KR20160112326A

KR20160112326A - Antistactic agnet for polyurethane form and articles of polyurethane form having antistactic properties using the same

Info

Publication number: KR20160112326A
Application number: KR1020150037912A
Authority: KR
Inventors: 김태호; 홍영택; 이장용; 유덕만; 김석제; 윤상준
Original assignee: 한국화학연구원
Priority date: 2015-03-19
Filing date: 2015-03-19
Publication date: 2016-09-28
Also published as: KR101733081B1

Abstract

The present invention relates to preparation of a polyurethane foam having a permanent antistatic function and manufacture of a boxy for electronic parts using the polyurethane foam. Particularly, the present invention relates to preparation of an internal addition type antistatic agent, which causes no leakage of an antistatic additive, and thus has no problem of contamination of a product stacked in a packaging material obtained by using the same, and allows the packaging material to be used permanently until it cannot be used any longer due to physical damages. The present invention also relates to preparation of an antistatic polyurethane foam to which the antistatic agent is added, and manufacture of a box for packaging electronic parts using the polyurethane foam. The permanent antistatic agent according to the present invention comprises a linear polyurethane polymer having a molecular weight of several hundred thousands and lithium ions, has excellent durability and causes no leakage, and thus imparts a permanent antistatic function to a polyurethane foam.

Description

TECHNICAL FIELD [0001] The present invention relates to an antistatic agent for polyurethane, and an antistatic agent for antistatic properties using polyurethane foam,

The present invention relates to a novel antistatic agent composition for imparting an antistatic function to a polyurethane foam and a polyurethane molded article to which an antistatic function is imparted by using the antistatic agent composition. More particularly, the present invention relates to a novel antistatic agent composition containing polyethylene glycol in a molecular structure An antistatic agent composed of a mixture of a polyurethane linear polymer and an alkali metal salt, and an antistatic functional water-foamed polyurethane foam prepared by the above antistatic agent, and a polyurethane foam, It is about.

Materials required for the packaging of electronic products or parts, such as semiconductors and LCDs, should not contain any emission of contaminants and the surface should contain adequate antistatic function. Contamination release or surface release can contaminate the product or the component itself and become a defect factor. An appropriate level of surface electrification is a necessary performance to prevent short-circuiting of the product and to prevent the occurrence of defects due to dust adsorption.

Currently used packaging boxes and cases for semiconductor wafers, LCD glasses, and other electronic parts are made by injection molding with polycarbonate, polypropylene, polyethylene resin, etc. and then coated with a conductive polymer such as antistatic treatment. The antistatic function should be added in order to avoid the surface charge due to the insulating property of the plastic. If there is no surface antistatic function, static electricity is generated in a normal external environment, especially in a clean room environment of low temperature and low humidity, Or the occurrence of defects due to adhesion of dust or foreign matter.

Conventionally, as a method of imparting antistaticity to a resin, a method of coating an antistatic agent made of a conductive substance, an ionic substance or the like on the surface of the resin molded article or adding the antistatic agent to the resin has been carried out. Examples of applications of these methods to polyurethane resins include: 1) a method of adding carbon black or a conductive filler, 2) a method of applying or adding an ionic surfactant, 3) a method of adding perchloric acid, thiocyanic acid, (Japanese Unexamined Patent Publication No. 63-43951 and Japanese Unexamined Patent Publication No. 4-298517), 4) a method of adding quaternary ammonium alkyl sulfate or quaternary ammonium perchlorate 4-298517 and 4-298518), 5) nonmetal antistatic compounds such as quaternary ammonium substituted sulfonic acid, metal antistatic compounds such as sulfonic acid metal salts, and methods of adding polar organic solvents, etc. (JP-A-2001-329253).

However, in the method 1) in which a conductive filler or the like is added, when added to a polyurethane raw material, the viscosity is remarkably increased, and thus there is a problem in moldability. In addition, the method 2) in which an ordinary ionic surfactant is added singly can not impart sufficient antistatic property. In addition, when perchlorate, thiocyanate, etc. are used alone in the method 3) in which perchlorate, thiocyanate, or the like is added, the resulting emulsion exhibits antistatic property, but the final performance of the molded article is insufficient. In addition, in the method 4) of adding quaternary ammonium alkyl perchlorate, the expression of the antistatic property immediately after molding is delayed, the final performance of the molded article is highly dependent on the humidity, and sufficient antistatic property is obtained under low temperature and low humidity conditions I could not get it.

