KR20120036574A - Method and structure for complex sheet waterproof using insulation non-woven fabric - Google Patents
Method and structure for complex sheet waterproof using insulation non-woven fabric Download PDFInfo
- Publication number
- KR20120036574A KR20120036574A KR1020100098325A KR20100098325A KR20120036574A KR 20120036574 A KR20120036574 A KR 20120036574A KR 1020100098325 A KR1020100098325 A KR 1020100098325A KR 20100098325 A KR20100098325 A KR 20100098325A KR 20120036574 A KR20120036574 A KR 20120036574A
- Authority
- KR
- South Korea
- Prior art keywords
- layer
- waterproofing
- glass fiber
- coating
- nonwoven fabric
- Prior art date
Abstract
본 발명은 저탄소 녹색성장을 지향하는 국가 정책에 맞추어진 것으로서, 특히 건축물 등 시공 면에 대한 한 번의 시공을 통해 방수 기능과 단열 기능을 모두 확보할 수 있고, 이를 통해 공기 단축 및 시공 비용의 절감을 가져오며, 복합시트 구조체의 내구성이 우수하므로 시공 후 열이나 충격 등 외부 조건에 의한 변형 및 훼손이 잘 방지될 수 있는 단열부직포를 이용한 복합시트 구조체 및 그를 이용한 복합시트 방수 공법에 관한 것으로서, 본 발명의 단열부직포를 이용한 복합시트 구조체는, 단열 기능을 하는 부직포 시트층과, 상기 부직포 시트층에 코팅되며, 주방수 기능 및 접착 기능을 하는 무기도막 방수제층과, 상기 무기도막 방수제층에 그 일면이 접착되어 적층되는 글라스 화이버층(glass fiber)과, 상기 글라스 화이버층(glass fiber)에 코팅되며, 방수 기능을 하는 무용제 우레탄 방수제층과, 상기 무용제 우레탄 방수제층에 코팅되는 아크릴수지 코팅제층을 포함하는 것을 특징으로 한다.The present invention is tailored to the national policy aiming at low carbon green growth, and in particular, it is possible to secure both waterproof and insulation functions through a single construction on a construction surface such as a building, thereby reducing air and reducing construction costs. The present invention relates to a composite sheet structure using an insulating non-woven fabric and a composite sheet waterproofing method using the same, which are excellent in durability of the composite sheet structure and thus prevent deformation and damage caused by external conditions such as heat or impact after construction. The composite sheet structure using the insulating nonwoven fabric of the nonwoven fabric sheet layer having a heat insulating function, the nonwoven fabric sheet layer is coated on the nonwoven fabric sheet layer, the inorganic coating waterproofing layer having a kitchen water function and adhesive function, and the inorganic coating waterproofing layer on one side thereof It is coated on the glass fiber layer (glass fiber) and the glass fiber layer (glass fiber) to be bonded and laminated, It is characterized in that it comprises a solvent-free urethane waterproofing layer having a water function, and an acrylic resin coating layer coated on the solvent-free urethane waterproofing layer.
Description
본 발명은 저탄소 녹색성장을 지향하는 국가 정책에 맞추어진 것으로서 옥상에 방수기능 뿐 아니라 단열기능까지 포함한 방수시트를 시공함으로 도시 열섬화를 완화하고 냉난방비 절감을 통해서 이산화탄소(CO2)발생을 줄여주게 하는 기능을 가진 단열부직포를 이용한 복합시트 구조체 및 그를 이용한 복합시트 방수 공법에 관한 것이다.The present invention is tailored to the national policy aimed at low carbon green growth, by installing a waterproof sheet on the roof as well as a heat-insulating function to alleviate urban heat island and reduce carbon dioxide (CO 2 ) generation by reducing heating and cooling costs The present invention relates to a composite sheet structure using an insulating nonwoven fabric having a function, and a composite sheet waterproofing method using the same.
또한, 본 발명은 특히 건축물 등 시공 면에 한 번의 시공으로 방수 기능과 단열 기능을 모두 확보할 수 있고, 이를 통해 공기 단축 및 시공 비용의 절감을 가져오며, 복합시트 구조체의 내구성이 우수하므로 시공 후 열이나 충격 등 외부 조건에 의한 변형 및 훼손이 잘 방지될 수 있는 단열부직포를 이용한 복합시트 구조체 및 그를 이용한 복합시트 방수 공법에 관한 것이다.
In addition, the present invention can ensure both waterproof and insulation functions in one construction, especially in the construction surface such as buildings, thereby reducing the air and reducing the construction cost, and excellent durability of the composite sheet structure after construction The present invention relates to a composite sheet structure using an insulating nonwoven fabric which can be easily prevented from being deformed or damaged by external conditions such as heat or impact, and a composite sheet waterproofing method using the same.
건축물의 방수를 위한 시공 방법으로서, 다양한 방수제를 방수 시공 면에 도포하는 방수 공법이 널리 사용되고 있다.As a construction method for waterproofing a building, a waterproofing method of applying various waterproofing agents to the waterproofing construction surface is widely used.
하지만, 이러한 종래의 방수 공법은 통상 방수 기능을 제공하는 것에 치중되어 있으며, 단열성을 확보하기위해서는 단열 시공을 한 후에 방수 시공을 하여야 한다.However, such a conventional waterproof method is usually focused on providing a waterproof function, in order to ensure the insulation, the waterproof construction should be performed after the insulation.
