KR20160116431A - Kintting yarn having retroreflectivity and retroreflective knitted fabric using the same - Google Patents

Kintting yarn having retroreflectivity and retroreflective knitted fabric using the same Download PDF

Info

Publication number
KR20160116431A
KR20160116431A KR1020150044060A KR20150044060A KR20160116431A KR 20160116431 A KR20160116431 A KR 20160116431A KR 1020150044060 A KR1020150044060 A KR 1020150044060A KR 20150044060 A KR20150044060 A KR 20150044060A KR 20160116431 A KR20160116431 A KR 20160116431A
Authority
KR
South Korea
Prior art keywords
yarn
retroreflective
slit
less
knitting
Prior art date
Application number
KR1020150044060A
Other languages
Korean (ko)
Other versions
KR101691435B1 (en
Inventor
배재천
Original Assignee
배재천
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 배재천 filed Critical 배재천
Priority to KR1020150044060A priority Critical patent/KR101691435B1/en
Publication of KR20160116431A publication Critical patent/KR20160116431A/en
Application granted granted Critical
Publication of KR101691435B1 publication Critical patent/KR101691435B1/en

Abstract

The present invention relates to a retroreflective knitting yarn and a retroreflective knitted fabric using the same. According to the present invention, a retroreflective knitting yarn is a composite yarn formed of a cross sectional retroreflective slit yarn with a cross section whose width is 0.37 mm or less; and a polyester texture yarn of 30d or less. In the cross sectional retroreflective slit yarn with the cross section described above, a retroreflective sheet in which a polyurethane-based adhesive layer, a reflective layer, and a glass bead layer are sequentially formed is slit to have a width less than 0.37 mm in one surface of a thermoplastic polyurethane (TPU) film. The composite yarn is obtained as a twisted yarn in which a retroreflective slit yarn and a polyester texture yarn are twisted with a twist number of 300-500 TPM; or a covering yarn obtained by using a retroreflective slit yarn as a core yarn, and winding the retroreflective slit yarn with a polyester texture yarn. Therefore, retroreflective properties are included and physical properties of a knitting yarn requiring flexibility and elasticity are included.

Description

재귀반사 편사 및 이를 이용한 재귀반사 편성물{Kintting yarn having retroreflectivity and retroreflective knitted fabric using the same}BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a knitted retroreflective knitted fabric,

본 발명은 재귀반사 편사 및 이를 이용한 재귀반사 편성물에 관한 것으로서, 재귀반사 특성을 나타내면서도 유연성과 신축성을 요구하는 편사로서의 물성을 구비한 편사와 이를 이용하여 편성되는 재귀반사 편성물에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a recursive reflective knitting yarn and a retroreflective knitted fabric using the same, and more particularly to a knitted yarn having physical properties as a knitting yarn requiring flexibility and stretchability while exhibiting retroreflective properties and a retroreflective knitted fabric knitted using the same.

재귀반사(retroreflection)란 빛을 제자리로 다시 돌려보낸다는 말로서, 광원에서 나온 빛이 다른 물체에 도달한 경우, 도달한 빛인 입사 광선을 그대로 광원으로 되돌려 반사시키는 것을 말한다.Retroreflection is a technique of returning light back to its original position. When a light from a light source reaches another object, the incident light, which is the light that has arrived, is reflected back to the light source as it is.

이러한 재귀반사의 원리를 이용하여, 굴곡이 심한 도로의 표지판이나 야간도로 작업표시판 등은 밤중에 물체를 쉽게 알아볼 수 있도록 대부분 재귀반사 제품을 사용하며, 야간에 도로에서 작업하는 교통경찰이나 환경미화원 등의 복장에서 재귀반사 직물 또는 시트를 부분적으로 사용하여 야간작업의 안전성을 도모하고 있다.Using this principle of reflex reflection, most signs of roads with severe bends and nighttime road sign boards use mostly recursive reflectors to easily recognize objects in the night, and traffic police and environmental workers working on the road at night In the attire of the garment, the recycled reflective fabric or sheet is partially used to secure the safety of night work.

최근에는 이러한 특수 용도의 안전복 뿐만 아니라, 레저나 스포츠를 포함한 일상적인 의복에도 이러한 재귀반사 특성을 구현하여 독특한 개성을 갖는 의복을 제조하고자 하는 시도가 이루어지고 있다.In recent years, attempts have been made to fabricate garments having distinctive personality by implementing such a retroreflective characteristic not only in safety clothes for special use but also in daily clothes including leisure and sports.

