KR20140049172A - Method to manufacture the woven fabrics for hanbok to use and the woven fabrics for hanbok is produced thereby - Google Patents

Abstract

The present invention relates to a method for preparing a Korean fabric using a polyester yarn, and more specifically, to a method for preparing a Korean fabric by using a polyester yarn having excellent moisture permeability, shape stability, and wash fastness, as warp, weft, or warp and weft, and the Koran fabric. Disclosed is a method for preparing a Korean fabric using a polyester yarn, the method comprising: a step of spinning a polyester yarn to have a single yarn fineness of 50-100 denier and a tension of 5-10 N to obtain a spun yarn; a pre-dyeing step of immersing the spun yarn in a dyeing liquid to dye the spun yarn; a step of weaving a fabric having a predetermined width by using the spun yarn, which is dried after the pre-dying, as warp, weft, or warp and weft; a step of, after the weaving, knitting a gold yarn, a silver yarn, or gold and silver yarns on one surface of the fabric to perform lifting to have 3-7 /inch per area; a step of, after the lifting, tentering the woven fabric by using a tentering machine, to mold a fabric having a width of 22-60 inch; and a step of designing traditional patterns on the molded fabric. [Reference numerals] (S100) Spinning; (S110) Pre-dyeing; (S120) Weaving; (S130) Lifting; (S140) Molding; (S150) Designing

Description

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method of manufacturing a hosiery cloth using polyester yarn and a method of manufacturing the hosiery cloth,

More particularly, the present invention relates to a method of producing a hosiery cloth using a polyester yarn excellent in moisture permeability, shape stability, and high washing fastness by using warp or weft yarns or warp yarns or weft yarns And a method of making the same.

Hanbok is a traditional costume of Korea which is attracting attention for its beauty all over the world. Silk, linen, synthetic fiber and so on are widely used for the production of hanbok.

Hanbok was made using different materials and made from 4 different seasonal fabrics. In the spring and autumn, there are national history, athoras, silver tide, and japanese. In autumn, jasmine, silkworms, In the summer, she enjoyed the cool and immaculate style of ramie and hemp, and she also revealed her fresh beauty in the form of woven-in-life, In the winter, we used gorgeous and elegant cloths such as satin and satin, and we put a silk scarf and cotton which was woven by hand in outerwear, and put on a quilted quilted coat to prevent the cold.

However, Hanbok has a disadvantage to solve. Since the material of Hanbok must maintain its original shape, most of the fabrics show a rigid nature such as an abdomen, so that they are wrinkled and wrinkled by wearing for a long time. Especially, because of the characteristics inherent in silk and fiber used in Hanbok, And wrinkles are especially common, and Lee point is the most discomfort factor in everyday life together with the form of Hanbok. Therefore, except for some special occasions, Hanbok gradually becomes weaker as a living fashion.

In order to solve these problems, methods for improving the problem by modifying the form or material of living Hanbok have been studied. However, the practicality of living Hanbok has improved, but the curvaceous appearance of Hanbok or the appearance of the Hanbok has a rugged feeling, and it focuses on improving the material.

Silk which is widely used as a material of Hanbok has elegant luster and excellent drape and is widely used in high quality Hanbok. It is cool in summer, warm in winter and good in ventilation, but lacks morphological stability due to moisture contraction, There are a lot of factors which hind the practicality such as occurrence, and it is a material which is often used, and the stability against moisture is good, but the wrinkle recovering property is bad, and there are many problems in spinning and spinning. In addition, it is a reality that the production cost is very high even in economical efficiency.

Recently, in order to improve these problems, the development of a hanbok using a synthetic fiber has been made, for example, a hanbok that is served by mixing nylon yarn with a metal yarn is known. However, nylon is vulnerable to heat, so special care is required in the dyeing process. The hanbok made of nylon yarn is difficult to wash in hot water, and the hanbok shrinks due to heat shrinkage after ironing. I have a problem.

Therefore, it is necessary to develop a hanbok that can improve the practicality of the hanbok after using a material that is resistant to heat, has excellent wrinkle recovery while securing stability against moisture, and has excellent shape stability during the dyeing process.

Disclosure of Invention Technical Problem [8] Accordingly, the present invention has been made keeping in mind the above problems occurring in the prior art, and an object of the present invention is to provide a polyester yarn excellent in moisture permeability and shape stability, The present invention relates to a method for producing Korean traditional hanbok which can be used for manufacturing traditional Korean hanbok, quilt or bag and the like, which is excellent in washing fastness capable of preventing creasing and washing with water, .

