KR101416040B1 - Manufacturing method of tree-dimensional emblems - Google Patents

Manufacturing method of tree-dimensional emblems Download PDF

Info

Publication number
KR101416040B1
KR101416040B1 KR1020130164924A KR20130164924A KR101416040B1 KR 101416040 B1 KR101416040 B1 KR 101416040B1 KR 1020130164924 A KR1020130164924 A KR 1020130164924A KR 20130164924 A KR20130164924 A KR 20130164924A KR 101416040 B1 KR101416040 B1 KR 101416040B1
Authority
KR
South Korea
Prior art keywords
emblem
aluminum sheet
pattern
semi
resin layer
Prior art date
Application number
KR1020130164924A
Other languages
Korean (ko)
Inventor
김형철
Original Assignee
한국내쇼날주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 한국내쇼날주식회사 filed Critical 한국내쇼날주식회사
Priority to KR1020130164924A priority Critical patent/KR101416040B1/en
Application granted granted Critical
Publication of KR101416040B1 publication Critical patent/KR101416040B1/en

Abstract

The present invention relates to a method for manufacturing a three-dimensional emblem, which gives a stately atmosphere and a three-dimensional effect to an emblem, prevents the emblem from being deformed by an external shock, realizes various patterns and colors of designs, and can reduce production time and process. The method comprises: a first step of printing, on an aluminum sheet, a color design which is formed using a pattern or one or more colors; a second step of coating the aluminum sheet with high gloss coatings by super gloss coating; a third step of blanking and foaming the aluminum sheet using a press die to form into a semi-finished emblem; and a fourth step of injecting resins with the semi-finished emblem fixed in an insert molding die to form a resin layer on the semi-finished emblem and drying the resin layer.

Description

입체형 엠블럼 제조방법{Manufacturing method of tree-dimensional emblems}[0001] The present invention relates to a manufacturing method of a three-dimensional emblem,

본 발명은 회사나 제품을 표시하는 입체형 엠블럼 제조방법에 관한 것으로서, 더욱 상세하게는 엠블럼의 중후함과 입체감을 높이고 외부 충격에도 변형되지 않도록 하며 다양한 패턴과 컬러의 문양을 구현할 수 있으며 생산시간과 공정을 단축할 수 있는 입체형 엠블럼 제조방법에 관한 것이다.
The present invention relates to a method of manufacturing a three-dimensional emblem representing a company or a product, and more particularly, to a method of manufacturing a three-dimensional emblem, To a method of manufacturing a three-dimensional emblem.

일반적으로 엠블럼은 자사에서 제조된 제품의 표면 또는 외관에 부착시켜 자사 제품임을 소비자들에게 각인시키기 위하여 부착되는 것이다. 즉, 엠블럼은 회사명이나 단체, 회사 마크, 로고 등을 나타내는 도형, 기호 또는 이들을 조합시켜 특정 회사나 단체를 간단하게 나타내는 인장(印章)으로 사용되는 것이다.Generally, the emblem is affixed to the surface or the appearance of the product manufactured by the company so as to imprint to the consumers that the product is its own product. That is, the emblem is used as a figure, a symbol representing a company name or a group, a company mark, a logo, or the like, or a combination of these to represent a specific company or a group.

이와 같은 엠블럼은 눈에 잘 띄도록 플라스틱 또는 금속 표면에 크롬 도금을 하게 되는데, 이러한 도금 방법으로는 전기적 도금, 화학적 도금, 용융 도금 등이 있다.Such an emblem is chrome plated on a plastic or metal surface in a conspicuous manner, such as electroplating, chemical plating, and hot-dip plating.

근래에는 이러한 엠블럼이 단순히 차량의 출처를 표시하던 것에서 벗어나 차량 외부 디자인과의 조화를 이루면서 나타나는 미감 또는 엠블럼 독자적인 형태로서의 미감도 중시되고 있으며, 그에 따라 종래의 단순한 평면형 디자인에서 벗어나 입체감을 강화시키는 형태들이 제안되고 있다.In recent years, these emblems have been emphasized not only as merely expressing the source of the vehicle but also as an aesthetic sense as an aesthetic sense or an emblem-unique form appearing in harmony with the exterior design of the vehicle. Accordingly, shapes that deviate from the conventional simple planar design and enhance the three- Has been proposed.