재귀반사 제품을 의복에 구현하는 방법은 기본적으로는 글라스비드 반사체를 직물이나 의복에 직접 코팅하여 도포하거나 프린트 기술을 이용하여 직물에 얇게 도포하여 만드는 기술이 있다. 이러한 방법은 재귀반사를 단순히 안전을 위한 야간의 시인성 확보를 위한 목적으로 사용하는 경우에는 별문제가 되지 않는다. 그러나, 이렇게 할 경우에 반사 기능성이 좋지 않고 세탁 등 마찰에 의하여 유리구슬이 직물에서 쉽게 탈락하므로 반복 마찰에 의하여 반사 기능성이 급격히 떨어지는 문제가 있으며 직물에 다양하고 선명한 색상을 부여하기 어려운 단점이 있다.The method of embodying a retroreflective article in a garment is basically a technique of directly coating a glass bead reflector on a fabric or a garment, or applying it thinly on a fabric using a printing technique. This method is not a problem when retroreflective is used merely for securing visibility at night for safety. However, in this case, the reflection function is not good, and the glass beads easily fall off from the fabric due to the friction of washing or the like, so that there is a problem that the reflection function falls rapidly due to repetitive friction and it is difficult to give various and bright colors to the fabric.

이를 개선하기 위하여, 최근에는 유리구슬을 폴리에스테르 필름에 도포하고 이를 세절한 슬릿사를 이용하여 제조한 재귀반사 원단을 사용하여 의복을 제작하는 기술이 제안되고 있다.In order to improve this, a technique has recently been proposed in which a glass bead is applied to a polyester film, and a garment is made using a retroreflective fabric fabricated by using a slit yarn in which three slits are formed.

그러나, 이러한 슬릿사를 이용한 종래의 재귀반사 원단은 모두가 직물지 형태이고, 촉감이나 유연성, 신축성 등의 문제로 인하여 재귀반사 슬릿사를 이용한 편성물은 개발된 바 없다.However, all conventional retroreflective fabrics using such a slit yarn are all in the form of a woven fabric, and knit products using a retroreflective slit yarn have not been developed due to problems such as tactile feeling, flexibility, and stretchability.

KRKR 10-1998-04296810-1998-042968 AA KRKR 10-061421910-0614219 B1B1 KRKR 10-100642810-1006428 B1B1

본 발명은 상술한 종래의 재귀반사사와 재귀반사 원단에 있어서의 문제점을 개선하기 위해 이루어진 것으로서, 재귀반사 성능과 내구성이 우수하면서도 유연성과 신축성이 뛰어나서, 편성물로서 편직이 가능한 재귀반사 편사와 이를 이용하여 제조되는 재귀반사 편성물을 제공하는 것을 목적으로 한다.The present invention has been made in order to solve the problems of the conventional retroreflective sheeting and retroreflective fabric described above. The present invention provides a retroreflective knitting yarn excellent in retroreflective performance and durability and excellent in flexibility and stretchability, And to provide a retroreflective knitted fabric which is produced.

상기 목적을 달성하기 위한 본 발명에 따른 재귀반사 편사는,According to another aspect of the present invention, there is provided a retroreflective sheet,

폭 0.37mm이하의 단면 재귀반사 슬릿사와, 30d 이하의 폴리에스테르 텍스처사를 포함하여 이루진 복합사 형태로서, A cross-section retroreflective slit having a width of 0.37 mm or less, and a polyester texture yarn of 30 d or less,

상기 단면 재귀반사 슬릿사는, TPU(Thermoplastic PolyUrethane) 필름의 일면에 폴리우레탄계 접착제층과 반사층 및 글라스비드층이 순차로 형성된 재귀반사 시트를 0.37mm 이하의 폭으로 슬릿한 것이고,The retroreflective reflection slit yarn is obtained by slitting a retroreflective sheet on which a polyurethane adhesive layer, a reflective layer and a glass bead layer are sequentially formed on one surface of a TPU (Thermoplastic Polyurethane) film to a width of 0.37 mm or less,

상기 복합사는 재귀반사 슬릿사와 폴리에스테르 텍스처사를 꼬임수 300~500TPM으로 합연한 합연사 또는 상기 재귀반사 슬릿사를 심사로 하고 폴리에스테르 텍스처사를 감은 커버링사 형태인 것을 특징으로 한다.The composite yarn is characterized in that the recursive reflection slit yarn and the polyester texture yarn are combined twist yarns at a twist number of 300 to 500 TPM or a covering yarn in which the recycled reflection slit yarn is inspected and the polyester texture yarn is wound.

