KR20180055734A - Manufacturing method of window using sheet like process - Google Patents
Manufacturing method of window using sheet like process Download PDFInfo
- Publication number
- KR20180055734A KR20180055734A KR1020170152363A KR20170152363A KR20180055734A KR 20180055734 A KR20180055734 A KR 20180055734A KR 1020170152363 A KR1020170152363 A KR 1020170152363A KR 20170152363 A KR20170152363 A KR 20170152363A KR 20180055734 A KR20180055734 A KR 20180055734A
- Authority
- KR
- South Korea
- Prior art keywords
- glass
- disk
- forming
- disk glass
- sheet
- Prior art date
Abstract
Description
The present invention relates to a method of manufacturing a side window-enhanced window glass using sheet cutting, more particularly, to minimize reflection of light in a chamber portion, to provide a chamfer feeling similar to a CNC polishing surface, The present invention can further improve the process yield and efficiency by further embodying a fixed portion formed to protrude from one side of the glass plate glass and at least one inflection point is formed in the chamfered portion of the side reinforced cover glass window to disperse the stress at the corner portion And more particularly, to a method of manufacturing a side-reinforced window glass using sheet cutting capable of further improving the strength of the window glass.
2. Description of the Related Art In general, touch screen type displays are widely used in various portable terminals such as a mobile phone, a smart phone, a tablet PC, a notebook, a navigation system, a PDA,
The display of such a mobile terminal is usually combined with a window glass on the front surface of the display in order to prevent damage due to an external impact and protect the internal touch screen panel due to the touch.
The window glass is used not only for protecting a display of a portable terminal as described above but also for protecting a display panel of various electrical and electronic products or for protecting a camera module provided in a portable terminal .
2. Description of the Related Art [0002] In recent years, there has been a demand for differentiated designs along with a demand for various functions of such portable terminals.
The window glass is not only coupled to the display panel to protect displays of various portable terminals, household appliances, and cafes, but also may be coupled to a camera lens module to protect the camera lens formed on the portable terminal, Is also being used.
A method of manufacturing such a window glass is a method in which a disk glass is cut into a predetermined shape and a functional layer, an antireflection layer, a moisture removal layer, an antistatic layer, a protective layer, a print layer, an electrode layer, (Hereinafter, referred to as 'function layer') for protecting the touch screen panel, the objective lens of the camera or the sensor module of the hometown key button by being coupled to the uppermost layer of the display or camera lens module.
Conventional window glass processes disc glass in a cell unit and chemically strengthens each processed cell unit substrate to form a functional layer. This is because the process is performed on a cell-by-cell basis, so that the defective ratio is high, There is a drawback that it takes.
In order to solve these problems, there has been conventionally used a disk unit process in which a disk glass is chemically reinforced and a functional layer is formed on a reinforced window cover glass substrate, followed by cutting and chamfering.
However, in the above-mentioned prior art, the upper and lower surfaces are maintained in a reinforced state during the cutting and chamfering process of the disk glass, but after the cutting, the sides are not reinforced, which causes a decrease in the impact strength, There is a problem that it is easily broken by impact.
In addition, the corner portion of the window glass manufactured by such a method is concentrated in the stress and causes the strength to be lowered.
SUMMARY OF THE INVENTION The present invention has been made in view of the above problems, and it is an object of the present invention to provide a side reinforced window using sheet cutting capable of minimizing reflection of light in a chamber portion and giving a chamfer feeling similar to a CNC- And to provide a method of manufacturing a glass.
It is another object of the present invention to provide a method for manufacturing a side window glass which can further improve the process yield and efficiency by further embodying a fixing part formed to protrude from one surface of the disc glass when forming the functional layer.
It is still another object of the present invention to provide a side-reinforced cover glass window which is capable of forming at least one inflection point in a chamfered portion of a side-reinforced cover glass window to disperse the stress at the corner portion, To provide a method of manufacturing a window glass.
According to another aspect of the present invention, there is provided a method of manufacturing a side window-enhanced window glass using sheet cutting, the method comprising: forming a mask layer on the upper and lower sides of a glass plate; Forming a sheet cutting portion penetrating up and down the exposed disc glass region without forming a breaking line by laser cutting the exposed disc glass region outside the mask layer region; Removing the mask layer and strengthening the disk glass to strengthen the side portion of the disk glass through the sheet cutting portion; And forming a cell unit window glass by cutting the disk glass using a laser or by applying a predetermined pressure to each cell unit, wherein wet etching is performed on the disk glass having the sheet cutting unit, A chamfer is further formed in the glass region, and a wet etching process for an anti-glare (AG) process is further performed on the chamfered portion.
According to another aspect of the present invention, there is provided a method of manufacturing a side-reinforced window glass using sheet cutting, the method comprising: forming a mask layer on the upper and lower sides of a glass plate; Forming a sheet cutting portion penetrating up and down the exposed disc glass region without forming a breaking line by laser cutting the exposed disc glass region outside the mask layer region; Removing the mask layer and strengthening the disk glass to strengthen the side portion of the disk glass through the sheet cutting portion; Forming functional layers on one surface of the disk glass in units of cells; And forming a cell unit window glass by cutting a disc glass on which the functional layer is formed by using a laser or by applying a predetermined pressure to each cell unit, wherein the functional glass is formed on one side of the disc glass And a fixing part protruding from one side of the glass plate at the cell unit window glass boundary part.
