KR20140122887A - Internal mold release agent of silicon rubber and silicon rubber moldings using the same - Google Patents
Internal mold release agent of silicon rubber and silicon rubber moldings using the same Download PDFInfo
- Publication number
- KR20140122887A KR20140122887A KR1020130039888A KR20130039888A KR20140122887A KR 20140122887 A KR20140122887 A KR 20140122887A KR 1020130039888 A KR1020130039888 A KR 1020130039888A KR 20130039888 A KR20130039888 A KR 20130039888A KR 20140122887 A KR20140122887 A KR 20140122887A
- Authority
- KR
- South Korea
- Prior art keywords
- silicone rubber
- release agent
- weight
- parts
- fatty acid
- Prior art date
Abstract
Description
본 발명은 실리콘고무의 내부 이형제 조성물 및 이를 이용한 실리콘고무 성형물에 관한 것으로서, 보다 상세하게는 실리콘고무의 성형시 실리콘고무에 첨가되는 실리콘고무의 내부 이형제 조성물 및 이를 이용한 실리콘고무 성형물에 관한 것이다.The present invention relates to an internal release agent composition for a silicone rubber and a silicone rubber molded article using the same. More particularly, the present invention relates to an internal release agent composition for a silicone rubber added to a silicone rubber when molding the silicone rubber, and a silicone rubber molded article using the same.
실리콘(silicone)은, 내열성, 내한성, 내후성, 전기절연성, 이형성, 발수성등 일반 유기계 폴리머와 다른 특이한 성질을 가지며, 오일(액체상), 레진(고체상), 고무상 등과 같은 다양한 제품형태를 나타내며, 산업계에 널리 보급되어 다양한 분야에 사용되고 있다.Silicone has various properties such as oil (liquid phase), resin (solid phase) and rubber phase, which are different from general organic polymers such as heat resistance, cold resistance, weather resistance, electrical insulation, releasability and water repellency. And has been used in various fields.
실리콘은, 일반적으로 실록산 결합을 골격으로 구성되어 있고, 그 규소원자에 유기기 등이 직접 결합한 유기규소 고분자 화합물을 총칭한다. 하지만, 출발물질인 오르가노실란, 폴리머인 폴리오르가노 실라잔, 폴리오르가노실란 등도 넓은 의미에서의 실리콘에 포함된다.Silicon is generally referred to as an organosilicon polymer compound having a skeleton of a siloxane bond and an organic group directly bonded to the silicon atom. However, organosilane as a starting material, polyorganosilazane as a polymer, polyorganosilane and the like are also included in silicon in a broad sense.
실리콘의 제품형태를 보면, 실리콘 오일, 실리콘 2차제품(그리스, 소포제, 이형제, 섬유처리제 등), 실리콘 레진, 실리콘 고무, 실란커플링제 등으로 분류된다.Silicone oil, silicone secondary products (grease, defoamer, release agent, fiber treatment agent, etc.), silicone resin, silicone rubber, and silane coupling agent are classified into silicone product types.
특히, 실리콘고무는 내열성, 내한성, 전기절연성, 압축복원성, 기밀성, 반발탄성, 무독성이 우수하여, 초내열 내한용 팩킹, 가스켓, 전기전열, 전선보호 팩킹, 무독성 식품패킹, 건축용 팩킹, 전파장애용 팩킹실드, 기계장치 및 자동차 팩킹, 및 기타 내열 및 내한 전기절연 부품 등으로 사용되고 있다.Particularly, silicone rubber has excellent heat resistance, cold resistance, electrical insulation, compressive stability, air tightness, rebound resilience and non-toxicity, and is used for ultra heat resistant cold resistant packing, gasket, electric heat, wire protection packing, Packing shields, machinery and automobile packing, and other heat-resistant and cold-weather electrical insulating parts.
이러한 실리콘고무는, 제조공장에서 미리 일정한 형상으로 성형설비에 의해 성형되어 제조되거나 경화성 실리콘 조성물을 현장에서 경화하여 실리콘 경화물로서 제조되는 것이 일반적이다.Such a silicone rubber is generally manufactured in a molding factory by molding equipment in a predetermined shape in a manufacturing factory, or is generally produced as a silicone cured product by curing the curable silicone composition in situ.
