KR20130101384A - Loose type semi-solid cosmetic compositions comprising high content of pearl powder and oil-binder - Google Patents
Loose type semi-solid cosmetic compositions comprising high content of pearl powder and oil-binder Download PDFInfo
- Publication number
- KR20130101384A KR20130101384A KR1020120022491A KR20120022491A KR20130101384A KR 20130101384 A KR20130101384 A KR 20130101384A KR 1020120022491 A KR1020120022491 A KR 1020120022491A KR 20120022491 A KR20120022491 A KR 20120022491A KR 20130101384 A KR20130101384 A KR 20130101384A
- Authority
- KR
- South Korea
- Prior art keywords
- mica
- cosmetic composition
- pearl powder
- semi
- oil
- Prior art date
Abstract
Description
본 발명은 고함량 펄 파우더 및 오일바인더를 포함하는 루스타입 반고형 화장료 조성물에 관한 것이다.
The present invention relates to a loose-type semi-solid cosmetic composition comprising a high-content pearl powder and an oil binder.
일반 파우더 화장료의 경우 일반 프레스드 타입이 주를 이루는데, 이 경우 파우더 분체를 오일이나 왁스와 섞어 분쇄한 후 접시에 충진하여 압축 성형 하는 것이 일반적이었다. 또한, 종래 반고형 제품들의 경우 휘발의 위험성도 있어 건조에 특히 취약하다는 단점이 있고, 색상 표현력과 펄광택감에도 한계점이 있다.In the case of general powder cosmetics, a general press type is mainly made up. In this case, powder powder is mixed with oil or wax and pulverized. In addition, conventional semi-solid products have a disadvantage that they are particularly vulnerable to drying due to the risk of volatilization, and there are limitations in color expressing power and pearl luster.
그러나 메이크업 제품이 점점 더 세분화 되고 소비자의 수준도 높아짐에 따라 좀 더 다양한 제품형태에 대한 소비자 욕구가 형성되었다. 이에 따라, 소재의 다양화와 더불어 기능과 시각적 미를 동시에 만족시키는 새로운 제형의 제품개발이 이루어지고 있다.However, as more and more make - up products become more sophisticated and consumers become more sophisticated, consumers' desire for more diverse product forms has been formed. As a result, new product formulations have been developed that satisfy functional and visual merits in addition to diversification of materials.
종래 주로 실리콘 겔과 실리콘계 오일 및 에스테르계 오일들을 함유한 오일상으로 이루어진 반고형 화장료들은 부드럽고 가벼운 사용감과 우수한 퍼짐성 등의 장점 및 가루날림이 없는 것을 특징으로 개발되고 있으나, 제품도포 시 크리미(creamy)하고, 번들거리는 현상의 개선은 여전히 미흡하며, 또한 실리콘 오일들의 낮은 계면장력으로 인한 오일 누액으로 인하여 용기 주변으로 오일막을 형성하는 단점들이 노출되고 있다. 더불어 성형 안정성도 불안하여 제품 충진 시 및 외부 충격으로 인한 내용물의 쏠림 현상이 발생하기도 한다.Conventionally, semi-solid cosmetic compositions comprising silicone gel, silicone oil and ester oil have been developed which are characterized by soft feeling and light feeling, excellent spreadability, and no flaking. However, creamy, The improvement of the bundling phenomenon is still insufficient, and the drawbacks of forming the oil film around the vessel due to the oil leakage due to the low interfacial tension of the silicone oils are being exposed. In addition, the stability of the molding is also unstable, which may lead to the inclusion of the contents due to the filling of the product and external impact.