위와 같이 입체감이 강화된 입체형 엠블럼은 입체적인 형상으로 이루어진 로고의 경계면에서 점진적으로 명도가 변화하는 그림자부가 형성된 그림자 플레이트가 부착되고, 이와 같이 입체적인 로그가 구비된 그림자 플레이트의 내부에 수납공간이 형성되며, 하부가 차량 등에 부착이 용이하도록 평평한 판형으로 이루어진 베이스 하우징에 결합됨으로써 입체적인 로그 주변에서의 그림자 효과에 의해 자연스러운 깊이감과 입체감을 향상시키고 있다.As described above, the three-dimensional emblem having the three-dimensional feeling is provided with a shadow plate having a shadow part formed with a shadow part whose brightness gradually changes at the interface of the logo formed in a three-dimensional shape, and a storage space is formed inside the shadow plate having the three- And is coupled to a base plate having a flat plate shape so that the lower portion thereof can be easily attached to a vehicle, thereby enhancing natural depth and stereoscopic effect by a shadow effect around the three-dimensional log.

이러한 입체형 엠블럼은 구조만으로도 입체감을 전달하고, 외부의 햇빛이나 조명에 노출되면 입체감이 향상되나, 외부 충격에 의해 변형되거나 흠집이 나는 문제점이 있다. 이에 종래에는 특허 제 10-0857881 호(2008. 09. 10. 등록공고)의 '알루미늄 시트를 이용한 멀티 패턴 부품 제조용 알루미늄 인서트 성형 사출방법 및 이를 이용하여 만든 자동차 재떨이'에서와 같이, 자동차 내장재 부품의 형상에 맞춰 알루미늄 시트를 블랭킹(blanking), 포밍(forming) 공정으로 형상화하여 공정 단축, 원가 절감 및 고품격 내장재 장식 제품을 성형하고 있다.Such a stereoscopic emblem conveys stereoscopic effect only by its structure, and when it is exposed to external sunlight or illumination, the stereoscopic effect is improved, but it is deformed or scratched due to an external impact. Conventionally, as in the "Aluminum insert injection molding method for manufacturing multi-pattern parts using aluminum sheet and automobile ashtray made using the same" of Patent No. 10-0857881 (Registered on Mar. 09, 2008, 2008) Aluminum sheet is shaped by blanking and forming process according to the shape to reduce process, reduce cost, and decorate high-quality interior decoration products.

즉, 종래에는 알루미늄 시트를 블랭킹, 1차 포밍, 2차 포밍, 반제품 세척 건조, 접착제 도포, 인서트 전 접착제 용융, 금형에 반제품 안착, 수지 인서트 성형, 보호 테이프 제거 및 검사, 스크래치 방지 테이프 부착 및 클립 조립 등과 같은 공정으로 처리해야 재떨이 등과 같은 자동차 내장재를 제조할 수 있으므로, 제조공정이 길어지고 생산원가를 높아지는 문제점이 있다.
That is, conventionally, the aluminum sheet has been conventionally subjected to blanking, primary forming, secondary forming, semi-finished product washing and drying, adhesive application, melt adhesive before insert, semi-product seating on a mold, resin insert molding, It is necessary to treat them by a process such as assembly, so that an automobile interior material such as an ashtray can be manufactured, so that the manufacturing process becomes long and the production cost increases.

국내 공개특허 제 10-2007-0073334 호(2007. 07. 10. 공개)Korean Patent Laid-Open No. 10-2007-0073334 (published on July 10, 2007)

상기한 바와 같은 종래기술의 문제점을 해결하기 위한 본 발명은 중후함과 입체감을 부여하고 외부 충격에도 변형되지 않으며, 다양한 패턴과 컬러의 문양을 구현하며, 생산시간과 공정을 단축할 수 있는 입체형 엠블럼 제조방법을 제공하는데 그 목적이 있다.
In order to solve the problems of the prior art as described above, the present invention is to provide a three-dimensional emblem capable of reducing the production time and the process, realizing patterns of various patterns and colors, And a manufacturing method thereof.

