KR101428995B1 - Surface Protector with Network Structure and Repairing Polymer Mortar Composite with Light Weight Aggregate for Concrete Structure Repairing System - Google Patents

Surface Protector with Network Structure and Repairing Polymer Mortar Composite with Light Weight Aggregate for Concrete Structure Repairing System Download PDF

Info

Publication number
KR101428995B1
KR101428995B1 KR1020140026564A KR20140026564A KR101428995B1 KR 101428995 B1 KR101428995 B1 KR 101428995B1 KR 1020140026564 A KR1020140026564 A KR 1020140026564A KR 20140026564 A KR20140026564 A KR 20140026564A KR 101428995 B1 KR101428995 B1 KR 101428995B1
Authority
KR
South Korea
Prior art keywords
weight
concrete
repairing
liquid phase
mortar
Prior art date
Application number
KR1020140026564A
Other languages
Korean (ko)
Inventor
나공열
Original Assignee
나공열
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 나공열 filed Critical 나공열
Priority to KR1020140026564A priority Critical patent/KR101428995B1/en
Application granted granted Critical
Publication of KR101428995B1 publication Critical patent/KR101428995B1/en

Abstract

The present invention relates to a repairing mixture for a concrete structure and to a method for building the same. According to the present invention, a concrete surface is cleaned, a primer application is performed, and then concrete restoring or repairing polymer mortar is applied thereunto. An alumina ceramic binder that is used in the polymer mortar is a ceramic binder having excellent chemical resistance, excellent corrosion resistance in particular, unlike portland cement. A polymer powder resin that is used in the polymer mortar mainly contains EVA and an acrylic powder resin, improves adhesiveness and waterproofness by being used with the ceramic binder, and shows excellent physical properties particularly in terms of wear resistance. According to the present invention, an anti-neutralization coating agent is applied so as to maintain a restored or repaired surface for a long period of time. An ultrafine silicone-acrylic polymer primer is used in the anti-neutralization coating agent so that adhesiveness is increased between the coating agent and the repairing mortar. According to the present invention, dropping and birdcaging after the restoration and repair of the concrete cross-section are reduced so that a significant improvement is made against future flaws. Also, the restored or repaired surface is protected by the neutralization water-repellent coating agent so that the appearance can be improved and weatherproofness can be maximized.

Description

망상구조를 가지는 중성화 방지제와 재생경량골재를 사용한 친환경 보수용 폴리머 몰탈 조성물 및 그 콘크리트 구조물 보수 시공공법{Surface Protector with Network Structure and Repairing Polymer Mortar Composite with Light Weight Aggregate for Concrete Structure Repairing System}TECHNICAL FIELD [0001] The present invention relates to a polymer mortar composition for environmentally friendly maintenance using an antifouling agent having a network structure and a regenerated lightweight aggregate, and a method for repairing and constructing a concrete structure of the same,

본 발명은 콘크리트 구조물의 보수용 조성물 및 그 시공방법에 관한 것으로서, 더욱 상세하게는 종래에 시공되어 있던 것으로서, 중성화로 인하여 열화된 콘크리트 구조물을 치핑하고 세척한 후, 그 위에 콘크리트 표면층을 중성화처리하거나 그 내부에 몰탈을 충진시키고 그 표면을 중성화처리하는 콘크리트 구조물의 보수용 조성물 및 그 시공방법에 관한 것이다.
More particularly, the present invention relates to a composition for repairing a concrete structure, and more particularly, to a concrete composition for repairing a concrete structure, and more particularly, to a concrete composition for repairing a concrete structure, The present invention relates to a repair composition for a concrete structure in which a mortar is filled therein and a surface of the mortar is neutralized, and a method for its construction.

우리나라의 산업화 과정에서 철근 콘크리트 제품의 사용은 토목 및 건축 분야에서 매우 큰 기여를 해왔었다. 1970년대를 기점으로 하여, 도로, 교량, 국가 항만 시설 등 콘크리트를 사용하는 토목 사업이 폭발적으로 늘어났고, 산업 기반을 공고히 해주는데 큰 역할을 담당하였다. The use of reinforced concrete products in the industrialization process of Korea has made a great contribution in civil engineering and construction. Starting from the 1970s, civil engineering projects using concrete such as roads, bridges, and port facilities increased explosively and played a major role in consolidating the industrial base.

그러나, 오늘날 토목 및 건축분야에서 각종 철근 콘크리트 구조물은 시간이 지남에 따라 외부적인 환경 요인의 복합적인 영향을 받게 되었고, 그로 인한 부식 내지 중성화, 열화현상 등은 피할 수 없는 상황을 맞이하게 되었다. 이러한 콘크리트 구조물의 중성화 내지 열화현상으로 인하여, 콘크리트 구조물 자체의 내구성이 저하되고 안정성이 떨어져서, 콘크리트 단면의 복수 내지 보수를 위한 공법이 절실히 요구되고 있다. However, in today 's civil engineering and construction field, various reinforced concrete structures have been affected by a combination of external environmental factors over time, and corrosion, neutralization and deterioration phenomena are inevitable. Due to the neutralization or deterioration of the concrete structure, the durability of the concrete structure itself deteriorates and the stability thereof deteriorates, and a method for repairing a plurality of sections of the concrete is urgently required.

현재, 이러한 콘크리트 구조물들을 보수하는데 많은 비용과 시간이 들어가고 있는 실정이다. 실질적으로 종래의 노후화된 콘크리트 구조물을 완전히 철거하고 이를 대체하는 신규 구조물을 만들기 보다는, 기존 콘크리트 구조물을 더 오래 유지하는 방향으로 가는 것이 여러가지 측면에서 유리하기 때문에 보강, 보수 공법이 일반화되고 있으며, 이에 대한 시공방법이나 장비 또는 보수재에 대한 기술개발이 활발하게 이루어지고 있으며, 이에 관련된 특허들이 많이 나오게 되는 계기가 되었다. At present, it takes a lot of time and cost to repair these concrete structures. Reinforcing and repairing methods are generally used because it is advantageous in various aspects to keep the existing concrete structure longer rather than to completely remove the old aged concrete structure and replace it with a new structure to replace it. The development of technology for construction methods, equipment, and repair materials has been actively carried out, and many patents related thereto have become the occasion.

종래 기술을 간략하게 정리하면, 대한민국 특허공보 제10-1185086호 "철근 콘크리트 구조물의 단면 보수 및 복구용 친환경 모르타르 조성물, 이의 제조 방법 및 시공 방법"을 예시할 수 있다. 상기 대한민국 특허공보 제10-1185086호에는 보수몰탈 조성물에 일반 시멘트를 사용하고 있는데, 이는 내화학성 및 내구성이 매우 떨어지는 것을 알 수 있으며, 특히 보수몰탈의 물성을 극대화하는 폴리머가 미함유되어 부착강도 및 내충격성이 현저히 낮음을 알 수 있다. A brief summary of the prior art is Korean Patent Publication No. 10-1185086 entitled " Environmentally friendly mortar composition for repairing and repairing a section of a reinforced concrete structure, its manufacturing method and construction method ". In the Korean Patent Publication No. 10-1185086, general cement is used as a maintenance mortar composition, which shows that chemical resistance and durability are very poor. In particular, the polymer does not contain the polymer maximizing the physical properties of the repair mortar, The impact resistance is remarkably low.

또한, 중성화 방지제 프라이머는 단순 아크릴 에멀젼에 에폭시 실란을 혼합 사용한 것으로 실제 침투가 잘 들어가는 부분에 대한 의구심을 줄 수 있다. 중성화 방지재는 일반 아크릴 에멀젼을 사용하여 도막 형성 후 선상 구조로 인해 내구성 및 내화학성이 떨어지는 요인이 된다. In addition, the anti-neutralizer primer is a mixture of a simple acrylic emulsion and an epoxy silane. The anti-neutralization agent is a factor that durability and chemical resistance are deteriorated due to the linear structure after formation of a coating film by using a general acrylic emulsion.

또한, 중성화 방지제로 등록된 특허공보 제10-2002-0010835호 "콘크리트의 중성화 및 열화방지 공법"은 에폭시 수지를 사용하여, 하도 작업과 상도 작업을 시공하는 공법인데, 내화학성은 우수하나 콘크리트 또는 보수 시공한 곳 위에 시공을 하게 되면 추후 습기 투과성이 없어서 전체적으로 들고 일어나는 현상이 발생한다. 이는 매우 심각한 상황으로 매년 보수에 막대한 비용을 다시 들여야 하는 문제점이 있다.
Patent Document No. 10-2002-0010835 entitled " Neutralization and deterioration prevention method of concrete ", which is registered as an anti-neutralizing agent, is a method of applying undercoating and topcoating using epoxy resin. If the construction is done on the place where the repair work is done, there is no moisture permeability and the phenomenon occurs as a whole. This is a very serious situation, and there is a problem that it is necessary to reap huge revenues every year.