실리콘고무를 성형설비에 의해 소정형상으로 성형하여 제품화하는 경우에는, 성형설비의 금형에서 성형된 실리콘고무의 탈형시 실리콘고무 성형물의 일부가 금형에 부착되어 실리콘고무 성형물이 탈형불량에 의해 손상되는 문제점이 있다. In the case of molding a silicone rubber into a predetermined shape by molding equipment, a part of the silicone rubber molding adheres to the mold when the silicone rubber molded in the mold of the molding equipment is demoulded, thereby causing the silicone rubber molding to be damaged .
이러한 탈형불량에 의한 실리콘고무 성형물의 손상을 방지하기 위해 실리콘고무의 성형작업시 이형제를 사용하게 된다. 이러한 이형제로는 성형 금형에 도포되는 외부 이형제와, 성형작업 전에 실리콘고무에 첨가되어 배합되는 내부 이형제로 분류된다. In order to prevent the silicone rubber molding from being damaged due to such defective mold release, a release agent is used in the molding operation of the silicone rubber. Such releasing agents are classified into an external releasing agent to be applied to a forming die and an internal releasing agent to be added to the silicone rubber before the molding operation.
외부 이형제는 성형시마다 금형의 내부 표면에 도포할 필요가 있기 때문에 성형물의 생산성이 나쁘고, 외부 이형제가 성형물 표면으로 이행하여 성형물 표면에 얼룩을 생기게 하거나, 도장 및 염색 불량을 일으키며, 더욱이 성형물에 주름무늬를 발생시키는 등의 문제점이 있다.Since the external mold release agent needs to be applied to the inner surface of the mold every time it is molded, the productivity of the molded article is poor, the external release agent migrates to the surface of the molded article, causing stains on the surface of the molded article, causing paint and dyeing defects, And the like.
한편, 내부 이형제는 실리콘고무 원료에 미리 첨가하는 이형제로서, 성형시 매회 금형에 도포할 필요가 없으므로 생산성 향상에는 유리하다는 장점이 있어, 최근에 실리콘고무의 성형시 내부 이형제가 주로 사용되고 있다.On the other hand, the internal mold release agent is a mold release agent previously added to the silicone rubber raw material, and since it is not necessary to apply it to the mold every time of molding, there is an advantage that productivity is improved, and internal mold release agent is mainly used in molding silicon rubber recently.
이러한 종래의 내부 이형제로는, 불소계 비이온 계면 활성제, 실리콘계 비이온 계면 활성제, 산성 인산 에스테르, 유동 파라핀, 왁스, 지방산의 금속염, 고급 지방족 알콜, 비스아미드류, 폴리실록산류, 지방족 아민 에틸렌옥시드 부가물 등이 사용되고 있다.Examples of such conventional internal release agents include fluorine-based nonionic surfactants, silicone-based nonionic surfactants, acidic phosphate esters, liquid paraffin wax, metal salts of fatty acids, higher aliphatic alcohols, bisamides, polysiloxanes, aliphatic amine ethylene oxide adducts Water and the like are used.
그러나, 종래의 내부 이형제는 외부 이형제에 비하여 생산성 향상에 있어서 유효하지만, 충분한 이형 성능을 갖고 있지 못하여, 이형시에 주형 표면에 실리콘고무가 잔존하거나, 박리를 일으키는 문제가 있다.However, the conventional internal mold release agent is effective in improving the productivity as compared with the external mold release agent, but does not have sufficient mold release performance, and there is a problem that the silicone rubber remains on the mold surface at the time of mold release or peeling occurs.
또한, 이형시의 저항으로 과도하게 큰 응력이 걸려서 성형물이 휘어지거나 비틀려 버리는 경우가 있었다. 더욱이, 이형성을 충분히 만족시키는 사용량에 있어서는 성형물에 흐름무늬가 생기기 쉬운 문제가 있다.In addition, excessive excessive stress is applied to the molded article due to the resistance at the time of mold release, resulting in warping or twisting of the molded article. Furthermore, there is a problem that flow patterns tend to be formed in the molded product when the amount of use sufficiently satisfying the releasability is present.
또한, 종래의 내부 이형제는 내화학성이 강한 이유로 부식성이 거의 없어, 자연 상태, 즉, 토양에 묻히거나 하천 등에 버려지게 되면, 전혀 썩지 않으므로, 토양 및 수질을 오염시켜, 자연환경을 훼손시키게 되는 매우 심각한 환경오염을 유발하는 문제가 있다.In addition, the conventional internal release agent has little corrosiveness due to its strong chemical resistance, and when it is buried in the soil or buried in a river or the like, it does not rot at all. Therefore, it contaminates the soil and water quality, There is a problem that causes serious environmental pollution.
