KR20120096375A - Polymer concrete composite and permeable block thereof - Google Patents
Polymer concrete composite and permeable block thereof Download PDFInfo
- Publication number
- KR20120096375A KR20120096375A KR20110015766A KR20110015766A KR20120096375A KR 20120096375 A KR20120096375 A KR 20120096375A KR 20110015766 A KR20110015766 A KR 20110015766A KR 20110015766 A KR20110015766 A KR 20110015766A KR 20120096375 A KR20120096375 A KR 20120096375A
- Authority
- KR
- South Korea
- Prior art keywords
- filler
- weight
- polymer concrete
- parts
- concrete composition
- Prior art date
Abstract
Description
본 발명은 폴리머 콘크리트 조성물 및 이를 이용한 투수블록에 관한 것으로서, 보다 상세하게는 도시의 사막화를 막고 수분의 저장 및 증발 능력을 극대화 시키고, 표면에 세라믹 중공 미립자를 분포시켜 표면온도를 저감시킴으로써 열섬현상(Heat Island)을 줄이고, 은 이온을 첨가하여 각종 세균을 살균하고 포름알데히드를 분해하는 폴리머 콘크리트 조성물 및 이를 이용한 투수블록에 관한 것이다.The present invention relates to a polymer concrete composition and a water permeation block using the same, and more particularly, to prevent desertification of the city, to maximize the storage and evaporation capacity of water, and to distribute the surface of ceramic hollow fine particles on the surface to reduce the surface temperature. The present invention relates to a polymer concrete composition which reduces heat islands, adds silver ions to sterilize various bacteria and decomposes formaldehyde, and a permeation block using the same.
바다와 지표면에 존재하는 수분이 증발하여 비나 눈의 형태로 지표면에 내리는 과정의 물의 순환에 따라 인간이 이의 일부를 이용하여 삶을 유지해오고 있다. 하지만, 인구의 증가에 따른 물의 양의 한계와 도시화 및 산업화가 가속됨에 따라 콘크리트 구조물, 도로 또는 인도 등의 아스팔트 및 콘크리트 포장으로 인해 우수의 침투가 사실상 불가능해짐에 따른 도시 홍수조절의 어려움과 지하수 고갈현상이 심각하게 진행되고 있다.As water in the ocean and the surface of the water evaporates and falls on the surface in the form of rain or snow, humans have been using their parts to maintain their lives. However, urban flooding and groundwater depletion due to the limited amount of water and increasing urbanization and industrialization due to the increase in population, the infiltration of rainwater is virtually impossible due to the asphalt and concrete pavement of concrete structures, roads or sidewalks. The situation is serious.
도 1은 서울의 토양피복 현황을 나타낸 토양피복 분포도이다. 도 1에 도시된 바와 같이, 서울 땅의 82%를 콘크리트가 덮고 있음을 알 수 있다. 이는 도심지일수록 우수의 침투가 불가능하다는 것을 보여주고 있다. 따라서, 도심지의 콘크리트화에 따른 도시사막화 가속과 이에 따른 지하 환경파괴 또는 오염이 사회 문제로 대두되고 있다. 1 is a soil coating distribution showing the current state of soil coating in Seoul. As shown in FIG. 1, it can be seen that concrete covers 82% of Seoul land. This shows that in urban areas it is impossible to infiltrate rainwater. Accordingly, acceleration of urban desertification and consequent underground environmental destruction or pollution are emerging as social problems.
이에 대한 대응책으로 도심지에서는 투수기능을 가진 제품을 권장하고, 그 일환으로 공사비가 저가이고, 시공이 간단한 장점을 갖는 투수콘크리트 포장, 투수 블록 포장이 널리 사용되고 있지만, 종래의 투수콘크리트는 투수성능이 오래 지속되지 못하여 이를 대체하기 위한 제품의 개발이 시급한 실정이다.As a countermeasure, a permeable concrete pavement and a permeable block pavement are widely used in urban areas, and as a part of them, the construction cost is low and the construction is simple. However, the conventional permeable concrete has a long permeability performance. Since it is not sustainable, it is urgent to develop a product to replace it.
