KR20160139705A - Electromagnetic wave shielding coating composition - Google Patents
Electromagnetic wave shielding coating composition Download PDFInfo
- Publication number
- KR20160139705A KR20160139705A KR1020150075054A KR20150075054A KR20160139705A KR 20160139705 A KR20160139705 A KR 20160139705A KR 1020150075054 A KR1020150075054 A KR 1020150075054A KR 20150075054 A KR20150075054 A KR 20150075054A KR 20160139705 A KR20160139705 A KR 20160139705A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- coating composition
- composition
- electromagnetic shielding
- Prior art date
Abstract
Description
The present invention relates to a coating composition for electromagnetic shielding.
Electromanetic wave is an electromagnetic wave composed of two types of waves, electric field and magnetic field. It is a kind of electromagnetic energy generated in electric and magnetic flow.
Recently, as various electronic devices have become indispensable in human living environment, the level of exposure to electromagnetic waves is gradually changing. This is because electromagnetic waves can be adversely affecting the human body beyond the level that adversely affects other electronic devices Various techniques for shielding electromagnetic waves are required.
(ELD), Vacuum Fluorescent Display (VFD), Liquid Crystal Display (LCD), and the like have been developed for various kinds of electromagnetic wave chafes. Particularly, various shielding technologies such as selection, placement, adjustment, isolation, , A surface conduction electron-emitting device display (SED), etc., are associated with optical problems such as transmittance of output light, so that the structure of a separate transparent electromagnetic wave shielding film is formed outside the display device housing or inside the circuit board In addition to the above.
As a result, although it is related to the weight and size of the entire device, there arises a problem that the structural complexity of the entire device configuration can also be increased, and the electromagnetic waves in the material side Research on shielding technology is required.
In this connection, a prior art for forming a coating film for shielding electromagnetic waves that improves the shielding efficiency by using metal particles and metal oxides is disclosed in Korean Patent Registration No. 10-0737634 entitled "Coating Agent for Electromagnetic Wave Shielding" , &Quot; prior art ").
However, existing electromagnetic shielding materials such as conventional art use metal particles such as copper and nickel, and the workability in the coating process is lowered due to precipitation and oxidation of the particles, and the non-uniformity of the coating film is high , There is a problem that many restrictions are imposed on the shape and the weight of the whole product.
In addition, in order to solve the above-mentioned problem, when a conductive filler is provided using silver particles which provide low electric resistance and high attenuation rate to prepare a material for shielding electromagnetic waves, too expensive silver particles are used, There is a problem that many restrictions are placed on practical use and commercialization of products.
SUMMARY OF THE INVENTION The present invention has been made to solve the above problems, and it is an object of the present invention to provide a coating film which is formed integrally on the surface of a film to be a base and has excellent electromagnetic shielding performance as well as a coating film having flexibility and transparency, The present invention provides a technique capable of forming a light emitting layer.
In order to achieve the above object, the present invention provides a coating composition for shielding electromagnetic interference comprising a base coating composition for forming a base coating on a base surface, wherein the base coating composition is silver nano silver Sol) 10 to 20 parts by weight; 80 to 90 parts by weight of an acrylic resin; 1 to 3 parts by weight of a dispersant; 0.1 to 3 parts by weight of a leveling additive; And 10 to 30 parts by weight of an organic solvent.
Here, the silver nanoparticles and the acrylic resin constitute a honeycomb structure in which a plurality of partition walls are formed as a conductive network in the undercoating layer.
The silver nanoparticles have a silver nanoparticle concentration of 5 to 15% by weight, and the silver nanoparticles have an average diameter of 30 to 100 nm.
The coating composition for electromagnetic shielding further comprises a top coating composition for forming a top coat on the surface of the undercoat formed through the undercoat composition, wherein the top coat composition comprises 20 to 40 parts by weight of a 9-functional urethane acrylate oligomer ; 3 to 10 parts by weight of an acrylate acrylate; 5 to 15 parts by weight of a trifunctional monomer; 3 to 7 parts by weight of a bifunctional monomer; 2 to 4 parts by weight of a photoinitiator; 0.1 to 1 part by weight of a leveling additive; And 40 to 50 parts by weight of an organic solvent.
Here, the top coating composition further comprises 2 to 5 parts by weight of an antistatic agent.