대한민국 등록특허 제10-2002-0010835호 "콘크리트의 중성화 및 열화방지 공법" (2005. 2. 25.);Korean Patent No. 10-2002-0010835 "Method for Preventing Neutralization and Degradation of Concrete" (Feb. 25, 2005); 대한민국 등록특허 제10-1185086호 "철근 콘크리트 구조물의 단면 보수 및 복구용 친환경 모르타르 조성물, 이의 제조 방법 및 시공 방법" (2012. 9. 17.).Korean Patent No. 10-1185086 entitled "Environmentally friendly mortar composition for repairing and repairing a section of a reinforced concrete structure, its manufacturing method and construction method" (2012. 9. 17.).

본 발명은, 상기 종래기술의 제반 문제점을 해결하기 위한 것으로, 콘크리트 구조물에 대한 복구 내지 보수 작업을 수행한 이후에, 기존의 콘크리트와 새롭게 보수한 보수 몰탈의 사이에 탈락이나 들뜸 현상을 일으키지 않고, 외관상으로도 심미성을 부여할 수 있고 내후성이 뛰어난 콘크리트 구조물의 보수용 조성물 및 그 시공방법을 제공하는데 그 목적이 있다.
It is an object of the present invention to solve the above-mentioned problems of the prior art, and to provide a method for repairing and repairing a concrete structure, in which after repairing or repairing a concrete structure, The present invention provides a composition for repairing a concrete structure having excellent appearance and weatherability and a method of constructing the same.

본 발명은, 상기 목적을 달성하기 위하여, The present invention, in order to achieve the above object,

a). 콘크리트의 하지면에 사용되어지는 것으로서, 아크릴 액상 10 ~ 20 중량%와, EVA 액상 10 ~ 20 중량%와, 나머지 물 60 ~ 80 중량%로 이루어진 콘크리트 단면 보수용 프라이머와; a). A concrete section repair primer for use in the base of concrete, which comprises 10 to 20% by weight of acrylic liquid phase, 10 to 20% by weight of EVA liquid phase, and 60 to 80% by weight of remaining water;

b). 알루미나 세라믹 바인더 20~25 중량%, 규사 40~55 중량%, 경량골재 10~14 중량%, 탄산칼슘 13~18 중량%, 분말 폴리머 1~3 중량% 를 포함하여 이루어진 콘크리트 구조물 보수용 몰탈과; b). A concrete structure repair mortar comprising 20 to 25% by weight of alumina ceramic binder, 40 to 55% by weight of silica sand, 10 to 14% by weight of lightweight aggregate, 13 to 18% by weight of calcium carbonate and 1 to 3% by weight of powder polymer;

c). 실리콘계 아크릴 폴리머 액상으로서 입자 사이즈가 7㎛ ~ 8㎛ 이고, 고형분이 25 중량% 내지 35 중량%로 구성된 콘크리트의 중성화 방지용 프라이머와; c). A silicone-based acrylic polymer liquid phase having a particle size of 7 to 8 占 퐉 and a solid content of 25 to 35% by weight;

d). 망상구조의 아크릴 액상 20 ~ 27 중량%, 탄산칼슘 50 ~ 65 중량%, 물 10 ~ 15 중량%, 안료 3 ~ 5 중량%, 증점제 1 ~ 3 중량%로 구성된 콘크리트의 중성화 방지용 코팅제; 를 포함하여 구성된 것을 특징으로 한, 콘크리트 보수용 혼합물을 제공한다. d). A coating agent for preventing the neutralization of concrete comprising 20 to 27% by weight of an acrylic liquid phase of a network structure, 50 to 65% by weight of calcium carbonate, 10 to 15% by weight of water, 3 to 5% by weight of a pigment and 1 to 3% by weight of a thickener; The present invention provides a concrete repairing admixture, comprising:

또한, 본 발명은 In addition,

a). 아크릴 액상 10 ~ 20 중량%와, EVA 액상 10 ~ 20 중량%와, 나머지 물 60 ~ 80 중량%로 이루어진 콘크리트 단면 보수용 프라이머를 제조하고, 상기 콘크리트 단면 보수용 프라이머를 보수하고자 하는 콘크리트 표면에 단위 표면적 ㎡당 100g 내지 200g 도포하는 제 1단계와; a). The present invention relates to a method for producing a concrete section repair primer comprising 10 to 20% by weight of an acrylic liquid phase, 10 to 20% by weight of an EVA liquid phase and 60 to 80% A first step of applying 100 g to 200 g per m 2 of surface area;

b). 알루미나 세라믹 바인더 20~25 중량%, 규사 40~55 중량%, 경량골재 10~14 중량%, 탄산칼슘 13~18 중량%, 분말 폴리머 1~3 중량% 를 포함하여 이루어진 콘크리트 단면 보수용 몰탈을 제조하고, 상기 콘크리트 단면 보수용 몰탈을 상기 제 1단계의 콘크리트 단면 보수용 프라이머 층 위에 도포하는 제 2단계와; b). A mortar of concrete having an aspect ratio of 20 to 25% by weight of alumina ceramic binder, 40 to 55% by weight of silica sand, 10 to 14% by weight of lightweight aggregate, 13 to 18% by weight of calcium carbonate and 1 to 3% A second step of applying the mortar for repairing the concrete section on the concrete section repair primer layer of the first stage;

c). 실리콘계 아크릴 폴리머 액상으로서 입자 사이즈가 7㎛ ~ 8㎛ 이고, 고형분이 25 중량% 내지 35 중량%로 구성된 콘크리트의 중성화 방지용 프라이머를 준비하고, 상기 제 2단계의 콘크리트 단면 보수용 몰탈 위에 도포하는 제 3단계와; c). A primer for preventing the neutralization of concrete having a particle size of 7 탆 to 8 탆 and a solid content of 25% by weight to 35% by weight as a silicone-based acrylic polymer liquid phase is prepared, and a third ;

d). 망상구조의 아크릴 액상 20 ~ 27 중량%, 탄산칼슘 50 ~ 65 중량%, 물 10 ~ 15 중량%, 안료 3 ~ 5 중량%, 증점제 1 ~ 3 중량%로 구성된 콘크리트의 중성화 방지용 코팅제를 준비하고, 상기 제 3단계의 중성화 방지용 프라이머 위에 도포하는 제 4단계; 를 순차적으로 시행함으로써, 종래의 콘크리트 구조물을 복구하거나 보수하는 방법을 제공한다.
d). A coating agent for preventing the neutralization of concrete comprising 20 to 27% by weight of an acrylic liquid phase of a network structure, 50 to 65% by weight of calcium carbonate, 10 to 15% by weight of water, 3 to 5% by weight of a pigment and 1 to 3% by weight of a thickener, A fourth step of applying the composition on the primer for neutralization of the third step; To provide a method of repairing or repairing a conventional concrete structure.

본 발명에 의한 콘크리트 구조물의 보수용 혼합물을 사용할 경우, 보수 몰탈의 탈락, 내구성, 내화학성 저하로 인한 문제점과 보수 몰탈 위에 도포하는 중성화 방지제의 내수성 문제로 인한 벗겨짐 및 내화학성 저하 현상 등의 문제점을 해결할 수 있다. When the mixture for repairing concrete structures according to the present invention is used, problems such as detachment of maintenance mortar, durability, deterioration of chemical resistance, and deterioration of chemical resistance due to the water resistance of the neutralization inhibitor applied on the maintenance mortar Can be solved.

본 발명은 콘크리트용 단면 보수용 프라이머와, 알루미나 세라믹 바인더와 폐유리 재생 경량골재를 사용한 콘크리트 구조물 보수용 몰탈을 사용함으로써, 내화학성 및 내구성을 증가시키고 적은 량으로 많은 면적을 도포하여 현장에서 신속한 보수가 가능한 장점이 있다.The present invention uses a primer for repairing a section for concrete, a mortar for repairing concrete structures using alumina ceramic binder and waste glass regenerated lightweight aggregate, thereby increasing chemical resistance and durability and applying a small amount of area for quick repair .

또한, 본 발명은 중성화 방지 코팅제 및 중성화 방지 코팅제 프라이머를 사용함으로써, 중성화 방지 코팅제와 보수 몰탈간의 접착력을 크게 향상시켰으며, 망상 구조의 아크릴 액상 바인더를 사용하여 내수성과 내구성을 현저히 향상시킴으로써, 시공 이후 하자를 최소화할 수 있는 장점이 있다.
Further, the present invention greatly improves the adhesion between the anti-neutralization coating agent and the maintenance mortar by using the anti-neutralization coating agent and the anti-neutralization coating agent primer, and significantly improves the water resistance and durability by using the acrylic liquid binder of the network structure. There is an advantage that the defect can be minimized.

도 1은 본 발명과 종래의 통상적인 콘크리트용 보수 몰탈의 시험편에 관하여 각각의 제품에 관한 내약품성을 측정한 사진자료이다. Fig. 1 is a photograph showing the chemical resistance of each product of the present invention and a conventional test piece of a repair mortar for concrete.

이하, 본 발명의 바람직한 실시예를 제조 프로세스와 더불어 상세히 설명한다. 다만, 실시예로서 제시된 구체적인 수치는 본 발명의 기술사상을 보다 상세하게 설명하기 위한 것일 뿐이며, 본 발명의 기술사상이 이에 한정되는 것이 아니며, 다양한 변형이 가능함을 미리 밝혀둔다.
Hereinafter, preferred embodiments of the present invention will be described in detail with reference to a manufacturing process. It should be noted, however, that the specific numerical values shown in the embodiments are only for explaining the technical idea of the present invention in more detail, and that the technical idea of the present invention is not limited thereto and that various modifications are possible.

