성시킬 수 있음은 물론 이미지를 균일하게 복제시킬 수 있는 장점을 제공할 수 있게 된다.At this time, the image processing unit 11 of the electroforming mold 10 is formed to have an intaglio or embossed or a mixed form thereof (engraved + embossed) through electroforming processing, the whole of the electroforming mold 10 The electroforming mold 10 may be used as a master mold for image transfer, thereby making the image more precisely than mechanical processing such as NC or CNC, laser processing, or injection molding. While being able to be expressed, the fine parts can be easily formed, as well as providing an advantage of uniformly replicating an image.
또한, 도시하지는 않았으나 전주금형(10)에는 이미지가공부(11)를 포함하여 홀로그램(간섭 줄무늬)이나 스핀(회전형 무늬) 또는 헤어라인(일자형 무늬) 등의 홀로그램가공부를 전체 또는 일부 배경패턴으로 더 형성시킴으로써 이미지의 이중처리 및 입체감을 부여하여 시각적인 미려함 및 심미감을 더할 수 있도록 구성할 수도 있다 할 것이다.In addition, although not illustrated, the electroforming mold 10 includes an image processing unit 11 and includes a hologram processing unit such as a hologram (interference stripe), a spin (rotational pattern), or a hairline (straight line pattern) as a whole or part of a background pattern. It may also be configured to add a visual aesthetic and aesthetic by giving a double processing and three-dimensional image of the image by further forming.
나아가, 전주 가공에 의해 형성된 전주금형(10)의 이미지가공부(11) 상에 NC나 CNC의 기계적 가공 또는 레이저 가공 등을 부가적으로 더 수행할 수 있다 할 것이며, 또한 이미지가공부(11)가 음각으로 형성된 경우 음각 내에 부분적으로 미세(微細)한 양각부를 포함되게 하거나 또는 양각으로 형성된 경우 양각 내에 부분적으로 미세한 음각부를 포함되게 함으로써 입체감을 부여할 수 있다 할 것이다.Further, the mechanical processing or laser processing of NC or CNC may be additionally performed on the image processing unit 11 of the electroforming mold 10 formed by the electroforming, and the image processing unit 11 may also be performed. In the case of being formed in the intaglio, it is possible to impart a three-dimensional feeling by including a partially fine embossed portion in the intaglio, or when the embossed portion includes a partially fine engraved portion in the embossed.
여기서, 이미지가공부(11)를 포함하는 전주금형(10)은 휴대폰이나 화장품의 케이스류 또는 커버류, 휴대폰의 윈도우 및 각종 전자제품의 윈도우, 전자제품의 키패드류, 자동차 내부패널 등 아이엠엘(IML) 시트의 적용용도에 따라 이미지 가공이 이루어지게 된다.Here, the electroforming mold 10 including the image processing unit 11 is an IML (IML) such as cases or covers of mobile phones or cosmetics, windows of mobile phones and windows of various electronic products, keypads of electronic products, automobile interior panels, etc. ) Image processing is performed according to the application of the sheet.
즉, 본 발명은 상술한 바와 같은 이미지의 이중처리 등을 통해서 입체감을 부여하게 되므로 단조로움보다는 시각적인 미려함을 더해줄 수 있게 된다.That is, the present invention is to give a three-dimensional impression through the dual processing of the image as described above, it is possible to add a visual beauty rather than monotony.
상기 이미지가공부(11)를 갖는 전주금형(10)의 상면에 도 2(b)에서 보여주는 바와 같이, UV(Ultra Violet)반응을 갖는 UV도료(P)를 도포한다(S2).As shown in Figure 2 (b) on the upper surface of the electroforming mold 10 having the image processing unit 11, UV coating (P) having a UV (Ultra Violet) reaction is applied (S2).