A method of producing a Korean traditional woven fabric using polyester yarn of the present invention, which solves the above problems, comprises the steps of spinning a polyester yarn so that the single yarn fineness is 50 to 100 denier and the tension is 5 to 10 N,

A dyeing step of dying the dyeing dye in the dyeing solution;

After the dyeing, the dried spun yarn is inclined or weft, or inclined and weft so as to have a constant width;

After the job, weaving gold, silver or gold and silver yarn on one surface of the fabric to lift to 3 ~ 7 / inch per unit area;

After the lift, forming the woven fabric with a tenter to form a straight width of 22 to 60 inches in width; And

And designing a traditional pattern on the formed fabric.

Here, the yarns are characterized by having a number of yarns of 11,000 to 22,000 and a yarn length of 500 to 1,300.

Here, the gold and silver used in the lifting step are twisted so that the number of twists is 55 to 110TM.

Here, the density of the above-mentioned cloth is 100 to 250, and the shrinkage rate is 3% or less.

According to the present invention, there is provided a Hanbok paper which is produced by any one of the above-mentioned production methods and has a density of 100 to 250, a shrinkage of 3% or less, and a wash fastness of 4 or more.

The fabric of the present invention produced by the method of the present invention is excellent in heat resistance, heat resistance, silk gloss, washing fastness, shrinkage of the fabric after ironing, In addition, it is possible to provide a Korean traditional lacquer which has excellent pulling resistance.

Also, the present invention can be applied not only to a traditional costume, but also to a quilt or a bag.

FIG. 1 is a block diagram showing an example of a method for manufacturing a Korean traditional dress paper according to the present invention.
2 is a process diagram showing an example of the method for manufacturing the Korean traditional dress paper of the present invention.
3 is a photograph showing an example of a Korean traditional dress made by the manufacturing method of the present invention.

BRIEF DESCRIPTION OF THE DRAWINGS The present invention will be described in more detail with reference to the accompanying drawings.

The above-described objects, features and advantages will become more apparent in light of the following description, and those skilled in the art will readily devise the technical idea of the present invention. In the following description, well-known functions or constructions are not described in detail since they would obscure the invention in unnecessary detail.

According to the present invention, the manufacturing of the hanbok is a method of manufacturing hanbok using a polyester yarn is a single yarn fineness of 50 to 100 denier, the step of obtaining a yarn to spun polyester yarn so that the tension 5 ~ 10N (S100); and the yarn Dyeing step by immersing in the dye solution (S110); and after the dyeing, the step of serving to have a certain straight width of the dried spun yarn inclined or weft, or inclined and weft (S120); Step of weaving gold yarn, silver or gold silver yarn on one surface of the water to be 3 to 7 / inch per unit area (S130); And after the lift, the step of forming the woven fabric paper by the tenter with a tenter to form a straight width of 22 to 60 inches in width (S140); And designing a traditional pattern on the formed fabric (S150).

After the designing step, further post-processing for improving the glossiness may be performed.

Hereinafter, the gold, silver, or gold silver is referred to as metal.

2, a polyester yarn 110 is produced by spinning polyester yarn in a conventional spinning machine 100. The polyester yarn 110 is produced by spinning a polyester yarn in a conventional spinning machine 100. [ At this time, the spun yarn is spun to have a single yarn fineness of 50 to 100 denier, a tension of 5 to 10 N, a yarn count of 11,000 to 22,000, and a yarn count of 500 to 1,300TM.

The yarn yarn 110 is guided by a guide roller 120 to be transferred to a dyeing tank 130 filled with a dyeing solution 140 to be dyed. At this time, a usual polyester dyeing method is applied for dyeing conditions. At this time, the color number of the dyeing solution to be used is selected according to the production conditions.

The dyed spun yarn is guided to the drying apparatus 160 and dried, and the dried spun yarn 110 is guided by the guide devices 170 and 180 to guide the weaving machine 300. At this time, the spun yarn is supplied in an inclined manner, and the synthetic yarn or natural fiber yarn, which is usually used, is simultaneously supplied to the weaving machine 300 as the weft yarn 220.

The fabric 320 is sewn in the weaving machine 300 is transferred to the lifting device 400 through the induction roller 310, at this time supply the metal yarn 440 at the same time weaving.

The textile fabric woven with the metal yarn 440 is tentered in the tenter machine 430 to have a predetermined width and is designed to have a traditional pattern on a fabric of a predetermined shape and then wound into a winding machine 500, To complete the Hanbok paper.

