KR20120074765A - Preparing method of polysulfone membrane using phase inversion - Google Patents

Preparing method of polysulfone membrane using phase inversion Download PDF

Info

Publication number
KR20120074765A
KR20120074765A KR1020100136703A KR20100136703A KR20120074765A KR 20120074765 A KR20120074765 A KR 20120074765A KR 1020100136703 A KR1020100136703 A KR 1020100136703A KR 20100136703 A KR20100136703 A KR 20100136703A KR 20120074765 A KR20120074765 A KR 20120074765A
Authority
KR
South Korea
Prior art keywords
solvent
polysulfone
prepared
separator
film forming
Prior art date
Application number
KR1020100136703A
Other languages
Korean (ko)
Other versions
KR101285870B1 (en
Inventor
이근우
이진영
한명진
Original Assignee
한국원자력연구원
한국수력원자력 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 한국원자력연구원, 한국수력원자력 주식회사 filed Critical 한국원자력연구원
Priority to KR1020100136703A priority Critical patent/KR101285870B1/en
Publication of KR20120074765A publication Critical patent/KR20120074765A/en
Application granted granted Critical
Publication of KR101285870B1 publication Critical patent/KR101285870B1/en

Abstract

PURPOSE: A method for manufacturing a polysulfone separating membrane using a phase conversion method is provided to adjust the thickness of a dense layer on the surface of the separating membrane. CONSTITUTION: A method for manufacturing a polysulfone separating membrane using a phase conversion method includes the following: polysulfone is mixed with a solvent and a non-solvent additive to obtain a film forming solution; the film forming solution is applied on the upper side of a substrate to form a film; and the film is immersed in a immersing bath filled with a non-solvent and is solidified. The solvent is n-methyl pyrrolidone, dimethyl acetamide, or dimethyl formamide. The non-solvent additive is carbon tetrachloride or cyclohexane.

Description

상전환법을 이용한 폴리설폰 분리막의 제조방법{Preparing method of polysulfone membrane using phase inversion}Preparation method of polysulfone membrane using phase inversion}

본 발명은 상전환법을 이용한 폴리설폰 분리막의 제조방법에 관한 것이다.
The present invention relates to a method for producing a polysulfone separator using a phase inversion method.

고분자 분리막은 분리 대상 물질에 따라 다양한 방법으로 제조할 수 있으며, 현재 고분자 분리막을 제조하는 가장 보편적인 방법은 상전환 현상을 이용하여 다공성을 갖게 하는 상전환법(Phase Inversion Process)이다. 상전환법은 용매와 비용매의 상호 교환에 의한 고분자의 고형화를 유도하여 막을 제조하는 공정으로, 상분리가 전제된 열역학적으로 안정된 고분자 용액을 제조하되 고분자 소재를 적절한 용매에 용해시켜 균일한 용액을 제조하는 것이 중요하다. 상기 고분자 용액을 유리판과 같은 지지체에 제막한 후 비용매에 침지시키면 용매와 비용매의 상호 확산에 의한 고분자 용액의 조성이 변하게 된다. 이때 액체-액체 상분리 현상을 포함한 고분자의 고형화 현상이 일어나게 되면서 용매와 비용매가 차지하고 있던 부분의 일부분이 기공으로 되어 막의 형상을 이루게 된다.
The polymer membrane can be prepared by various methods according to the material to be separated, and at present, the most common method of preparing the polymer membrane is the phase inversion process (Phase Inversion Process) to have a porosity using a phase inversion phenomenon. The phase inversion method is a process for preparing a membrane by inducing solidification of a polymer by mutual exchange of a solvent and a non-solvent, and preparing a thermodynamically stable polymer solution premised on phase separation, but dissolving the polymer material in an appropriate solvent to prepare a uniform solution. It is important to do. When the polymer solution is formed on a support such as a glass plate and then immersed in a non-solvent, the composition of the polymer solution is changed by the mutual diffusion of the solvent and the non-solvent. At this time, the solidification of the polymer, including the liquid-liquid phase separation phenomenon occurs as a portion of the portion occupied by the solvent and the non-solvent becomes a pore to form the membrane.

분리 대상 물질이 액체인 경우 역삼투압막을 제외한 한외여과 및 정밀여과용 고분자 분리막은 다공성의 표면을 지니는 것이 일반적이며, 기체 분리에 사용되는 막의 경우 표면이 비다공성 성질을 지니는 것이 일반적이라 할 수 있다. 다공성막의 제조는 고분자를 적합한 용매에 용해시킨 고분자 용액을 필름, 튜브 또는 중공사 (hollow fiber) 형태로 성형한 후 비용매 욕조에 침지하며, 용매와 비용매의 상호 교환에 의하여 고분자를 응집시켜 고형화시키거나, 투명 필름, 레이저 등을 사용한 2차 처리를 통해 기공성을 부여하여 제조하는 방법이 널리 이용되고 있다. 반면, 비다공성막은 고분자 용액을 제조한 후 휘발성 용매를 빠르게 증발시켜 제막용액의 표면 밀집도를 향상시킨 후 비용매 욕조에 침지시켜 제조할 수 있다.
When the material to be separated is a liquid, the ultrafiltration and microfiltration membranes except for the reverse osmosis membrane generally have a porous surface, and in the case of a membrane used for gas separation, the surface has a non-porous property. In the preparation of the porous membrane, the polymer solution in which the polymer is dissolved in a suitable solvent is formed into a film, tube or hollow fiber, and then immersed in a non-solvent bath, and the polymer is solidified by agglomeration of the solvent and the non-solvent. Or a method of imparting porosity through secondary treatment using a transparent film, laser, or the like, has been widely used. On the other hand, the non-porous membrane may be prepared by preparing a polymer solution and rapidly evaporating a volatile solvent to improve the surface density of the film forming solution and then immersing it in a non-solvent bath.

일반적으로 고분자 분리막은 분리성능을 향상시키기 위하여 막의 표면층에서 선택 분리하는 기능을 갖는 치밀층을 유지하고, 그 하부의 지지층은 다공성 구조를 가지는 비대칭형 막으로 제조된다. 이러한 비대칭형 막의 제조에 가장 널리 활용되는 상전환법을 통한 분리막의 제조 공정에서 막의 구조에 영향을 미치는 요인은 용매와 비용매의 상호 확산 속도와 이에 따른 조성 변화에 의해 일어나는 용액의 상분리 현상이라 할 수 있다. 용매와 비용매의 상호 확산이 빠르고 비용매가 고분자와 열역학적으로 호환성이 낮아 상분리 현상이 급격히 진행될 경우 막의 내부에 큰 기공구조(finger-like structure)가 생기는 것이 일반적이며, 상분리 현상이 지연될 경우 치밀한 표면층과 함께 막의 내부에 균일한 미세 기공구조(sponge-like structure)가 생성되는 것이 일반적이다. 이때 고분자, 용매, 비용매의 상호작용이 열역학적 상분리도에서 상분리가 일어나는 경계선(binodal 또는 spinodal curve)을 결정하게 된다.
In general, the polymer membrane maintains a dense layer having a function of selectively separating from the surface layer of the membrane in order to improve separation performance, and the support layer below is made of an asymmetric membrane having a porous structure. The most important factor affecting the structure of the membrane through the phase inversion method, which is widely used for the production of such asymmetric membranes, is the phase separation of the solution caused by the rate of diffusion of the solvent and the non-solvent and the composition change. Can be. The rapid diffusion of solvents and non-solvents and the non-solvents are incompatible with polymers thermodynamically lead to large pore-like structures inside the membrane when the phase separation progresses rapidly, and a dense surface layer when the phase separation is delayed. In addition, a uniform sponge-like structure is generally generated inside the membrane. At this time, the interaction of the polymer, the solvent, and the non-solvent determines the boundary line (binodal or spinodal curve) in which the phase separation occurs in the thermodynamic phase separation.

