KR20180131826A - Organic-inorganic hybrid powder paint for waterproofing and anticorrosion of concrete site and the construction method of waterproofing and anticorrosion of concrete using the same - Google Patents
Organic-inorganic hybrid powder paint for waterproofing and anticorrosion of concrete site and the construction method of waterproofing and anticorrosion of concrete using the same Download PDFInfo
- Publication number
- KR20180131826A KR20180131826A KR1020170068423A KR20170068423A KR20180131826A KR 20180131826 A KR20180131826 A KR 20180131826A KR 1020170068423 A KR1020170068423 A KR 1020170068423A KR 20170068423 A KR20170068423 A KR 20170068423A KR 20180131826 A KR20180131826 A KR 20180131826A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- waterproofing
- concrete
- powder
- parts
- Prior art date
Abstract
Description
본 발명은 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물 및 이를 이용한 콘크리트 방수, 방식 시공방법에 관한 것으로, 보다 상세하게는 기존 하수관, 하수종말 처리장, 배수지 콘크리트 벽면 구조물과의 접착성과 각 구조물 특성상 방식, 방수 기능이 우수하고, 분말페인트 분진저감 및 시공 후 청소 최소화 에 따른 양호한 작업성을 유지하며, 단시간에 보수 및 시공을 용이하게 할 수 있는 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물 및 이를 이용한 콘크리트 방수, 방식 시공방법에 관한 것이다.The present invention relates to a hybrid water-based and water-based hybrid powder paint composition, and a concrete waterproofing method and a concrete waterproofing method using the same. More particularly, the present invention relates to a water- , A hybrid water-repellent and water-repellent hybrid powder paint composition excellent in waterproof function, capable of reducing powder paint dust, minimizing cleaning after construction and maintaining good workability and facilitating repair and construction in a short time, and Concrete waterproofing, and method of construction.
세계 기후가 점점 변화가 심해지면서 물을 자원화 하는 것이 매우 중요하게 되었다. 특히 우리나라처럼 여름 장마철에 1년 강수량의 60%가 집중되어 있는 상황에서 물의 저장은 국민의 삶에 바로 직결되어 있어 정책적으로 많은 노력을 하고 있다. As the global climate has become increasingly changing, it has become very important to recycle water. Especially, as 60% of the annual rainfall is concentrated in the summer rainy season in Korea, the water storage is directly connected to the lives of the people, and the policy efforts are being made.
또한, 점점 도시화 및 인구가 한곳에 집중되어 있어 하루 사용되는 물의 량이 해마다 늘어 나고 있으며 이를 대처하기 위해 매년 배수지, 하수관 및 하수처리장 등 물과 관련된 시설물을 건설하여 수요을 맞춰가고 있는 실정이다.In addition, as urbanization and population are increasingly concentrated in one place, the amount of water used per day is increasing each year. In order to cope with this, water-related facilities such as drainage, sewage and sewage treatment plants are being built every year to meet demand.
특히, 배수지, 하수관, 하수처리는 물을 저장하고 사용한 물을 이송하고 이를 처리하여 하천에 방류하는 시스템에서는 방수, 방식제의 선택이 매우 중요하다. Particularly, in the system of reservoir, sewage and sewage treatment, it is very important to select the waterproofing agent and the cushioning agent in the system where water is stored and the used water is transported and processed and discharged into the river.
현재, 물의 이송 및 저장에 관련된 콘크리트 구조물은 신축과 보수로 나눠져 있으며 신축은 주로 에폭시 코팅, 세라믹 코팅의 주로 얇은 코팅재로 마감하고 있으며, 보수인 경우 다양한 공법이 나오고 있는데 대체적으로 쉬트(SHEET) 공법 및 단면복구 몰탈을 선호하고 있는 상태이다. Currently, the concrete structures related to water transport and storage are divided into expansion and repair. The expansion and contraction is mainly made up of thin coatings of epoxy coatings and ceramic coatings. Various methods of repairing are available. In general, SHEET It is in favor of single-sided recovery mortar.
하지만, 코팅공법은 도막이 0.2~0.3mm로 얇아서 쉽게 파손 및 콘크리트 구조체 들뜸 현상이 발생한다. 또한 쉬트(SHEET) 방식은 높은 시공 단가와 쉬트 사이의 실링(SEALING) 처리를 잘못하면 전체적으로 큰 하자를 낳고 있고 단면복구 몰탈은 콘크리트 하지면 칩핑하는 과정에 손상을 일으킬 수 있다. However, the coating method is as thin as 0.2 ~ 0.3mm and easily breaks and lifts the concrete structure. In addition, the SHEET method incurs a large deficiency as a result of erroneous sealing treatment between the high construction cost and the sheet, and the single-sided repair mortar can cause damage to the concrete chipping process.
이와 같이, 물을 처리하는 시설은 국가 구조물로서 국민의 안전과 생활에서 매우 중요한 시설물임을 감안할 때, 위 두가지 공법으로 인한 문제점을 해결하여 소량의 물도 손실되지 않도록 방식, 방수 기능을 향상시키면서 콘크리트 구조물과의 일체화 및 전체적으로 이음새 없이 방식, 방수 시공이 가능한 방수, 방식재 및 이를 이용한 시공공법의 개발이 시급한 실정이다.Considering that the water treatment facility is a national structure and is a very important facility for people's safety and life, it is necessary to solve the problems caused by the above two methods so as to improve the waterproof function and improve the concrete structure It is urgently necessary to develop a seamless waterproofing method, a waterproofing material capable of waterproofing construction, and a construction method using the same.
현재까지 개발된 방수, 방식재료 및 그 시공방법을 살펴 보면, 한국등록특허 특0180111(1998년11월30일)에 1.4 내지 0.07㎜ 범위의 입도로 조정된 규사 100중량부에 대해 포틀랜드 시멘트가 70 내지 130중량부로 구성된 방수용 베이스 몰탈 조성물 100중량부에 대해, 재유화형 분말수지 2 내지 6중량부, 물의 표면장력 감소와 젖음성 향상을 위한 계면활성제 0.1 내지 0.4중량부, 몰탈 슬러리의 점도 조절과 보수성 증진을 위한 세룰로스 에틸계의 점증제 0.05 내지 0.20중량부, 발수성의 칼슘 스테아린산계의 고급지방산 금속염0.3 내지 1.0중량부, 길이 2㎜이하인 셀룰로스계 단섬유 0.3 내지 0.7중량부로 이루어진 방수용 몰탈조성물이 공지되어 있다.As to the waterproofing materials and the method of construction which have been developed so far, when 100 weight parts of silica sand adjusted to a particle size in the range of 1.4 to 0.07 mm in Korean Patent Registration No. 0180111 (November 30, 1998) To 100 parts by weight of a water-borne base mortar composition composed of 0.1 to 0.4 parts by weight of a surfactant for reducing the surface tension of water and improving wettability, viscosity control and maintenance of the mortar slurry 0.05 to 0.20 parts by weight of an increasing agent of the cellulose ethylacetate, 0.3 to 1.0 part by weight of a water-soluble calcium stearic acid-based higher fatty acid metal salt and 0.3 to 0.7 part by weight of a cellulose-based short fiber having a length of 2 mm or less are known have.