본 발명에서 사용되는 콘크리트 단면 보수용 프라이머는 콘크리트의 하지면에 사용되어지고, 상기 콘크리트 하지면과 보수몰탈 사이의 중계 접착력을 증대시켜주기 위하여 사용되어진다. 상기 콘크리트 단면 보수용 프라이머는 아크릴 액상에 EVA 액상을 혼합한 제품으로 서로 다른 입자 사이즈를 혼용하여 형성될 수 있다. 상기 콘크리트 단면 보수용 프라이머는 아크릴 액상 10 ~ 20 중량%와, EVA 액상 10 ~ 20 중량%와, 나머지 물 60 ~ 80 중량%으로 조성되어 진다. The primer for repairing the section of the concrete used in the present invention is used for the bottom surface of concrete and is used to increase the adhesive strength between the concrete foundation and the repair mortar. The primer for repairing the section of concrete may be formed by mixing an acrylic liquid and an EVA liquid and mixing different particle sizes. The concrete section repair primer is composed of 10 to 20% by weight of acrylic liquid phase, 10 to 20% by weight of EVA liquid phase, and 60 to 80% by weight of remaining water.

상기 아크릴 액상은 입자 사이즈가 75㎛ ~ 85㎛로 고형분이 35 중량% 내지 45 중량%이고, 비중이 1.01인 제품을 사용하는 것이 바람직하다. 상기 아크릴 액상의 사용량이 10 중량% 미만인 경우, 콘크리트 하지면에 대한 침투력이 저하되어지거, 상기 아크릴 액상의 사용량이 20 중량% 이상일 경우에는 pH 안정성이 떨어지게되므로, 바람직스럽지 못하다. The acrylic liquid phase preferably has a particle size of 75 탆 to 85 탆, a solid content of 35% to 45% by weight, and a specific gravity of 1.01. When the use amount of the acrylic liquid phase is less than 10% by weight, the penetration ability to the concrete base surface is lowered, and when the use amount of the acrylic liquid phase is 20% by weight or more, the pH stability is lowered.

상기 EVA 액상은 입자 사이즈가 100㎛ ~ 150㎛로 고형분이 45 중량% 내지 55 중량%이고, 비중이 1.02인 제품을 사용하는 것이 바람직하다. 상기 EVA 액상의 사용량이 10 중량% 미만인 경우, 그 위에 도포되어지게 될 콘크리트 구조물 보수용 몰탈과의 접착력 저하가 발생하며, 상기 EVA 액상의 사용량이 20 중량% 이상일 경우에는, 콘크리트 하지면의 위에서 프라이머 도막이 필름 형상으로 형성되어지게 되므로, 내수성에 취약해지는 단점이 있다. The EVA liquid phase preferably has a particle size of 100 mu m to 150 mu m, a solid content of 45 wt% to 55 wt%, and a specific gravity of 1.02. When the amount of the EVA liquid phase used is less than 10% by weight, the adhesion of the EVA liquid phase to the concrete structure repair mortar to be applied thereon is lowered. When the amount of the EVA liquid phase is 20% by weight or more, Since the coating film is formed in a film shape, it is disadvantageous in that it becomes vulnerable to water resistance.

본 발명은 상기 아크릴 액상과 상기 EVA 액상 및 물을 혼합하고 균일하게 혼련하여서 복구하거나 보수하고자 하는 콘크리트의 표면에 균일하게 도포한다. 도포하는 방식은 붓이나 로라 또는 에어리스와 같은 통상적인 방법으로 수행될 수 있고, 도포 두께는 대략 단위 ㎡ 당 100 그램 내지 200 그램 정도가 바람직하다.
In the present invention, the acrylic liquid phase, the EVA liquid phase, and water are mixed and homogeneously kneaded to uniformly coat the surface of the concrete to be repaired or repaired. The coating method can be carried out by a conventional method such as brush, roller or airless, and the coating thickness is preferably about 100 to 200 grams per square meter.

본 발명에서 사용되는 콘크리트 구조물 보수용 몰탈은 알루미나 세라믹 바인더 20~25 중량%, 규사 40~55 중량%, 경량골재 10~14 중량%, 탄산칼슘 13~18 중량%, 분말 폴리머 1~3 중량% 를 포함하여 이루어지고, 사용시 물에 혼합하여 상기 단면 보수용 프라이머 위에 사용되어진다. The mortar for repairing concrete structures used in the present invention is a mortar for repairing concrete structures comprising 20 to 25% by weight of alumina ceramic binder, 40 to 55% by weight of silica sand, 10 to 14% by weight of lightweight aggregate, 13 to 18% by weight of calcium carbonate, And is mixed with water at the time of use and used on the above-mentioned section repair primer.

본 발명에 있어서, 상기 알루미나 세라믹 바인더는 주성분이 알루미나, 생석회, CaO, 무수규산 등의 응용물인 시멘트를 의미하고, CaOAl2O3 및 5CaO3Al2O3이 주요 광물로서 포함되어 있는 것이며, 포틀랜드 시멘트에 비해서 알루미나 성분이 상당히 많고, 포틀랜드 시멘트에 비하여 내식성, 내화성, 급결성이 우수하다. 이로 인해 본 발명에서 내식성, 초속경, 속건성의 물성 증진 효과를 나타낸다. In the present invention, the alumina ceramic binder means cement which is mainly applied to alumina, burnt lime, CaO, silicic anhydride and the like, CaOAl 2 O 3 and 5CaO 3 Al 2 O 3 are included as major minerals, Compared to cement, alumina content is considerably high, and it is superior in corrosion resistance, fire resistance and quickness compared with Portland cement. As a result, the present invention exhibits the effect of improving corrosion resistance, fast speed and quick-drying properties.

상기 알루미나 세라믹 바인더는 석회석과 보크사이트 또는 반토혈암 등 알루미나 성분이 많은 점토류와 배합하여 1500 ~ 1600℃에서 용융한 다음, 유출시켜서 냉각한 후, 미세한 분말로 함으로써 제조될 수 있다. 상기 알루미나 세라믹 바인더의 사용량은 20 ~ 25 중량%이고, 바람직하게는 21 ~ 23 중량%이다. 상기 알루미나 세라믹 바인더의 사용량이 20 중량% 미만이면 경화 속도가 느려지고, 25 중량%를 초과하면 급결로 인한 수축으로 갈라짐 현상이 발생되므로 바람직스럽지 못하다. The alumina ceramic binder may be prepared by mixing the alumina ceramic binder with alumina-rich clay materials such as limestone, bauxite or alumina shale, melting at a temperature of 1500 to 1600 占 폚, allowing the alumina ceramic to flow out, and then finely powdering it. The amount of the alumina ceramic binder to be used is 20 to 25% by weight, preferably 21 to 23% by weight. If the amount of the alumina ceramic binder is less than 20% by weight, the curing rate is slow. If the amount of the alumina ceramic binder is more than 25% by weight, cracking due to shrinkage may occur.

본 발명에 있어서, 상기 규사는 특별히 제한되지는 않으나, 바람직하게는 0.3mm 이하의 미립자를 사용한다. 상기 규사는 수분함량이 3% 이하인 것이 바람직하다. 규사의 사용량은 40 ~ 55 중량% 인 것이 바람직하다. 규사의 사용량이 40 중량% 미만이면 압축강도가 저하되고 시공 두께를 높이기가 어렵고, 55 중량%를 초과하면 몰탈을 제조할 경우 유동성이 저하되고, 시공 이후 크랙 및 수축이 발생할 수 있으므로 바람직스럽지 못하다.  In the present invention, the silica sand is not particularly limited, but preferably fine particles of 0.3 mm or less are used. The silica sand preferably has a water content of 3% or less. The amount of silica sand is preferably 40 to 55% by weight. When the amount of silica sand is less than 40 wt%, the compressive strength is lowered and the thickness of the construction is difficult to increase. When the amount of silica sand is more than 55 wt%, the flowability is lowered when the mortar is produced, and cracks and shrinkage may occur after the construction.