상기한 바와 같은 본 발명의 목적은, 알루미늄 시트에 패턴 또는 한가지 이상의 색상으로 구현되는 컬러 문양을 인쇄하는 제 1 단계; 상기 알루미늄 시트에 슈퍼 글로스 코팅에 의해 고광택 코팅제를 도막 처리하여 코팅하는 제 2 단계; 상기 알루미늄 시트를 프레스 금형을 이용하여 블랭킹 및 포밍작업을 하여 반제품 엠블럼으로 성형하는 제 3 단계; 및 상기 반제품 엠블럼을 인서트 사출금형 내에 고정한 상태에서 수지를 주입하여 반제품 엠블럼에 수지층을 형성시켜 건조하는 제 4 단계를 포함하여 구성되는 입체형 엠블럼 제조방법에 의해 달성된다.SUMMARY OF THE INVENTION Accordingly, the present invention has been made in view of the above problems, and an object of the present invention is to provide a color printing method and a color printing method, A second step of coating and coating a high-gloss coating agent on the aluminum sheet by super-gloss coating; A third step of blanking and forming the aluminum sheet using a press mold to form the aluminum sheet into a semi-finished product emblem; And a fourth step of injecting resin in a state in which the semi-finished product emblem is fixed in the insert injection mold, thereby forming a resin layer on the semi-finished product emblem and drying the molded product.

본 발명의 하나의 측면에 의하면, 상기 패턴과 컬러 문양은, 실크 스크린 인쇄방법에 의해 구현되는 것을 특징으로 한다.According to one aspect of the present invention, the pattern and the color pattern are embodied by a silk screen printing method.

본 발명의 다른 측면에 의하면, 상기 제 1 단계는, 상기 알루미늄 시트에 에칭을 통해 문양을 형성하거나 보석을 부착하는 단계를 더 구비하는 것을 특징으로 한다.According to another aspect of the present invention, the first step further includes the step of forming patterns on the aluminum sheet through etching or attaching gems.

본 발명의 또 다른 측면에 의하면, 상기 수지층은, 투명재질의 수지인 것을 특징으로 한다.According to another aspect of the present invention, the resin layer is a transparent resin.

본 발명의 또 다른 측면에 의하면, 상기 수지층은, 아크릴로 이루어지는 것을 특징으로 한다.According to another aspect of the present invention, the resin layer is formed of acrylic.

본 발명의 또 다른 측면에 의하면, 상기 수지층은, 1.0∼2.5 ㎜의 두께를 가지는 것을 특징으로 한다.
According to another aspect of the present invention, the resin layer has a thickness of 1.0 to 2.5 mm.

따라서 본 발명에 의하면, 알루미늄 시트와 일체형으로 아크릴을 성형함으로써 중후함과 입체감을 부여하는 한편 외부 충격에도 변형되지 않으며, 다양한 패턴과 컬러의 문양을 구현할 수 있으며, 기존방식에서 접착제 도포공정 등 일부 공정을 제외함으로써 생산시간과 공정을 단축할 수 있는 효과가 있다.
Therefore, according to the present invention, it is possible to realize various pattern and color patterns without deforming by external impact, while imparting dignity and dimensional sensation by molding acrylic into an integral body with aluminum sheet. In the conventional method, It is possible to shorten the production time and process.

도 1a 내지 도 1c는 본 발명에 의한 반제품 엠블럼의 사진이다.
도 2는 본 발명에 의한 입체형 엠블럼의 사진이다.
도 3은 본 발명에 의한 입체형 엠블럼의 제조과정을 보인 흐름도이다.1A to 1C are photographs of a semi-finished product emblem according to the present invention.
2 is a photograph of a stereoscopic emblem according to the present invention.
3 is a flowchart illustrating a process of manufacturing a three-dimensional emblem according to the present invention.

