KR20140036439A - Airmash fastener having improved firmness - Google Patents

Airmash fastener having improved firmness Download PDF

Info

Publication number
KR20140036439A
KR20140036439A KR1020120102205A KR20120102205A KR20140036439A KR 20140036439 A KR20140036439 A KR 20140036439A KR 1020120102205 A KR1020120102205 A KR 1020120102205A KR 20120102205 A KR20120102205 A KR 20120102205A KR 20140036439 A KR20140036439 A KR 20140036439A
Authority
KR
South Korea
Prior art keywords
layer
fiber
fastener
iron powder
powder resin
Prior art date
Application number
KR1020120102205A
Other languages
Korean (ko)
Other versions
KR101979820B1 (en
Inventor
송위현
장미희
Original Assignee
송위현
장미희
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 송위현, 장미희 filed Critical 송위현
Priority to KR1020120102205A priority Critical patent/KR101979820B1/en
Publication of KR20140036439A publication Critical patent/KR20140036439A/en
Application granted granted Critical
Publication of KR101979820B1 publication Critical patent/KR101979820B1/en

Abstract

The present invention relates to an air mesh fastener with improved firmness, and more specifically, to an air mesh fastener which has improved firmness to improve workability during the mass-production of seats. The fastener according to the present invention includes a ribbon layer which has a plurality of hooks on the bottom, a complementary layer bonded to the upper layer of the ribbon layer, an iron powder resin layer bonded to the upper layer of the complementary layer, a fiber layer in which a plurality of support fibers are arranged on the top of the iron powder resin layer, and a fiber structure layer which has a fiber cloth which has fiber to be coupled to the fiber layer and holes in the fiber cloth.

Description

강연도가 보강된 에어메쉬 파스너{Airmash Fastener having improved firmness}Airmesh Fastener having improved firmness}

본 발명은 강연도가 보강된 에어메쉬 파스너에 관한 것으로, 더욱 상세하게는 시트의 대량 생산시 작업성 향상을 위하여 강연도가 보강된 파스너에 관한 것이다.The present invention relates to an air mesh fastener reinforced with stiffness, and more particularly, to a fastener with reinforced stiffness for improved workability in mass production of sheets.

자동차나 비행기 등에는 사람이 착석하거나 눕기 위한 좌석시트가 설치되어 있다. 이러한 좌석시트는 사용자 편의를 위하여 프레임에 소위 스펀지와 같은 발포제를 고정하고 다시 발포제를 헝겊으로 둘러 싸 봉제하여 마감한 성형 제품이 대부분을 차지하고 있다. 발포제로는 폴리우레탄폼(polyurethane foam)이 널리 사용되고 있고 다른 재료를 사용할 수도 있다.Cars and airplanes are equipped with seat seats for people to sit or lie down. Such seat seats are formed by fixing a foaming agent such as a sponge on the frame for user convenience and then wrapping and sewing the foaming agent with a cloth. Polyurethane foam is widely used as the blowing agent and other materials may be used.

이러한 성형물인 발포제를 갖는 구조의 좌석시트의 경우에 발포제를 둘러싸는 커버를 발포제와 고정하지 않게 되면 커버가 한쪽으로 밀리는 경우가 반드시 발생하고 결국 좌석시트가 제 역할을 하지 못하게 된다. 이러한 문제점을 해결하기 위하여 커버와 발포제를 일정한 위치마다 고정하게 되는 체결 수단이 반드시 필요하다. 본 발명은 이러한 체결구 어셈블리와 관련된다. 이러한 체결구 어셈블리는 커버와 발포제를 서로 고정하도록 도와 제 위치에 고정되도록 한다. 도 1에 그 일례가 되어 있다. 좌석시트(10)에는 표시된 부분과 같은 위치에 체결구 어셈블리(20)가 함께 성형되어 제품화되는 것이다.In the case of the seat seat of the structure having a foaming agent of such a molding, if the cover surrounding the foaming agent is not fixed with the foaming agent, the cover is necessarily pushed to one side and the seating seat does not play its role. In order to solve this problem, a fastening means for fixing the cover and the foaming agent at certain positions is necessary. The present invention relates to such fastener assemblies. This fastener assembly helps to secure the cover and the foam to each other and to hold it in place. An example thereof is shown in FIG. 1. The seating seat 10 is molded into the fastener assembly 20 in the same position as the marked portion is to be produced.