또한, 사회 경제적으로 선진화에 따른 국민의 생활수준 향상에 따라 삶의 질에 대한 관심이 높아지면서 안전하고 쾌적한 생활에 대한 요구가 점점 증대되고 있다. 이에 따라, 차도 및 보도의 재질, 친환경성, 디자인, 기능성 등에 대한 요구가 증대되고 있다. 그러므로 이러한 목적을 달성하기 위한 제품의 개발이 요구된다.In addition, as the people's living standards are improved due to socio-economic advancement, the demand for safe and comfortable living is increasing. Accordingly, there is an increasing demand for materials for roadways and sidewalks, eco-friendliness, design, functionality, and the like. Therefore, the development of a product to achieve this purpose is required.
따라서, 본 발명은 상기의 문제점을 해결하기 위하여 창출된 것으로서, 도시의 사막화를 막고 수분의 저장 및 증발 능력을 극대화 시키고, 표면에 세라믹 중공 미립자를 분포시켜 표면온도를 저감시킴으로써 열섬현상(Heat Island)을 줄이고, 은 이온을 첨가하여 각종 세균을 살균하고 포름알데히드를 분해하는 폴리머 콘크리트 조성물 및 이를 이용한 투수블록을 제공하는데 그 목적이 있다.Therefore, the present invention was created to solve the above problems, to prevent desertification of the city, to maximize the storage and evaporation capacity of water, and to distribute the ceramic hollow particles on the surface to reduce the surface temperature (Heat Island) The purpose of the present invention is to provide a polymer concrete composition and a water permeation block using the same to reduce the amount, and add silver ions to sterilize various bacteria and decompose formaldehyde.
상기와 같은 본 발명의 목적은 골재 70 내지 75 중량부; 불포화폴리에스터 수지, 에폭시수지, 우레탄수지, 메타크릴산메틸수지, 열경화성수지 및 열가소성수지 중 적어도 어느 하나로 이루어진 결합재 5 내지 9 중량부; 제 1 충전재 3 내지 15 중량부; 제 1 충전재 보다 상대적으로 입자가 굵은 제 2 충전재 3 내지 15 중량부; 및 차열재 1 내지 20 중량부;를 포함하는 것을 특징으로 하는 폴리머 콘크리트 조성물에 의해 달성될 수 있다. An object of the present invention as described above is 70 to 75 parts by weight of aggregate; 5 to 9 parts by weight of a binder composed of at least one of an unsaturated polyester resin, an epoxy resin, a urethane resin, a methyl methacrylate resin, a thermosetting resin, and a thermoplastic resin; 3 to 15 parts by weight of the first filler; 3 to 15 parts by weight of the second filler, wherein the second filler is relatively coarse than the first filler; And 1 to 20 parts by weight of the heat shield; it can be achieved by the polymer concrete composition comprising a.
이때, 골재는 입자의 크기가 13mm 이하인 쇄석, 강자갈, 규사 및 인공경량 골재 중 적어도 어느 하나이다.At this time, the aggregate is at least one of crushed stone, cobbles, silica sand and artificial lightweight aggregate having a particle size of 13 mm or less.
또한, 제 1 충전재는 입경이 1㎛ 내지 30㎛인 중질 탄산칼슘, 석분, 슬래그, 시멘트, 플라이애쉬 및 제지애쉬 중 적어도 어느 하나이고, 제 2 충전재는 입경이 20㎛ 내지 40㎛인 미세규사이다.Further, the first filler is at least one of heavy calcium carbonate, stone powder, slag, cement, fly ash and paper ash having a particle diameter of 1 μm to 30 μm, and the second filler is fine silica having a particle diameter of 20 μm to 40 μm. .
