KR20190020962A - Soft contact lends - Google Patents

Soft contact lends Download PDF

Info

Publication number
KR20190020962A
KR20190020962A KR1020170105939A KR20170105939A KR20190020962A KR 20190020962 A KR20190020962 A KR 20190020962A KR 1020170105939 A KR1020170105939 A KR 1020170105939A KR 20170105939 A KR20170105939 A KR 20170105939A KR 20190020962 A KR20190020962 A KR 20190020962A
Authority
KR
South Korea
Prior art keywords
vitamin
soft contact
contact lens
lens
derivative
Prior art date
Application number
KR1020170105939A
Other languages
Korean (ko)
Inventor
권인찬
이다솜
Original Assignee
광주과학기술원
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 광주과학기술원 filed Critical 광주과학기술원
Priority to KR1020170105939A priority Critical patent/KR20190020962A/en
Publication of KR20190020962A publication Critical patent/KR20190020962A/en

Abstract

Disclosed is a soft contact lens which can alleviate a dry eye syndrome. The soft contact lens according to the present invention comprises a lens body which is a reaction product of a thermally polymerizable composition, wherein the lens body contains vitamin A or derivatives of the vitamin A.

Description

소프트 콘택트 렌즈{SOFT CONTACT LENDS}Soft contact lenses {SOFT CONTACT LENDS}

본 발명은 소프트 콘택트 렌즈에 관한 것으로, 보다 상세하게는 비타민 A를 포함하여 안구 건조증을 완화시킬 수 있는 콘택트 렌즈에 관한 것이다.
The present invention relates to a soft contact lens, and more particularly, to a contact lens including vitamin A to relieve dry eye syndrome.

일반적으로 콘택트 렌즈는 구성되는 성분에 따라 유연한 소프트 콘택트 렌즈와 상기 소프트 콘택트 렌즈보다 단단한 하드 콘택트 렌즈로 구분된다.Generally, a contact lens is divided into a soft soft contact lens and a hard contact lens harder than the soft contact lens, depending on the constituent components.

하드 콘택트 렌즈는 산소 투과성이 부족하여 수분을 함유하기 어려운 반면, 소프트 콘택트 렌즈는 수분을 함유하여 안구에 편안함을 제공하며 다양한 연령층에서 사용되고 있다.Hard contact lenses are difficult to contain moisture due to lack of oxygen permeability, while soft contact lenses contain moisture to provide comfort in the eye and are used in various age groups.

하지만, 눈은 많은 균들로부터 쉽게 노출되어 있기 때문에, 소프트 콘택트 렌즈를 눈에 직접 착용함에 있어 각막에 여러 가지 문제점을 발생시킨다. 예를 들어, 소프트 콘택트 렌즈는 각막보다 넓은 부위를 덮고 있기 때문에 렌즈의 움직임이 적고 눈물 순환의 틈새가 없어 산소 공급이 원활하지 못한 단점이 있다. 이에 따라, 눈물이 지나치게 증발하게 되거나 눈물의 구성 성분이 불균형적으로 맞지 않아 안구 표면이 손상되고 자극감, 이물감, 건조감 등을 느끼는 안구 건조증이 발생하게 된다. 이러한 안구 건조증은 안구 표면에 생긴 염증에 의해 발생하기도 하며, 오래 지속될 경우, 각막의 손상으로 시력이 손실되는 문제점까지 발생되기도 한다.However, because the eyes are easily exposed to many bacteria, the wear of the soft contact lens directly on the eyes causes various problems in the cornea. For example, since soft contact lenses cover a larger area than the cornea, there is a disadvantage in that the movement of the lens is small and there is no clearance of the circulation of the eyes, and the oxygen supply is not smooth. As a result, the tear is evaporated too much or the constituents of the tears are unbalanced, resulting in damage to the surface of the eyeball and dryness of the eye, which senses irritation, foreign body and dryness. This dry eye syndrome is caused by inflammation on the surface of the eye, and if it lasts for a long time, it may cause loss of vision due to damage of the cornea.

