KR20190018827A - Bathroom floor coating composition and preparing method of the same - Google Patents
Bathroom floor coating composition and preparing method of the same Download PDFInfo
- Publication number
- KR20190018827A KR20190018827A KR1020170103419A KR20170103419A KR20190018827A KR 20190018827 A KR20190018827 A KR 20190018827A KR 1020170103419 A KR1020170103419 A KR 1020170103419A KR 20170103419 A KR20170103419 A KR 20170103419A KR 20190018827 A KR20190018827 A KR 20190018827A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- oil
- liquid silicone
- silicone
- Prior art date
Abstract
Description
본원은 욕실 바닥 코팅제 및 그 제조방법에 관한 것이다 The present invention relates to a bathroom floor coating agent and a method for producing the same
더욱 상세하게 본 발명은 수영장, 욕실 바닥의 미끄럼을 방지하기 위해 욕실 바닥에 도포하는 미끄럼 방지용 바닥 코팅제에 관한 것으로서, 보다 상세하게는 미끄럼 방지 효과를 극대화하고, 내마모성, 방수성, 장기 접착성 등이 우수한 미끄럼 방지용 바닥 코팅제에 관한 것이다.More particularly, the present invention relates to an anti-slip floor coating agent applied on the floor of a bathroom to prevent slipping on the bottom of a swimming pool or a bathroom. More specifically, the present invention relates to a floor coating agent for anti- Slip floor coatings.
토목, 건축구조물의 벽면 및 각종 시설물에는 주변에서 발생되는 대기중의 무기 및 유기물질이 흡착되고, 이 중 유기물질을 먹이로 하는 각종 곰팡이, 세균이 벽면 및 시설물의 표면에 번식한다. 곰팡이는 온난 다습한 환경에서 주로 생기며 곰팡이를 방지하기 위해서는 포자와 접촉하는 것을 차단하고 온도, 수분, 영양분 등을 생육에 부적당한 상태로 유지시키는 것이 필요하다. 백화현상은 시멘트 벽돌, 타일 및 석재 등에 남아있는 수산화칼슘이 재료 내의 수분이 증발함과 함께 표면으로 드러나 공기중의 탄산가스와 반응하여 하얀 백색 가루가 남는 현상이다. 이는 벽의 미관을 해치며 정도가 심할 경우 재료에 침투해 물리적인 변화를 일으키기도 한다. 또한 벽돌이나 석재, 콘크리트 블록 등을 쌓을 경우 표면에 생기는 이음매 근을 통칭하여 줄눈이라고 하는데, 이는 물때나 곰팡이 등으로 인해 쉽게 오염되는 탓에 미관을 해치며 위생상 좋지 못하다. Atmospheric inorganic and organic substances are adsorbed on the walls and various structures of civil engineering and architectural structures, and various fungi and bacteria that feed on organic matter propagate on the surface of walls and facilities. Fungi occur mainly in warm and humid environments. In order to prevent fungi, it is necessary to block contact with spores and to keep temperature, water, nutrients, etc. unsuitable for growth. The whitening phenomenon is a phenomenon in which calcium hydroxide remaining in cement brick, tile, and stone evaporates moisture in the material and reacts with carbon dioxide in the air as it is exposed to the surface, leaving white white powder. This can damage the aesthetics of the wall and, if severe, penetrate the material and cause physical changes. Also, joints that occur on the surface when bricks, stone, concrete blocks are piled up are collectively referred to as joints, which are easily contaminated due to water and mold, which is harmful to beauty and hygienic.
상기와 같은 곰팡이, 백화현상, 줄눈 등의 문제점들은 벽의 노화나 변질을 야기하며 미관을 해치고 내구성을 낮춘다. 이를 완화시키기 위하여 벽면이나 시설물을 공사할 때 실리콘 발수제로 외부 및 내부에 마감을 하지만 이는 수분을 차단하는 효과만을 위한 단편적인 조치일 뿐 벽의 노화 및 변질의 원인을 적극적으로 차단하는 해결책이 되지 않는다. 특히 기존의 벽면 발수제는 벽에 침투하여 발수를 하는 형태로서 많은 양을 사용해야만 하는 단점이 존재하며, 일반적인 벽면 코팅제는 온도 차에 의한 신축성이 작다는 단점이 있다. [대한민국 등록 특허 제 1016781100000호] Problems such as mold, whitening, and joints cause aging or deterioration of the wall, which deteriorates the appearance and lowers durability. In order to mitigate this, it is necessary to finish the exterior or interior with silicone water repellent when constructing walls or facilities, but this is only a piecemeal measure only for the effect of blocking moisture, but it is not a solution to actively block the cause of aging and deterioration of the wall . In particular, the conventional wall surface water repellent has a drawback that it must be used in a large amount as a form of water repellent penetration into the wall, and a general wall surface coating has a drawback in that the elasticity due to the temperature difference is small. [Korean Patent No. 1016781100000]
한편, 일반적으로 욕실이나 공중목욕탕, 사우나, 수영장 등의 바닥에는 디자인의 미감을 향상시키기 위하여 각종 타일 또는 대리석 등의 무기계 바닥재들이 시공되고 있다.On the other hand, inorganic flooring materials such as various tiles or marble are generally applied to the floor of bathrooms, public baths, saunas, pools and the like in order to improve the beauty of design.
이러한 무기계 바닥재는 내마모성과 내구성, 내변색성이 우수할 뿐만 아니라, 고광택 및 고평활 표면 특성을 발휘하므로 그 사용은 현저하게 증가하고 있는 추세이다.These inorganic flooring materials are not only excellent in abrasion resistance, durability and discoloration resistance, but also exhibit high gloss and high smooth surface properties, and their use is remarkably increasing.
그러나, 이러한 무기계 바닥제는 고평활성과 미끄럼 표면 특성 때문에 사람이 보행시에 미끄러지기 쉽고, 특히 수용성 물질이나 비눗물 등이 표면에 묻어 있는 경우에는 수막현상에 의해 미끄러짐이 빈발하여 종종 심각한 안전사고로까지 이어지기도 한다.However, these inorganic flooring agents tend to slip when walking because of their high smoothness and sliding surface characteristics. Particularly, when water-soluble substances or soapy water are present on the surface, slip occurs frequently due to water film phenomenon, I will.
상기와 같은 문제점을 해결하고자 종래에는 접착형태의 미끄럼 방지 물질을 도포하기도 하였으나, 이는 사용수명에의 한계가 있고, 장기 접착성이 저하되고 쉽게 오염되는 문제점이 있었다.In order to solve the above-mentioned problems, the conventional anti-slip material is applied, but it has a problem in that it has a limited life span and deteriorates long-term adhesiveness and is easily contaminated.
이에, 본원은 욕실 바닥 코팅제 및 그 제조방법을 제공하고자 한다. Accordingly, the present invention provides a bathroom floor coating agent and a method for producing the same.
그러나, 본원이 해결하고자 하는 과제는 이상에서 언급한 과제로 제한되지 않으며, 언급되지 않은 또 다른 과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.However, the problems to be solved by the present invention are not limited to the above-mentioned problems, and other problems not mentioned can be clearly understood by those skilled in the art from the following description.