한편, 주로 실리콘 겔과 실리콘계 오일 및 에스테르계 오일들을 함유한 오일상으로 이루어진 반고형 색조 화장료들은 부드럽고 가벼운 사용감과 우수한 퍼짐성 등의 장점 및 가루날림이 없는 것을 특징으로 개발되고 있으나(대한민국특허등록번호 제0983217호 및 제0943395호), 제품 도포시 크리미(creamy)하고, 번들거리는 현상의 개선은 여전히 미흡하며, 또한 실리콘 오일들의 낮은 계면장력으로 인한 오일 누액으로 인하여 용기 주변으로 오일막을 형성하는 단점들이 노출되고 있다. 더불어 성형 안정성도 불안하여 제품 충진 시 및 외부 충격으로 인한 내용물의 쏠림 현상이 발생하기도 한다.On the other hand, semi-solid type color cosmetics composed mainly of silicone gel, silicone oil and ester oil have been developed to have a soft feeling and light feeling, excellent spreadability, and free from dusting (Korean Patent Registration No. 0983217 and 0943395), the improvement of the creamy and bundling phenomenon is still insufficient during application of the product, and the disadvantages of forming an oil film around the container due to the leakage of the oil due to the low interfacial tension of the silicone oils, . In addition, the stability of the molding is also unstable, which may lead to the inclusion of the contents due to the filling of the product and external impact.
현재 시판되고 있는 반고형 형태의 메이크업 제품들과는 차별화된 것으로 유성타입이 아니며, 기존 자타입 반고형 제품들의 경우 휘발의 위험성도 있어 건조에 특히 취약하다는 단점이 있고, 색상 표현력과 펄광택감에도 한계점이 있다.It is not oil-based type which is different from semi-solid type make-up products currently available on the market, and existing self-type semi-solid products have a drawback in that they are particularly vulnerable to drying due to the risk of volatilization, .
따라서, 성형성 뿐 만 아니라 발림성, 색상표현력, 펄광택감등과 같은 메이컵 효과를 나타내는 반고형 화장료 조성물의 필요성이 대두되고 있다.
Accordingly, there is a need for a semi-solid cosmetic composition showing not only moldability but also make-up effects such as spreadability, color expressing power, pearl luster, and the like.
본 명세서 전체에 걸쳐 다수의 논문 및 특허문헌이 참조되고 그 인용이 표시되어 있다. 인용된 논문 및 특허문헌의 개시 내용은 그 전체로서 본 명세서에 참조로 삽입되어 본 발명이 속하는 기술 분야의 수준 및 본 발명의 내용이 보다 명확하게 설명된다.
Numerous papers and patent documents are referenced and cited throughout this specification. The disclosures of the cited papers and patent documents are incorporated herein by reference in their entirety to better understand the state of the art to which the present invention pertains and the content of the present invention.
본 발명자들은 형성 뿐 만 아니라 발림성, 색상표현력, 펄광택감등과 같은 메이컵 효과를 나타내는 반고형 화장료 조성물을 개발하고자 예의 연구 노력하였다. 그 결과, 펄 파우더와 오일바인더를 고함량으로 포함하는 경우 발림성, 색상표현력 및 펄광택감이 매우 향상됨을 규명함으로써, 본 발명을 완성하게 되었다.The present inventors have tried to develop a semi-solid cosmetic composition that exhibits a makeup effect such as spreadability, color expressive power, pearl luster and the like as well as formation. As a result, the inventors have found that when the pearl powder and the oil binder are contained in a high content, the spreading ability, the color expressive power and the luster of the pearl luster are greatly improved, thereby completing the present invention.
따라서, 본 발명은 고함량 펄 파우더 및 오일바인더를 포함하는 루스타입 반고형 화장료 조성물을 제공하는 것을 목적으로 한다.
Accordingly, it is an object of the present invention to provide a loose-type semi-solid cosmetic composition comprising a high-content pearl powder and an oil binder.
본 발명의 다른 목적 및 이점은 하기의 발명의 상세한 설명, 청구범위 및 도면에 의해 보다 명확하게 된다.
Other objects and advantages of the present invention will become more apparent from the following detailed description of the invention, claims and drawings.
본 발명의 일 양태에 따르면, 본 발명은 마이카/티타네이티드 마이카/아이론옥사이드를 포함하는 펄 파우더상 50-79.99 중량%, 오일바인더상 20-40 중량% 및 첨가제 0.01-5 중량%를 포함하는 루스타입 반고형 화장료 조성물을 제공한다.