또한, 한국공개특허 10-2007-0088974(2007년08월30일)에는 시멘트 광물계 결합재 12~30중량%와, 에틸렌 초산 비닐(EVA) 또는 초산비닐/비닐바사테이트(Va/VeoVa) 중 선택된 어느 하나 이상의 시멘트 혼화용 재유화형 분말수지 23~70중량%와, 규사 18~47중량%로 이루어지는 것을 특징으로 하는 도막방수재 조성물이 공지되어 있다.In addition, Korean Patent Laid-Open Publication No. 10-2007-0088974 (Aug. 30, 2007) discloses that 12 to 30% by weight of a cement mineral binder and one selected from ethylene vinyl acetate (EVA) or vinyl acetate / vinyl versatate (Va / VeoVa) A waterproofing material composition comprising 23 to 70% by weight of at least one re-oiling type resin powder for cement admixture and 18 to 47% by weight of silica sand.
또한, 한국등록특허 10-1254139(2013년04월08일)에는 10~50중량부를 갖는 마그네시아, 10~40중량부를 갖는 인산염, 5~40중량부를 갖는 플라이애시, 20~50중량부를 갖는 충전재, 0.5~10중량부를 갖는 지연제, 0.1~10중량부를 갖는 첨가제가 혼합된 마그네시아인산염계 복합체로 이루어져 콘크리트구조물의 표면에 도포되는 바탕조정재층(20); 및 40~60중량부를 갖는 무기계졸과, 20~40중량부를 갖는 에폭시수지와, 10~30중량부를 갖는 용매로 이루어지는 무기계졸-에폭시 혼합물과, 20~30 중량부를 갖는 변성지환족아민과, 10~20 중량부를 갖는 용매와, 10~20중량부를 갖는 탄산칼슘과, 10~20중량부를 갖는 산화티탄과, 10~30중량부를 갖는 유색안료와, 2~4중량부를 갖는 첨가제로 이루어지는 경화제를 혼합시킨 유무기 하이브리드 코팅제층(30);으로 이루어지되, 상기 유무기 하이브리드 코팅제층(30)은 무기계졸-에폭시 혼합물과와 경화제가 11 : 7의 중량비로 혼합되는 것을 특징으로 하는 콘크리트 구조물용 방수/방식제가 공지되어 있다.In addition, Korean Patent No. 10-1254139 (Apr. 08, 2013) discloses a process for producing a ferrite powder comprising 10 to 50 parts by weight of magnesia, 10 to 40 parts by weight of phosphate, 5 to 40 parts by weight of fly ash, 20 to 50 parts by weight of filler, 0.5 to 10 parts by weight of a retarder, and 0.1 to 10 parts by weight of an additive, wherein the additive is applied to the surface of the concrete structure; And 40 to 60 parts by weight of an inorganic sol-epoxy mixture comprising 20 to 40 parts by weight of an epoxy resin and 10 to 30 parts by weight of an inorganic sol-epoxy mixture, 20 to 30 parts by weight of a modified- 20 parts by weight of calcium carbonate having 10 to 20 parts by weight, titanium oxide having 10 to 20 parts by weight, coloring pigment having 10 to 30 parts by weight, and an additive having 2 to 4 parts by weight Wherein the inorganic hybrid coating layer (30) is mixed with an inorganic sol-epoxy mixture and a curing agent at a weight ratio of 11: 7, wherein the organic solvent-hybrid coating layer (30) I am known.
또한, 한국등록특허 10-1652306(2016년08월24일)에는 무기질 분말 도포 방수제에 있어서, 50 내지 60중량부의 포틀랜드 시멘트, 40 내지 50중량부의 인조규사, 25 내지 30중량부의 아크릴레이트 공중합체, 10 내지 15중량부의 실리카흄 및 5 내지 10중량부의 에틸렌/비닐라우레이트/비닐클로라이드 삼원 공중합체로 이루어진 주제부; 40 내지 50 중량부의 규산소다, 40 내지 50 중량부의 규산알루미늄 및 15 내지 35 중량부의 수산화나트륨이 혼합되어 형성되는 공극 생성 방지제; 이소프렌(isoprene ; C5H8 )의 중합체로서, 모노테르펜(C10H16), 세스키(sesqui)테르펜(C15 H24 ), 디테르펜(C20H32) 중 하나 또는 2 이상을 혼합하여 형성된 방충재; 디라우릴 티오디프로피오네이트(dilauryl thiodipropionate)로 형성된 산화방지제; 40 내지 50 중량부의 이소시네이트 프리폴리머(isocynate prepolymer), 20 내지 30 중량부의 크실렌, 5 내지 10 중량부의 메틸 에틸 캐톤(methyl ethyle ketone), 5 내지 10 중량부의 셀로솔브 아세테이트(cellosolve acetate), 1 내지 5 중량부의 트리메톡실란(trimetoxysilane), 1 내지 5 중량부의 광촉매 및 1 내지 5 중량부의 실버 더스트로 이루어진 방식제; 30~50 중량부의 에멀젼과, 40~60 중량부의 충진제와, 0.5~2 중량부의 증점제와, 0.5~1중량부의 증점 보조제와, 0.1~0.3 중량부의 pH 조절제와, 0.1~0.5 중량부의 가교촉진제와, 0.1~0.5 중량부의 가소제로 이루어진 균열방지제; 및 30~50 중량부의 아초산염과, 20~30 중량부의 프로필 셀로솔브와, 10~20 중량부의 칼륨인산염과, 5~10 중량부의 변성 나프탈렌 축합물로 이루어진 동결방지제를 포함하며: 상기 주제부 : 공극 생성 방지제 : 방충제 : 산화방지제 : 방식제 : 균열방지제 : 동결방지제의 혼합비는 100 중량부: 5 ~ 10 중량부: 5 ~ 7 중량부: 2 ~ 4 중량부 : 5 ~ 10 중량부: 4 ~ 8 중량부: 4 ~ 5 중량부인 것을 특징으로 하는 무기질 분말 도포 방수제가 가 공지되어 있다.Korean Patent No. 10-1652306 (Aug. 24, 2016) discloses an inorganic powder coating waterproofing agent comprising 50 to 60 parts by weight of Portland cement, 40 to 50 parts by weight of synthetic silica, 25 to 30 parts by weight of an acrylate copolymer, 10 to 15 parts by weight of silica fume and 5 to 10 parts by weight of an ethylene / vinyl laurate / vinyl chloride terpolymer; 40 to 50 parts by weight of sodium silicate, 40 to 50 parts by weight of aluminum silicate, and 15 to 35 parts by weight of sodium hydroxide; An insecticide formed by mixing one or more of monoterpene (C10H16), sesqui terpene (C15H24), and diterpene (C20H32) as a polymer of isoprene (C5H8); An antioxidant formed of dilauryl thiodipropionate; 40 to 50 parts by weight of an isocynate prepolymer, 20 to 30 parts by weight of xylene, 5 to 10 parts by weight of methyl ethyl ketone, 5 to 10 parts by weight of cellosolve acetate, An anticorrosive consisting of 5 parts by weight of trimethoxysilane, 1 to 5 parts by weight of a photocatalyst and 1 to 5 parts by weight of silver dust; The emulsion of 30 to 50 parts by weight, the filler of 40 to 60 parts by weight, the thickener of 0.5 to 2 parts by weight, the viscosity auxiliary agent of 0.5 to 1 part by weight, the pH adjuster of 0.1 to 0.3 parts by weight, the crosslinking accelerator of 0.1 to 0.5 parts by weight, , 0.1 to 0.5 parts by weight of a plasticizer; And a cryoprotectant consisting of 30 to 50 parts by weight of acetic acid salt, 20 to 30 parts by weight of propylcellosolve, 10 to 20 parts by weight of potassium phosphate and 5 to 10 parts by weight of modified naphthalene condensate, 5 to 10 parts by weight: 5 to 7 parts by weight: 2 to 4 parts by weight: 5 to 10 parts by weight: 4 to 10 parts by weight: Antifoaming agent: Antifouling agent: Antioxidant: Corrosion inhibitor: 8 parts by weight: 4 to 5 parts by weight.