본원의 제 1 측면은, 오일 100중량부에 물 60~80중량부, 실리콘 점토 20~30중량부 및 목공용 풀 40~60중량부를 포함하는 액상 실리콘을 제조하는 단계; 및 상기 액상 실리콘에 메탄올을 첨가하여 혼합하는 단계를 포함한다.According to a first aspect of the present invention, there is provided a process for producing a liquid silicone, comprising: preparing liquid silicone containing 60 to 80 parts by weight of water, 20 to 30 parts by weight of silicone clay and 40 to 60 parts by weight of a wood pulp in 100 parts by weight of oil; And mixing and adding methanol to the liquid silicone.
또한, 상기 액상 실리콘을 제조하는 단계는, A: 오일 100중량부를 80℃로 가열하며 실리콘 점토 20~30중량부를 혼합하는 단계; B: 상기 가열된 오일 및 실리콘 점토 혼합액에 30~80℃의 물 60~80중량부를 혼합하여 80℃로 5~10분 동안 가열하는 단계; 및 C: 상기 가열된 오일, 실리콘 점토 및 물 혼합액에 목공용 풀 40~60중량부를 첨가하여 80℃로 가열하는 단계로 이루어 질 수 있다.The step of preparing the liquid silicone may include: mixing 100 parts by weight of the A: oil at 80 DEG C and 20 to 30 parts by weight of the silicone clay; B: mixing 60 to 80 parts by weight of water at 30 to 80 캜 with the heated oil and silicone clay mixture and heating at 80 캜 for 5 to 10 minutes; And C: adding 40 to 60 parts by weight of a wood-working pulp to the heated oil, silicone clay and water mixture, and heating to 80 캜.
또한, 상기 액상 실리콘을 제조하는 단계 후 상기 액상 실리콘 100중량부에 자외선 차단 오일을 3~5중량부로 혼합하여 자외선 차단 액상 실리콘을 제조하는 단계를 추가 포함할 수 있다.Further, after the step of preparing the liquid silicone, the step of preparing ultraviolet-shielding liquid silicone by mixing ultraviolet shielding oil at 3 to 5 parts by weight with 100 parts by weight of the liquid silicone may be further included.
또한, 상기 자외선 차단 액상 실리콘을 제조하는 단계는 상기 액상 실리콘 100중량부에 자외선 차단 오일을 3~5중량부로 혼합하여 80℃로 5~10분간 가열하는 것으로 수행되는 것일 수 있다.The step of preparing the ultraviolet barrier liquid silicone may be performed by mixing 100 parts by weight of the liquid silicone with 3 to 5 parts by weight of ultraviolet shielding oil and heating the mixture at 80 ° C for 5 to 10 minutes.
또한, 상기 자외선 차단 오일은 오일 100중량부에 자외선 차단제 40~60중량부를 혼합한 후 80~100℃로 가열하여 제조되는 것일 수 있다.The ultraviolet shielding oil may be prepared by mixing 40 to 60 parts by weight of an ultraviolet screening agent with 100 parts by weight of the oil and then heating the mixture to 80 to 100 ° C.
또한, 상기 오일은 옥수수 기름, 면실유, 포도씨유, 삼씨 기름(hempseed oil), 아마씨유, 야생 겨자유(wild mustard oil), 땅콩 기름, 들기름, 양귀비씨 기름, 평지씨 기름, 홍화씨 오일, 참기름, 콩기름, 해바라기씨 기름, 캐놀라 오일, 톨유 및 이들의 조합들로 이루어진 군에서 선택되는 것을 포함하는 것일 수 있다.The oil may also be selected from the group consisting of corn oil, cottonseed oil, grapeseed oil, hempseed oil, flaxseed oil, wild mustard oil, peanut oil, perilla oil, poppy seed oil, rapeseed oil, safflower oil, , Sunflower seed oil, canola oil, tall oil, and combinations thereof.
또한, 상기 액상 실리콘을 제조하는 단계 후 상기 액상 실리콘 100중량부에 글리세린 4~6중량부를 혼합하는 단계를 추가 포함할 수 있다.The method may further include mixing 4 to 6 parts by weight of glycerin with 100 parts by weight of the liquid silicone after the step of preparing the liquid silicone.
또한, 상기 자외선 차단 액상 실리콘을 제조하는 단계 후 상기 자외선 차단 액상 실리콘 100중량부에 글리세린 4~6중량부를 혼합하는 단계를 추가 포함할 수 있다.Further, after the step of preparing the ultraviolet-shielding liquid silicone, 100 parts by weight of the ultraviolet barrier liquid silicone may be mixed with 4 to 6 parts by weight of glycerin.
또한, 상기 액상 실리콘에 메탄올을 첨가하여 혼합하는 단계는 상기 액상 실리콘 100중량부에 메탄올 30~50중량부를 혼합하여 수행되는 것일 수 있다.The step of adding and mixing methanol to the liquid silicone may be performed by mixing 30 to 50 parts by weight of methanol with 100 parts by weight of the liquid silicone.
본원의 제 2 측면은, 상기 제 1 측면의 방법에 의해 제조된, 코팅제를 제공한다. A second aspect of the present invention provides a coating prepared by the method of the first aspect.
본원의 제 3 측면은, 오일 100중량부에 물 60~80중량부, 실리콘 점토 20~30중량부 및 목공 풀 40~60중량부를 포함하는 액상 실리콘; 및 A third aspect of the invention is a liquid silicone composition comprising 100 parts by weight of oil, 60 to 80 parts by weight of water, 20 to 30 parts by weight of silicone clay and 40 to 60 parts by weight of a wood pulp; And
상기 액상 실리콘을 100중량부로 할 때, 글리세린 4~6중량부 및 메탄올 30~50중량부를 포함하는 코팅제를 제공한다.And 4 to 6 parts by weight of glycerin and 30 to 50 parts by weight of methanol when the liquid silicone is 100 parts by weight.
본원의 제 4 측면은, 오일 100중량부에 물 60~80중량부, 실리콘 점토 20~30중량부 및 목공 풀 40~60중량부를 포함하는 액상 실리콘; 및 상기 액상 실리콘을 100중량부로 할 때, 자외선 차단 오일 3~5중량부, 글리세린 4~6중량부 및 메탄올 30~50중량부를 포함하는, 코팅제를 제공한다.A fourth aspect of the present invention is a liquid silicone composition comprising 100 parts by weight of oil, 60 to 80 parts by weight of water, 20 to 30 parts by weight of silicone clay and 40 to 60 parts by weight of a wood pulp; And 3 to 5 parts by weight of an ultraviolet barrier oil, 4 to 6 parts by weight of glycerin and 30 to 50 parts by weight of methanol when the liquid silicone is 100 parts by weight.
본 발명은 욕실 및 화장실 타일에 뿌려짐으로써 타일의 광택을 내주고, 곰팡이를 제거하며 동시에 미끄러움을 방지할 수 있다.The present invention can be applied to bathrooms and toilet tiles to provide gloss of tiles, remove mold and prevent slip at the same time.
본 발명은 표면만 코팅이 가능한 코팅제에 침투성을 지닌 발수제의 특성을 결합한 코팅제를 제공함으로써 효율적으로 벽을 보존할 수 있다. The present invention can effectively preserve walls by providing a coating agent combining the characteristics of a water repellent agent having permeability to a coating agent capable of coating only the surface.