According to another aspect of the present invention, there is provided a method of manufacturing a side window-enhanced window glass using sheet cutting, the method comprising: forming a mask layer on the upper and lower sides of a glass plate; Forming a sheet cutting portion penetrating up and down the exposed disc glass region without forming a breaking line by laser cutting the exposed disc glass region outside the mask layer region; Removing the mask layer and strengthening the disk glass to strengthen the side portion of the disk glass through the sheet cutting portion; And forming a cell unit window glass by cutting the disk glass using a laser or by applying a predetermined pressure to each cell unit, wherein wet etching is performed on the disk glass having the sheet cutting unit, A chamfer is further formed in the glass region, and the chamfer portion has at least one inflection point.
Here, the fixing portion may be formed at a corner of the cell unit window glass.
Preferably, a chamfer is further formed on the exposed disk glass region by performing wet etching on the disk glass on which the sheet cutting portion is formed.
In addition, the pan glass portion and the chamfer portion may be formed in the edge portion of the disk glass by a wet etching process, and the inflection point may have a longitudinal sectional shape in which the direction of bending is changed at least once.
It is preferable that the number of inflection points is controlled by control of an etching factor or by a plurality of wet etching processes according to different etching factors.
In addition, it is preferable that the etch rate is controlled by the etching solution concentration, the temperature of the etching solution, and the etching time.
Further, it is preferable that the edge portion of the chamfer portion is rounded.
The curvature of the inflection point is preferably 0.01 mm to 100 mm.
The forming of the mask layer may be performed by a photolithography process by laminating DFR (Dry Film Photoresist) on the upper and lower portions of the reinforced disk glass.
It is preferable that the chamfer portion is formed at a depth of about 0.5% to 25% from the upper and lower surfaces of the disk glass.
Further, it is preferable that the etching amount in the horizontal direction is 100 +/- 50 mu m and the etching amount in the vertical direction is 60 + 30 mu m / -20 mu m on the surface of the disk glass.
Preferably, the chamfer portion is formed in a different shape on the upper side and the lower side of the glass substrate.
In addition, the chamfered portion may be asymmetric up or down or right and left.
In addition, the strengthening of the disk glass is preferably chemical tempered at a temperature of 350 ° C to 450 ° C using potassium nitrate (KNO 3 ).
In addition, it is preferable that the cell unit window glass is implemented on the disc glass so as to be spaced apart from each other, or continuously without interval.
In addition, it is preferable that the step of forming the sheet cutting portion has a different laser spot spacing in a corner portion and a straight portion of the cell.
Also, the window glass can be used in any one of a display window, a camera lens window, and a home key button unit.
According to the method for manufacturing a side window-enhanced window glass using sheet cutting according to the present invention, a chamfer formed by wet etching is formed on a disc glass having a sheet cutting portion formed therein, Anti-glare treatment, thereby minimizing the reflection of light and providing a chamfering feeling similar to that of the CNC polishing surface.
In addition, it is also possible to use a sheet cutting process (SLP, Sheet Like Process) in which a sheet cutting portion is formed on a disk glass and a sheet process can be carried out while holding the disk glass, By further implementing the government, there is also an advantage in that the mass productivity and yield are remarkably improved and the price competitiveness is excellent.
Further, at least one bending direction (inflection point) is formed in the chamfered portion of the side-reinforced cover glass window so that the stress at the corner portion can be dispersed, thereby further improving the strength of the window glass.
In addition, the shimmering and reflection of the chamfered portion can be minimized, and the coupling and detachment of the camera module with the peripheral structure can be facilitated and firmly fixed.
In addition, in the conventional sheet process, the side surface, which is the cut surface of the disc glass, is not reinforced, and the lateral strength is weak. However, since the window glass using the sheet cutting according to the present invention can simultaneously implement the side surface strengthening while maintaining the sheet state, And strength improvement is excellent.
FIGS. 1 to 4 are schematic views illustrating a method of manufacturing a side-reinforced window glass using sheet cutting according to
5 is a schematic view illustrating a chamfer according to an embodiment of the present invention.
FIG. 6 is a view showing the scattering degree of light in the conventional chamfer portion, FIG. 6 (b) showing the scattering degree of light in the chamfer portion by the additional wet etching process according to the embodiment of the present invention, And FIG. 5C is a diagram showing the degree of scattering of light in the chamber portion by the additional wet etching process according to an embodiment of the present invention.
FIGS. 7 and 8 are schematic views illustrating a method of manufacturing a side-reinforced window glass using sheet cutting according to another embodiment of the present invention.
9 is a schematic view showing a fixing unit according to the present invention.
10 is a schematic view of a case where a substrate masked by a conventional mask layer is etched by a wet etching process.
11 and 12 are views showing vertical cross-sectional shapes of a window glass according to an embodiment of the present invention.
13 is a photograph showing a state in which cells are separated from each other in a stack or between cells along a crack between holes and holes according to the present invention.
FIG. 14 is a view showing SEM / EDS measurement results of the K ion concentration of the side reinforcing layer according to the present invention. FIG.