According to an aspect of the present invention, the present invention comprises 50-79.99% by weight of pearl powder containing mica / titanate mica / iron oxide, 20-40% by weight of oil binder and 0.01-5% by weight of additive. Provided is a loose type semi-solid cosmetic composition.
본 발명은 반고형 화장료 조성물로서 펄 파우더와 오일바인더가 고함량으로 포함된 것을 특징으로 한다. 보다 구체적으로, 본 발명은 종래 반고형 화장료 조성물에 성형성, 특히 메이크업시 발림성, 색상표현력, 펄광택감 및 반죽경도가 떨어지는 문제점을 극복하고자 펄 파우더와 오일바인더의 고함량으로 포함시킨 것이다. The present invention is a semi-solid cosmetic composition characterized by a high content of a pearl powder and an oil binder. More specifically, the present invention includes a high content of a pearl powder and an oil binder in order to overcome the problem that the conventional semi-solid cosmetic composition is inferior in moldability, especially in make-up shineability, color expressive power, pearl luster and kneading hardness.
또한, 본 발명은 성형성, 발림성, 색상표현력, 펄광택감 및 반죽경도 향상 효과를 극대화 시키기 위하여 펄 파이더와 오일바인더가 최적으로 포함되어 있으며, 제형의 안정성을 유지하면서 발색 및 광택감이 우수한 신개념 메이크업 화장료 조성물이다.In addition, the present invention optimally includes a pearl fiber and an oil binder in order to maximize the effect of improving moldability, spreading ability, color expressive power, pearl luster and kneading hardness, and to provide a new concept makeup Cosmetic composition.
본 발명에서 마이카/티타네이티드 마이카/아이론옥사이드를 포함하는 펄 파우더상에는 화장품 분야의 당업계에서 이용되는 펄 파우더가 포함될 수 있으며, 색과 향을 증진시킬 뿐 만 아니라 펄 파우더상의 물리적 특성(예컨대, 가루날림)을 개선시키기 위하여 첨가물이 포함될 수 있다.In the present invention, the pearl powder phase including the mica / titanate mica / iron oxide may include pearl powder used in the art in the cosmetic field, and not only enhances color and aroma but also physical properties of the pearl powder (eg, Additives may be included to improve flouring).
본 발명의 바람직한 구현예에 따르면, 본 발명에서 펄 파우더상은 마그네슘 미리스테이트, 칼슘알루미늄보로실리케이트, 티타네이티드 마이카, 마이카/티타네이티드 및 마이카/아이론옥사이드로 이루어진 군으로부터 선택된 하나 이상의 펄 파우더 원료를 추가적으로 포함한다.According to a preferred embodiment of the present invention, the pearl powder phase in the present invention is at least one pearl powder raw material selected from the group consisting of magnesium myristate, calcium aluminum borosilicate, titanated mica, mica / titanate and mica / iron oxide It further includes.
본 발명은 색상표현력 및 펄광택감을 극대호시키기 위하여 펄파우더상이 최적으로 포함되어 있다.The present invention optimally includes a pearl powder phase to maximize color expressive power and pearl luster.
바람직하게는, 본 발명에서의 펄파우더상의 함량은 조성물 총 중량 대비 55-75 중량%로 포함되며, 보다 바람직하게는 65-75 중량%로 포함되고, 가장 바람직하게는 70 중량%로 포함된다.Preferably, the content of the pearl powder phase in the present invention is included in the range of 55-75 wt%, more preferably 65-75 wt%, and most preferably 70 wt%, based on the total weight of the composition.