기존의 발수제는 발수액을 많이 뿌리기 때문에 발수액이 흩날려 주변에 피해를 주지만 본원의 코팅제는 적은 양으로도 효과를 볼 수 있으며, 또한 일반적인 코팅제는 계절이 바뀌면서 수축과 이완을 반복하며 코팅이 깨지는 크랙 현상이 발생하는데, 본 발명으로 제조된 코팅제는 신축성이 좋기 때문에 크랙 현상이 기존의 코팅제에 비해 적게 발생한다.The conventional water repellent agent sprayed a lot of foot fluid, so that the foot fluids were scattered to cause damage to the surroundings. However, the coating agent of the present invention is effective in a small amount, and the general coating agent is repeatedly shrunk and relaxed as the season changes, Cracking phenomenon occurs. However, since the coating material prepared according to the present invention has good stretchability, cracking phenomenon occurs less than conventional coating materials.
본원에 의한 코팅제는 수분과 함께 햇빛에 의해 일어날 수 있는 황변을 막고 나무에 피는 곰팡이나 벽에 생기는 백화현상, 줄눈의 산화 및 오염을 방지하는 것으로 벽을 오래 보존시키며, 광고물의 부착을 막는 효과가 있고, 또한 코팅제 자체가 투명하고 광택이 있기 때문에 미관상으로 보기 좋다.The coating agent according to the present invention protects the yellowing which can be caused by the sunlight with moisture and prevents the bleaching and oxidation and contamination of the mold and the wall caused by the blooming on the tree, thereby preserving the wall for a long time and preventing the adhesion of the advertisement The coating itself is transparent and glossy, so it looks good.
이하, 본 발명의 구현예를 상세히 설명하기로 한다. 다만, 이는 예시로서 제시되는 것으로, 이에 의해 본 발명이 제한되지는 않으며 본 발명은 후술할 청구항의 범주에 의해 정의될 뿐이다.Hereinafter, embodiments of the present invention will be described in detail. However, the present invention is not limited thereto, and the present invention is only defined by the scope of the following claims.
본원의 제 1 측면은, 오일 100중량부에 물 60~80중량부, 실리콘 점토 20~30중량부 및 목공용 풀 40~60중량부를 포함하는 액상 실리콘을 제조하는 단계; 및 상기 액상 실리콘에 메탄올을 첨가하여 혼합하는 단계를 포함하는, 코팅제 제조 방법을 제공한다.According to a first aspect of the present invention, there is provided a process for producing a liquid silicone, comprising: preparing liquid silicone containing 60 to 80 parts by weight of water, 20 to 30 parts by weight of silicone clay and 40 to 60 parts by weight of a wood pulp in 100 parts by weight of oil; And Adding methanol to the liquid silicone, and mixing the liquid silicone.
본원의 일 구현예에 있어서, 상기 액상 실리콘을 제조하는 단계는, A: 오일 100중량부를 80℃로 가열하며 실리콘 점토 20~30중량부를 혼합하는 단계; B: 상기 가열된 오일 및 실리콘 점토 혼합액에 30~80℃의 물 60~80중량부를 혼합하여 80℃로 5~10분 동안 가열하는 단계; 및 C: 상기 가열된 오일, 실리콘 점토 및 물 혼합액에 목공용 풀 40~60중량부를 첨가하여 80℃로 가열하는 단계로 이루어진다. 상기 A 단계에서 오일을 80℃로 가열하는 것과 상기 B 단계에서 오일, 실리콘 점토 및 물 혼합액을 80℃로 가열하는 것은 오일, 실리콘 점토 및 물이 혼합되는 온도가 80℃이기 때문이다. 상기 A 단계에서 오일 및 실리콘 점토를 먼저 혼합하고 상기 B 단계에서 물을 추가로 혼합하며 상기 C단계에서 목공용 풀을 마지막으로 추가 혼합함으로써 각 재료가 보다 균일하게 혼합된 액상 실리콘 제조를 유도하였다. 상기 오일 100중량부에 물 60~80중량부, 실리콘 점토 20~30중량부 및 목공용 풀 40~60중량부의 비율로 혼합하여 기존의 실리콘 발수제나 욕실 바닥 코팅제에 비하여 오일의 비율을 증가시킴으로써 본 코팅제로 벽 코팅을 할 경우 오일로 인하여 표면에 코팅막 형성이 용이할 수 있다. 또한, 메탄올을 액상 실리콘에 혼합하여 액상실리콘이 분무기를 통해 분무될 수 있을 정도로 액상 실리콘의 점성을 낮출 수 있다In one embodiment of the present invention, the step of preparing the liquid silicone comprises: mixing 100 parts by weight of A: oil at 80 DEG C and 20 to 30 parts by weight of silicone clay; B: mixing 60 to 80 parts by weight of water at 30 to 80 캜 with the heated oil and silicone clay mixture and heating at 80 캜 for 5 to 10 minutes; And C: adding 40 to 60 parts by weight of a wood pulp to the heated oil, silicone clay and water mixture, and heating the mixture to 80 캜. The reason why the oil is heated to 80 ° C in the step A and the mixed oil, silicone clay and water are heated to 80 ° C in the step B is that the temperature at which the oil, the silicon clay and the water are mixed is 80 ° C. In step A, the oil and silicone clay were first mixed, water was further mixed in step B, and finally in step C, the wood paste was further mixed to induce a more uniformly mixed liquid silicone. By mixing 100 parts by weight of the oil at a ratio of 60 to 80 parts by weight of water, 20 to 30 parts by weight of silicone clay and 40 to 60 parts by weight of wood pulp, the proportion of oil is increased compared to conventional silicone water- When the wall coating is performed with a coating agent, the coating film can be easily formed on the surface due to the oil. In addition, methanol can be mixed into the liquid silicon to lower the viscosity of the liquid silicone so that the liquid silicone can be sprayed through the atomizer
본원의 일 구현예에 있어서, 상기 액상 실리콘을 제조하는 단계 후 상기 액상 실리콘 100중량부에 자외선 차단 오일을 3~5중량부로 혼합하여 자외선 차단 액상 실리콘을 제조하는 단계 및 상기 자외선 차단 액상 실리콘에 실리콘 희석제를 첨가하여 혼합하는 단계를 추가 포함할 수 있다. In one embodiment of the present invention, after the step of preparing the liquid silicone, 100 parts by weight of the liquid silicone is mixed with 3 to 5 parts by weight of an ultraviolet barrier oil to prepare an ultraviolet barrier liquid silicone, Adding a diluent to the mixture, and mixing.
본원의 일 구현예에 따르면, 상기 상기 자외선 차단 액상 실리콘을 제조하는 단계는 상기 액상 실리콘 100중량부에 자외선 차단 오일을 3~5중량부로 혼합하여 80℃로 5~10분간 가열하는 것으로 수행될 수 있다. 상기 액상 실리콘 100중량부에 자외선 차단 오일을 5중량부 초과로 혼합하면 코팅제의 투명도가 떨어지며, 3중량부 미만으로 혼합하면 자외선 차단 효과가 미미하므로 상기 자외선 차단 오일의 비율은 3~5중량부가 바람직하다. 상기 자외선 차단 오일을 액상 실리콘에 혼합함으로써 코팅제에 자외선 차단 효과가 부여된다. 또한 상기 자외선 차단 오일의 혼합으로 인하여 코팅제의 방수효과도 증가된다. 코팅제에 자외선 차단 효과가 부여되면 벽의 황변을 막아 벽이 본래 가지고 있던 모양과 색을 유지하며 벽의 변질 요소를 방지하여 내구성을 증가시킬 수 있다. According to an embodiment of the present invention, the step of preparing the ultraviolet barrier liquid silicone may be performed by mixing 3 to 5 parts by weight of ultraviolet shielding oil in 100 parts by weight of the liquid silicone and heating the mixture at 80 ° C for 5 to 10 minutes have. When the ultraviolet shielding oil is mixed in an amount of more than 5 parts by weight with 100 parts by weight of the liquid silicone, the transparency of the coating agent is lowered. When the ultraviolet shielding oil is mixed with less than 3 parts by weight, Do. The ultraviolet shielding effect is imparted to the coating agent by mixing the ultraviolet shielding oil with the liquid silicone. Also, the waterproof effect of the coating agent is increased due to the mixing of the ultraviolet shielding oil. When the coating has an ultraviolet shielding effect, it can block the yellowing of the wall to maintain the original shape and color of the wall, thereby preventing dullness of the wall and increasing durability.