또한, 차열재는 중공의 구상형태를 갖는 알루미노 실리케이트 세라믹 및 실리카 알루미나 세라믹 중 적어도 어느 하나인 무기질 미립자이다.In addition, the heat shield is an inorganic fine particle which is at least one of an aluminosilicate ceramic and a silica alumina ceramic having a hollow spherical form.
또한, 폴리머 콘크리트 조성물은 0.5 중량부 내지 5 중량부의 경화제를 더 포함한다.In addition, the polymer concrete composition further comprises 0.5 parts by weight to 5 parts by weight of the curing agent.
또한, 결합재의 총 중량의 4 중량부 내지 5 중량부의 은 이온 항균제를 더 포함한다.Further, 4 to 5 parts by weight of the silver ion antibacterial agent of the total weight of the binder is further included.
다른 카테고리로서, 본 발명의 목적은 전술한 폴리머 콘크리트 조성물을 이용한 투수 블록에 의해 달성될 수 있다. As another category, the object of the present invention can be achieved by a permeable block using the polymer concrete composition described above.
본 발명에 따르면 물을 사용하지 않고, 내광성이 높고, 온도민감성이 작은 수지를 이용하며 각각의 조성물을 배합함으로써, 결합력이 우수하여 탈리가 일어나지 않고, 투수력을 장기간 보유할 수 있는 효과가 있다.According to the present invention, by using a resin having a high light resistance, a low temperature sensitivity, and blending each composition according to the present invention, the bonding strength is excellent, so that no detachment occurs and the water permeability can be retained for a long time.
또한, 중공의 구상형태를 갖는 무기질 미립자를 함유함으로써, 태양광 반사효과와 단열성을 갖고, 곰팡이 방지 및 항균효과가 우수한 효과가 있다.In addition, by containing the inorganic fine particles having a hollow spherical shape, it has a solar reflection effect and heat insulating properties, it is excellent in mold prevention and antibacterial effect.
또한, 은 이온 항균제를 포함하여 천연 아미노산이 피부 알레르기 유발물질인 포름알데히드를 분해하고, 은 이온이 폐렴균, 대장균, 황색포도상구균 등 대부분의 세균에 대하여 높은 살균력을 얻을 수 있는 효과가 있다. In addition, natural amino acids, including silver ion antimicrobial agents, decompose formaldehyde, which is a skin allergen, and silver ions have an effect of obtaining high bactericidal power against most bacteria such as pneumococci, Escherichia coli, and Staphylococcus aureus.
또한, 본 발명에 따른 폴리머 콘크리트 조성물을 이용하여 제조한 투수 블록은 투수성능이 높고, 투수력을 장기간 보유할 수 있는 효과가 있다. 이로 인해, 본 발명에 따른 투수블록을 도시의 도로, 공원 또는 광장 등에 설치함으로써, 도시의 사막화를 방지하고, 수분의 저장 및 증발 능력을 극대화시킬 수 있는 효과가 있다. 또한, 세라믹 중공 미립자로 인해 도로 등의 표면온도를 저감시킴으로써 열섬현상을 방지할 수 있는 효과가 있다. In addition, the permeable block prepared using the polymer concrete composition according to the present invention has a high permeability performance, there is an effect that can retain the permeability for a long time. Thus, by installing the water permeable block according to the present invention, such as roads, parks or squares in the city, it is possible to prevent desertification of the city and to maximize the storage and evaporation capacity of the water. In addition, there is an effect that can prevent the heat island phenomenon by reducing the surface temperature of the road due to the ceramic hollow fine particles.
본 명세서에서 첨부되는 다음의 도면들은 본 발명의 바람직한 실시예를 예시하는 것이며, 발명의 상세한 설명과 함께 본 발명의 기술사상을 더욱 이해시키는 역할을 하는 것이므로, 본 발명은 그러한 도면에 기재된 사항에만 한정되어 해석되어서는 아니 된다.
도 1은 서울의 토양피복 현황을 나타낸 토양피복 분포도,The following drawings, which are attached in this specification, illustrate preferred embodiments of the present invention, and together with the detailed description thereof, serve to further understand the technical spirit of the present invention. It should not be interpreted.