상기 UV도료(P)가 도포된 전주금형(10)의 상면으로 도 2(c)에서와 같이 PET, PP, PC, 아크릴 중의 어느 하나로 이루어진 투명재질의 모재필름(110)을 안착 배치한다(S3).As the upper surface of the electroformed mold 10 coated with the UV paint (P), as shown in FIG. 2 (c), a transparent base material film 110 made of any one of PET, PP, PC, and acryl is placed and disposed (S3). ).
상기 모재필름(110)을 전주금형(10) 상에 안착 배치한 후에는 도 2(d)에서와 같이 압착롤러(20)를 이용하여 평탄하게 압착 처리(S4)하고, 전주금형(10)의 상부에서 도 2(e)에서와 같이 자외선을 조사함으로써 자외선과의 반응을 통해 UV도료(P)를 경화시킨다(S5).After the base film 110 is seated and disposed on the electroforming mold 10, as shown in (d) of FIG. The UV coating (P) is cured through reaction with ultraviolet rays by irradiating ultraviolet rays as shown in FIG.
이때, 압착롤러(20)를 통한 압착작업에 의해 모재필름(110)과 UV도료(P)는 상호 접착되어 강한 결합관계를 형성하게 되고 UV도료(P)측에는 전주금형(10)의 이미지가공부(11) 및/또는 홀로그램가공부 상에 형성된 이미지 및 배경패턴(홀로그램패턴)이 전사(傳寫)되어 증식되어진다.At this time, the base film 110 and the UV paint (P) is bonded to each other by a pressing operation through the pressing roller 20 to form a strong bonding relationship, the image processing portion of the electroforming mold 10 on the UV paint (P) side (11) and / or the image and the background pattern (hologram pattern) formed on the hologram processing portion are transferred and propagated.
여기서, UV도료(P)를 이용하여 전주금형(10) 상의 이미지가공부(11) 및/또는 홀로그램가공부에 대한 이미지 및 배경패턴의 복제를 수행하므로 이미지나 패턴의 복제를 미세한 부분까지 용이하면서도 정교하게 행할 수 있으며 복제(패턴증식)에 따른 균질성을 확보할 수 있게 된다.Here, since the image and the background pattern for the image processing unit 11 and / or the hologram processing unit on the electroform mold 10 is replicated using the UV paint (P), the image or pattern can be easily duplicated and finely refined. It can be done in a simple manner and can ensure homogeneity due to replication (pattern growth).
그리고, 상기 전주금형(10)으로부터 모재필름(110)을 탈리시켜 분리해낸다(S6).Then, the base film 110 is detached from the electroforming mold 10 and separated (S6).
이때, 모재필름(110)을 전주금형(10)으로부터 분리해내면, 도 2(f)에서와 같이 모재필름(110)에 UV도료층(120)이 적층되어 형성되어지되 UV도료층 면에 UV전사방식에 의해 전사된 이미지 및/또는 홀로그램패턴을 갖는 이미지형성필름(100a)을 얻어낼 수 있다.At this time, when the base film 110 is separated from the electroforming mold 10, as shown in Figure 2 (f) UV film layer 120 is laminated on the base film 110 is formed, but UV on the UV paint layer surface An image forming film 100a having an image and / or a hologram pattern transferred by a transfer method can be obtained.
한편, 상기한 6단계 이후에는 도 2(g1) 및 도 2(g2)에서 보여주는 바와 같이, 이미지형성필름(100a) 상에 금속증착막(130)을 형성시키는 공정을 선택적으로 더 수행할 수 있다 할 것이다(S7).Meanwhile, after the above six steps, as shown in FIGS. 2 (g1) and 2 (g2), a process of forming the metal deposition film 130 on the image forming film 100a may be selectively performed. (S7).