본 발명에 따른 재귀반사 편성물은 상기 재귀반사 편사로 편성된 부분을 포함하여 이루어진 편성물인 것을 특징으로 한다.The retroreflective knitted fabric according to the present invention is a knitted fabric comprising a portion knitted with the above-described retroreflective knitting yarn.

본 발명에 따르면, 기재로 TPU 필름을 사용하고 세폭이면서 단면에만 재귀반사층이 형성된 형태의 슬릿사를 사용하기 때문에, 종래의 슬릿사 형태의 재귀반사용 직사들에 비해 유연성과 신축성을 갖는다.According to the present invention, since a slit yarn in which a TPU film is used as a substrate and a retroreflective layer is formed only on a cross section with a narrow width is used, it has flexibility and stretchability in comparison with conventional slit yarn type recursive yarn direct yarns.

또한, 재귀반사 슬릿사를 폴리에스테르 텍스처사와 합연 또는 커버링사 형태로 복합화함으로써, 재귀반사 성능을 가지면서도 텍스처사에 의해 촉감과 볼륨감이 향상되고, 신축성을 가짐으로써 편직을 통해 재귀반사 편성물을 제조할 수 있게 된다.In addition, by combining the retroreflective slit yarn with the polyester texture yarn in the form of a sintered or covered yarn, the retroreflective knitted fabric is produced through knitting by having a retroreflective property, .

도 1은 본 발명에 따른 재귀반사 편사의 제조에 사용되는 슬릿사의 단면구조를 보여주는 단면 모식도;
도 2는 본 발명의 일실시예에 따른 합연사 형태의 재귀반사 편사의 외관을 보여주는 사시도;
도 3은 본 발명의 일실시예에 따른 커버링사 형태의 재귀반사 편사의 외관을 보여주는 사시도.1 is a cross-sectional view showing a cross-sectional structure of a slit yarn used in the production of a reflex reflective knitting yarn according to the present invention;
FIG. 2 is a perspective view showing the appearance of a reflex reflective knitting yarn in the form of a combined twist yarn according to an embodiment of the present invention; FIG.
3 is a perspective view showing the appearance of a retroreflective knitting yarn in the form of a covering yarn according to an embodiment of the present invention;

도 1은 본 발명에 따른 재귀반사 편사의 제조에 사용되는 슬릿사의 단면구조를 보여주는 단면 모식도이고, 도 2는 본 발명의 일실시예에 따른 합연사 형태의 재귀반사 편사의 외관을 보여주는 사시도이며, 도 3은 본 발명의 일실시예에 따른 커버링사 형태의 재귀반사 편사의 외관을 보여주는 사시도이다. FIG. 1 is a schematic cross-sectional view showing a cross-sectional structure of a slit yarn used in the production of a recursive reflective knitting yarn according to the present invention, FIG. 2 is a perspective view showing the appearance of a reflex reflective knitting yarn in the form of a combined yarn according to an embodiment of the present invention, FIG. 3 is a perspective view showing the appearance of a covering yarn in the form of a reflective yarn according to an embodiment of the present invention.

이하, 이들 도면을 참조한 실시예를 통하여 본 발명의 구체적인 실시예를 좀 더 상세하게 설명한다.Hereinafter, specific embodiments of the present invention will be described in more detail by way of examples with reference to the drawings.

본 발명에 따른 재귀반사 편사(1, 1')는, 도 2 내지 도 3에서 보는 것과 같이, 재귀반사 슬릿사(10)와 폴리에스테르 텍스처사(20)를 포함하여 이루어지는 복합사이다. The retroreflective knitting yarn 1, 1 'according to the present invention is a composite yarn comprising a retroreflective slit yarn 10 and a polyester texture yarn 20 as shown in Figs. 2 to 3.

상기 재귀반사 슬릿사(10)는 한면에만 재귀반사층이 형성된 단면 재귀반사 슬릿사 형태로서, 단면 재귀반사 시트를 폭 0.37mm 이하, 바람직하게는 0.1~0.25mm 이하로 슬릿하여 제조되며, 도 1에서 보는 것과 같이 TPU(Thermoplastic PolyUrethane) 필름(11)의 일면에 폴리우레탄계 접착제층(12)과 반사층(13) 및 글라스비드층(14)이 순차로 형성된 것이다.The retroreflective slit yarn 10 is in the form of a cross-section of a retroreflective slit with a retroreflective layer formed on only one side thereof. The cross-sectional retroreflective sheet is manufactured by slitting the cross-section 0.37 mm or less, preferably 0.1 to 0.25 mm or less, A polyurethane based adhesive layer 12, a reflective layer 13 and a glass bead layer 14 are sequentially formed on one surface of a TPU (Thermoplastic Polyurethane) film 11 as shown in FIG.