For these methods, a polar organic solvent such as cyclic carbonic ester such as formamide, ethylene carbonate, and propylene carbonate is added to a mixture of a nonmetal antistatic compound and a metal antistatic compound in order to exhibit excellent antistatic performance even under a low temperature condition A method of adding an antistatic agent composition to a polyurethane has been proposed. However, if formamide or cyclic carbonic ester is added to the polyurethane resin or the polyol as the resin raw material, they may bleed out after molding and the storage stability may be deteriorated. In particular, since formamide affects the safety of the human body There is a hygiene problem. The cyclic carbonic ester is decomposed easily when heated in the presence of a catalyst. Therefore, when it is premixed with a polyol component as a raw foaming solution, a molded product with stable physical properties can not be obtained due to abnormal foaming behavior with time, There was a practical problem in line production.

On the other hand, the most widely used method of antistatic method on the surface of the packaging material for the electronic industry is to process the packaging material in the form of a box, a sheet, a film, or the like, and then to apply a conductive polymer such as PEDOT . The other is to add an antistatic additive to the polymer matrix, such as ionic materials including ionic polymers, surfactants, and the like. The ionic material itself is often conductive, so that it forms an antistatic function by networking on the surface of the polymer after the injection molding. The surfactant migrates to the surface of the molding and adsorbs the moisture in the air, By forming a moisture film, an antistatic function is imparted to the surface of the molded article.

Korean Patent No. 10-065811 discloses a polyurethane resin foamed body prepared by using a sulfonic quaternary ammonium-based cationic antistatic compound and a metal salt-based anionic antistatic compound, .

However, since most of the polymers have hydrophobic properties, compatibility with hydrophilic substances such as ionic materials including ionic polymers and surfactants is poor, and migration due to surface migration of the added hydrophilic material It is difficult to overcome the phenomenon originally. Particularly, in the case of general surfactants, the dissolution rate is fast and wide, and the contamination of the surface of the molded article is seriously generated, so that it is hardly applied in the electronic industry which requires high clarity. For this reason, in the electronic industry, which is currently required to thoroughly manage pollution and manage foreign objects, despite the various advantages of the anti-static antistatic agent, most of the antistatic packing materials manufactured by the method of reminiscing the surface of the molded part to conductive polymer It is in use.

On the other hand, in the case of an LCD packaging box used for carrying an LCD glass, the LCD glass part is packed with an antistatic polyolefin film, and then a buffer such as an EPS is put into a paper box. This is a troublesome operation requiring various steps, which causes a rise in the cost of the product. However, polyurethane foam is suitable for making various packing boxes in box or sheet form due to low price per unit volume, light weight and elasticity, and it is suitable for packaging of cracked or fragile products such as LCD glass parts In addition, since it is a suitable packing material because of its elasticity on the surface, if the characteristic inherent to the polyurethane foam is added to the permanent antistatic property, the optimum packing material for storing and transporting the product in a single operation requiring no multi- Which will greatly increase its usability.

Japanese Patent Laid-Open No. 63-43951 Japanese Patent Application Laid-Open No. 4-298517 Japanese Patent Application Laid-Open No. 4-298518 Japanese Patent Laid-Open No. 2001-329253 Korean Patent No. 10-0658111

The present invention provides permanent antistatic properties to a polyurethane foam formed article having a suitable strength and elasticity on the surface thereof and capable of replacing various materials in the packaging of a product, and a polyurethane foam molded article having such antistatic properties And an antistatic agent for polyurethane which can utilize a packaging box and a packaging sheet for a product.

Another object of the present invention is to provide a novel polyurethane foam having an antistatic function using a water-blowing method in which a mixture containing an antistatic agent for polyurethane and an antistatic agent is foamed with water To provide a molded article.

It is still another object of the present invention to provide a polyurethane foam molded article having an antistatic function including a skin layer of a silicone-based polymer.

In order to achieve the above object, the antistatic agent for polyurethane of the present invention may include a polyurethane linear polymer and a metal salt containing polyethylene glycol in a molecular structure, and the antistatic agent for polyurethane may further include polyethylene glycol .

The polyurethane foam molded article according to one aspect of the present invention may be foam molded using a mixture of an antistatic agent, a polyol, and a diisocyanate for the polyurethane, and the mixture may further comprise a trimerized ammonium salt as a catalyst.