따라서, 장시간 착용시에도 건강한 눈 상태를 유지할 수 있으며, 안구 건조증을 완화시킬 수 있는 소프트 콘택트 렌즈의 연구가 필요한 실정이다.Therefore, it is necessary to study a soft contact lens that can maintain a healthy eye condition even when worn for a long time and mitigate dry eye syndrome.

본 발명에 관련된 배경기술로는 대한민국 등록특허공보 제10-1533075호(2015.06.25. 등록)가 있으며, 생체친화형 소프트 콘택트렌즈 및 이의 제조방법이 기재되어 있다. 상기 문헌에는 기존의 HEMA 단량체와에 가교제와 중합개시제를 첨가 사용하여 친수성의 성질을 높이고, 안구건조를 방지하는 렌즈가 기재되어 있으나, 가교제와 개시제의 성분만으로는 안구건조증을 완화시키거나 방지하기에는 한계가 있다.
A background art related to the present invention is Korean Patent Registration No. 10-1533075 (registered on June 25, 2015), which describes a biocompatible soft contact lens and a manufacturing method thereof. In the above document, there is disclosed a lens for enhancing the hydrophilic properties and preventing ocular dryness by adding a conventional HEMA monomer and a crosslinking agent and a polymerization initiator to the monomer. However, only the components of the crosslinking agent and the initiator have limitations for alleviating or preventing dry eye syndrome have.

본 발명의 목적은 안구 건조증을 완화시킬 수 있는 소프트 콘택트 렌즈를 제공하는 것이다.
It is an object of the present invention to provide a soft contact lens capable of alleviating dry eye syndrome.

상기 하나의 목적을 달성하기 위한 본 발명에 따른 소프트 콘택트 렌즈는 열중합성 조성물의 반응 생성물인 렌즈체를 포함하며, 상기 렌즈체는 비타민 A 또는 상기 비타민 A의 유도체를 포함하는 것을 특징으로 한다.According to an aspect of the present invention, there is provided a soft contact lens comprising a lens body, which is a reaction product of a thermosetting composition, and the lens body comprises vitamin A or a derivative of the vitamin A.

상기 비타민 A의 유도체는 폴리에톡실레이티드레틴아마이드, 레티노익산, 레티놀, 레티닐 아세테이트 및 레티닐 팔미테이트 중 1종 이상을 포함할 수 있다.The derivative of vitamin A may include at least one of polyethoxylated retinamide, retinoic acid, retinol, retinyl acetate and retinyl palmitate.

상기 열중합성 조성물은 2-하이드록시에틸메타크릴레이트(2-hydroxyethylmethacrylate, HEMA), 글리시딜메타크릴레이트(glycidylmethacrylate, GMA), 에틸렌글리콜디메타크릴레이트(ethyleneglycoldimethacrylate, EGDMA) 및 N-비닐피롤리돈(N-vinylpyrrolidone, NVP)를 포함할 수 있다.The thermosetting composition may include at least one of 2-hydroxyethylmethacrylate (HEMA), glycidylmethacrylate (GMA), ethyleneglycoldimethacrylate (EGDMA), and N -vinylpyrrolidone ( N- vinylpyrrolidone, NVP).

상기 열중합성 조성물 100중량부에 대하여, 상기 비타민 A 또는 비타민 A의 유도체 0.1~10중량부를 포함할 수 있다.
0.1 to 10 parts by weight of the vitamin A or vitamin A derivative may be contained relative to 100 parts by weight of the thermosetting composition.

본 발명에 따른 비타민 A를 포함하는 소프트 콘택트 렌즈는 안구에 착용 시 안구 건조증 완화에 기여할 수 있으며, 염증 치료와 자외선 차단 기능의 효과도 우수하다.The soft contact lens containing vitamin A according to the present invention can contribute to alleviation of dry eye syndrome when worn on the eyeball, and has an excellent effect of treating inflammation and ultraviolet ray blocking function.

또한, 본 발명의 소프트 콘택트 렌즈에 안구 건조증을 치료하기 위한 약물을 함께 사용하여 치료용 콘택트 렌즈로도 응용 가능하다.
Further, the soft contact lens of the present invention can also be used as a therapeutic contact lens by using a drug for treating dry eye syndrome.