The present invention has the following effects.
First, a coating film for electromagnetic wave shielding formed integrally with a base film can be provided.
Second, a coating film for shielding electromagnetic waves having a high level of flexibility and transparency in addition to excellent electromagnetic wave shielding performance can be formed.
Thirdly, through the conductive network of honeycomb structure constructed with silver nanosol and acrylic resin, it is possible to provide a coating composition capable of providing a sufficient electromagnetic shielding performance by lowering the production cost.
BRIEF DESCRIPTION OF DRAWINGS FIG. 1 is an enlarged photograph showing a state of a coating film formed using the coating composition for electromagnetic shielding of the present invention. FIG.
FIG. 2 is an enlarged photograph showing the state of the coating film formed using the coating composition for electromagnetic shielding according to the composition of the comparative example.
FIG. 3 is an enlarged photograph showing the state of the coating film formed using the coating composition for shielding electromagnetic waves according to the composition of the comparative example.
4 is a flowchart showing a method for producing a coating film using the coating composition for electromagnetic shielding of the present invention.
The preferred embodiments of the present invention will be described in more detail with reference to the accompanying drawings, in which the technical parts already known will be omitted or compressed for the sake of brevity.
1. Description of coating composition for electromagnetic wave shielding
The coating composition for electromagnetic shielding according to the present invention is composed of a lower coating composition and an upper coating composition, and each lower and upper coating composition has a composition and content of different compositions to fulfill the properties of the respective layers formed .
(1) Undercoating composition for electromagnetic wave shielding
The undercoating composition in the coating composition for electromagnetic shielding according to the present invention is a coating composition capable of providing a undercoating film having a conductive network structure for shielding electromagnetic waves on a base material layer as a base. Examples of the coating composition include silver nano sol; Acrylic resin; Dispersing agent; Leveling additives; And an organic solvent.
Here, the base material of the coating composition for electromagnetic wave shielding is a film made of a transparent material, and more specifically, a cover film or a housing in various electronic devices such as a display device requiring shielding of electromagnetic waves, etc., The undercoating on the underlying surface in the form of a transparent film provides the function of electromagnetic shielding and provides a certain level of transparency.
First, the silver nano sol will be described. The silver nano sol is a colloidal aqueous solution having silver nanoparticles as conductive metal particles, and is manufactured based on silver nitrate (AgNO 3 ). More specifically, sodium citrate (TSC, trisodium citrate), polyacrylic acid (PAA), or polyvinyl pyrrolidone (PVP), silver nanoparticles having a predetermined particle size are synthesized The colloidal form of the included nano-sol can be provided.
Here, the silver nanosol is provided in an amount of 10 to 20 parts by weight, and the concentration of the silver nanoparticles contained in the silver nanosol is set in the range of 5 to 10% by weight. Also, the average diameter of the silver nanoparticles contained in the silver nanosol at such a concentration level is set at a level of 30 to 100 nm.
This is because if the silver nanosol is less than 10 parts by weight, the surface resistance to the undercoat film becomes high due to the lack of silver nanoparticles in the undercoating film formed by the undercoat paint, The adhesion to the underlying surface of the undercoating film is lowered and the peeling phenomenon becomes frequent and the optical characteristics such as the transmittance and turbidity (permeation haze) of the undercoating film become poor.
The concentration of the silver nanoparticles in the silver nanosol is preferably 5 to 10% by weight. If the concentration of the silver nanoparticles is less than 5% by weight, the surface resistance value required for electromagnetic wave shielding can not be satisfied. When the particle concentration exceeds 10% by weight, the size of the silver nanoparticles increases and the dispersion ratio of sufficient silver nanoparticles in the undercoating material can not be shown. In addition, optical properties such as transmittance and turbidity (permeation haze) This results in a problem of poor quality.
Here, the concentration value at the level of 5 to 10% by weight, which indicates the content of the solid content (particularly, silver nano-particles) in the silver nanosol, is determined not by simple addition of silver nanoparticles but by separate washing process, It is preferable to provide it by repeatedly making it highly concentrated.