여기서 제공하는 체결구 어셈블리(20)로는 소위 찍찍이인 파스너가 사용되어진다. 파스너는 한쪽에 다수개의 미세한 후크가 형성된 면을 갖고, 그 반대에 그 후크들이 끼워져 결합되는 상대물을 갖는다. 보통 후크를 갖는 파스너는 성형물인 발포제와 함께 성형되고, 상대물은 커버 쪽에 부착되어 서로를 고정한다. 따라서 성형물의 발포시 그 발포제 성형물에 파스너가 들러붙도록 성형해야 한다.As the fastener assembly 20 provided here, a so-called snapper fastener is used. The fastener has a side with a plurality of fine hooks formed on one side and a counterpart on which the hooks are fitted. Fasteners, usually with hooks, are molded together with the foaming agent, which is a molding, and the counterparts are attached to the cover side to fix each other. Therefore, when the molded product is foamed, it should be molded so that the fasteners may stick to the foamed product molding.

이를 위한 기술이 대한민국 특허 제0590668호로 기재되어 있다. 이 기술은 후크를 갖는 파지 시트에 자력에 대하여 인력을 갖을 수 있도록 된 재료층이 접합되고, 그 재료층 외면에 발포제층이 접합되어 이루어진 적층형 테이프를 제공한다. 이러한 테이프는, 도 2를 참고하면, 성형을 위한 주형(30)에 설치된 성형편(31)에 테이프(20)가 놓이게 된다. 성형편(31)은 테이프(20)의 후크(21), 파지시트, 재표층, 그리고 발포제층(22)의 일부가 안착되도록 사방으로 리브가 형성된다. 그 상태에서는 주형에 자력이 있기 때문에 테이프(20)가 제대로 잘 안착된 상태로 된다. 그런 상태에서 발포제가 부어져 발포가 이루어지기 시작하면 압력에 의해 테이프(20)의 발포제층(22)이 리브쪽으로 들러붙어 그 사이 공간이 들뜨지 않게 되어 발포제가 성형편(31) 안쪽으로 침투하지 않게 되고, 성형 후 후크(21) 쪽으로 발포제가 스며들지 않아 제대로 성형제품이 완성된다.A technology for this is described in Korean Patent No. 0590668. This technique provides a laminated tape in which a layer of a material capable of attracting a magnetic force is bonded to a gripping sheet having a hook, and a foaming agent layer is bonded to an outer surface of the material layer. 2, the tape 20 is placed on the molded piece 31 installed in the mold 30 for molding. The molded piece 31 is ribbed in all directions so that a part of the hook 21, the gripping sheet, the back surface layer, and the foaming agent layer 22 of the tape 20 is seated. In this state, since the mold has magnetic force, the tape 20 is properly settled. When the foaming agent is poured in such a state and foaming starts to occur, the foaming layer 22 of the tape 20 sticks toward the ribs by the pressure so that the space therebetween does not rise, so that the foaming agent does not penetrate into the molded piece 31. After the molding, the foaming agent does not penetrate into the hook 21, so that the molded product is completed properly.

그러나 실제로 제작하여 보면 발포제층과 성형물이 같은 재료라도 시간이 흘르게 되면 그 접합력이 떨어지게 되는 문제점이 있다.However, in actual production, even if the material is the same as the foaming agent layer, there is a problem that the bonding strength is lowered over time.