한편, 폴리설폰은 우수한 물리 화학적 특성을 나타내어 정밀여과 또는 한외여과를 위한 공정에 직접 사용되거나 역삼투압 및 나노여과막의 지지층 등 다양하게 이용되고 있다. 또한, 상전환공정에 적용되기에 적합한 용해도 특성을 지니고 있어 고분자를 이용한 상전환 분리막의 제조 공정에서 폴리설폰이 널리 이용되어 왔으며, 폴리설폰 분리막의 구조 및 형상 변화를 위해 제막용액에 비용매를 첨가하거나 제조된 고분자 막의 표면 개질을 유도하는 방법 등 다양한 방법이 연구되고 있다.
On the other hand, polysulfone exhibits excellent physicochemical properties and is used directly in the process for microfiltration or ultrafiltration, or variously used as a support layer of reverse osmosis and nanofiltration membranes. In addition, polysulfone has been widely used in the process of manufacturing a phase inversion membrane using a polymer because it has solubility characteristics suitable for the phase inversion process, and a nonsolvent is added to the film forming solution to change the structure and shape of the polysulfone separator. In addition, various methods such as a method of inducing surface modification of the prepared polymer membrane have been studied.

이에 본 발명자들은 고분자 분리막의 투과도를 향상시킬 수 있는 방법을 연구하던 중 비용매 첨가제 및 폴리설폰의 조성을 적절히 조절하여 사용함으로써 제막용액의 열역학적 안정성을 변화시켜 고분자 분리막의 형상 및 투과 특성을 제어할 수 있는 상전환법을 이용한 폴리설폰 분리막의 제조방법을 개발하고, 본 발명을 완성하였다.
Accordingly, the present inventors can control the shape and permeation characteristics of the polymer membrane by changing the thermodynamic stability of the membrane forming solution by appropriately adjusting the composition of the non-solvent additive and polysulfone while studying a method for improving the permeability of the polymer membrane. To develop a method for producing a polysulfone separation membrane using a phase inversion method, and completed the present invention.

본 발명의 목적은 상전환법을 이용한 폴리설폰 분리막의 제조방법을 제공하는데 있다.
An object of the present invention to provide a method for producing a polysulfone separation membrane using a phase inversion method.

상기 목적을 달성하기 위하여, 본 발명은 폴리설폰을 용매 및 비용매 첨가제와 혼합하여 제막용액을 제조하는 단계(단계 1); 상기 단계 1에서 제조된 제막용액을 기판 상부로 도포하여 막을 형성시키는 단계(단계 2); 및 상기 단계 2에서 제조된 막을 비용매가 채워진 침지조에 침지하여 고형화시키는 단계(단계 3)를 포함하는 것을 특징으로 하는 상전환법을 이용한 폴리설폰 분리막의 제조방법법을 제공한다.
In order to achieve the above object, the present invention comprises the steps of preparing a film forming solution by mixing polysulfone with a solvent and a non-solvent additive (step 1); Coating the film forming solution prepared in step 1 on the substrate to form a film (step 2); And solidifying the membrane prepared in step 2 by immersing the membrane prepared in a non-solvent-filled dipping tank (step 3).

본 발명에 따른 상전환법을 이용한 폴리설폰 분리막의 제조방법은 폴리설폰, 용매 및 비용매 첨가제의 조성을 적절히 조절하여 제막용액을 형성하고, 상기 제막용액으로부터 상전환법을 이용하여 분리막을 제조함으로써, 분리막 표면의 치밀층 두께를 조정할 수 있어 분리막의 투과도를 제어할 수 있다.
In the method for preparing a polysulfone separator using the phase inversion method according to the present invention, a film forming solution is formed by appropriately adjusting the composition of polysulfone, a solvent and a nonsolvent additive, and by preparing a separator using the phase inversion method from the film forming solution, The thickness of the dense layer on the surface of the separator can be adjusted to control the permeability of the separator.

도 1은 비교예 1 내지 4에서 제조된 분리막 단면의 주사전자현미경 사진이고;
도 2는 비교예 5에서 제조된 분리막 단면의 주사전자현미경 사진이고;
도 3은 실시예 1 내지 4에서 제조된 분리막 단면의 주사전자현미경 사진이고;
도 4는 실시예 5 내지 8에서 제조된 분리막 단면의 주사전자현미경 사진이고;
도 5는 투과율 측정장치 및 디스크 모듈의 개략도이고;
도 6은 실시예 1 내지 4에서 제조된 분리막의 투과율을 측정한 그래프이고; 및
도 7은 실시예 5 내지 8에서 제조된 분리막의 투과율을 측정한 그래프이다.1 is a scanning electron micrograph of the cross section of the separator prepared in Comparative Examples 1 to 4;
2 is a scanning electron micrograph of a cross section of the separator prepared in Comparative Example 5;
3 is a scanning electron micrograph of the cross section of the separator prepared in Examples 1 to 4;
4 is a scanning electron micrograph of the cross section of the separator prepared in Examples 5 to 8;
5 is a schematic diagram of an apparatus for measuring transmittance and a disk module;
6 is a graph measuring the transmittance of the separator prepared in Examples 1 to 4; And
7 is a graph measuring the transmittance of the separator prepared in Examples 5 to 8.

본 발명은 폴리설폰을 용매 및 비용매 첨가제와 혼합하여 제막용액을 제조하는 단계(단계 1);The present invention comprises the steps of preparing a film forming solution by mixing polysulfone with a solvent and a non-solvent additive (step 1);

상기 단계 1에서 제조된 제막용액을 기판 상부로 도포하여 막을 형성시키는 단계(단계 2); 및Coating the film forming solution prepared in step 1 on the substrate to form a film (step 2); And

상기 단계 2에서 제조된 막을 비용매가 채워진 침지조에 침지하여 고형화시키는 단계(단계 3)를 포함하는 것을 특징으로 하는 상전환법을 이용한 폴리설폰 분리막의 제조방법을 제공한다.
It provides a method for producing a polysulfone separation membrane using a phase inversion method comprising the step (step 3) of immersing the membrane prepared in step 2 in a non-solvent-filled immersion tank.

이하, 본 발명을 상세히 설명한다.
Hereinafter, the present invention will be described in detail.