부연하면, 상기 금속증착막(130)은 도 2(g1)에서와 같이 UV도료층(120) 형성면에 증착시켜 위에서 아래로 모재필름(110)과 UV도료층(120) 및 금속증착막(130)을 순차 형성되게 할 수 있고, 도 2(g2)에서와 같이 모재필름(110) 면에 증착시켜 위에서 아래로 UV도료층(120)과 모재필름(110) 및 금속증착막(130)이 순차 형성되게 구성 및 배치할 수 있다.In other words, the metal deposition film 130 is deposited on the UV coating layer 120 forming surface as shown in Figure 2 (g1) from top to bottom, the base film 110 and the UV coating layer 120 and the metal deposition film 130 2 may be sequentially formed, and as shown in FIG. 2 (g2), the UV coating layer 120, the base film 110, and the metal deposition film 130 are sequentially formed from the top to the bottom of the base film 110. Can be configured and deployed.
여기서, 상기 금속증착막(130)은 스퍼터링(sputtering) 등의 물리적 기상증착방식(PVD), 화학적 기상증착방식(CVD), 스프레이 분사식 도장처리의 건식증착방식 중에서 어느 하나를 선택적으로 활용하여 크롬이나 니켈 또는 구리 등의 금속을 증착시킴으로써 형성시킬 수 있으며, 이 금속증착막(130)은 박막으로 아주 얇게 입혀지는 것으로 본 발명에 의해 제조되는 아이엠엘 시트(100) 및 시트가 부착되는 제품에 금속의 느낌을 표출시켜주는 기능을 하게 된다.Here, the metal deposition film 130 is chromium or nickel by selectively using any one of physical vapor deposition method (PVD), such as sputtering, chemical vapor deposition method (CVD), dry deposition method of spray injection coating treatment Alternatively, it may be formed by depositing a metal such as copper, and the metal deposition film 130 is coated very thinly with a thin film to produce the impression of the metal on the ILM sheet 100 and the product to which the sheet is attached according to the present invention. It will function to express.
그리고, 상기한 6단계 이후 또는 7단계 이후에는 금속증착막(130)이 없거나 또는 금속증착막(130)을 형성시킨 상태에 도 2(h1) 및 도 2(h2)에서 보인 바와 같이, 이미지형성필름(100a)의 배면에 인쇄층(140)이 형성되게 한다(S8).After the sixth or seventh step, as shown in FIG. 2 (h1) and FIG. 2 (h2), the metal deposition film 130 is absent or the metal deposition film 130 is formed. The print layer 140 is formed on the back surface of 100a (S8).
부연하면, 상기 인쇄층(140)은 금속증착막(130)이 없을 경우 UV도료층(120) 형성면에 접하여 인쇄될 수 있고 또는 모재필름(110) 면에 접하여 인쇄될 수 있으며, 금속증착막(130)이 형성된 경우 금속증착면에 접하도록 인쇄된다 할 것이다.In other words, the printing layer 140 may be printed in contact with the UV coating layer 120 forming surface when there is no metal deposition film 130, or may be printed in contact with the surface of the base film 110, the metal deposition film 130 ) Will be printed in contact with the metal deposition surface.
이때, 상기 인쇄층(140)은 제조되는 시트의 배면에 최종 위치되게 배치하는 것으로 각종 이미지 및 형성패턴에 대한 시인성을 높일 수 있도록 하기 위함이며, 하부면에서 상부면 위에 위치되는 시야측으로 빛의 투과를 차단할 수 있을 정도의 색상으로 인쇄함이 바람직하다 할 것인데, 이때에는 유채색 및 무채색을 다 적용할 수 있다 할 것이며, 빛 투과차단기능을 발휘할 수 있는 정도이면 다 적용 가능하다 할 것이다.At this time, the printed layer 140 is to be placed in the final position on the back of the sheet to be made to increase the visibility for various images and formation patterns, the transmission of light from the lower surface to the viewing side located on the upper surface It is desirable to print in a color enough to block the, it will be possible to apply both the chromatic and achromatic color, if it can be applied to the extent that can exhibit the light transmission blocking function.