또한, 도 3을 참고하면 강연도의 부족에 따른 작업성이 떨어지는 문제점이 있다. 통상 자동차 시트 등의 제작시 주형이 컨베이어를 타고 작업자를 지나가게 되는데 작업자는 주어진 시간에 도 2와 같이 테이프(20)를 정확하게 성형편(31)에 안착시켜야 한다. 작업 시간은 한 개당 통상 몇 초가 주어진다. 따라서 그 시간 안에 안착시키지 못하면 컨베이어를 멈추어야 하고 작업성이 떨어지게 된다. 이를 위하여 사용자가 손으로 테이프(20)를 쥐었을 때 쥐는 위치로부터 어느 정도 처지는 것이 방지되어야 한다. 즉 어느 정도 이상의 강연도를 가지고 있어야 한다. 도 3을 참고하면, A의 경우에는 강연도가 합격점이라고 판단하고 B의 경우에는 부적격이라고 판단할 수 있다. 너무 쳐지게 되면 제 위치에 테이프(20)를 안착시킬 수가 없다. 이런 강연도 요구 사항을 만족해야만 대량생산에 적용될 수 있는 테이프(20)이다. 그러나 실제로 종래의 기술에 의한 테이프(20)로는 이 강연도를 만족하지 못한다. 따라서 대량 생산기술에 적용이 어렵다.
In addition, referring to Figure 3 there is a problem in the workability due to the lack of lecture. In the manufacturing of a car seat or the like, the mold is passed by a worker on a conveyor, and the worker has to accurately seat the tape 20 on the molded piece 31 as shown in FIG. 2 at a given time. The working time is usually given a few seconds per piece. Therefore, if it does not settle in that time, the conveyor must be stopped and workability is reduced. To this end, when the user grips the tape 20 by hand, it should be prevented from sagging to some extent from the grip position. That is, it must have a certain degree of lecture. Referring to FIG. 3, in the case of A, the lecture degree may be determined as a passing point, and in the case of B, it may be determined as ineligible. If too struck, the tape 20 cannot be seated in place. It is a tape 20 that can be applied to mass production only when this lecture requirement is satisfied. In practice, however, the tape 20 according to the prior art does not satisfy this lecture degree. Therefore, it is difficult to apply to mass production technology.

본 발명은 상술한 종래기술에 의한 문제점을 해결하게 위하여 안출된 것으로서, 자력에 상응하는 철 파우더 층과 결합되도록 구성하여 강연도를 보강함으로써 대량 생산에 작업성을 향상시킬 수 있는 강연도가 보강된 에어메쉬 파스너를 제공하는데 그 목적이 있다.The present invention has been made in order to solve the problems according to the prior art described above, it is configured to be combined with the iron powder layer corresponding to the magnetic force to reinforce the stiffness reinforcement of the stiffness which can improve the workability in mass production The purpose is to provide an air mesh fastener.

본 발명에 의한 파스너는 하부에 복수 개의 후크를 구비하는 리본층과, 상기 리본층의 상부에 접착되는 보완층과, 상기 보완층의 상부에 접착되는 철 파우더 수지층과, 다수의 지지섬유가 상기 철 파우더 수지층의 상부에서 상하방향으로 배열된 섬유층과, 상기 섬유층과 결합되도록 섬유가 형성되는 섬유 보를 구비하며, 상기 섬유 보 사이에 구멍이 형성된 섬유 구조층을 포함한다.Fastener according to the present invention is a ribbon layer having a plurality of hooks at the bottom, the complement layer bonded to the upper portion of the ribbon layer, the iron powder resin layer adhered to the upper portion of the supplement layer, and a plurality of support fibers It includes a fiber layer arranged in the vertical direction from the top of the iron powder resin layer, and a fiber beam to form a fiber to be bonded to the fiber layer, and comprises a fiber structure layer formed with a hole between the fiber beam.

바람직하게는, 상기 섬유 구조층의 구멍이 평면 형상이 사각 형상, 육각 형상, 팔각 형상, 원 형상 중에 선택되는 어느 한 형태로 형성된다.
Preferably, the hole of the fiber structure layer is formed in any one shape in which the planar shape is selected from a rectangular shape, a hexagonal shape, an octagonal shape, and a circular shape.

본 발명에 의한 파스너는 리본층의 상부에 보완층 및 철 파우더 수지층을 형성하기 때문에 파스너의 강연도를 높여 프레임에 보다 쉽게 안착시킬 수 있는 효과를 제공한다.Fastener according to the present invention provides an effect that can be more easily seated on the frame to increase the stiffness of the fastener to form a complementary layer and the iron powder resin layer on top of the ribbon layer.

또한, 본 발명에 의한 파스너는 리본층으로부터 섬유 구조층을 형성하기 때문에 섬유 구조층에 공급되는 발포제와 섬유 구조층 간의 박리 강도를 향상시킬 수 있는 효과가 있다.In addition, the fastener according to the present invention has an effect of improving the peel strength between the foaming agent supplied to the fiber structure layer and the fiber structure layer because the fiber structure layer is formed from the ribbon layer.

