KR20180064899A - Method of manufacturing natural nacre appendages for clothing - Google Patents

Abstract

The present invention relates to a method for producing natural mother-of-pearl accessories for coating, comprising the following steps: preparing a natural mother-of-pearl film; coating the top of the natural mother-of-pearl film with a transparent film; treating the coated natural mother-of-pearl film with heat and then printing specific patterns or logo on top of the natural mother-of-pearl film; cutting the printed natural mother-of-pearl film in a specific size; and bonding the cut natural mother-of-pearl film onto a body of the accessories.

Description

METHOD OF MANUFACTURING NATURAL NACRE APPENDAGES FOR CLOTHING [0002]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for manufacturing a natural mother-of-pearl accessory, and more particularly, to a method for manufacturing a natural mother-of-pearl accessory such as a clothing button or a label.

In general, natural mother-of-pearl is an expensive material, and work productivity is not good, so that it is difficult to apply it to accessories for covering. Accordingly, artificial knitted fabrics conventionally formed of synthetic resin have been widely used.

Such a conventional dressing accessory (e.g., a synthetic button) may include a sheet plate forming step 100, a primary blank forming step 110, a secondary blank forming step 120, The button embossing step 130, the surface processing step 140, the washing step 150 and the dehydrating and drying step 160, the logo engraving step 170, the coating layer forming step 180, the gilding step fixing step 190, And a surface polishing step (200).

 In the sheet plate forming step 100, a predetermined amount of the pearl film required for a certain amount of synthetic resin is mixed and supplied to a centrifugal molding machine to centrifugally form the sheet plate.

The primary blank forming step 110 is performed by forming the primary blank having a predetermined diameter by the punching process of the sheet plate. The secondary blank forming step 120 is a step of placing the primary blank formed by the punching process in the recess for blanket placement of the primary blank mold so as to bend downward, Thereby forming a blank.

In the button processing step 130, the secondary blank is processed into a spare button having a button shape by an automatic button processing machine so as to have a predetermined button shape, and the surface processing step is performed by polishing the surface of the spare button processed by the automatic button processing machine And the surface processing step 140 completes the synthetic button by processing the surface so that the surface of the spare button processed by the automatic button processing machine becomes glossy.

Then, the washing step 150 is performed by washing with water to remove foreign matter such as powder buried on the surface of the synthetic mother-of-pearl button, and in the dehydrating and drying step, the synthetic mother-child button with moisture is dewatered by a dehydrating dryer, It forms an embroidered button. A logo engraving step 170 may then be added to engrave the company ' s logo on the button to represent a particular brand. Further, a coating layer forming step 180, a gold and silver foil fixing step 190, or a surface polishing step 200 may be selectively performed thereafter.

On the other hand, the conventional artificial apothecary accessories have a problem in that they are less aesthetically pleasing than the natural artificial apotheosis and the commerciality thereof is lowered. Accordingly, there is a growing demand for applying the natural mother apotheosis to the appendages.

However, when such natural mother-of-pearl is applied to an appendage, problems of brittleness and durability are easily broken or damaged. As a result, it is difficult to manufacture accessories for covering using natural mother-of-pearl, and it is difficult to manufacture accessories in the form of labels due to brittleness problems.

Prior Art 1: Korean Patent Publication No. 2001-0095813 (Published on November 7, 2001)

The present invention has been developed in order to overcome the above problems, and it is possible to easily attach a natural mother-of-pearl in the form of a film (thin film) to a button or a label to be applicable as a variety of covering accessories. And to provide a method for manufacturing a natural mother-of-pearl accessory capable of improving the skin.

According to an aspect of the present invention, there is provided a method for manufacturing a natural mother liquor; Coating the natural mother liquor film with a transparent film; Heat-treating the coated natural mother liquor film and printing a pattern or logo on the natural mother liquor film in a predetermined pattern; Cutting the printed natural motherboard film to a predetermined size; And adhering the cut natural mother liquor film to an accessory body.

The coating with the transparent film may be performed by pressing at least one of a polyurethane film, a polyester film, a polyethylene film, a polypropylene film, and a PVC film to at least one side of the natural stretch film at a high temperature.

The accessory body is a pad. The method may further include, after the step of printing the logo, applying the epoxy to the natural mother-of-pearl film and attaching the natural mother liquor film to the pad.

The accessory body may be a button or an accessory, and may further comprise the step of applying the epoxy on the natural mother-of-pearl film after the attachment of the natural mother-of-pearl film to the button or accessory.

According to the present invention, it is possible to prevent the natural mother-of-pearl in the form of a film (film) from being broken or damaged and to improve manufacturing performance and durability while applying it to various ornaments, buttons and labels.

BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a process flow chart showing a manufacturing process of a conventional wearing-
FIG. 2 is a flow chart of a method of manufacturing a natural napkin fitting for covering according to the first embodiment of the present invention,
3 is a flow chart of a method of manufacturing a natural jacket for covering according to the first embodiment of the present invention,
4 is a flow chart of a method of manufacturing a natural mother-of-pearl fitting according to a second embodiment of the present invention, and
5 is a photograph showing a natural mother-of-pearl accessory manufactured by the method of manufacturing the natural mother-of-pearl accessory according to the first embodiment of the present invention.

Hereinafter, preferred embodiments of the present invention will be described with reference to the accompanying drawings. It is to be understood that the terminology used herein is for the purpose of describing particular embodiments of the invention only and is not intended to be limiting.