이렇게 상기 인쇄층까지 형성시킨 결과물에 대해 NC, CNC, 레이저 등의 기계적 가공으로 커팅하거나 또는 프레스로 타발하는 등에 의해 외형을 가공하면, 도 2(i)에서와 같이 전주금형 및 UV패턴증식을 이용한 아이엠엘 시트(100)를 제조할 수 있게 된다(S9).Thus, when the outer shape is processed by cutting by mechanical processing such as NC, CNC, laser, or punching on the resultant formed up to the printed layer, as shown in FIG. The EL sheet 100 can be manufactured (S9).
이와 같은 제조방법에 의해 제조된 아이엠엘 시트(100)는 각종 이미지의 용이한 구현은 물론 입체감을 위한 홀로그램패턴을 표출할 수 있게 되며, 정밀하면서도 미세한 패턴까지 표출할 수 있으므로 아이엠엘 시트를 더욱 다양하게 생산할 수 있을 뿐만 아니라 균일한 품질로 제조할 수 있게 된다.The EL sheet 100 manufactured by the manufacturing method as described above can display hologram patterns for three-dimensional image as well as easy implementation of various images, and can display precise and fine patterns, thereby making the EL sheet more diverse. Not only can it be produced easily but it can also be manufactured with uniform quality.
한편, 도 3은 본 발명에 의해 제조된 아이엠엘 시트(100)의 적용 예시를 보인 도면으로서, 본 발명에 의한 아이엠엘 시트(100)는 휴대폰이나 화장품의 케이스류 또는 커버류, 휴대폰의 윈도우 및 각종 전자제품의 윈도우, 전자제품의 키패드류, 자동차 내부패널이 되는 각종 사출성형품의 표면에 입혀 아이엠엘 제품(200)을 만드는데 활용할 수 있는데, 본 발명의 아이엠엘 시트(100)를 통해 각종 이미지 및/또는 미세한 홀로그램패턴을 표면에 갖는 아이엠엘 제품(200)을 생산할 수 있다 할 것이며, 이렇게 본 발명에 의해 제조된 아이엠엘용 시트(100)를 적용함으로써 기존 인몰드 사출제품에서 지적되고 있는 높은 불량률과 필름 박리의 문제점은 물론 제품의 휨 발생 등 후변형의 우려를 개선할 수 있게 된다.
On the other hand, Figure 3 is a view showing an application example of the LM sheet 100 manufactured by the present invention, LM sheet 100 according to the present invention is a case or cover of a mobile phone or cosmetics, windows and various kinds of mobile phones It can be utilized to make ILM products 200 by coating them on the surface of various injection molded articles that become windows of electronic products, keypads of electronic products, and automobile interior panels, and various images and / or through ILM sheet 100 of the present invention. Or it will be able to produce the IML product 200 having a fine hologram pattern on the surface, and by applying the sheet for ILM manufactured in accordance with the present invention in this way the high defect rate pointed out in the existing in-mold injection products As well as the problem of film peeling, it is possible to improve the risk of post-deformation, such as warpage of the product.
10: 전주금형 11: 이미지가공부
20: 압착롤러 100: 아이엠엘 시트
100a: 이미지형성필름 110: 모재필름
120: UV도료층 130: 금속증착막
140: 인쇄층
10: Jeonju Mold 11: Image Processing Department
20: pressing roller 100: IML sheet
100a: image forming film 110: the base film
120: UV paint layer 130: metal deposition film
140: print layer

Claims (5)

  1. 정교하면서도 미세한 패턴의 형성을 가능하게 하는 전주 가공을 통해 이미지가공부 및/또는 홀로그램가공부를 형성시킨 전주금형을 구비하는 제1단계;
    상기 전주금형의 상면에 UV반응을 갖는 UV도료를 도포하는 제2단계;
    상기 UV도료가 도포된 전주금형의 상면으로 모재필름을 안착시키는 제3단계;
    상기 모재필름 상부 전체면을 압착롤러로 평탄하게 압착 처리하는 제4단계;
    상기 모재필름의 상측에서 자외선을 조사하여 UV도료를 경화시키는 제5단계;
    상기 전주금형으로부터 모재필름을 분리해내어 모재필름의 하부면에 위치하여 UV도료층을 갖되 UV전사에 의해 이미지 및/또는 홀로그램이 형성된 이미지형성필름을 얻어내는 제6단계;
    상기 이미지형성필름의 배면에 위치하도록 인쇄되며, 빛 투과차단기능의 발휘를 위한 인쇄층을 형성시키는 제7단계를 포함하여 제조되는 것을 특징으로 하는 전주금형 및 UV패턴증식을 이용한 아이엠엘 시트 제조방법.