이하, 본 발명의 바람직한 실시예를 첨부도면을 참조하여 상세히 설명하기로 한다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 1a 내지 도 1c는 본 발명에 의한 반제품 엠블럼의 사진으로서, 도 1a의 타원형의 알루미늄 시트(10)는 Ｈ자 형상의 문양부(11)를 가지며, 바닥부(12)에는 망 형상의 문양이 인쇄되고, 테두리(14)는 검게 인쇄되어 있다. 또한, 도 1b의 타원형의 알루미늄 시트(10)는 Ｈ자 형상의 문양부(11)를 가지며, 문양부(11)와 테두리(14)에는 에칭에 의한 문양이 형성되거나 보석이 부착되고, 바닥부(12)는 검게 인쇄되어 있다. 그리고 도 1c의 타원형의 알루미늄 시트(10)는 Ｈ자 형상의 문양부(11)를 가지며, 경사부(13)에는 에칭에 의한 문양이 형성되거나 보석이 부착되고, 바닥부(12)는 검게 인쇄되어 있다.1A to 1C are photographs of a semi-finished product emblem according to the present invention. The elliptical aluminum sheet 10 of FIG. 1A has an H-shaped pattern portion 11, And the rim 14 is printed in black. The elliptical aluminum sheet 10 of Fig. 1B has an H-shaped pattern portion 11 and patterns are formed on the pattern portion 11 and the rim 14 by etching or attached with jewels, (12) is printed in black. The elliptical aluminum sheet 10 of Fig. 1C has an H-shaped embossed pattern 11, the pattern of etching is formed on the inclined portion 13 or the gem is attached to the inclined portion 13, .

여기서, 알루미늄 시트(10)는 중앙이 볼록하게 나온 타원형의 돔 형상을 가지는 것으로서, 문양부(11)는 Ｈ자 등과 같이 사용자가 필요로 하는 특정 문양을 구현하고, 테두리(14)는 문양부(11)와 동일한 곡면으로 연장된 알루미늄 시트(10)를 외곽을 말하며, 바닥부(12)는 문양부(11)보다 낮은 부분을 그리고 경사부(13)는 문양부(11)와 경사부(13)를 연결하는 부분으로서 입체형 엠블럼의 입체감을 부여하는 역할을 한다.Here, the aluminum sheet 10 has an elliptical dome shape protruding from the center, and the pattern unit 11 implements a specific pattern required by the user such as the letter H, and the frame 14 is a pattern The bottom portion 12 has a portion lower than the pattern portion 11 and the slope portion 13 has a shape of a curved portion 11 and an inclined portion 13 ) As a part for connecting the three-dimensional emblem.

물론, 알루미늄 시트(10)의 모양이나 형상은 위의 예로 한정되지 않고 다양한 모양이나 형상으로 변형 가능하다.Of course, the shape and the shape of the aluminum sheet 10 are not limited to the above examples, and can be changed into various shapes and shapes.

또한, 알루미늄 시트(10) 위(볼록한 면을 말한다)에는 슈퍼 글로스 코팅에 의해 고광택 코팅제가 도막 처리되어 있다.On the aluminum sheet 10 (convex surface), a high-gloss coating agent is applied by super-gloss coating.

도 2는 본 발명에 의한 입체형 엠블럼의 사진으로서, 알루미늄 시트(10) 위에는 고광택 코팅제와 함께 아크릴 등과 같은 투명재질의 수지층이 형성되어 있는데, 이 수지층은 인서트 사출방식에 의해 형성된다.FIG. 2 is a photograph of a three-dimensional emblem according to the present invention. A transparent resin layer such as acrylic is formed on an aluminum sheet 10 together with a high-gloss coating agent. The resin layer is formed by an insert injection method.

도 3은 본 발명에 의한 입체형 엠블럼의 제조과정을 보인 흐름도이다.3 is a flowchart illustrating a process of manufacturing a three-dimensional emblem according to the present invention.

먼저, 작업자는 알루미늄 시트에 패턴이나 한 가지 이상의 색상으로 구현되는 컬러 문양 등을 실크 스크린 방식으로 인쇄하거나 에칭을 통해 문양을 형성하거나 또는 각종 보석을 부착하여 입체형 엠블럼을 고급화한다(S11).First, a worker prints a pattern on a sheet of aluminum sheet or a color pattern embodied in one or more colors by a silk screen method, forms a pattern through etching, or attaches various kinds of jewelry to enhance a three-dimensional emblem (S11).