본 발명에 따른 상전환법을 이용한 폴리설폰 분리막의 제조방법에 있어서, 단계 1은 폴리설폰을 용매 및 비용매 첨가제와 혼합하여 제막용액을 제조하는 단계이다. 상기 단계 1에서 폴리설폰, 용매 및 비용매 첨가제를 혼합하여 제조되는 제막용액은 분리막 형성을 위한 원료로서 폴리설폰, 용매 및 비용매 첨가제의 조성이 적절하게 조절되어 제조된다. 상기 용매는 폴리설폰을 용해시키는 극성의 비양성자성(polar aprotic)특성을 가짐으로써, 폴리설폰을 균질하게 용해시킬 수 있으며, 이때 상기 용매는 n-메틸 피롤리돈(n-methyl pyrrolidone), 디메틸아세트아마이드(dimethylacetamide), 디메틸포름아마이드(dimethylformamide) 등을 사용할 수 있다. 상기 용매 각각의 용해도 특성을 나타내는 지표인 용해도상수 (solubility parameter)를 폴리설폰과 비교하여 살펴보면 분산력 기여도를 나타내는 δd는 폴리설폰 값에 근접한 반면, 극성성분의 기여도 (δp)를 나타내는 값은 이들 용매들의 극성 특성으로 인해 폴리설폰과 큰 차이가 있다. In the method for preparing a polysulfone separator using the phase inversion method according to the present invention, step 1 is a step of preparing a film forming solution by mixing polysulfone with a solvent and a non-solvent additive. The film forming solution prepared by mixing the polysulfone, the solvent and the non-solvent additive in step 1 is prepared by properly adjusting the composition of the polysulfone, the solvent and the non-solvent additive as a raw material for forming the separator. The solvent has a polar aprotic property of dissolving polysulfone, thereby homogeneously dissolving polysulfone, wherein the solvent is n-methyl pyrrolidone, dimethyl Acetamide (dimethylacetamide), dimethylformamide (dimethylformamide) and the like can be used. When comparing the solubility parameter (solubility parameter), which is an indicator of the solubility characteristics of each solvent, with polysulfone, δ d representing the dispersibility is close to the polysulfone value, while values representing the contribution of the polar component (δ p ) are these. Due to the polar nature of the solvents there is a big difference from polysulfone.

따라서, 비용매 첨가제로서 극성성분 기여도 값(δp)이 낮고 폴리설폰을 분산시키지않는 사염화탄소, 싸이클로헥산 등을 사용할 수 있다. 상기 비용매 첨가제를 첨가함으로써 제막용액의 점도가 낮아지게 하므로 유동성이 증가하게 된다. 이에 따라, 상기 비용매 첨가제가 첨가된 제막용액을 상전환법을 이용하여 분리막으로 제조하면, 분리막의 표면층 두께를 조절할 수 있어 투과도 등의 특성을 제어할 수 있다.Therefore, as the non-solvent additive, carbon tetrachloride, cyclohexane, or the like having low polar component contribution value (δ p ) and not dispersing polysulfone can be used. By adding the nonsolvent additive, the viscosity of the film forming solution is lowered, thereby increasing the fluidity. Accordingly, when the film-forming solution to which the non-solvent additive is added is prepared as a separator using a phase inversion method, the thickness of the surface layer of the separator can be adjusted to control characteristics such as permeability.

상기 단계 1에 있어서, 폴리설폰은 용매에 대하여 10 내지 20 중량%로 혼합되는 것이 바람직하다. 상기 폴리설폰이 10 중량% 미만으로 혼합되는 경우 제조된 제막용액 중 폴리설폰의 함량이 낮아 고분자 분리막으로 제조할 수 없는 문제가 있고, 폴리설폰이 20 중량%를 초과하여 혼합되는 경우 제막용액의 점도가 높아져 분리막의 투과도가 저하되는 문제가 있다.In step 1, the polysulfone is preferably mixed in 10 to 20% by weight relative to the solvent. When the polysulfone is mixed at less than 10% by weight, there is a problem in that the content of polysulfone is not low because of the low content of polysulfone prepared in the prepared membrane solution. There is a problem in that the permeability of the separation membrane is lowered.

상기 단계 1에 있어서, 비용매 첨가제는 용매에 대하여 1 내지 20 중량%로 혼합되는 것이 바람직하다. 상기 비용매 첨가제가 1 중량% 미만으로 혼합되는 경우 제조된 제막용액으로 분리막을 제조하여도 표면층의 두께 및 내부 다공성 층의 형상을 제어하지 못하는 문제가 있고, 비용매 첨가제가 20 중량%를 초과하여 혼합되는 경우 제조된 제막용액의 점도가 과도하게 낮아져 막 형성이 어려운 문제가 있다.
In step 1, the non-solvent additive is preferably mixed at 1 to 20% by weight based on the solvent. When the non-solvent additive is mixed at less than 1% by weight, there is a problem in that the thickness of the surface layer and the shape of the inner porous layer are not controlled even when the separation membrane is manufactured with the prepared film-forming solution. When mixed, the viscosity of the prepared film forming solution is excessively low, and there is a problem that film formation is difficult.

본 발명에 따른 상전환법을 이용한 폴리설폰 분리막의 제조방법에 있어서, 단계 2는 상기 단계 1에서 제조된 제막용액을 기판 상부로 도포하여 막을 형성시키는 단계이다. 이때, 상기 단계 2의 기판은 유리판 등을 사용할 수 있으나, 이에 제한되는 것은 아니다. 다만, 상기 단계 2의 기판으로 유리판을 사용함으로써 공정가격을 낮출 수 있으며, 평탄하고 균질한 막을 형성시킬 수 있다.
In the method for producing a polysulfone separator using the phase inversion method according to the invention, step 2 is a step of forming a film by applying the film forming solution prepared in step 1 to the upper substrate. In this case, the substrate of step 2 may be a glass plate or the like, but is not limited thereto. However, by using the glass plate as the substrate of step 2, the process price can be lowered, and a flat and homogeneous film can be formed.

본 발명에 따른 상전환법을 이용한 폴리설폰 분리막의 제조방법에 있어서, 단계 3은 상기 단계 2에서 제조된 막을 비용매가 채워진 침지조에 침지하여 고형화시키는 단계이다. 상기 단계 2에서 제조된 막을 비용매가 채워진 침지조에 침지함으로써, 막의 고형화가 이루어지고 기판으로부터 분리하여 고분자 분리막을 제조할 수 있다.In the method for producing a polysulfone separation membrane using the phase inversion method according to the present invention, step 3 is a step of solidifying the membrane prepared in step 2 by immersing in a non-solvent-filled immersion tank. By immersing the membrane prepared in step 2 in a non-solvent-filled immersion tank, the membrane is solidified and can be separated from the substrate to prepare a polymer separator.