본 발명에서 오일바인더는 펄파우더간 균일한 결합, 성형 안정성, 반죽이 잘 되지 않고 압축, 성형 시, 내용물이 부서지거나 표면에 미세 크랙 현상이 일어나는 문제점을 억제하기 위하여 최적의 함량으로 포함되어 있다.In the present invention, the oil binder is contained in an optimum amount in order to prevent the uniform binding between the pearl powders, the stability of the molding, the problems of crumbling of the contents or fine cracks on the surface at the time of compression, molding,
바람직하게는, 본 발명에서의 오일바인더의 함량은 조성물 총 중량 대비 25-35 중량%로 포함되며, 보다 바람직하게는 28-32 중량%로 포함되고, 가장 바람직하게는 30 중량%로 포함된다.Preferably, the content of the oil binder in the present invention is 25 to 35 wt%, more preferably 28 to 32 wt%, and most preferably 30 wt%, based on the total weight of the composition.
본 발명의 바람직한 구현예에 따르면, 본 발명에서 오일바인더는 디펜타에리스리틸 헥사하이드록시스테아레이트/헥사스테아레이트/헥사로지네이트(dipentaerythrityl hexahydroxystearate/hexastearate/hexarosinate), 트리메칠실록시실리케이트/디메치콘크로스폴리머(trimethylsiloxysilicate/dimethicone crosspolymer), 페닐메치콘(phenyl methicone), 디이소스테아릴말레이트(diisostearyl malate), 피토스테릴/이소스테아릴/세틸/스테아릴/베헤닐다이머디리놀레이트(phytosteryl/isostearyl/cetyl/stearyl/behenyl dimer dilinoleate), 디글리세릴 트리이소스테아레이트(diglyceryl triisostearate) 및 하이드로제네이티드 디폴리이소부텐(hydrogenated polyisobutene)으로 이루어진 군으로부터 선택된 하나 이상의 오일 바인더를 포함하며, 보다 바람직하게는 디펜타에리스리틸 헥사하이드록시스테아레이트/헥사스테아레이트/헥사로지네이트, 트리메칠실록시실리케이트/디메치콘크로스폴리머, 페닐메치콘 및 디이소스테아릴말레이트로 이루어진 군으로부터 선택된 하나 이상의 오일 바인더를 포함한다.According to a preferred embodiment of the present invention, the oil binder in the present invention is dipentaerythrityl hexahydroxystearate / hexastearate / hexaloginate (dipentaerythrityl hexahydroxystearate / hexastearate / hexarosinate), trimethylsiloxysilicate / dimethicone crosscross Trimethylsiloxysilicate / dimethicone crosspolymer, phenyl methicone, diisostearyl malate, phytosteryl / isostearyl / cetyl / stearyl / behenyl dimer dilinoleate (phytosteryl / isostearyl at least one oil binder selected from the group consisting of / cetyl / stearyl / behenyl dimer dilinoleate, diglyceryl triisostearate, and hydrogenated polyisobutene, more preferably Dipentaerythryl hexahydroxystearate / hexastearate / One or more oil binders selected from the group consisting of hexaloginate, trimethylsiloxysilicate / dimethicone crosspolymer, phenylmethicone and diisostearylmaleate.
본 발명의 바람직한 구현예에 따르면, 본 발명에서 화장료는 파운데이션, 아이브라우(eyebrow), 아이섀도우(eyeshadow), 볼연지(blusher), 하이라이터(highlighter) 및 컨실러(concealer)로 이루어진 군으로부터 선택된 하나 이상의 화장료이며, 보다 바람직하게는 아이섀도우, 볼연지 및 컨실러로 이루어진 군으로부터 선택된 하나 이상의 화장료이고, 보다 더 바람직하게는 아이섀도우, 볼연지 또는 이의 모두를 포함하는 화장료이다. According to a preferred embodiment of the present invention, the cosmetic material of the present invention is selected from the group consisting of foundation, eyebrow, eyeshadow, blusher, highlighter and concealer. More preferably at least one cosmetic selected from the group consisting of eye shadow, ball lotion and concealer, and even more preferably cosmetic comprising eye shadow, ball lotion or both.