도 1은 본 발명에 따른 소프트 콘택트 렌즈의 모식도를 나타낸 것이다.
도 2는 본 발명에 따른 소프트 콘택트 렌즈의 시간에 따른 흡광도 측정 결과를 나타낸 그래프이다.
1 is a schematic view of a soft contact lens according to the present invention.
2 is a graph showing the results of absorbance measurements of the soft contact lenses according to the present invention with time.

본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 첨부되는 도면과 함께 상세하게 후술되어 있는 실시예들을 참조하면 명확해질 것이다. 그러나 본 발명은 이하에서 개시되는 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 본 실시예들은 본 발명의 개시가 완전하도록 하며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 발명은 청구항의 범주에 의해 정의될 뿐이다. 명세서 전체에 걸쳐 동일 참조 부호는 동일 구성요소를 지칭한다.BRIEF DESCRIPTION OF THE DRAWINGS The advantages and features of the present invention, and the manner of achieving them, will be apparent from and elucidated with reference to the embodiments described hereinafter in conjunction with the accompanying drawings. The present invention may, however, be embodied in many different forms and should not be construed as being limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art. Is provided to fully convey the scope of the invention to those skilled in the art, and the invention is only defined by the scope of the claims. Like reference numerals refer to like elements throughout the specification.

이하 첨부된 도면을 참조하여 본 발명의 바람직한 실시예에 따른 소프트 콘택트 렌즈에 관하여 상세히 설명하면 다음과 같다.
Hereinafter, a soft contact lens according to a preferred embodiment of the present invention will be described in detail with reference to the accompanying drawings.

도 1은 본 발명에 따른 소프트 콘택트 렌즈의 모식도를 나타낸 것이다.1 is a schematic view of a soft contact lens according to the present invention.

도 1을 참조하면, 소프트 콘택트 렌즈에 비타민 A를 포함함으로써, 노란빛을 나타내는 렌즈를 제조할 수 있다. 또한, 노란빛이 시각 형성에 방해가 된다고 느끼는 경우에는 패터닝(patterning)을 통해 렌즈의 동공 외부에만 비타민 A를 흡수시켜 렌즈의 착용감을 높일 수 있다.
Referring to Fig. 1, by including vitamin A in a soft contact lens, a lens exhibiting yellow light can be manufactured. In addition, if the yellow color interferes with visual formation, patterning can absorb the vitamin A only outside the pupil of the lens, thereby enhancing the wearing comfort of the lens.

본 발명에 따른 소프트 콘택트 렌즈는 열중합성 조성물의 반응 생성물인 렌즈체를 포함하며, 상기 렌즈체는 비타민 A 또는 상기 비타민 A의 유도체를 포함한다.
The soft contact lens according to the present invention includes a lens body which is a reaction product of a thermosetting composition, and the lens body includes vitamin A or a derivative of the vitamin A.

비타민 A는 [구조식 1]로 표시되며, 망막 속 로돕신이라는 감광색소를 만들어내는데 필요한 요소이다. Vitamin A is expressed as [Structural Formula 1] and is a necessary factor for producing a photosensitizing dye called rhodopsin in the retina.

[구조식 1][Structural formula 1]

Figure pat00001
Figure pat00001

일반적으로, 체내에 비타민 A가 부족한 경우, 망막에 로돕신이 생성되지 않아 어두운 곳에서 사물을 잘 못 보는 야맹증을 유발할 수 있으며, 안구 건조증 또는 각막 연화증을 유발할 수 있다. In general, when vitamin A is lacking in the body, rhodopsin is not produced in the retina, which can cause night blindness in dark places and can cause dry eye syndrome or corneal softening.

본 발명에서는 소프트 콘택트 렌즈에 비타민 A 또는 상기 비타민 A의 유도체를 포함시켜, 소프트 콘택트 렌즈 착용 시 비타민 A에 의해 안구 건조증을 완화시키고, 안구 표면에 생긴 염증을 치료할 수 있는 효과를 제공한다. 또한, 본 발명의 소프트 콘택트 렌즈에 안구 건조증을 치료하기 위한 약물을 함께 사용하여 치료용 콘택트 렌즈로도 응용 가능하다.
In the present invention, vitamin A or a derivative of vitamin A is included in the soft contact lens, thereby alleviating dry eye syndrome caused by vitamin A upon wearing a soft contact lens and providing an effect of treating inflammation on the eyeball surface. Further, the soft contact lens of the present invention can also be used as a therapeutic contact lens by using a drug for treating dry eye syndrome.