일반적으로, 기존의 실리콘 발수제 혹은 수영장 바닥 코팅제는 벽이나 바닥에 침투를 많이 시켜야만 효과가 있기 때문에 아주 많은 양을 이용해야 벽이나 바닥에 스며들어가 굳어져서 발수의 효과가 제대로 있었다. 그러나 상기 자외선 차단 오일을 액상 실리콘에 혼합한 본원의 코팅제는 벽이나 바닥 표면에 코팅을 할 수 있을 정도의 침투성을 가지며 이에 따라 벽이나 바닥 표면에 코팅막을 형성하여 발수 및 방수를 가능하게 한다. 또한 기존의 일반적인 코팅제는 외부의 온도 차에 의한 신축성이 떨어져 크랙 현상이 많이 발생하지만, 자외선 차단 오일을 액상 실리콘에 혼합한 본원의 코팅제는 액상 실리콘을 베이스로 하여 자외선 차단 오일로 코팅효과를 발휘함으로써 신축성이 좋아 기존의 코팅제에 비해 크랙 현상이 적게 발생한다. 따라서 본원에 따른 코팅제는, 액상 실리콘에 의한 발수 성능과 자외선 차단 오일에 의한 표면 코팅 성능을 모두 포함하여 보다 효율적으로 발수 및 방수성능을 발휘할 수 있다. 이를 통하여, 여름철 강한 자외선에 노출되는 수영장 등 바닥의 발수 및 방수 성능 향상과 동시에 미끄럼 방지 기능까지 향상시킬 수 있다.In general, existing silicone water repellent or pool floor coatings are only effective if they penetrate walls or floors, so they must be used in very large amounts so that they penetrate into walls and floors and become hardened and water-repellent. However, the coating material of the present invention, which is obtained by mixing the ultraviolet shielding oil with liquid silicone, has permeability enough to be coated on the wall or floor surface, thereby forming a coating film on the wall or floor surface, In addition, conventional conventional coatings suffer from cracking due to external temperature difference. However, the present coating material, which is prepared by mixing ultraviolet shielding oil with liquid silicone, is coated with ultraviolet shielding oil based on liquid silicone There is less cracking than conventional coatings because of its good stretchability. Therefore, the coating agent according to the present invention can exhibit water repellency and waterproof performance more efficiently, including both water repellency by liquid silicone and surface coating performance by ultraviolet shielding oil. Through this, it is possible to improve the water repellency and waterproof performance of the floor such as a swimming pool exposed to strong ultraviolet rays in summer, and to improve the anti-slip function.
본원의 일 구현예에 따르면, 상기 자외선 차단 오일은, 오일 100중량부에 자외선 차단제 40~60중량부를 혼합한 후 80~100℃로 가열하여 제조된 것일 수 있다. 상기 자외선 차단제는, 오일에 혼합하여 자외선 차단 오일로 제조한 후 상기 액상 실리콘에 혼합하여야 고른 혼합이 이루어진다. 따라서 자외선 차단제를 액상 실리콘에 혼합하는 것 보다 자외선 차단 오일을 제조하여 액상 실리콘에 혼합하는 것이 바람직하다. According to one embodiment of the present invention, the ultraviolet shielding oil may be prepared by mixing 40 to 60 parts by weight of an ultraviolet screening agent with 100 parts by weight of oil, and heating the mixture to 80 to 100 ° C. The ultraviolet screening agent is mixed with an oil to prepare an ultraviolet screening oil and then mixed with the liquid silicone. Therefore, it is preferable to prepare an ultraviolet shielding oil and mix it with liquid silicon rather than mixing the ultraviolet screening agent into the liquid silicone.
상기 상기 자외선 차단제는 일반적으로 이용되는 화학적 자외선 차단제 및 물리적 자외선 차단제를 모두 이용할 수 있다. 예를 들어 상기 자외선 차단제는 페닐벤지미다졸설포닉애씨드[PhenylbenzimidazoleSulfonicAcid], 부틸메톡시디벤조일메탄[Butyl Methoxydibenzoylmethane], 시녹세이트[Cinoxate], 옥틸살리실레이트[Octylsalicylate], 티타늄옥사이드[Titanium Oxide], 벤조페논[Benzophenone]계 및 이들의 조합들로 이루어진 군에서 선택되는 것을 이용할 수 있으나 이에 제한되지 않는다. 그러나 화학적 자외선 차단제의 경우 자외선이 흡수되면 분해되는 원리를 이용하는 것이기 때문에 열과 광에 대한 안정성이 떨어지며 용제에 대한 용해성이 좋지 않아 벽 코팅제에는 물리적으로 자외선을 산란하는 방식인 물리적 자외선 차단제를 이용하는 것이 보다 바람직하다.The ultraviolet screening agent may be any of generally used chemical ultraviolet screening agents and physical ultraviolet screening agents. For example, the ultraviolet screening agent may be selected from the group consisting of phenylbenzimidazole sulfonic acid, butyl methoxydibenzoylmethane, cinoxate, octylsalicylate, titanium oxide, benzophenone, [Benzophenone] system, and combinations thereof. However, the present invention is not limited thereto. However, since the chemical ultraviolet screening agent utilizes the principle of decomposition when ultraviolet light is absorbed, the stability against heat and light is poor and the solubility in solvents is poor. Therefore, it is more preferable to use a physical ultraviolet screening agent Do.
상기 오일은 일반적으로 이용되는 식물성 기름이면 특별한 제한 없이 이용할 수 있다. 예를 들어 상기 오일은 옥수수 기름, 면실유, 포도씨유, 삼씨 기름(hempseed oil), 아마씨유, 야생 겨자유(wild mustard oil), 땅콩 기름, 들기름, 양귀비씨 기름, 평지씨 기름, 홍화씨 오일, 참기름, 콩기름, 해바라기씨 기름, 캐놀라 오일, 톨유 및 이들의 조합들로 이루어진 군에서 선택되는 것을 이용할 수 있으나, 이에 제한되지 않는다. The oil is generally used vegetable oil and can be used without any particular limitation. For example, the oil may be selected from the group consisting of corn oil, cottonseed oil, grapeseed oil, hempseed oil, flaxseed oil, wild mustard oil, peanut oil, perilla oil, poppy seed oil, rapeseed oil, safflower oil, Soybean oil, sunflower seed oil, canola oil, tall oil, and combinations thereof.