본 발명은 상기와 같은 종래의 문제점을 해소하기 위해 안출한 것으로서, 실리콘고무의 성형시 이형성능을 향상시켜 실리콘고무 성형물의 손상을 방지할 수 있고, 혼합을 용이하게 하는 계면활성기능 및 대전을 방지하는 대전방지기능을 향상시킬 수 있고, 내부 이형제를 친환경적인 성분으로 구성하여 자연 분해성이 향상되는 동시에 이로 인해 환경오염을 감소시킬 수 있고, 실리콘고무와의 배합성을 향상시키는 동시에 실리콘고무의 고유특성을 그대로 유지할 수 있는 실리콘고무의 내부 이형제 조성물 및 이를 이용한 실리콘고무 성형물을 제공하는 것을 그 목적으로 한다. Disclosure of the Invention The present invention has been devised to overcome the above-described problems of the prior art, and it is an object of the present invention to provide a silicone rubber composition which can improve mold release performance during molding of silicone rubber to prevent damage to the molded silicone rubber, It is possible to improve the antistatic function of the silicone rubber and to improve the natural decomposability by constituting the internal release agent as an environmentally friendly component, thereby reducing the environmental pollution and improving the compatibility with the silicone rubber, The present invention also provides a silicone rubber molded article using the same.
상기와 같은 목적을 달성하기 위한 본 발명은, 실리콘고무의 성형시 실리콘고무에 첨가되는 실리콘고무의 내부 이형제 조성물로서, 85∼95 중량부의 1종 이상의 식물성 오일; 및 5∼15 중량부의 1종 이상의 4∼10 몰농도의 지방산;을 포함하는 것을 특징으로 한다.In order to accomplish the above object, the present invention provides an internal release agent composition for a silicone rubber, which is added to a silicone rubber when the silicone rubber is molded, comprising: 85 to 95 parts by weight of at least one vegetable oil; And 5 to 15 parts by weight of at least one fatty acid at a concentration of 4 to 10 moles.
본 발명의 상기 식물성 오일은, 상기 식물성 오일 100 중량부를 기준해서 단일 불포화 또는 다중 불포화 C10-C22 지방산의 트리글리세리드를 70 중량부 이상 함유한다.The vegetable oil of the present invention contains at least 70 parts by weight of triglycerides of monounsaturated or polyunsaturated C10-C22 fatty acids based on 100 parts by weight of the vegetable oil.
본 발명의 상기 지방산은, 에톡실화 C10-C22 지방산이다. 본 발명의 상기 식물성 오일은, 팜유, 카카오유 및 야자유 중 1종 이상을 선택한다.The fatty acid of the present invention is an ethoxylated C10-C22 fatty acid. The vegetable oil of the present invention may be at least one selected from palm oil, cacao oil and palm oil.
또한, 본 발명은 상기 기재된 실리콘고무의 내부 이형제 조성물을 이용한 실리콘고무 성형물로서, 실리콘고무 100 중량부를 기준해서 상기 실리콘고무의 내부 이형제 조성물을 0.3∼0.5 중량부 첨가하여 성형한 것을 특징으로 한다.Also, the present invention is a silicone rubber molded product using the silicone rubber inner release agent composition described above, wherein 0.3 to 0.5 parts by weight of the silicone rubber inner release agent composition is added based on 100 parts by weight of the silicone rubber.
이상에서 살펴본 바와 같이, 본 발명은 식물성 오일과 지방산의 혼합 조성물을 실리콘고무의 내부 이형제로 사용함으로써, 실리콘고무의 성형시 이형성능을 향상시켜 실리콘고무 성형물의 손상을 방지할 수 있는 효과를 제공한다.INDUSTRIAL APPLICABILITY As described above, the present invention provides an effect of preventing deterioration of the molded silicone rubber by improving the releasing performance during molding of the silicone rubber by using a mixed composition of a vegetable oil and a fatty acid as an internal releasing agent of the silicone rubber .
또한, 식물성 오일에 불포화 지방산을 함유시키고, 지방산으로 에톡실화 지방산을 사용함으로써, 혼합을 용이하게 하는 계면활성기능 및 대전을 방지하는 대전방지기능을 향상시킬 수 있게 된다.In addition, by containing an unsaturated fatty acid in a vegetable oil and using an ethoxylated fatty acid as a fatty acid, it is possible to improve a surfactant function for facilitating mixing and an antistatic function for preventing electrification.