상기 단계 3의 비용매는 이소프로필알코올, 메틸알코올, 에틸알코올 등의 저분자성 알코올을 사용할 수 있다. 이에 따라, 상기 비용매와 상기 단계 2의 비극성 첨가제가 첨가된 막의 기여도 값(δp) 차이에 따른 열역학적 변화에 있어, 열역학적으로 균일성을 유지할 수 있는 영역이 줄어들게 되고, 단계 3에서 제조되는 분리막의 표면층의 두께가 변화된다. 즉, 상기와 같이 열역학적으로 균일성을 유지할 수 있는 영역이 줄어들어 열역학적 호환성이 감소되는 경우 상전환법을 통해 제조된 막의 투과도가 향상되고, 막의 내부에 거대 기공이 형성되어 표면층의 밀집도가 감소되는 현상이 나타난다. 이때, 상기 분리막 표면층의 두께는 제막용액의 조성에 따라 조절될 수 있고, 이에 따라 막 투과도를 조절할 수 있다.
The non-solvent of step 3 may be a low molecular alcohol such as isopropyl alcohol, methyl alcohol, ethyl alcohol. Accordingly, in the thermodynamic change according to the difference in the contribution value (δp) of the membrane to which the non-solvent and the nonpolar additive of step 2 are added, the area capable of maintaining thermodynamic uniformity is reduced, and the separation membrane prepared in step 3 The thickness of the surface layer is changed. That is, when the area capable of maintaining uniformity in the thermodynamics is reduced as described above, when the thermodynamic compatibility is reduced, the permeability of the membrane produced through the phase inversion method is improved, and macropores are formed in the membrane to reduce the density of the surface layer. Appears. In this case, the thickness of the membrane surface layer may be adjusted according to the composition of the film forming solution, thereby adjusting the membrane permeability.

본 발명에 따른 상전환법을 이용한 폴리설폰 분리막의 제조방법은 상기 단계 3에서 제조된 분리막을 증류수가 채워진 침지조에 1 내지 2회 재침지하는 단계를 더 포함할 수 있다. 본 발명에 따라 제조된 폴리설폰 분리막을 증류수가 채워진 침지조에 1 내지 2회 재침지하여 상기 단계 3에서 사용되었던 비용매와 증류수와의 교환이 이루어지며, 폴리설폰 분리막의 자연 건조를 통하여 막 내부에 다공성층이 형성된다.
The method for producing a polysulfone separator using the phase inversion method according to the present invention may further include re-immersing the separator prepared in step 3 in a dipping water-filled dipping tank once or twice. The polysulfone separator prepared according to the present invention is immersed once or twice in a dipping tank filled with distilled water to exchange non-solvent and distilled water used in step 3, and the inside of the membrane through natural drying of the polysulfone separator A porous layer is formed.

본 발명은 폴리설폰을 용매 및 비용매 첨가제와 혼합하여 제막용액을 제조하고, 상기 제조된 제막용액을 유리판 상부로 도포하여 막을 형성시킨 후 비용매가 채워진 침지조에 침지함으로써 제조되는 폴리설폰 분리막을 제공한다.The present invention provides a polysulfone membrane prepared by mixing a polysulfone with a solvent and a nonsolvent additive to prepare a film forming solution, applying the prepared film forming solution to the upper glass plate to form a film, and then immersing it in a non-solvent-filled dipping tank. .

본 발명에 따른 폴리설폰 분리막은 비용매와 상기 비극성 첨가제의 기여도 값(δp) 차이에 따른 열역학적 변화로 인하여, 열역학적으로 균일성을 유지할 수 있는 영역이 줄어들어 분리막 표면의 밀집층의 두께가 감소하며, 이에 따라 우수한 투과도를 나타낸다. 상기 표면 밀집층의 두께 감소는 비극성 첨가제를 포함하는 제막용액으로부터 침지용 비용매로의 확산이 나타났기 때문으로, 비극성 첨가제와 비용매와의 열역학적 불안정성이 증가하여도, 상전환법으로 제조되는 막의 형상 및 투과특성을 결정하는 주요 인자인 제막용액에서의 용매와 침지용 비용매 사이의 상호확산이 제막용액으로부터 침지용 비용매로의 확산에 의해 주도되었음을 나타낸다. In the polysulfone separator according to the present invention, due to the thermodynamic change according to the difference of the contribution value (δp) of the non-solvent and the non-polar additive, the area capable of maintaining the thermodynamic uniformity is reduced, so that the thickness of the dense layer on the surface of the separator is reduced. This shows excellent transmittance. The decrease in the thickness of the surface dense layer is due to the diffusion from the film forming solution containing the nonpolar additive to the non-solvent for immersion, so that even if the thermodynamic instability between the nonpolar additive and the nonsolvent increases, the shape of the film produced by the phase inversion method is increased. And the interdiffusion between the solvent and the immersion nonsolvent in the film forming solution, which are the main factors for determining the permeation characteristics, were driven by the diffusion from the film forming solution to the immersion nonsolvent.

또한, 본 발명에 따른 폴리설폰 분리막은 액체폐기물 처리에 이용될 수 있다. 본 발명에 따른 폴리설폰 분리막은 우수한 막 투과성을 가지며, 내부 다공성 층에 거대기공이 존재하여, 이물질로 인하여 분리막의 투과성이 저하되는 문제를 방지할 수 있어 액체폐기물 처리에 유용하게 이용될 수 있다.
In addition, the polysulfone separator according to the present invention can be used for liquid waste treatment. Polysulfone separator according to the present invention has excellent membrane permeability, there is a large pore in the inner porous layer, it is possible to prevent the problem that the permeability of the separator due to the foreign matter can be usefully used for the liquid waste treatment.

이하, 본 발명을 하기의 실시예에 의해 더욱 상세히 설명한다. 단, 하기의 실시예는 본 발명을 예시할 뿐, 본 발명의 내용이 하기의 실시예에 의해 한정되는 것은 아니다.
Hereinafter, the present invention will be described in more detail by the following examples. However, the following examples merely illustrate the present invention, and the contents of the present invention are not limited by the following examples.

<실시예 1> 폴리설폰 분리막의 제조 1 Example 1 Preparation of Polysulfone Separation Membrane 1

단계 1: 폴리설폰 15 중량%, 싸이클로 헥산 5 중량% 및 용매인 n-메틸피롤리돈 80 중량%를 자력교반기를 이용하여 혼합함으로써 제막용액을 제조하였다.
Step 1: A film forming solution was prepared by mixing 15% by weight of polysulfone, 5% by weight of cyclohexane, and 80% by weight of a solvent, n-methylpyrrolidone, using a magnetic stirrer.

단계 2: 상기 단계 1에서 제조된 제막용액을 유리판 상부로 닥터블레이드(doctor blade)를 사용하여 300 μm의 두께로 제막하였다.
Step 2: The film forming solution prepared in Step 1 was formed into a film having a thickness of 300 μm by using a doctor blade on the glass plate.

단계 3: 상기 단계 2에서 제막된 막을 이소프로필알코올이 담긴 침지조에 24 시간 동안 침지한 후, 증류수가 담긴 침지조에 24 시간 동안 재침지하여 폴리설폰 분리막을 제조하였다.
Step 3: The membrane formed in step 2 was immersed in an immersion tank containing isopropyl alcohol for 24 hours, and then immersed in an immersion tank containing distilled water for 24 hours to prepare a polysulfone separator.