상기 비타민 A의 유도체는 폴리에톡실레이티드레틴아마이드, 레티노익산, 레티놀, 레티닐 아세테이트 및 레티닐 팔미테이트 중 1종 이상을 포함할 수 있다.The derivative of vitamin A may include at least one of polyethoxylated retinamide, retinoic acid, retinol, retinyl acetate and retinyl palmitate.

상기 열중합성 조성물 100중량부에 대하여, 상기 비타민 A 또는 비타민 A의 유도체 0.1~10중량부를 포함할 수 있다. 이는 상기 열중합성 조성물로부터 제조되는 렌즈체 100중량부에 대하여, 상기 비타민 A 또는 비타민 A의 유도체 0.1~10중량부를 포함할 수 있음을 의미한다.
0.1 to 10 parts by weight of the vitamin A or vitamin A derivative may be contained relative to 100 parts by weight of the thermosetting composition. This means that 0.1 to 10 parts by weight of the vitamin A or vitamin A derivative may be contained in 100 parts by weight of the lens body manufactured from the thermosetting composition.

상기 열중합성 조성물은 2-하이드록시에틸메타크릴레이트(2-hydroxyethylmethacrylate, HEMA), 글리시딜메타크릴레이트(glycidylmethacrylate, GMA), 에틸렌글리콜디메타크릴레이트(ethyleneglycoldimethacrylate, EGDMA) 및 N-비닐피롤리돈(N-vinylpyrrolidone, NVP)를 포함할 수 있다.
The thermosetting composition may include at least one of 2-hydroxyethylmethacrylate (HEMA), glycidylmethacrylate (GMA), ethyleneglycoldimethacrylate (EGDMA), and N -vinylpyrrolidone ( N- vinylpyrrolidone, NVP).

상기 2-하이드록시에틸메타크릴레이트(2-hydroxyethylmethacrylate, HEMA)는 [구조식 2]로 표시된다. 소프트 콘택트 렌즈에 가장 기본으로 사용되는 주 모노머로서 현재 가장 많이 쓰이는 재질이며, ph, 온도, 삼투압 등에 매우 안정된 재질이다. Side-chain에 있는 수산기(OH) 때문에 물을 흡수하는 성질이 있으며 상기 HEMA가 포함되는 소프트 콘택트 렌즈는 약 36% 이상의 함수율을 가진다. The 2-hydroxyethylmethacrylate (HEMA) is represented by [formula 2]. It is the most used material as the most basic monomer used in soft contact lenses. It is a very stable material such as pH, temperature, osmotic pressure. There is a property of absorbing water due to the hydroxyl group (OH) in the side-chain, and the soft contact lens containing the HEMA has a water content of about 36% or more.

[구조식 2][Structural formula 2]

Figure pat00002

Figure pat00002

가교제로서 글리시딜메타크릴레이트(glycidylmethacrylate, GMA)는 [구조식 3]으로 표시되며, 주 기능은 고분자를 안정시키는 것이다.Glycidylmethacrylate (GMA) as a crosslinking agent is represented by [Formula 3], and the main function is to stabilize the polymer.

[구조식 3][Structural Formula 3]

Figure pat00003
Figure pat00003

예를 들어, 상기 열중합성 조성물은 HEMA 100중량부에 대하여, GMA 0.1~5중량부를 포함할 수 있으나, 이에 제한되는 것은 아니다.
For example, the thermosetting composition may include, but is not limited to, 0.1 to 5 parts by weight of GMA relative to 100 parts by weight of HEMA.

가교제로서 에틸렌글리콜디메타크릴레이트(EGDMA)는 [구조식 4]로 표시되며, 하나의 모노머(monomer)에 두 개의 메타아크레이트기를 갖고 있고, 주 기능은 고분자를 안정시키는 것이다. 가교제를 과다하게 사용하면 딱딱해지고 함수율이 낮아지며 신축성이 감소하기 때문에 적정 함량으로 조절하는 것이 바람직하다.Ethylene glycol dimethacrylate (EGDMA) as a crosslinking agent is represented by [Formula 4], and has two methacrylate groups in one monomer. The main function is to stabilize the polymer. When the cross-linking agent is used in excess, it is preferable to adjust the content to an appropriate level because it becomes hard, decreases the water content, and decreases the stretchability.