도 1은 일반적인 자동차 시트의 성형물로서 파스너가 부착되어 성형된 모습을 보여준다.
도 2는 일반적인 자동차 시트의 성형 작업시 파스너 테이프를 성형편에 안착하는 모습을 보여주는 사시도이다.
도 3은 자동차 시트 제작에 제공되는 테이프의 처짐 정도인 강연도를 측정하는 모습을 보여준다.
도 4a 및 도 4b는 본 발명에 의한 파스너의 상하부 사시도이다.
도 5a 및 도 5b는 도 4의 도면을 절단한 파스너의 단면도이다.
도 6은 도 4a의 일부분을 확대한 상세도이다.
도 7은 본 발명에 의한 파스너가 접착된 것을 도시한 단면도이다.Figure 1 shows a state in which a fastener is attached as a molding of a typical automobile seat.
2 is a perspective view showing a state in which a fastener tape is seated on a molded piece in a molding operation of a general automobile seat.
Figure 3 shows how to measure the extent of the sag of the tape provided in the automobile seat manufacturing.
4A and 4B are top and bottom perspective views of the fastener according to the present invention.
5A and 5B are cross-sectional views of the fastener cut out of the view of FIG. 4.
FIG. 6 is an enlarged detailed view of a portion of FIG. 4A.
7 is a cross-sectional view showing that the fastener according to the present invention is bonded.

본 발명에 의한 파스너(120)는 도 4a 내지 7을 참조하면, 리본층(124), 보완층(123), 철 파우더 수지층(122), 섬유층(121) 및 섬유 구조층(121a)으로 구성된다. 4A to 7, the fastener 120 according to the present invention includes a ribbon layer 124, a complement layer 123, an iron powder resin layer 122, a fiber layer 121, and a fiber structure layer 121a. do.

상기 리본층(124)은 상하면이 형성되어 있다. 상기 리본층(124)의 하면, 하부에는 다수의 후크(124a)가 형성된다. 상기 리본층(124)은 폴리에스테르(polyester) 재질의 섬유가 판상으로 직조되어 형성된다. 또한, 상기 후크(124a)는 종래기술과 마찬가지로 리본층(124)의 상면에 외측방향으로 돌출되도록 형성된다. 상기 후크(124a)는 플라스틱과 같은 합성수지로 형성되는 것이 바람직하다. 상기 합성수지는 폴리프로필렌(polypropylene) 수지를 사용한다.Upper and lower surfaces of the ribbon layer 124 are formed. A plurality of hooks 124a are formed on the lower surface of the ribbon layer 124. The ribbon layer 124 is formed by weaving polyester fibers into a plate shape. In addition, the hook 124a is formed to protrude outward on the upper surface of the ribbon layer 124 as in the prior art. The hook 124a is preferably formed of a synthetic resin such as plastic. The synthetic resin uses a polypropylene resin.

상기 보완층(123)은 리본층(124)의 상면에 접착되는 하면과 상면을 포함한다. 상기 보완층(123)은 리본층(124)의 상부에 합성 고분자로 형성된 접착제를 통하여 접착된다. 상기 접착제는 폴리우레탄(polyurethane)을 사용할 수 있다. 또한, 상기 보완층(120)은 부드러운 섬유 재질의 리본층(124)과 합지되어 파스너(120)의 강연도를 보완하기 위한 강연 보강용 합성수지로 이루어질 수 있다. 상기 강연 보강용 합성수지는 폴리에틸렌 테레프탈레이트(PET; polyethylene terephthalate) 수지가 적합하다. 또한, 상기 보완층(123)은 접착제를 매개로 리본층(124)의 상부에 얇은 두께, 예를 들면, 대략 30-250㎛로 형성되는 것이 바람직하다.The complementary layer 123 includes a lower surface and an upper surface adhered to the upper surface of the ribbon layer 124. The complementary layer 123 is adhered through an adhesive formed of a synthetic polymer on top of the ribbon layer 124. The adhesive may use polyurethane. In addition, the supplementary layer 120 may be made of a synthetic resin for reinforcing reinforcement to complement the ductility of the fastener 120 by laminating with the ribbon layer 124 of a soft fiber material. The reinforcement synthetic resin for reinforcing the polyethylene terephthalate (PET; polyethylene terephthalate) resin is suitable. In addition, the complementary layer 123 is preferably formed in a thin thickness, for example, approximately 30-250㎛ on top of the ribbon layer 124 through the adhesive.