The average diameter of the silver nanoparticles in the silver nanoparticles is preferably 30 to 100 nm. When the average diameter of the silver nanoparticles is less than 30 nm, the silver nanoparticles may be connected to the acrylic resin to be described below. As shown in FIG. 2 or 3, The structural durability of the barrier rib formed through the conductive network formed in the coating film is deteriorated. As a result, the degree of electromagnetic shielding provided by the undercoating film is impaired. When the thickness exceeds 100 nm, coagulation phenomena between the particles are frequent, The safety is lowered and the surface resistance value is increased.
The acrylic resin plays a role as a binder and is a component to form a barrier wall by forming a conductive network in the undercoating layer connected with the silver nanosol. The addition of the acrylic resin is a necessary condition for the electroconductive environment It is possible to reduce the required amount of various metal nanostructures based on silver nanoparticles including silver nanoparticles required for equipments, and as a result, it is possible to save the total production cost by reducing the amount of materials such as silver nanosol having an expensive price, Shielding, flexibility and transparency.
If the acrylic resin is less than 80 parts by weight, the dispersibility of silver nano-sol in the silver nanoparticles is lowered, the pencil hardness of the undercoat film is lowered, and the surface of the base And if it exceeds 90 parts by weight, the value of the surface resistance to the undercoating film becomes high, so that a sufficient electromagnetic shielding function can not be provided.
In addition, the silver nanosol and the acrylic resin are provided in the range of the above-mentioned content levels, thereby forming a conductive network in the undercoating film formed on the base surface by coating the undercoating material, A honeycomb type honeycomb structure that forms a cell through the honeycomb structure.
Here, a partition wall having a honeycomb structure is formed through a coffee-ring effect. The coffee ring effect means that when the dispersion fluid is discharged onto the solid surface and evaporation occurs, the evaporation proceeds from the edge of the droplet preferentially from the edge of the droplet and from the center of the droplet. Accordingly, This means that the liquid in the droplet flows from the center to the edge to compensate for the loss so that the particles in the droplet are stacked from the edge of the droplet.
In other words, since the acrylic resin connects the metal particles such as the silver nanoparticles dispersed in the undercoat layer and acts as a bridge, the conductive network made of only the metal nanostructure and the conductive resin and the silver nanosol The formed conductive network is formed in a honeycomb shape with a certain level of structural safety and uniformity. Through this, the undercoating composition gives a shielding function of electromagnetic wave on the surface of the base, and forms a base coat as a transparent coating film having a high level of transmittance and a low level of haze (penetration haze).
Here, the change from the contents of the present invention to the constitution and the constitutional content of the undercoat paint composition may result in the deterioration of the conductive network structure such as breakdown of the structure of the barrier ribs or formation of cells as shown in FIG. 2 and FIG. So that the electromagnetic wave shielding performance is lowered.
In addition, the acrylic resin is a cation-type acrylic resin in which a functional group is introduced by using a methyl acrylamide-based monomer, an anion-type acrylic resin in which the functional group is introduced by using acrylic acid, and polyethylenes methacrylate A non-ion type acrylic resin into which the functional group is introduced, or a mixed type acrylic resin containing these functional groups. More specifically, it is preferable to use a non-ion type acrylic resin.
The dispersant is an element for improving the electromagnetic wave shielding function by preventing precipitation or agglomeration of silver nanoparticles in the silver nanosol, and is preferably provided in 1 to 3 parts by weight.
If the amount of the dispersing agent is less than 1 part by weight, the storage stability of the silver nano-sol in the undercoating material and the dispersibility of the silver nanoparticles are lowered and the optical properties such as the transmittance and turbidity (permeation haze) The silver nanosol and the acrylic resin are connected to each other and the connection state is poor on the conductive network formed in the undercoating layer and the degree of the portion where the cells are not properly formed is increased.
Here, the dispersing agent can be selectively used in the range of dispersants such as BYK-182 and BYK-162, which are cationic dispersing agents, BYK-110, which is an anionic dispersing agent, or BYK-9076 and B-142, More specifically, a cationic dispersing agent such as BYK-182 is preferably used, but not limited thereto, can be selected within the range of known dispersing agents.
The leveling additive is preferably added in an amount of 0.1 to 3 parts by weight to improve the smoothness and workability of the undercoating formed through the undercoating composition in the coating composition for electromagnetic shielding of the present invention. If the amount is less than 3 parts by weight, the leveling of the undercoating layer becomes poor, and if the amount is more than 3 parts by weight, the deposition adhesion becomes poor.