1 is a soil coating distribution chart showing the status of soil coating in Seoul,
이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예를 상세하게 설명한다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.
<폴리머 콘크리트 조성물>Polymer Concrete Composition
본 발명에 따른 폴리머 콘크리트 조성물은 골재, 결합재, 제 1 충전재, 제 2 충전재 및 차열재를 포함한다.The polymer concrete composition according to the invention comprises an aggregate, a binder, a first filler, a second filler and a heat shield.
본 발명에 따른 골재는 입자의 크기가 13mm 이하인 쇄석, 강자갈, 규사 등이 사용되며, 경우에 따라서는 인공경량 골재를 사용하고, 폴리머 콘크리트 조성물 총 중량의 70 내지 75 중량부를 포함된다. 이때, 골재는 완전건조시켜서 사용하여야 하고, 고강도 골재를 사용할수록 폴리머 콘크리트 조성물의 전체 강도 역시 높아진다. The aggregate according to the present invention is a crushed stone, steel gravel, silica sand and the like having a particle size of 13mm or less, in some cases using artificial lightweight aggregate, and includes 70 to 75 parts by weight of the total weight of the polymer concrete composition. At this time, the aggregate should be used to dry completely, the higher the strength of the aggregate, the higher the overall strength of the polymer concrete composition.
본 발명에 따른 결합재(바인더 : Binder)는 폴리머 콘크리트 조성물 총 중량의 5 내지 9 중량부가 함유된다. 이때, 결합재의 종류로는 불포화폴리에스터(UP : Unsaturated Polyester)수지, 에폭시(Epoxy)수지, 우레탄(Urethane)수지, 메타크릴산메틸(MMA : Methyl Methacrylate)수지, 열경화성수지 및 열가소성수지를 단독으로 사용하거나 혼합하여 사용한다. 바람직하게는 불포화폴리에스터수지, 메타크릴산메틸수지를 사용하거나, 불포화폴리에스터수지 및 메타크릴산메틸수지를 혼합하여 사용하는 것이 좋다. 만약, 결합재가 5 중량부 미만인 경우에는 강도 저하가 큰 문제점이 있고, 9 중량부를 초과하는 경우에는 공극 막힘 현상으로 투수성이 저하되는 문제점이 있다.The binder (Binder) according to the present invention contains 5 to 9 parts by weight of the total weight of the polymer concrete composition. At this time, as the type of binder, an unsaturated polyester (UP) resin, an epoxy resin, a urethane resin, a methyl methacrylate (MMA) resin, a thermosetting resin, and a thermoplastic resin alone Use or mix. Preferably, unsaturated polyester resin and methyl methacrylate resin are used, or unsaturated polyester resin and methyl methacrylate resin are mixed and used. If the binder is less than 5 parts by weight, there is a problem in that the strength decreases significantly. If the binder is more than 9 parts by weight, there is a problem in that the water permeability is lowered due to a pore blocking phenomenon.
본 발명에 따른 제 1 충전재 및 제 2 충전재는 결합재의 증량, 작업성의 증진, 강도 및 내구성 개선을 위해 사용되는 것으로서, 제 2 충전재는 제 1 충전재와 비교하여 상대적으로 입자가 굵은 충전재를 사용한다. The first filler and the second filler according to the present invention are used for increasing the binder, improving workability, improving strength and durability, and the second filler uses a relatively coarse filler as compared to the first filler.