FIG. 15 is a side view of a cell after punching according to the present invention. The left SEM photograph is a photograph of a sheet type surface, and the right side is a cell type surface photograph.
16 and 17 are graphs showing the distribution of the side K concentration after the secondary reinforcement according to the present invention.
The present invention may be embodied in many other forms without departing from its spirit or essential characteristics. Accordingly, the embodiments of the present invention are to be considered in all respects as merely illustrative and not restrictive.
The terms first, second, etc. may be used to describe various components, but the components should not be limited by the terms.
The terms are used only for the purpose of distinguishing one component from another. For example, without departing from the scope of the present invention, the first component may be referred to as a second component, and similarly, the second component may also be referred to as a first component.
It is to be understood that when an element is referred to as being "connected" or "connected" to another element, it may be directly connected or connected to the other element, .
On the other hand, when an element is referred to as being "directly connected" or "directly connected" to another element, it should be understood that there are no other elements in between.
The terminology used in this application is used only to describe a specific embodiment and is not intended to limit the invention. The singular expressions include plural expressions unless the context clearly dictates otherwise.
In the present application, the terms "comprises", "having", "having", and the like are intended to specify the presence of stated features, integers, steps, operations, components, Steps, operations, elements, components, or combinations of elements, numbers, steps, operations, components, parts, or combinations thereof.
Unless defined otherwise, all terms used herein, including technical or scientific terms, have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs.
Terms such as those defined in commonly used dictionaries are to be interpreted as having a meaning consistent with the contextual meaning of the related art and are to be interpreted as either ideal or overly formal in the sense of the present application Do not.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings, in order that the present invention may be easily understood by those skilled in the art. .
Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings.
≪ Example 1 >
As shown in FIGS. 1 and 3, a method of manufacturing a side-enhanced cover glass window using sheet cutting according to a first embodiment of the present invention includes the steps of forming a mask layer on the upper and lower sides of a glass plate, Forming a sheet cutting portion penetrating up and down the exposed disk glass region without forming a breaking line by performing sheet cutting of an exposed disk glass region outside the mask layer region with a laser; And reinforcing the side glass portion of the disk glass through the sheet cutting portion by reinforcing the disk glass; and cutting the reinforced disk glass by a laser or using a predetermined pressure to form a cell-based cover glass window The method comprising the steps of:
First, prepare a disc glass.
The disc glass is reinforced by a strengthening process, which will be described later, using those that are not reinforced.
In order to check whether or not the original glass contains scratches or foreign substances, both sides of the original glass are polished and cleaned in order to improve surface precision and transparency.
Then, a mask layer is formed on the upper and lower portions of the disk glass in units of cells.
Preferably, the mask layer is formed by a photolithography process by laminating DFR (Dry Film Photoresist) on the upper and lower portions of the disk glass, and forms a mask layer having a predetermined interval. As a method of forming the mask layer, conventionally known method such as screen ink may be used.
FIG. 1 shows that the mask layer is continuously formed on the disk glass without forming a dummy section in the formation of the mask layer on a cell-by-cell basis. FIG. 3 shows a dummy section that is spaced apart from each other by a certain degree.
Thus, the cell-unit cover glass windows finally manufactured can be realized on the disc glass continuously without a gap or spaced apart from each other on the disc glass.
This can be achieved by adjusting the interval between the cell-based cover glass windows according to the storage and supply specifications of the product according to the size of the cell-based cover glass window. Generally, as the size of the cell-based cover glass window is smaller, Can be supplied in a formed form.
Then, the exposed disc glass region outside the mask layer region is subjected to sheet cutting by laser to form a sheet cutting portion in the exposed disc glass region.
Wherein the sheet cutting portion is formed in the exposed disc glass region without forming a mask layer between the mask layer regions with the laser, and the sheet cutting portion forms a breaking line by the laser with the exposed disc glass region And cracks penetrating the upper and lower portions are formed.
This is because the disc glass regions on both sides of the sheet cutting section made of cracks are engaged with each other in a zigzag form or in the same manner as the screw engagement so that the disc glass regions on both sides of the sheet cutting section are held in mutual engagement force, The sheet is maintained in a state of being formed even though the sheet cutting portion composed of cracks is formed.
As described above, in the present invention, it is referred to as sheet cutting in which only a crack is formed without forming a breaking line due to the laser and is maintained in a sheet state.
Therefore, in the present invention, laser cutting is performed without further forming a breaking line, but the original glass can be kept in a sheet state to enable a process on a sheet (hereinafter referred to as "SLP " Is the most important feature.
When the mask glass is removed and the glass plate is cleaned and then the glass plate is reinforced, the side surface of the glass plate is reinforced through the sheet cutting portion. The upper and lower surfaces of the glass plate And a reinforcing layer of about 20 to 90 mu m is formed on the side surface portion.
Specifically, the tempering process is performed by using chemical nitrate (KNO 3 ) at a temperature of 350 ° C to 450 ° C. After the tempering, the steel is slowly cooled to prevent cracking. The disc glass is cleaned.
That is, the disc glass which is in the state of the present sheet state is strengthened. In this case, not only the upper and lower surfaces of the disc glass but also the side surfaces of the disc glass, that is, the cut surface are strengthened accordingly.
This strengthening process is performed by the SLP process. Since the reinforcing process is performed while the disc glass is maintained in a sheet state, the sheet process can be performed, thereby improving the productivity and durability as compared with the conventional cell type process.