    A first step of providing an electroforming mold in which an image processing unit and / or a hologram processing unit are formed through electroplating to enable formation of a fine and fine pattern;
    A second step of applying a UV paint having a UV reaction on the upper surface of the electroforming mold;
    A third step of seating the base film on the upper surface of the electroforming mold to which the UV coating is applied;
    A fourth step of flat pressing the entire upper surface of the base film with a pressing roller;
    A fifth step of curing UV paint by irradiating ultraviolet rays from the upper side of the base film;
    A sixth step of separating the base film from the electroforming mold to obtain an image forming film having a UV coating layer on the lower surface of the base film, the image and / or hologram being formed by UV transfer;
    Printed to be positioned on the back of the image forming film, the EL sheet manufacturing method using the electroforming mold and UV pattern growth, characterized in that it comprises a seventh step of forming a printed layer for exhibiting the light transmission blocking function .
  2. 제 1항에 있어서, 상기 제6단계와 제7단계 사이에는 이미지형성필름에 인쇄층을 형성하기 전에 건식증착방식에 의한 금속증착막을 형성시키는 단계가 개입될 수 있는 것을 특징으로 하는 전주금형 및 UV패턴증식을 이용한 아이엠엘 시트 제조방법.The electroforming mold and UV of claim 1, wherein a step of forming a metal deposition film by a dry deposition method may be interposed between the sixth and seventh steps before the printing layer is formed on the image forming film. IMD sheet manufacturing method using the pattern growth.
  3. 제 1항에 있어서, 상기 전주 가공으로 형성된 전주금형의 이미지가공부에 NC나 CNC의 기계적 가공 또는 레이저 가공을 행하여 미세한 이미지나 패턴을 더 부가함으로써 이미지에 대한 입체감 및 심미감을 높일 수 있도록 구성한 것을 특징으로 하는 전주금형 및 UV패턴증식을 이용한 아이엠엘 시트 제조방법.The method of claim 1, wherein the image processing of the electroformed mold formed by the electroplating process to the NC or CNC mechanical processing or laser processing to add a fine image or pattern further configured to enhance the three-dimensional feeling and aesthetics of the image IMD sheet manufacturing method using the electroforming mold and UV pattern growth.
  4. 제 1항에 있어서, 상기 이미지가공부는 음각으로 형성된 경우 음각 내에 부분적으로 미세한 이미지나 패턴의 양각부를 포함되게 구성하거나 또는 양각으로 형성된 경우 양각 내에 부분적으로 미세한 이미지나 패턴의 음각부를 포함되게 구성할 수 있는 것을 특징으로 하는 전주금형 및 UV패턴증식을 이용한 아이엠엘 시트 제조방법.The image processing unit of claim 1, wherein the image processing unit is configured to include an embossed portion of a partially fine image or pattern in the intaglio when formed in an intaglio, or to include an engraved portion of a partially fine image or pattern in the embossed in the embossed form. IMD sheet manufacturing method using a electroforming mold and UV pattern growth, characterized in that it can be.
  5. 상기한 제 1항 내지 제 4항 중의 어느 한 항에 의한 제조방법에 의해 제조된 것을 특징으로 하는 아이엠엘 시트.IMD sheet manufactured by the manufacturing method according to any one of claims 1 to 4.
KR1020100020701A 2010-03-09 2010-03-09 Manufacturing method of window iml sheet using electro forming mold and uv pattern transfer and iml sheet manufactured by this KR100960818B1 (en)