그러나, 상기 방수, 방식제들은, 수분 또는 습기가 존재하거나 외부 또는 열악한 환경에 시공되는 경우, 공극 또는 기포가 발생될 수 있고, 산화가 발생되어 부식이 초래될 수 있으며, 시간이 지남에 따라 균열이 발생될 수 있다는 문제점이 여전히 남아 있다. However, when the waterproofing and antifouling agents are present in the presence of moisture or moisture, or in an external or inadequate environment, pores or bubbles may be generated, oxidation may occur and corrosion may occur, and cracks There is still a problem in that it may occur.
뿐만 아니라, 상기 한국등록특허 10-1652306의 주제와 경화제로 이루어지는 2재형은 현장에서 배합 사용하므로 공사기간이 길어지고, 취급이 용이하지 않으며, 점성 및 유동성을 조절하기가 어려운 문제점이 있었다.In addition, the above-mentioned Korean Patent No. 10-1652306 and the above-mentioned two-component molding comprising a curing agent are used in the field, so that the construction period is long, handling is difficult, and viscosity and fluidity are difficult to control.
이에 본 발명자는 상기와 같은 종래 문제점을 해결하기 위하여, 무기바인더와 유기 바인더를 혼용 사용하여 무기 바인더의 콘크리트와의 접착 일체화를 완성하고 유기바인더의 방수, 방식 기능을 극대화하며, 특히 두께를 2~3mm 시공하여 충분한 장기 내구성을 도모하고, 이음새 없이 한번에 시공을 하여 충분한 방수성을 확보함과 동시에, 수처리 및 저장시에 필요한 방수, 방식 기능성을 발휘하고, 특히, 대부분의 작업현장이 밀폐된 지하공간이고 추후 식용수를 담수하는 곳이기 때문에 시공시 분진이 발생되지 않도록 하며, 시공 후 청소를 최소화하기 위한 분진저감 분말페인트를 개발하여 먹는 물에 대한 안정성 및 염소에 대한 저항성을 유지할 수 있는 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물 및 이를 이용한 콘크리트 방수, 방식 시공방법을 개발하여 본 발명을 완성하게 되었다.In order to solve the above-mentioned problems, the inventor of the present invention has found that, by using an inorganic binder and an organic binder in combination, it is possible to complete the bonding and integration of the inorganic binder with the concrete, maximize the waterproofing and functioning of the organic binder, 3mm is applied to achieve sufficient long-term durability, and it is possible to secure sufficient waterproofness by performing the construction at one time without seams, and to exhibit the waterproofing and functioning necessary for water treatment and storage, and in particular, Because it is the place where the drinking water is desiccated, it does not generate dust at the time of construction and develops dust-reduced powder paint to minimize the cleaning after construction. It is waterproof concrete and can maintain resistance to water and resistance to chlorine. Hybrid Powder Paint Composition and Concrete Waterproofing Using It, Room And the present invention has been completed.
본 발명은 상기 문제점을 해결하기 위하여, 기존 하수관, 하수종말 처리장, 배수지 콘크리트 벽면 구조물과의 접착성과 각 구조물 특성상 방식, 방수 기능이 우수하고, 분말페인트 분진저감 및 시공 후 청소 최소화에 따른 양호한 작업성을 유지하며, 단시간에 보수 및 시공을 용이하게 할 수 있는 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물 및 이를 이용한 콘크리트 방수, 방식 시공방법을 제공하는 것을 해결하고자 하는 과제로 한다.In order to solve the above problems, the present invention has been made to solve the above-mentioned problems, and it is an object of the present invention to provide a water treatment system that is excellent in adhesion to existing sewer pipes, sewerage end treatment plants and drainage concrete wall structures, The present invention is directed to a hybrid water-based paint composition for concrete waterproofing and waterproofing, which can maintain maintenance and construction in a short time, and a concrete waterproofing and waterproofing method using the same.
특히, 본 발명은 무기바인더와 유기 바인더를 혼용 사용하여 무기 바인더의 콘크리트와의 접착 일체화를 완성하고 유기바인더의 방수, 방식 기능을 극대화하며, 특히 두께를 2~3mm 시공하여 충분한 장기 내구성을 도모하고, 이음새 없이 한번에 시공을 하여 충분한 방수성을 확보함과 동시에, 수처리 및 저장시에 필요한 방수, 방식 기능성을 발휘하고, 특히, 대부분의 작업현장이 밀폐된 지하공간이고 추후 식용수를 담수하는 곳이기 때문에 시공시 분진이 발생되지 않도록 하며, 시공 후 청소를 최소화하기 위한 분진저감 분말페인트를 개발하여 먹는 물에 대한 안정성 및 염소에 대한 저항성을 유지할 수 있는 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물 및 이를 이용한 콘크리트 방수, 방식 시공방법을 제공하는 것을 해결하고자 하는 과제로 한다.In particular, the present invention relates to a method for manufacturing an organic binder, which comprises mixing an inorganic binder and an organic binder to complete the bonding and bonding of the inorganic binder with concrete, maximizing the waterproofing and functioning of the organic binder, , It is possible to secure sufficient waterproof property by performing the construction at one time without any seams. At the same time, it exhibits the waterproofing and functioning necessary for water treatment and storage, and especially since most of the work sites are underground space, Water-repellent hybrid type powder paint composition capable of maintaining the stability of water and resistance to chlorine by developing dust-reduced powder paint for minimizing the dust after the construction and minimizing the cleaning after installation Concrete waterproofing, and methods for providing a method We will do it.
본 발명은, 상기 과제를 해결하기 위하여, 백색 알루미나 시멘트(CAC) 20 내지 40중량부, 충전제로서 탄산칼슘 40 내지 60 중량부, EVA 재유화형 분말수지 5 내지 15 중량부, 실리콘 파우더 0.03~0.05중량부, 분진저감 천연섬유 0.1~0.5중량부, 경화촉진제로서 소석회 0.1 내지 1중량부, 증점제 0.1 내지 1중량부를 포함하여 조성되는 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물을 과제의 해결수단으로 한다.The present invention, in order to solve the above problems, is characterized by comprising 20 to 40 parts by weight of white alumina cement (CAC), 40 to 60 parts by weight of calcium carbonate as a filler, 5 to 15 parts by weight of an EVA re- 0.1 to 0.5 parts by weight of dust-reduced natural fiber, 0.1 to 1 part by weight of slaked lime as a curing accelerator, and 0.1 to 1 part by weight of a thickener are used as means for solving the problems of the present invention. .
상기 충전제로서 탄산칼슘의 입자크기는 200mesh 이하인 것을 과제의 해결수단으로 한다.And the particle size of the calcium carbonate as the filler is 200mesh or less.
상기 실리콘 파우더는 미분말 탄산칼슘에 저분자 실리콘을 미세하게 분사시켜 탄산칼슘 미립자에 실리콘이 코팅된 것을 과제의 해결수단으로 한다.The silicone powder is a means for solving the problem that silicon fine particles of calcium carbonate are finely sprayed on fine calcium carbonate to be coated with silicon.