In other words, in the conventional sheet process, the side surface, which is the cut surface of the disk glass, is not reinforced and the lateral strength is weak. However, since the SLP method according to the present invention can simultaneously perform side strengthening while maintaining the sheet state, It can be improved.
When the process is completed with the disk glass kept in the state of the sheet until the reinforcing process, a breaking line is formed on the disk glass by using a laser, and the breaking line is formed and cut in a cell unit or a certain pressure is applied, Thereby forming a cell-unit cover glass window.
≪ Example 2 >
Example 2 according to the present invention is similar to Example 1 except that reinforced disc glass is used and a chamfer is further formed after the formation of the sheet cutting portion. .
FIG. 2 shows that the mask layer is continuously formed on the disk glass without forming a dummy section in the formation of the mask layer on a cell-by-cell basis, and FIG. 4 shows a dummy section that is spaced apart from each other by a certain degree.
Compressive Stress (CS) is 300MPa ~ 900MPa and reinforced glass with DOL (Depth of Layer) 40㎛ or less is used for strengthened glass plate.
As in
In the wet etching, the disk glass is fully immersed in the etching solution by dipping, so that the etching is further performed on the portion where the sheet cutting portion is formed.
In this case, the disk glass still maintains the sheet state, and the etching layer formed by the wet etching is formed at a depth of about 0.5% to 25% from the upper and lower surfaces of the disk glass, So that the sheet state can be maintained continuously.
Here, the wet etching process is performed by treating the etching solution containing HF at a temperature of 20 ° C to 30 ° C for 5 to 30 minutes, and exposing the disk glass having the mask layer formed thereon to the etching solution for a predetermined time And a chamfer portion is formed between the mask layers.
When forming the chamfered portion by the wet etching process, micro-cracks are generated on the cut surface due to the sheet cutting portion by the physical laser cutting in the previous process. When the etching is chemically performed on the laser cutting portion, micro-cracks are smoothed So that the etching of the disk glass in the cell unit proceeds while the side surface is strengthened to a certain extent.
Meanwhile, it is preferable to further perform a wet etching process for the anti-glare (AG) process on the chamfered portion.
Generally, FIG. 5 shows a chamfer according to an embodiment of the present invention, and a shiny phenomenon occurs due to reflection of light on an etched surface due to a height difference of a chamfered portion (chamfered etching portion) in a dotted line portion.
FIG. 6 shows a case where a cell-based cover glass window according to the present invention is used as a camera lens window in an embodiment. FIG. 6 (a) shows the scattering degree of light in a conventional chamber portion, The light from the mounting portion is reflected to deteriorate the aesthetics on the rim. Further, by performing the wet etching process for the AG process, the light in the chamfer portion is dispersed so that the rim portion is similar to the CNC polishing surface Give it a sense of sight.
In the wet etching process for the AG process according to the present invention, a hydrofluoric acid-based etching solution is used as one embodiment and dipped at a temperature of 22 ± 5 ° C for about 25 seconds.
FIG. 6 (b) shows the degree of light scattering in the chamfered portion by the additional wet etching process according to an embodiment of the present invention, and FIG. 6 (c) And the degree of light scattering in the chamfered portion (left) and the chamfered portion (right side) of the improved type in which the additional wet etching process is performed according to an embodiment of the present invention.
As shown in the figure, when the additional wet etching process is performed, the reflection of light due to the AG effect minimizes the reflection of light in the chamber portion, giving a chamfering feeling similar to that of the CNC polishing surface.
When the mask layer is stripped and the disk glass is further strengthened, the side surface of the disk glass is also strengthened through the sheet cutting portion. By further strengthening the upper and lower surfaces of the disk glass, And a reinforcing layer having a thickness of about 20 mu m to about 90 mu m is formed on the side surface portion.
Specifically, the additional strengthening step is performed by using chemical nitrate (KNO 3 ) at a temperature of 350 ° C to 450 ° C. After the strengthening, it is gradually cooled to prevent cracking. When finished, clean the original glass.
That is, the original glass sheet which is in the state of the current sheet is further strengthened. In this case, not only the upper and lower surfaces of the glass plate, but also the side surface of the glass plate, that is, the cut surface are strengthened accordingly.
This additional strengthening step is performed by the SLP method, and the additional strengthening step is performed while the disc glass is maintained in the sheet state, so that the sheet process can be performed, thereby improving the mass productivity and durability as compared with the conventional cell type process.
In other words, in the conventional sheet process, the side surface, which is the cut surface of the disk glass, is not reinforced and the lateral strength is weak. However, since the SLP method according to the present invention can simultaneously perform side strengthening while maintaining the sheet state, It can be improved.
≪ Example 3 >
A mask layer is formed on the upper and lower portions of the disk glass in units of cells and the exposed disk glass regions outside the mask layer region are subjected to sheet cutting by laser to form upper and lower portions of the exposed disk glass region The present invention provides a disc glass sheet panel in which a through cut sheet cutting portion is formed, the mask layer is removed, and the disc glass is strengthened to reinforce the side portion of the disc glass through the sheet cutting portion.
