KR20140115166A - Acrylic Emulsion Comprising Tackifier, Method of Producing the Same and Acrylic Emulsion Adhesive with the Same - Google Patents

Abstract

The present invention relates to an acrylic emulsion including a tackifier, a method for preparing the same and an acrylic emulsion adhesive including the same, and more particularly, to an acrylic emulsion including a tackifier, a method for preparing the same and an acrylic emulsion adhesive including the same, wherein the adhesive comprises (a) a pre-emulsion solution including i) a (meth) acrylic acid ester monomer including an alkyl group having 1 to 12 carbon atoms, ii) at least one monomer selected from the group consisting of allyl ester, vinyl ester, unsaturated acetate and unsaturated nitril, iii) a mixed monomer including at least one monomer selected from the group consisting of an unsaturated carboxylic acid and a hydroxyl group-containing unsaturated monomer and iv) a cross linker; and (b) a tackifier.

Description

TECHNICAL FIELD [0001] The present invention relates to an acrylic emulsion containing a tackifier, a method for producing the same, and an acrylic emulsion tackifier comprising the same,

The present invention relates to an acrylic emulsion containing a tackifier, a process for producing the same, and an acrylic emulsion pressure-sensitive adhesive comprising the same. More particularly, the present invention relates to: (a) , ii) at least one monomer selected from the group consisting of allyl esters, vinyl esters, unsaturated acetates and unsaturated nitriles, iii) a mixed monomer comprising at least one monomer selected from the group consisting of unsaturated carboxylic acids and hydroxyl group-containing unsaturated monomers And iv) a pre-emulsion solution comprising a crosslinking agent; And (b) a tackifier; And a process for producing the acrylic emulsion, and an acrylic emulsion pressure-sensitive adhesive containing the acrylic emulsion.

Recently, the use of sticker-type surface finishing materials such as interior / exterior materials, interior materials, and advertisement materials of a building to which a pressure-sensitive adhesive is applied has been greatly increased. Conventional oil-based pressure-sensitive adhesives, as the pressure-sensitive adhesive, have a problem of causing headache, irritation of the eyes, cough, itching, dizziness, fatigue, loss of concentration, etc. due to the residual solvent being discharged into the air for a long time after the construction And exposure to long-term exposure causes problems with Sick House Syndrome, which causes respiratory diseases, heart disease, cancer, and the like.

For this reason, there is a growing interest in water-based emulsion pressure-sensitive adhesives that are environmentally friendly and do not emit harmful substances by using water as a dispersion medium. The aqueous emulsion pressure-sensitive adhesive can use a polymer having a higher molecular weight than the solvent-based polymer because the viscosity of the pressure-sensitive adhesive and the molecular weight of the dispersion polymer are independent of each other, and the concentration range of the solid content can be widely obtained and the aging resistance is low, It has good adhesiveness in a solid content region and has good compatibility with other polymers.

However, since water is used as a solvent, there is a problem that the drying speed is slow, the adhesiveness to the hydrophobic adhesive surface and the non-porous adhesive agent is low, the selection range of the curing agent is narrow and the initial adhesive force is low, And a dispersant, the water resistance is low and the properties of the adhesive are not as high as those of the oil-based adhesive.

The deterioration of the physical properties of the water-based emulsion pressure-sensitive adhesive is caused by various additives added during the emulsion polymerization and the addition process. The surfactant which imparts stability to the acrylic emulsion is present on the surface of the adhesive resin after coating, And interfere with the coalescence of the acrylic emulsion particles in the pressure-sensitive adhesive at the time of coating, thereby lowering the cohesive force.

Also, a wetting agent that improves the wettability of the surface of the silicone release paper by lowering the surface tension of the pressure-sensitive adhesive is a kind of surfactant, which causes problems similar to those of the surfactant, and defoaming agents and various inorganic additives also affect the physical properties .

On the other hand, a tackifier may be further added to improve the initial adhesion of the water-based emulsion pressure-sensitive adhesive and to increase the adhesion to a low-surface-adherence agent. Examples of the tackifier include rosin, terpene, xylene, . The tackifier having compatibility with the acrylic emulsion in the tackifier improves the tack strength up to 50 parts by weight based on 100 parts by weight of the acrylic emulsion. However, when the tackifier is used in an amount exceeding 50 parts by weight, the tack strength is lowered and the storage stability is lowered.