또한, 식물성 오일로 팜유, 카카오유 및 야자유 등과 같은 채종유를 사용함으로써, 내부 이형제를 친환경적인 성분으로 구성하여 자연 분해성이 향상되는 동시에 이로 인해 환경오염을 감소시킬 수 있게 된다.In addition, by using a vegetable oil such as palm oil, cacao oil and palm oil, the internal release agent can be constituted as an environmentally friendly ingredient to improve the natural decomposability and thereby reduce environmental pollution.
또한, 실리콘고무에 대한 내부 이형제 조성물의 첨가량을 소정량으로 한정함으로써, 실리콘고무와의 배합성을 향상시키는 동시에 실리콘고무의 고유특성을 그대로 유지할 수 있는 효과를 제공한다.Further, by limiting the amount of the internal release agent composition added to the silicone rubber to a predetermined amount, it is possible to improve the compatibility with the silicone rubber and maintain the intrinsic properties of the silicone rubber.
이하, 본 발명의 바람직한 일실시예에 의한 실리콘고무의 내부 이형제 조성물을 더욱 상세히 설명한다. Hereinafter, the silicone rubber inner release agent composition according to a preferred embodiment of the present invention will be described in more detail.
본 실시예의 실리콘고무의 내부 이형제 조성물은 식물성 오일과 지방산을 포함하여 이루어져, 실리콘고무의 성형시 실리콘고무에 첨가되는 실리콘고무의 내부 이형제 조성물이다.The internal release agent composition of the silicone rubber of the present embodiment comprises a vegetable oil and a fatty acid, and is an internal release agent composition of silicone rubber added to the silicone rubber when the silicone rubber is molded.
식물성 오일(vegetable oil)은 85∼95 중량부의 1종 이상의 식물성 오일을 사용하는 것이 바람직하다. 그 이유는 식물성 오일의 함유량이 85 중량부 보다 작으면 실리콘고무의 이형성능이 저하되고, 95 중량부 보다 많으면 실리콘고무의 지지강도가 저하되어 내구성이 저하되기 때문이다.The vegetable oil preferably contains 85 to 95 parts by weight of at least one vegetable oil. If the content of the vegetable oil is less than 85 parts by weight, the releasability of the silicone rubber is deteriorated. If the content is more than 95 parts by weight, the supporting strength of the silicone rubber is lowered and the durability is lowered.
이러한 식물성 오일은, 식물성 오일 100 중량부를 기준해서 단일 불포화(monounsaturted) 또는 다중 불포화(polyunsaturated) C10-C22 지방산의 트리글리세리드(triglyceride)를 70 중량부 이상 함유하는 것이 더욱 바람직하다.It is more preferable that such a vegetable oil contains not less than 70 parts by weight of triglyceride of monounsaturated or polyunsaturated C10-C22 fatty acid based on 100 parts by weight of vegetable oil.
이러한 트리글리세리드는, 화학식 1에 나타낸 바와 같이 탄소에 결합된 R2가 R1 및 R3의 반대편에 위치하기 때문에 저온에서 결정화가 용이하므로, 실리콘고무의 성형시 이형성능을 향상시켜 성형금형에서 실리콘고무의 이형시 손상을 방지할 수 있게 된다.Since triglyceride is located on the opposite side of R1 and R3 bonded to carbon as shown in Formula (1), crystallization is easy at low temperatures, so that the release performance during molding of the silicone rubber is improved, It is possible to prevent damage.
이러한 식물성 오일은, 팜유(palm oil), 카카오유(cacao oil) 및 야자유(coconut oil) 중 1종 이상의 채종유를 선택하는 것이 바람직하다. It is preferable that at least one of the vegetable oils is selected from palm oil, cacao oil and coconut oil.
팜유는, 팜나무의 열매를 압축 채유되는 식물성 기름으로서, 올레산(oleic acid), 팔미트산(palmitic acid), 리놀레산(linoleic acid) 등의 혼합 트리글리세리드를 주성분으로 구성되며, 녹는점이 30∼43℃이다.Palm oil is a vegetable oil which is obtained by compressing palm tree fruit and is composed mainly of mixed triglycerides such as oleic acid, palmitic acid and linoleic acid, and has a melting point of 30 to 43 ° C to be.