결과적으로 종래에는 방수와 단열을 위해 2중의 시공이 필요하고, 이에 따라 별도의 방수 시공과 단열 시공에 의해 공기가 길어지는 동시에 시공 비용도 증가하게 된다. 또한 아무리 기본적인 단열시공을 잘 했다 하더라도 완전한 단열을 보장할 수 없어서 겨울철 혹한이나 여름철의 뜨거운 태양열이 실내로 들어오는 것을 온전히 차단할 수 없다.As a result, in the related art, double construction is required for waterproofing and thermal insulation, and accordingly, the air is lengthened by separate waterproof construction and insulation construction, and the construction cost also increases. In addition, no matter how good the basic insulation is done, it is impossible to guarantee complete insulation, so it is not possible to completely block the heat from the cold of winter or the heat of summer.
다시 말해, 옥상에 방수효과 뿐 아니라 단열효과도 주기 때문에 냉난방비를 절감해주고 이로 인하여 공기 중으로 배출되는 이산화탄소의 양을 줄이는데 기여할 수 있는 방수 공법이 요구된다.
In other words, the waterproofing method is required to reduce the cooling and heating costs and contribute to reducing the amount of carbon dioxide emitted into the air because it gives not only a waterproof effect on the roof but also an insulation effect.
따라서, 본 발명은 한 번의 시공을 통해 방수 기능과 단열 기능을 모두 확보할 수 있도록 하는 단열부직포를 이용한 복합시트 구조체를 제공하는 것을 목적으로 한다.Therefore, an object of the present invention is to provide a composite sheet structure using a non-insulating non-woven fabric to ensure both waterproof and heat insulating function through a single construction.
또한, 본 발명은 방수 시공과 단열 시공을 한 번의 시공으로 동시에 할 수 있어 공기 단축 및 시공 비용의 절감을 가져오는 단열부직포를 이용한 복합시트 구조체를 제공하는 것을 목적으로 한다.In addition, it is an object of the present invention to provide a composite sheet structure using a non-insulating nonwoven fabric that can be carried out at the same time in a single construction of waterproof construction and thermal insulation construction.
또한, 본 발명은 내구성이 우수하여 열이나 충격 등 외부 조건에 의한 변형 및 훼손이 잘 방지될 수 있는 단열부직포를 이용한 복합시트 구조체를 제공하는 것을 목적으로 한다.In addition, an object of the present invention is to provide a composite sheet structure using a non-insulating nonwoven fabric that is excellent in durability and can be well prevented deformation and damage caused by external conditions such as heat or impact.
또한, 본 발명은 단열부직포를 이용한 복합시트 구조체에 의해 한 번의 시공을 통해 방수 시공과 단열 시공을 동시에 진행할 수 있는 복합시트 구조체를 이용한 방수 공법을 제공하는 것을 목적으로 한다.
In addition, an object of the present invention is to provide a waterproofing method using a composite sheet structure that can be carried out at the same time through a single construction by a composite sheet structure using a non-insulating nonwoven fabric.
상기 목적을 달성하기 위하여, 본 발명에 따른 단열부직포를 이용한 복합시트 구조체는, 단열 기능을 하는 부직포 시트층과, 상기 부직포 시트층에 코팅되는 주방수 및 접착 기능을 하는 무기도막 방수제층과, 상기 무기도막 방수제층에 그 일면이 접착되어 적층되는 글라스 화이버(glass fiber)층과, 상기 글라스 화이버층에 코팅되며, 방수 기능, 외관 색상 제공 기능 그리고 광택기능을 하는 무용제 우레탄 방수제층과, 상기 무용제 우레탄 방수제층의 광택을 보호하고, 변색을 방지하며, 스크래치를 방지하여 보호기능을 하는 아크릴 코팅제층을 포함하는 것을 특징으로 한다.In order to achieve the above object, the composite sheet structure using a non-insulating nonwoven fabric according to the present invention, the non-woven fabric sheet layer having a heat insulating function, the inorganic coating waterproofing layer having a kitchen water and an adhesive function coated on the non-woven fabric sheet layer, A glass fiber layer laminated on one side of the inorganic coating waterproofing layer by laminating, and a solvent-free urethane waterproofing layer coated on the glass fiber layer, providing a waterproof function, an appearance color function, and a gloss function, and the solventless urethane. It is characterized in that it comprises an acrylic coating layer to protect the gloss of the waterproofing agent layer, to prevent discoloration, and to prevent scratching.
또한, 상기 부직포 시트층은, 면 30~40%, 셀룰로즈 30~40%, 폴리에스터 20~30%를 포함하는 부직포로 형성되고, 상기 부직포의 열전도율이 0.034Kcal/mh℃이며, 6㎜이상의 두께로 형성되는 것을 특징으로 한다.In addition, the nonwoven fabric sheet layer is formed of a nonwoven fabric containing 30 to 40% cotton, 30 to 40% cellulose, 20 to 30% polyester, the thermal conductivity of the nonwoven fabric is 0.034 Kcal / mh ℃, thickness of 6 mm or more Characterized in that formed.