The leveling additives that can be used in the present invention include silicone leveling additives such as DC-11, BYK-310, BYK-306 and BYK-358N or non-silicone leveling additives such as Tego-500, Tego-270 and Tego- It is preferred to be provided through a combination of one or a leveling additive selected from each group, more specifically, through a combination of a non-silicon leveling agent and a silicon leveling agent, but not limited thereto, a range of known leveling additives ≪ / RTI >
The organic solvent contained in the undercoat paint composition is an element for maintaining the thickness of the undercoat film and improving paint workability, adhesion at drying speed and particle dispersibility of the silver nanoparticles, and is preferably 10 to 30 parts by weight If the amount of the organic solvent is less than 10 parts by weight, the coating workability is deteriorated and the appearance becomes poor. If the amount is more than 30 parts by weight, sufficient film formation is not effected and the dispersibility of silver nano- The conductive network structure formed in connection with the acrylic resin is partially irregular or broken to form a problem that the surface resistance of the undercoat film is increased.
Here, the organic solvent that can be used in the present invention may be an organic solvent such as acetate, ketone, alcohol, ester, aromatic or aliphatic base, But it is not limited thereto and may be selected within the range of known organic solvents.
To be more specific, organic solvents such as aromatic benzene, toluene, xylene, isobutyl alcohol, n-butyl alcohol (n- butyl alcohol, isopropyl alcohol, ethyl alcohol, methyl alcohol, ketone-based acetone, methyl ethyl ketone, methyl isobutyl ketone Methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, ethyl acetate, butyl acetate, ester cell ethyl cellosolve, butyl cellosolve, Butyl cellosolve, Cellosolve acetate, Aliphaticbased Solvesso # 100, Solvesso # 150 and the like can be used.
Here, more specifically, it is preferable to use toluene as the organic solvent. However, the structural characteristics of the conductive network formed through the silver nanosol and the acrylic resin in the undercoating composition described above are strengthened, so that the partition wall having a more rigid and stable structure It is most preferable to mix an organic solvent having a polarity and an organic solvent having a non-polarity so as to form a non-polar organic solvent.
That is, as described above, 10 to 20 parts by weight of silver nanosol; 80 to 90 parts by weight of an acrylic resin; 1 to 3 parts by weight of a dispersant; 0.1 to 3 parts by weight of a leveling additive; And 10 to 30 parts by weight of an organic solvent. The undercoating composition in the coating composition for electromagnetic shielding according to the present invention has a conductive network structure on the surface of a base material layer (in particular, a transparent material for a display device) (Transparency) such as transmittance and turbidity (permeation haze) required to minimize the loss of optical characteristics of light emitted through a base layer such as a transparent film for a display device A lower coating film can be formed.
(2) Top coat composition for electromagnetic wave shielding
The top coat composition in the coating composition for electromagnetic shielding according to the present invention can improve the electromagnetic wave shielding performance of the undercoating layer and improve the electromagnetic shielding performance of the undercoat layer to form the top coat layer as a finish layer which can satisfy physical properties such as hardness and appearance required for the entire coating layer As the coating composition, a 9-functional urethane acrylate oligomer; Acrylic acrylate; Trifunctional monomer; Bifunctional monomers; Photoinitiators; Leveling additives; And an organic solvent.
Description of the Aliphatic urethane acrylate oligomer will be given as the top coat positioned at the top of the entire coating film formed by the coating agent for shielding electromagnetic wave of the present invention. The properties of the film, such as hardness, abrasion resistance, EABRYL-9260, Ebecryl-1290, Ebecryl-80, Ebecryl-830, Ebecryl-9970 from ENTIS, CN929 and CN939 from Sartomer Company, which are components for providing the polyfunctional aliphatic urethane acrylate, , MIRAMER SC2010, MIRAMER SC2011, MIRAMER SC2020, MIRAMER SC2021, MIRAMER SC2054, MIRAMER SC2100, and the like, but are not limited to the following: CN963, CN964, CN965, CN980, CN985, CN983, CN971, MIRAMER PU210, MIRAMER PU610, MIRAMER SC2010, But may be selected within the range of polyfunctional aliphatic urethane acrylates having two or more acryl groups which are known.