<실시예 2> 폴리설폰 분리막의 제조 2 Example 2 Preparation of Polysulfone Separation Membrane 2

상기 실시예 1의 싸이클로 헥산을 10 중량% 사용하고, n-메틸피롤리돈을 75 중량% 사용하여 제막용액을 제조한 것을 제외하고는 상기 실시예 1과 동일하게 수행하여 폴리설폰 분리막을 제조하였다.
A polysulfone separator was prepared in the same manner as in Example 1 except that 10 wt% of hexane was used as the cycle of Example 1 and 75 wt% of n-methylpyrrolidone was used to prepare a film forming solution. .

<실시예 3> 폴리설폰 분리막의 제조 3Example 3 Preparation of Polysulfone Separation Membrane 3

상기 실시예 1의 싸이클로 헥산을 15 중량% 사용하고, n-메틸피롤리돈을 70 중량% 사용하여 제막용액을 제조한 것을 제외하고는 상기 실시예 1과 동일하게 수행하여 폴리설폰 분리막을 제조하였다.
A polysulfone separator was prepared in the same manner as in Example 1, except that 15 wt% of hexane was used as the cycle of Example 1 and 70 wt% of n-methylpyrrolidone was used to prepare a film forming solution. .

<실시예 4> 폴리설폰 분리막의 제조 4Example 4 Preparation of Polysulfone Separation Membrane 4

상기 실시예 1의 싸이클로 헥산을 20 중량% 사용하고, n-메틸피롤리돈을 65 중량% 사용하여 제막용액을 제조한 것을 제외하고는 상기 실시예 1과 동일하게 수행하여 폴리설폰 분리막을 제조하였다.
A polysulfone separator was prepared in the same manner as in Example 1 except that 20 wt% of hexane was used as the cycle of Example 1 and 65 wt% of n-methylpyrrolidone was used to prepare a film forming solution. .

<실시예 5> 폴리설폰 분리막의 제조 5Example 5 Preparation of Polysulfone Separation Membrane 5

상기 실시예 1의 싸이클로 헥산 대신 사염화탄소 5 중량%를 사용하여 제막용액을 제조한 것을 제외하고는 실시예 1과 동일하게 수행하여 폴리설폰 분리막을 제조하였다.
A polysulfone separator was prepared in the same manner as in Example 1, except that 5 wt% carbon tetrachloride was used instead of hexane as the cycle of Example 1 to prepare a film forming solution.

<실시예 6> 폴리설폰 분리막의 제조 6Example 6 Preparation of Polysulfone Separation Membrane 6

상기 실시예 5의 사염화탄소를 10 중량% 사용하고, n-메틸피롤리돈을 75 중량% 사용하여 제막용액을 제조한 것을 제외하고는 상기 실시예 5와 동일하게 수행하여 폴리설폰 분리막을 제조하였다.
A polysulfone separator was prepared in the same manner as in Example 5 except that 10 wt% of carbon tetrachloride of Example 5 was used and 75 wt% of n-methylpyrrolidone was used to prepare a film forming solution.

<실시예 7> 폴리설폰 분리막의 제조 7Example 7 Preparation of Polysulfone Separation Membrane 7

상기 실시예 5의 사염화탄소를 15 중량% 사용하고, n-메틸피롤리돈을 70 중량% 사용하여 제막용액을 제조한 것을 제외하고는 상기 실시예 5와 동일하게 수행하여 폴리설폰 분리막을 제조하였다.
A polysulfone separator was prepared in the same manner as in Example 5 except that 15 wt% of carbon tetrachloride of Example 5 was used and 70 wt% of n-methylpyrrolidone was used to prepare a film forming solution.

<실시예 8> 폴리설폰 분리막의 제조 8 Example 8 Preparation of Polysulfone Separation Membrane 8

상기 실시예 5의 사염화탄소를 20 중량% 사용하고, n-메틸피롤리돈을 65 중량% 사용하여 제막용액을 제조한 것을 제외하고는 상기 실시예 5와 동일하게 수행하여 폴리설폰 분리막을 제조하였다.
A polysulfone separator was prepared in the same manner as in Example 5, except that 20 wt% of carbon tetrachloride of Example 5 was used and 65 wt% of n-methylpyrrolidone was used to prepare a film forming solution.

<비교예 1> 폴리설폰 분리막의 제조 9 Comparative Example 1 Preparation of Polysulfone Separation Membrane 9

단계 1: 폴리설폰 15 중량% 및 용매인 n-메틸피롤리돈 85 중량%를 자력교반기를 이용하여 혼합함으로써 제막용액을 제조하였다.
Step 1: A film forming solution was prepared by mixing 15% by weight of polysulfone and 85% by weight of a solvent, n-methylpyrrolidone, using a magnetic stirrer.

단계 2: 상기 단계 1에서 제조된 제막용액을 유리판 상부로 닥터블레이드(doctor blade)를 사용하여 300 μm의 두께로 제막하였다.
Step 2: The film forming solution prepared in Step 1 was formed into a film having a thickness of 300 μm by using a doctor blade on the glass plate.

단계 3: 상기 단계 2에서 제막된 막을 이소프로필알코올이 담긴 침지조에 24 시간 동안 침지한 후, 증류수가 담긴 침지조에 24 시간 동안 재침지하여 폴리설폰 분리막을 제조하였다.
Step 3: The membrane formed in step 2 was immersed in an immersion tank containing isopropyl alcohol for 24 hours, and then immersed in an immersion tank containing distilled water for 24 hours to prepare a polysulfone separator.

<비교예 2> 폴리설폰 분리막의 제조 10Comparative Example 2 Preparation of Polysulfone Separation Membrane 10

단계 1: 폴리설폰 15 중량%, 벤젠 20 중량% 및 용매인 n-메틸피롤리돈 65 중량%를 자력교반기를 이용하여 혼합함으로써 제막용액을 제조하였다.
Step 1: A film forming solution was prepared by mixing 15% by weight of polysulfone, 20% by weight of benzene and 65% by weight of a solvent, n-methylpyrrolidone, using a magnetic stirrer.

단계 2: 상기 단계 1에서 제조된 제막용액을 유리판 상부로 닥터블레이드(doctor blade)를 사용하여 300 μm의 두께로 제막하였다.
Step 2: The film forming solution prepared in Step 1 was formed into a film having a thickness of 300 μm by using a doctor blade on the glass plate.

단계 3: 상기 단계 2에서 제막된 막을 이소프로필알코올이 담긴 침지조에 24 시간 동안 침지한 후, 증류수가 담긴 침지조에 24 시간 동안 재침지하여 폴리설폰 분리막을 제조하였다.
Step 3: The membrane formed in step 2 was immersed in an immersion tank containing isopropyl alcohol for 24 hours, and then immersed in an immersion tank containing distilled water for 24 hours to prepare a polysulfone separator.