상기 철 파우더 수지층(122)은 보완층(123)의 상면에 접착되는 하면과 상기 상면의 반대면인 상면을 포함한다. 상기 철 파우더 수지층(122)은 보완층(123)의 상면에 코팅됨으로써 형성된다. 상기 철 파우더 수지층(122)은 철 분말과 합성 고분자 수지의 혼합으로 이루어질 수 있다. 예를 들면, 상기 합성 고분자 수지는 종래기술과 마찬가지로 발포제와 동일한 재질로 형성될 수 있다.The iron powder resin layer 122 includes a lower surface adhered to the upper surface of the complementary layer 123 and an upper surface opposite to the upper surface. The iron powder resin layer 122 is formed by coating on the upper surface of the complementary layer 123. The iron powder resin layer 122 may be made of a mixture of iron powder and synthetic polymer resin. For example, the synthetic polymer resin may be formed of the same material as the blowing agent as in the prior art.

본 발명에서는 상기 합성 고분자 수지를 발포제와 동일한 수지로 형성하여 파스너(120)와 종래기술과 마찬가지로 발포제의 접착력을 향상시킬 수 있게 된다. 예로 상기 발포제(140)가 폴리우레탄 수지라면 철 파우더 수지층(122)을 형성하는 수지는 폴리우레탄 수지일 수 있다. In the present invention, the synthetic polymer resin may be formed of the same resin as the blowing agent to improve the adhesion between the fastener 120 and the blowing agent as in the prior art. For example, if the blowing agent 140 is a polyurethane resin, the resin forming the iron powder resin layer 122 may be a polyurethane resin.

상기 철 파우더 수지층(122)을 구성하는 철 분말과 합성 고분자 수지는 1:1 내지 1: 1.5의 비율로 혼합될 수 있다. 상기 합성 고분자 수지가 철 분말에 대하여 1.1배 이하의 비율로 혼합되는 경우에는 발포제와의 접착력이 약해지게 되고, 1.5배 이상의 비율로 혼합되는 경우에는 프레임 하면에 위치된 자석물질과의 자력이 약해지기 때문이다.The iron powder constituting the iron powder resin layer 122 and the synthetic polymer resin may be mixed in a ratio of 1: 1 to 1: 1.5. When the synthetic polymer resin is mixed at a ratio of 1.1 times or less with respect to the iron powder, the adhesive strength with the foaming agent is weakened. When the synthetic polymer resin is mixed at a ratio of 1.5 times or more, the magnetic force with the magnetic material located on the lower surface of the frame becomes weak. Because.

상기 섬유층(121)은 철 파우더 수지층(100)의 상면에 접착되도록 형성된다. 상기 섬유층(121)은 섬유가 철 파우더 수지층(122)의 상면, 즉 상부에서 상하방향으로 배열되어 형성된다. 상기 섬유층(121)은 철 파우더 수지층(122)의 상부에 합성 고분자로 형성된 접착제로 접착된다. 상기 접착제는 폴리우레탄을 사용한다.The fiber layer 121 is formed to be bonded to the upper surface of the iron powder resin layer 100. The fiber layer 121 is formed of fibers arranged in the vertical direction from the upper surface of the iron powder resin layer 122, that is, the top. The fiber layer 121 is bonded with an adhesive formed of a synthetic polymer on top of the iron powder resin layer 122. The adhesive uses polyurethane.