본 발명에 있어서, 상기 경량골재는 폐유리를 재활용한 경량골재를 사용한다. 폐유리를 1200 ℃로 녹여서 바람을 불어 회전하여 제조한 경량 골재로, 사이즈는 0.2 ~ 0.5mm 정도를 이루고, 표면에는 기공이 있는 제품을 사용한다. 이로 인해 상기 알루미나 세라믹 바인더와 분말 폴리머 사이에 접착력을 향상시켜주고, 몰탈의 중량 감소로 인해 작업자의 운반 시에 신체에 무리를 덜 주고 부피가 커서 적은 량으로 넓은 면을 도포할 수 있어서 빠른 현장 보수에 적합한 기능을 제공한다. 상기 경량골재는 바람직하게 10 ~ 14 중량%를 사용한다. 상기 경량 골재 10 중량% 미만인 경우에는 경량성을 발현하기 어렵고, 상기 경량 골재가 14 중량% 이상일 경우에는 비용 상승으로 제품 실현이 힘들어지는 단점이 있다. In the present invention, the lightweight aggregate is lightweight aggregate recycled from waste glass. Lightweight aggregate made by blowing wind by melting waste glass at 1200 ℃, size is about 0.2 ~ 0.5mm, and product with pore on surface is used. As a result, the adhesive force between the alumina ceramic binder and the powder polymer is improved. As a result, the weight of the mortar is reduced, thereby reducing the load on the body during transportation of the worker. . The lightweight aggregate preferably uses 10 to 14% by weight. When the lightweight aggregate is less than 10% by weight, it is difficult to exhibit lightweightness. When the lightweight aggregate is more than 14% by weight, the cost is increased and the product becomes difficult to realize.

본 발명에 있어서, 상기 탄산칼슘은 특별히 제한되지는 않으나, 입자 사이즈가 350㎛ 이하이고, 흡유량이 1% 이하인 것이 바람직하다. 탄산칼슘 사용량은 13 ~ 18 중량%이고, 바람직하게는 14 내지 16 중량%이다. 상기 탄산칼슘의 양이 13 중량% 미만이면 강도가 저하되고 초기 건조속도가 느려지며, 상기 탄산칼슘의 양이 18 중량%를 초과하면 유동성 저하를 초래하고, 재료분리(Bleeding) 및 레이턴스(Laitance) 등의 현상이 발생될 수 있으므로 바람직스럽지 못하다. In the present invention, the above-mentioned calcium carbonate is not particularly limited, but it is preferable that the particle size is 350 mu m or less and the oil absorption amount is 1% or less. The amount of calcium carbonate used is 13 to 18% by weight, preferably 14 to 16% by weight. If the amount of the calcium carbonate is less than 13% by weight, the strength is lowered and the initial drying rate is slowed. If the amount of the calcium carbonate exceeds 18% by weight, the flowability is lowered and the bare and lateness ) May occur, which is not preferable.

본 발명에 있어서, 상기 분말 폴리머는 접착 보조재 및 물성 증가제로서 수분이 건조되면 알루미나 세라믹 바인더 및 규사, 경량골재 사이에 바인더 역할을 해주어 접착력 증가, 내마모성 향상, 크랙 및 박리현상 방지, 휨강도를 강화시켜 준다. 상기 분말 폴리머로서 재유화형 분말수지를 사용하는 것이 바람직하다. 상기 재유화형 분말수지는 특별히 제한되지는 않으나, 바람직하게는 에틸렌 비닐아세테이트(EVA), 에틸렌 비닐 클로라이드 비닐 라우에이트를 사용하고, 보다 바람직하게는 바잘트 산 에틸렌 비닐 에스테르(Vinyl ester of versatic acid ethylene vinyl acetate, VA/VeoVA)를 사용할 수 있다. 상기 바잘트 산 에틸렌 비닐 에스테르는 입경이 75㎛ ~ 85㎛이고, 비중이 0.45 ~ 0.6이며, 유리전이온도가 15 ~ 35℃인 것이 바람직하다. 상기 분말 폴리머의 사용량은 1 ~ 3 중량%이다. 상기 분말 폴리머의 사용량이 1 중량% 미만이면 접착력, 내마모성 등의 물리적 물성이 나오지 않고, 3 중량%를 초과하면 경화가 지연되고 압축강도가 떨어지는 단점이 있다. In the present invention, the powder polymer serves as an adhesion promoter and a physical property enhancer, and acts as a binder between alumina ceramic binder and silica sand and lightweight aggregate when moisture is dried, thereby improving adhesion, improving abrasion resistance, preventing cracking and peeling, give. It is preferable to use a re-oiling type powder resin as the powder polymer. The re-melting type powder resin is not particularly limited, but preferably ethylene vinyl acetate (EVA) and ethylene vinyl chloride vinyl laureth are used, and more preferably, vinyl ester of versatic acid ethylene vinyl acetate, VA / VeoVA) can be used. It is preferable that the ethylene vinyl esters of bazaric acid have a particle diameter of 75 to 85 탆, a specific gravity of 0.45 to 0.6, and a glass transition temperature of 15 to 35 캜. The amount of the powder polymer used is 1 to 3% by weight. If the amount of the powder polymer used is less than 1% by weight, physical properties such as adhesion and abrasion resistance are not exhibited. If the amount is more than 3% by weight, the curing is delayed and the compressive strength is lowered.

본 발명에 따른 콘크리트 구조물 보수용 몰탈은 작업환경에 따라 물성을 조정하기 위하여 유동화제와 증점제 등과 같은 첨가제를 더욱 추가하여 포함할 수 있다. 이들의 함량은 통상의 범위 내에서 사용될 수 있으므로 특별히 제한되지는 않지만, 바람직하게는 상기 콘크리트 보수용 몰탈에 대하여 유동화제 0.01 ~ 2 중량%와 증점제 0.01 ~ 2 중량%를 사용할 수 있다. The mortar for repairing concrete structures according to the present invention may further include additives such as a fluidizing agent and a thickener for adjusting physical properties according to the working environment. The content of these can be used within a usual range, so that it is not particularly limited, but 0.01 to 2% by weight of a fluidizing agent and 0.01 to 2% by weight of a thickening agent can be used for the concrete repair mortar.

본 발명에 있어서, 상기 유동화제는 보수몰탈의 유동성을 증가시키기 위해 사용된다. 본 발명에서 유동화제는 분자 속에 한 개 이상의 극성 그룹을 가지고 있는 중합체를 의미하며, 화학 구조상 세라믹 바인더 입자를 분산시키는 성능이 뛰어나고 감수성능이 우수하며, 아울러 응결지연 및 과다한 공기연행이나 강도저하 등의 부작용 없이 단위 혼수량을 대폭 감수시킬 수 있는 혼화제를 말한다. 상기 조건에 따르는 한 특별히 제한되지는 않지만, 바람직하게 본 발명에 사용될 수 있는 유동화제의 예는 리그노술폰산염, 하이드록시 폴리 카르본산, 나프탈렌 포름 알데하이드 술폰산염 및 멜라민 포름 알데하이드 술폰산염으로 구성된 그룹에서 선택된 것을 포함하고, 보다 바람직하게는 친환경 소재인 하이드록시 폴리 카르본산이 선호된다. In the present invention, the fluidizing agent is used to increase the fluidity of the repair mortar. In the present invention, the fluidizing agent means a polymer having at least one polar group in the molecule. The fluidity agent is excellent in the performance of dispersing the ceramic binder particles in chemical structure and excellent in water-reducing performance, and also has the effect of delaying condensation, It is an admixture that can greatly reduce the unit water content without side effects. Although not particularly limited as far as the above conditions are met, examples of the fluidizing agent which can preferably be used in the present invention include a group consisting of a lignosulfonic acid salt, a hydroxycarboxylic acid, a naphthalene formaldehyde sulfonic acid salt and a melamine formaldehyde sulfonic acid salt Hydroxypolycarboxylic acid, which is an eco-friendly material, is more preferred.

본 발명에 있어서, 상기 증점제는 메틸 셀룰로오스(methyl cellulose)계 증점제를 사용한다. 상기 증점제의 사용량은 전체 조성물의 중량 대비 0.01 ~ 2 중량%가 바람직하다. 상기 증점제의 사용량이 상기 범위일 때 겉마름 현상이 발생하지 않게 되어 표면 갈라짐이 방지되면서도 물속에서의 씻겨짐 현상을 방지해줘서 작업성 향상을 도모할 수 있다. 
In the present invention, the thickener is a methyl cellulose thickener. The amount of the thickener is preferably 0.01 to 2% by weight based on the weight of the entire composition. When the amount of the thickening agent used is within the above range, the surface phenomenon does not occur and surface cracking is prevented, while washing up in water is prevented, so that workability can be improved.

본 발명이 제안하는 콘크리트용 중성화 방지제 조성물은 프라이머와 코팅제로 나뉜다. The antifouling composition for concrete proposed by the present invention is divided into a primer and a coating agent.

본 발명에 있어서, 중성화 방지용 프라이머는 실리콘계 아크릴 폴리머 액상을 사용하며, 입자 사이즈가 7㎛~8㎛로 일반 아크릴 폴리머 사이즈보다 10분의 1 정도 작기 때문에, 상기 보수용 몰탈에 깊숙이 침투되어 중성화 방지제와의 부착강도를 증진시킬 수 있다. 상기 실리콘계 아크릴 폴리머 액상은 고형분이 30 중량%이고, 비중이 1.01인 것으로서, 반투명의 액상 완제품을 사용하는 것이 바람직하다. In the present invention, since the silicone-based acrylic polymer liquid phase is used, the particle size of the primer for neutralization prevention is in the range of 7 탆 to 8 탆, which is about one tenth the size of the general acrylic polymer. Therefore, Can be increased. The silicone-based acrylic polymer liquid phase has a solid content of 30% by weight and a specific gravity of 1.01, and it is preferable to use a semi-transparent liquid product.