본원의 일 구현예에 따르면, 본 코팅제를 제조하는 방법은, 상기 액상 실리콘을 제조하는 단계 후 상기 액상 실리콘 100중량부에 글리세린 4~6중량부를 혼합하는 단계를 추가 포함할 수 있다. 또 다른 구현예로서, 본 코팅제를 제조하는 방법은, 상기 자외선 차단 액상 실리콘을 제조하는 단계 후 상기 자외선 차단 액상 실리콘 100중량부에 글리세린 4~6중량부를 혼합하는 단계를 추가 포함할 수 있다. 상기 글리세린 4~6중량부는 본 벽 코팅제의 점도를 조절하기 위한 것으로서, 상기 액상 실리콘에 자외선 차단 오일을 혼합하기 전에 글리세린을 먼저 혼합하는 것도 가능하고 상기 액상 실리콘에 자외선 차단 오일을 혼합한 후에 글리세린을 혼합하는 것도 가능하다. 상기 글리세린을 혼합하는 방법은 특별한 제한이 없으나, 글리세린이 20℃가 넘으면 폭발하는 성질이 있으므로 상기 자외선 차단 액상 실리콘 또는 상기 액상 실리콘을 20℃ 이하로 식힌 후 글리세린을 혼합하는 것이 바람직하다. 코팅제는 적당한 점도를 가져야만 코팅제 사용 시 적은 사용량으로 벽 코팅을 용이하게 할 수 있으므로 상기 글리세린의 비율은 상기 자외선 차단 액상 실리콘 100중량부에 글리세린 4~6중량부가 바람직하다. 상기 글리세린의 비율로 제조된 코팅제는 점도와 벽 침투도가 적절하여 코팅제를 분무기로 분사하는 행위로 간단하게 사용할 수 있다. 상기 글리세린은 상기 자외선 차단 오일과 함께 코팅제에 자외선 차단효과 및 방수효과를 증가시킨다.According to one embodiment of the present invention, the method for preparing the coating agent may further include mixing 4 to 6 parts by weight of glycerin with 100 parts by weight of the liquid silicone after the step of preparing the liquid silicone. In yet another embodiment, the method of preparing the coating may further comprise adding 4 to 6 parts by weight of glycerin to 100 parts by weight of the ultraviolet barrier liquid silicone after the step of preparing the ultraviolet barrier liquid silicone. 4 to 6 parts by weight of the glycerin is used for controlling the viscosity of the present wall coating. It is also possible to mix glycerin first before mixing the ultraviolet barrier oil into the liquid silicone, and after mixing the ultraviolet barrier oil with the liquid silicone, Mixing is also possible. There is no particular limitation on the method of mixing the glycerin. However, since the ultraviolet barrier liquid silicone or the liquid silicone is cooled to 20 캜 or lower, it is preferable to mix glycerin. The coating agent may have a suitable viscosity to facilitate wall coating with a small amount when the coating agent is used, so that the ratio of the glycerin is preferably 4 to 6 parts by weight of glycerin to 100 parts by weight of the ultraviolet barrier liquid silicone. The coating agent prepared by the above-mentioned ratio of glycerin can be used simply as an act of spraying the coating agent with the sprayer since the viscosity and the wall penetration degree are appropriate. The glycerin increases ultraviolet blocking effect and waterproof effect on the coating agent together with the ultraviolet shielding oil.
또한, 글리세린을 액상 실리콘에 메탄올을 혼합한 혼합액을 100중량부로 할 때, 상기 혼합액에 1중량부로 하여 첨가하여 혼합할 수 있다. 글리세린을 혼합함으로써 본 발명에 따른 코팅제로 코팅한 후 타일에 광택을 유지할 수 있다. 또한, 타일과 타일 사이의 줄눈과 같은 간격에 본 혼합액으로 스프레이코팅을 하게 되므로 줄눈에 습기가 침투할 수 없게 되어, 습기로 인한 곰팡이 발생을 방지하게 된다. 또한, 타일 바닥면의 코팅으로 인해 욕실, 화장실, 수영장 등의 바닥이 방수가 되고, 본 혼합액에 포함하는 고무성분의 연성에 따른 마찰면 확대로 발이 미끄러지지 않게 됩니다. 또한, 발수성 향상으로 물기가 코팅면을 차지하는 면적이 적게 되어 물기로 인한 미끄러짐도 방지할 수 있다.When 100 parts by weight of a mixed solution of glycerin and liquid silicon mixed with methanol is added to the above mixed solution in an amount of 1 part by weight, the mixture can be mixed. By mixing glycerin it is possible to maintain gloss on the tile after coating with the coating according to the invention. In addition, since the spray mixture is spray-coated at the same interval as the joint between the tile and the tile, moisture can not penetrate into the joint, thereby preventing mold caused by moisture. In addition, the floor of the bathroom, toilet, pool, etc. becomes waterproof due to the coating of the floor surface of the tile, and the foot does not slip due to the expansion of the friction surface according to the ductility of the rubber component contained in this mixed solution. Further, the water repellency improves the area occupied by the water on the coated surface, and slip due to water can be prevented.
본원의 일 구현예에 따르면, 상기 자외선 차단 액상 실리콘에 실리콘 희석제를 첨가하여 혼합하는 단계는 자외선 차단 액상 실리콘 100중량부에 실리콘 희석제 30~50중량부를 혼합하여 수행되는 것일 수 있다. 상기 실리콘 희석제는 일반적으로 이용되는 실리콘 희석제라면 특별한 제한 없이 이용할 수 있으며, 예를 들어 신나를 이용할 수 있다. 상기 실리콘 희석제의 비율에 따라 본 코팅제의 점도를 조절하여 코팅 시 적은 사용량으로 벽 코팅을 용이하게 할 수 있으며 상기 실리콘 희석제의 비율은 상기 자외선 차단 액상 실리콘 100중량부에 실리콘 희석제 30~50중량부가 바람직하다. 상기 실리콘 희석제의 비율로 제조된 코팅제는 점도와 벽 침투도가 적절하여 코팅제를 분무기로 분사하는 행위로 간단하게 사용할 수 있다. 상기 혼합은 일반적으로 희석제를 혼합할 때 사용되는 방법이면 특별한 제한이 없이 이용할 수 있고 예를 들어, 자외선 차단 액상 실리콘 100중량부에 실리콘 희석제 30~50중량부를 넣고 혼합기를 5분간 작동시키는 것일 수 있으나, 이에 제한되지 않는다.According to an embodiment of the present invention, the step of adding and mixing a silicone diluent to the ultraviolet barrier liquid silicone may be performed by mixing 30 to 50 parts by weight of a silicone diluent with 100 parts by weight of ultraviolet barrier liquid silicone. The silicon diluent can be used without any particular limitation as long as it is a commonly used silicon diluent. For example, thinner can be used. The viscosity of the coating composition may be controlled according to the ratio of the silicone diluent to facilitate wall coating with a small amount of the coating. The ratio of the silicone diluent is preferably 30 to 50 parts by weight to 100 parts by weight of the ultraviolet barrier liquid silicone Do. The coating agent prepared by the ratio of the silicone diluent may be simply used as an act of spraying the coating agent with the sprayer since the viscosity and wall penetration are appropriate. For example, 30 to 50 parts by weight of the silicone diluent may be added to 100 parts by weight of the ultraviolet barrier liquid silicone, and the mixer may be operated for 5 minutes. However, , But is not limited thereto.