또한, 상기 무기도막 방수제층은 수용성 아크릴에멀젼수지(물성:유리전이온도(Tg) -10±3℃, 고형분 40%, 점도2500±500cps) 30~35%, 포틀랜트 시멘트 15~25%, 규사6호사 30~40%, 규산 알루미늄(Alumino silicate)이 주성분인 미세진공 세라믹 분말로 열전도율 0.0560Kcal/m.h.℃이고 입자 사이즈가 20~300㎛인 기능성 진공 Micro 세라믹 첨가제 2~8%, 유동화제 0.3~1%, 물 10~15% 을 포함하는 무기도막 방수제로 형성되며, 상기 무기도막 방수제의 도포량이 1300~1500g/㎡인 것을 특징으로 한다.In addition, the inorganic coating waterproof layer is a water-soluble acrylic emulsion resin (property: glass transition temperature (Tg) -10 ± 3 ℃, solid content 40%, viscosity 2500 ± 500cps) 30-35%, Portland cement 15-25%, silica sand 30 ~ 40% of yarn No. 6, micro silica ceramic powder composed mainly of aluminum silicate, 2 ~ 8% functional vacuum micro ceramic additive with a thermal conductivity of 0.0560 Kcal / mh ℃ and particle size of 20 ~ 300㎛, fluidizing agent 0.3 ~ It is formed of an inorganic coating waterproofing agent containing 1% and water 10-15%, characterized in that the coating amount of the inorganic coating waterproofing agent is 1300 ~ 1500g / ㎡.
또한, 상기 글라스 화이버층은, 글라스 로빙(glass roving)을 제직하여 형성된 유리섬유 직물시트로 형성되며, 상기 유리섬유 직물시트의 무게가 300± 20g/㎡인 것을 특징으로 한다.In addition, the glass fiber layer is formed of a glass fiber fabric sheet formed by weaving glass roving (glass roving), characterized in that the weight of the glass fiber fabric sheet is 300 ± 20g / ㎡.
또한, 상기 무용제 우레탄 방수제층은, 주제와 경화제로 이루어지는 2액형으로 형성되며, 상기 주제는 폴리에테르-폴리에스테르 폴리올(branched polyether-polyester polyol)35~40%, 필러 중탄산칼륨 30~50%, 색소 3~10%, 소포제0.1~0.5%, 자외선 차단제 0.1~0.3%, 경화제 4.4, 디페닐 메탄 디이소시아네이트(MDI) 15~20%를 포함하여 형성되고, 도포량이 500~800g/㎡인 것을 특징으로 한다.In addition, the solvent-free urethane waterproofing layer is formed in a two-component type consisting of a main material and a curing agent, the main material is 35-40% of a branched polyether-polyester polyol, 30-50% filler potassium bicarbonate, pigment 3 to 10%, antifoaming agent 0.1 to 0.5%, sunscreen 0.1 to 0.3%, curing agent 4.4, diphenyl methane diisocyanate (MDI) is formed including 15 to 20%, characterized in that the coating amount is 500 ~ 800g / ㎡ do.
또한, 상기 아크릴 코팅제층은, 용제형 아크릴수지 유리전이온도(Tg)가 56±5℃인 제품과 유리전이온도(Tg)가 1±3℃인 제품을 (3:7)혼합하여 여기에 자외선 차단제 티뉴빈(Tinubin) 296 0.1~0.3%을 배합한다. 용제형 아크릴 코팅제의 도포량이 80~100g/㎡인 것을 특징으로 한다.In addition, the acrylic coating layer, (3: 7) by mixing the product of the solvent-type acrylic resin glass transition temperature (Tg) of 56 ± 5 ℃ and the product of glass transition temperature (Tg) of 1 ± 3 ℃ (3: 7) Combine 0.1 to 0.3% of the blocking agent Tinubin 296. The coating amount of the solvent-type acrylic coating is characterized in that 80 ~ 100g / ㎡.
또한, 본 발명에 따른 복합시트 방수 공법은, 바탕면에 단열 기능의 부직포 시트층을 적층하는 단계와, 상기 부직포 시트층에 주방수 및 접착 기능의 무기도막 방수제층이 코팅되는 단계와, 상기 무기도막 방수제층에 글라스 화이버층의 일면이 접착되어 상기 무기도막 방수제층의 상기 글라스 화이버층이 적층되는 단계와, 상기 글라스 화이버층 위에 방수, 외관의 색상, 광택 기능의 무용제 우레탄 방수제층이 코팅되는 단계와, 상기 무용제 우레탄 방수제층 위에 광택 보호, 변색 및 스크래치 방지를 통한 보호용의 아크릴수지 코팅제층이 코팅되는 단계를 포함하는 것을 특징으로 한다.In addition, the composite sheet waterproofing method according to the present invention, the step of laminating a non-woven fabric sheet layer having a thermal insulation function on the base surface, the step of coating the inorganic coating waterproof layer of the kitchen water and adhesive function on the non-woven fabric sheet layer, the inorganic One surface of the glass fiber layer is bonded to the coating film waterproofing layer so that the glass fiber layer of the inorganic coating waterproofing layer is laminated, and the solvent-free urethane waterproofing layer of waterproof, appearance color, gloss function is coated on the glass fiber layer. And, it characterized in that it comprises a step of coating the acrylic resin coating layer for protection through the gloss protection, discoloration and scratch prevention on the solvent-free urethane waterproofing layer.