상기 섬유층(121)은 소정의 직경을 갖는 다수의 섬유가 상하 방향으로 배열되어 형성된다. 상기 섬유는 철 파우더 수지층(122) 상부의 접착제에 심겨지게 되며, 접착제에 결합되는 부분이 접착제에 의하여 지지되면서 상부 방향으로 배열되도록 형성된다. 상기 섬유는 접착제를 이용한 별도의 공정을 통하여 철 파우더 수지층(122)에 결합될 수 있다. 상기 섬유는 종래의 다양한 섬유로 형성된다.The fiber layer 121 is formed by arranging a plurality of fibers having a predetermined diameter in the vertical direction. The fiber is planted in an adhesive on the upper portion of the iron powder resin layer 122, and the portion bonded to the adhesive is formed to be arranged in the upper direction while being supported by the adhesive. The fiber may be bonded to the iron powder resin layer 122 through a separate process using an adhesive. The fibers are formed of various conventional fibers.

상기 섬유는 섬유 구조층(121a)을 지지하는 역할과 파스너(120)에 적절한 탄성력을 부여할 수 있도록 형성된다. 상기 섬유는 100 데니아 내지 400 데니아(Denier)의 굵기로 형성될 수 있다.The fiber is formed to support the fiber structure layer 121a and to impart an appropriate elastic force to the fastener 120. The fiber may be formed to a thickness of 100 denier to 400 denier (Denier).

상기 섬유 구조층(121a)은 섬유층(121)과 결합되도록 섬유가 직조되어 판형상으로 형성된다. 상기 섬유 구조층(121)은 섬유 보가 수평 방향으로 연장되는 형태로 형성되어 섬유 보 사이에 주입 구멍을 구비하여 형성된다. 상기 섬유 구조층(121a)은 섬유층(121)과의 사이에 발포제(140)가 충진될 수 있는 공간을 형성할 수 있도록 한다.The fiber structure layer 121a is formed in a plate shape by weaving fibers to be combined with the fiber layer 121. The fiber structure layer 121 is formed in a shape in which the fiber beams extend in the horizontal direction and is formed with injection holes between the fiber beams. The fiber structure layer 121a may form a space in which the foaming agent 140 may be filled between the fiber structure layer 121a and the fiber layer 121.

상기 섬유 보는 상부 방향으로 연장되는 섬유)와 함께 직조되면서 섬유의 상부를 지지하게 된다. 상기 지지 섬유는 하부가 철 파우더 수지층(122)의 접착제에 고정되고, 상부가 섬유 구조층(121a)에 고정되면서 섬유 구조층(121a)이 철 파우더 수지층(122)의 접착제에 대하여 일정한 간격으로 지지될 수 있도록 기둥 역할을 하게 된다. The fiber beams support the top of the fiber while being woven together). The support fiber has a lower portion fixed to the adhesive of the iron powder resin layer 122, and the upper portion is fixed to the fiber structure layer 121a while the fiber structure layer 121a is fixed to the adhesive of the iron powder resin layer 122 at regular intervals. It will act as a pillar so that it can be supported.

상기 섬유 보는 철 파우더 수지층(122) 상부의 접착제와 섬유 구조층(121a) 사이의 공간에 공급되는 발포제(140)를 고정하는 작용을 하게 된다. The fiber beam serves to fix the foaming agent 140 supplied to the space between the adhesive on the iron powder resin layer 122 and the fiber structure layer 121a.

상기 섬유는, 섬유 보의 길이 방향에 대한 수직 방향으로, 섬유 보를 중심으로 철 파우더 수지층(122)으로 갈수록 서로 벌어지는 형태로 접착제에 고정된다. The fibers are fixed to the adhesive in the form of openings toward the iron powder resin layer 122 about the fiber beams in a direction perpendicular to the longitudinal direction of the fiber beams.

상기 주입구멍은, 파스너(120)의 상부로 발포제(140)가 공급될 때, 발포제(140)가 섬유 구조층(121a)과 철 파우더 수지층(122) 사이로 공급될 수 있도록 하는 역할을 한다. 주입구멍의 모양과 크기를 필요에 따라 다양하게 형성할 수 있다. The injection hole serves to allow the blowing agent 140 to be supplied between the fiber structure layer 121a and the iron powder resin layer 122 when the blowing agent 140 is supplied to the upper portion of the fastener 120. The shape and size of the injection hole can be variously formed as necessary.