본원의 일 구현예에 따르면, 상기 액상 실리콘에 메탄올을 첨가하여 혼합하는 단계는 상기 액상 실리콘 100중량부에 메탄올 30~50중량부를 혼합하여 수행되는 것일 수 있다. 메탄올의 비율에 따라 본 코팅제의 점도를 조절하여 코팅 시 분무기를 통해 코팅을 할 수 있다. 액상 실리콘 100중량부에 메탄올을 30 중량부 미만으로 혼합하는 경우, 액상 실리콘의 점도가 높아 분무기를 통한 분무가 불가능한다. 또한, 메탄올을 50 중량부 초과하여 혼합하는 경우, 액상 실리콘이 경화되는 문제점이 발생한다. 이에 메탄올을 30~50중량부만큼 혼합하여 일반적인 분무기를 통한 욕실, 화장실, 수영장 바닥 코팅을 할 수 있다. 또한, 분무기와 같은 스프레이 장치를 통해 분무하기 때문에 특별한 경험이 없는 사람들도 가정이나 사무실, 욕실 등 타일에 대하여 스프레이하여 바로 사용할 수 있다. 또한, 메탄올은 실리콘 희석제 대신 첨가하여 혼합되는 것일 수 있다.According to an embodiment of the present invention, the step of adding methanol to the liquid silicone may be performed by mixing 30 to 50 parts by weight of methanol with 100 parts by weight of the liquid silicone. Depending on the ratio of methanol, the viscosity of the coating can be adjusted to coat the coating through the sprayer. When 100 parts by weight of liquid silicone is mixed with less than 30 parts by weight of methanol, the viscosity of the liquid silicone is high and spraying through the atomizer is impossible. Further, when the methanol is mixed in an amount exceeding 50 parts by weight, there arises a problem that the liquid silicone is cured. By mixing 30 ~ 50 parts by weight of methanol, it is possible to coat bathroom, toilet and swimming pool floor through general spraying machine. In addition, sprayers are sprayed through the same spray device, so those who have no special experience can spray the tiles at home, office, or bathroom. In addition, methanol may be added and mixed in place of the silicon diluent.
본원의 제 2 측면은, 상기 본원의 제 1 측면의 코팅제의 제조방법에 따라 제조된 코팅제를 제공한다. 본원에 따른 상기 코팅제에 대하여 본원의 제 1측면에 대하여 기술된 내용을 모두 적용 할 수 있다. The second aspect of the present invention provides a coating agent prepared according to the method for producing the coating agent of the first aspect of the present invention. All of the teachings of the first aspect of the present application can be applied to the coating agent according to the present application.
본원의 제 3 측면은, 오일 100중량부에 물 60~80중량부, 실리콘 점토 20~30중량부 및 목공 풀 40~60중량부를 포함하는 액상 실리콘; 및 상기 액상 실리콘을 100중량부로 할 때, 글리세린 4~6중량부 및 메탄올 30~50중량부를 포함하는, 코팅제를 제공한다.A third aspect of the invention is a liquid silicone composition comprising 100 parts by weight of oil, 60 to 80 parts by weight of water, 20 to 30 parts by weight of silicone clay and 40 to 60 parts by weight of a wood pulp; And 4 to 6 parts by weight of glycerin and 30 to 50 parts by weight of methanol when the liquid silicone is 100 parts by weight.
본원의 제 4 측면은, 오일 100중량부에 물 60~80중량부, 실리콘 점토 20~30중량부 및 목공 풀 40~60중량부를 포함하는 액상 실리콘; 및 상기 액상 실리콘을 100중량부로 할 때, 자외선 차단 오일 3~5중량부, 글리세린 4~6중량부, 및 메탄올 30~50중량부를 포함하는, 코팅제를 제공한다.A fourth aspect of the present invention is a liquid silicone composition comprising 100 parts by weight of oil, 60 to 80 parts by weight of water, 20 to 30 parts by weight of silicone clay and 40 to 60 parts by weight of a wood pulp; And 3 to 5 parts by weight of an ultraviolet barrier oil, 4 to 6 parts by weight of glycerin and 30 to 50 parts by weight of methanol when the liquid silicone is 100 parts by weight.
본원의 제 5 측면은, 오일 100중량부에 물 60~80중량부, 실리콘 점토 20~30중량부 및 목공 풀 40~60중량부를 포함하는 액상 실리콘; 및 상기 액상 실리콘을 100중량부로 할 때, 자외선 차단 오일 3~5중량부, 글리세린 4~6중량부, 실리콘 희석제 30~50중량부 및 메탄올 30~50중량부를 포함하는, 코팅제를 제공한다.A fifth aspect of the invention is a liquid silicone composition comprising 100 parts by weight of oil, 60 to 80 parts by weight of water, 20 to 30 parts by weight of silicone clay and 40 to 60 parts by weight of a wood pulp; And 3 to 5 parts by weight of an ultraviolet shielding oil, 4 to 6 parts by weight of glycerin, 30 to 50 parts by weight of a silicone diluent and 30 to 50 parts by weight of methanol when the liquid silicone is 100 parts by weight.
이하 본 발명의 실시예를 기재한다. 그러나 하기의 실시예는 본 발명의 일 실시예 일 뿐 본 발명이 하기한 실시예에 한정되는 것은 아니다.Hereinafter, examples of the present invention will be described. However, the following examples are only illustrative of the present invention and are not intended to limit the scope of the present invention.
하기와 같은 방법으로 본 발명에 따른 자외선 차단 효과를 지닌 코팅제를 제조하였다. A coating agent having an ultraviolet blocking effect according to the present invention was prepared by the following method.
1. 액상 실리콘의 제조 One. Production of liquid silicon
(1) 식물성 기름 2ℓ에 80℃의 열을 가하면서 실리콘 점토 500g을 넣고 40℃의 물 2ℓ를 넣고 80℃로 5분 동안 가열하였다.(One) 500 g of silicon clay was added to 2 liters of vegetable oil while heating at 80 DEG C, 2 liters of water at 40 DEG C was added, and the mixture was heated at 80 DEG C for 5 minutes.
(2) 상기 식물성 기름, 실리콘 점토 및 물 혼합액에 목공용 풀 1ℓ를 첨가하여 80℃로 가열하였다. (2) To the mixture of vegetable oil, silicone clay and water was added 1 L of wood pulp and heated to 80 ° C.
(3) 상기 식물성 기름, 실리콘 점토, 물 및 목공용 풀 혼합액의 온도를 20℃로 낮추고 글리세린을 275 mℓ첨가하여 혼합하였다. (3) The temperature of the vegetable oil, silicone clay, water and wood paste mixture was lowered to 20 ° C and 275 ml of glycerin was added and mixed.
2. 자외선 차단 오일의 제조 2. Manufacture of sunscreen oil
옥수수기름 100g에 티타늄 옥사이드 40g을 넣고 80℃로 가열하며 혼합하였다. 40 g of titanium oxide was added to 100 g of corn oil, and the mixture was heated to 80 캜 and mixed.
3. 자외선 차단 액상 실리콘의 제조 3. Manufacture of ultraviolet-shielding liquid silicone
상기 1의 액상 실리콘 100중량부에 20℃로 식힌 상기 2의 자외선 차단 오일을 4중량부로 혼합하였다. To 100 parts by weight of the liquid silicone 1 described above, 4 parts by weight of the ultraviolet blocking oil of the above 2, which had been cooled to 20 캜, were mixed.
4. 메탄올의 첨가 4. Addition of methanol
상기 3의 가열된 자외선 차단 액상 실리콘을 식힌 후, 상기 자외선 차단 액상 실리콘 100중량부에 메탄올 30중량부를 혼합하여 혼합기에 넣고 5분 동안 혼합기를 작동시켰다. After cooling the heated ultraviolet barrier liquid silicone 3, 100 parts by weight of the UV-blocking liquid silicone was mixed with 30 parts by weight of methanol, and the mixture was put into a mixer for 5 minutes.