여기서, 제 1 충전재는 입경이 1㎛ 내지 30㎛로 미세 분말인 중질 탄산칼슘, 석분, 슬래그, 시멘트, 플라이애쉬 및 제지애쉬 중 적어도 어느 하나를 사용하고, 폴리머 콘크리트 조성물 총 중량의 3 내지 15 중량부가 포함된다. 이러한 미세 분말로 이루어진 제 1 충전재는 저가이고 물성이 좋지만, 많이 사용하는 경우에는 강도가 저하되는 문제점이 있기 때문에 폴리머 콘크리트 조성물의 총 중량에서 15 중량부가 넘지 않도록 하는 것이 좋다. 만약, 제 1 충전재가 3 중량부 미만인 경우에는 충전재로서의 의미가 없고, 15 중량부를 초과하는 경우에는 작업성 저하 및 결합재의 양이 증가하여 비용이 높아지는 문제점이 있다. Here, the first filler using at least any one of fine calcium carbonate, stone powder, slag, cement, fly ash and paper ash having a fine powder with a particle diameter of 1 to 30 ㎛, 3 to 15 weight of the total weight of the polymer concrete composition Addition is included. Although the first filler made of such a fine powder is inexpensive and has good physical properties, it is preferable not to exceed 15 parts by weight based on the total weight of the polymer concrete composition because of the problem that the strength is lowered when it is used a lot. If the first filler is less than 3 parts by weight, there is no meaning as a filler. If the first filler is more than 15 parts by weight, the workability is lowered and the amount of the binder is increased to increase the cost.
또한, 본 발명에 따른 제 2 충전재는 입경이 20㎛ 내지 40㎛인 미세규사를 사용하는 것이 좋고, 보다 바람직하게는 #8호사 규사를 사용하는 것이 좋다. 이러한 제 2 충전재는 폴리머 콘크리트 조성물 총 중량의 3 내지 15 중량부가 포함된다. 만약, 제 2 충전재가 3 중량부 미만인 경우에는 충전재로서의 의미가 없고, 15 중량부를 초과하는 경우에는 결합재의 양이 증가하여 비용이 높아지는 문제점이 있다. In the second filler according to the present invention, it is preferable to use fine silica sand having a particle diameter of 20 μm to 40 μm, and more preferably # 8 yarn sand. This second filler comprises from 3 to 15 parts by weight of the total weight of the polymer concrete composition. If the second filler is less than 3 parts by weight, there is no meaning as a filler, and if the second filler is more than 15 parts by weight, the amount of the binder is increased to increase the cost.
본 발명에 따른 차열재(세라믹중공입자)는 차열과 단열 효과를 향상하기 위한 것으로서, 중공의 구상형태를 갖고 기포형태로 태양광 발사효과와 단열성을 갖는 중공의 구상형태를 알루미노 실리케이트(Alumino Siliccate) 세라믹 및 실리카 알루미나 세라믹 등과 같은 무기질 미립자를 단독 또는 혼합하여 사용한다. 이러한 차열재는 폴리머 콘크리트 조성물 총 중량의 1 내지 20 중량부가 포함된다. 바람직한 차열재로써 본 발명에서는 알루미노 실리케이트계로 상품화된 인슐래드(Insuladd)를 사용한다. 본 발명에서는 인슐래드를 사용하지만, 차열기능을 갖는 소재라면 어떠한 것을 사용하여도 무방하다. 만약, 차열재가 1 중량부 미만인 경우에는 차열작용이 없고, 20 중량부를 초과하는 경우에는 결합재의 사용량이 증가하여 단가가 상승하는 문제점이 있다. 특히, 결합재는 15 중량부 이상 사용에서는 큰 차이가 없고, 적정 용량으로는 6 중량부 내지 12 중량부를 사용하는 것이 좋다. Heat shielding material (ceramic hollow particles) according to the present invention is to improve the heat shielding and thermal insulation effect, alumina silicate (Alumino Siliccate) having a hollow spherical shape and a hollow spherical shape having a solar firing effect and heat insulation in the form of bubbles ) Inorganic fine particles such as ceramics and silica alumina ceramics are used alone or in combination. Such heat shield includes 1 to 20 parts by weight of the total weight of the polymer concrete composition. As a preferred heat shield, the present invention uses an insuladd commercialized with an aluminosilicate system. In the present invention, the insulation is used, but any material can be used as long as it has a heat shielding function. If the heat shield is less than 1 part by weight, there is no heat shielding effect. If the heat shield is more than 20 parts by weight, the amount of the binder is increased to increase the unit cost. In particular, the binder is not significantly different in use of 15 parts by weight or more, it is preferable to use 6 parts by weight to 12 parts by weight as appropriate capacity.