상기 단면 재귀반사 시트는, 박막 폴리에스테르 캐리어 필름이나 종이 상에 점착제를 도포하고, 도포된 점착제상에 글라스비드를 낙하시켜 고착시킨 다음, 글라스비드 위에 반사층을 형성시키고, 반사층 위에 폴리우레탄계 접착제를 도포하여 접착제층을 형성시키고, 접착제층에 기재시트인 TPU 필름을 적층한 다음, 글라스비드가 고착된 점착제를 제거하는 단계를 통해 제조될 수 있다.The cross-section retroreflective sheeting can be obtained by applying a pressure-sensitive adhesive on a thin film polyester carrier film or paper, dropping the glass bead onto the applied pressure-sensitive adhesive to fix it, then forming a reflective layer on the glass bead, applying a polyurethane- To form an adhesive layer, laminating a TPU film as a base sheet to the adhesive layer, and then removing the adhesive to which the glass beads are adhered.

상기 TPU 필름(11)은 충격, 마찰, 절단, 인열강도가 우수하며, 유연성과 탄성이 우수하며, 본 발명에서는 PET 등이 아닌 TPU를 기재 필름으로 이용하여 재귀반사 슬릿사(10)를 제조함으로써, 이 슬릿사를 이용하여 제조되는 편사가 우수한 탄성과 유연성을 갖게 된다. The TPU film 11 is excellent in impact, friction, cutting and tear strength, and is excellent in flexibility and elasticity. In the present invention, the TPU film 11 is used as a base film to produce the recursive reflective slit yarn 10 Thus, the knitting yarn produced using this slit yarn has excellent elasticity and flexibility.

또한, 본 발명에서 사용되는 재귀반사 슬릿사(10)는 TPU 필름(11)의 한쪽 면에만 반사층(13) 및 글라스비드층(14)을 형성한 단면 재귀반사 형태로서, 반사층과 글라스비드층에 의해 촉감이 딱딱해지고 유연성과 탄성이 저하되는 것을 최소화한 것이다.The retroreflective slit yarn 10 used in the present invention is a retroreflective form having a reflective layer 13 and a glass bead layer 14 formed on only one side of the TPU film 11, Thereby minimizing the deterioration of flexibility and elasticity.

상기 반사층(13)은, 알루미늄 또는 실버 안료를 수지에 혼합한 것을 코팅하거나, 고분자 수지와 용제 및 알루미늄, 백금, 니켈, 크롬 및 실버로 이루어지는 군으로부터 선택되는 1종 이상의 금속으로 이루어진 수지 조성물을 직접 도포하거나 또는 스프레이 방식으로 접착제층 상에 코팅하여 이루어질 수 있다.The reflective layer 13 may be formed by coating a mixture of aluminum or a silver pigment with a resin or by coating a resin composition composed of a polymer resin, a solvent and at least one metal selected from the group consisting of aluminum, platinum, nickel, Or by coating on the adhesive layer by a spraying method.

한편, 통상의 재귀반사 슬릿사는 반사층(13)에 의해 은색을 나타내는데, 본 발명에 따르면 폴리우레탄계 접착제층(12)을 형성할 때에 폴리우레탄계 접착제에 착색 안료를 첨가함으로써, 다양한 색상을 가진 재귀반사 슬릿사(10)를 제조할 수 있으며, 이를 이용함으로써 작업복이 아니라 다양한 색상의 일상복으로 활용이 가능한 유색의 재귀반사 편사(1, 1')를 제조할 수 있다.On the other hand, a typical retroreflective slit yarn exhibits silver color by the reflective layer 13. According to the present invention, by adding a color pigment to a polyurethane adhesive agent when forming the polyurethane based adhesive layer 12, a retroreflective slit It is possible to manufacture colored retroreflective knitting yarns 1, 1 'that can be used as everyday clothes of various colors instead of work clothes.