또한, 상기 부직포 시트층은 6㎜이상의 두께로서 상기 바탕층이 적층되는 것을 특징으로 한다.In addition, the nonwoven fabric sheet layer is characterized in that the base layer is laminated with a thickness of 6mm or more.
또한, 상기 무기도막 방수제층의 상기 부직포 시트층에 대한 적층은 무기도막 방수제를 1300~1500g/㎡로 도포하여 이루어지고, 상기 글라스 화이버층의 상기 무기도막 방수제층에 대한 적층은 유리섬유 직물시트를 무게 300± 20g/㎡로 적층하여 이루어지며, 상기 무용제 우레탄 방수제층의 상기 글라스 화이버층에 대한 적층은 무용제 우레탄 방수제를 500~800g/㎡로 도포하여 이루어지고, 상기 아크릴수지 코팅제층의 상기 무용제 우레탄 방수제층에 대한 적층은 용제형 아크릴수지 코팅제를 80~100g/㎡로 도포하여 이루어지는 것을 특징으로 한다.
In addition, lamination of the inorganic coating waterproof layer of the nonwoven fabric sheet layer is made by applying an inorganic coating waterproofing agent of 1300 ~ 1500g / ㎡, lamination of the inorganic film waterproofing layer of the glass fiber layer is a glass fiber fabric sheet It is made by laminating at a weight of 300 ± 20g / ㎡, lamination of the solvent-free urethane waterproofing layer to the glass fiber layer is made by applying a solvent-free urethane waterproofing agent to 500 ~ 800g / ㎡, the solvent-free urethane of the acrylic resin coating layer Lamination to the waterproofing agent layer is characterized in that it is made by applying a solvent type acrylic resin coating agent at 80 ~ 100g / ㎡.
본 발명에 따르면, 건축물 등 시공 면에 대한 한 번의 시공을 통해 방수 기능과 단열 기능을 모두 확보할 수 있게 된다.According to the present invention, it is possible to secure both the waterproof function and the thermal insulation function through a single construction for the construction surface such as a building.
또한, 건축물 등 시공 면에 대한 방수 시공과 단열 시공을 한 번의 시공으로 동시에 할 수 있으므로, 공기 단축 및 시공 비용의 절감을 가져오게 된다.In addition, the waterproof construction and insulation construction on the construction surface, such as buildings can be performed at the same time in a single construction, resulting in shortening the air and reducing the construction cost.
또한, 건축물 등 시공 면에 시공된 복합시트 구조체가 내구성이 우수하므로, 열이나 충격 등 외부 조건에 의한 변형 및 훼손이 잘 방지될 수 있다.In addition, since the composite sheet structure constructed on the construction surface such as buildings is excellent in durability, deformation and damage due to external conditions such as heat or impact can be well prevented.
또한, 본 발명은 단열부직포를 이용한 복합시트 구조체에 의해 한 번의 시공을 통해 방수 시공과 단열 시공을 동시에 진행할 수 있는 복합시트 구조체를 이용한 방수 공법이 제공된다.
In addition, the present invention provides a waterproof method using a composite sheet structure capable of simultaneously performing waterproof construction and insulation construction through a single construction by the composite sheet structure using a non-insulating nonwoven fabric.
도 1은 본 발명의 일 실시예에 따른 단열부직포를 이용한 복합시트 구조체의 구성을 예시한 도면
도 2는 본 발명의 일 실시예에 따른 단열부직포를 이용한 복합시트 구조체의 시험 성적서를 보인 도면
도 3은 본 발명의 일 실시예에 따른 복합시트 방수 공법의 시공 과정을 보인 흐름도1 is a view illustrating a configuration of a composite sheet structure using a non-insulating nonwoven fabric according to an embodiment of the present invention
Figure 2 is a view showing a test report of a composite sheet structure using a non-insulating nonwoven fabric according to an embodiment of the present invention
Figure 3 is a flow chart showing the construction process of the composite sheet waterproofing method according to an embodiment of the present invention
이하에서는 도면을 참조하여 본 발명의 일 실시예를 통해 본 발명을 더욱 상세하게 설명한다.Hereinafter, the present invention will be described in more detail with reference to the accompanying drawings.
도 1은 본 발명의 일 실시예에 따른 단열부직포를 이용한 복합시트 구조체의 구성을 예시한 도면이다.1 is a view illustrating a configuration of a composite sheet structure using a non-insulating nonwoven fabric according to an embodiment of the present invention.