Usually, the tackifier is prepared by mixing an acrylic emulsion. For reference, U.S. Patent No. 5,623,011 discloses an example of adhesion of a tackifier, wherein the tackifier is used in an amount of 8 to 15 parts by weight based on 100 parts by weight of the adhesive resin, and US Patent Application Publication No. 2007/0167546 discloses a tackifier containing toluene As an example of preparing an adhesive agent and mixing it with an adhesive resin, a protective colloid was applied with an ammonium salt as an emulsifier for stability of the tackifier, Korean Patent Laid-Open Publication No. 2006-0005936 discloses a method in which a rosin- And a method of preparing a pressure-sensitive adhesive by dispersing the pressure-sensitive adhesive in water at a high shear force, and mixing the pressure-sensitive adhesive with water-based pressure-sensitive adhesive resin. Korean Patent Laid-Open No. 2006-0102197 discloses a method for producing an aqueous emulsion pressure-sensitive adhesive for PVC tiles, which comprises adding toluene and rosin in a ratio of 1: 1 to an acrylic emulsion to prepare an aqueous emulsion pressure-sensitive adhesive.

However, in this case, a process for dispersing the tackifier is separately required, and a large amount of surfactant must be used for the dispersion stability of the tackifier, which causes a problem of deterioration of the adhesion by the surfactant.

A method of polymerizing an acrylic emulsion by incorporating the tackifier into an acrylate monomer has also been disclosed. U.S. Patent No. 6,288,148 discloses a method in which a xylene-based tackifier is dissolved in an acrylate monomer to effect emulsion polymerization. The tackifier includes 6 parts by weight of a xylene-based tackifier relative to 100 parts by weight of an acrylic emulsion, and Korean Patent Publication No. 2006-0073805 Discloses an aqueous emulsion pressure-sensitive adhesive for olefin which has a problem of adhesion with low polarity, wherein rosin-modified maleic acid and rosin-modified glycerol ester are used as a tackifier.

However, in this case, there is a problem that it is difficult to make a pressure-sensitive adhesive containing a high-content tackifier due to the problem of reaction stability such as leaching of the tackifier during the reaction.

Therefore, there is a high need for a technique of an acrylic emulsion pressure-sensitive adhesive excellent in initial adhesion and reaction stability.

SUMMARY OF THE INVENTION It is an object of the present invention to solve the above-described problems of the prior art and the technical problems required from the past.

The inventors of the present application have conducted intensive research and various experiments and have found that when an acrylic emulsion is prepared by adding a tackifier having a particle diameter within a specific range to a pre-emulsion solution, a small amount of tackifier is used and an acrylic emulsion The initial adhesive force and the reaction stability of the composition can be improved, and the present invention has been accomplished.

Accordingly, the acrylic emulsion according to the present invention comprises (a) at least one monomer selected from the group consisting of i) a (meth) acrylic acid ester monomer having an alkyl group having 1 to 14 carbon atoms, ii) an allyl ester, a vinyl ester, an unsaturated acetate and an unsaturated nitrile. And iii) a mixed monomer comprising at least one monomer selected from the group consisting of an unsaturated carboxylic acid and a hydroxyl group-containing unsaturated monomer, and iv) a pre-emulsion solution comprising a crosslinking agent; And (b) a tackifier; And a control unit.

In the present specification, the term " mixed monomer " used herein is not particularly limited as long as a pre-emulsion solution is prepared based on the monomers. For example, the monomers may be prepared by being mixed together, And monomers can be manufactured by sequentially injecting them.

In one specific example, the tackifier of (b) is added to increase the adhesion of the acrylic emulsion and is selected from the group consisting of rosin, terpene, petroleum, xylene, coumarone and polybutene But may be at least one selected from the group consisting of rosin, hydrogenated rosin and hydrogenated rosin ester.