또한, 상기 재귀반사 시트에 프린팅에 의해 다양한 색상의 무늬를 형성한 후, 슬릿하면, 길이방향으로 위치에 따라 색상이 변하는 재귀반사 슬릿사(10)를 얻을 수 있으며, 이와 같이 위치에 따라 색상이 달라지는 재귀반사 슬릿사(10)를 사용하여, 길이방향으로 부분마다 색상이 달라지는 재귀반사 편사(1, 1')를 제조할 수도 있다.In addition, when the retroreflective sheet is formed by printing a pattern of various colors and then slit, the retroreflective slit yarn 10 whose color changes according to the position in the longitudinal direction can be obtained, The retroreflective knit yarns 1, 1 'may be manufactured by using the recursive reflective slit yarns 10 different in color from each other in the longitudinal direction.

상기와 같이 재귀반사 시트에 프린팅에 의해 생성되는 무늬는 디지털 프린팅기에 의해 상기 반사층과 상기 글라스비드층 사이의 공간에 인날되는 것이 바람직하다.As described above, the pattern generated by printing on the retroreflective sheet is preferably passed through a space between the reflective layer and the glass bead layer by a digital printer.

한편, 상기 재귀반사 슬릿사(10)와 복합사를 구성하는 폴리에스테르 텍스처사(20)는, 폴리에스테르 멀티 필라멘트사를 기계적인 처리에 의하여 루프 또는 권축을 만들어 필라멘트들의 평행하고 조밀한 구조를 헤쳐서 신축성을 향상시키고 함기량을 크게 하여 필라멘트사의 단점을 개선한 실로서 가공사라고도 한다. 텍스처사는 가연법, 공기분사법, 찰과법, 충전법, 기어권축법, 편성권축법 등의 다양한 방법에 의해 얻어지며, DTY(DRAW TEXTURED YARN) 또는 TTY(TRAWSTER TEXTURED YARN) 등을 포함한다.On the other hand, the polyester texturizing yarn 20 constituting the composite yarn with the recursive reflection slit yarn 10 is formed by looping or crimping a polyester multifilament yarn by a mechanical treatment so as to penetrate the parallel and dense structure of the filaments It is a yarn that improves the stretchability and improves the disadvantages of the filament yarn by increasing the amount of yarn. The texture is obtained by various methods such as the twisting method, the air jet method, the brush method, the filling method, the gear crimping method, and the weaving method, and includes DTY (DRAW TEXTURED YARN) or TTY (TRAWSTER TEXTURED YARN).

상기 폴리에스테르 텍스처사(20)는 30d 이하인 것이 사용되며, 10~25d의 것이 바람직하고, 20~25d의 것이 가장 바람직하다.The polyester texture yarn 20 is preferably 30 d or less, more preferably 10 to 25 d, and most preferably 20 to 25 d.

이 폴리에스테르 텍스처사(20)를 이용하여 상기 단면 재귀반사 슬릿사(10)와 복합하여 복합사로 함으로써, 재귀반사 슬릿사(10)의 유연성과 탄성의 부족을 폴리에스테르 텍스처사(20)가 보완하여, 편사로서 적합한 유연성과 신축성 등을 갖도록 할 수 있다.This polyester texture yarn 20 is used in combination with the above-described one-side retroreflective slit yarn 10 to form a composite yarn, whereby the flexibility and elasticity of the retroreflective slit yarn 10 are compensated by the polyester texture yarn 20 So that it is possible to have flexibility and stretchability suitable for the knitting yarn.

복합사를 구성하는 방법은 다양한 방법이 알려져 있으나, 본 발명에서 사용되는 편사(1, 1')는 도 2 내지 도 3에 나타낸 합연사 형태의 복합사인 편사(1) 또는 커버링사 형태의 복합사인 편사(1')일 수 있다.Various methods are known for forming the composite yarn, but the knitting yarns 1, 1 'used in the present invention are not limited to the composite yarn 1 of composite yarn type shown in Figs. 2 to 3 or composite yarns in the form of covering yarn May be a knit yarn 1 '.

상기 합연사 형태의 복합사인 편사(1)는 도 2에서 보는 것과 같이, 재귀반사 슬릿사(10)와 폴리에스테르 텍스처사(20)를 합사하여, 꼬임수 300~500TPM으로 함께 연사하여 제조된다.As shown in Fig. 2, the composite suture knitting yarn 1 in the form of a combined twist yarn is produced by folding together a retroreflective slit yarn 10 and a polyester texture yarn 20 and twisting together at a twist number of 300 to 500 TPM.