본 발명은 화장료 조성물의 물성 향상 및 제품의 질을 향상시키기 위하여 첨가제가 포함되며, 첨가제는 방부제 또는 향료가 포함한다.The present invention includes additives in order to improve the physical properties and quality of the cosmetic composition, and the additives include preservatives or perfumes.
바람직하게는, 본 발명에서의 첨가제는 0.1-3 중량%를 포함하며, 보다 바람직하게는 0.5-1 중량%가 포함된다.Preferably, the additive in the present invention comprises 0.1-3 wt%, more preferably 0.5-1 wt%.
본 발명은 이와 같은 문제점을 개선하고자, 선택적 오일 결합제를 이용한 새로운 제형의 반고형 메이크업 화장 조성물로, 색상 표현력과 펄 광택감을 동시에 향상시키면서 내용물의 건조 및 성형 안정성에 대한 해결점을 제시하는 화장료 조성물 및 그 제조 방법을 제공하는 것이다.In order to solve the above problems, the present invention provides a cosmetic composition which is a new semi-solid make-up cosmetic composition using a selective oil binder and presents a solution to the drying and molding stability of the contents while enhancing the color expressing power and the luster glossiness, And a method for manufacturing the same.
본 발명의 화장료 조성물을 제조하는 경우, 통상적인 제조방법의 공정은 대한민국특허출원공개번호 제10-2011-0001541호(발명의 명칭: 돔형 분말 아이섀도우 화장료 조성물 및 그 제조 방법)와 대한민국특허등록번호 제1048675호(발명의 명칭: 파우더타입 메이크업 화장료 조성물 제조용 유화베이스, 상기 유화베이스의 제조방법, 상기 유화베이스를 포함하는 파우더타입 메이크업 화장료 조성물 및 그의 제조방법)를 참조하여 제조될 수 있다.
In the case of producing the cosmetic composition of the present invention, the process of a typical manufacturing method is disclosed in Korean Patent Application Publication No. 10-2011-0001541 (the name of the invention: a domed powder eye shadow cosmetic composition and its manufacturing method) No. 1048675, entitled "Emulsion Base for Making Powder Type Makeup Cosmetic Composition, Method for Manufacturing Emulsion Base, Powder Type Makeup Cosmetic Composition Containing Emulsion Base, and Manufacturing Method Thereof".
본 발명의 특징 및 이점을 요약하면 다음과 같다:The features and advantages of the present invention are summarized as follows:
(ⅰ) 본 발명은 고함량 펄 파우더 및 오일바인더를 포함하는 루스타입 반고형 화장료 조성물을 제공한다.(I) The present invention provides a loose-type semi-solid cosmetic composition comprising a high-content pearl powder and an oil binder.
(ⅱ) 본 발명은 종래 루즈타입 반고형 화장료 조성물과 비교하여 첨가제외에 펄 파우더 및 오일 바인더를 고함량으로 포함시킴으로써 성형성이 우수하고, 발림성, 색상표현력, 펄광택감 및 반죽경도가 매우 우수할 뿐 만 아니라 제품의 시각적 차별화 효과까지 발휘할 수 있는 장점을 가진다.(Ii) The present invention is superior to the conventional loose-type semi-solid cosmetic composition in that it contains a high content of pearl powder and oil binder in addition to the additives, thereby providing excellent formability and excellent spreading ability, color expressing power, pearl glossiness and kneading hardness But also the effect of visual differentiation of the product.
(ⅲ) 또한, 본 발명은 펄과 오일바인더만으로 물성 및 메이크업 효과를 개선시켰다는 점을 제시함에 따라 색조화장품 제조 및 응용분야에 있어서 기초적인 자료를 제공한다.
(Iii) The present invention also provides basic data on the manufacture and application of color cosmetics by suggesting that only pearls and oil binders improve physical properties and makeup effects.
이하, 실시예를 통하여 본 발명을 더욱 상세히 설명하고자 한다. 이들 실시예는 오로지 본 발명을 보다 구체적으로 설명하기 위한 것으로, 본 발명의 요지에 따라 본 발명의 범위가 이들 실시예에 의해 제한되지 않는다는 것은 당업계에서 통상의 지식을 가진 자에 있어서 자명할 것이다.