이때 패턴, 컬러 문양, 에칭에 의한 문양 및 보석 등은 문양부, 바닥부, 경사부, 테두리 등에 대응되게 형성된다. 물론, 패턴, 컬러 문양, 에칭에 의한 문양 및 보석 중 하나 또는 복수가 문양부, 바닥부, 경사부, 테두리 중 하나 또는 복수에 형성될 수 있을뿐더러 형성되지 않을 수도 있다.At this time, the pattern, the color pattern, the pattern by etching, and the gemstone are formed so as to correspond to the pattern part, the bottom part, the inclined part, the rim and the like. Of course, one or more of the pattern, the color pattern, the pattern by etching, and the gem may be formed on one or more of the pattern, the bottom, the slope, and the rim, and may not be formed.

위와 같이 알루미늄 시트 위에 형성된 패턴, 컬러 문양, 에칭에 의한 문양 및 보석 등을 보호하기 위해, 작업자는 패턴, 컬러 문양, 에칭에 의한 문양 및 보석 등이 형성된 알루미늄 시트 위에 슈퍼 글로스 코팅에 의해 고광택 코팅제를 도막 처리한다(S12).In order to protect the pattern, color pattern, etched pattern and jewelry formed on the aluminum sheet as described above, the operator puts a high gloss coating agent on the aluminum sheet on which the pattern, color pattern, etching pattern and jewelry are formed by super gloss coating (S12).

이렇게 알루미늄 시트 위에 고광택(Super Gloss)코팅제를 도막 처리한 작업자는 해당 알루미늄 시트를 프레스 금형을 이용하여 블랭킹 및 포밍작업을 하여 필요한 모양이나 형상의 반제품 엠블럼으로 성형한다(S13).An operator who has applied a super gloss coating agent on the aluminum sheet is subjected to blanking and forming operations using the press mold to form the aluminum sheet into a semi-finished product emblem of a desired shape or shape (S13).

위와 같은 과정을 거쳐 도 1a 내지 도 1c와 같은 반제품 엠블럼을 제조한 작업자는 반제품 엠블럼을 인서트 사출금형 내에 고정한 상태에서 수지를 주입하여 반제품 엠블럼 위에 추가로 수지층을 형성시켜 건조한다(S14). 이때 반제품 엠블럼을 인서트 사출성형하여 수지층을 형성하는 과정이 고광택 코팅제를 도막 처리하는 과정에서 알루미늄 시트에 가해진 열이 완전히 식지 않은 상태에서 이루어지기 때문에 도 2와 같이 입체형 엠블럼 인서트 사출성형시 잔열을 이용할 수 있어 에너지 절감효과를 얻을 수 있다.After the semi-finished product emblem is fixed in the insert injection mold, the operator injects the resin to form a resin layer on the semi-finished product emblem to dry the semi-finished product emblem (S14). Since the process of forming the resin layer by insert injection molding of the semi-finished product emblem is performed in a state in which the heat applied to the aluminum sheet is not completely cooled during the coating process of the high-gloss coating agent, the residual heat is used during injection molding of the three- And the energy saving effect can be obtained.

여기서, 수지층은 투명재질의 수지로서 아크릴 등이 그 예가 될 수 있다.Here, the resin layer may be an acrylic resin or the like as a transparent resin.

또한, 수지층의 두께는 알루미늄 위에 형성된 패턴, 컬러 문양, 에칭에 의한 문양 및 보석 등을 보호하면서도 선명하게 보일 수 있도록 하기 위해, 1.0∼2.5 ㎜로 하는 것이 바람직하다.Further, the thickness of the resin layer is preferably 1.0 to 2.5 mm in order to protect the pattern formed on the aluminum, the color pattern, the pattern by etching, and the gemstones while protecting them clearly.

지금까지 본 발명에 따른 구체적인 실시예에 관하여 설명하였으나, 본 발명의 범위에서 벗어나지 않는 한도 내에서는 여러 가지 변형이 가능함은 물론이다. 그러므로, 본 발명의 범위는 설명된 실시예에 국한되어 정해져서는 안 되며, 후술하는 특허청구의 범위뿐 아니라 이 특허청구의 범위와 균등한 것들에 의해 정해져야 한다.While the present invention has been described in connection with what is presently considered to be practical exemplary embodiments, it is to be understood that the invention is not limited to the disclosed embodiments. Therefore, the scope of the present invention should not be limited to the described embodiments, but should be determined by the scope of the appended claims and equivalents thereof.