FIG. 2 is a process flow chart of a method of manufacturing a natural napkin fitting according to a first embodiment of the present invention, and FIG. 3 is a process diagram of a method of manufacturing a natural napkin fitting according to the first embodiment of the present invention.

Referring to FIGS. 2 and 3, a method for manufacturing a natural mother-of-pearl accessory of the present invention comprises a step (S 10) of preparing a natural mother-of-pearl film. In this step S 10, natural mother-of-pearl is prepared in the form of a thin film (film) at a predetermined size.

Next, a natural mother-of-pearl coating step (S 20) is performed in which a transparent film is coated on the upper and lower surfaces of the natural mother-of-pearl film, respectively. As the transparent film, for example, a polyurethane film, a polyester film, a polyethylene film, a polypropylene film, a PVC film and the like can be applied. These transparent films can improve the functional role of protecting the natural mother-of-pearl film, which is relatively weak in embrittlement, from being easily broken, and the aesthetics that make the surface of the natural mother lyra film look shiny. The coating of such a transparent film can be accomplished by hot pressing at a high temperature (for example, 130 to 150 DEG C) using a rolling roll. Thereafter, the coated natural mother liquor film can be heat treated (S 30).

Then, the operation of cutting the natural mother-of-pearl film to a predetermined size is performed, and after the cutting step (S50), a step (S40) of printing a logo or a pattern on the natural mother-of- At this time, the two steps (S 50 and S 40) are interchanged, and a step (S 40) of printing a logo or pattern of a predetermined pattern on the entire coated natural motherboard film is preceded, ) May be made. Therefore, this process sequence can be applied differently depending on manufacturing conditions and conditions. In the printing step, flat type printing, silk printing, pad printing and the like can be applied, and various patterns, letters, patterns and the like can be displayed on the mother film.

Each cut natural mother liquor film may be subjected to an epoxy treatment step (S 75) to apply a reinforcing epoxy. This epoxy treatment step (S75) serves to prevent the natural mother liquor film from being easily broken or damaged from external impact by forming an epoxy layer having a certain thickness on the coated natural mother liquor film.

In addition, it is possible to form a natural volume (outer curved surface) on the natural mother-of-pearl film, thereby giving a three-dimensional feeling. Then, an attachment body attaching step (S60) of attaching an epoxy-treated natural mother-of-pearl film to the attachment body can be performed. At this time, a pad 20 (see FIG. 5) may be applied as an accessory body. Here, the pad 20 may be one of a leather pad, a silicone pad, an artificial leather pad, and a rubber pad.

In the meantime, after the cutting step (S50) as in the above-described embodiment, the epoxy treatment step (S75) may be performed, the attachment body attaching step (S60) may be performed, and the cut natural mother- (S85) may be performed after the epoxy is adhered to its upper surface. Depending on the type of accessory, the epoxy treatment step (S 75 or S 80) may be applied in a different order.

FIG. 5 is a photograph showing the natural mother-of-pearl accessories manufactured by the method of manufacturing the natural mother-of-pearl accessories according to the first embodiment of the present invention. As shown in FIG. 5, So that it can be made into a label-like covering attachment. At this time, the natural mother-of-pearl accessories of the label type are coated with a transparent film on the upper surface, and the logo 35, the character 45 and the sewing mark line 25 may be provided in a printed form. The natural mother liquor film 10 is positioned between the upper transparent film 10 and the lower pad 20 so that the aesthetics of the accessories can be improved.

4 is a process diagram of a method of manufacturing a natural mother-of-pearl accessory according to a second embodiment of the present invention. As shown in FIG. 4, the present invention is a method of manufacturing a natural mother- The laser cutting step S35 is carried out and then the step S85 of attaching the natural mother-of-cut film cut to the body of the button or the cloth accessories (including the ornaments) and the epoxy treatment to the surface thereof is carried out Lt; / RTI > After the epoxy treatment step (S 85), the final product can be produced through a curing process for a certain period of time.

The present invention can prevent the natural mother-of-pearl in the form of a film (film) from being broken or damaged, and can be applied to various ornaments, buttons, and labels, thereby improving manufacturing performance and improving durability.

While the present invention has been particularly shown and described with reference to the particular embodiments thereof, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, It will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention.

10: natural mother-of-pearl film
25: sewing mark
35: Logo
45: Character

Claims (4)

Preparing a natural mother liquor film;
Coating the natural mother liquor film with a transparent film;
Heat-treating the coated natural mother liquor film and printing a pattern or logo on the natural mother liquor film in a predetermined pattern;
Cutting the printed natural motherboard film to a predetermined size; And
And bonding the cut natural mother liquor film to an accessory body. The method according to claim 1,
Wherein the coating with the transparent film comprises:
Wherein at least one of a polyurethane film, a polyester film, a polyethylene film, a polypropylene film, and a PVC film is pressed on at least one surface of the natural stretch film at a high temperature. The method according to claim 1,
Wherein the accessory body is a pad and further comprising the step of applying the epoxy to the natural mother liquor film and then attaching the natural mother liquor film to the pad after printing the logo. Way. The method according to claim 1,
The accessory body is a button or accessory,
Further comprising the step of applying the epoxy on the natural mother-of-pearl film after the natural mother-of-pearl film is attached to the button or accessory.