상기 분진저감 천연섬유는 천연섬유를 Mineral Oil에 분산한 후, 건조시켜 천연섬유에 Mineral Oil이 코팅된 것을 과제의 해결수단으로 한다.The dust-reduced natural fiber is a solution to the problem that natural fibers are dispersed in mineral oil and then dried to coat natural fibers with mineral oil.
상기 증점제는 Methyl ethyl hydroxyethyl cellulose(MEHEC) 증점제 또는 폴리사카라이드 증점제로부터 선택된 1종 또는 2종 혼합한 것을 과제의 해결수단으로 한다.Wherein the thickener is one or two selected from a methyl ethyl hydroxyethyl cellulose (MEHEC) thickener or a polysaccharide thickener.
또한, 본 발명은, 콘크리트 표면을 고압세척기를 사용하여 이물질을 제거, 세척하여 하지면을 정리하는 단계와; 상기 정리된 하지면에 프라이머를 도포하는 단계와; 상기 프라이머 도포면에 상기 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물을 도포하는 단계와; 상기 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물을 양생하는 단계;를 포함하여 구성되는 콘크리트 방수, 방식 시공방법을 과제의 해결수단으로 한다.The present invention also relates to a method of manufacturing a concrete structure, comprising the steps of: removing a surface of a concrete using a high-pressure washer; Applying a primer to the cleaned surface; Applying the concrete waterproof, anticorrosive, organic powder paint composition to the primer application surface; And curing the hybrid inorganic powder paint composition for concrete waterproofing and curing. The present invention also provides a concrete waterproofing and curing method for concrete.
상기 프라이머는 아크릴 개질 에멀젼 수지로서 스티렌-아크릴 수지 에멀젼을 사용하며, 에멀젼 분산 입자크기가 1~50㎛인 것을 과제의 해결수단으로 한다.The primer used is a styrene-acrylic resin emulsion as the acrylic modified emulsion resin, and the emulsion dispersed particle size is 1 to 50 μm.
상기 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물을 도포하는 단계에서는 백색 알루미나 시멘트(CAC), 탄산칼슘, EVA 재유화형 분말수지, 실리콘 파우더, 분진저감 천연섬유, 증점제를 포함하는 분말조성물 투입구와; 경화촉진제로서 소석회 투입구와; 상기 분말조성물 투입구와 소석회 투입구로부터 투입된 분말조성물과 소석회가 균일 혼합되는 혼합부와; 상기 혼합부에서 혼합된 유무기 하이브리드 분말페인트 조성물을 분사하는 토출노즐;로 구성되는 에어리스 노즐을 사용하여 도포하는 것을 과제의 해결수단으로 한다.Wherein the step of applying the concrete waterproofing / antifouling hybrid inorganic powder paint composition comprises: a powder composition inlet including white alumina cement (CAC), calcium carbonate, EVA rewarming powder resin, silicone powder, dust reduction natural fiber and thickener; A hydrated lime inlet as a hardening accelerator; A mixing portion in which the powder composition introduced from the powder composition inlet and the slurry inlet are uniformly mixed with slaked lime; And an ejection nozzle for spraying the mixed organic / inorganic hybrid powdery paint composition in the mixing portion.
본 발명의 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물 및 이를 이용한 콘크리트 방수, 방식 시공방법은, 기존 하수관, 하수종말 처리장, 배수지 콘크리트 벽면 구조물과의 접착성과 각 구조물 특성상 방식, 방수 기능이 우수하고, 분말페인트 분진저감 및 시공 후 청소 최소화에 따른 양호한 작업성을 유지하며, 단시간에 보수 및 시공을 용이하게 할 수 있는 우수한 효과가 있다.The concrete waterproofing and antifouling hybrid type powder paint composition of the present invention and the concrete waterproofing and method construction method using the same have excellent adhesion to existing sewage pipe, sewage end treatment plant and drainage concrete wall structure, , Powder paint dust reduction and good workability due to minimized cleaning after construction are maintained, and it is possible to facilitate maintenance and construction in a short time.
특히, 본 발명의 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물 및 이를 이용한 콘크리트 방수, 방식 시공방법은, 무기바인더와 유기 바인더를 혼용 사용하여 무기 바인더의 콘크리트와의 접착 일체화를 완성하고 유기바인더의 방수, 방식 기능을 극대화하며, 두께를 2~3mm 시공하여 충분한 장기 내구성을 도모하고, 이음새 없이 한번에 시공을 하여 충분한 방수성을 확보함과 동시에, 수처리 및 저장시에 필요한 방수, 방식 기능성을 발휘하고, 특히, 대부분의 작업현장이 밀폐된 지하공간이고 추후 식용수를 담수하는 곳이기 때문에 시공시 분진이 발생되지 않도록 하며, 시공 후 청소를 최소화하기 위한 분진저감 분말페인트를 개발하여 식수에 대한 안정성 및 염소에 대한 저항성을 유지할 수 있는 우수한 효과가 있다.Particularly, the concrete waterproofing method, the method of the present invention, and the method of waterproofing concrete and waterproofing method using the same, can be accomplished by mixing the inorganic binder with the concrete by using the inorganic binder and the organic binder together, Waterproof, and maximizing the function of the system, and 2 ~ 3mm in thickness to achieve sufficient long-term durability, and to ensure sufficient waterproofness by performing the construction at one time without any seams. At the same time, Since most work sites are closed underground space and water is desalinated in the future, dust is not generated at the time of construction and dust-reducing powder paint is developed to minimize the cleaning after installation. There is an excellent effect of maintaining the resistance to heat.
도 1은 본 발명의 분말페인트 조성물을 이용하여 방수, 방식 시공한 사진
도 2는 본 발명에서 사용되는 에어리스 노즐 개념도FIG. 1 is a photograph showing a waterproof and a method construction using the powder paint composition of the present invention
2 is a schematic view of an airless nozzle used in the present invention.
본 발명은, 백색 알루미나 시멘트(CAC) 20 내지 40중량부, 충전제로서 탄산칼슘 40 내지 60 중량부, EVA 재유화형 분말수지 5 내지 15 중량부, 실리콘 파우더 0.03~0.05중량부, 분진저감 천연섬유 0.1~0.5중량부, 경화촉진제로서 소석회 0.1 내지 1중량부, 증점제 0.1 내지 1중량부를 포함하여 조성되는 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물을 기술구성의 특징으로 한다.The present invention relates to a resin composition comprising 20 to 40 parts by weight of white alumina cement (CAC), 40 to 60 parts by weight of calcium carbonate as a filler, 5 to 15 parts by weight of an EVA re-oil type powder resin, 0.03 to 0.05 parts by weight of silicone powder, 0.1 to 1 part by weight of slaked lime as a curing accelerator, and 0.1 to 1 part by weight of a thickening agent, based on the total weight of the composition.
상기 충전제로서 탄산칼슘의 입자크기는 200mesh 이하인 것을 기술구성의 특징으로 한다.And the particle size of the calcium carbonate as the filler is 200mesh or less.
상기 실리콘 파우더는 미분말 탄산칼슘에 저분자 실리콘을 미세하게 분사시켜 탄산칼슘 미립자에 실리콘이 코팅된 것을 기술구성의 특징으로 한다.The silicone powder is characterized in that silicon fine particles of calcium carbonate are finely sprayed on fine calcium carbonate to coat silicon fine particles.
상기 분진저감 천연섬유는 천연섬유를 Mineral Oil에 분산한 후, 건조시켜 천연섬유에 Mineral Oil이 코팅된 것을 기술구성의 특징으로 한다.The dust-reducing natural fiber is characterized in that the natural fiber is dispersed in mineral oil and then dried to coat the natural fiber with mineral oil.