In one specific example, the tackifier of (b) may be included in 5 to 30 parts by weight, specifically 10 to 20 parts by weight, based on 100 parts by weight of the pre-emulsion solution. When the content is less than 5 parts by weight, it is difficult to achieve the desired effect of improving the adhesive strength of the acrylic emulsion. When the content exceeds 30 parts by weight, deterioration of the adhesive strength and storage stability is undesirably caused.

In one specific example, the average particle size of the tackifier of (b) may be from 100 nm to 500 nm, and more specifically from 100 nm to 300 nm. When the average particle diameter of the tackifier is out of the above range, the reaction stability of the tackifier is lowered, for example, leaching easily occurs in reaction with the pre-emulsion solution, so that the desired effect can not be obtained.

That is, the acrylic emulsion of the present invention is prepared by adding a tackifier having a particle size within a specific range to the pre-emulsion solution to improve the reaction stability and the initial tackiness of the acrylic emulsion. Thus, the acrylic-based emulsion adhesive comprising the acrylic- It is possible to have an initial adhesive strength superior to that of the pressure-sensitive adhesive.

Hereinafter, the substances contained in the pre-emulsion solution (a) according to the present invention will be described in detail.

In one specific example, the pre-emulsion solution comprises, based on the total weight of the pre-emulsion solution, i) 60 to 90% by weight of a (meth) acrylic acid ester monomer having an alkyl group of 1 to 14 carbon atoms, ii) From 5 to 35% by weight of at least one monomer selected from the group consisting of acrylic acid, methacrylic acid, maleic anhydride, acrylic acid, and unsaturated nitrile, iii) 0.5 to 5% by weight of at least one monomer selected from the group consisting of unsaturated carboxylic acids and hydroxyl group- And iv) from 0.1 to 3% by weight of a crosslinking agent.

In one specific example, the monomer of i) is selected from the group consisting of methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, isopropyl (meth) acrylate, butyl (Meth) acrylate, isodecyl acrylate, decyl (meth) acrylate, isopropyl (meth) acrylate, t-butyl methacrylate, pentyl methacrylate, hexyl methacrylate, heptyl acrylate, isooctyl acrylate, octyl methacrylate, (Meth) acrylate monomer may be at least one member selected from the group consisting of methacrylate, dodecyl methacrylate, isobornyl methacrylate, and lauryl (meth) acrylate, - 60 to 80% by weight of ethylhexyl acrylate and 20 to 40% by weight of butyl acrylate.

As described above, the monomer of i) may be contained in an amount of 60 to 90% by weight based on the total weight of the pre-emulsion solution. When the amount of the monomer is less than 60% by weight, the initial adhesion of the acrylic emulsion can not be secured. %, The transfer of the adhesive to the adherend is largely undesirably caused at the time of removal after use.

The number of carbon atoms of the alkyl group in i) may be 1 to 14, more specifically 2 to 14, and when the number of carbon atoms is less than 1, the cohesive force of the acrylic emulsion is deteriorated and more than 14 , The acrylic emulsion becomes too soft and the adhesive property deteriorates, which is not preferable.

In one specific example, the monomer of ii) is selected from the group consisting of vinyl acetate, vinyl butanoate, vinyl propionate, vinyl laurate, vinyl pyrrolidone, styrene, acrylonitrile and methacrylonitrile And more specifically vinyl acetate, styrene, vinyl butyrate or acrylonitrile.

As described above, the monomer of ii) may be contained in an amount of 5 to 35% by weight, more specifically 7 to 25% by weight, based on the total weight of the pre-emulsion solution, , The acrylic emulsion becomes too soft and can not secure sufficient adhesive property. When the acrylic emulsion is contained in an amount exceeding 35% by weight, the acrylic emulsion becomes excessively firm and the adhesive force is remarkably lowered, which is not preferable.

In one specific example, the monomer of iii) is selected from the group consisting of acrylic acid, itaconic acid, maleic anhydride, fumaric acid, crotonic acid methacrylic acid, ethylmethacrylic acid, hydroxymethyl (meth) acrylate, hydroxyethyl , Hydroxypropyl (meth) acrylate, hydroxybutyl (meth) acrylate, hydroxyhexyl (meth) acrylate, hydroxyoctyl Glycol (meth) acrylate, and the like.