이상과 같이 본 발명은 비록 한정된 실시예와 도면에 의해 설명되었으나, 본 발명은 상기의 실시예에 한정되는 것은 아니며, 이는 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 이러한 기재로부터 다양한 수정 및 변형이 가능하다. 따라서, 본 발명 사상은 아래에 기재된 특허청구범위에 의해서만 파악되어야 하고, 이의 균등 또는 등가적 변형 모두는 본 발명 사상의 범주에 속한다고 할 것이다.
While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed exemplary embodiments, but, on the contrary, Modification is possible. Accordingly, the spirit of the present invention should be understood only in accordance with the following claims, and all equivalents or equivalent variations thereof are included in the scope of the present invention.

10 : 알루미늄 시트 11 : 문양부
12 : 바닥부 13 : 경사부
14 : 테두리 10: Aluminum sheet 11: Pattern
12: bottom part 13: inclined part
14: Border

Claims (6)

알루미늄 시트에 패턴 또는 한가지 이상의 색상으로 구현되는 컬러 문양을 인쇄하는 제 1 단계;
상기 알루미늄 시트에 슈퍼 글로스 코팅에 의해 고광택 코팅제를 도막 처리하여 코팅하는 제 2 단계;
상기 알루미늄 시트를 프레스 금형을 이용하여 블랭킹 및 포밍작업을 하여 반제품 엠블럼으로 성형하는 제 3 단계; 및
상기 반제품 엠블럼을 상기 제 2 단계에서 상기 알루미늄 시트에 고광택 코팅제를 도막 처리하는 과정에서 가해진 열이 잔류하는 상태에서 인서트 사출금형 내에 고정하고 수지를 주입하여 반제품 엠블럼에 수지층을 형성시켜 건조하는 제 4 단계;
를 포함하여 구성되는 입체형 엠블럼 제조방법.A first step of printing a pattern on the aluminum sheet or a color pattern embodied in one or more colors;
A second step of coating and coating a high-gloss coating agent on the aluminum sheet by super-gloss coating;
A third step of blanking and forming the aluminum sheet using a press mold to form the aluminum sheet into a semi-finished product emblem; And
The semi-finished product emblem is fixed in the insert injection mold in a state in which heat is applied in the process of applying a high-gloss coating agent to the aluminum sheet in the second step, and resin is injected to form a resin layer on the semi-finished product emblem, step;
Wherein the emblem is embodied as a three-dimensional emblem. 제 1 항에 있어서,
상기 패턴과 컬러 문양은, 실크 스크린 인쇄방법에 의해 구현되는 것을 특징으로 하는 입체형 엠블럼 제조방법.The method according to claim 1,
Wherein the pattern and the color pattern are embodied by a silk screen printing method. 제 1 항에 있어서,
상기 제 1 단계는, 상기 알루미늄 시트에 에칭을 통해 문양을 형성하거나 보석을 부착하는 단계를 더 구비하는 것을 특징으로 하는 입체형 엠블럼 제조방법.The method according to claim 1,
Wherein the first step further comprises the step of forming a pattern on the aluminum sheet by etching or attaching gemstones. 제 1 항에 있어서,
상기 수지층은, 투명재질의 수지인 것을 특징으로 하는 입체형 엠블럼 제조방법. The method according to claim 1,
Wherein the resin layer is a resin of a transparent material. 제 1 항 또는 제 4 항에 있어서,
상기 수지층은, 아크릴로 이루어지는 것을 특징으로 하는 입체형 엠블럼 제조방법. The method according to claim 1 or 4,
Wherein the resin layer is made of acrylic. 제 1 항 또는 제 4 항에 있어서,
상기 수지층은, 1.0∼2.5 ㎜의 두께를 가지는 것을 특징으로 하는 입체형 엠블럼 제조방법.




The method according to claim 1 or 4,
Wherein the resin layer has a thickness of 1.0 to 2.5 mm.




KR1020130164924A 2013-12-27 2013-12-27 Manufacturing method of tree-dimensional emblems KR101416040B1 (en)