상기 커버링사 형태의 복합사인 편사(1')는, 상기 재귀반사 슬릿사(10)를 심사로 하고 폴리에스테르 텍스처사(20)를 상기 심사의 주위에 감아서 이루어지는 것으로, 도면에서와 같이 심사인 재귀반사 슬릿사(10)의 주위를 완전히 감지 않고 심사의 일부가 외부에 노출될 수 있도록 커버링 간격을 조절하여 재귀반사 성능이 유지되도록 한다.The cover yarn-shaped composite suture knitting yarn 1 'is formed by inspecting the retroreflective slit yarn 10 and winding the polyester texture yarn 20 around the examination. As shown in the figure, The retroreflective performance is maintained by adjusting the covering interval so that a part of the examination is exposed to the outside without sensing the periphery of the retroreflective slit yarn 10 completely.

이와 같은 본 발명에 따른 재귀반사 편사(1, 1')는 다른 편사와 함께 전체적으로 편직하거나, 편성물의 일부에 짜넣음으로써, 재귀반사 편사로 편성된 부분을 포함하여 이루어진 재귀반사 편성물을 제조할 수 있다.The retroreflective knitting yarn 1, 1 'according to the present invention can be manufactured by knitting the whole knit with other knitting yarn, or by incorporating it into a part of the knitted fabric, have.

1, 1': 재귀반사 편사
10: 재귀반사 슬릿사
11: TPU 필름
12: 접착제층
13: 반사층
14: 글라스비드층
20: 텍스처사1, 1 ': Retroreflective knitting yarn
10: Retroreflective slit yarn
11: TPU film
12: adhesive layer
13: Reflective layer
14: glass bead layer
20: Texture History

Claims (4)

폭 0.37mm이하의 단면 재귀반사 슬릿사와;
30d 이하의 폴리에스테르 텍스처사를 포함하여 이루진 복합사로서,
상기 단면 재귀반사 슬릿사는, TPU(Thermoplastic PolyUrethane) 필름의 일면에 폴리우레탄계 접착제층과 반사층 및 글라스비드층이 순차로 형성된 재귀반사 시트를 0.37mm 이하의 폭으로 슬릿한 것이고,
상기 복합사는 재귀반사 슬릿사와 폴리에스테르 텍스처사를 꼬임수 300~500TPM으로 합연한 합연사 또는 상기 재귀반사 슬릿사를 심사로 하고 폴리에스테르 텍스처사를 감은 커버링사 형태인 것을 특징으로 하는 재귀반사 편사.Sectional retroreflective slit having a width of 0.37 mm or less;
Composite yarns composed of polyester texture yarns of 30d or less,
The retroreflective reflection slit yarn is obtained by slitting a retroreflective sheet on which a polyurethane based adhesive layer, a reflective layer and a glass bead layer are sequentially formed on one surface of a TPU (Thermoplastic Polyurethane) film to a width of 0.37 mm or less,
Wherein the composite yarn is a combined twist yarn composed of a recursive reflecting slit yarn and a polyester texture yarn at a twisting number of 300 to 500 TPM or a covering yarn wound around the polyester texture yarn by judging the recursive reflection slit yarn. 제 1항에 있어서, 상기 재귀반사 슬릿사의 폴리우레탄계 접착제층에 착색 안료가 포함되어 재귀반사 슬릿사가 색상을 갖는 것을 특징으로 하는 재귀반사 편사. The retroreflective knit according to claim 1, wherein the coloring pigment is contained in the polyurethane adhesive layer of the retroreflective slit yarn so that the retroreflective slit yarn has a color. 제 1항에 있어서, 상기 재귀반사 슬릿사는, 프린팅에 의해 색 무늬가 형성된 재귀반사 시트를 슬릿하여 이루어진 위치에 따라 색상이 변하는 것임을 특징으로 하는 재귀반사 편사.2. The retroreflective knit according to claim 1, wherein the color of the retroreflective slit yarn changes depending on the position where the retroreflective sheet having the colored pattern formed by printing is slit. 제 1항 내지 제 3항 중 어느 한항에 따른 재귀반사 편사로 편성된 부분을 포함하여 이루어진 것을 특징으로 하는 재귀반사 편성물.A retroreflective knitted fabric comprising a portion knitted with a reflex reflective knitting yarn according to any one of claims 1 to 3.
KR1020150044060A 2015-03-30 2015-03-30 Kintting yarn having retroreflectivity and retroreflective knitted fabric using the same KR101691435B1 (en)