본 발명에 있어서, 중성화 방지용 코팅제는 망상구조를 갖는 아크릴 액상을 사용하여 제조된다. 일반적인 아크릴 액상은 도막 형성 후 구조가 선형 구조이지만, 본 발명에 사용된 아크릴 액상은 도막 형성 후 망상구조를 가진 것으로서 좀더 치밀한 구조로 외부 저항성이 극대화한 제품이다. 상기 중성화 방지용 코팅제의 조성은 망상구조 아크릴 액상 20 ~ 27 중량%, 탄산칼슘 50 ~ 65 중량%, 물 10 ~ 15 중량%, 안료 3 ~ 5 중량%, 증점제 1 ~ 3 중량%로 구성된 제품이 바람직하다. In the present invention, the anti-neutralization coating agent is prepared using an acrylic liquid phase having a network structure. In general, the acrylic liquid phase has a linear structure after the formation of the coating film, but the acrylic liquid phase used in the present invention has a reticulated structure after the formation of the coating film and has a more dense structure to maximize external resistance. The composition of the anti-neutralization coating agent is preferably composed of 20 to 27% by weight of a network acrylic liquid phase, 50 to 65% by weight of calcium carbonate, 10 to 15% by weight of water, 3 to 5% by weight of pigment and 1 to 3% by weight of a thickener Do.

상기 아크릴 액상은 망상구조를 갖는 아크릴 바인더로 고형분이 45 중량% 내지 55 중량% 이고, 비중이 1.01인 제품을 사용한다. 상기 아크릴 액상은 상기 중성화 방지용 코팅제의 전체 조성물의 중량대비 20 ~27 중량%가 바람직하다. 상기 아크릴 액상이 20 중량% 이하로 첨가될 경우, 내수성이 떨어지는 반면에, 상기 아크릴 액상이 27 중량% 이상 첨가될 경우, 가격 경쟁력이 저하되어지고, 경화 지연을 초래할 수 있다. The acrylic liquid phase is an acrylic binder having a network structure, having a solid content of 45 wt% to 55 wt% and a specific gravity of 1.01. The acrylic liquid phase is preferably 20 to 27% by weight based on the weight of the total composition of the anti-neutralization coating agent. When the acrylic liquid phase is added in an amount of 20 wt% or less, the water resistance is poor. On the other hand, when the acrylic liquid phase is added in an amount of 27 wt% or more, the price competitiveness is lowered and the curing is delayed.

본 발명에서 사용되는 탄산칼슘은 특별히 제한되지는 않으나, 입자 사이즈가 350㎛ 이하이고, 흡유량이 1% 이하인 것이 바람직하다. 상기 탄산칼슘의 사용량은 50 ~ 65 중량%이고, 탄산칼슘의 양이 50 중량% 미만이면 초기 건조속도가 느려지며, 65 중량%를 초과하면 유동성 저하 및 표면 내마모성 저하 현상이 발생할 수 있으므로 바람직스럽지 못하다. The calcium carbonate used in the present invention is not particularly limited, but preferably has a particle size of 350 mu m or less and an oil absorption amount of 1% or less. If the amount of calcium carbonate is less than 50% by weight, the initial drying rate is lowered. If the amount of calcium carbonate is more than 65% by weight, the fluidity and surface abrasion resistance may be lowered, which is not preferable .

본 발명에 의한 중성화 방지용 코팅제는, 물성을 조정하기 위하여 안료와 증점제 등을 추가로 포함할 수 있다. 상기 안료와 증점제의 함량은 통상의 범위 내에서 사용될 수 있으므로 특별히 제한되지는 않지만, 바람직하게는 안료 3 ~ 5 중량%, 증점제 1 ~ 3 중량%를 사용할 수 있다.
The anti-neutralization coating agent according to the present invention may further include a pigment and a thickener for adjusting physical properties. The content of the pigment and the thickening agent can be used within a usual range, so that it is not particularly limited, but preferably 3 to 5% by weight of the pigment and 1 to 3% by weight of the thickener can be used.

이와 같이 구성된 본 발명에 따른 콘크리트 구조물의 보수용 조성물은 다음과 같은 방식으로 노후화된 콘크리트 벽면 등에 시공될 수 있다. The composition for repairing a concrete structure according to the present invention may be applied to an aged concrete wall or the like in the following manner.

1). 표면 보수 공법: (중성화 방지 시공방법) One). Surface repair method: (Anti-neutralization construction method)

본 발명은 아래와 같은 단계로 상기 중성화 방지용 프라이머 및 중성화 방지용 코팅제를 사용하여 시공하게 된다. In the present invention, the anti-neutralization primer and anti-neutralization coating agent are used in the following steps.

Figure 112014022042953-pat00001
Figure 112014022042953-pat00001

본 발명은 주변환경으로 인하여 또는 준공기간이 장기간 경과됨으로 인하여 콘크리트 벽면에 중성화 현상이 발생될 경우, 이를 방지하고 보수하기 위하여, 상기 중성화 방지 시공방법을 활용할 수 있다. The present invention can utilize the anti-neutralization method in order to prevent and repair the neutralization phenomenon in the concrete wall due to the surrounding environment or the long-term completion period.

먼저, 시공하고자 하는 콘크리트의 표면을 선정하고, 그라인더와 같은 공구를 이용하여 그 표면을 얇게 제거한다. 상기 콘크리트 표면의 처리방식은 통상의 방법 및 공구를 이용하여 진행될 수 있다. First, the surface of the concrete to be applied is selected and its surface is thinly removed by a tool such as a grinder. The treatment of the concrete surface can be carried out using conventional methods and tools.

그라인더에 의해 열화된 표면이 제거된 콘크리트층의 표면 부분에 대해 고압의 물을 분사하여 세척하고, 그 표면층을 건조시킨다. High-pressure water is sprayed on the surface portion of the concrete layer from which the surface deteriorated by the grinder is removed, and the surface layer is dried.

작업을 진행 중인 콘크리트 표면층에 대해, 중성화 방지용 프라이머를 얇게 도포한다. 상기 중성화 방지재 전용 프라이머를 붓 또는 로라를 이용하여 도포하는 것이 좋다. Apply a thin layer of anti-neutralization primer to the concrete surface layer in progress. It is preferable to apply the primer for anti-neutralization material by using a brush or roller.

상기 중성화 방지재 전용 프라이머가 굳어지면, 그 위에 본 발명에 의한 상기 중성화 방지용 코팅제를 로라, 에어리스, 뿜칠 도구 등을 이용하여 도포하는 것이 좋다.
When the primer for the anti-neutralization material is hardened, it is preferable to apply the anti-neutralization coating material according to the present invention by using a roller, an airless, a spraying tool or the like.

2). 단면복구 보수 공법: 2). Section repair repair method:

본 발명은 아래와 같은 단계로 상기 단면복구용 프라이머 및 상기 콘크리트용 몰탈과, 상기 중성화 방지용 프라이머 및 중성화 방지용 코팅제를 사용하여 시공하게 된다. In the present invention, the primer for end face repair, the mortar for concrete, the primer for neutralization prevention and the coating agent for neutralization prevention are used in the following steps.

Figure 112014022042953-pat00002

Figure 112014022042953-pat00002

본 발명은 시공하고자 하는 노후화된 콘크리트의 벽면을 깨뜨리고, 노후화된 콘크리트 파편들을 제거한다. The present invention breaks the wall of the aged concrete to be constructed and removes the aged concrete debris.

노후화된 콘크리트 파편들이 제거된 부위에 대하여 고압의 물을 분사시켜서 세척하고, 그 표면층을 건조한다. High pressure water is sprayed on the area from which the aged concrete debris is removed, and the surface layer is dried.

콘크리트 파편을 제거한 내부에 철근이 존재할 경우에는, 그 철근에 방청제를 도포하여 철근의 부식작용을 방지하도록 한다. 건조된 상기 콘크리트 벽면의 표면층 위에 상기 단면 복구 내지 보수용 프라이머를 얇게 도포해주는 것이 좋다. If there is a reinforcing bar inside the concrete debris, remove the reinforcing bar to prevent corrosion of the reinforcing bar. It is preferable that the above-mentioned section repairing and repairing primer is thinly coated on the surface layer of the dried concrete wall surface.

상기 단면 복구 내지 보수용 프라이머 층이 경화되어지면, 그 위에 상기 단면 복구 내지 보수용 몰탈을 미장흙손으로 치핑한 두께로 복구 시공하고, 상기 보수 몰탈이 경화될 때까지 기다린다. After the above-mentioned single-sided repairing and repairing primer layer is cured, the above-mentioned section repairing and repairing mortar is restored to a thickness chipped with a trowel and then waited until the repair mortar is cured.

상기 보수 몰탈이 경화되어지면, 그 위에 상기 중성화 방지용 프라이머를 붓, 로라, 에어리스, 뿜칠 도구 등을 이용하여 도포하는 것이 좋다. 상기 중성화 방지용 프라이머가 굳어지면, 그 위에 본 발명에 의한 상기 중성화 방지용 코팅제를 도포한다. When the repair mortar is cured, it is preferable that the anti-neutralization primer is applied thereon by using a brush, a roller, an airless, a spraying tool, or the like. When the anti-neutralization primer is hardened, the anti-neutralization coating agent according to the present invention is applied thereto.