<비교예 3> 폴리설폰 분리막의 제조 11Comparative Example 3 Preparation of Polysulfone Membrane 11

상기 비교예 2의 벤젠을 40 중량% 사용하고, n-메틸피롤리돈을 45 중량% 사용하여 제막용액을 제조한 것을 제외하고는 상기 비교예 2와 동일하게 수행하여 폴리설폰 분리막을 제조하였다.
A polysulfone separator was prepared in the same manner as in Comparative Example 2 except that 40 wt% of benzene of Comparative Example 2 and 45 wt% of n-methylpyrrolidone were used to prepare a film forming solution.

<비교예 4> 폴리설폰 분리막의 제조 12Comparative Example 4 Preparation of Polysulfone Separation Membrane 12

상기 비교예 2의 벤젠을 60 중량% 사용하고, n-메틸피롤리돈을 25 중량% 사용하여 제막용액을 제조한 것을 제외하고는 상기 비교예 2와 동일하게 수행하여 폴리설폰 분리막을 제조하였다.
A polysulfone separator was prepared in the same manner as in Comparative Example 2, except that 60 wt% of the benzene of Comparative Example 2 was used and 25 wt% of n-methylpyrrolidone was used to prepare a film forming solution.

<비교예 5> 폴리설폰 분리막의 제조 10Comparative Example 5 Preparation of Polysulfone Separation Membrane 10

단계 1: 폴리설폰 15 중량%와 용매인 n-메틸피롤리돈 85 중량%를 자력교반기를 이용하여 혼합함으로써 제막용액을 제조하였다.
Step 1: A film forming solution was prepared by mixing 15% by weight of polysulfone and 85% by weight of a solvent, n-methylpyrrolidone, using a magnetic stirrer.

단계 2: 상기 단계 1에서 제조된 제막용액을 유리판 상부로 닥터블레이드(doctor blade)를 사용하여 300 μm의 두께로 제막하였다.
Step 2: The film forming solution prepared in Step 1 was formed into a film having a thickness of 300 μm by using a doctor blade on the glass plate.

단계 3: 상기 단계 2에서 제막된 막을 증류수가 담긴 침지조에 24 시간 동안 침지하여 폴리설폰 분리막을 제조하였다.
Step 3: The polysulfone membrane was prepared by immersing the membrane formed in step 2 in an immersion tank containing distilled water for 24 hours.

분석analysis

(1) 흐림점(cloud point) 측정(1) cloud point measurement

제막용액의 조성에 따른 상분리현상의 변화를 측정하기 위하여, 실시예 1 내지 8 및 비교예 1의 단계 1까지 수행되어 제조된 제막용액을 삼각플라스크에 담고 고무격막으로 막고, 자력교반기를 이용하여 혼합하고 24 시간 경과 후 균일한 용액이 생성된 것을 확인하고, 교반을 계속 수행하며 비용매인 이소프로필알코올을 고무격막을 통해 주사기를 이용하여 주입하였으며, 용액이 흐리게 변하는 순간의 이소프로필알코올 첨가량을 측정하였다. 상기 측정의 결과는 표 1에 나타내었다.
In order to measure the change of phase separation according to the composition of the film forming solution, the film forming solution prepared by performing steps 1 to 8 and Comparative Example 1 was placed in a Erlenmeyer flask, blocked with a rubber diaphragm, and mixed using a magnetic stirrer. After 24 hours, it was confirmed that a uniform solution was formed, stirring was continued, and non-solvent isopropyl alcohol was injected through a rubber diaphragm using a syringe, and the amount of isopropyl alcohol added at the moment when the solution turned cloudy was measured. . The results of the measurements are shown in Table 1.

이소프로필알코올 첨가량 (g/중량%)Isopropyl alcohol added amount (g / weight%) 실시예 1Example 1 11.42 / 22.211.42 / 22.2 실시예 2Example 2 11.06 / 21.711.06 / 21.7 실시예 3Example 3 10.61 / 20.910.61 / 20.9 실시예 4Example 4 9.90 / 19.89.90 / 19.8 실시예 5Example 5 11.87 / 22.911.87 / 22.9 실시예 6Example 6 11.20 / 21.911.20 / 21.9 실시예 7Example 7 10.93 / 21.510.93 / 21.5 실시예 8Example 8 10.42 / 20.710.42 / 20.7 비교예 1Comparative Example 1 14.11 / 26.114.11 / 26.1

상기 표 1에 나타낸 바와 같이, 실시예 1 내지 8의 단계 1에서 제조된 제막용액은 비용매 첨가제인 싸이클로헥산 또는 사염화탄소의 함량이 증가할수록 흐림점에 도달할 때까지의 이소프로필알코올 첨가량이 감소하는 것을 알 수 있다. 반면 비교예 1의 단계 1에서 제조된 제막용액은 비용매 첨가제가 첨가되지 않아, 이소프로필알코올의 첨가량이 14.11g (26.1 중량%)가 첨가되었을 때 흐림점에 도달하는 것을 알 수 있다. 이는 비용매 첨가제가 첨가됨으로써, 액체-액체 상분리 현상이 더욱 촉진되는 것을 의미하며, 본 발명에 따른 상전환법을 이용한 폴리설폰 분리막의 제조방법에서 비용매 첨가제를 사용함으로써 상전환공정에서 상분리를 용이하게 할 수 있음을 확인하였다.
As shown in Table 1, in the film forming solution prepared in Step 1 of Examples 1 to 8, as the content of cyclohexane or carbon tetrachloride, which is a nonsolvent additive, increases, the amount of isopropyl alcohol added until reaching the cloud point is decreased. It can be seen that. On the other hand, the film forming solution prepared in Step 1 of Comparative Example 1 is not added to the non-solvent additive, it can be seen that the cloud point reaches when the addition amount of isopropyl alcohol 14.11g (26.1% by weight) is added. This means that the liquid-liquid phase separation phenomenon is further promoted by the addition of the non-solvent additive, and the phase separation process is facilitated by using the non-solvent additive in the method for producing a polysulfone separator using the phase shift method according to the present invention. It was confirmed that it can be made.

(2) 점도측정(2) viscosity measurement

제막용액의 조성에 따른 점도 변화를 측정하기 위하여, 실시예 1 내지 8 및 비교예 1의 단계 1까지 수행되어 제조된 제막용액을 Brookfield 점도계를 이용하여 점성계수를 확인하는 방법으로 측정하였고, 결과는 표 2에 나타내었다.
In order to measure the change in viscosity according to the composition of the film forming solution, the film forming solution prepared by performing steps 1 to 8 and Comparative Example 1 was measured by checking the viscosity coefficient using a Brookfield viscometer. Table 2 shows.