본 발명에 따른 폴리머 콘크리트 조성물은 사용양태에 따라 소량의 경화제를 더 포함할 수 있다. 이때, 경화재는 폴리머 콘크리트 조성물 총 중량의 0.5 중량부 내지 5 중량부를 포함할 수 있다. The polymer concrete composition according to the present invention may further comprise a small amount of curing agent depending on the use. In this case, the hardener may include 0.5 parts by weight to 5 parts by weight of the total weight of the polymer concrete composition.
또한, 본 발명에 따른 폴리머 콘크리트 조성물은 항균효과를 위해 결합재의 총 중량에 대해 4 중량부 내지 5 중량부의 은 이온 항균제를 함유할 수 있다. 이때, 은 이온 항균제는 액상 페이스트 또는 파우더 상태로 함유될 수 있다. 이때, 사용되는 은 이온 항균제로는 유기용액계 실버 아미노산을 사용하는 것이 좋다. 이와 같이, 은 이온 항균제를 더 포함하면, 천연 아미노산이 피부 알레르기 유발물질인 포름알데히드를 분해하고, 폐렴균, 대장균, 황색포도상구균 등을 살균하는 효과를 더 얻을 수 있다. In addition, the polymer concrete composition according to the present invention may contain 4 parts by weight to 5 parts by weight of silver ion antibacterial agent based on the total weight of the binder for the antibacterial effect. In this case, the silver ion antimicrobial agent may be contained in a liquid paste or powder state. In this case, it is preferable to use an organic solution-based silver amino acid as the silver ion antimicrobial agent to be used. As such, when the silver ion antimicrobial agent is further included, natural amino acids decompose formaldehyde, which is a skin allergen, and further sterilize pneumococci, Escherichia coli, and Staphylococcus aureus.
전술한 조성을 포함하는 폴리머 콘크리트 조성물의 바람직한 일 실시예는 다음의 [표 1]과 같은 배합으로 이루어진다. One preferred embodiment of the polymer concrete composition comprising the above-described composition is made of a combination as shown in Table 1 below.
(탄산칼슘)1st filler
(Calcium Carbonate)
(#8호사규사)2nd filler
(# 8 Hoshi Sasa)
(인슐래드)Heat shield
(Insulin)
(규사1호사)aggregate
(Gyusa 1)
사용 양태에 따라, 경화제가 0.5 중량부 내지 5 중량부 및 은 이온 항균제가 결합재 총 중량의 4 중량부 내지 5 중량부 더 포함될 수 있다.
Depending on the use aspect, 0.5 parts by weight to 5 parts by weight of the curing agent and 4 parts by weight to 5 parts by weight of the total weight of the silver ion antimicrobial agent may be further included.
<투수 블록 제조방법><Pitching block manufacturing method>
본 발명에 따른 투수 블록은 전술한 폴리머 콘크리트 조성물을 이용하여 제조되고, 그 제조방법은 다음과 같다.The permeable block according to the present invention is manufactured using the above-described polymer concrete composition, the production method is as follows.
우선, 블록을 제작하기 위해 제작하는 투수 블록의 형상 및 크기에 대응되도록 몰드를 조립한다. First, the mold is assembled so as to correspond to the shape and size of the permeable block to be manufactured to produce the block.
다음으로, 조립된 몰드의 내부에 폴리머 콘크리트의 탈형이 용이하도록 이형제를 골고루 도포한다. 이대, 이형제가 과다 사용되면 폴리머 콘크리트의 경화시 문제가 발생할 수 있으므로, 이형제가 과다하게 도포된 부분은 마른 천을 이용하여 제거한다. Next, the release agent is evenly applied to the inside of the assembled mold to facilitate demolding of the polymer concrete. If the release agent is excessively used, problems may occur during curing of the polymer concrete, and the excessively applied portion of the release agent is removed using a dry cloth.