The 9-functional urethane acrylate oligomer is preferably 20 to 40 parts by weight, and if the content of the 9-functional urethane acrylate oligomer is less than 20 parts by weight, the hardness and impact resistance of the top coat are deteriorated. When the amount of the 9-functional urethane acrylate oligomer is more than 40 parts by weight, There is a problem that the coating film has poor resistance to discoloration and impact resistance.
Acrylic Acrylate is an element for improving the adhesion and leveling property between the undercoating film and the top coat described above, and is preferably 3 to 10 parts by weight. If the amount of the acryl acrylate is less than 3 parts by weight, the adhesion to the undercoating film and the flexibility of the topcoating film to be formed deteriorate, and if the amount exceeds 10 parts by weight, there is a problem that the appearance becomes poor due to the lowering of the leveling property of the topcoating film .
Here, acryl acrylate is a kind of polyacrylate resin, which is synthesized by synthesizing a general acrylic resin to form a main chain of the polymer and then attaching acrylate to the side chain of the polymer.
The trifunctional monomer is preferably 5 to 15 parts by weight, and the bifunctional monomer is preferably 3 to 7 parts by weight. If the trifunctional monomer is 5 parts by weight and the bifunctional monomer is less than 3 parts by weight, adhesion to the undercoat layer is not sufficiently provided. When the trifunctional monomer is 15 parts by weight and the bifunctional monomer is more than 7 parts by weight, And the problem of deterioration of the curability occurs.
Herein, the low-functional (trifunctional, bifunctional) monomer means an acrylate monomer, and the trifunctional monomer includes TPT (trimethylolpropane triacrylate), ethoxylated trimethylolpropane triacrylate, ethoxylated trimethylolpropane methacrylate Triacrylate, trimethylolpropane triacrylate (TMPTA), and polyethylene terephthalate (PETE). The bifunctional monomers include triphenylglycol diacrylate, polyethylene glycol diacrylate, 1,4-butanediol Diacrylate, HDDA (Hexanedioldiacrylate), DPGDA (Dipropylene glycol Diacrylate), TPGDA (Tripropylene Glycol Diacrylate) and the like.
The photoinitiator in the top coat composition is preferably an element for ultraviolet curing of the top coat formed by the top coat composition, and it is preferably 2 to 4 parts by weight. If the amount of the photoinitiator is less than 2 parts by weight, the curability is deteriorated. , There is a problem that the impact resistance and sulfur modification of the top coat film become poor.
The leveling additive in the top coat composition is preferably added in an amount of 0.1 to 1 part by weight to improve smoothness and workability in the top coat formed through the top coat composition of the present invention, If the amount is less than 1 part by weight, the leveling of the top coat becomes poor. If the amount of the top coat exceeds 1 part by weight, the adhesion of the top coat is lowered and cratering occurs on the surface.
The organic solvent in the top coating composition is preferably contained in an amount of 40 to 50 parts by weight to maintain the thickness of the top coat and improve the workability of the coating. If the amount of the organic solvent is less than 40 parts by weight, If the amount exceeds 50 parts by weight, the paint may flow down to the coating film or a sufficient film may not be formed.
Here, the organic solvent that can be used in the present invention may be an organic solvent such as acetate, ketone, alcohol, ester, aromatic or aliphatic base, But it is not limited thereto and may be selected within the range of known organic solvents.
In addition, the top coat composition in the coating composition for electromagnetic shielding of the present invention may further include an antistatic agent to improve the electromagnetic wave shielding performance by further lowering the level of the surface resistance lowered by the undercoating layer.
Here, the antistatic agent may be selectively used in the range of various antistatic agents provided with phenad, a surfactant type antistatic agent, a metal ion type antistatic agent, or the like, and more specifically, a metal ion type antistatic agent is preferably used.
These antistatic agents include ELECON-500DA, 700DA, 100ED, PRIZOL-600DA (NanoCamTech) and SY-ICA-P212B, SY-ICA-P211 IL-11, IL-A5, IL-AP3, IL-P14 and the like of KOEI Co. However, the present invention is not limited thereto and the range of known antistatic agent ≪ / RTI >
It is preferable that the antistatic agent is provided in an amount of 2 to 5 parts by weight. If the antistatic agent is less than 2 parts by weight, the value of the surface resistance can not be lowered. If the antistatic agent is more than 5 parts by weight, the turbidity (permeation haze) .