카카오유는, 지방산의 조성이 포화산인 스테아린산(Stearic Acid) 및 팔미틴산(palmitic acid)과, 불포화산인 올레산(oleic acid) 및 소량의 리놀산(linolic acid)으로 구성되며, 1, 3-포화, 2-불포화-트리글리세리드를 주성분으로 이루어지며, 녹는점이 35∼36℃이다.Cacao oil is composed of stearic acid and palmitic acid, which are saturated acids, and oleic acid and a minor amount of linolic acid, which are unsaturated fatty acids. It is composed mainly of unsaturated-triglycerides and has a melting point of 35 to 36 ° C.
야자유는, 열대지방의 해안에 자생하는 야자나무 열매의 핵에서 압착에 의하여 채취되는 지방으로서, 로르산글리세리드(lauric acid glyceride)가 주성분으로 구성되고, 소량의 데칸산(decanoic acid)이나 카프릴산(Caprylic acid) 등의 저급 지방산의 글리세리드(glyceride)를 함유하며, 녹는점이 23∼28℃이다.Palm oil is a fat that is extracted from the nucleus of palm fruit that grows on the coast of the tropics by compression and is composed mainly of lauric acid glyceride and contains a small amount of decanoic acid or caprylic acid (Glyceride) of lower fatty acids such as caprylic acid, and has a melting point of 23 to 28 ° C.
또한, 식물성 오일로 사용되는 다른 채종유로는 옥수수유(corn oil)나 해바라기유(sunflower oil) 등과 같이 다양한 식물성 오일을 사용하는 것도 가능함은 물론이다.It is needless to say that various vegetable oils such as corn oil and sunflower oil may be used as other kinds of vegetable oils used as vegetable oil.
옥수수유(corn oil)는 옥수수의 배아에서 추출한 식물성 오일로서, 특히 정재된 옥수수기름은 99%의 트리글리세리드(triglyceride)로 구성되며, 이러한 옥수수기름의 트리글리세리드는 83%의 불포화지방산과 13%의 포화지방산으로 이루어져 있다.Corn oil is a vegetable oil extracted from an embryo of corn. Especially, the corn oil is composed of 99% triglyceride. The triglyceride of this corn oil contains 83% unsaturated fatty acid and 13% saturated fatty acid Lt; / RTI >
해바라기유(sunflower oil)는 해바라기 종자에서 채취되는 건성유로서, 리놀레산(linoleic acid)과 올레산(oleic acid)의 혼합 트리글리세리드가 주성분이며, 특히 리놀레산을 많이 함유하고 있다.Sunflower oil is a dry oil extracted from sunflower seeds. It is mainly composed of mixed triglycerides of linoleic acid and oleic acid. Especially, it contains a lot of linoleic acid.
지방산(fatty acid)은 5∼15 중량부의 1종 이상의 4∼10 몰농도(M)의 지방산을 사용하는 것이 바람직하다. 그 이유는 지방산의 함유량이 5 중량부 보다 작으면 실리콘고무의 지지강도가 저하되어 내구성이 저하되고, 15 중량부 보다 많으면 실리콘고무의 이형성능이 저하되기 때문이다. 또한 지방산의 몰농도가 상기 범위를 벗어나면 식물성 오일과 혼합이 잘 이루어지지 않기 때문이다.It is preferable to use at least one fatty acid having a concentration of 4 to 10 mol (M) of fatty acid in an amount of 5 to 15 parts by weight. If the content of the fatty acid is less than 5 parts by weight, the supporting strength of the silicone rubber is lowered and the durability is lowered. If the content is more than 15 parts by weight, the releasability of the silicone rubber is deteriorated. Also, when the molar concentration of the fatty acid is out of the above range, mixing with the vegetable oil is not performed well.
이러한 지방산으로는, 에톡실화(ethoxylated) C10-C22 지방산을 사용하는 것이 더욱 바람직하다. 이러한 에톡실화 지방산은 혼합을 용이하게 하는 계면활성제 또는 탈형을 용이하게 하는 이형제나 대전을 방지하는 대전방지제 등에 사용된다.As such a fatty acid, it is more preferable to use an ethoxylated C10-C22 fatty acid. These ethoxylated fatty acids are used as surfactants for facilitating mixing, antiseptics for facilitating demixing, and antistatic agents for preventing electrification.