다음으로, 폴리머 콘크리트를 배합한다. 이때, 폴리머 콘크리트는 전술한 내용과 같은 배합비로 배합되어 믹서를 통해 믹싱한다. 폴리머 콘크리트 배합과정을 보다 상세히 설명하면 다음과 같다.Next, the polymer concrete is blended. At this time, the polymer concrete is mixed at the same mixing ratio as described above and mixed through a mixer. The polymer concrete mixing process will be described in more detail as follows.
믹서에 계량된 골재를 투입하고 결합재에 경화제를 믹싱하여 골재에 부어 3분 정도 믹싱한다. 이때, 결합재의 믹싱은 1분 이상 실시하여 경화제의 혼련이 완전히 이루어지도록 하는 것이 좋다.Weigh the aggregates into the mixer, mix the hardener in the binder and pour into the aggregates for 3 minutes. At this time, the mixing of the binder is preferably carried out for 1 minute or more so as to completely knead the curing agent.
다음으로, 배합된 폴리머 콘크리트 조성물을 스쿠프를 이용하여 몰드에 채워 넣는다. 이때, 폴리머 콘크리트 조성물은 몰드의 상부로 약 1cm 정도 볼록하게 채워넣은 후 다짐을 실시한다.Next, the blended polymer concrete composition is filled into a mold using a scoop. At this time, the polymer concrete composition is compacted by filling the top of the mold about 1 cm convex.
다음으로, 상부 표면을 가압하여 표면을 매끄럽게 하여 표면 마무리를 한다. Next, the upper surface is pressed to smooth the surface to finish the surface.
다음으로, 상온에서 외력이 가해지지 않도록 보관하며 몰드에 채워진 폴리머 콘크리트 조성물을 이용한 투수블록을 양생한다. Next, the permeation block is cured using the polymer concrete composition filled in the mold and stored so that no external force is applied at room temperature.
마지막으로, 폴리머 콘크리트 조성물의 경화가 완료되면 투수블록을 몰드에서 탈형함으로써 투수 블록의 제조가 완료된다.
Finally, when the curing of the polymer concrete composition is completed, the permeation block is demolded from the mold to manufacture the permeation block.
<투수 블록의 설치방법><Installation method of pitcher block>
본 발명에 따른 투수 블록의 설치방법은 다음과 같다. The installation method of the pitcher block according to the present invention is as follows.
우선, 설치 공간을 정하고, 설치 후의 지면 높이를 고려하여 터파기를 실시하여 투수블록을 설치할 수 있는 공간을 확보한다. First of all, the installation space is determined, and in order to secure the space for installing the permeation block by digging in consideration of the height of the ground after installation.
다음으로, 규사를 이용하여 바탕면의 수평을 잡고 바탕조정을 한 후, 투수블록을 설치할 장소를 확보한다.Next, after leveling the ground surface using silica sand, and secure the place to install the pitcher block.
다음으로, 일정간격 이격되도록 투수블록을 설치한다. 이때, 각각의 투수블록은 동일한 간격으로 이격되도록 설치한다. 하지만, 사용양태 및 설치 환경 등을 고려하여 각각의 투수블록을 이격하지 않고 설치하거나, 서로 다른 간격으로 설치할 수 있다.Next, install a pitcher block to be spaced apart a certain interval. At this time, each pitcher block is installed to be spaced apart at the same interval. However, the permeation block may be installed without being spaced apart from each other, or may be installed at different intervals in consideration of the use mode and installation environment.
다음으로, 각각의 투수블록 사이에 규사를 채워넣고, 블록 표면에 있는 잉여 규사를 제거함으로써 투수블록의 설치를 완료한다.
Next, the installation of the permeation block is completed by filling silica sand between each permeation block and removing excess silica sand on the block surface.