상기 증점제는 Methyl ethyl hydroxyethyl cellulose(MEHEC) 증점제 또는 폴리사카라이드 증점제로부터 선택된 1종 또는 2종 혼합한 것을 기술구성의 특징으로 한다.Wherein the thickener is one or two selected from a methyl ethyl hydroxyethyl cellulose (MEHEC) thickener or a polysaccharide thickener.
또한, 본 발명은, 콘크리트 표면을 고압세척기를 사용하여 이물질을 제거, 세척하여 하지면을 정리하는 단계와; 상기 정리된 하지면에 프라이머를 도포하는 단계와; 상기 프라이머 도포면에 상기 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물을 도포하는 단계와; 상기 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물을 양생하는 단계;를 포함하여 구성되는 콘크리트 방수, 방식 시공방법을 기술구성의 특징으로 한다.The present invention also relates to a method of manufacturing a concrete structure, comprising the steps of: removing a surface of a concrete using a high-pressure washer; Applying a primer to the cleaned surface; Applying the concrete waterproof, anticorrosive, organic powder paint composition to the primer application surface; And curing the hybrid inorganic powder paint composition for the concrete waterproofing and the corrosion-proofing method.
상기 프라이머는 아크릴 개질 에멀젼 수지로서 스티렌-아크릴 수지 에멀젼을 사용하며, 에멀젼 분산 입자크기가 1~50㎛인 것을 기술구성의 특징으로 한다.The primer used is a styrene-acrylic resin emulsion as the acrylic modified emulsion resin, and the emulsion dispersed particle size is 1 to 50 μm.
상기 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물을 도포하는 단계에서는 백색 알루미나 시멘트(CAC), 탄산칼슘, EVA 재유화형 분말수지, 실리콘 파우더, 분진저감 천연섬유, 증점제를 포함하는 분말조성물 투입구와; 경화촉진제로서 소석회 투입구와; 상기 분말조성물 투입구와 소석회 투입구로부터 투입된 분말조성물과 소석회가 균일 혼합되는 혼합부와; 상기 혼합부에서 혼합된 유무기 하이브리드 분말페인트 조성물을 분사하는 토출노즐;로 구성되는 에어리스 노즐을 사용하여 도포하는 것을 기술구성의 특징으로 한다.Wherein the step of applying the concrete waterproofing / antifouling hybrid inorganic powder paint composition comprises: a powder composition inlet including white alumina cement (CAC), calcium carbonate, EVA rewarming powder resin, silicone powder, dust reduction natural fiber and thickener; A hydrated lime inlet as a hardening accelerator; A mixing portion in which the powder composition introduced from the powder composition inlet and the slurry inlet are uniformly mixed with slaked lime; And an ejection nozzle for spraying the mixed organic / inorganic hybrid powdery paint composition in the mixing part.
이하에서는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 바람직한 실시예 및 도면을 통하여 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며, 여기에서 설명하는 실시예에 한정되지 않는다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. The present invention may, however, be embodied in many different forms and should not be construed as limited to the embodiments set forth herein.
특히, 본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 첨부되는 도면과 함께 상세하게 후술되어 있는 실시예를 참조하면 명확해질 것이다. 그러나 본 발명은 여기서 설명되는 실시예들에 한정되지 않고 다른 형태로 구체화될 수도 있다. 오히려, 여기서 소개되는 실시예들은 개시된 내용이 철저하고 완전해질 수 있도록 그리고 당업자에게 본 발명의 사상이 충분히 전달될 수 있도록 하기 위해 제공되는 것이다.In particular, advantages and features of the present invention and methods of achieving them will be apparent from and elucidated with reference to the embodiments described hereinafter in conjunction with the accompanying drawings. However, the present invention is not limited to the embodiments described herein but may be embodied in other forms. Rather, the embodiments disclosed herein are provided so that the disclosure can be thorough and complete, and will fully convey the scope of the invention to those skilled in the art.
본 출원에서 사용한 용어는 단지 특정한 실시예를 설명하기 위해 사용된 것으로, 본 발명을 한정하려는 의도가 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 출원에서, "포함하다" 또는 "가지다" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.The terminology used in this application is used only to describe a specific embodiment and is not intended to limit the invention. The singular expressions include plural expressions unless the context clearly dictates otherwise. In this application, the terms "comprises", "having", and the like are used to specify that a feature, a number, a step, an operation, an element, a part or a combination thereof is described in the specification, But do not preclude the presence or addition of one or more other features, integers, steps, operations, components, parts, or combinations thereof.
다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미가 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥상 가지는 의미와 일치하는 의미가 있는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.Unless otherwise defined, all terms used herein, including technical or scientific terms, have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. Terms such as those defined in commonly used dictionaries are to be interpreted as having a meaning consistent with the meaning in the context of the relevant art and are to be construed as ideal or overly formal in meaning unless explicitly defined in the present application Do not.
우선, 본 발명의 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물은 백색 알루미나 시멘트(CAC) 20 내지 40중량부, 충전제로서 탄산칼슘 40 내지 60 중량부, EVA 재유화형 분말수지 5 내지 15 중량부, 실리콘 파우더 0.03~0.05중량부, 분진저감 천연섬유 0.1~0.5중량부, 경화촉진제로서 소석회 0.1 내지 1중량부, 증점제 0.1 내지 1중량부를 포함하여 조성된다.First, 20 to 40 parts by weight of white alumina cement (CAC), 40 to 60 parts by weight of calcium carbonate as a filler, 5 to 15 parts by weight of an EVA re-oiled powdery resin, 0.03 to 0.05 parts by weight of silicon powder, 0.1 to 0.5 parts by weight of dust-reduced natural fibers, 0.1 to 1 part by weight of slaked lime as a curing accelerator, and 0.1 to 1 part by weight of a thickener.
상기 백색 알루미나 시멘트는 염소에 강하여 일반 시멘트는 염소에 표면이 하얗게 반응(백화현상)을 하는데 백색 알루미나 시멘트(CAC)를 사용하면 백화 현상이 발생되지 않는다. The white alumina cement is resistant to chlorine, and general cement reacts with chlorine whiteness (whitening phenomenon). When white alumina cement (CAC) is used, whitening does not occur.
상기 백색 알루미나 시멘트(CAC)는 Al2O3가 30 중량% 이상 함유되어 있고, 주된 화합물은 CaO, CaOAl2O3, 5CaO3Al2O3이며 3종의 알루미네이트 중에서 CaOAl2O3(CA)의 강도 특성이 가장 뛰어나기 때문에 일반적으로 CA가 주성분이 되도록 제조하고 있다.The white alumina cement (CAC) contains 30 wt% or more of Al 2 O 3 , and the main compounds are CaO, CaOAl 2 O 3 , and 5CaO 3 Al 2 O 3. Among the three aluminates, CaOAl 2 O 3 (CA ) Is most excellent in strength characteristics, so that CA is generally manufactured as a main component.
상기 칼슘 알루미네이트는 주성분이 알루미나, 생석회, CaO, 무수규산 등의 응용물인 시멘트를 의미하고, CaOAl2O3 및 5CaO3Al2O3이 주요 광물로서 포틀랜드 시멘트에 비해서 알루미나 성분이 상당히 많고, 포틀랜드 시멘트 보다 내식성, 내화성, 급결성이 우수하다. 이로 인해 본 발명의 조성물은 염소에 대한 백화 방지 효과를 나타낸다. The calcium aluminate refers to cement which is mainly applied to alumina, quick lime, CaO, silicic anhydride, etc. CaOAl 2 O 3 and 5CaO 3 Al 2 O 3 are major minerals as compared to Portland cement, It is excellent in corrosion resistance, fire resistance and quickness. As a result, the composition of the present invention exhibits an anti-whitening effect on chlorine.