도시된 바와 같이, 본 발명의 일 실시예에 따른 단열부직포를 이용한 복합시트 구조체(100 : 이하 복합시트 구조체라 약칭 함)는, 부직포 시트층(110), 무기도막 방수제층(120), 글라스 화이버층(130), 무용제 우레탄 방수제층(140), 아크릴수지 코팅제층(150)을 포함하여 형성된다. 즉, 복합시트 구조체(100)는 부직포 시트층(110)을 시작으로 무기도막 방수제층(120), 글라스 화이버층(130), 무용제 우레탄 방수제층(140), 아크릴수지 코팅제층(150)이 순차적으로 적층되는 형태이다.As shown, the composite sheet structure (100: hereinafter referred to as composite sheet structure) using a heat insulating non-woven fabric according to an embodiment of the present invention, the nonwoven
부직포 시트층(110)은 복합시트 구조체(100)가 단열성을 갖게 하는 기능을 하며, 무기도막 방수제층(120)은 복합시트 구조체(100)의 주방수층으로 작용한다. 그리고, 글라스 화이버(glass fiber)층(130)은 복합시트 구조체(100)의 강도 보강을 통해 변형을 방지하는 기능을 한다. 또한, 무용제 우레탄 방수제층(140)은 방수 기능 및 복합시트 구조체(100)의 외관을 미려하게 하는 기능을 하며, 아크릴수지 코팅제층(150)은 복합시트 구조체(100)의 자외선 차단(변색), 광택, 스크래치로 부터 보호하는 기능을 한다.The
다음은 복합시트 구조체(100)를 형성하는 각 층에 대해 더 구체적으로 설명한다.Next, each layer forming the
부직포 시트층(110)은 복합시트 구조체(100)에 단열성을 부여하며, 이에 따라 복합시트 구조체(100)는 단열 기능을 갖는다. 또한, 부직포 시트층(110)은 무기도막 방수제에 의한 무기도막 방수제층(120)의 중심 기재 역할을 한다. 그리고, 이러한 부직포 시트층(110)은, 면 30~40%, 셀룰로즈 30~40%, 폴리에스터 20~30%를 포함하는 부직포로 형성되고, 부직포의 열전도율이 0.034Kcal/m.h.℃이다. 또한, 부직포 시트층(110)은 6㎜이상의 두께로 형성되는 것으로서, 이러한 부직포 시트층(110)의 두께는 복합시트 구조체(100)에 양호한 단열성을 부여할 수 있는 동시에 무기도막 방수제의 중심 기재 역할을 하기에 충분한 두께에 해당된다.The
무기도막 방수제층(120)은 부직포 시트층(110)의 일면에 무기도막 방수제를 도포하여 형성되며, 이러한 무기도막 방수제층(120)은 복합시트 구조체(100)의 주방수층을 형성하고, 접착력을 가져 글라스 화이버(glass fiber)층(130)을 그 일면에 접착시키는 기능을 한다. 그리고, 무기도막 방수제층(120)을 형성하는 무기도막 방수제는, 수용성 아크릴에멀젼수지(물성:유리전이온도(Tg) -10± 3℃, 고형분 40%, 점도2500±500cps) 30~35%, 포틀랜트 시멘트 15~25%, 규사6호사 30~40%, 규산 알루미늄(Alumino silicate)이 주성분인 미세진공 세라믹 분말로 열전도율 0.0560Kcal/m.h.℃이고 입자 사이즈가 20~300㎛인 기능성 진공 Micro 세라믹 첨가제 2~8%, 유동화제 0.3~1%, 물 10~15% 를 포함하여 형성된다. 여기서, 무기도막 방수제의 조성물질 및 그 혼합비율은 복합시트 구조체(100)가 유연성을 갖는 조건에 충족되는 수치들이다. 그리고, 무기도막 방수제층(120)은 무기도막 방수제의 도포량이 1300~1500g/㎡이다.The inorganic
글라스 화이버층(130)은 글라스 로빙(glass roving)을 제직하여 형성된 비교적 두꺼운 유리섬유 직물시트를 무기도막 방수제층(120)의 일면에 무기도막 방수제의 접착력을 통해 접착하여 형성된다. 이에 따라 글라스 화이버층(130)은 복합시트 구조체(100)의 강도 보강 및 변형 방지 기능을 한다. 그리고, 글라스 화이버층(130)은 유리섬유 직물시트의 무게가 300± 20g/㎡이다.The
무용제 우레탄 방수제층(140)은 복합시트 구조체(100)의 방수 기능 및 색상, 광택 등 외관 기능을 제공한다. Solvent-free urethane
이러한 무용제 우레탄 방수제층(140)은 글라스 화이버층(130)의 일면에 무용제 우레탄 방수제를 도포하여 형성되며, 무용제 우레탄 방수제는 주제와 경화제로 이루어지는 2액형으로 형성된다. 여기서, 주제는 폴리에테르-폴리에스테르 폴리올 (branched polyether-polyester polyol)35~40%, 중탄산칼륨 30~50%, 색소 3~10% 소포제 0.1~0.5%, 자외선 차단제 0.1~0.3%, 경화제 4.4, 디페닐 메탄 디이소시아네이트(MDI) 15~20%를 포함하여 형성된다. 그리고, 무용제 우레탄 방수제층(140)은 무용제 우레탄 도포량이 500~800g/㎡이다.The solvent-free
아크릴수지 코팅제층(150)은 무용제 우레탄 방수제층(140)의 일면에 용제형 아크릴수지 코팅제를 도포하여 형성되며, 이러한 아크릴수지 코팅제층(140)은 자외선 차단을 통한 변색 방지 기능, 광택을 제공하는 기능, 스크래치 등 훼손 방지를 통한 보호 기능을 한다. 그리고, 아크릴수지 코팅제층(150)은 용제형 아크릴수지 유리전이온도(Tg)가 56±5℃인 제품과 유리전이온도(Tg)가 1± 3℃인 제품을 (3:7)혼합하여 여기에 자외선 차단제 티뉴빈(Tinubin) 296 0.1~0.3%을 배합한다.The acrylic
또한, 아크릴수지 코팅제층은 용제형 아크릴수지 코팅제의 도포량이 80~100g/㎡이다.
In addition, the coating amount of the solvent type acrylic resin coating agent is 80-100 g / m <2> in an acrylic resin coating layer.