필요할 경우, 본 발명은 상기 중성화 방지용 코팅제에 적절한 안료를 포함시켜서 주변환경에 적합하거나 새로운 감각의 콘크리트 표면을 형성할 수 있다.
If necessary, the present invention can incorporate a suitable pigment in the anti-neutralization coating to form a new sense of concrete surface suitable for the surrounding environment.

다음에는, 본 발명에 따른 콘크리트 구조물의 보수용 조성물 및 그 시공방법의 바람직한 실시예를 설명한다. 그러나 아래의 실시예는 단지 본 발명을 구체적으로 설명하기 위한 것으로서, 이 실시예에 의해 본 발명의 범위를 한정하는 것은 아니다.
Next, preferred embodiments of the repair composition and the construction method of the concrete structure according to the present invention will be described. However, the following examples are intended to illustrate the present invention only and do not limit the scope of the present invention.

<< 실시예 1 >> &Lt; Example 1 &gt;

콘크리트 구조물 보수용 몰탈의 중계접착력을 증가시키기 위해 프라이머 사용 유무에 따른 실시예를 진행하였다. 여기에 사용된 프라이머 조성은 대흥특수화학 709S 아크릴 1.67 Kg, Wacker KOREA 6709 EVA 1.79 Kg, 물 6.54 Kg으로 제조된 제품을 사용하였고, 붓으로 중량을 측정하여 1 ㎡ 에 0.1kg 을 도포하였다. In order to increase the adhesive strength of mortar for repairing concrete structures, an example according to the presence or absence of primer was conducted. The primer composition used herein was 1.67 Kg of Daeheung Specialty Chemical 709S acrylic, 1.79 Kg of Wacker KOREA 6709 EVA and 6.54 Kg of water, and the weight was measured with a brush and 0.1 kg was applied to 1 m 2.

한편, 알루미나 세라믹 바인더(독일 Cement Fondu 제품) 3 Kg, 규사 3 Kg, 경량골재 (독일 포라베르 제품) 1.5 Kg, 탄산칼슘 (Omya 10) 2 Kg, 분말 폴리머 (독일 Wacker, Vinnapas 5010N) 0.4 Kg, 유동화제 (케미콘, Powercon 100) 20 g, 증점제 (케미콘, Setafix NG) 80 g을 칭량하여 혼합 용기에 투입하고, 여기에 물 3.5 Kg을 첨가하여 5분간 혼합한 후, 콘크리트용 구조물 보수용 몰탈을 제조하여 준비하였다.
On the other hand, 0.4 Kg of a powder polymer (Wacker, Vinnapas 5010N, Germany), 2 Kg of calcium carbonate (Omya 10), 1.5 Kg of a lightweight aggregate (manufactured by Porabere of Germany), 3 Kg of alumina ceramic binder Fluidizer (Chemcon, Powercon 100) And 80 g of a thickener (Chemicon, Setafix NG) were weighed and placed in a mixing vessel. 3.5 Kg of water was added thereto and mixed for 5 minutes. Then, a mortar for repairing concrete structures was prepared and prepared.

상기 실시예 1에 의한 상기 콘크리트 단면 보수용 프라이어머와 상기 콘크리트 구조물 보수용 몰탈을 이용하여 시편을 제작하고, 그 시편에 관한 압축강도와 부착강도와 휨강도와 내충격성 등의 시험을 진행하였다. 이와 같은 시험은 KS 시험방법에 따랐으며, 그에 관한 시험결과를 아래의 표 1로 정리하였다. Test specimens were prepared using the concrete primer for repairing the section of concrete according to Example 1 and the mortar for repairing the concrete structure, and the compressive strength, bond strength, bending strength and impact resistance of the specimen were tested. These tests were performed according to the KS test method, and the results of the tests are summarized in Table 1 below.

본 발명의 콘크리트 구조물 보수용 몰탈의 시험항목 및 그 결과 Test items and results of the mortar for repairing concrete structures of the present invention 시험항목  Test Items 양생일 및 기타 Sheep birthday and other 시험결과  Test result 시험방법   Test Methods
압축강도(N/㎟)

Compressive strength (N / mm2)

28일

28th

35.1

35.1

KS F 4042

KS F 4042

부착강도(N/㎟)

Bond strength (N / mm2)

28일

28th

20.2

20.2

KS F 4042

KS F 4042

휨강도(N/㎟)

Bending strength (N / mm2)

28일

28th

8.7

8.7

KS F 4042

KS F 4042

내충격성

Impact resistance

28일

28th

이상 없음

clear

KS F 4937

KS F 4937

물 흡수율

Water absorption rate

(%)

(%)

10% 이하

below 10

KS L 1592

KS L 1592

내약품성
(압축강도 N/㎟)

Chemical resistance
(Compression strength N / mm 2)

5% H2SO4

5% H 2 SO 4

22.3

22.3

168시간 침지 후

After 168 hours immersion

10% Na2SO4

10% Na 2 SO 4

24.8

24.8

168시간 침지 후

After 168 hours immersion

상기 표 1에서 확인되는 바와 같이, 압축강도, 부착강도, 휨강도, 내마모성, 내충격성은 각각 KS F 4042 시험 방법 규정에 맞추어 측정하였다.As shown in Table 1, the compressive strength, the adhesive strength, the flexural strength, the abrasion resistance and the impact resistance were measured in accordance with the test method of KS F 4042, respectively.

시험 결과, 본 발명은 알루미나 세라믹 바인더를 사용함으로서 내약품성이 우수하게 나왔으며, 특히 분말 폴리머를 사용하여 휨강도와 내충격성이 높게 나왔음을 알 수 있다.
As a result of the test, it was found that the use of an alumina ceramic binder resulted in excellent chemical resistance, and in particular, the use of a powder polymer results in a high bending strength and high impact resistance.

<< 비교예 1 >>  &Lt; Comparative Example 1 >

상기 실시예 1에 있어서, 상기 알루미나 세라믹 바인더를 사용하는 대신에, 일반 포틀랜드 시멘트를 대체하여 사용하였고, 그 이외의 조건을 상기 실시예 1과 동일하게 한 상태에서 통상적인 콘크리트 단면 보수용 몰탈을 제조하여 준비하였다.  In place of using the alumina ceramic binder in Example 1, ordinary Portland cement was used in place of the alumina ceramic binder. In the same manner as in Example 1 except for the other conditions, a conventional mortar for repairing a concrete section was manufactured Respectively.

상기 통상적인 콘크리트 보수용 몰탈을 이용하여 시편을 제작하고, 그 시편에 관한 내약품성 시험을 진행하였다. 이와 같은 시험은 역시 위와 동일하게 KS 시험방법에 따랐으며, 그에 관한 시험결과를 아래의 표 2로 정리하였다. Specimens were prepared using the conventional concrete repair mortar, and the chemical resistance test was conducted on the specimens. These tests were also conducted according to the KS test method, and the test results are summarized in Table 2 below.

통상적인 콘크리트 보수용 몰탈의 시험항목 및 그 결과 Test Items and Results of Conventional Mortar for Concrete Repair 시험항목   Test Items 양생일 및 기타  Sheep birthday and other 시험 결과    Test result 시험방법    Test Methods
내약품성
(압축강도 N/㎟)

Chemical resistance
(Compression strength N / mm 2)

5% H2SO4

5% H 2 SO 4

12.3

12.3

168시간 침지 후

After 168 hours immersion

10% Na2SO4

10% Na 2 SO 4

13.4

13.4

168시간 침지 후

After 168 hours immersion

상기 표 2 에서 알 수 있듯이, 일반 포틀랜드 시멘트를 사용한 비교예 1은 내약품성이 매우 떨어져 있음을 알 수 있다. 다시 말해서, 28일 양생 후 5% 황산 용액에 침지한 후 압축강도는, 본 발명의 경우 22.3 (N/㎟)이었던 것에 비하여, 상기 비교예 1의 경우에는 12.3 (N/㎟)이었던 것이다. 또한, 10% 황산소다 용액에 침지한 후 측정한 압축강도는, 본 발명의 경우 24.8 (N/㎟)이었던 것에 비하여, 상기 비교예 1의 경우에는 13.4 (N/㎟)이었던 것이다.
As can be seen from Table 2, it can be seen that Comparative Example 1 using common Portland cement has a very low chemical resistance. In other words, the compressive strength after immersion in a 5% sulfuric acid solution after curing for 28 days was 22.3 (N / mm 2) in the case of the present invention and 12.3 (N / mm 2) in the case of Comparative Example 1. In addition, the compressive strength measured after immersion in a 10% sodium sulfate solution was 24.8 (N / mm 2) in the case of the present invention and 13.4 (N / mm 2) in the case of Comparative Example 1.

도 1은 본 발명과 종래의 통상적인 콘크리트용 보수 몰탈의 시험편에 관하여 각각의 제품에 관한 내약품성을 측정한 사진자료를 보여주고 있다.
Fig. 1 shows photographic data measuring the chemical resistance of each product with respect to the test piece of the present invention and conventional conventional concrete repair mortar.