The foam molding according to an aspect of the present invention may be water-blowing using water, and the polyurethane foam molding may further include a skin layer of a silicone-based polymer.

The present invention relates to a method for producing a polyurethane foam having a permanent antistatic function by using a polyurethane linear polymer containing polyethylene glycol in a molecular structure and an antistatic agent for polyurethane which comprises an alkali metal salt as a main component, As a result of demonstrating the molding processability of such permanent antistatic polyurethane foam, it is possible to provide a new type of packaging material that is economical and environmentally friendly compared to the current semiconductor electronic parts and products that are subjected to various working steps using this material Can be applied.

The present invention relates to an antistatic agent for polyurethane, which is capable of imparting permanent antistatic property to a polyurethane foam molded article and capable of utilizing such a antistatic polyurethane foam molded article as a packaging box for electronic products and a packaging sheet.

The present invention also relates to a novel polyurethane foam molded article having an antistatic function using a water-blowing method in which a mixture containing an antistatic agent for polyurethane and an antistatic agent is foamed with water will be.

The present invention also relates to a polyurethane foam molded article to which an antistatic function is imparted including a skin layer of a silicone-based polymer.

In addition, the polyurethane foam molded article to be applied in the present invention is a water-foamed polyurethane foam using water as a foaming agent, unlike the conventional foaming agents such as HFC, HCFC, and cyclopentane.

Hereinafter, the present invention will be described in more detail with reference to Examples.

The present invention provides a technique relating to the production of an antistatic agent for polyurethane suitable for a polyurethane foam molded article and the production of a polyurethane foam box produced by molding a polyurethane foam containing the antistatic agent thus prepared.

The antistatic property of the polymer is achieved by coating a conductive material on the surface or adding an antistatic agent to the polymer raw material during processing. However, antistatic additives that are more compatible with the target polymer than surface coatings are not common. Therefore, the anti-static antistatic agent is generally used only for the purpose of producing a temporary antistatic effect of the product, or for the preparation of an antistatic packaging material having no particular problem even if there is surface elution. The representative is dodecyl sulfate as dissolution occurs within the can at room temperature for one as a surface active agent and the antistatic effect of 10 ⁸ to 10 the surface resistance required for the usual Semiconductor component of the normal 10 ¹⁰ Ω / sq or more, such as It is difficult to implement ⁹ Ω / sq.

In contrast, the permanent antistatic agent provided in the present invention is a mixture of a polyurethane linear polymer containing polyethylene glycol and a lithium salt in a molecular structure, and the polyurethane linear polymer containing polyethylene glycol in the molecular structure is a polyurethane And has a higher molecular weight than a general surfactant. Therefore, after being mixed into a polyurethane foam matrix, it is semi-permanently present in the matrix and does not dissolve. Participating lithium ions are present along the polyethylene glycol molecules existing between the urethane functional groups The ion jumping mechanism can exhibit the surface antistatic function.

The antistatic agent for polyurethane of the present invention comprises 70 to 90 parts by weight of a linear polyurethane containing polyethylene glycol in a molecular structure, 5 to 15 parts by weight of polyethylene glycol and 2 to 7 parts by weight of an alkali metal salt, The liquid silicone dispersant preferably comprises 3 to 8 parts by weight. These mixtures were sufficiently stirred with strong stirring to prepare an antistatic agent for polyurethane. The antistatic agent is preferably added in an amount of 5 to 10% by weight based on the polyol component in the production of the polyurethane foam.

The linear polyurethane comprising polyethylene glycol in the molecular structure of the present invention can be prepared according to the following Reaction Scheme 1 by the reaction of diisocyanate with polyethylene glycol, and the diisocyanate used is preferably diphenylmethane diisocyanate (MDI) And polyethylene glycol (PEG) has a molecular weight (the degree of polymerization n is 6 to 22) in the molecular weight range of 300 to 1,000 g / mol.