회전속도 (rpm)Rotation speed (rpm) 점도 (cP)Viscosity (cP) 토크 (%)talk (%) 실시예 1
Example 1
5050 110.1110.1 8.68.6 100100 111.3111.3 17.417.4 실시예 2
Example 2
5050 107.5107.5 8.48.4 100100 108.8108.8 17.017.0 실시예 3
Example 3
5050 104.9104.9 8.28.2 100100 106.2106.2 16.616.6 실시예 4
Example 4
5050 102.4102.4 8.08.0 100100 105.0105.0 16.416.4 실시예 5
Example 5
5050 133.1133.1 10.410.4 100100 135.7135.7 21.721.7 실시예 6
Example 6
5050 122.9122.9 9.69.6 100100 124.8124.8 19.519.5 실시예 7
Example 7
5050 120.3120.3 9.49.4 100100 122.3122.3 19.119.1 실시예 8
Example 8
5050 119.0119.0 9.39.3 100100 121.0121.0 18.918.9 비교예 1
Comparative Example 1
5050 138.2138.2 10.810.8 100100 138.9138.9 21.721.7

상기 표 2에 나타낸 바와 같이, 실시예 1 내지 8의 단계 1에서 제조된 제막용액은 비용매 첨가제인 싸이클로헥산 또는 사염화탄소의 함량이 증가할수록 점도 및 토크 값이 감소하는 것을 알 수 있다. 반면 비교예 1의 단계 1에서 제조된 제막용액은 비용매 첨가제가 첨가되지 않아, 점도가 약 138 cP로 상대적으로 매우 높은 것을 알 수 있다. 따라서 비용매 첨가제가 첨가됨으로써 제막용액의 점도가 낮아져 유동성이 높아지는 것을 확인하였으며, 제막용액 중의 용매와 비용매 간의 상호확산 속도가 증가할 수 있음을 확인하였다.
As shown in Table 2, the film forming solution prepared in Step 1 of Examples 1 to 8 can be seen that the viscosity and torque value decreases as the content of cyclohexane or carbon tetrachloride, which is a non-solvent additive, increases. On the other hand, the film forming solution prepared in Step 1 of Comparative Example 1 is not added to the non-solvent additive, it can be seen that the viscosity is relatively very high as about 138 cP. Therefore, it was confirmed that the addition of the non-solvent additive lowers the viscosity of the film forming solution, thereby increasing the fluidity, and the interdiffusion rate between the solvent and the non-solvent in the film forming solution may be increased.

(3) 비극성 용매의 상호확산도 측정(3) Measurement of interdiffusion of nonpolar solvent

비극성 용매에 따른 상호확산도의 변화를 측정하기 위하여 Wilke-Chang 식을 이용하여 비극성 용매의 종류에 따른 각각의 확산계수를 계산하였고, 결과를 표 3에 나타내었다.
In order to measure the change of the interdiffusion according to the nonpolar solvent, the diffusion coefficient of each nonpolar solvent was calculated using the Wilke-Chang equation, and the results are shown in Table 3.


상호확산도 (cm2/s×10-6)Mutual Diffusion (cm 2 / s × 10 -6 ) DA →N D A → N DN →A D N → A 사염화탄소 (첨가제) / 이소프로필알코올 (비용매)Carbon tetrachloride (additive) / Isopropyl alcohol (non-solvent) 4.894.89 19.719.7 싸이클로헥산 (첨가제) / 이소프로필알코올 (비용매)Cyclohexane (Additive) / Isopropyl alcohol (Non-solvent) 4.504.50 14.414.4 벤젠 (첨가제) / 이소프로필알코올 (비용매)Benzene (Additive) / Isopropyl Alcohol (Non-solvent) 5.055.05 20.920.9

A : 첨가제A: additive

N : 비용매
N: non-sold

상기 표 3에 나타낸 바와 같이, 비용매 첨가제의 종류에 따라 상호확산도가 변화하는 것을 알 수 있으며, 벤젠의 경우 사염화탄소 및 싸이클로헥산보다 확산속도가 더욱 빠른 것으로 나타났다.
As shown in Table 3, it can be seen that the degree of interdiffusion changes according to the type of non-solvent additive, and benzene was found to have a faster diffusion rate than carbon tetrachloride and cyclohexane.

<실험예 1> 주사전자현미경 분석Experimental Example 1 Scanning Electron Microscope Analysis

본 발명에 따른 실시예 1 내지 8 및 비교예 1 내지 5를 통해 제조된 폴리설폰 분리막 내부의 미세구조를 관찰하기 위하여 주사전자현미경으로 분석하였고, 결과를 도 1 내지 도 4에 나타내었다.In order to observe the microstructure of the polysulfone separator prepared in Examples 1 to 8 and Comparative Examples 1 to 5 according to the present invention was analyzed by a scanning electron microscope, the results are shown in FIGS.

도 1 내지 도 4에 나타낸 바와 같이, 비교예 1 내지 4에서 제조된 고분자 분리막은 비용매 첨가제인 벤젠의 첨가량이 증가함에 따라 표면 치밀층의 두께가 증가하는 것을 알 수 있으며, 벤젠의 첨가량이 60 중량%인 비교예 4의 경우 약 3 배 이상 표면 치밀층의 두께가 증가한 것을 알 수 있다. 또한, 비교예 5에서 증류수로 침지되어 제조된 고분자 분리막의 경우 거대 기공구조가 생긴 것을 알 수 있다. 이는 상전환이 급격하게 발생함에 따라 제막용액 표면의 고형화가 촉진되었기 때문이다. 반면, 실시예 1 내지 8에서 제조된 폴리설폰 분리막은 비용매 첨가제인 싸이클로헥산 또는 사염화탄소의 함량이 증가함에 따라, 표면 치밀층의 두께가 감소하는 것을 알 수 있으며, 사염화탄소의 함량이 20 중량%가 첨가된 실시예 8의 경우 표면 밀집층이 거의 사라진 것을 알 수 있었다. 이를 통하여, 비용매 첨가제가 첨가됨에 따라 표면 치밀층의 두께를 조절할 수 있음을 확인하였으며, 증류수가 아닌 이소프로필알코올과 같은 비용매에 침지하여 폴리설폰 분리막을 제조함으로써 분리막 내부 다공성 층의 기공구조가 치밀하게 형성되는 것을 알 수 있었다 (도 1의 (a): 비교예 1 , (b): 비교예 2 , (c): 비교예 3 , (d): 비교예 4; 도 3의 (a): 실시예 1 , (b): 실시예 2 , (c): 실시예 3 , (d): 실시예 4; 도 4의 (a): 실시예 5 , (b): 실시예 6 , (c): 실시예 7 , (d): 실시예 8 이다).
As shown in Figures 1 to 4, in the polymer membranes prepared in Comparative Examples 1 to 4 it can be seen that the thickness of the surface dense layer increases with the addition amount of benzene as a non-solvent additive, the amount of benzene added 60 In the case of Comparative Example 4, which is% by weight, it can be seen that the thickness of the surface dense layer is increased by about three times or more. In addition, it can be seen that in the case of the polymer membrane prepared by dipping in distilled water in Comparative Example 5, a large pore structure was formed. This is because the solidification of the surface of the film forming solution was accelerated as the phase inversion rapidly occurred. On the other hand, the polysulfone separator prepared in Examples 1 to 8 can be seen that the thickness of the surface dense layer decreases as the content of cyclohexane or carbon tetrachloride, which is a non-solvent additive, increases, and the content of carbon tetrachloride is 20% by weight. In the case of the added Example 8, it was found that the surface dense layer almost disappeared. Through this, it was confirmed that the thickness of the surface dense layer can be adjusted as the non-solvent additive is added, and the pore structure of the porous layer inside the separator is obtained by preparing a polysulfone separator by dipping in a non-solvent such as isopropyl alcohol, not distilled water. It can be seen that it is formed densely (Fig. 1 (a): Comparative Example 1, (b): Comparative Example 2, (c): Comparative Example 3, (d): Comparative Example 4; Figure 3 (a) Example 1, (b) Example 2, (c) Example 3, (d) Example 4 Figure 4 (a) Example 5, (b) Example 6, (c ): Example 7, (d): Example 8).