도 2는 본 발명의 일 실시 예에 따른 단열부직포를 이용한 복합시트 구조체의 시험 성적서를 보인 도면이다. 2 is a view showing a test report of a composite sheet structure using a non-insulating nonwoven fabric according to an embodiment of the present invention.
도 2는 복합시트 구조체(100)의 물성을 인장 강도와 신장률로 나타내고 있으며, 샘플A부터 샘플D까지 서로 다른 구조의 방수시트의 물성을 비교한 것이다. 여기서, 시험방법은 KS F4917 기준 이다.FIG. 2 shows the properties of the
여기서, 샘플 A는 단열 부직포 원단이고, 샘플 B는 단열 부직포에 무기도막 방수제를 도포한 형태이며, 그리고 샘플 C는 단열 부직포에 무기도막 방수제 및 무용제 우레탄 방수제층을 차례로 적층한 형태이다. 또한, 샘플 D는 부직포 시트층, 무기도막 방수제층, 글라스 화이버층, 무용제 우레탄 방수제층, 아크릴 수지 코팅제층으로 구성된 본 발명의 일 실시 예에 따른 복합시트 구조체이다.Here, Sample A is an insulating nonwoven fabric, Sample B is a form in which an inorganic coating waterproofing agent is applied to the insulating nonwoven fabric, and Sample C is a form in which an inorganic coating waterproofing agent and a solventless urethane waterproofing layer are sequentially laminated on the insulating nonwoven fabric. In addition, Sample D is a composite sheet structure according to an embodiment of the present invention composed of a nonwoven fabric sheet layer, an inorganic coating waterproof layer, a glass fiber layer, a solvent-free urethane waterproof layer, an acrylic resin coating layer.
시험 결과치를 보면, 본 발명의 일 실시예에 따른 복합시트 구조체(100)는 그 인장강도가 78.7(N/㎜2)이고 신장율이 9%이다.According to the test results, the
본 발명의 일 실시예에 따른 복합시트 구조체(100)는 방수 시트로 사용 가능한 충분하고도 우수한 인장성능을 구비하고 있음을 알 수 있다. It can be seen that the
따라서, 본 발명의 일 실시예에 따른 복합시트 구조체(100)에 의해서, 건축물 등 시공 면에 대한 복합시트 구조체(100)의 일 회 시공을 통해 방수 기능과 단열 기능을 모두 확보할 수 있다.Therefore, by the
또한, 이를 통해 방수 시공 및 이에 더하여 단열 시공에 필요한 공기의 단축 및 시공 비용의 절감이 가능하다.In addition, it is possible to shorten the air required for waterproof construction and in addition to the insulation construction and to reduce the construction cost.
또한, 건축물 등 시공 면에 시공된 복합시트 구조체(100)가 인장강도와 신장률을 포함한 내구성이 우수하므로, 열이나 충격 등 외부 조건에 의한 변형 및 훼손이 잘 방지될 수 있다
In addition, since the
도 3은 본 발명의 일 실시예에 따른 복합시트 방수 공법의 시공 과정을 보인 흐름도이다.Figure 3 is a flow chart showing the construction process of the composite sheet waterproofing method according to an embodiment of the present invention.
도시된 바와 같이, 복합시트 방수 공법은, 먼저, 바탕면(160) 상에 단열 기능의 부직포 시트층(110)을 적층한다. 이때, 부직포 시트층(110)은 6㎜이상의 두께로 적층된다.As shown, the composite sheet waterproofing method, first, laminating the
다음으로, 부직포 시트층(110)의 일면에 무기도막 방수제가 코팅되어 무기도막 방수제층(120)이 적층된다. 여기서, 무기도막 방수제층(120)의 무기도막 방수제 도포량은 1300~1500g/㎡이다.Next, an inorganic coating waterproofing agent is coated on one surface of the nonwoven
다음으로, 무기도막 방수제층(120)의 일면에 글라스 화이버층(130)이 적층된다. 여기서, 글라스 화이버층(130)은 글라스 로빙(glass roving)을 제직하여 형성된 유리섬유 직물시트로 이루어지며, 이러한 유리섬유 직물시트가 무기도막 방수제의 접착력을 통해 접착되어 글라스 화이버층(130)을 형성한다. 여기서, 글라스 화이버층(130)을 형성하는 유리섬유 직물시트의 무게는 300± 20g/㎡이다.Next, the
다음으로, 글라스 화이버층(130)의 일면에 무용제 우레탄 방수제가 코팅되어 무용제 우레탄 방수제층(140)이 적층된다. 여기서, 무용제 우레탄 방수제층(140)을 형성하는 무용제 우레탄 방수제의 도포량은 500~800g/㎡이다.Next, a solvent-free urethane waterproofing agent is coated on one surface of the
마지막으로, 무용제 우레탄 방수제층(140)의 일면에 아크릴 코팅제층(150)이 적층되는 것으로서, 아크릴 코팅제층(150)은 무용제 우레탄 방수제층(140)의 일면에 용제형 아크릴 코팅제를 코팅하여 형성된다. 여기서, 아크릴 코팅제층(150)을 형성하는 용제형 아크릴 코팅제의 도포량은 80~100g/㎡이다.