The linear polyurethane comprising polyethylene glycol in the molecular structure prepared according to the above Reaction Scheme 1 preferably has a molecular weight of 200,000 to 300,000 g / mol. Although the linear polyurethane is excellent in compatibility with the polyurethane foam, which is a matrix, when the molecular weight is less than 200,000 g / mol, the continuity between the polyethylene glycols contained in the linear polyurethane is low, so that the added alkali metal ions are contained between the urethane functional groups It is difficult to exhibit the surface antistatic function by the ion jumping mechanism along the existing polyethylene glycol molecule whereas when the molecular weight exceeds 300,000 g / mol, the molecular weight increase of the polyethylene glycol molecule contained in the molecular structure of the linear polyurethane The compatibility with the polyurethane foam according to the present invention may be deteriorated.

In the antistatic agent provided in the present invention, a polyurethane linear polymer containing polyethylene glycol in a molecular structure and an alkali metal salt and a high molecular weight polyethylene glycol may be partially added. This not only improves the compatibility between the polyurethane linear polymer containing polyethylene glycol and the polyurethane foam matrix formed in the foam formation process in the molecular structure with the alkali metal ion attached thereto, but also enhances the mobility of alkali metal ions and the antistatic property It helps to appear.

It is more preferable that the polyethylene glycol to be added has a molecular weight of 200,000 g / mol to 1,000,000 g / mol. In particular, the addition of a high molecular weight polyethylene glycol is more effective when the molecular weight of the polyurethane linear polymer containing polyethylene glycol in the molecular structure is large.

The alkali metal salt of the present invention are _{LiPF 6, LiBF 4, LiSbF 6} , LiClO 4, LiCF 3 SO 3, LiAsF 6, LiC (CF 3 SO 3) 3, LiN (CF 3 SO 3) 2, LiI, LiBr, LiCl , LiF, NaPF ₆ , NaClO ₄ , NaI, NaSCN, KSCN, KPF ₆ and KClO ₄ . The alkali metal salt is more preferably a lithium salt, more preferably _{LiN (CF 3 SO 3) 2} .

The polyurethane foam is produced by the reaction of a diisocyanate and a polyol. The foam is formed simultaneously with the polyurethane formation by the gas which is volatilized before and after the reaction with the two monomers. Polyurethane foam is used not only as an advanced insulating material and filler due to its excellent physical strength, flame retardancy, heat insulation and moisture permeability but also being applied to various products by using light weight. Generally, the polyurethane foam is capable of producing a hard molded body having a hard strength such as an ordinary polymer, from a very soft softness by adjusting the expansion ratio.

The foaming of the polyurethane generally refers to the third foaming gas. The foaming gas is the ozone-depleting substance. Freon, the first-generation foaming gas that is currently prohibited for use worldwide, has a relatively low degree of destruction of the ozone layer, Generation Foam Gas such as HFC-365fc, which does not cause ozone depletion but has a recent explosion risk, but is considerably cheaper than the third generation HFC gas, and the Global Warming Index Cyclopentane and the like are also used. The second-generation HCFC-141b is not used in developed countries. In developing countries, usage is determined according to the quota, and annual usage is decreasing. Third generation foam gas has global warming problem, but more than 10,000 won per kg It is not widely used for the production of polyurethane foam. On the other hand, large companies that can put specifications for explosion prevention facilities or safety management during manufacturing operations use cyclopentane as a foaming gas widely. Nevertheless, cyclopentane is dangerous for many small and medium-sized polyurethane foam makers, and since foam characteristics are not stable, small and medium-sized companies still use 141b as the main foaming gas roll.

The water-foamed polyurethane foam according to the present invention is a foam prepared by using water as a blowing agent. It does not cause foaming by water vapor formed by evaporation of water, but rather reacts water and isocyanate to cause carbon dioxide Gas to form the foam. The basic reaction of urethane and the reaction of water with isocyanate are shown in the following reaction formula 2.

(1) Basic reaction of urethane

R-OH + R'-NCO R'-NHCOOR

(2) Reaction between water and MDI

Carbon dioxide generation reaction: HOH + R'-NCO R'-NH ₂ + CO ₂

Urea _{reaction: R'-NH 2 + R '} ' - NCO R '' - NHCONH-R '( Urea reaction)

Burette reaction: R "-NHCONH-R '+ R" -NCO R "-NHCON (CONH-R') R"

When water reacts with isocyanate, carbon dioxide is generated and this carbon dioxide expands the reaction mixture and makes it cell structure. Although water can be useful in the production of flexible polyurethane foams, in the case of rigid polyurethane foams, the physical properties and cell structure of the resulting foam are poor in quality and are expensive, However, in the method of producing a rigid polyurethane foam using water and a foaming agent, as shown in the above formula (2), the isocyanate functional group is destroyed by water, and an amine is formed. It is difficult to control the molecular weight and cross-linking density of the resultant polyurethane due to the isocyanate reaction with the isocyanate and the formation of the cells constituting the foam due to the instability of crosslinking is uneven and is not closed, cell is a general foam gas It is formed relatively much in comparison with the use form. As a result, water-foamed polyurethane foam is inferior to general foamed polyurethane foam in terms of mechanical strength, surface elasticity, and heat insulating property, so that it can not be used as an actual structural material or an insulating material.