상기 주입 구멍은 섬유 보의 굵기 대비 1 내지 10 배의 폭을 갖도록 형성된다. 본 발명에서는 섬유 보 사이에 형성된 주입구멍 내부로 공급되는 발포제(140)와 섬유 구조층(121a) 간의 박리 강도를 향상시킬 수 있게 된다. The injection hole is formed to have a width of 1 to 10 times the thickness of the fiber beam. In the present invention, the peel strength between the blowing agent 140 and the fiber structure layer 121a supplied into the injection hole formed between the fiber beams can be improved.

도 6을 참조하면, 상기 파스너(120)는 발포제(140)와의 결합을 위해 일정 크기로 재단된다. 상기 재단된 파스너(120)는 금형(130) 내부의 프레임(131)에 안착되되, 프레임(131) 내부 아래쪽에 후크(124a)가 위치되고, 섬유 구조층(121a)이 위쪽에 위치된다. 그러므로 상기 금형(130) 내부로 발포제(140)가 투입되는 경우 재단된 파스너(120)의 리본층(122)에 형성된 후크(124a)에는 발포제(140)가 닿지 않고, 섬유 구조층(121a)의 상면에 발포제(140)가 접착된다. Referring to FIG. 6, the fastener 120 is cut to a predetermined size for coupling with the blowing agent 140. The cut fastener 120 is seated on the frame 131 inside the mold 130, the hook 124a is positioned below the inside of the frame 131, and the fiber structure layer 121a is positioned above. Therefore, when the foaming agent 140 is introduced into the mold 130, the foaming agent 140 does not come into contact with the hook 124a formed on the ribbon layer 122 of the cut fastener 120. Foaming agent 140 is adhered to the upper surface.

상기 섬유 구조층(121a)의 상면에 발포제(140)가 투입되면, 투입된 발포제(140)가 섬유층(121) 하부에 형성되는 철 파우더 수지층(122)에 자력에 의해 보다 용이하게 접착될 수 있다. When the blowing agent 140 is injected into the upper surface of the fiber structure layer 121a, the injected blowing agent 140 may be more easily adhered to the iron powder resin layer 122 formed under the fiber layer 121 by magnetic force. .

이상에서 설명한 본 발명은 전술한 실시예 및 첨부된 도면에 의해 한정되는 것이 아니고, 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 여러 가지 치환, 변형 및 변경이 가능함은 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 명백할 것이다.It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit or scope of the inventions. It will be apparent to those of ordinary skill in the art.

120 : 파스너 121 : 섬유
122 : 철 파우더 수지층 123 : 보완층
124 : 리본층 130: 금형
131: 프레임 140: 발포제120: fastener 121: fiber
122: iron powder resin layer 123: complement layer
124: ribbon layer 130: mold
131: frame 140: blowing agent

Claims (2)

하부에 복수 개의 후크를 구비하는 리본층;
상기 리본층의 상부에 접착되는 보완층;
상기 보완층의 상부에 접착되는 철 파우더 수지층;
다수의 지지섬유가 상기 철 파우더 수지층의 상부에서 상하방향으로 배열된 섬유층;
상기 섬유층과 결합되도록 섬유가 형성되는 섬유 보를 구비하며 상기 섬유 보 사이에 구멍이 형성된 섬유 구조층;
을 포함하는 강연도가 보강된 에어메쉬 파스너.A ribbon layer having a plurality of hooks at a lower portion thereof;
A complementary layer adhered to an upper portion of the ribbon layer;
An iron powder resin layer adhered to an upper portion of the complement layer;
A fiber layer in which a plurality of support fibers are arranged in a vertical direction from an upper portion of the iron powder resin layer;
A fiber structure layer having a fiber beam formed with a fiber to be bonded to the fiber layer and having a hole formed between the fiber beams;
Air mesh fastener reinforced stiffness comprising a. 제1항에 있어서,
상기 섬유 구조층의 구멍이 평면 형상이 사각 형상, 육각 형상, 팔각 형상, 원 형상 중에 선택되는 어느 한 형태로 형성된 강연도가 보강된 에어메쉬 파스너.The method of claim 1,
An air mesh fastener having a stiffness of reinforcement formed in any one of the hole of the fiber structure layer is selected from among a rectangular shape, a hexagonal shape, an octagonal shape, and a circular shape.
KR1020120102205A 2012-09-14 2012-09-14 Airmash Fastener having improved firmness KR101979820B1 (en)