도 1에 의하면, 5% 황산 용액에 침지하기 이전의 시편의 사진과, 침지한 이후의 사진자료를 나타낸 것으로서, 상기 실시예 1과 상기 비교예1의 콘크리트 보수 몰탈의 시험편은 상기 5% 황산 용액에 침지하기 이전에는 모두 반듯하고 표면이 매끄러운 것임에 비하여, 상기 5% 황산 용액에 침지한 이후에는 상기 실시예 1의 경우 전체적인 형상은 거의 변화가 없고, 그 표면에서 약간 거칠게 보인 반면에, 상기 비교예 1의 경우 전체적인 형상에 비틀림 현상을 발견할 수 있고, 그 표면에서도 심하게 부식되거나 부분적으로 함몰된 부위를 많이 발견할 수 있다.
1 shows photographs of specimens before immersion in a 5% sulfuric acid solution and photographic data after immersion. The specimens of the concrete repair mortar of Example 1 and Comparative Example 1 were the same as the 5% sulfuric acid solution And the surface is smooth. On the other hand, after immersion in the 5% sulfuric acid solution, the overall shape of the Example 1 is almost unchanged and slightly rough on the surface thereof, In Example 1, a twist phenomenon can be found in the overall shape, and a lot of parts that are deeply corroded or partially depressed can be found on the surface.

<< 비교예 2 >> &Lt; Comparative Example 2 &gt;

콘크리트 구조물 보수용 몰탈의 부착강도를 확인하기 위하여, 콘크리트 표면에 프라이머 처리를 행한 경우와 콘크리트 표면에 프라이머 처리를 행하지 않은 경우를 서로 대비하여 살펴보기로 하였다. In order to confirm the bond strength of mortar for repairing concrete structures, we examined the case where the primer treatment was performed on the concrete surface and the case where the primer treatment was not performed on the concrete surface.

먼저, 본 발명의 상기 콘크리트 단면 복구 보수용 프라이머를 처리한 다음, 상기 실시예 1에 의한 보수 몰탈을 가지고 시편을 만들어 준비하고, 또한 아무런 보수용 프라이머를 처리하지 않고 상기 비교예 1에 의한 통상적인 콘크리트용 단면 복구 보수용 몰탈을 제조하여 준비하였다. First, the concrete end face repair and repair primer of the present invention was treated, then, a specimen was prepared by using the repair mortar of Example 1, and a conventional one according to Comparative Example 1 was prepared without any maintenance primer treatment. The mortar for repair and maintenance of concrete section was prepared and prepared.

모두 시험방법은 KS F 4042 방식으로 진행하였으며, 그에 관한 각각의 시험결과를 아래의 표 3으로 정리하였다.
All the test methods were carried out using the KS F 4042 method, and the results of the respective tests are summarized in Table 3 below.

콘크리트 구조물 보수용 몰탈의 부착강도에 관한 상호 비교 시험결과 Cross-sectional test results on the bond strength of mortar for repairing concrete structures 시험항목   Test Items 양생일 및 기타 Sheep birthday and other 실시예 1  Example 1 비교예 2  Comparative Example 2 시험방법  Test Methods
부착강도(N/㎟)

Bond strength (N / mm2)

28일

28th

20.2

20.2

12.4

12.4

KS F 4042

KS F 4042

상기 표 3에서 알 수 있듯이, 본 발명에 의한 프라이머를 사용하였을 경우, 보수 몰탈의 부착강도는 20.2 (N/㎟)인데 반하여, 상기 프라이머를 사용하지 않았을 경우, 보수 몰탈의 부착강도는 12.4 (N/㎟) 임을 알 수 있다.  As shown in Table 3, when the primer according to the present invention was used, the adhesion strength of the repair mortar was 20.2 (N / mm 2), whereas when the primer was not used, the adhesion strength of the repair mortar was 12.4 (N / Mm &lt; 2 &gt;).

이는 종래의 보수 몰탈의 부착 강도에 비하여, 본 발명에 의한 보수 몰탈의 부착 강도는 163% 정도로 향상되었음을 의미한다.
This means that the adhesion strength of the repair mortar according to the present invention is improved to about 163% as compared with the adhesion strength of the conventional repair mortar.

<< 실시예 2 >> &Lt; Example 2 &gt;

중성화 방지 코팅제를 제조하기 위하여, 망상구조 아크릴 액상 2.5 Kg, 탄산칼슘 5.8 Kg, 물 1.2 Kg, 안료 0.4 Kg, 증점제 0.1 Kg 을 각각 칭량하여 준비하고, 이것을 혼합용기에 투입한 다음, 800rmp으로 1시간 동안 고속 혼합하여 균일한 상태의 코팅제 조성물을 제조하였다. To prepare an anti-neutralization coating agent, 2.5 kg of network liquid acrylic liquid, 5.8 Kg of calcium carbonate, 1.2 Kg of water, 0.4 Kg of pigment and 0.1 Kg of thickener were weighed and put into a mixing vessel, Were mixed at high speed to prepare a uniform coating composition.

한편, 상기 중성화 방지 코팅제 이전에 사용할 프라이머를 실리콘계 아크릴 폴리머 액상으로 준비하였다. 상기 액상의 실리콘계 아크릴 폴리머 입자 사이즈는 7㎛ ~ 8㎛ 이었고, 고형분이 30% 인 것을 사용하였다. On the other hand, a primer to be used before the anti-neutralization coating agent was prepared as a silicone acrylic polymer liquid. The liquid silicone-based acrylic polymer particle size was 7 탆 to 8 탆 and a solid content of 30% was used.

시험방법은 모두 KS 시험 방식에 따랐으며, 그에 관한 시험 항목 및 시험 결과를 아래의 표 4로 정리하였다.
All the test methods were in accordance with the KS test method, and the test items and test results were summarized in Table 4 below.

시험항목  Test Items 실시예 2   Example 2 시험방법   Test Methods
부착강도(N/㎟)

Bond strength (N / mm2)

15.7

15.7

KS F 4042

KS F 4042

물 흡수율(%)

Water Absorption Rate (%)

5% 이하

Less than 5%

KS L 1592

KS L 1592

10% NaOH

10% NaOH

이상 없음

clear


KS M ISO 2812(1)-'07


KS M ISO 2812 (1) - '07

10% H2SO4

10% H 2 SO 4

이상 없음

clear

<< 비교예 3 >> &Lt; Comparative Example 3 &gt;

중성화 방지 코팅제 전용 프라이머를 사용하지 않고, 부착강도 시험을 진행하였으며, 그 실험의 결과를 아래의 표 5로 정리하였다.
The adhesion strength test was carried out without using a primer dedicated to the anti-neutralization coating, and the results of the experiment were summarized in Table 5 below.

시험항목  Test Items 실시예 2   Example 2 비교예 3   Comparative Example 3 시험방법   Test Methods
부착강도(N/㎟)

Bond strength (N / mm2)

15.7

15.7

8.9

8.9

KS F 4042

KS F 4042

상기 표 4 및 상기 표 5를 상호 대비하여 살펴볼 경우, 상기 실시예 2의 경우 부착강도는 15.7 (N/㎟)인데 반하여, 상기 비교예 3의 경우 부착강도는 8.9 (N/㎟)임을 알 수 있다. As shown in Table 4 and Table 5, the bond strength of Example 2 was 15.7 (N / mm 2), while the bond strength of Comparative Example 3 was 8.9 (N / mm 2) have.

이는 본 발명에 의한 중화 방지 코팅제를 사용하였을 경우, 종래의 통상적인 경우에 비하여, 그 부착강도가 무려 176% 정도 향상되었음을 의미하는 것이다.
This means that when the anti-neutralization coating agent of the present invention is used, the adhesion strength is improved by as much as 176% as compared with the conventional case.

이상에서 본 발명에 의한 콘크리트 구조물의 보수용 조성물 및 그 시공방법을 구체적으로 설명하였으나, 이는 본 발명의 가장 바람직한 실시양태를 기재한 것일 뿐, 본 발명이 이에 한정되는 것은 아니며, 첨부된 특허청구범위에 의해서 그 범위가 결정되어지고 한정되어진다. While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, The range is determined and limited.

또한, 이 기술분야에서 통상의 지식을 가진 자라면 누구나 본 발명의 명세서의 기재내용에 의하여 다양한 변형 및 모방을 행할 수 있을 것이나, 이 역시 본 발명의 범위를 벗어난 것이 아님은 명백하다고 할 것이다. It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the scope of the present invention.