In the present invention, polyurethane foam is produced by water blowing because the water blowing method is more environment-friendly than the conventional gas blowing, the production process is stable, and the manufacturing cost is advantageous. In the present invention, in order to overcome the above-mentioned general disadvantages of the water-foamed polyurethane foam, unlike general water-blowing raw materials, an amine compound known as a trimerization catalyst or gelling catalyst together with a diamine Respectively.

The amine compound as the trimerization catalyst of the present invention is preferably at least one selected from the group consisting of tetraethylenediamine, dimethylethylamine and tetraethylenediamine. Among these amines, dimethylethylamine is more preferable.

The main components of the raw material composition of the water-blown polyurethane foam used in the present invention are 100 parts by weight of polyol, 200 parts by weight of diisocyanate, 2 parts by weight, the foaming agent 3 parts by weight, and water 5 parts by weight. However, each component can be scaled according to the elasticity and strength conditions of the foamed molding, and other small amounts of additives can be added. The antistatic agent prepared for antistatic treatment is preferably added in an amount of 5 to 10% by weight based on the polyol component in the production of the polyurethane foam.

The polyurethane foam used in the present invention preferably has a foaming ratio of 20 to 45 times (volume ratio of foam relative to the liquid material) and a specific gravity of 33 to 50 kg / m ³ because if the expansion ratio is too high, If the magnification is too low, the elasticity of the surface may fall and the semiconductor or LCD parts inside the packaging material that is sensitive to impact during transportation or work may be broken.

The polyurethane foam molded article according to the present invention facilitates the detachment of the molded article from the mold by applying the surface of the mold with the silicone-based polymer releasing agent during the production of the polyurethane molded article for the surface strength and elasticity, Was bonded to the polyurethane foam on the surface of the box or sheet-like packaging case, which is the result of the foaming molding, so that the surface of the silicone polymer was prevented from being crushed or hardened by forming the skin.

Hereinafter, the present invention will be described in further detail with reference to the following examples. However, the present invention is not limited by the following examples and comparative examples.

Example 1: Preparation of antistatic agent

A polyurethane linear polymer (weight average molecular weight 270,000) containing polyethylene glycol in a molecular structure in which diphenylmethane diisocyanate (MDI) and polyethylene glycol (PEG) having an average molecular weight of 600 g / mol (average degree of polymerization 13) parts by weight of polyethylene glycol (average molecular weight: 200,000) 10 parts by weight of lithium bis-tree with methanesulfonic mid fluoro _{(LiN (CF 3 SO 3)} 2) 5 parts by weight of a silicone-based dispersant 5 parts by weight of 8,000 rpm was placed into a mixer Or more for 10 minutes to obtain a powdery antistatic agent mixture.

Example 2: Preparation of antistatic polyurethane foam

300 g of a polyol (YD-4110A, China YD Chemicals), 6.0 g of a foam stabilizer, 90 g of a flame retardant TCPP (Tris-2-chloropropyl phosphate), 4.5 g of dimethylethylamine as an amine catalyst, 15.0 g of water, A mixture of 28 g of the mixture (preferably an antistatic agent in an amount of about 7 wt% of the total weight) was stirred vigorously to obtain a uniform mixed solution. 390 g of diphenylmethane diisocyanate (MDI) was further added to the resulting mixture to obtain 15 After vigorously stirring for a few seconds, the surface was poured into a 20 L plastic container coated with silicone release polymer. The foaming proceeded for about 5 minutes to obtain a polyurethane foam. The specific gravity of the obtained polyurethane foam was 36 kg / m ³ . When the production conditions of the antistatic polyurethane foam were varied, antistatic polyurethane foam having a specific gravity of 35 to 40 kg / m ³ was obtained. The flexural strength was 38 N / cm ² , the compressive strength was 38 N / cm ² , and the surface resistivity was 3 × ^{10 10} Ω / sq (24, 50% relative humidity).