Hereinafter, the present invention will be described in more detail with reference to Examples. It is to be understood by those skilled in the art that these embodiments are only for describing the present invention in more detail and that the scope of the present invention is not limited by these embodiments in accordance with the gist of the present invention .
실시예Example
본 명세서 전체에 걸쳐, 특정 물질의 농도를 나타내기 위하여 사용되는 “%“는 별도의 언급이 없는 경우, 고체/고체는 (중량/중량) %, 고체/액체는 (중량/부피) %, 그리고 액체/액체는 (부피/부피) %이다.
Throughout this specification, "%" used to denote the concentration of a particular substance is intended to include solids / solids (wt / wt), solid / liquid (wt / The liquid / liquid is (vol / vol)%.
파우더 펄 Powder Pearl 베이이스Bayes 제조 Produce
하기 표 1과 같은 성분과 배합비율을 이용하여 다음과 같이 파우더 펄 베이스를 제조하였다.Powdered pearl base was prepared as follows using the components and mixing ratios shown in Table 1 below.
1) 원료 1-6을 헨셀 믹서에 넣고 2500 rpm으로 1분간 혼합하였다.1) The raw material 1-6 was placed in a Henschel mixer and mixed at 2500 rpm for 1 minute.
2) 원료 7-11을 75-80℃로 가온하고 1)에 미세 분사후 1500 rpm으로 1분간, 2500 rpm으로 1분간 혼합하고 분쇄 처리하였다.
2) The raw material 7-11 was heated to 75-80 ° C, 1) was finely pulverized and mixed at 1500 rpm for 1 minute and 2500 rpm for 1 minute.
레이트/헥사스테아레이트/헥사로지네이트
(화천)7. dipentaerythrylhexahydroxystea-
Latex / hexastearate / hexaloginate
(Hwacheon)
/디메치콘크로스폴리머(고원화성)10. Trimethylsiloxysilicate
Dimethicone Crosspolymer (Highly Efficient)
루스타입Loose type 반고형Semi-solid 반제품 제조 Semi-finished product manufacturing
하기 표 2와 같은 성분과 배합비율을 이용하여 다음과 같이 루스타입 반고형 반제품을 제조하였다.A loose-type semi-solid semi-finished product was produced as follows using the components and mixing ratios shown in Table 2 below.
1) 원료 1-8을 헨셀 믹서에 넣고 2500 rpm 1분간 혼합하였다.1) The raw material 1-8 was placed in a Henschel mixer and mixed at 2500 rpm for 1 minute.
2) 원료 7-13를 75-80℃로 가온하고 1)에 미세 분사후 1500 rpm으로 1분간, 2500 rpm으로 1분간 혼합하고 분쇄 처리하였다.2) The raw materials 7-13 were heated to 75-80 ° C, 1) was finely pulverized after mixing at 1500 rpm for 1 minute and 2500 rpm for 1 minute.
3) 2)까지 만들어진 내용물을 선택적 조합을 통해 1~4가지 반제품을 일정한 용기에 원하는 색과 디자인을 위해 적량의 배합으로 넣은 다음 가볍게 혼합하였다.3) 2), 1 ~ 4 semi-finished products were put into a certain container in an appropriate combination for desired color and design, and then lightly mixed.
5) 혼합된 내용물에 자타입 용기에 충진하여 압축 성형하였다.
5) The mixed contents were filled in a self-contained container and compression molded.