<Example 4>
As shown in FIGS. 7 and 8, the fourth embodiment of the present invention is an additional process for the laser-cut cell-based cover glass window according to the first or second embodiment, Forming a cell unit window glass by forming a functional layer on a cell-by-cell basis, and cutting the disk-shaped glass on which the functional layer is formed by using a laser or by applying a predetermined pressure to cut the cell unit cell, And the functional layer is further formed on the one surface of the plate glass and the fixing portion formed to protrude from one surface of the plate glass at the cell unit window glass boundary portion.
Further, reinforced disc glass is used, and after formation of the sheet cutting portion, a chamfer portion is further formed.
In this embodiment, a pattern may be further formed on the front, back, or both surfaces of the disk glass before the disk glass is strengthened. That is, it is possible to further form an etching pattern by dry etching or wet etching after the formation of the cell unit mask layer or after the formation of the sheet cutting portion. In this case, when applied on a display window, a haze effect And to give a sense of a three-dimensional pattern to the periphery except for the transmissive portion when applied to a camera lens window.
A functional layer is formed on one side of the side-strengthened disk glass in units of cells. Even in this case, the disc glass is maintained in a sheet state, and the formation of the functional layer is performed by the SLP process, so that the productivity and the yield are significantly improved as compared with the conventional case where the functional layer is formed on a cell-by-cell basis.
The functional layer is formed as a single layer or a plurality of layers in accordance with the intended use such as an antireflection layer, a moisture removal layer, an antistatic layer, a protective layer, a decorative layer, a print layer, an electrode layer and a metal layer. A decorative layer, a printing layer, an electrode layer, an anti-static layer, a protective layer, and the like for forming a bezel, etc., can be formed. When used in a camera lens window, a printing layer, a decorative layer, Or an antistatic layer, an antireflection layer, or the like may be formed on the front surface or the back surface.
Further, in the case of the camera lens window, a print layer, a decorative layer, a color layer, a deposition layer, and the like may be formed on the periphery of the transmissive portion, except for a transmissive portion through which light is transmitted.
Here, the functional layer may be formed on one surface of the disk glass at the time of forming the functional layer, and the fixing portion may be formed so that the functional layer protrudes from one side of the disk glass at the cell unit window glass boundary portion.
This is because unintentional intermittent intermittent cell-based window glass escapes during the other process before completely separating and separating the cell unit window glass from the disk glass in which the sheet cutting portion is formed, resulting in a decrease in the process yield, In order to prevent the occurrence of the problem.
The fixing part protrudes from the cell unit window glass boundary part when the functional layer is formed, and the functional layer is formed to be extended. That is, the fixing portion is also formed at the time of forming the printing layer, the decorative layer, the color layer, the deposition layer, and the like, which is realized by a separate pattern continuous to the functional layer at the time of coating, So that the ink used for the functional layer covers the cutting line to fix the cell.
Thus, the fixing unit prevents the cell unit window glass from being separated from the disc glass uninterruptedly, thereby improving the process yield and efficiency.
As shown in FIG. 9, it is preferable that the fixing portion is formed at the corner portion in the case of the rounded square shape of the cell unit window glass. This is because as the protruding area of the fixing part is wider, secondary appearance defects due to ink scraping may occur at the time of complete separation of the cell unit window glass, and there is room for defective appearance of the straight line section due to the fixing part. Which is difficult to be identified.
Since the formation of the chamfered portion is substantially the same as that of the above-described embodiment, further detailed description will be omitted.
7 and 8, the functional layer is covered on the sheet cutting area. In this case, the fixing part is not formed on the entire sheet cutting area, Likewise, it is formed in a part of the corner portion to prevent the cell from falling off on the original glass plate.
When the process is completed while the disk glass remains in the sheet state until the functional layer is formed, a breaking line is formed on the disk glass using a laser to cut the cell unit or apply a certain pressure to the cell unit To form a cell unit window glass.
≪ Example 5 >
In other words, when the substrate masked by the mask layer is etched by the wet etching process, it has an isotropic etching tendency as shown in Fig. 10, and the etching rate of the masked edge portion in the vicinity of the masking edge portion The etched surface becomes tau (tau) shape, which may cause a decrease in the strength of the product.
Accordingly, in the present embodiment, the chamfered portion is formed at the corner of the glass substrate (disc glass) shaped into a unit of cells by the sheet cutting step, and the sheet cutting portion formed along the edge portion of the glass substrate has a stress The edge portion of the chamfered portion is formed to be rounded due to an increase in the etching amount at this portion during the wet etching process for forming the chamfered portion.
That is, when the wet etching process for forming the chamfered portion according to the present invention is performed, the etching amount is relatively increased at the portion where the stress is concentrated, whereby the edge portion of the chamfered portion has the shape of the edge portion of the conventional FIG. The problem of the strength reduction at the edge portion is minimized even if the wet etching process for forming the chamfer portion is performed.
The window glass processed by such a process includes a glass substrate and a chamfer formed at a corner of the glass substrate by a wet etching process. The chamfer is etched to a predetermined depth from the surface of the glass substrate, And has a longitudinal section shape in which the direction of bending is changed at least once.
The wet etching is performed by dipping or spraying, and the etching is performed to a region where the sheet cutting portion is formed or a peripheral portion thereof.