Claims (7)

a). 콘크리트의 하지면에 사용되어지는 것으로서, 아크릴 액상 10 ~ 20 중량%와, EVA 액상 10 ~ 20 중량 %와, 나머지 물 60 ~ 80 중량%으로 이루어진 콘크리트 단면 보수용 프라이머와;
b). 알루미나 세라믹 바인더 20~25 중량%, 규사 40~55 중량%, 경량골재 10~14 중량%, 탄산칼슘 13~18 중량%, 분말 폴리머 1~3 중량% 를 포함하여 이루어진 콘크리트 구조물 보수용 몰탈과;
c). 실리콘계 아크릴 폴리머 액상으로서 입자 사이즈가 7㎛ ~ 8㎛ 이고, 고형분이 25 중량% 내지 35 중량%로 구성된 콘크리트의 중성화 방지용 프라이머와;
d). 망상구조의 아크릴 액상 20 ~ 27 중량%, 탄산칼슘 50 ~ 65 중량%, 물 10 ~ 15 중량%, 안료 3 ~ 5 중량%, 증점제 1 ~ 3 중량%로 구성된 콘크리트의 중성화 방지용 코팅제; 를 포함하여 구성된 것을 특징으로 한, 콘크리트 구조물의 보수용 혼합물.
a). A concrete section repair primer used for a concrete foundation surface, which comprises 10 to 20% by weight of acrylic liquid phase, 10 to 20% by weight of EVA liquid phase, and 60 to 80% by weight of remaining water;
b). A concrete structure repair mortar comprising 20 to 25% by weight of alumina ceramic binder, 40 to 55% by weight of silica sand, 10 to 14% by weight of lightweight aggregate, 13 to 18% by weight of calcium carbonate and 1 to 3% by weight of powder polymer;
c). A silicone-based acrylic polymer liquid phase having a particle size of 7 to 8 占 퐉 and a solid content of 25 to 35% by weight;
d). A coating agent for preventing the neutralization of concrete comprising 20 to 27% by weight of an acrylic liquid phase of a network structure, 50 to 65% by weight of calcium carbonate, 10 to 15% by weight of water, 3 to 5% by weight of a pigment and 1 to 3% by weight of a thickener; Wherein the concrete mixture comprises at least one of the following components.
제 1 항에 있어서,
상기 콘크리트 구조물 보수용 몰탈에 대하여 유동화제 0.01 ~ 2 중량%와 증점제 0.01 ~ 2 중량%를 더욱 포함하고 있으며,
상기 유동화제는 리그노술폰산염, 하이드록시 폴리 카르본산, 나프탈렌 포름 알데하이드 술폰산염 및 멜라민 포름 알데하이드 술폰산염으로 구성된 그룹에서 선택된 어느 하나를 사용하고,
상기 증점제는 메틸 셀룰로오스(methyl cellulose)계 증점제를 사용하는 것을 특징으로 한, 콘크리트 구조물의 보수용 혼합물.
The method according to claim 1,
The mortar for repairing concrete structures further comprises 0.01 to 2% by weight of a fluidizing agent and 0.01 to 2% by weight of a thickening agent,
Wherein the fluidizing agent is selected from the group consisting of a lignosulfonic acid salt, a hydroxycarboxylic acid, a naphthalene formaldehyde sulfonic acid salt and a melamine formaldehyde sulfonic acid salt,
Characterized in that the thickener is a methyl cellulose thickener.
제 1 항에 있어서,
상기 아크릴 액상은 입자 사이즈가 75㎛ ~ 85㎛ 이고, 고형분은 35 중량% 내지 45 중량%이며, 비중이 1.01인 제품을 사용하고,
상기 EVA 액상은 입자 사이즈가 100㎛ ~ 150㎛ 이고, 고형분이 45 중량% 내지 55 중량%이며, 비중이 1.02인 제품을 사용하는 것을 특징으로 한, 콘크리트 구조물의 보수용 혼합물.
The method according to claim 1,
The acrylic liquid phase had a particle size of 75 탆 to 85 탆, a solid content of 35 wt% to 45 wt% and a specific gravity of 1.01,
Wherein the EVA liquid phase has a particle size of 100 mu m to 150 mu m, a solid content of 45 wt% to 55 wt%, and a specific gravity of 1.02.
제 1 항에 있어서,
상기 알루미나 세라믹 바인더는 석회석과 보크사이트 또는 반토혈암의 알루미나 성분이 많은 점토류와 배합하여 1500℃ ~ 1600℃의 고온에서 소성하고 냉각시킨 후, 미세한 분말로 제조된 것이고,
상기 경량골재는 폐유리를 1200 ℃로 녹여서 소성하고 냉각시켜서 그 표면에 기공이 있는 것으로 입자 크기를 0.2 ~ 0.5mm 의 범위로 사용하는 것을 특징으로 한, 콘크리트 구조물의 보수용 혼합물.
The method according to claim 1,
The alumina ceramic binder is produced by mixing fine clay with a large amount of alumina components such as limestone, bauxite or alumina shale, calcining it at a high temperature of 1500 to 1600 占 폚, cooling it,
The lightweight aggregate is characterized in that the waste glass is melted at 1200 DEG C, fired and cooled to have pores on its surface, and the particle size is used in the range of 0.2 to 0.5 mm.
제 1 항에 있어서,
상기 분말 폴리머는 재유화형 분말수지를 사용하고,
상기 재유화형 분말수지는 에틸렌 비닐아세테이트(EVA), 에틸렌 비닐 클로라이드 비닐 라우에이트, 바잘트 산 에틸렌 비닐 에스테르를 포함하는 그룹 중에서 선택된 어느 하나를 사용하는 것을 특징으로 한, 콘크리트 구조물의 보수용 혼합물.
The method according to claim 1,
The powdered polymer is prepared by using a re-
Characterized in that the re-firing powder resin uses any one selected from the group consisting of ethylene vinyl acetate (EVA), ethylene vinyl chloride vinyl laureth, and bazaric acid ethylene vinyl ester.
제 5 항에 있어서,
상기 바잘트 산 에틸렌 비닐 에스테르는 입경이 75㎛ ~ 85㎛이고, 비중이 0.45 ~ 0.6이며, 유리전이온도가 15 ~ 35℃인 것을 특징으로 한, 콘크리트 구조물의 보수용 혼합물.
6. The method of claim 5,
Characterized in that the ethylene vinyl esters of bazaric acid have a particle size of 75 to 85 占 퐉, a specific gravity of 0.45 to 0.6 and a glass transition temperature of 15 to 35 占 폚.
a). 아크릴 액상 10 ~ 20 중량%와, EVA 액상 10 ~ 20 중량%와, 나머지 물 60 ~ 80 중량%로 이루어진 콘크리트 단면 보수용 프라이머를 제조하고, 상기 콘크리트 단면 보수용 프라이머를 보수하고자 하는 콘크리트 표면에 단위 표면적 ㎡당 100g 내지 200g 을 도포하는 제 1단계와;
b). 알루미나 세라믹 바인더 20~25 중량%, 규사 40~55 중량%, 경량골재 10~14 중량%, 탄산칼슘 13~18 중량%, 분말 폴리머 1~3 중량% 를 포함하여 이루어진 콘크리트 구조물 보수용 몰탈을 제조하고, 상기 콘크리트 구조물 보수용 몰탈을 상기 제 1단계의 콘크리트 단면 보수용 프라이머 층 위에 도포하는 제 2단계와;
c). 실리콘계 아크릴 폴리머 액상으로서 입자 사이즈가 7㎛ ~ 8㎛ 이고, 고형분이 25 중량% 내지 35 중량%로 구성된 콘크리트의 중성화 방지용 프라이머를 준비하고, 상기 제 2단계의 콘크리트 구조물 보수용 몰탈 위에 도포하는 제 3단계와;
d). 망상구조의 아크릴 액상 20 ~ 27 중량%, 탄산칼슘 50 ~ 65 중량%, 물 10 ~ 15 중량%, 안료 3 ~ 5 중량%, 증점제 1 ~ 3 중량%로 구성된 콘크리트의 중성화 방지용 코팅제를 준비하고, 상기 제 3단계의 중성화 방지용 프라이머 위에 도포하는 제 4단계; 를 포함하고 있는 것을 특징으로 한, 콘크리트 구조물의 보수공법.
a). The present invention relates to a method for producing a concrete section repair primer comprising 10 to 20% by weight of an acrylic liquid phase, 10 to 20% by weight of an EVA liquid phase and 60 to 80% A first step of applying 100 g to 200 g per m 2 of surface area;
b). A mortar for concrete structure repair comprising 20 to 25% by weight of alumina ceramic binder, 40 to 55% by weight of silica sand, 10 to 14% by weight of lightweight aggregate, 13 to 18% by weight of calcium carbonate and 1 to 3% A second step of applying the mortar for repairing the concrete structure onto the concrete section repair primer layer of the first stage;
c). A primer for preventing the neutralization of concrete having a particle size of 7 탆 to 8 탆 and a solid content of 25% by weight to 35% by weight as a silicone-based acrylic polymer liquid phase is prepared and applied to a mortar for repairing concrete structures of the second stage ;
d). A coating agent for preventing the neutralization of concrete comprising 20 to 27% by weight of an acrylic liquid phase of a network structure, 50 to 65% by weight of calcium carbonate, 10 to 15% by weight of water, 3 to 5% by weight of a pigment and 1 to 3% by weight of a thickener, A fourth step of applying the composition on the primer for neutralization of the third step; Wherein the concrete structure comprises a plurality of projections.
KR1020140026564A 2014-03-06 2014-03-06 Surface Protector with Network Structure and Repairing Polymer Mortar Composite with Light Weight Aggregate for Concrete Structure Repairing System KR101428995B1 (en)