As described above, the monomer of iii) may be contained in an amount of 0.5 to 5% by weight based on the total weight of the pre-emulsion solution. If the amount of the monomer is less than 0.5% by weight, the acrylic emulsion becomes too soft, If it is contained in an amount of more than 5% by weight, the acrylic emulsion becomes excessively firm and a remarkable deterioration of the adhesion strength is undesirably caused.

In one specific example, the mixed monomer for preparing the pre-emulsion solution may further contain an epoxy group-containing unsaturated monomer, and the epoxy group-containing unsaturated monomer is specifically exemplified by glycidyl (meth) acrylate, (Meth) acrylate, allyl glycidyl ether, oxocyclohexyl (meth) acrylate, 3,4-epoxycyclohexylmethyl (meth) acrylate, and more particularly, (Meth) acrylate or allyl glycidyl ether.

In one specific example, the epoxy group-containing unsaturated monomer may be contained in an amount of 0.1 to 3% by weight based on the total weight of the pre-emulsion solution, and the acrylic emulsion has sufficient cohesion within the above range.

In one specific example, the crosslinking agent of iv) is added to reinforce the cohesive force, and it may include 5 to 15 alkylene oxide groups, specifically, 6 to 12, At room temperature, aging tackiness, and stability.

For reference, the number of alkylene oxide groups means the average number of alkylene oxide groups contained in the cross-linking agent used, and when the number of alkylene oxide groups in the cross-linking agent is less than 5, the acrylic emulsion prepared becomes more rigid than necessary, And when the number of alkylene oxide groups is more than 15, the acrylic emulsion becomes unnecessarily soft and adhesive property is deteriorated, which is not preferable.

In one specific example, the crosslinking agent is an organic crosslinking agent such as polyethylene glycol diacrylate, polypropylene glycol diacrylate, 1,6-hexanediol diacrylate, trimethylolpropane triacrylate, ethoxylated trimethylpropane triacrylate, Trimethylolpropyl methacrylate, vinyltrimethoxysilane and divinylbenzene, and the like, and an inorganic crosslinking agent such as aluminum acetyl (meth) acrylate such as tripropylene glycol diacrylate, 1,3-butanediol diacrylate, pentatrytol triacrylate, Acetone, zinc acetate, zirconium carbonate and the like, and more specifically, it may be at least one selected from the group consisting of polyethylene glycol diacrylate and polypropylene glycol diacrylate.

The present invention also discloses a process for producing the acrylic emulsion.

(A) 60 to 90% by weight of a (meth) acrylic acid ester monomer having an alkyl group having 1 to 14 carbon atoms based on the total weight of the pre-emulsion solution, ii) 60 to 90% And 5 to 35% by weight of at least one monomer selected from the group consisting of unsaturated nitriles, and iii) 0.5 to 5% by weight of at least one monomer selected from the group consisting of unsaturated carboxylic acids and hydroxyl group-containing unsaturated monomers. And iv) 0.1 to 3% by weight of a crosslinking agent; (B) adding a tackifier to the pre-emulsion solution of step (A) and stirring the mixture; And (C) polymerizing the pre-emulsion solution to which the tackifier is added in step (B) to prepare an acrylic emulsion; .

In one specific example, the average particle size of the tackifier added in the process (B) may be 100 nm to 500 nm, and more specifically, 100 nm to 300 nm.

The method of producing the acrylic emulsion is not particularly limited when emulsion polymerization is used, but a monomer addition method or a seed polymerization method which can easily control the reaction heat can be used.

Specifically, the acrylic emulsion of the present invention by emulsion polymerization is prepared by adding water and a surfactant to a reactor, elevating the temperature to remove oxygen, dissolving an initiator to prepare a solution, By weight of at least one monomer selected from the group consisting of i) 60 to 90% by weight of a (meth) acrylic acid ester monomer having an alkyl group of 1 to 14 carbon atoms, ii) 5 to 35% by weight of at least one monomer selected from the group consisting of allyl esters, vinyl esters, unsaturated acetates and unsaturated nitriles %, And iii) 0.5 to 5% by weight of at least one monomer selected from the group consisting of unsaturated carboxylic acids and hydroxyl group-containing unsaturated monomers, and iv) 0.1 to 3% by weight of a crosslinking agent. After the pre-emulsion solution was prepared by administering an electrolyte and a surfactant, the pre-emulsion Adding a tackifier to the solution and stirring the mixture, then continuously feeding the pre-emulsion solution and the initiator to the reactor, cooling the mixture at normal temperature, and then adjusting the pH to 7 to 8.