The shape of the chamfer portion is determined by control of the etching rate and the etching amount according to the etching factor such as the concentration of the etching solution, the temperature, the exposure time to the etching solution (the dipping time in the case of dipping, the discharging time in the case of spraying) .
That is, the higher the concentration and temperature of the etching solution, the higher the etching rate, and the longer the exposure time, the larger the etching amount. These factors are taken into consideration to determine the shape of the chamfer portion.
In this case, the disc glass still maintains the sheet state, and the chamfered portion is formed by etching to a predetermined depth from the surface of the glass substrate, and the etching layer formed by the wet etching is 0.5% to 25% So that the sheet state can be continuously maintained even in the subsequent process.
Specifically, it is preferable that the chamfer portion has an etching amount of 100 ± 50 μm in the horizontal direction and an etching amount of 60 + 30 μm / -20 μm in the vertical direction on the surface of the disk glass.
Here, the wet etching process is performed by treating the etching solution (
The chamfered portion formed by the wet-etching process proceeds by such a sheet cutting process has a vertical sectional shape in which the direction of bending is changed at least once.
≪ Example 6 >
The chamfered portion of the side reinforced cover glass window manufactured according to
The number of times the shape of the chamfered portion or the direction of bending of the chamfered portion is changed may be controlled by controlling the etching factor such as the concentration of the etching solution, the temperature of the etching solution and the etching exposure time, or a plurality of wet etching Can be controlled by the progress of the process.
That is, the shape of the chamfered portion can be controlled by controlling the etching rate and the etching amount by controlling the etching factor or performing a plurality of wet etching processes having different etching factors.
The shape in which the bending direction of the chamfered portion of FIG. 11 is changed twice is formed by setting the concentration of the etching solution to be high because the etching amount should be large. The shape in which the bending direction of the chamfered portion of FIG. 12 is changed three times is small, The concentration of the etching solution is set to be relatively low, and the etching is performed by the first wet etching step and the second wet etching step with different concentrations of the etching solution.
In addition, it is preferable that the curvature at the point where the bending direction changes is 0.01 to 100 mm, and it is possible to disperse the stress concentration at the edge portion of the glass substrate and the edge portion of the chamfered portion, If it is out of the range, it will not serve as a chamfer part.
In the case of a cover glass window having an inflection point, it is possible to minimize the sparkle and reflection of the corner portion (chamfer portion), and to easily attach and detach from the peripheral structure during the coupling on the front surface of the display or the camera module, .
The chamfer portion may be formed in different shapes on the upper and lower sides of the glass substrate according to a product model specification, and it is also possible by controlling the etching factors.
≪ Example 7 >
The first reinforced disc glass is prepared and cut by a laser to cut the cell, but it is designed so that the cell can not be separated in a sheet state but can be post-processed into a sheet state.
A mask layer is formed on the upper and lower portions of the disk glass in units of cells, and the exposed portions are cut by a laser sheet.
As shown in Fig. 13, the hole size of the laser is 0.2 to 2.0 mu m in diameter, and the pitch between holes is 1 to 4 mu m. In this manner, regular holes are cut and cut, And a certain level of external pressure is required to separate the sheet from the sheet. When a laser or an external pressure is applied, the cells are separated from the dummy or between the cells along the crack shown in FIG.
Thereby forming a sheet cutting portion and forming a chamfered portion.
The chamfer part is immersed in a mixed solution after cutting the laser sheet by a wet etching method, and the etching solution penetrates between the dummy and the cell, or between the cell and the cell. Thereby forming a chamfered portion.
The chamfered portion is applied to prevent window cracking due to chipping and to prevent an assembly failure due to overprinting.
The chamfer portion was processed to have an etching amount of 100 +/- 50 mu m in the upper and lower portions in the horizontal direction and an etching amount of 60 + 30 mu m / -20 mu m in the vertical direction.
After that, secondary reinforcement is carried out through the sheet cutting part. That is, the primary strengthened glass plate is cut by using a laser, and when the chamfered portion is formed, the weak side portion is exposed to the outside.
The secondary reinforcement process is to reinforce the exposed side of the exterior. In the secondary strengthening step, the reinforcement liquid penetrates through the sheet cutting portion to generate a K ion exchange reaction, and the side portions are strengthened by the reaction.
The second strengthening condition was set at 400 ° C for 2hrs and 2hrs for the second strengthening condition. CS 500 to 580 MPa before strengthening, CS 809 MPa after strengthening at DOL 16 ~ 20um, DOL 37.9 um and CT 94.7 MPa, respectively. CS 825MPa, DOL 40um, and CT 106MPa, which were measured in cell type processing, were similar to each other. 14 is a SEM / EDS measurement result of the K ion concentration of the side reinforcing layer, and the K concentration value is almost the same as that of the cell type.
And after the secondary strengthening process to strengthen the side, the cover glass window is coated with color, pattern, etc. by the printing process.
In the case of the conventional cell type, a cell is placed on a printing jig and printing is performed on a separate printing screen to coat a color pattern or the like on the cell. However, the SLP (Sheet Like Process) A printing process such as silk screen printing becomes possible.
Once the printing is completed, AR coating and AF coating are carried out as needed. In this process, the sheet can be put in a sheet state without any separate jig seaming / desorption process.