That is, as described above, 20 to 40 parts by weight of a 9-functional urethane acrylate oligomer; 3 to 10 parts by weight of an acrylate acrylate; 5 to 15 parts by weight of a trifunctional monomer; 3 to 7 parts by weight of a bifunctional monomer; 2 to 4 parts by weight of a photoinitiator; 0.1 to 1 part by weight of a leveling additive; 40 to 50 parts by weight of an organic solvent; And 2 to 5 parts by weight of an antistatic agent according to an embodiment of the present invention. The top coat composition in the coating composition for electromagnetic shielding of the present invention, which is provided with excellent adhesion with the undercoat layer and finish treatment for the base layer, The surface resistance of the undercoating film can be further improved while the optical characteristics of the undercoat film are not deteriorated while satisfying the physical properties such as leveling property and curability.
2. Description of a method for producing a coating film using a coating composition for electromagnetic shielding
Hereinafter, how the process for producing a coating film using the coating composition for shielding electromagnetic waves according to the present invention is performed will be described in detail with reference to FIG.
(1) Preparation of Coating Composition for Electromagnetic Wave Car < S100 >
In this step, a process of preparing each of the primer and top coat used in the process of manufacturing a coating film using the coating composition for shielding electromagnetic waves is performed.
Herein, the undercoating composition corresponding to the undercoating composition of the coating composition for electromagnetic shielding according to the present invention comprises 10 to 20 parts by weight of silver nano sol as described above; 80 to 90 parts by weight of an acrylic resin; 1 to 3 parts by weight of a dispersant; 0.1 to 3 parts by weight of a leveling additive; And 10 to 30 parts by weight of an organic solvent, wherein the concentration and the average diameter of silver nanoparticles contained in the silver nanosol are set at a level of 5 to 10% by weight and 30 to 100 nm.
In addition, the top coating composition of the coating composition for electromagnetic shielding according to the present invention may comprise 20 to 40 parts by weight of a functional urethane acrylate oligomer, 3 to 10 parts by weight of an acrylate acrylate; 5 to 15 parts by weight of a trifunctional monomer; 3 to 7 parts by weight of a bifunctional monomer; 2 to 4 parts by weight of a photoinitiator; 0.1 to 1 part by weight of a leveling additive; 40 to 50 parts by weight of an organic solvent; And 2 to 5 parts by weight of an antistatic agent.
The composition and composition of the undercoating composition and topcoat composition of the coating composition for electromagnetic shielding according to the present invention are the same as those described in the above description of " Description of Coating Composition for Electromagnetic Shielding " Therefore, detailed explanation is omitted.
(2) Underlayer formation step < S200 >
In this step, a primer coating layer is prepared by applying the primer coating composition prepared in step S100 on the surface of the base material.
Here, the base material is preferably various transparent films to be applied to various display devices, but the present invention is not limited to this. However, all of the various film-like members provided in the electronic equipment and shielding the electromagnetic wave, The coating composition of the electromagnetic shielding coating composition of the present invention is subjected to a coating operation.
In detail, first, the undercoating composition prepared in step S100 is dispersed in a coating composition using an agitator such as an ultrasonic stirrer, and the undercoat composition, which has undergone the dispersion process, It is applied on the surface of the base material of the film material.
The drying process of the undercoating film is performed at a room temperature and a drying process at a temperature environment of 90 to 150 ° C is 1 to 10 Minute, and the coating film is dried. Finally, the dried undercoat film is ultraviolet cured by UV irradiation to form a final undercoat film.
Through this process, the undercoating film is formed to have a film thickness of 5 to 20 μm, and more specifically, to have a film thickness of 9 to 10 μm.
If the thickness of the undercoat film is less than 5 μm, the structure of the conductive network formed in the undercoat film is irregular and unstable and the surface resistance is measured to be high. If the thickness is more than 20 μm, the flexibility and permeability of the undercoat film and the haze This is because the optical characteristics of the light emitting layer are deteriorated.
(3) Upper layer formation step < S300 >
In this step, a top coating layer is formed on the surface of the undercoat layer by applying the topcoat composition prepared in step S100 on the undercoat layer formed in step S200.