The initiator in the emulsion polymerization may be a water-soluble initiator such as a persulfate of ammonium or alkali metal, a hydrogen peroxide, a peroxide, a hydroperoxide and the like. In order to carry out the emulsion polymerization reaction at a low temperature, . The reducing agent may be sodium bisulfite, sodium metabisulfite, sodium hydrosulfite, sodium thiosulfate, sodium formaldehyde sulfoxylate, ascorbic acid, and the like.

The temperature of the emulsion polymerization reaction may be in the range of 0 to 100 ° C, more specifically 40 to 90 ° C. The initiator may be used singly or in combination with at least one of the initiator and the reducing agent Method and the like.

The electrolyte used in the polymerization reaction is one which regulates the pH and imparts stability to the polymerized acrylic emulsion. Specific examples thereof include one kind selected from the group consisting of sodium bicarbonate, sodium carbonate, sodium phosphate, sodium sulfate and sodium chloride And specifically may be sodium carbonate, and may be 0.1 to 2 parts by weight, more specifically 0.3 to 1 part by weight, based on 100 parts by weight of the mixture.

The surfactant is used in the emulsion polymerization for initial particle formation, size control of the generated particles, and stability of particles. The surfactant is composed of a hydrophilic group and a lipophilic group, and is divided into an anion, a cation and a nonionic surfactant. It mainly uses anionic and nonionic surfactants, and is mixed with other surfactants to compensate for mechanical stability and chemical stability.

The anionic surfactant may be sodium alkyldiphenyl oxide disulfonate, sodium polyoxyethylene alkyl ether sulfate, sodium polyoxyethylene lauryl ether sulfate, sodium dialkyl sulfosuccinate, sodium lauryl sulfate, The ionic surfactants may be polyethylene oxide alkyl aryl ethers, polyethylene oxide alkyl amines, polyethylene oxide alkyl esters, etc. These may be used singly or in combination of two or more. Anionic surfactants and nonionic surfactants may be used in combination Can be more effective.

The acrylic emulsion is an alkaline substance and its pH can be adjusted. The pH of the acrylic emulsion can be 6 to 9 in detail, more specifically 7 to 8, and the alkaline substance can be a monovalent metal or a 2-valent Metal hydroxides, chlorides, carbonates and the like, ammonia, organic amines, and the like.

The present invention provides an acrylic emulsion pressure-sensitive adhesive comprising the above acrylic emulsion.

The acrylic emulsion pressure-sensitive adhesive may further include a thickening agent and a wetting agent in order to prevent shrinkage of the acrylic emulsion generated when the silicone release paper is coated on the surface of the silicone release paper.

The thickening agent may be CMC (Carboxyl Methyl Cellulose), acrylic sol, polyvinyl alcohol, starch, alginate, dextrin and the like, and more specifically polyvinyl alcohol.

The wetting agent may be a surfactant mixture, and may further include a glycol or an alcohol. The hydrophilic adhesive may be hydrophobic to closely adhere the adhesive to the surface of the hydrophobic silicone release paper.

Since the acrylic emulsion pressure-sensitive adhesive contains a surfactant, foaming occurs during the mixing of the adherent (thickener, wetting agent, etc.), and this foam makes the coated surface of the pressure-sensitive adhesive uneven, so that it can be removed using a defoaming agent .

The antifoaming agent is classified into a silane coupling agent, a surfactant agent, a paraffin agent, a mineral oil agent and the like, preferably a silicone agent.

 The present invention also provides an adhesive sheet for forming the pressure-sensitive adhesive layer by applying the above acrylic emulsion pressure-sensitive adhesive onto an ink film or sheet.

The pressure-sensitive adhesive sheet may be an indoor or outdoor building material, an interior material, an advertising film, or a labeling film or sheet of a label. The pressure-sensitive adhesive layer may have a thickness of 10 to 100 탆, specifically 15 to 30 탆, And has sufficient adhesive property.