하기와 같은 방법으로 본 발명에 따른 자외선 차단 효과를 지닌 코팅제를 제조하였다. A coating agent having an ultraviolet blocking effect according to the present invention was prepared by the following method.
1. 액상 실리콘의 제조 One. Production of liquid silicon
(1) 식물성 기름 2ℓ에 80℃의 열을 가하면서 실리콘 점토 500g을 넣고 40℃의 물 2ℓ를 넣고 80℃로 5분 동안 가열하였다.(One) 500 g of silicon clay was added to 2 liters of vegetable oil while heating at 80 DEG C, 2 liters of water at 40 DEG C was added, and the mixture was heated at 80 DEG C for 5 minutes.
(2) 상기 식물성 기름, 실리콘 점토 및 물 혼합액에 목공용 풀 1ℓ를 첨가하여 80℃로 가열하였다. (2) To the mixture of vegetable oil, silicone clay and water was added 1 L of wood pulp and heated to 80 ° C.
(3) 상기 식물성 기름, 실리콘 점토, 물 및 목공용 풀 혼합액의 온도를 20℃로 낮추고 글리세린을 275 mℓ첨가하여 혼합하였다. (3) The temperature of the vegetable oil, silicone clay, water and wood paste mixture was lowered to 20 ° C and 275 ml of glycerin was added and mixed.
2. 자외선 차단 오일 - 팀버렉스 헤비 듀티 UV 오일을 사용하였다. 2. UV protection oil - Timber Rex Heavy Duty UV oil was used.
3. 자외선 차단 액상 실리콘의 제조 3. Manufacture of ultraviolet-shielding liquid silicone
상기 1의 액상 실리콘 100중량부에 20℃로 식힌 상기 2의 자외선 차단 오일을 4중량부로 혼합하였다. To 100 parts by weight of the liquid silicone 1 described above, 4 parts by weight of the ultraviolet blocking oil of the above 2, which had been cooled to 20 캜, were mixed.
4. 메탄올의 첨가 4. Addition of methanol
상기 3의 가열된 자외선 차단 액상 실리콘을 식힌 후, 상기 자외선 차단 액상 실리콘 100중량부에 메탄올 30중량부를 혼합하여 혼합기에 넣고 5분 동안 혼합기를 작동시켰다.After cooling the heated ultraviolet barrier liquid silicone 3, 100 parts by weight of the UV-blocking liquid silicone was mixed with 30 parts by weight of methanol, and the mixture was put into a mixer for 5 minutes.
(비교예 1)(Comparative Example 1)
하기와 같은 방법으로 자외선 차단 오일이 포함되지 않은 코팅제를 제조하였다. A coating agent not containing an ultraviolet barrier oil was prepared by the following method.
1. 액상 실리콘의 제조 One. Production of liquid silicon
(1) 식물성 기름 2ℓ에 80℃의 열을 가하면서 실리콘 점토 500g을 넣고 40℃의 물 2ℓ를 넣고 80℃로 5분 동안 가열하였다.(One) 500 g of silicon clay was added to 2 liters of vegetable oil while heating at 80 DEG C, 2 liters of water at 40 DEG C was added, and the mixture was heated at 80 DEG C for 5 minutes.
(2) 상기 식물성 기름, 실리콘 점토 및 물 혼합액에 목공용 풀 1ℓ를 첨가하여 80℃로 가열하였다. (2) To the mixture of vegetable oil, silicone clay and water was added 1 L of wood pulp and heated to 80 ° C.
(3) 상기 식물성 기름, 실리콘 점토, 물 및 목공용 풀 혼합액의 온도를 20℃로 낮추고 글리세린을 275 mℓ첨가하여 혼합하였다. (3) The temperature of the vegetable oil, silicone clay, water and wood paste mixture was lowered to 20 ° C and 275 ml of glycerin was added and mixed.
2. 실리콘 희석제의 첨가 2. Addition of silicone diluent
상기 1의 액상 실리콘 100중량부에 실리콘 희석제(신나) 30중량부를 혼합하여 혼합기에 넣고 5분 동안 혼합기를 작동시켰다.100 parts by weight of the above liquid silicone 1 was mixed with 30 parts by weight of a silicone diluent (thinner), and the mixture was put into a mixer for 5 minutes.
(실험예 1)(Experimental Example 1)
상기 자외선 차단 및 미끄럼 방지 코팅제 조성물을 실험하기 위해 40㎝ 정사각형 나무판에 높이 20㎝의 아스콘을 타설하여 아스콘을 타설한 가운데 부분에 온도계를 눈금이 보이도록 묻어 만든 시편 세 개를 제작하였다. 상기 시편 세 개 각각에, 하나는 실시예 1에서 제조된 자외선 차단 및 미끄럼 방지 코팅제 조성물 14g을 분무기로 골고루 도포하여 12시간 동안 완전 건조시키고, 다른 하나는 실시예 2에서 제조된 자외선 차단 및 미끄럼 방지 코팅제 조성물 14g을 분무기로 골고루 도포하여 12시간 동안 완전 건조시키고, 또 다른 하나는 처음 제작된 상태로 두고 공간이 밀폐된 시험기에 파장영역이 넓은 적외선 전구인 네른스튼 전구 두 개를 설치하고 시험기 안의 내부 온도의 변화에 따른 아스콘의 내부 온도를 온도계로 측정하여 표 1과 같은 온도 변화의 시험치를 얻을 수 있었다.In order to test the above UV blocking and anti-slip coating composition, three specimens were prepared by placing 20 cm height ascon on a 40 cm square wooden plate and placing a thermometer on the center of the ascon. One of each of the three specimens was coated with 14 g of the ultraviolet blocking and anti-slip coating composition prepared in Example 1 evenly using an atomizer and completely dried for 12 hours, and the other was subjected to ultraviolet blocking and anti-slip 14 g of the coating composition was spread evenly using an atomizer and completely dried for 12 hours, and the other was a test tube having a space sealed for the first time, and two Nernsted bulbs, each having a wide wavelength range, were installed. The internal temperature of the ascon was measured with a thermometer according to the change of the temperature, and the test value of the temperature change as shown in Table 1 was obtained.
시료 1: 실시예 1에서 제조된 자외선 차단 및 미끄럼 방지 코팅제 조성물을 도포한 상태의 아스콘Sample 1: Ascone in the state of applying the ultraviolet blocking and anti-slip coating composition prepared in Example 1
시료 2: 실시예 2에서 제조된 자외선 차단 및 미끄럼 방지 코팅제 조성물을 도포한 상태의 아스콘Sample 2: Ascontron coated with the ultraviolet barrier and anti-slip coating composition prepared in Example 2
시료 3: 자외선 차단 코팅제 조성물을 도포하지 않은 상태의 아스콘Sample 3: Ascon in a state in which the ultraviolet barrier coating composition was not applied
상기 표 1의 결과에서 실시예 1 및 실시예 2에서 제조된 자외선 차단 및 미끄럼 방지 코팅제 조성물을 도포한 상태의 아스콘의 온도가 코팅제 조성물을 도포하지 않은 상태의 아스콘보다 온도가 적게 상승하는 것을 확인할 수 있다. From the results shown in Table 1, it can be seen that the temperature of the ascon in the state of applying the ultraviolet blocking and anti-slip coating composition prepared in Example 1 and Example 2 is lower than that of the ascon in the state that the coating composition is not applied have.