여기서, 알루미나 시멘트(CAC) 함량이 40 중량부를 넘으면 급결성이 높아 작업성 저하 및 수축크랙이 발생할 수 있고, 20 중량부 이하인 경우 강도가 떨어지고 내화학성능이 저하된다. If the content of alumina cement (CAC) is more than 40 parts by weight, productivity may be lowered and workability may be lowered and shrinkage cracks may occur. When the amount is less than 20 parts by weight, strength and chemical resistance may deteriorate.
상기 탄산칼슘은 입자사이즈가 200mesh 이하 제품을 사용한다. 습기 함량이 0.5 중량% 제품을 사용하며, 탄산칼슘 함량이 60 중량부가 넘으면 상대적인 무기바인더 함량이 줄어 강도 및 표면저항 저하되고, 탄산칼슘 함량이 40중량부 이하인 경우 상대적으로 무기바인더를 사용으로 인한 가격상승 및 충진기능성이 저하된다. The above-mentioned calcium carbonate uses a product having a particle size of 200 mesh or less. When the calcium carbonate content is more than 60 parts by weight, the relative inorganic binder content is decreased and the strength and surface resistance are lowered. When the calcium carbonate content is less than 40 parts by weight, The rise and fill functionality are degraded.
상기 EVA 재유화형 분말수지는 내수성(방수), 내화학성(방식)이 우수한 분말 상태의 유기 폴리머 바인더 수지로서, 라텍스나 에멀젼을 분무하여 건조시킨 입자 표면에 무기질의 응집방지제(anti-cakingpowder)를 코팅하여 입자끼리 서로 뭉치지 않고 장기간 보존할 수 있도록 제조한 것으로 물 또는 알칼리용액 중에서 재유화하여 수성 폴리머 디스퍼젼의 형태로 된다. 상기 EVA 재유화형 분말수지는 액상형태의 폴리머 디스퍼젼에 비해 건조 상태의 시멘트 및 골재를 혼합한 형태로 제품을 제조한 후 물만 첨가하여 사용할 수 있는 프리팩키지 형태의 제품 제조가 용이한 장점이 있다.The EVA re-oil type powder resin is an organic polymer binder resin in powder form which is excellent in water resistance (waterproof) and chemical resistance (method). It is coated with an inorganic anti-caking powder on the surface of a dried particle by spraying latex or emulsion And the particles can be preserved for a long time without being clumped together. Re-emulsification is carried out in water or an alkaline solution to form an aqueous polymer dispersion. The EVA re-oil type powder resin is advantageous in that it is easier to produce a product in the form of a mixture of dry cement and aggregate as compared with a liquid polymer dispersion, and then prepackage-type products which can be used by adding only water.
상기 EVA 재유화형 분말수지 함량이 15 중량부 이상 넣게 되면 제품 가격 상승 및 오히려 도막 형성 시간이 지연될 수 있으며, 5 중량부 이하일 경우 전체적인 방수기능이 현격히 떨어진다. If the amount of the EVA re-oiled powder resin is more than 15 parts by weight, the product price may rise and the film formation time may be delayed. If the amount is less than 5 parts by weight, the waterproof function is greatly reduced.
이때, 상기 EVA 재유화형 분말수지는 일반적인 분말페인트에 사용하여 내수성 및 접착력, 내마모성능을 증진시키지만, 발수성 및 염소 저항성이 떨어지는 단점이 있다. 이를 개선 하기 위해 실리콘 파우더를 사용하는데. 실리콘 파우더는 잘못 사용하면 부착강도 저하가 발생할 수 있기 때문에 주의하여야 한다.At this time, the EVA re-oil type powder resin is used in ordinary powder paint to improve the water resistance, adhesion and abrasion resistance, but it is disadvantageous in that water repellency and chlorine resistance are poor. I use silicone powder to improve this. Caution should be exercised when the silicone powder is used incorrectly because it may cause a decrease in the adhesion strength.
이에 따라, 본 발명에서 사용하는 실리콘 파우더는 약0.0025mm의 미분말 탄산칼슘에 저분자 실리콘을 약150℃에서 미세하게 분사시켜 탄산칼슘 미립자에 실리콘이 코팅된 것을 사용하므로 내수성 및 염소에 대한 몰탈 중성화 방지 역할을 할 수 있으며, 또한 콘크리트 모체와 접착력을 향상시키는데 도움을 주도록 한다.Accordingly, since the silicone powder used in the present invention is obtained by finely spraying low-molecular-weight silicon at about 150 ° C into fine calcium carbonate having a particle size of about 0.0025 mm, silicon fine particles coated with silicon are used to prevent water resistance and mortar neutralization against chlorine And also helps to improve adhesion to the concrete matrix.
한편, 분말페인트의 분진저감을 최소화하도록 본 발명에서는 분진저감 천연섬유를 사용한다.On the other hand, in order to minimize dust reduction of the powder paint, dust-reduced natural fibers are used in the present invention.
상기 분진저감 천연섬유는 0.1~0.5mm 천연섬유를 Mineral Oil에 분산한 후, 건조시켜 천연섬유에 Mineral Oil이 코팅된 것을 사용하며, 이때, Mineral Oil이 코팅된 천연섬유는 분진을 잡아주고 섬유보강역할로 전체적인 인장력을 확보할 수 있어 하지 크랙에 대한 저항성도 동시에 얻을 수 있다The dust-reduced natural fiber is made by dispersing 0.1 to 0.5 mm of natural fiber in mineral oil and then drying and coating the natural fiber with mineral oil. In this case, the natural fiber coated with mineral oil absorbs dust, As a result, the overall tensile force can be secured and the resistance against the under crack can be obtained at the same time
즉, 상기 분진저감용 천연 섬유는 분진 발생시 분진이 천연섬유에 코팅된 오일에 붙어 분진의 무게를 순간 높여줘서 공기중에 확산되는 것을 최소화하고 다시 가라앉히는 역할을 하므로 밀폐된 작업장에서의 분진저감을 최소하여 작업자의 안전 및 분진으로 인한 폭발 사전예방 및 시공 후 청소를 용이하게 하는 효과가 있으며, 섬유로 인한 분말페인트 인장력 향상으로 내크랙성을 향상시키는 효과도 있다. That is, the dust-reducing natural fibers increase the weight of the dust by attaching to the oil coated on the natural fiber at the time of dust generation to minimize the diffusion into the air and to sink the dust again so that the dust reduction in the closed workplace is minimized And it has an effect of facilitating cleaning after installation and prevention of explosion due to safety and dust of an operator, and also has an effect of improving crack resistance by improving tensile strength of powder paint due to fiber.
상기 증점제는 Methyl ethyl hydroxyethyl cellulose(MEHEC) 증점제 또는 폴리사카라이드 증점제로부터 선택된 1종 또는 2종 혼합한 것을 사용한다.The thickener may be one selected from the group consisting of methyl ethyl hydroxyethyl cellulose (MEHEC) thickener and polysaccharide thickener.
..