INDUSTRIAL APPLICABILITY As described above, according to the present invention, the acrylic emulsion is prepared by adding the tackifier to the pre-emulsion solution in the pre-emulsion step, which is the reaction step, so that the initial tack and reaction And the stability can be improved.

Further, by using a tackifier having a particle diameter within a specific range, there is an effect that the reaction stability can be further improved.

Hereinafter, the present invention will be described with reference to Examples. However, the following Examples are intended to illustrate the present invention and the scope of the present invention is not limited thereto.

≪ Example 1 >

200 g of water, 30 g of a 30% sodium polyoxyethylene lauryl ether sulfate solution as a surfactant, and 3 g of a 30% solution of sodium lauryl sulfate in a glass reactor of 2 L capacity equipped with a thermometer, a stirrer, a dropping funnel, 10 g was added, the inside of the reactor was replaced with nitrogen while stirring, and then the temperature was raised to 80 DEG C under a nitrogen atmosphere, and this was maintained for 60 minutes.

Separately, in the beaker, 140 g of butyl acrylate, 430 g of 2-ethylhexyl acrylate, 50 g of vinyl acetate, 35 g of acrylonitrile, 20 g of acrylic acid, 14 g of styrene, 1 g of polyethylene glycol diacrylate g and 0.3 g of normal dodecyl mercaptan, 5 g of a 60% sodium dioctyl sulfosuccinate solution, 24 g of a 30% sodium polyoxyethylene lauryl ether sulfate solution, 3 g of sodium carbonate, 3 g of nate and 150 g of water was added and mixed with a stirrer to prepare a white emulsion.

60 g of a rosin-based tackifier having an average particle diameter of 200 nm was added to the whitened preemulsion emulsion and stirred for 10 minutes.

The glass reactor was charged with 3.5 g of a 10% ammonium persulfate solution and dissolved by stirring for 10 minutes.

The emulsion and 90 g of a 10% ammonium persulfate solution were continuously added to the glass reactor continuously for 4 hours, followed by further adding 2 g of a 10% ammonium persulfate solution. Then, the temperature was raised to 80 ° C for 30 minutes, , And then cooled to room temperature to prepare an acrylic emulsion.

A 28% aqueous ammonia solution was added to the acrylic emulsion to adjust the pH to 7 to 8

≪ Comparative Example 1 &

Except that the tackifier to be added to the pre-emulsion emulsion in Example 1 was changed to a rosin-based tackifier having an average particle diameter of 600 nm.

≪ Comparative Example 2 &

The procedure of Example 1 was repeated except that the tackifier added to the pre-emulsion emulsion was changed to a rosin-based tackifier having an average particle diameter of 50 nm.

≪ Comparative Example 3 &

Except that the rosin-based tackifier having an average particle diameter of 200 nm was added to a mixture of monomers during the preparation of the pre-emulsion and stirred together to prepare a white turbid emulsion. Respectively.

≪ Comparative Example 4 &

The rosin-based tackifier having an average particle size of 600 nm was added to a mixture of monomers during the preparation of the pre-emulsion and stirred together to prepare an emulsion of opacifying agent in the same manner as in Example 1 Respectively.

≪ Comparative Example 5 &

The procedure of Example 1 was repeated except that a rosin-based tackifier having an average particle size of 200 nm was added after preparing an acrylic emulsion.

≪ Comparative Example 6 >

The procedure of Example 1 was repeated except that a rosin-based tackifier having an average particle size of 600 nm was added after preparing an acrylic emulsion.

<Experimental Example 1>

Manufacture of Adhesive Coated Adhesive Specimen

The acrylic emulsion was coated on a 39 탆 PET film and dried in an oven at 70 캜 for 1 minute to make the acrylic emulsion adhesive layer 20 탆 thick. This was coated on a silicone release paper sheet, dried in an oven at 120 ° C for 1 minute, laminated on an art paper to produce an adhesive tape, and cut to a size of 1 inch x 100 mm to prepare an adhesive tape sheet.

The adhesive properties of the acrylic emulsion pressure-sensitive adhesive prepared in Example 1 and Comparative Examples 1 to 6 were tested by the following methods, and the results are shown in Table 1 below.