The sheet glass held in such a sheet state is separated in a cell unit. In the process of separating the sheet unit sample in which the printing and deposition processes have been completed in a cell unit, the sheet is pressed with a certain pressure, specifically, Push to disconnect the cell.
When the cell separation is completed, the separation jig and the sheet are removed and the protective film is attached to the cell. The protective film is attached to prevent scratches and foreign matter from entering, and it is possible to attach a protective film on both the front and back sides.
The perforation load for separating the cells from the sheet was 0.75 Kgf or more, and the cell weight was 0.1 g. The side roughness after the cell piercing was as shown in Fig. The left SEM photograph is a photograph of a sheet type surface and the right side is a photograph of a cell type surface. The surface roughness was measured using Mitutoyo SJ500. The measurement speed was 20 ㎛ / sec and 600 ㎛ distance, and it was confirmed that the side surface roughness of the sheet type specimen was more compact than the cell type. In the case of the sheet type specimen, the Ra value was 0.6 to 1.3 탆, and the Ra value of the cell side realized by the CNC machining of the cell type under the same conditions was found to be 1.7 탆.
On the other hand, unlike the cell type which is strengthened after the cell cutting, in the case of the sheet type, there is a problem that the nascent screen is exposed to the outside after cutting the glass fabric to which the primary reinforcement is applied. And the K concentration distribution before and after the second reinforcement was confirmed to confirm whether the reinforcement was side strengthened.
FIG. 16 is a graph showing the distribution of the side K concentration after the secondary reinforcement. It can be seen that the surface K concentration is increased after the reinforcement compared to the reinforcement.
As shown in Fig. 17, the DOL of the upper surface was confirmed to be 37.9 mu m, and the concentration of K at this time was 6%. In the same way, when the DOL with the concentration of 6% is found in the side graph, it has an intersection at 20 μm. Therefore, the reinforcing depth of the side surface is estimated to be 20 μm.
The most important meaning of the process improvement from the cell type to the sheet type is that the laser, etching, strengthening, and printing / deposition processes can be performed on a sheet basis in comparison with the cell type which is individually processed. In addition, it was possible to reduce the process loss and the process of placing and detaching each cell in the jig, and it was possible to reduce the process loss, and the production efficiency of the sheet type was higher than that of the cell type production. In the case of the sheet type, the manufacturing time was improved by 20% to 30% by 12.31 seconds.
In addition, it was confirmed that the side surface roughness Ra of the product processed by laser cutting and etching for forming a sheet cutting portion was not greater than Ra 1.7 ~ Other reliability Single component test, distribution test, camera image quality test and dimensional measurement result were shown to be different from those of the cell type manufacturing process.
≪ Example 8 >
(First and second reinforced sheets) reinforced according to Examples 1 to 2, particularly Example 2 were used (the upper and lower surfaces of the disk glass were strengthened), and the sheet cut portions When performing the secondary reinforcement (secondary reinforcement, additional reinforcement), the upper and lower surfaces of the disc glass as well as the side surfaces of the disc glass, i.e., the cut surface, are strengthened.
The strengths at the side portion and the surface portion due to the primary and secondary reinforcement have different profiles, respectively. As a result, it can be seen that the stress and strain at the side portion and the surface portion have different values.
≪ Example 9 >
The chamfered portion manufactured according to an embodiment of the present invention may be asymmetric in the up and down direction, asymmetric in the left and right direction, and angle of the chamfered portion may be formed in various shapes so that the chamfered portion can be applied in various forms according to the difference of the peripheral structure or the inner / do.
The shape control of the chamfer portion can be controlled by the etching amount, that is, the concentration of the etching liquid, the temperature, the exposure time, etc., and can also be controlled by the dipping method and the like.
≪ Example 10 >
The cover glass window manufactured according to an embodiment of the present invention may have a pattern in which the upper and lower surfaces are formed in a non-patterned pattern, only the upper surface is patterned, only the lower surface is patterned, or both the upper and lower surfaces are patterned.
That is, a non-pattern, a top pattern (exposure pattern, front pattern), a bottom pattern (back pattern), a double-sided pattern, or the like can be formed.
The pattern may be formed after removing the mask layer, or may be formed after strengthening the side surface, and may be formed in various forms according to specifications of the portable terminal or the electric / electronic product to be applied.
The pattern may be formed in various forms by sequentially performing dry etching or wet etching or a combination thereof.
Further, after the side portion is strengthened, the pattern can be formed by printing or vapor deposition.
The pattern may be formed on the entire surface of the cover glass window, but may be partially formed according to product specifications. In the case of the camera cover glass window, it may be partially or wholly formed in the periphery of the transmissive portion excluding the transmissive portion.
After forming such a pattern, a vapor deposition layer, a printing layer, a color layer (functional layer), or the like can be further formed to improve the three-dimensional effect and the aesthetics of the pattern as needed. May not be necessary.
≪ Example 11 >
The shape of the chamfered portion manufactured according to one embodiment of the present invention can be controlled in various ways.
And can be controlled by various methods such as wet etching, dry etching, multi-etching combined with an etching method such as CNC, selective etching selectively formed in a specific region, and the like.
That is, the upper surface of the chamfered portion may be subjected to wet etching, the lower surface thereof may be subjected to dry etching, or may be subjected to various processes such as wet etching, CNC, CNC, wet etching, or dry etching.