(대원유나이티드)7. Mica / Titanated Mica / Iron Oxide
(Daewon United)
(대원유나이티드)8. Titanated Mica
(Daewon United)
/디메치콘크로스폴리머(고원화성)14. Trimethylsiloxysilicate
Dimethicone Crosspolymer (Highly Efficient)
성형성 및 Moldability and 발림성Brittle 평가 evaluation
상기 표 2에 대한 실시예 1, 2, 3 및 비교예1의 조성물에 대하여 하기 방법으로 반제품 성형성을 평가 하였다. 그 결과를 하기 표 3에 나타내었다. 반죽 성형성 정도는 5점 평가 (5 : 매우 우수, 4 : 우수, 3 : 보통, 2 : 나쁨, 1 : 매우 나쁨)를 기준으로 하였다. 점수가 낮을수록 뭉침성이 떨어져 가루날림이 있는 것으로 평가했다.
The compositions of Examples 1, 2 and 3 and Comparative Example 1 for the above Table 2 were evaluated for semi-finished product formability by the following methods. The results are shown in Table 3 below. The degree of moldability was evaluated based on a 5 point rating (5: excellent, 4: excellent, 3: moderate, 2: poor, 1: very poor). The lower the score, the less lumpy the powder was evaluated as having the flaking.
실시예 2 및 3은 반죽상태가 다소 푸석하고 뭉침 현상이 약하여 내용물 충진 시 용기 주변이 지저분해지고 여러번 사용했을 시 가루날림 현상이 발생하는 반면 비교예1은 반죽 경도가 높아 내용물 취해짐이 덜하여 피부 표현력이 떨어지는 결과를 확인할 수 있었다.In Examples 2 and 3, when the contents were filled, the periphery of the container became dirty and the powdery flakes occurred when used many times. On the other hand, in Comparative Example 1, since the dough hardness was high, I was able to confirm the result of poor expressiveness.
실시예 1에서는 가루날림 현상이 현저히 낮고 반죽상태가 차져서 충진시에도 깨끗하게 마무리되며 어플리케이터인 손으로 내용물을 취했을 때도 취해지는 양도 적량으로 피부 도포시 발림성에 대한 우수한 결과를 나타내었다.In Example 1, the dusting phenomenon was remarkably low and the kneaded state became clear, so that it was finished cleanly even when filled. Also, the amount of the product obtained when the contents were taken with the hand applied by the applicator showed excellent results in application of the skin.
실시예 1에 비해, 실시예 2 및 3으로 갈수록 반죽 형성이 윤활치 못하고 푸석하게 되는 것은 오일 결합제 이외에도 마이카 기재가 영향을 미친다는 결과를 나타내었다. 동량대비 칼슘알루미늄보로실리케이트의 함량이 늘어날수록 반죽경도가 약하여 푸석한 내용물이 얻어지는 결과가 나타내었다.
Compared to Example 1, the results of Examples 2 and 3 show that the dough formation is not lubricious and fuzzy as the dough formation becomes more affected by the mica substrate in addition to the oil binder. As the content of calcium aluminum borosilicate increases, the hardness of kneading is weaker than that of calcium aluminosilicate.
발림성Brittle
, 색상표현력, , Color expressiveness,
펄광택감Pearl shine
및 And
반죽경도Kneading hardness
평가 evaluation
/디메치콘크로스폴리머12. Trimethylsiloxysilicate
Dimethicone Crosspolymer
가장 좋은 평가 결과가 나온 표2 실시예 1에 대한 처방을 가지고 오일 바인더의 배합 비율에 따른 사용감의 차이를 알아보기 위해 발림성, 색상표현력, 펄광택감 및 반죽경도 실험을 실시하였다. 20-30세 여성 20명을 시험대상으로 하여 관능시험을 실시하였고, 5점 평가 (5 : 매우 좋은, 4 : 좋음, 3 : 보통, 2 : 나쁨, 1 : 매우 나쁨)를 기준으로 화장시의 사용느낌을 평가하였다. 평가한 결과를 평균하여 하기 표 5에 나타내었다.The results of the best evaluation are shown in Table 2. In order to examine the difference in feeling according to the blending ratio of the oil binders with respect to the formulation of Example 1, the rubbing resistance, color expressive power, pearl glossiness and kneading hardness test were conducted. A 20-year-old female was subjected to a sensory test with a 5-point rating (5: very good, 4: good, 3: normal, 2: poor, 1: very poor) The feeling of use was evaluated. The evaluation results are averaged and shown in Table 5 below.