이와 같은 실리콘고무의 내부 이형제 조성물은, PVC 필름이나 PVC 시트 및 폴리올레핀(polyolefine)의 안정제, 건조제, 러버몰드(rubber mold)의 이형 및 윤활제, 분산제 등으로 사용될 수 있다.The internal release agent composition of the silicone rubber may be used as a stabilizer for a PVC film or a PVC sheet and a polyolefin, a drying agent, a release agent for a rubber mold, a lubricant, a dispersant, and the like.
이하, 본 발명의 바람직한 일실시예에 의한 실리콘고무의 내부 이형제 조성물을 이용한 실리콘고무 성형물을 더욱 상세히 설명한다. Hereinafter, the silicone rubber molding using the silicone rubber inner release agent composition according to one preferred embodiment of the present invention will be described in more detail.
본 실시예의 실리콘고무의 내부 이형제 조성물을 이용한 실리콘고무 성형물은, 실리콘고무 100 중량부를 기준해서 상기 실시예의 실리콘고무의 내부 이형제 조성물을 0.3∼0.5 중량부 첨가하여 성형설비에 의해 성형되어 이루어진다.The silicone rubber molded product using the silicone rubber inner release agent composition of the present embodiment is formed by adding 0.3 to 0.5 parts by weight of the inner release agent composition of the silicone rubber of the above example based on 100 parts by weight of the silicone rubber and molded by the molding equipment.
실리콘고무의 성형시 내부 이형제 조성물의 첨가량을 0.3∼0.5 중량부로 한정하는 이유는, 내부 이형제 조성물을 0.3 중량부 보다 적게 첨가하면 실리콘고무의 이형효과가 미미하게 되고, 0.5 중량부 보다 많이 첨가하게 되면 실리콘고무의 고유특성이 저하되기 때문이다.The reason why the amount of the internal release agent composition added to the silicone rubber is limited to 0.3 to 0.5 parts by weight is that when the internal release agent composition is added in an amount of less than 0.3 part by weight, the release effect of the silicone rubber becomes insignificant. The intrinsic properties of the silicone rubber deteriorate.
이러한 실리콘고무 성형물은 성형금형의 형상에 따라 실링재, 패킹재, 절연재 등의 형상으로 다양하게 성형되며, 내열성이 우수하여 항공기나 발열부위의 마감재료로 사용되며, 고무롤러, 패킹재료, 전기 절연재료 등에도 널리 사용된다.Such a silicone rubber molding is molded into various shapes such as sealing material, packing material, and insulating material according to the shape of the molding die and is excellent in heat resistance and used as a finishing material for airplane and heat generating part. Rubber rollers, packing materials, Also widely used.
또한, 실리콘고무의 성형시 첨가되는 안정제로는, CAS Number(Chemical Abstract Service Number)가 557-05-1이며, 분자량(Molecular Weight: MW)이 597인 징크스테아레이트(Zinc Stearate)를 사용하는 것이 바람직하다.As a stabilizer to be added in molding the silicone rubber, it is preferable to use zinc stearate having a Chemical Abstract Service Number (CAS Number) of 557-05-1 and a molecular weight (MW) of 597 desirable.
이러한 징크스테아레이트는, 325 매쉬(mesh)를 99%가 통과하는 백색의 미세 분말로 이루어지며, 습기(moisture)가 최대 0.5%이며, 유리산(free acid)이 최대 0.5%이며, 아연성분(Zn content)이 10.5∼11.5%이며, 녹는점(meltlng point)이 116∼125℃로 구성되어 있다.This zinc stearate is composed of a white fine powder that passes 99% of 325 mesh and has a moisture content of 0.5%, a free acid content of 0.5%, a zinc content Zn content) of 10.5 to 11.5% and a melting point of 116 to 125 캜.
이와 같이 본 발명의 실리콘고무의 내부 이형제 조성물을 이용한 실리콘고무 성형물은, 종래의 금형에서 탈형시 이형불량률이 대략 20% 정도 발생되던 문제가 해소되어 이형불량률이 대략 5% 정도로 감소되어 실리콘고무의 성형시 이형성능이 향상됨을 알 수 있다.As described above, the silicone rubber molded article using the silicone rubber inner mold release composition of the present invention solves the problem that the mold release defect rate is about 20% in the mold removal in the conventional mold, and the mold release defect rate is reduced to about 5% It can be seen that the time-release performance is improved.