Finally, as the
이상에서 설명한 것은 본 발명에 따른 단열부직포를 이용한 복합시트 구조체 및 그를 이용한 복합시트 방수 공법을 실시하기 위한 하나의 실시예에 불과한 것으로서, 본 발명은 상기한 실시 예에 한정되지 않고, 이하의 특허청구범위에서 청구하는 바와 같이 본 발명의 요지를 벗어남이 없이 당해 발명이 속하는 분야에서 통상의 지식을 가진 자라면 누구든지 다양한 변경 실시가 가능한 범위까지 본 발명의 기술적 정신이 있다고 할 것이다.What has been described above is just one embodiment for carrying out the composite sheet structure and the composite sheet waterproofing method using the insulating nonwoven fabric according to the present invention, the present invention is not limited to the above embodiment, the following claims As claimed in the scope of the present invention, those skilled in the art to which the present invention pertains will have the technical spirit of the present invention to the extent that various modifications can be made.
100 : 복합시트 구조체 110 : 부직포 시트층
120 : 무기도막 방수체층 130 : 글라스 화이버층
140 : 무용제 우레탄 방수제층 150 : 아크릴수지 코팅제층
160 : 바탕층100: composite sheet structure 110: non-woven sheet layer
120: inorganic coating waterproof layer 130: glass fiber layer
140: solvent-free urethane waterproofing layer 150: acrylic resin coating layer
160: ground floor
Claims (9)
상기 부직포 시트층에 코팅되며, 주방수 기능 및 접착 기능을 하는 무기도막 방수제층;
상기 무기도막 방수제층에 그 일면이 접착되어 적층되는 글라스 화이버(glass fiber)층;
상기 글라스 화이버(glass fiber)층에 코팅되며, 방수 기능을 하는 무용제 우레탄 방수제층;
상기 무용제 우레탄 방수제층에 코팅되는 아크릴수지 코팅제층을 포함하는 것을 특징으로 하는 단열부직포를 이용한 복합시트 구조체.Nonwoven sheet layer having a heat insulating function;
An inorganic coating waterproofing layer coated on the nonwoven fabric sheet layer and having a kitchen water function and an adhesive function;
A glass fiber layer having one surface bonded to the inorganic coating waterproofing layer and laminated;
A solvent-free urethane waterproof layer coated on the glass fiber layer and having a waterproof function;
Composite sheet structure using a non-insulating nonwoven fabric characterized in that it comprises an acrylic resin coating layer coated on the solvent-free urethane waterproofing layer.
면 30~40%, 셀룰로즈 30~40%, 폴리에스터 20~30%를 포함하는 부직포로 형성되고, 상기 부직포의 열전도율이 0.034Kcal/mh℃이며, 6㎜이상의 두께로 형성되는 것을 특징으로 하는 단열부직포를 이용한 복합시트 구조체.The method of claim 1, wherein the nonwoven sheet layer,
Insulation is formed of a nonwoven fabric containing 30 to 40% cotton, 30 to 40% cellulose, 20 to 30% polyester, the thermal conductivity of the nonwoven fabric is 0.034 Kcal / mh ℃, characterized in that formed to a thickness of 6 mm or more Composite sheet structure using nonwoven fabric.
수용성 아크릴에멀젼 (물성:유리전이온도(Tg) -10± 3℃, 고형분 40%, 점도2500± 500cps) 30~35%, 포틀랜트 시멘트 15~25%, 규사6호사 30~40%, 규산 알루미늄(Alumino silicate)이 주성분인 미세진공 세라믹 분말로 열전도율 0.0560Kcal/m.h.℃이고 입자 사이즈가 20~300㎛인 기능성 진공 Micro 세라믹 첨가제 2~8%, 유동화제 0.3~1%, 물 10~15% 를 포함하여 형성되며, 상기 무기도막 방수제의 도포량이 1300~1500g/㎡인 것을 특징으로 하는 단열부직포를 이용한 복합시트 구조체.The method of claim 1, wherein the inorganic coating waterproofing layer,
Water-soluble acrylic emulsion (property: glass transition temperature (Tg) -10 ± 3 ℃, solid content 40%, viscosity 2500 ± 500cps) 30 ~ 35%, Portland cement 15 ~ 25%, silica sand No. 6 30 ~ 40%, aluminum silicate (Alumino silicate) is a micro-vacuum ceramic powder containing 2 ~ 8% functional vacuum micro ceramic additive with a thermal conductivity of 0.0560Kcal / mh ℃ and a particle size of 20 ~ 300㎛, 0.3 ~ 1% of glidant, and 10 ~ 15% of water. It is formed, including, the composite sheet structure using an insulating nonwoven fabric, characterized in that the coating amount of the inorganic coating waterproofing agent is 1300 ~ 1500g / ㎡.
상기 글라스 화이버층은, 글라스 로빙(glass roving)을 제직하여 형성된 유리섬유 직물시트로 형성되며, 상기 유리섬유 직물시트의 무게가 300± 20g/㎡인 것을 특징으로 하는 단열부직포를 이용한 복합시트 구조체.The method of claim 1,
The glass fiber layer is formed of a glass fiber fabric sheet formed by weaving glass roving (glass roving), the composite sheet structure using an insulating nonwoven fabric, characterized in that the weight of the glass fiber fabric sheet is 300 ± 20g / ㎡.