In detail, first, the top coating composition prepared in step S100 is applied on the surface of the undercoating film, and then the drying process at a temperature of 90 to 150 ° C. is continued for about 1 to 10 minutes, Is dried.
Thereafter, the dried top coat film undergoes ultraviolet ray hardening through UV irradiation to form a final top coat film, and a coating film for shielding electromagnetic waves is formed on the surface of the base material, which is formed by combining both the undercoating film and the top coat film thus formed .
The top coat formed in this manner is preferably formed to have a coating thickness of 1 to 5 μm after curing, and more specifically, a coating thickness of 1 to 2 μm.
This is because if the thickness of the top coat is less than 1 μm, the hardness of the entire coating film as well as the top coat is lowered, and if it exceeds 5 μm, the adhesion of the top coat to the undercoating film and the flexibility of the top coat are impaired .
As a result, the coating film formed of the undercoating film and the overcoat film through all the processes of S100 to S300 is coated and laminated on the surface of the work subject, which is the base, such as a transparent film, thereby forming a conductive network having electromagnetic wave shielding performance. At the same time, has transparency of excellent performance which reduces the optical loss of the light to be transmitted through the film, and satisfies the property required to have sufficient flexibility for movement or external force.
3. Description of coating properties of coating composition for shielding electromagnetic wave
For each of the coating layers formed by providing the coating composition for electromagnetic shielding according to the present invention in various embodiments, physical properties such as electromagnetic shielding performance, coating film flexibility and transparency of the coating composition are measured And the following experimental methods were used for the purpose of defining the properties by means obvious to those skilled in the art.
Accordingly, the embodiments described below can provide a coating composition for electro-magnetic shielding which is manufactured by preparing and testing components constituting the coating composition for electromagnetic shielding at various ratios, and then solving the problems of the coating film formed by the conventional coating composition for shielding electromagnetic waves, This is a preferred embodiment configured to verify an appropriate blend ratio that can satisfy the physical properties required for shielding electromagnetic waves.
First, various experimental methods for measuring physical properties of the coating film are as follows.
(1) Adhesion: A tape peeling test is carried out in accordance with ASTM D 3359. After the surface was cleaned with a soft brush and the tape (JIS Z 1522) was firmly attached, the tape was pulled out strongly at a 90 한 angle to one side and checked with reference to Table 1 below.
(2) Peeling along the straight line is not recognized
(2) Peeling along the straight line is not recognized
(2) Peeling along a straight line is recognized
(3) One side of the snow board is not peeled off more than 50% of the coating
(2) About 5 pieces of peeled checkered snow
(2) About 20 pieces of peeled checkered snow
(2) Pencil hardness: Pencil hardness due to artificial scratching was measured under arbitrary pencil load conditions having a hardness in the range of 3B to 7H in accordance with JIS K 5600.
(3) Surface resistance value: The resistance value was measured with a digital multimeter (4-probe) apparatus according to ASTM D257, and the surface resistance was measured at 10 points or more by grounding the surface of the upper and lower coating films.
(4) Transmittance and Haze: According to ASTM D1003, the haze meter was used to measure the 550 nm transmittance and haze of the film against light.
(5) Thickness of Film and Coating Film: The thickness of the film was measured using a static pressure measuring device in accordance with ASTM D3562.
(6) Outer appearance of the coating film (leveling property): Whether or not the variation of the coated film thickness was satisfied within 10% was measured with a Digimatic thickness gauge.
The blending forms of Examples 1 to 4 of the undercoat paint composition in the electromagnetic wave shielding paint composition are shown in Table 2 below.
Each of the undercoating compositions of Examples 1 to 4 prepared in the form of formulation as shown in Table 2 was subjected to a process of "a method for producing a coating film using an electromagnetic wave shielding coating composition" And physical properties of the respective coating films were measured by various experimental methods described above. The results are shown in Table 3 below.
The results of Table 3 show that the undercoat formed through the undercoating composition according to Example 1 is capable of providing a sufficient electromagnetic shielding function as a result of the test of physical properties of each undercoat layer, Of the composition of the present invention was provided with sufficient property that it could provide the composition without any loss, and thus Example 1 was found to be the most appropriate among each composition ratio of each undercoating composition in the electromagnetic wave shielding coating composition of the present invention.