* Initial Adhesion Test : Test Method FINAT TEST METHOD NO. 9, the acrylic emulsion pressure-sensitive adhesive pressure-sensitive adhesive tape sheet was formed into a ring shape and attached to the glass surface without applying pressure. After 5 seconds, the pressure was measured while peeling off at a rate of 300 mm / min using a TA Texture Analyzer.

* Peel strength test : Test method FINAT TEST METHOD NO. 2, the acrylic-based emulsion pressure-sensitive adhesive tape sheet was reciprocated twice at a speed of 2 kg roller 300 mm / min, attached on a glass plate, aged at room temperature for 20 minutes, and then developed with a TA Texture Analyzer at a speed of 300 mm / min And was measured while peeling at 90 degrees.

* Coagulate measurement: The acrylic emulsion adhesive was filtered through a 200 mesh fabric filter, and the filtered precipitate was dried at 120 ° C for 3 hours and then weighed.

division Initial Adhesion (N / in) 90 degree peel force (N / in) Coagulation product (%) Example 1 31 13 0.04 Comparative Example 1 28 11 0.05 Comparative Example 2 22 9 0.08 Comparative Example 3 20 9 0.20 Comparative Example 4 16 6 0.23 Comparative Example 5 17 6 0.07 Comparative Example 6 14 4 0.10

As shown in Table 1, it can be seen that in Example 1, both the initial adhesive force and the peeling force were excellent, and the reaction stability was improved, whereby the amount of the coagulated material was remarkably reduced.

On the other hand, in Comparative Examples 1 and 2, since the average particle diameter of the tackifier is out of the specified range of the present invention, it can be understood that the initial tack and peel force are reduced and the amount of the solidification product is increased as compared with Example 1. The effect of the difference in average particle size can be seen not only in Example 1 and Comparative Examples 1 and 2, but also in Comparative Examples 3 and 4 and Comparative Examples 5 and 6, respectively. Specifically, compared to Comparative Example 3, Comparative Example 6 had a smaller initial force and peel force than Comparative Example 3, and the amount of solidified material was increased.

In Comparative Examples 3 and 4, since the tackifier is added to a mixture of monomers other than the pre-emulsion solution, the initial tack and peel force are remarkably reduced and the amount of the coagulated material is remarkably increased as compared with Example 1 have.

In addition, in Comparative Examples 5 and 6, since the tackifier was added after the preparation of the acrylic emulsion, the amount of the coagulated material was relatively small as compared with Example 1, but the initial tack and peel strength were remarkably reduced.

Those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims.

Claims (21)