[구조식 4][Structural Formula 4]

Figure pat00004
Figure pat00004

예를 들어, 상기 열중합성 조성물은 HEMA 100중량부에 대하여, EGDMA 0.1~5중량부를 포함할 수 있으나, 이에 제한되는 것은 아니다.
For example, the thermosetting composition may include, but is not limited to, 0.1 to 5 parts by weight of EGDMA relative to 100 parts by weight of HEMA.

상기 N-비닐피롤리돈(N-vinylpyrrolidone, NVP)는 [구조식 5]로 표시되며, 소프트 콘택트 렌즈의 수분 함량을 증가시키기 위해 사용되는 보조 모노머이고, 습윤성 증가를 위해 사용한다. 이것은 고함수율을 갖는 재료로 적정 함량으로 50 ~ 80%에 이르는 넓은 범위의 함수율을 가질 수 있으며, 산소투과도도 높일 수 있다. The N - vinylpyrrolidone (N -vinylpyrrolidone, NVP) is represented by [formula 5], and the secondary monomer is used in order to increase the water content of the soft contact lens, it is used to increase the wettability. It is a material with a high water content and can have a wide range of water content ranging from 50 to 80% in an optimum content, and can also increase the oxygen permeability.

[구조식 5][Structural Formula 5]

Figure pat00005
Figure pat00005

예를 들어, 상기 열중합성 조성물은 HEMA 100중량부에 대하여, NVP 0.1~10중량부를 포함할 수 있으나, 이에 제한되는 것은 아니다.
For example, the thermosetting composition may include, but is not limited to, 0.1 to 10 parts by weight of NVP relative to 100 parts by weight of HEMA.

본 발명의 소프트 콘택트 렌즈는 다음과 같이 제조될 수 있다.The soft contact lens of the present invention can be manufactured as follows.

상기 열중합성 조성물을 교반한 후, 소프트 콘택트 렌즈 성형용 몰드에 주입하고 오븐에 넣는다. 오븐 온도는 1차로 대략 70~90℃로 유지할 수 있으며, 2차로 90~110℃로 유지할 수 있다. 필요에 따라 3차로 대략 100~120℃로 유지하여 열중합 반응시킴으로써, 반응 생성물인 렌즈체, 즉, 소프트 콘택트 렌즈를 제조할 수 있다. After the thermosetting composition is stirred, it is poured into a soft contact lens molding mold and placed in an oven. The oven temperature can be maintained at about 70 to 90 ° C as the first stage, and 90 to 110 ° C as the second stage. The lens product, that is, the soft contact lens, which is a reaction product, can be produced by maintaining the temperature at about 100 to 120 ° C as a third step, if necessary, and performing a thermal polymerization reaction.

본원발명에서는 제조된 소프트 콘택트 렌즈에 비타민 A를 흡수시킴으로써, 특수한 조성으로부터 콘택트 렌즈를 제조하지 않고도 시판되는 상품들에 비타민 A를 용이하게 적용할 수 있다.
In the present invention, by absorbing vitamin A in the manufactured soft contact lens, it is possible to easily apply vitamin A to commercially available products without manufacturing a contact lens from a specific composition.

이처럼, 소프트 콘택트 렌즈는 2-Hydroxyethyl methacrylate(HEMA)를 기본 단량체로 하여 개시제, 가교제에 의한 열중합으로 제조된 후, 비타민 A를 흡수시킴으로써, 유연성이 우수하고, 안구 건조증 완화, 염증 치료 및 자외선 차단 효과를 나타낼 수 있다.
As such, soft contact lenses are made of 2-Hydroxyethyl methacrylate (HEMA) as a basic monomer by thermal polymerization with initiator and cross-linking agent and then absorbed vitamin A. Therefore, soft contact lenses are excellent in flexibility and can be used for relieving dryness of eyes, Effect can be shown.