Next, the blending forms constituting Examples 1 to 4 of the top coat composition in the electromagnetic wave shielding coating composition are shown in Table 4 below.
Each of the top coat compositions of Examples 1 to 4 prepared in the form of formulations shown in Tables 1 to 3 was subjected to the above-described "method for producing a coating film using the coating composition for electromagnetic shielding" The coating film was applied on the surface of the coating film to form a predetermined coating film, and physical properties of each coating film were measured by various experimental methods described below. The results are shown in Table 5 below. Here, the reference primer coating is a primer coating formed by using the primer coating composition prepared based on Example 1, which has been proved to have the most appropriate formulation ratio.
The results of Table 5 show that the top coat formed through the top coat composition of Example 1 is capable of providing a sufficient electromagnetic shielding function at the level of the surface resistance as a result of each physical property test, Of the composition of the present invention was provided with sufficient properties that it could provide the composition without any loss, and thus Example 1 was found to be the most appropriate among the composition ratios of the respective top coat compositions in the electromagnetic wave shielding coating composition of the present invention.
That is, as can be seen from the physical property evaluation results of Tables 3 and 5, it is possible to provide a high level of electromagnetic wave shielding performance by having a low surface resistance value, and at the same time to minimize the loss of optical characteristics through transmission of light, 10 to 20 parts by weight of silver nano sol as in Example 1; 80 to 90 parts by weight of an acrylic resin; 1 to 3 parts by weight of a dispersant; 0.1 to 3 parts by weight of a leveling additive; And 10 to 30 parts by weight of an organic solvent; and 20 to 40 parts by weight of a 9-functional urethane acrylate oligomer; 3 to 10 parts by weight of an acrylate acrylate; 5 to 15 parts by weight of a trifunctional monomer; 3 to 7 parts by weight of a bifunctional monomer; 2 to 4 parts by weight of a photoinitiator; 0.1 to 1 part by weight of a leveling additive; 40 to 50 parts by weight of an organic solvent; And 2 to 5 parts by weight of an antistatic agent, can satisfy the optimum required properties.
Accordingly, the undercoating composition and the overcoating composition of the coating composition for electromagnetic shielding coating of the present invention are applied in a laminated form on a base surface of a transparent film material to which an electromagnetic wave shielding function is to be imparted in order to be integrally provided, The underlying film itself not only provides electromagnetic shielding performance, but also provides excellent levels of flexibility and transparency, thereby reducing the limitations of coating applications and minimizing the loss in optical properties of the light transmitted through the film.
The embodiments disclosed in the present invention are not intended to limit the scope of the present invention but to limit the scope of the technical idea of the present invention. The scope of protection is to be construed in accordance with the following claims, and all technical ideas within the scope of equivalents thereof should be construed as being included in the scope of the present invention.
Claims (6)
The above-
10 to 20 parts by weight of silver nano Sol;
80 to 90 parts by weight of an acrylic resin;
1 to 3 parts by weight of a dispersant;
0.1 to 3 parts by weight of a leveling additive; And
And 10 to 30 parts by weight of an organic solvent
A coating composition for electromagnetic shielding.
Wherein the silver nanosol and the acrylic resin form a honeycomb structure in which a plurality of partition walls are formed as a conductive network in the undercoat layer
A coating composition for electromagnetic shielding.
Wherein the concentration of the silver nanoparticles of the silver nanosol is 5 to 15% by weight
A coating composition for electromagnetic shielding.
Wherein the silver nanoparticles have an average diameter of 30 to 100 nm
A coating composition for electromagnetic shielding.
The coating composition for electromagnetic shielding further comprises an upper coating composition for forming a top coat on the surface of the undercoat formed through the undercoat composition,
The top coating composition may contain,
20 to 40 parts by weight of a 9-functional urethane acrylate oligomer;
3 to 10 parts by weight of an acrylate acrylate;
5 to 15 parts by weight of a trifunctional monomer;
3 to 7 parts by weight of a bifunctional monomer;
2 to 4 parts by weight of a photoinitiator;
0.1 to 1 part by weight of a leveling additive; And
40 to 50 parts by weight of an organic solvent
A coating composition for electromagnetic shielding.
Wherein the topcoat composition further comprises 2 to 5 parts by weight of an antistatic agent
A coating composition for electromagnetic shielding.