상기 MEHEC 증점제의 경우 셀룰로오즈 유도체(MEHEC) 등과 같은 수용성 폴리머가 증점제로 사용되는 것으로서, 셀룰로오스(cellulose) 분자는 무수 글루코오즈 단량체 사슬로 이루어져 있고, 단량체의 숫자는 점도에 매우 중요한 역할을 하게 된다. 상기 폴리사카라이드 증점제는 식물(감자, 옥수수, 타피오카 등)에서 추출하며, 증점효과나 처짐방지, 재료분리방지 등의 기능적 물성을 부여할 수 있다.In the MEHEC thickener, a water-soluble polymer such as a cellulose derivative (MEHEC) or the like is used as a thickening agent. The cellulose molecule is composed of anhydrous glucose monomer chain, and the number of monomers plays a very important role in viscosity. The polysaccharide thickener is extracted from plants (potato, corn, tapioca, etc.) and can impart functional properties such as thickening effect, prevention of sagging and prevention of separation of materials.
특히, 상기 증점제는 작업능률을 향상시킬 수 있는 기능성이 있는 만큼 점도는 400cps 제품을 사용한다. 상기 증점제 함량이 1 중량부 이상 넣게 되면 물이 많이 들어가게 되어 경화 시간지연이 발생하며, 0.1 중량부로 이하로 들어가면 보수율과 작업성 저하가 발생된다. Particularly, the viscosity of the thickener is 400 cps because it has a function to improve the working efficiency. If the content of the thickener is more than 1 part by weight, a large amount of water will be introduced and a curing time delay will occur. If the content is less than 0.1 part by weight, the water treatment rate and workability will be lowered.
또한, 본 발명에는 경화의 속도를 빠르게 하기 위해 경화 촉진제로 소석회를 넣는데 소석회는 pH를 높여줘 알루미나 시멘트의 경화속도를 높이는 역할을 한다. 소석회 함량이 1 중량부 이상이면 경화 속도가 높아 기계 시공이 어려움 있고, 0.1 중량부 이하인 경우 시공후 경화가 늦어서 후속공정 진행이 어려워 진다. In addition, in the present invention, in order to accelerate the curing speed, slaked lime is added as a hardening accelerator, and the slaked lime serves to increase the pH and increase the hardening speed of the alumina cement. If the amount of the slaked lime is more than 1 part by weight, the hardening speed is high, which makes the mechanical construction difficult. If the amount is less than 0.1 part by weight, the subsequent hardening becomes difficult because the hardening is delayed.
한편, 본 발명의 콘크리트 방수, 방식 시공방법은 콘크리트 표면을 고압세척기를 사용하여 이물질을 제거, 세척하여 하지면을 정리하는 단계와; 상기 정리된 하지면에 프라이머를 도포하는 단계와; 상기 프라이머 도포면에 상기 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물을 도포하는 단계와; 상기 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물을 양생하는 단계;를 포함하여 구성된다.The concrete waterproofing method of the present invention includes the steps of cleaning the surface of the concrete using a high-pressure washer to remove foreign substances and cleaning the surface of the concrete; Applying a primer to the cleaned surface; Applying the concrete waterproof, anticorrosive, organic powder paint composition to the primer application surface; And curing the concrete waterproofing and curing organic / inorganic hybrid powder paint composition.
이때, 상기 프라이머는 아크릴 개질 에멀젼 수지로서 스티렌-아크릴 수지 에멀젼을 사용하며, 에멀젼 분산 입자크기가 1~50㎛인 것을 사용하는데, 이는 콘크리트와 분말페인트간의 중계접착력을 향상시키는 역할을 하며. 특히 입자사이즈 1~50㎛로 콘크리트와의 침투를 극대화하는 것이 바람직하다.At this time, the primer used is a styrene-acrylic resin emulsion as an acrylic modified emulsion resin, and emulsion dispersed particles having a particle size of 1 to 50 μm are used, which improves the adhesion between the concrete and the powder paint. Particularly, it is desirable to maximize the penetration of concrete with a particle size of 1 to 50 μm.
상기 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물을 이용하여 콘크리트 방수, 방식 시공을 하게 되면, [도 1]에 도시한 바와 같이, 깨끗하고 내구성이 있는 콘크리트 방수, 방식 시공을 할 수 있다.As shown in FIG. 1, when the concrete waterproofing method and the corrosion-proofing method using the organic / inorganic hybrid powder paint composition are used, the concrete waterproofing and the method construction can be clean and durable as shown in FIG.
또한, 상기 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물을 도포하는 단계에서는 [도 2]에 도시한 바와 같이, 백색 알루미나 시멘트(CAC), 탄산칼슘, EVA 재유화형 분말수지, 실리콘 파우더, 분진저감 천연섬유, 증점제를 포함하는 분말조성물 투입구와; 경화촉진제로서 소석회 투입구와; 상기 분말조성물 투입구와 소석회 투입구로부터 투입된 분말조성물과 소석회가 균일 혼합되는 혼합부와; 사익 혼합부에서 혼합된 유무기 하이브리드 분말페인트 조성물을 분사하는 토출노즐;로 구성되는 에어리스 노즐을 사용하여 도포하는 것이 바람직하다.In addition, as shown in Fig. 2, in the step of applying the hybrid water-based paint composition for concrete waterproofing and waterproofing, the white alumina cement (CAC), calcium carbonate, EVA re-powdered powder resin, silicone powder, A powder composition inlet including a natural fiber and a thickener; A hydrated lime inlet as a hardening accelerator; A mixing portion in which the powder composition introduced from the powder composition inlet and the slurry inlet are uniformly mixed with slaked lime; And an ejection nozzle for spraying the mixed organic / inorganic hybrid powdery paint composition in a sand blending part.
[유무기 [Existing machine 하이브리드hybrid 분말페인트 조성물 제조 및 물성측정] Powder paint composition preparation and physical property measurement]
이하 원료를 기재된 양만큼 초퍼가 있는 패들 혼합기에 넣고 5분간 1000rpm으로 혼합해서 분말 페인트를 제조하였다. The raw materials were put into a paddle mixer having the chopper by the amount described and mixed at 1000 rpm for 5 minutes to prepare a powder paint.
상기와 같은 실시예 1로 제조된 분말페인트의 부착강도 및 염소에 대한 저항성을 측정하였다. 내수성은 50*50*50mm 큐빅몰드 제작하여 6면중 수분이 닿는 바닥을 제외하고 5면을 모두 에폭시로 도포를 하여 수분이 들어가지 않게 하고 순수하게 바닥면에서 흡수하는 량을 측정하였다. 최초 규빅몰드 무게는 약 275g이었다. 그 결과를 이하 표에 나타낸다.The adhesion strength and chlorine resistance of the powder paint prepared in Example 1 were measured. The water resistance was 50 * 50 * 50mm cubic mold, and all sides were coated with epoxy except for the floor where the moisture was in contact with the 6 sides, so that moisture was not introduced and the amount absorbed on the floor was measured purely. The initial cubic mold weight was about 275 g. The results are shown in the following table.
염소 침지후 질량감소가 6g으로 실제 1.2% 감소한 것을 일반 몰탈 10% 감소보다 3배 이상 물성이 우수함을 알 수 있다. It can be seen that the mass reduction after chlorine immersion is 6g, which is 1.2% lower than that of general mortar by 3%.
[유무기 [Existing machine 하이브리드hybrid 분말페인트 조성물 제조 및 물성측정] Powder paint composition preparation and physical property measurement]
실시예 1과 유사한 방법으로 이하 원료를 나타낸 양만큼 사용하여 분말페인트를 제조하였는데, 실시예 2에서는 실시예 1과 달리 방수,방식 EVA수지를 소량 첨가하고 몰탈을 제조하였다.In the same manner as in Example 1, powder coatings were prepared by using the amounts shown in the following amounts. In Example 2, mortar was prepared by adding a small amount of waterproof and system EVA resin, unlike Example 1.