반죽경도는 제품의 용기인 자타입 용기에 가루날림이 없으면서 어플리케이터인 손에 의해 페이오프(pay off)양이 적당한 지 2항목에 대한 실험평가를 한 결과를 5점 평가(5 : 매우 좋은, 4 : 좋음, 3 : 보통, 2 : 나쁨, 1 : 매우 나쁨)를 기준으로 평가한 결과를 하기 표 5에 나타내었다.
The kneading hardness was evaluated by evaluating 5 items (5: very good, 4 items) in which the amount of pay off was appropriate by the applicator hand without dusting in the self-type container which is the container of the product. : Good, 3: Normal, 2: Bad, 1: Very poor) are shown in Table 5 below.
실시예 4 및 6의 색상표현력 및 펄광택감은 유사하지만 발림성에 있어 다소 확연한 차이의 결과를 확인할 수 있었다. 실시예 5의 경우 내용물 떠짐 현상(pay off)이 부족하여 발림성에 있어 취약한 결과를 보였다.The color expressive power and pearl luster of Examples 4 and 6 were similar, but the results of the somewhat distinct difference in the spreadability were confirmed. In the case of Example 5, there was a lack of content pay off and the result was poor in spreadability.
반죽경도는 실시예 6보다 실시예 4가 낮은 결과를 보였지만, 발림성과 색상표현력 및 펄광택감에 있어 우수한 평가를 나타냈고 반죽경도 또한 상대적으로 낮은 것으로 비교예2 및 실시예 5보다는 높게 나타났다.
The kneading hardness of Example 4 was lower than that of Example 6, but the kneading hardness, color expressive power and pearl luster were excellent, and the kneading hardness was also relatively low, which was higher than Comparative Examples 2 and 5.
이상으로 본 발명의 특정한 부분을 상세히 기술하였는바, 당업계의 통상의 지식을 가진 자에게 있어서 이러한 구체적인 기술은 단지 바람직한 구현예일 뿐이며, 이에 본 발명의 범위가 제한되는 것이 아닌 점은 명백하다. 따라서 본 발명의 실질적인 범위는 첨부된 청구항과 그의 등가물에 의하여 정의된다고 할 것이다.
While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the same is by way of illustration and example only and is not to be construed as limiting the scope of the present invention. It is therefore intended that the scope of the invention be defined by the claims appended hereto and their equivalents.
Claims (4)
Loose type comprising 50-79.99% by weight of pearl powder containing mica / titanated mica / iron oxide, 20-40% by weight of oil binder and 0.01-5% by weight of additive Semi-solid cosmetic composition.
The method of claim 1, wherein the pearl powder phase further comprises one or more pearl powder raw material selected from the group consisting of magnesium myristate, calcium aluminum borosilicate, titanated mica, mica / titanate and mica / iron oxide Loose type semi-solid cosmetic composition.
The method of claim 1, wherein the oil binder phase is dipentaerythrityl hexahydroxystearate / hexastearate / hexarogenate (dipentaerythrityl hexahydroxystearate / hexastearate / hexarosinate), trimethylsiloxy silicate / dimethicone crosspolymer (trimethylsiloxysilicate / dimethicone crosspolymer, phenyl methicone, diisostearyl malate, phytosteryl / isostearyl / cetyl / stearyl / behenyldimerdilinoleate (phytosteryl / isostearyl / cetyl / stearyl / A loose type semi-solid cosmetic composition comprising at least one oil binder selected from the group consisting of behenyl dimer dilinoleate), diglyceryl triisostearate, and hydrogenated polyisobutene.
The cosmetic composition according to claim 1, wherein the cosmetic composition is at least one cosmetic selected from the group consisting of foundation, eyebrow, eyeshadow, blusher, highlighter and concealer ≪ / RTI >