주제와 경화제로 이루어지는 2액형으로 형성되며, 상기 주제는 폴리에테르-폴리에스테르 폴리올(branched polyether-polyester polyol)35~40%, 필러 중탄산칼륨 30~50%, 색소3~10%, 소포제0.1~0.5%, 자외선 차단제 0.1~0.3%, 경화제 4.4, 디페닐 메탄 디이소시아네이트(MDI) 15~20%를 포함하여 형성되고, 도포량이 500~ 800g/㎡인 것을 특징으로 하는 단열부직포를 이용한 복합시트 구조체.The method of claim 1, wherein the solvent-free urethane waterproofing layer,
It is formed in a two-component form consisting of a main agent and a curing agent, wherein the main agent is 35-40% of a branched polyether-polyester polyol, 30-50% of a filler potassium bicarbonate, 3-10% of a pigment, and an antifoaming agent of 0.1-0.5. %, Sunscreen 0.1 to 0.3%, curing agent 4.4, diphenyl methane diisocyanate (MDI) is formed comprising 15 to 20%, the composite sheet structure using an insulating nonwoven fabric, characterized in that the coating amount is 500 ~ 800g / ㎡.
상기 아크릴 코팅제층은,
용제형 아크릴수지로써 유리전이온도(Tg)가 56±5℃인 제품과 유리전이온도(Tg)가 1±3℃인 제품을 (3:7) 비율로 혼합하여 여기에 자외선 차단제 티뉴빈(Tinubin) 296 0.1~0.3%을 배합한 용제형 아크릴수지 코팅제로 형성되며, 상기 용제형 아크릴수지 코팅제의 도포량이 80~100g/㎡인 것을 특징으로 하는 단열부직포를 이용한 복합시트 구조체.The method of claim 1,
The acrylic coating agent layer,
As a solvent type acrylic resin, a product with a glass transition temperature (Tg) of 56 ± 5 ° C and a product having a glass transition temperature (Tg) of 1 ± 3 ° C (3: 7) are mixed and added to the sunscreen Tinubin. 296. A composite sheet structure using an insulating nonwoven fabric, which is formed of a solvent type acrylic resin coating agent containing 0.1% to 0.3%, and the coating amount of the solvent type acrylic resin coating agent is 80 to 100 g / m 2.
상기 부직포 시트층에 주방수 기능 및 접착 기능의 무기도막 방수제층이 코팅되는 단계;
상기 무기도막 방수제층에 글라스 화이버층의 일면이 접착되어 상기 무기도막 방수제층의 상기 글라스 화이버층이 적층되는 단계;
상기 글라스 화이버층에 방수 기능의 무용제 우레탄 방수제층이 코팅되는 단계;
상기 무용제 우레탄 방수제층에 아크릴수지 코팅제층이 코팅되는 단계를 포함하는 것을 특징으로 하는 복합시트 구조체를 이용한 방수 공법.Laminating a nonwoven sheet layer having a thermal insulation function to the base surface;
Coating an inorganic coating waterproofing layer having a kitchen water function and an adhesive function on the nonwoven fabric sheet layer;
Attaching one surface of the glass fiber layer to the inorganic coating waterproofing layer so that the glass fiber layer of the inorganic coating waterproofing layer is laminated;
Coating a waterproof solvent-free urethane waterproofing layer on the glass fiber layer;
Waterproofing method using a composite sheet structure comprising the step of coating an acrylic resin coating layer on the solvent-free urethane waterproofing layer.
상기 부직포 시트층은 두께는 6㎜이상 부직포의 중량은 300±20g/㎡ 이상으로써 상기 바탕층에 적층되는 것을 특징으로 하는 복합시트 구조체를 이용한 방수 공법.The method of claim 7, wherein
The non-woven fabric sheet layer is a waterproof method using a composite sheet structure, characterized in that the thickness of the non-woven fabric is more than 6mm laminated on the base layer to 300 ± 20g / ㎡ or more.
상기 무기도막 방수제층의 상기 부직포 시트층에 대한 적층은 무기도막 방수제를 1300~1500g/㎡로 도포하여 이루어지고, 상기 글라스 화이버층의 상기 무기도막 방수제층에 대한 적층은 유리섬유 직물시트를 무게 300± 20g/㎡로 적층하여 이루어지며, 상기 무용제 우레탄 방수제층의 상기 글라스 화이버층에 대한 적층은 무용제 우레탄 방수제를 500~800g/㎡로 도포하여 이루어지고, 상기 아크릴 코팅제층의 상기 무용제 우레탄 방수제층에 대한 적층은 용제형 아크릴 코팅제를 80~100g/㎡로 도포하여 이루어지는 것을 특징으로 하는 복합시트 구조체를 이용한 방수 공법.The method of claim 7, wherein
Lamination of the inorganic coating waterproofing layer of the nonwoven fabric sheet layer is made by applying an inorganic coating waterproofing agent of 1300 ~ 1500g / ㎡, lamination of the inorganic coating waterproofing layer of the glass fiber layer weighs 300 glass fiber fabric sheet It is made by lamination to ± 20g / ㎡, the lamination to the glass fiber layer of the solvent-free urethane waterproofing layer is made by applying a solvent-free urethane waterproofing agent to 500 ~ 800g / ㎡, to the solvent-free urethane waterproofing layer of the acrylic coating layer Lamination is a waterproof method using a composite sheet structure, characterized in that the coating is made of a solvent type acrylic coating at 80 ~ 100g / ㎡.