(a) at least one monomer selected from the group consisting of i) a (meth) acrylic acid ester monomer having an alkyl group having 1 to 14 carbon atoms, ii) an allyl ester, a vinyl ester, an unsaturated acetate and an unsaturated nitrile, and iii) And a hydroxyl group-containing unsaturated monomer, and iv) a pre-emulsion solution comprising a cross-linking agent; And
(b) a tackifier;
Based on the total weight of the emulsion. The pre-emulsion solution according to claim 1, wherein the pre-emulsion solution (a) comprises i) 60 to 90% by weight of a (meth) acrylic acid ester monomer having an alkyl group having 1 to 14 carbon atoms, ii) From 5 to 35% by weight of at least one monomer selected from the group consisting of vinyl esters, unsaturated acetates and unsaturated nitriles, iii) from 0.5 to 5% by weight of at least one monomer selected from the group consisting of unsaturated carboxylic acids and hydroxyl group-containing unsaturated monomers, And iv) from 0.1 to 3% by weight of a crosslinking agent, based on the total weight of the acrylic emulsion. The acrylic emulsion according to claim 1, wherein the tackifier (b) is contained in an amount of 5 to 30 parts by weight based on 100 parts by weight of the pre-emulsion solution. The acrylic emulsion according to claim 1, wherein the average particle diameter of the tackifier (b) is 100 nm to 500 nm. The acrylic emulsion according to claim 1, wherein the average particle diameter of the tackifier (b) is 100 nm to 300 nm. The acrylic emulsion according to claim 1, wherein the tackifier (b) is rosin-based. The acrylic emulsion according to claim 6, wherein the rosin-based tackifier is at least one selected from the group consisting of rosin, hydrogenated rosin and hydrogenated rosin esters. The acrylic emulsion according to claim 1, wherein the mixed monomer for preparing the pre-emulsion solution further contains an epoxy group-containing unsaturated monomer. The acrylic emulsion according to claim 8, wherein the epoxy group-containing unsaturated monomer is contained in an amount of 0.1 to 3% by weight based on the total weight of the pre-emulsion solution. The acrylic emulsion according to claim 8, wherein the epoxy group-containing unsaturated monomer is glycidyl (meth) acrylate or allyl glycidyl ether. The method of claim 1, wherein the monomer of i) is selected from the group consisting of methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, isopropyl (meth) (Meth) acrylate, isodecyl acrylate, decyl (meth) acrylate, isopropyl (meth) acrylate, t-butyl methacrylate, pentyl methacrylate, hexyl methacrylate, heptyl acrylate, isooctyl acrylate, octyl methacrylate, Wherein the acrylic emulsion is at least one selected from the group consisting of methacrylate, dodecyl methacrylate, isobornyl methacrylate, and lauryl (meth) acrylate. [2] The composition of claim 1, wherein the monomer of i) is a mixture of 60 to 80% by weight of 2-ethylhexyl acrylate and 20 to 40% by weight of butyl acrylate based on the total weight of the (meth) acrylic acid ester monomer Acrylic emulsion. The method according to claim 1, wherein the monomer of ii) is at least one selected from the group consisting of vinyl acetate, vinyl butanoate, vinyl propionate, vinyl laurate, vinyl pyrrolidone, styrene, acrylonitrile and methacrylonitrile By weight based on the total weight of the acrylic emulsion. The composition of claim 1, wherein the monomer of iii) is selected from the group consisting of acrylic acid, itaconic acid, maleic anhydride, fumaric acid, crotonic acid methacrylic acid, ethylmethacrylic acid, hydroxymethyl (meth) acrylate, hydroxyethyl , Hydroxypropyl (meth) acrylate, hydroxybutyl (meth) acrylate, hydroxyhexyl (meth) acrylate, hydroxyoctyl (Meth) acrylate, and glycol (meth) acrylate. The acrylic emulsion according to claim 1, wherein the crosslinking agent in iv) contains 5 to 15 alkylene oxide groups and is a compound having an acrylate group or a vinyl group. 16. The acrylic emulsion according to claim 15, wherein the crosslinking agent is at least one selected from the group consisting of polyethylene glycol diacrylate and polypropylene glycol diacrylate. The method for producing an acrylic emulsion according to claim 1,
(A) from 60 to 90% by weight, based on the total weight of the pre-emulsion solution, of i) 60 to 90% by weight of a (meth) acrylic acid ester monomer having an alkyl group having from 1 to 14 carbon atoms, ii) from the group consisting of allyl esters, vinyl esters, unsaturated acetates and unsaturated nitriles From 5 to 35% by weight of at least one selected monomer, and iii) from 0.5 to 5% by weight of at least one monomer selected from the group consisting of unsaturated carboxylic acids and hydroxyl group-containing unsaturated monomers, and iv) 3% by weight of a pre-emulsion solution;
(B) adding a tackifier to the pre-emulsion solution of step (A) and stirring the mixture; And
(C) preparing an acrylic emulsion by polymerizing the pre-emulsion solution to which the tackifier is added in the step (B);
Wherein the acrylic emulsion has an average particle size of less than 100 nm. The method of claim 17, wherein the average particle size of the tackifier added in step (B) is 100 nm to 500 nm. 18. The method according to claim 17, wherein the average particle diameter of the tackifier added in the step (B) is 100 nm to 300 nm. An acrylic emulsion pressure-sensitive adhesive comprising the acrylic emulsion according to claim 1. The pressure-sensitive adhesive sheet according to claim 20, wherein the pressure-sensitive adhesive layer is formed by applying the acrylic-based emulsion pressure-sensitive adhesive according to claim 20 onto a pressure-sensitive adhesive film or sheet.