(실험예 2)(Experimental Example 2)
상기 자외선 차단 및 미끄럼 방지 코팅제 조성물의 발수 및 방수 성능을 실험하기 위해 40㎝ 정사각형 나무판에 높이 20㎝의 아스콘을 타설하여 만든 시편 6개를 제작하였다. 상기 시편 6개 각각에, 상기 실시예 1 및 실시예 2에서 제조된 자외선 차단 벽 코팅제 조성물 130g 및 14g과, 상기 비교예에서 제조된 코팅제 조성물 130g 및 14g을 분무기로 골고루 도포한 후 12 시간 동안 건조하였다. 건조 후 각각의 시편 표면에 대해 50mℓ의 물을 분무기로 도포하고 육안으로 확인하였다. 평가 기준은 물방울 잔흔 유무를 육안으로 관찰하였다. 물방울이 구형으로 미끄러져 떨어져서 물방울 흔적이 남지 않은 것을 "◎", 물방울이 구형으로 미끄러져 떨어져서 물방울 흔적이 대부분 남지 않은 것을 "○", 물방울이 구형으로 미끄러져 떨어졌지만 물방울 흔적이 남은 것을 "△", 물방울이 구형으로 미끄러져 떨어지지 않고 물방울 흔적이 남은 것을 "×"로 하였다.In order to test the water repellency and waterproofing performance of the UV blocking and anti-slip coating composition, six specimens were prepared by placing 20 cm height ascon on a 40 cm square wooden plate. 130 g and 14 g of the ultraviolet blocking wall coating composition prepared in Examples 1 and 2 and 130 g and 14 g of the coating composition prepared in the above Comparative Example were uniformly sprayed on each of the above six specimens and spray dried for 12 hours Respectively. After drying, 50 mℓ of water was applied to the surface of each specimen with an atomizer and visually confirmed. The evaluation criteria were visually observed for water droplet residue. "◎" when the water droplet slipped down into a spherical shape and the water droplet remained "◎", the water droplet slipped down into the spherical shape and most of the water droplet remnants remained "○", the water droplet slipped down into the spherical shape, &Quot;, "x ", in which the water droplet slipped into the spherical shape and did not fall off, and remained water droplet remained.
시료 1: 상기 실시예 1에서 제조된 자외선 차단 및 미끄럼 방지 코팅제 조성물을 130g 도포한 상태의 아스콘Sample 1: 130 g of the ultraviolet light blocking and anti-slip coating composition prepared in Example 1 was applied,
시료 2: 상기 실시예 2에서 제조된 자외선 차단 및 미끄럼 방지 코팅제 조성물을 130g 도포한 상태의 아스콘Sample 2: 130 g of the ultraviolet blocking and anti-slip coating composition prepared in Example 2,
시료 3: 상기 비교예에서 제조된 코팅제 조성물을 130g 도포한 상태의 아스콘Sample 3: 130 g of the coating composition prepared in the above Comparative Example was applied,
시료 4: 상기 실시예 1에서 제조된 자외선 차단 및 미끄럼 방지 코팅제 조성물을 14g 도포한 상태의 아스콘Sample 4: 14 g of the ultraviolet light blocking and anti-slip coating composition prepared in Example 1 was applied,
시료 5: 상기 실시예 2에서 제조된 자외선 차단 및 미끄럼 방지 코팅제 조성물을 14g 도포한 상태의 아스콘Sample 5: 14 g of the ultraviolet light blocking and anti-slip coating composition prepared in Example 2,
시료 6: 상기 비교에에서 제조된 코팅제 조성물을 14g 도포한 상태의 아스콘Sample 6: 14 g of the coating composition prepared in the above comparison was applied,
상기 표 2의 결과에서 실시예 1 및 실시예 2에서 제조된 자외선 차단 및 미끄럼 방지 코팅제 조성물을 도포한 상태의 아스콘이 상기 비교예에서 제조된 자외선 차단 오일을 혼합하지 않은 코팅제 조성물을 도포한 아스콘보다 물방울이 적게 맺히는 것을 확인할 수 있었다.The results of Table 2 show that the ascon in the state of applying the ultraviolet barrier and anti-slip coating composition prepared in Example 1 and Example 2 is higher than that of the ascon in which the anti- It was confirmed that water drops were formed less.
본 발명은 상기 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 제조될 수 있으며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다.It will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the present invention as defined by the following claims. As will be understood by those skilled in the art. It is therefore to be understood that the above-described embodiments are illustrative in all aspects and not restrictive.
Claims (12)
상기 액상 실리콘에 메탄올을 첨가하여 혼합하는 단계
를 포함하는, 욕실 바닥 코팅제 제조 방법.Preparing liquid silicone containing 100 parts by weight of oil, 60 to 80 parts by weight of water, 20 to 30 parts by weight of silicone clay and 40 to 60 parts by weight of wood pulp; And
Adding methanol to the liquid silicone and mixing
≪ / RTI >
A: 오일 100중량부를 80℃로 가열하며 실리콘 점토 20~30중량부를 혼합하는 단계;
B: 상기 가열된 오일 및 실리콘 점토 혼합액에 30~80℃의 물 60~80중량부를 혼합하여 80℃로 5~10분 동안 가열하는 단계; 및
C: 상기 가열된 오일, 실리콘 점토 및 물 혼합액에 목공용 풀 40~60중량부를 첨가하여 80℃로 가열하는 단계로 이루어지는, 욕실 바닥 코팅제 제조 방법.2. The method of claim 1,
A: mixing 100 parts by weight of oil with 80 to 20 parts by weight of silicone clay 20 to 30 parts by weight;
B: mixing 60 to 80 parts by weight of water at 30 to 80 캜 with the heated oil and silicone clay mixture and heating at 80 캜 for 5 to 10 minutes; And
C: 40 to 60 parts by weight of a wood-working paste is added to the heated oil, silicone clay and water mixture, and heated to 80 占 폚.
상기 자외선 차단 액상 실리콘을 제조하는 단계는
상기 액상 실리콘 100중량부에 자외선 차단 오일을 3~5중량부로 혼합하여 80℃로 5~10분간 가열하는 것으로 수행되는 것인, 욕실 바닥 코팅제 제조 방법.The method of claim 3,
The step of producing the ultraviolet-shielding liquid silicone
And 100 parts by weight of the liquid silicone is mixed with 3 to 5 parts by weight of ultraviolet shielding oil and heated at 80 DEG C for 5 to 10 minutes.
상기 액상 실리콘을 100중량부로 할 때, 글리세린 4~6중량부 및 메탄올 30~50중량부를 포함하는, 욕실 바닥 코팅제.Liquid silicon containing 60 to 80 parts by weight of water, 20 to 30 parts by weight of silicone clay and 40 to 60 parts by weight of a wood pulp in 100 parts by weight of oil; And
And 4 to 6 parts by weight of glycerin and 30 to 50 parts by weight of methanol when the liquid silicone is 100 parts by weight.
상기 액상 실리콘을 100중량부로 할 때, 자외선 차단 오일 3~5중량부, 글리세린 4~6중량부 및 메탄올 30~50중량부를 포함하는, 욕실 바닥 코팅제.
Liquid silicon containing 60 to 80 parts by weight of water, 20 to 30 parts by weight of silicone clay and 40 to 60 parts by weight of a wood pulp in 100 parts by weight of oil; And
3 to 5 parts by weight of an ultraviolet shielding oil, 4 to 6 parts by weight of glycerin and 30 to 50 parts by weight of methanol when the liquid silicone is 100 parts by weight.