Comparative Example: Production of polyurethane foam

300 g of a polyol (YD-4110A, China YD Chemical), 6.0 g of a foam stabilizer, 90 g of a flame retardant TCPP, 4.5 g of dimethylethylamine as an amine-based catalyst and 15.0 g of water were mixed with vigorous stirring to obtain a uniform viscous solution, Again 390 g of diphenylmethane diisocyanate (MDI) was added and stirred vigorously for 15 seconds and then poured into a 20 L plastic container having a silicone release polymer applied to its surface. The foaming proceeded for about 5 minutes to obtain a polyurethane foam. The specific gravity of the obtained foam was 38 kg / m ³ . The flexural strength was 48 N / cm ² , the compressive strength was 40 N / cm ² , and the surface resistance was 3 × ¹⁰ ¹⁴ Ω / sq (24, 50% relative humidity).

Property evaluation: Antistatic performance evaluation

The polyurethane foam prepared in Example 2 was cut into a size of 100 mm in length, height and height, and then placed in a chamber having a temperature of 80 ° C. and a relative humidity of 90% for 72 hours. The polyurethane foam was washed several times with water, washed once with ethanol Respectively. The measured surface resistance is 5x10 ¹⁰ Ω / sq (24, 50% relative humidity), which shows a resistance value almost similar to that of the initial value, which not only keeps the applied antistatic function constant but also provides the antistatic function (24, 50% relative humidity) of 3 × ^{10 14} Ω / sq, which is the surface resistance of the polyurethane foam.

Example 5: Polyurethane foam packaging box molding

The polyurethane foam molded article was prepared by mixing the polyol mixture obtained in the same manner as in Example 2 with isocyanate and then measuring the size of the outer wall of each of 200 mm x 200 mm x 150 mm in height and width, 170 mm x 170 mm x 150 mm, and the upper part of the mold, which was made of SUS steel sheet having a thickness of 1 mm, was placed on a flat metal plate having a width of 250 mm and a width of about 250 mm. At this time, the inner portion of the mold was previously coated with a silicone-based polymer releasing agent. After 10 minutes, it was judged that the foaming was completed and sufficient time had elapsed. The mold was removed to cut off the foam formed on the mold height, and then the outer wall made of a wall having a thickness of 15 mm was polished with 200 mm, 200 mm, A urethane foam box was obtained.

The prepared polyurethane foam box had a silicone-based polymer skin on the outer surface of the polyurethane foam, and the polyurethane foam box in which the silicone-based polymer skin was present was surface-damaged or hardened due to the quality of the additional surface skin layer, Can be prevented.

Claims

An antistatic agent for polyurethane, which comprises a polyurethane linear polymer containing polyethylene glycol and an alkali metal salt in a molecular structure.

The method according to claim 1,
Wherein the antistatic agent further comprises polyethylene glycol.

The method according to claim 1,
Wherein the polyurethane linear polymer has a molecular weight of 200,000 g / mol to 300,000 g / mol.

The method of claim 2,
Wherein the polyethylene glycol has a molecular weight of 200,000 g / mol to 1,000,000 g / mol.

The method according to claim 1,
The alkali metal salt may be at least one selected from the group consisting of LiPF ₆ , LiBF ₄ , LiSbF ₆ , LiClO ₄ , LiCF ₃ SO ₃ , LiAsF ₆ , LiC (CF ₃ SO ₃ ) ₃ , LiN (CF ₃ SO ₃ ) ₂ , LiI, LiBr, NaPF ₆ , NaClO ₄ , NaI, NaSCN, KSCN, KPF ₆ , KClO _4, and the like.

An antistatic agent according to any one of claims 1 to 5;
Polyols; And polyisocyanate, and a mixture of polyisocyanate and diisocyanate.

The method of claim 6,
Wherein the antistatic agent is used in an amount of 5 to 10% by weight based on the weight of the polyol.

The method of claim 6,
Wherein the mixture further comprises dimethylethylamine as an amine compound as a trimerization catalyst.

The method of claim 6,
Wherein the foam molding is a water-blowing method of foaming using water. &Lt; RTI ID = 0.0 > 11. < / RTI >

The method of claim 6,
Wherein the polyurethane foam molding comprises a skin layer of a silicone-based polymer.