As shown in FIG. 3, the clothes can be obtained as an example of the clothes.

According to the present invention, the gold or silver yarn used in the lifting step may be a plain yarn without twist, and preferably has a twist number (T / M) of 20 to 50. When the number of T / M is less than 20, the resistance of the final clothes becomes less than grade 3, and when the number of T / M is more than 50, the resistance of the wire becomes less than grade 3 due to excessive twisting.

The above-mentioned gold silver is composed of gold and silver, and the twisted yarn is twisted so that the twist number is 55 to 110. Preferably, the mixed ratio of gold and silver is best mixed with twisted so as to have a composition ratio of gold: silver = 8: 2 to 2: 8.

It is preferable that the hanbok prepared according to the above-described manufacturing method of the present invention has a density of 100 to 250ol and shrinkage of 3% or less.

According to the present invention, there is provided a Korean traditional dress paper which is manufactured by any one of the above-described manufacturing methods and has a density of 100 to 250, a shrinkage of 3% or less, and a wash fastness of 4 or more.

Hereinafter, the present invention will be described in more detail with reference to preferred embodiments. However, the present invention is not limited to the following examples.

[Examples 1 to 6]

The fabric having a width of 22 inches, 44 inches, and 60 inches was prepared so as to satisfy the conditions shown in Table 1 below. The density, washfastness and shrinkage of each fabric prepared above were measured and the results are shown in Table 2. At that time, the tensile strength of the polyester yarn used was in the range of 5 ~ 10N. The evaluation of physical properties in the following Table 2 was based on the physical properties of commonly known Korean wool fabrics woven with silk. The density of Hanbok paper woven in silk is 100 ~ 250, the heat shrinkage is less than 3%, the washing fastness is 4 ~ 5 grade, and the wrinkle resistance is 4 ~ 5 grade.

<Table 1>

<Table 2>

The density was measured by counting the number of ounces per inch. The heat shrinkage was measured in boiling water 100 and the wash fastness was measured by a dry cleaning method.

As a result, the wrinkle resistance of each of the widths of Example 1 was 4, 5, and 4, and that of Example 2 was measured. The wrinkle resistance of each of the widths was 4th, 5th, and 4th grades. In Example 3, the wrinkle resistances of the respective widths were 4th, 5th, and 4th grades. 5, and 5, respectively. In Example 5, the wrinkle resistances of the respective widths were 4, 5, and 5, and the wrinkle resistance of each of the widths of Example 6 was 5, 5, and 5.

From the above results, it was found that the fabric of the present invention provided excellent shrinkage ratio of less than 3% after washing and superior in form stability to that of Hanbok, which was woven in silk with a washing fastness of 4 to 5 or more, Wrinkle resistance was superior to silk.

In addition, it was confirmed that the Korean traditional dress according to the present invention has excellent wrinkle recovering property, which is almost free of wrinkling even in simple operation of hand rubbing after wrinkling.

100: spinning machine 110: yarn spinning machine
120, 150, 210: guide roller 130: dyeing tank
140: Dye solution 160: Drying device
170, 180: Guide device 200: Weft
300: weaving machine 310: guide roller
320: fabric 400: lift device
410, 420: guide roller 430: tenter
440: Metal yarn 500: Winder

Claims (5)

Obtaining a yarn by spinning a polyester yarn so that the single yarn fineness is 50 to 100 denier and the tension is 5 to 10 N;
A dyeing step of dying the dyeing dye in the dyeing solution;
After the dyeing, the dried spun yarn is inclined or weft, or inclined and weft so as to have a constant width;
After the job, weaving gold, silver or gold and silver yarn on one surface of the fabric to lift to 3 ~ 7 / inch per unit area;
After the lift, forming the woven fabric with a tenter to form a straight width of 22 to 60 inches in width; And
And designing a traditional pattern on the formed fabric. &Lt; RTI ID = 0.0 &gt; 8. &lt; / RTI &gt;
The method according to claim 1,
Wherein the yarns have a number of yarns of 11,000 to 22,000 and a yarn number of 500 to 1,300TM.
The method according to claim 1,
Wherein the gold yarn and the silver yarn used in the step of lifting are twisted so as to have a twist number of 55 to 110TM.
The method according to claim 1,
Wherein the density of the cloth is 100 to 250, and the shrinkage is 3% or less.
A Hanbok paper produced by the method of any one of claims 1 to 4 and having a density of 100 to 250, a shrinkage of 3% or less, and a wash fastness of 4 or more.