도 2는 본 발명에 따른 소프트 콘택트 렌즈의 시간에 따른 흡광도 측정 결과를 나타낸 그래프이다.2 is a graph showing the results of absorbance measurements of the soft contact lenses according to the present invention with time.

비타민 A를 흡수시킨 소프트 콘택트 렌즈를 체액과 비슷한 PBS 용액에 담가놓고, 시간마다 렌즈가 담겨진 용액을 채취하여 흡광도를 측정하였다. 흡광도는 300nm에서 측정되었으며, 1~6시간 동안 흡수된 빛의 양이 0.3~1.2를 나타내어 시간에 따라 흡광도가 증가하는 것으로 보아, 렌즈로부터 비타민 A가 계속적으로 서서히 방출되고 있음을 알 수 있다. The absorbance of the vitamin A-absorbed soft contact lens was measured by immersing the lens in a PBS solution similar to body fluids. The absorbance was measured at 300 nm, and the amount of absorbed light for 1 to 6 hours was 0.3 to 1.2, indicating that the absorbance increased with time, indicating that the vitamin A was continuously and gradually released from the lens.

또한, 자외선 영역의 빛을 흡수하는 것으로 보아, 비타민 A가 포함된 소프트 콘택트 렌즈가 자외선으로부터 안구를 보호하는 것을 예측할 수 있다.
In addition, by absorbing light in the ultraviolet region, it can be predicted that a soft contact lens containing vitamin A protects the eye from ultraviolet rays.

이상 첨부된 도면을 참조하여 본 발명의 실시예들을 설명하였으나, 본 발명은 상기 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 제조될 수 있으며, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다.While the present invention has been described in connection with what is presently considered to be practical exemplary embodiments, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, It is to be understood that the invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. It is therefore to be understood that the above-described embodiments are illustrative in all aspects and not restrictive.

Claims (4)

열중합성 조성물의 반응 생성물인 렌즈체를 포함하며,
상기 렌즈체는 비타민 A 또는 상기 비타민 A의 유도체를 포함하는 것을 특징으로 하는 소프트 콘택트 렌즈.
And a lens body which is a reaction product of the thermosetting composition,
Wherein the lens body comprises vitamin A or a derivative of the vitamin A. 2. The soft contact lens according to claim 1,
제1항에 있어서,
상기 비타민 A의 유도체는 폴리에톡실레이티드레틴아마이드, 레티노익산, 레티놀, 레티닐 아세테이트 및 레티닐 팔미테이트 중 1종 이상을 포함하는 것을 특징으로 하는 소프트 콘택트 렌즈.
The method according to claim 1,
Wherein the derivative of vitamin A comprises at least one of polyethoxylated retinamide, retinoic acid, retinol, retinyl acetate and retinyl palmitate.
제1항에 있어서,
상기 열중합성 조성물은 2-하이드록시에틸메타크릴레이트(2-hydroxyethylmethacrylate, HEMA), 글리시딜메타크릴레이트(glycidylmethacrylate, GMA), 에틸렌글리콜디메타크릴레이트(ethyleneglycoldimethacrylate, EGDMA) 및 N-비닐피롤리돈(N-vinylpyrrolidone, NVP)를 포함하는 것을 특징으로 하는 소프트 콘택트 렌즈.
The method according to claim 1,
The thermosetting composition may include at least one of 2-hydroxyethylmethacrylate (HEMA), glycidylmethacrylate (GMA), ethyleneglycoldimethacrylate (EGDMA), and N -vinylpyrrolidone Wherein the soft contact lens comprises N- vinyl pyrrolidone (NVP).
제1항에 있어서,
상기 열중합성 조성물 100중량부에 대하여, 상기 비타민 A 또는 비타민 A의 유도체 0.1~10중량부를 포함하는 것을 특징으로 하는 소프트 콘택트 렌즈.
The method according to claim 1,
Wherein 0.1 to 10 parts by weight of the vitamin A or vitamin A derivative is contained relative to 100 parts by weight of the heat-polymerizable composition.
KR1020170105939A 2017-08-22 2017-08-22 Soft contact lends KR20190020962A (en)