≪ Example 12 >
The shape of the chamfered portion manufactured according to an embodiment of the present invention can be controlled to control or guide the side strengthening penetration path, depth, and shape during the side strengthening process.
That is, the degree of crack spreading of the sheet cutting portion after formation of the chamfered portion is controlled to control the side strengthening depression path and the like.
Whereby the degree of strengthening of the side portion can be controlled.
As described above, according to the present invention, a cracking sheet cutting portion penetrating the upper and lower portions of the disk glass is formed using a laser without forming a breaking line, and then the reinforcing is performed, and the reinforcing process is carried out while holding the disk glass Sheet process can be performed, and the mass productivity and the yield are drastically improved as compared with the conventional cell type process, resulting in excellent price competitiveness.
In addition, in the conventional sheet process, the side surface, which is the cut surface of the disc glass, is not reinforced, and the lateral strength is weak. However, since the SLP method according to the present invention can simultaneously perform side strengthening while maintaining the sheet state, .
In addition, the cover glass window in the present invention can be used not only for use in a display window for protecting a touch screen panel, but also for protecting the internal devices with a transparent window, It can be used anywhere.
It is to be understood that the invention is not limited to the form set forth in the foregoing description. Accordingly, the true scope of the present invention should be determined by the technical idea of the appended claims. It is also to be understood that the invention includes all modifications, equivalents, and alternatives falling within the spirit and scope of the invention as defined by the appended claims.
Claims (20)
Forming a sheet cutting portion penetrating up and down the exposed disc glass region without forming a breaking line by laser cutting the exposed disc glass region outside the mask layer region;
Removing the mask layer and strengthening the disk glass to strengthen the side portion of the disk glass through the sheet cutting portion; And
Forming a cell unit window glass by cutting the disk glass using a laser or by applying a constant pressure to each cell unit,
Wet etching is performed on the disk glass having the sheet cutting portion formed therein to form a chamfer in the exposed disk glass region and a wet etching process for AG (anti-glare) process is further performed on the chamfered portion Wherein the glass sheet is a glass sheet.
Forming a sheet cutting portion penetrating up and down the exposed disc glass region without forming a breaking line by laser cutting the exposed disc glass region outside the mask layer region;
Removing the mask layer and strengthening the disk glass to strengthen the side portion of the disk glass through the sheet cutting portion;
Forming functional layers on one surface of the disk glass in units of cells; And
And forming a cell unit window glass by cutting the disc glass on which the functional layer is formed by using a laser or by applying a predetermined pressure to each cell unit,
Wherein the functional glass is further provided on one side of the disk glass and the fixing part formed to protrude from one end of the disk glass at the boundary between the disk glass and the cell unit window glass. ≪ / RTI >
Forming a sheet cutting portion penetrating up and down the exposed disc glass region without forming a breaking line by laser cutting the exposed disc glass region outside the mask layer region;
Removing the mask layer and strengthening the disk glass to strengthen the side portion of the disk glass through the sheet cutting portion; And
Forming a cell unit window glass by cutting the disk glass using a laser or by applying a constant pressure to each cell unit,
Wherein a chamfer is formed in the exposed disk glass region by performing wet etching on the disk glass having the sheet cutting portion formed therein and the chamfer portion has at least one inflexion point. A method of manufacturing a window glass.
Wherein the fixing unit is formed at a corner of the cell unit window glass.
Wherein wet etching is performed on the disk glass on which the sheet cutting portion is formed, and a chamfer is further formed on the exposed disk glass region.
Wherein the pan plate is formed by a wet etching process on the edge glass of the disc glass, and the inflection point has a vertical profile shape in which the direction of bending is changed at least once. Method of manufacturing glass.
Wherein the number of inflection points is controlled by control of an etch factor or by a plurality of wet etch processes according to different etch factors. ≪ Desc / Clms Page number 21 >
Wherein the etch rate is controlled by the etching solution concentration, the temperature of the etching solution, and the exposure time of the etchant.
Wherein a curvature of the inflection point is 0.01 mm to 100 mm.
Wherein the mask layer is formed by laminating DFR (Dry Film Photoresist) on the upper and lower portions of the reinforced disk glass and performing a photolithography process.
Wherein the chamfered portion is formed at a depth of about 0.5% to about 25% from the upper and lower surfaces of the disk glass.
Wherein the etch amount in the horizontal direction is 100 +/- 50 mu m and the etching amount in the vertical direction is 60 +/- 30 mu m / -20 mu m on the surface of the disc glass.
Wherein the chamfered portion is formed in a different shape on the upper side and the lower side of the glass substrate.
Wherein the chamfered portion is asymmetrical up and down or right and left.
Wherein the reinforcing of the disk glass is chemical tempered at a temperature of 350 ° C to 450 ° C using potassium nitrate (KNO 3 ).
Wherein the cell unit window glass is formed on the disc glass so as to be spaced apart from each other or continuously formed without a space therebetween.
Wherein the forming of the sheet cutting part comprises forming a laser spot interval at a corner part and a straight part of a cell differently from each other.
Wherein the window glass is used in one of a display window, a camera lens window, and a home key button unit.
Wherein a pattern is further formed on a front surface or a rear surface of the disk glass before the disk glass is strengthened.