이상에서 설명한 바와 같이, 본 발명이 속하는 기술분야의 당업자는 본 발명이 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 상술한 실시예들은 모든 면에 예시적인 것이며 한정적인 것이 아닌 것으로서 이해해야만 한다. 본 발명의 범위는 상세한 설명보다는 후술하는 특허청구범위에 의하여 나타내어지며, 특허청구범위의 의미 및 범위 그리고 등가 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.As described above, those skilled in the art will understand that the present invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. It is therefore to be understood that the above-described embodiments are to be considered in all respects as illustrative and not restrictive. The scope of the present invention is defined by the appended claims rather than the detailed description and all changes or modifications derived from the meaning and scope of the claims and their equivalents should be construed as being included within the scope of the present invention.
Claims (7)
불포화폴리에스터 수지, 에폭시수지, 우레탄수지, 메타크릴산메틸수지, 열경화성수지 및 열가소성수지 중 적어도 어느 하나로 이루어진 결합재 5 내지 9 중량부;
제 1 충전재 3 내지 15 중량부;
상기 제 1 충전재 보다 상대적으로 입자가 굵은 제 2 충전재 3 내지 15 중량부; 및
차열재 1 내지 20 중량부;를 포함하는 것을 특징으로 하는 폴리머 콘크리트 조성물.70 to 75 parts by weight of aggregate;
5 to 9 parts by weight of a binder composed of at least one of an unsaturated polyester resin, an epoxy resin, a urethane resin, a methyl methacrylate resin, a thermosetting resin, and a thermoplastic resin;
3 to 15 parts by weight of the first filler;
3 to 15 parts by weight of the second filler is relatively thicker than the first filler; And
1 to 20 parts by weight of the heat shield; the polymer concrete composition comprising a.
상기 골재는 입자의 크기가 13mm 이하인 쇄석, 강자갈, 규사 및 인공경량 골재 중 적어도 어느 하나인 것을 특징으로 하는 폴리머 콘크리트 조성물.The method of claim 1,
The aggregate is a polymer concrete composition, characterized in that the particle size is at least any one of crushed stone, steel gravel, silica and artificial light aggregate of 13mm or less.
상기 제 1 충전재는 입경이 1㎛ 내지 30㎛인 중질 탄산칼슘, 석분, 슬래그, 시멘트, 플라이애쉬 및 제지애쉬 중 적어도 어느 하나이고,
상기 제 2 충전재는 입경이 20㎛ 내지 40㎛인 미세규사인 것을 특징으로 하는 폴리머 콘크리트 조성물.The method of claim 1,
The first filler is at least one of heavy calcium carbonate, stone powder, slag, cement, fly ash and paper ash having a particle diameter of 1㎛ 30㎛,
The second filler is a polymer concrete composition, characterized in that the fine silica having a particle diameter of 20㎛ to 40㎛.
상기 차열재는 중공의 구상형태를 갖는 알루미노 실리케이트 세라믹 및 실리카 알루미나 세라믹 중 적어도 어느 하나인 무기질 미립자인 것을 특징으로 하는 폴리머 콘크리트 조성물.The method of claim 1,
The heat shield is a polymer concrete composition, characterized in that the inorganic fine particles of at least one of aluminosilicate ceramic and silica alumina ceramic having a hollow spherical shape.
폴리머 콘크리트 조성물은 0.5 중량부 내지 5 중량부의 경화제를 더 포함하는 것을 특징으로 하는 폴리머 콘크리트 조성물.The method of claim 1,
The polymer concrete composition further comprises 0.5 parts by weight to 5 parts by weight of a curing agent.
상기 결합재의 총 중량의 4 중량부 내지 5 중량부의 은 이온 항균제를 더 포함하는 것을 특징으로 하는 폴리머 콘크리트 조성물.The method of claim 1,
4 to 5 parts by weight of the silver ion antimicrobial agent of the total weight of the binder further comprises a polymer concrete composition.