<실시예 2> 막 투과율 측정Example 2 Membrane Permeability Measurement

본 발명에 따른 실시예 1 내지 8에 따라 제조된 폴리설폰 분리막을 막 투과율을 도 5에 나타낸 장치 및 33.17 cm2의 면적인 디스크 타입의 모듈을 사용하였으며, 이때의 조작압력은 3 kgf/cm2 이었고, 20 리터의 순수한 물을 펌프를 통해 모듈에 공급하여 투과율을 측정하였다. 상기 측정의 결과는 도 6 및 도 7에 나타내었다.In the polysulfone separator prepared according to Examples 1 to 8 according to the present invention, the membrane permeability of the apparatus shown in FIG. 5 and a 33.17 cm 2 area disk type module were used, and the operating pressure was 3 kgf / cm 2. 20 liters of pure water was supplied to the module via a pump to measure the transmittance. The results of the measurements are shown in FIGS. 6 and 7.

도 6 및 도 7에 나타낸 바와 같이, 비용매 첨가제인 싸이클로헥산 또는 사염화탄소의 함량이 증가함에 따라, 순수한 물의 투과율이 증가하는 것을 알 수 있다. 이는 비용매 첨가제가 첨가됨에 따라 제조된 분리막의 표면의 치밀층의 두께가 감소하여 투과저항이 감소하기 때문으로, 본 발명에 따른 상전환법을 이용한 폴리설폰 분리막의 제조방법으로 투과율이 향상된 폴리설폰 분리막을 제조할 수 있음을 확인하였다.As shown in Figure 6 and 7, it can be seen that as the content of cyclohexane or carbon tetrachloride, which is a non-solvent additive, increases, the transmittance of pure water increases. This is because the thickness of the dense layer on the surface of the prepared membrane decreases as the non-solvent additive is added, thereby reducing the permeation resistance. Thus, the polysulfone having improved transmittance with the polysulfone separator using the phase shift method according to the present invention. It was confirmed that the separator can be prepared.

Claims (10)

폴리설폰을 용매 및 비용매 첨가제와 혼합하여 제막용액을 제조하는 단계(단계 1);
상기 단계 1에서 제조된 제막용액을 기판 상부로 도포하여 막을 형성시키는 단계(단계 2); 및
상기 단계 2에서 제조된 막을 비용매가 채워진 침지조에 침지하여 고형화시키는 단계(단계 3)를 포함하는 것을 특징으로 하는 상전환법을 이용한 폴리설폰 분리막의 제조방법.
Preparing a film forming solution by mixing polysulfone with a solvent and a nonsolvent additive (step 1);
Coating the film forming solution prepared in step 1 on the substrate to form a film (step 2); And
Method of producing a polysulfone separation membrane using a phase inversion method comprising the step of immersing the membrane prepared in step 2 in a non-solvent-filled immersion tank (step 3).
제1항에 있어서, 상기 단계 1의 용매는 n-메틸 피롤리돈(n-methyl pyrrolidone), 디메틸아세트아마이드(dimethylacetamide) 또는 디메틸포름아마이드(dimethylformamide)인 것을 특징으로 하는 상전환법을 이용한 폴리설폰 분리막의 제조방법.
The polysulfone of claim 1, wherein the solvent of step 1 is n-methyl pyrrolidone, dimethylacetamide or dimethylformamide. Method for producing a separator.
제1항에 있어서, 상기 단계 1의 비용매 첨가제는 사염화탄소 또는 싸이클로헥산인 것을 특징으로 하는 상전환법을 이용한 폴리설폰 분리막의 제조방법.
The method of claim 1, wherein the nonsolvent additive of step 1 is carbon tetrachloride or cyclohexane.
제1항에 있어서, 상기 단계 1의 폴리설폰은 10 내지 20 중량%로 혼합되는 것을 특징으로 하는 상전환법을 이용한 폴리설폰 분리막의 제조방법.
The method of claim 1, wherein the polysulfone of step 1 is mixed at 10 to 20% by weight.
제1항에 있어서, 상기 단계 1의 비용매 첨가제는 1 내지 20 중량%로 혼합되는 것을 특징으로 하는 상전환법을 이용한 폴리설폰 분리막의 제조방법.
The method of claim 1, wherein the non-solvent additive of step 1 is mixed at 1 to 20% by weight.
제1항에 있어서, 상기 단계 2의 기판은 유리판인 것을 특징으로 하는 상전환법을 이용한 폴리설폰 분리막의 제조방법.
The method of claim 1, wherein the substrate of step 2 is a glass plate.
제1항에 있어서, 상기 단계 3의 비용매는 이소프로필알코올, 에틸알코올 또는 메틸알코올인 것을 특징으로 하는 상전환법을 이용한 폴리설폰 분리막의 제조방법.
The method of claim 1, wherein the non-solvent of step 3 is isopropyl alcohol, ethyl alcohol or methyl alcohol.
제1항에 있어서, 상기 단계 3에서 제조된 분리막을 증류수가 채워진 침지조에 1 내지 2회 재침지하는 단계를 더 포함하는 것을 특징으로 하는 상전환법을 이용한 폴리설폰 분리막의 제조방법.
The method of claim 1, further comprising re-immersing the separator prepared in step 3 in a dipping water-filled dipping tank once or twice.
폴리설폰을 용매 및 비용매 첨가제와 혼합하여 제막용액을 제조하고, 상기 제조된 제막용액을 유리판 상부로 도포하여 막을 형성시킨 후 비용매가 채워진 침지조에 침지하여 제조되는 폴리설폰 분리막.
A polysulfone separator prepared by mixing polysulfone with a solvent and a nonsolvent additive to prepare a film forming solution, and applying the prepared film forming solution to an upper portion of a glass plate to form a film, and then immersing it in a non-solvent-filled dipping tank.
제9항에 있어서, 상기 폴리설폰 분리막은 액체폐기물 처리용 분리막인 것을 특징으로 하는 폴리설폰 분리막.The polysulfone separator according to claim 9, wherein the polysulfone separator is a liquid waste treatment separator.
KR1020100136703A 2010-12-28 2010-12-28 Preparing method of polysulfone membrane using phase inversion KR101285870B1 (en)