이상 설명한 바와 같이, 본 발명에 따르면 식물성 오일과 지방산의 혼합 조성물을 실리콘고무의 내부 이형제로 사용함으로써, 실리콘고무의 성형시 이형성능을 향상시켜 실리콘고무 성형물의 손상을 방지할 수 있는 효과를 제공한다.INDUSTRIAL APPLICABILITY As described above, according to the present invention, by using a mixed composition of a vegetable oil and a fatty acid as an internal release agent for a silicone rubber, it is possible to improve the release performance during molding of the silicone rubber, thereby preventing the damage of the silicone rubber molding .
또한, 식물성 오일에 불포화 지방산을 함유시키고, 지방산으로 에톡실화 지방산을 사용함으로써, 혼합을 용이하게 하는 계면활성기능 및 대전을 방지하는 대전방지기능을 향상시킬 수 있게 된다.In addition, by containing an unsaturated fatty acid in a vegetable oil and using an ethoxylated fatty acid as a fatty acid, it is possible to improve a surfactant function for facilitating mixing and an antistatic function for preventing electrification.
또한, 식물성 오일로 팜유, 카카오유 및 야자유 등과 같은 채종유를 사용함으로써, 내부 이형제를 친환경적인 성분으로 구성하여 자연 분해성이 향상되는 동시에 이로 인해 환경오염을 감소시킬 수 있게 된다.In addition, by using a vegetable oil such as palm oil, cacao oil and palm oil, the internal release agent can be constituted as an environmentally friendly ingredient to improve the natural decomposability and thereby reduce environmental pollution.
또한, 실리콘고무에 대한 내부 이형제 조성물의 첨가량을 소정량으로 한정함으로써, 실리콘고무와의 배합성을 향상시키는 동시에 실리콘고무의 고유특성을 그대로 유지할 수 있는 효과를 제공한다.Further, by limiting the amount of the internal release agent composition added to the silicone rubber to a predetermined amount, it is possible to improve the compatibility with the silicone rubber and maintain the intrinsic properties of the silicone rubber.
이상 설명한 본 발명은 그 기술적 사상 또는 주요한 특징으로부터 벗어남이 없이 다른 여러 가지 형태로 실시될 수 있다. 따라서 상기 실시예는 모든 점에서 단순한 예시에 지나지 않으며 한정적으로 해석되어서는 안 된다. The present invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. Therefore, the above embodiments are merely illustrative in all respects and should not be construed as limiting.
Claims (5)
85∼95 중량부의 1종 이상의 식물성 오일; 및
5∼15 중량부의 1종 이상의 4∼10 몰농도의 지방산;을 포함하는 것을 특징으로 하는 실리콘고무의 내부 이형제 조성물.An internal release agent composition for a silicone rubber added to a silicone rubber during molding of the silicone rubber,
85 to 95 parts by weight of at least one vegetable oil; And
And 5-15 parts by weight of at least one fatty acid at a concentration of 4-10 moles.
상기 식물성 오일은, 상기 식물성 오일 100 중량부를 기준해서 단일 불포화 또는 다중 불포화 C10-C22 지방산의 트리글리세리드를 70 중량부 이상 함유하는 것을 특징으로 하는 실리콘고무의 내부 이형제 조성물.The method according to claim 1,
Wherein the vegetable oil contains at least 70 parts by weight of a triglyceride of a monounsaturated or polyunsaturated C10-C22 fatty acid based on 100 parts by weight of the vegetable oil.
상기 지방산은, 에톡실화 C10-C22 지방산인 것을 특징으로 하는 실리콘고무의 내부 이형제 조성물.The method according to claim 1,
Wherein the fatty acid is an ethoxylated C10-C22 fatty acid.
상기 식물성 오일은, 팜유, 카카오유 및 야자유 중 1종 이상을 선택하는 것을 특징으로 하는 실리콘고무의 내부 이형제 조성물.The method according to claim 1,
Wherein the vegetable oil is at least one selected from palm oil, cacao oil and palm oil.
실리콘고무 100 중량부를 기준해서 상기 실리콘고무의 내부 이형제 조성물을 0.3∼0.5 중량부 첨가하여 성형한 것을 특징으로 하는 실리콘고무 성형물.A silicone rubber molded article using the internal release agent composition of the silicone rubber according to claim 1,
Wherein the silicone rubber is formed by adding 0.3 to 0.5 parts by weight of the internal release agent composition of the silicone rubber based on 100 parts by weight of the silicone rubber.