실시예 2에서 제조된 분말페인트를 이용하여 시편을 제조하고, 실시예 1과 유사한 방법으로 물성을 측정하였다.Specimens were prepared using the powder paint prepared in Example 2, and physical properties were measured in the same manner as in Example 1. [
실시예 2를 보면 EVA 수지량을 줄이면 부착강도 및 염소 침지 후 질량감소, 내수성이 떨어짐을 알 수 있다. From Example 2, it can be seen that decreasing the amount of EVA resin leads to decrease in adhesion strength, decrease in mass after chlorine immersion, and in water resistance.
[유무기 [Existing machine 하이브리드hybrid 분말페인트 조성물 물성측정] Powder Paint Composition Property Measurement]
상기 실시예 1과 유사한 방법으로 몰탈을 제조하였다. 상기 실시예 1에서 아크릴 프라이머 입자 사이즈에 따른 부착강도를 비교하여 기능성의 차이점을 측정하였다. A mortar was prepared in the same manner as in Example 1 above. The difference in functionality was measured by comparing the adhesion strength according to the acrylic primer particle size in Example 1 above.
실시예 3에서 제조된 몰탈을 이용하여 시편을 제조하고, 실시예 1과 같이 부착강도 물성을 측정하였다.Specimens were prepared using the mortar prepared in Example 3, and the physical properties of the bond strength were measured as in Example 1.
아크릴 프라이머 입자 사이즈가 작을수록 콘크리트 모체에 침투성이 높아 부착강도가 상대적으로 높게 나왔다. The smaller the acrylic primer particle size, the higher the bond strength to the concrete matrix and the higher the bond strength.
[유무기 [Existing machine 하이브리드hybrid 분말페인트 조성물 물성측정] Powder Paint Composition Property Measurement]
상기와 같은 실시예 1과 현장에서 온도가 낮을 경우 노즐에 촉진액을 흘러 들어가게 한 후 경화 시간을 측정하였다. 촉진액은 물에 소석회를 중량대비 10% 첨가하여 pH를 9로 맞춘 용액이다. The curing time was measured after flowing the promoter into the nozzle when the temperature was low in Example 1 and the site as described above. The accelerating solution is a solution prepared by adding 10% by weight of calcium hydroxide to water and adjusting the pH to 9.
* 온도 습도 80%, 10℃ * Temperature Humidity 80%, 10 ℃
실시예 1에서 현장 특수 노즐을 통해 분사된 분말 페인트 경화 속도가 향상됨을 알 수 있다.In Example 1, it can be seen that the powder paint curing rate injected through the spot special nozzles is improved.
이상의 설명은 본 발명의 기술사상을 예시적으로 설명한 것에 불과한 것으로서, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 수정 및 변형이 가능할 것이다. 따라서, 본 발명에 개시된 실시예 및 도면들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시예 및 도면들에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.The foregoing description is merely illustrative of the technical idea of the present invention, and various changes and modifications may be made by those skilled in the art without departing from the essential characteristics of the present invention. Therefore, the embodiments and the drawings disclosed in the present invention are intended to illustrate rather than limit the scope of the present invention, and the scope of the present invention is not limited by these embodiments and drawings. The scope of protection of the present invention should be construed according to the following claims, and all technical ideas within the scope of equivalents should be construed as falling within the scope of the present invention.
Claims (8)
20 to 40 parts by weight of white alumina cement (CAC), 40 to 60 parts by weight of calcium carbonate as a filler, 5 to 15 parts by weight of an EVA re-oiling type powder resin, 0.03 to 0.05 part by weight of silicone powder, 0.1 to 0.5 parts by weight of dust- 0.1 to 1 part by weight of slaked lime as a curing accelerator, and 0.1 to 1 part by weight of a thickener as a curing accelerator.
상기 충전제로서 탄산칼슘의 입자크기는 200mesh 이하인 것을 특징으로 하는 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물
The method according to claim 1,
Wherein the particle size of the calcium carbonate as the filler is 200mesh or less.
상기 실리콘 파우더는 미분말 탄산칼슘에 저분자 실리콘을 미세하게 분사시켜 탄산칼슘 미립자에 실리콘이 코팅된 것을 특징으로 하는 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물
The method according to claim 1,
Wherein the silicone powder is finely sprayed with fine-particle silicon on fine calcium carbonate to coat the fine particles of calcium carbonate with silicone. The present invention relates to a hybrid water-
상기 분진저감 천연섬유는 천연섬유를 Mineral Oil에 분산한 후, 건조시켜 천연섬유에 Mineral Oil이 코팅된 것을 특징으로 하는 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물
The method according to claim 1,
The dust-reduced natural fiber is a concrete waterproof, airtight hybrid type powder paint composition for concrete, characterized in that natural fibers are dispersed in mineral oil and then dried to be coated with mineral oil
상기 증점제는 Methyl ethyl hydroxyethyl cellulose(MEHEC) 증점제 또는 폴리사카라이드 증점제로부터 선택된 1종 또는 2종 혼합한 것을 특징으로 하는 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물
The method according to claim 1,
Wherein the thickener is one or a mixture of two or more selected from methyl ethyl hydroxyethyl cellulose (MEHEC) thickener or polysaccharide thickener.
Cleaning the surface of the concrete using a high-pressure washer to clean and clean the surface; Applying a primer to the cleaned surface; Applying a concrete waterproofing and curing type organic solvent paint composition according to any one of claims 1 to 5 to the primer application surface; And curing the organic / inorganic hybrid powder paint composition for concrete waterproofing and curing.
상기 프라이머는 아크릴 개질 에멀젼 수지로서 스티렌-아크릴 수지 에멀젼을 사용하며, 에멀젼 분산 입자크기가 1~50㎛인 것을 특징으로 하는 콘크리트 방수, 방식 시공방법
The method according to claim 6,
Wherein the primer is a styrene-acrylic resin emulsion as the acrylic modified emulsion resin, and the emulsion dispersed particle size is 1 to 50 탆.
상기 콘크리트 방수, 방식용 유무기 하이브리드 분말페인트 조성물을 도포하는 단계에서는 백색 알루미나 시멘트(CAC), 탄산칼슘, EVA 재유화형 분말수지, 실리콘 파우더, 분진저감 천연섬유, 증점제를 포함하는 분말조성물 투입구와; 경화촉진제로서 소석회 투입구와; 상기 분말조성물 투입구와 소석회 투입구로부터 투입된 분말조성물과 소석회가 균일 혼합되는 혼합부와; 상기 혼합부에서 혼합된 유무기 하이브리드 분말페인트 조성물을 분사하는 토출노즐;로 구성되는 에어리스 노즐을 사용하여 도포하는 것을 특징으로 하는 콘크리트 방수, 방식 시공방법The method according to claim 6,
Wherein the step of applying the concrete waterproofing / antifouling hybrid inorganic powder paint composition comprises: a powder composition inlet including white alumina cement (CAC), calcium carbonate, EVA rewarming powder resin, silicone powder, dust reduction natural fiber and thickener; A hydrated lime inlet as a hardening accelerator; A mixing portion in which the powder composition introduced from the powder composition inlet and the slurry inlet are uniformly mixed with slaked lime; And a discharge nozzle for spraying the organic / inorganic hybrid powder paint composition mixed in the mixing part. [7] The waterproofing method according to claim 1,